IS : 432(Partl)-1982
( Reaffirmed 1995 )

Indian Standard
SPECIFICATION FOR
MILD STEEL AND MEDIUM TENSILE STEEL
BARS AND HARD-DRAWN STEEL WIRE FOR
CONCRETE REINFORCEMENT
PART I MILD STEEL AND MEDIUM TENSILE STEEL BARS

( Third Revision )
Fifth Reprint DECEMBER 1992

UDC 669.141.24-422+669.14-018*295-422 : 666 982~24

0 Copyright 1982

BUREAU OF JNDJAN STANDARDS
MANAK BHAVAN, 9 BAHADUR SHAH ZAFAR MARG
NEW DELHI 110002

Gr 3 June 1982

IS : 43!2( Part I ) - 1982

Indian Standard
SPECIFICATION FOR
PART 1 MILD STEEL AND MEDIUM TENSILE STEEL BARS

( Third Revision )
Joint Sectional Committee for Concrete Reinforcement, BSMDC 8
Chuirman Representing
SBRI G. S. RAO Central Public Works Department, New Delhi
Members
S~~PERINTENDIN~ ENGINEER ( CD0 ) ( AIttr~tc to
Shri G. S. Rao )
DxJ. L. Asmax The Tata Iron & Steel Co Ltd, Jamshedpur
SHRI A. N. MITRA ( Alternate )
SHHI S. BANERJEE Steel Re-rolling Mills Association of India, Calcutta
SEIKIS. N. CHANIU Metallurgical and Engineering Consultants ( India )
Ltd, Ranchi
SHR.I R. D. CHOUDI~ARY ( Altcrnafe )
CHIEF ENGINEER ( D & R ) Irrigation Department, Government of Punjab,
Chandigarh
DIRECTOR ( CD ) ( Alternafe )
DEPUTY D~REOTOR, STAND~RDJ Research, Designs & Standards Organization,
( B & S )-I Lucknow
ASSISTANT D I R E c T o R,
STANDARDS ( B & S )-II ( ANcrnate )
SHRI M. R. DOCTOR Special Steels Ltd, Bombay
SHRI S. G. JOSHI ( Alternate )
SHRI V. GULATI Heatly & Gtesham ( India ) Ltd, New Delhi
SHRI P. K. G~PTE National Metallurgical Laboratory ( CSJR ),
Jamshedpur
SHRI N. C. Jnw Stup Consultants Ltd, Bombay
SHRI M. C. TANDON ( AIternate )
SHRI M. P. JASGJA Research & Development Centre for Iron & Steel
( Steel Authority of India Ltd ), Ranchi
SHRI A. JAYAQOPAL Engineer-in-Chief’s Branch, Army Headquarters,
New Delhi
MutaJ CHANDRASEKHAXAN ( Alternatc )
R.
( Continued on page 2 1

@ Cbpyr:ghr 1992
BUREAU OF INDIAN STANDARDS
Tbu publication is protected under the Indiun Gpyrtght Act ( XIV of 1957 ) iM1
reproduction in whole or in part by any means except with written permission of the
publiler &tall be deemed to be an infringement of copyright under the said Act
4

IS : 432 ( Part I ) - 1982

( Conhud from page 1 )
Members Raprtscnling
SHR1 S. Y. ?&AN Killick Nixon Ltd. Bombay
SHRI P. S. VENKAT ( Afttrnute )
SERI K. K. KHANNA National Buildings Organization, New Delhi
SERI K. S. .%tIN-rvASAN ( AhlMlt )
SBEI M. N. KHANNA Bhilai Steel Plant, Bbilai
SERI C. Daaom=~~ ( AltcrMrr )
SERI S. N. MANOHAR Tata Consulting Engineers, Bombay
SHRI N. NAOARAJ ( Al;& )
SHRI R. K. MATHUR Public Works Department, Lucknow
SBRJ Y. K. MEHTA The Concrete Association of India, Bombay
SHRI E. T. ANTIA ( Altcrmtc )
DR P. K. MORANTY Tor Steel Research Foundation in Indii, Calcutta
DR INO. P. K. BANERJEE ( Al-t )
SERI -4. D. NARA~ Roads Wing, Ministry of Shipping and Transport
DuV.P. NARAYANABWAYY Struc;oy:kFengineering Research Centre ( CSIR ),

SERI Z. GEOROE Altmu:t )
(
SERI S. N. PAL M. N. Dastur & Co (P) Ltd, Calcutta
SHRI SALIL ROY ( Aknnuft )
SHRI B. K. PANTHAKY Hindustan Construction Co Ltd, Bombay
SHRI P. V. KAIK ( Alternate )
DR G. P. SAX.4 Gammon India Ltd, Bombay
SHRI A. C. ROY ( Ahrnalc )
SFIRI T. SBN IRC Steels Ltd, CalcuttP
SERI SEIRE!IH H. SHAH Tensile Steel Ltd, Bombay
SRRI M. S. PATHAX ( Altcrrurlt )
SHRI C. N. SRINIVASAN C. R. Narayana Rao, Madras
SARI C. N. RA~HA~ENDRAN ( Ahnab )
SERX S. SUBRAMANIAN Cement Research Institute of India, New Delhi
SHRI AWL KUMAR ( Ahmalt )
SERX G. RAMAN, Director Gwteral,BIS ( &-o@ Mti )
Director ( Civ Engg )

&Mary
SHRI M. N. NEELAKAXDHA~
As&ant Director ( Civ Engg ) BIS

2

IS : 432 ( Part I ) - 1982

Indian Standard
SPECIFICATION FOR
PART I MILD STEEL AND MEDIUM TENSILE STEEL BARS

( Third Revision )

0. FOREWORD
0.1 This Indian Standard ( Part I ) ( Third Revision ) was adopted by the
Indian Standards Institution on 31 March 15’82, after the draft finalized
by the Joint Sectional Committee for Concrete Reinforreuent had been
approved by the Civil Engineering Division Council and the Structural
and Metals Division Council.
0.2 This standard was first published in 1953 and subsequently revised
in 1960 and 1966. The present revision hay been taken up with a view
to modifying the earlier provisions in the light of the experience gained
during the use of this standard by both manufacturers and users.

0.3 This standard adopts SI units in specifying the various physical
requirements. Further, some of the provisions have been revised ba?ed
on the latest Indian Standards, such as IS : 22G-ltr75*, IS : 961-1975t,
IS : 1599-1974:, IS : 1608-1972$, IS : 1732-197111, IS : 1762 ( Part I )-
19741 and IS : 1977-1975**.
0.4 The concrete reinforcement having an ultimate tensile strength of
not less than 540 N/mm2 has been categorized as ‘ medium tensile steel ’
instead of ‘ high tensile steel ’ ( see IS : 961-1975t ) in this standard. In
concrete reinforcement, the term ‘ high tensile steel ’ is, as a general
_._-.__
*Specification for structural steel ( standard quality ) (fiflh rwision ).
+Specilication for structural steel ( high tensile ) ( second
reckion).
*Method for bend test for steel products other than sheet, strip, wire and tube ( jirst
rcviGn ) .
§Method foi tensile testing of steel products ( jirirst
w&ion ).
IlDimensions for round and square steel bars for structural and gcncral cnginecrirg
purposes (J&t revision ).
ICode for designation of steel : Part I Based on letter symbols (jirrf r&ion ).
**Specification for structural steel ( ordinary quality ) ( second rcoism 11.

3

IS : 432 ( Part I ) - 1982

practice, used IO mean steel having tensile strengths in a &ill higher
range, say 1 000-2 200 N/mm’ which is generally used in prestrqsed
concrete.

0.5 Grade II mild steel bars are not recommended for use in structures
located in earthquake zones subjected to severe damage and for
structures subjected to dynamic loading ( other than wind loading ),
such as railway and highway bridges ( see IS : 1893-1975* and
IS : 1977-1973t ).

0.6 Velding of reinforcement bars covered in this specification shall be
done in accordance with t!le requirements of IS : 2751-1966:.

0.7 In the formulation of this standard, due weightage has been given to
international coordination among the standards and practices preva%ng
in different countries in addition to re!ating it to the Practices in the field
in this country.

0.8 For the purpose of deciding whether a particular requirement of
this standard, is complied with, the final value, observed or calculated,
expressing the result of a test or analysis, shall be rounded off in accord-
ance with IS : 2-19604. The number of significant places retained in the
rounded off value should be the same as that of the specified value in this
standard.

1. SCOPE
1.1 This standard ( Part I ) covers the requirements of mild steel and
medium tensile steel plain bars in round and square sections for use as
reinforcement in concrete.

2. TEBMINOLOGY

2.0 For the purpose of this standard, the following definitions shall
apply.
2.1 Bar - A hot-rolled bar of steel of circular or square cross-section.

2.2 Bundle - Two or more ‘ coils ’ or a number of lengths properly
bound together.

2.3 Coil - One continuous bar as rolled in the form of a coil.

‘Criteria for earthquake resistant design of structures (r&d rtiiun ).
tSpecifi:ation for structural steel ( ordinary quality ) ( sccmdretiion ).
$Code of practice for welding of mild steel bars used for reinforced concrete
construction.
&Rules for rounding off numerical valua ( m&d).

4

IS : 432 ( Part I ) - 1982

2.4 Elongation - Increase in length of a tensile test piece under .stress.
The elongation at fracture is conventionally expressed as a percentage of
the original gauge len-,th of a standard test piece.

2.5 Nominal Size - The nominal size of a bar shall be the dimension
of the diameter of round bars and side of square bars.

2.6 Parcel - Any quantity of bars whether in coils or bundles, presented
for examination and test at any one time.

2.7 Ultimate Tensile Stress - The maximum load reached in a
tensile test clivi:!ed by the original cro;s-sectional area of the gauge length
portion of ihe test piece.

2.8 Yield Stress - Stress ( that is, load per unit cross-sectional area )
at which elongation first occurs in the test piece without increasing the
load during tcn;ile test. In the case of steels with no such definite yield
point, the yield stress is the stress under the prescribed testing conditions
at v!lich the ohserv-ed increase in the gauge length is l/200 of the gauge
length when the rate at which the load applied is not more than 5
N/mm’js when approaching the yield stress.

3. TYPES AND GRADES

3.1 Reinforcement supplied in accordance with this standard shall be
classified into the following types:

a) Mild stee! bars, and
b) Medium tcnrile steel bars.

3.1.1 Mild steel bars shall be supplied in the following two grades:

a) Mild steel bars, Grade I; and
b) Milcl steel bars, Grade II.

4. MANUFACTURE AND CHEMICAL COMPOSITION

4.1 Steel for mild steel reinforcement bars, Grade I shall be manufactured
and have the chemical compositicn in accordance with the requirements
of Steel Designation Fe 410-S of JS : 226-1975*.

4.2 Steel for mild steel reinforcement bars, Grade II shall be manu-
factured and have the chemical composition in accordance with the
requirements of Steel Designation Fe 410-O of IS : 1977-1975t.

*Specification for structural stc:rl ( standard quality ) ( jjlh recision ).
tSpecification for ztructural steel ( ordinary quality ) ( secon’d recision ).

5

IS:432(PartI)-1982

4.3 Medium tensile steel bars shall be manufactured and have the
chemical composition in accordance with the requirements of Steel
Designation Fe 540 --HT of IS : C61-1975*

5. FREEDOM FROM DEFECTS
5.1 All finished bars shall be well and cleanly rolled to the dimensicns
and weights specified. They shall be free from cracks, surface flas,
laminations and rough, jagged and imperfect edges and all other harmful
defects,
6. NOMINAL SIZES AND MASS
6.1 Sizes - Mild steel and medium tensile steel bars shall be supplied in
the following nominal sizes:
Diameter of round bars or side 5, 6,8, 10, 12, 16, 20,22,25, 28,
of square bars 32,36,40,45 and 50 mm
6.2 Mass - The mass of bars shall be in accordance with IS : 1732-
1971?.

7. TOLERANCES
7.1 The rolling and cutting tolerances shall be in accordance with IS :
1852-1973$.

8. PHYSICAL REQmMENTS
8.1 The ultimate tensile stress, yield stress and percentage elongation
when determined in accordance with 9.2 shall be as given in Table 1.
8.2 The bars shall also withstand the bend test specified in 9.3.

9. TESTS
9.1 Selection and Preparation of Test Samples - Unless other-
wise specified in this standard, the requirements of IS : 226-15753 shall
apply.
9.1.1 All test pieces of bars shail be selected by the purchaser or his
authorized representative, either:
a) from the cutting of bars; or

*Specification for structural steel ( high tewile ) ( zecondwrkion ).
tDimensions for round and square steel bars for structural and general engineering
purpose3 ( i;.rr fcciJion ) .
$Specii%atio~n for rolling and cutting tolerances for hot-rolled steel products ( secomi
fmiJim ).
#pecification for structural steel ( standard quality ) (jj?h rmi.rion ).

6

IS : 432 ( Part I ) - 1982

TABLE I MECHANICAL PROPERTIES OF BARS
( ClaUJI 8.1 )

SL No. TYPE AND NOYR(AL SIZE ULT~ATE YIELD STRESS ELONaATION*
OF BAR TENSILE PERCENT,
STREBB,
Min Min Min

I. Mild SteelGmdr I

For bars up to and including 410 250 23
20 mm
For bars over 20 mm, up to 410 240 23
and including 50 mm

2. Mild Steel Grade II

For pmuz to and including 370 225 23

and including 50 mm

3. M&urn 7caril.s S~ccl

For l~~~;p to and including 540 350 20

and including 32 mm
and Including 50 mm

*Elongation on a gauge length 5.65 c/ Sowhere So is the cross-sectional area of the
tut piece.

b) if he so desires, from any bar or the coil, after it has been cut to
the required or specified length and the test piece taken from any
part of it.

9.1.1.1 In neither case, the test piece shall be detached from the bar
or the coil, except in the presence of the purchaser or his authorized
representative.

9.1.1.2 Before test pieces are selected, the manufacturer or supplier
shall furnish the purchaser or his authorized representative with copies
of the mill records giving the number of bars in each cast with sizes as
well as the identification marks whereby the bars from their cast or each
coil can be identified.

7

IS : 432 ( Part I ) - 1982

9.2 Tensile Test - The ultimate rensiie stres+, yield stress and elonga-
tion of bars shall be determined in accordance with the requirements of
IS : l.608-19i2* read in conjunction lvith I5 : 226-1975t. The ‘test
pieces shall be cut from the finished material and straightened where
necessary. They shall not be annealed or otherwise subjected 10 heat
treatment. Any slight straightening lvhich may be required shal! be done
cold.

9.2.1 In case of bars, the size of which is not uniform rhrou$out the
length of test piece, limits shall be applied according to the actual maxi-
mum thickness of the piece selected for testing.

9.2.2 Should a tensile test piece break ontside the middle half of its
gauge length and the percentage elongation obtained is less than that
specified, the test may be discarded at the manufacturer’s option, and
another test made from the same bar.

9.3 Bend Test - The bend test .shall be performed in accordance with
the requirements of IS : 1599-1974: read in conjunction with 1s : 226-
1975t.

9.4 Retest - Should any one of the test pieces first selected fail to pass
any of the tests specified in this standard, tvo further samples shall be
selected for testing in respect of each failure. Should the test pieces from
both these additional samples pass, the material represented by the test
samples shall be deemed to comply with the requireinents of that parti-
cular test. Should the test piece from either of these additional samples
fail, the material represented by the test samples shall be considered as
not having complied with this standard.

9.5 Sampling - Sampling for tensile and bend tests shall be in accdrd-
ante with IS : 226-1975t.

10. DELIVERY, INSPECTION AND TESTING FACILITIES
10.1 ‘Unless otherwise specified, general requirements relating to the
supply of material, inspection and testing shall conform to IS :, 1387-
19675.

10.2 Ko material shall be despatched from the manufacturer’s or
suppliers’ premises prior to its being certified
by the purchaser or hir
authorized representative as having fulfil!ed the tests and requirements
laid down in this standard except where the bundle or coil containing
the bars is marked with the IS1 Certification Mark.

*Method for tensile testing of steel products (fist rnisM ).
Wpecification for structural steel ( standard quality ) ( jifh revision ).
fblethod for bend test for steel products other than sheet, strip, wire and tube
(first Wztiion).
weneral requhements for therupply of metallurgical materials (/irsl rclfnr ).

8

IS : 432 ( Part I ) - 1982

10.3 The purchaser or his authorized representative shall be at liberty
to inspect ,and verify the steel maker’s certificate of cast analysis at the
premises of the manufacturer or supplier; when the purchaser requires
an actual analysis of finished material, this shall be made at a place
agreed to between the purchaser and the manufacturer or supplier.

10.4 Manufacturer’s Certificate -In the case of bars which have
not been inspected at the manufacturer’s works, the manufacturer or
supplier, as the case may be, shall supply the purchaser or his authorized
representative with the certificate stating the process of manufacture
and also the test sheet signed by the manufacturer giving the result of
each mechanical test applicable to the material purchased, and the
chemical composition, if required. Each test sheet shall indicate the
number or identification mark of the cast to which it applies, corres-
ponding to the number or identification mark to be found on the
material.

11. IDENTIFICATION AND MARKING
11.1 The manufacturer or supplier shall have ingots, billets and bars or
bundles of bars marked in such a way that all finished bars can be traced
to the cast from which they were made. Every facility shall be given to
the purchaser or his authorized representative for tracing the bars to the
cast from which they were made.
11.2 The medium tensile steel bars shall be suitably marked to identify
them from mild steel bars. Mild steel b ars Grade I and II shall have
distinctive identification tags.

11.3 Each bundle or coil containing the bars may also be suitably
marked with the Standard Mark, in which case the concerned test arti-
ficate shall also bear the Standard Mark.

NOTE -The use of the Standard Mark is governed by the provisions of the
Bureau of Indian Standards Act, 1956 and the Rules and Regulations made there-
under. The Standard Mark oa products covered by an Indian Standard conveys
the assurance that they have been produced to comply with the requirements of that
standard under a well defined system of inspection, testing and quality control
which is devised and supervised by BIS and operated by the producer.. Standard
marked products are also continuously checked by BIS for conformity to that
standard as a further safeguard. Details of conditions under which a license for
the use OF the Standard Mark may be granted to manufacturers or producers may
be obtained from the Bureau of Indian Standards.

9

BUREAU OF INDIAN S-f-ANDARDS

Headquarters :
Manak Bhavan, 9 Bahadur Shah Zafar Marg. NEW DELHI 110002
Telephones : 331 01 31 Telegrams : Manaksansthe
331 13 75 (Common to all Offices)
Regional Offices : Telephone
Central : Manak Bhavan, 9, Bahadur Shah Zafar Marg. 331 01 31
NEW DELHI 110002 331 13 75
l Eastern : l/14 C.I.T. Scheme VII M. 37 86 62
V.I.P. Road, Maniktola, CALCUTTA 700054
Northern : SC0 445-446, Sector 35-C, CHANDIGARH 160036 21843
Southern : C.I.T. Campus, IV Cross Road, MADRAS 600113 41 29 16
t Western : Manakalaya, E9 MIDC. Marol. Andheri (East). 6 32 92 95
BOMBAY 400093
Branch Offices :
‘Pushpak’, Nurmohamed Shaikh Marg. Khanpur, AHMADABAD 380001 2 63 48
t Peenya Industrial Area, 1st Stage. Bangalorn-Tumkur Road. 39 49 55
BANGALORE 560058
Gangotri Complex, 5th Floor, Bhadbhada Road. T.T. Nagar. 55 40 21
BHOPAL 462003
Plot No. 82/83, Lewis Road, BHUBANESHWAR 751002 5 36 27
Kalai Kathir Building, 6/48-A Avanasi Road, COIMBATORE 641037 2 67 05
Quality Marking Centre, N.H. IV, N.I.T., FARIDABAD 121001 -
Savitri Complex, 116 G. T. Road, GHAZIABAD 201001 8-71 19 96
5315 Ward No. 29, R.G. Barua Road. 5th By-lane, 3 31 77
GUWAHATI 781003
5-8-56C L. N. Gupta Marg, ( Nampally Station Road ) 23 10 83
HYDERABAD 500001
RI4 Yudhister Marg, C Scheme, JAIPUR 302005 6 34 71
117/418 B Sarvodaya Nagar, KANPUR 208005 21 68 76
Plot No. A-9, House No. 561/63, Sindhu Nagar. Kanpur’ Road, 5 55 07
LUCKNOW 226005
Patliputra lndustria Estate, PATNA 800013 6 23 05
District Industries Centre Complex. Bagh-e-Ali Maidan
SRINAGAR 190011
T. C. No. 14/1421, University P. 0.. Palayam. 6 21 04
THIRUVANANTHAPURAM 695034
hpection Offices (With Sale Point) :
Pushpanjali. First Floor, 205-A West High Court Road. 52 61 71
Shankar Nagar Square, NAGPUR 440010
Institution of Engineers (India) Building, 1332 Shivaji Nager 5 24 35
PUNE 411005
-
*Sales Office Calcutta is at 5 Chowringhee Approach. 27 68 06
P. 0. Princep Street, CALCUTTA
t Safes Office iS at NoveltyChambers, Grant Road, BOMBAY 89 65 28
# Sales Office is at Unitv Building, Narasimharaja Square. 22 39 71
BANGALORE

Printed at Dee Kay Prmters. New Delhi. India

432 1

More Related Content

What's hot (20)

Similar to 432 1 (20)

More from Siddhartha Bhamidipati (17)

Recently uploaded (20)

432 1