Application of nanotechnologies: energy

NANOYOU Teachers Training Kit in Nanotechnologies

Chapter 3‐
Energy
MODULE 2‐ Applications of Nanotechnologies

Written by Luisa Filipponi and Duncan Sutherland
Interdisciplinary Nanoscience Centre
Aarhus University, Denmark
January 2010

Creative Commons Attribution ShareAlike 3.0 unless indicated in text or figure captions.

NANOYOU Teachers Training Kit – Module 2‐ Chapter 3

Contents
Solar Energy ...................................................................................................................................................................
6

Photovoltaics .............................................................................................................................................................
6

Nanocrystals ..........................................................................................................................................................
7

Biomimetic approaches using nanotechnologies ......................................................................................................
8

Artificial photosynthesis ........................................................................................................................................
8

Quantum dot sensitized solar cells ...................................................................................................................... 0
1

Lotus‐mimicking PV coatings ............................................................................................................................... 0
1

Solar energy storage ................................................................................................................................................ 1
1

Solar heating ............................................................................................................................................................ 1
1

Hydrogen Society ......................................................................................................................................................... 2
1

Hydrogen production ............................................................................................................................................... 3
1

Nanotechnologies for improving photoinduced water splitting .......................................................................... 3
1

Hydrogen storage .................................................................................................................................................... 5
1

Solid metallic nanostructured supports ............................................................................................................... 6
1

The hydrogen fuel cell .............................................................................................................................................. 7
1

Proton exchange membrane fuel cell .................................................................................................................. 8
1

Thermoelectricity ......................................................................................................................................................... 9
1

Rechargeable Batteries ................................................................................................................................................ 1
2

Nanotechnologies to impact energy capacity, battery power, charge rate and lifetime ........................................ 1
2

Page 2 of 29

The research leading to these results has received funding from the European Community's Seventh Framework Programme
(FP7/2007‐2013) under grant agreement n° 233433


Nanomaterials as alternatives to conventional electrodes ................................................................................. 2
2

“Paper battery” .................................................................................................................................................... 3
2

Battery operation range, lifetime and safety .......................................................................................................... 3
2

Supercapacitors ....................................................................................................................................................... 4
2

Energy Saving .............................................................................................................................................................. 5
2

Catalysis ................................................................................................................................................................... 5
2

Advanced materials ................................................................................................................................................. 6
2

Insulators and ‘smart’ coatings ............................................................................................................................... 6
2

Energy‐harvesting materials .................................................................................................................................... 7
2

Efficient lighting ....................................................................................................................................................... 8
2

Efficient energy transport ........................................................................................................................................ 8
2

This document has been created in the context of the NANOYOU project (WP 4 Task 4.1). All information is
provided “as is” and no guarantee or warranty is given that the information is fit for any particular purpose. The
user thereof uses the information at its sole risk and liability. The document reflects solely the views of its
authors. The European Commission is not liable for any use that may be made of the information contained

Page 3 of 29



Chapter 3: Applications of
Nanotechnologies‐
Energy

Today’s world energy demands are satisfied mainly via the combustion of fossil fuels. Of the 210 million
barrels of oil equivalent per day used worldwide, about 85 million barrels come from oil; the rest comes
from coal (23%), gas (17%), biomass (17%), some fission (5%), little hydroelectric (6%) and almost none
from renewable resources (Figure 1).

It is estimated that by 2050 we will need twice the
amount of energy that we are burning or
consuming today (about 14 Terawatts, TW) and
that most energy will have to come from solar,
wind and geothermal (50%) energy. By then it is
expected that the world’s population will rise from
today’s 6.3 billion people to 9 billion people.
Relying on fossil fuels (oil, coal and natural gas) to
‘feed’ the world’s future energy needs is not a
responsible environmental option, since there is
Figure 1 Global primary energy consumption. some evidence that the combustion of fossil fuels
is the main cause of the high levels of greenhouse
gases such as carbon anhydride (CO2) that are
accumulating in the atmosphere, with consequent dramatic worldwide climatic changes.

Page 4 of 29



But the problem is not limited to the Ranking Problem
Table 1: List of the most
environmental impact of using fossil fuels. 1 Energy important problems
The availability of fossil fuels is limited and 2 Clean Water facing humanity for the
its supply presently decreasing, so as the 3 Food next 50 years (adapted
demand for energy increases, so does the 4 Environment from 1. R. E. Smalley,
cost of fossil fuels. Affordable energy is 5 Population
Future Global Energy
6 Disease
instrumental for basically every aspect of Prosperity: The Terawatt
7 War/Terrorism
our present societies, including preserving Challenge, Materials
8 Poverty
global peace. In fact, in the list of the most 9 Matters Bulletin, Vol. 30,
Education
June 2005, 412‐417).
important problems facing humanity for the 10 Land
next 50 years, energy is on the top (Table
1). The reason is that affordable energy is fundamental for dealing with the problems herein listed: the
availability of clean water, food, down to poverty and education.

So we are presently living an “energy challenge” and there is an urgent need for energy resources
alternative to fossil fuels. Of these, renewable energy sources that are CO2‐neutral1 (solar, wind,
geothermal, hydro etc.) are an option. However, tremendous technology breakthrough will need to
occur in the next years to make the conversion of these energy resources an efficient and economically
viable option. Solar energy is an excellent example. Every day the Earth is hit by 165,000 TW of solar
power; to put it in the words of Nobel Prize Richard E. Smalley, every day “we are bathed in energy”2.
The problem is that renewable energy sources like solar energy are not constant in time and evenly
distributed geographically (Figure 2). Therefore, solar energy collection, conversion, storage and
distribution are major challenges: the entire process needs to be efficient and cost effective. Current
solar panels have about 15‐20% energy conversion efficiency, but they are very expensive. Since solar
light is only available during part of the day, suitable storage solutions also need to be found.

Another alternative energy carrier is hydrogen, but hydrogen fuel cell technology will have to face a
number of issues (e.g., hydrogen extraction, hydrogen storage, fuel cell lifetime and cost, just to
mention few) before a hydrogen economy can become a reality. Solving the future energy challenges
does not only require advancements in the field of energy conversion and storage, but also energy

1
CO2‐neutral here is intended as an energy carrier that does not produce directly CO2 upon conversion (like solar
energy or hydrogen).
2
‘Energy challenge’ discussed by Professor R. E. Smalley see http://smalley.rice.edu
Page 5 of 29



saving, considering how much energy is wasted today using conventional incandescent lights. As
discussed in this paper, nanotechnologies not only have the potential to solve many of the issues that
the energy sector is facing, but its application to this sector has already resulted in advanced research
projects and some commercial realities.

Solar Energy
Among the renewable sources of energy, solar energy holds a great potential. Solar light, though, is not
constant, it is only available during part of the day, and it is geographically uneven, some countries
receive a much higher illumination then others. Figure 2 gives an idea of the area that should be covered
worldwide in order to produce a little more than the world's current total primary energy demand
(assuming a conversion efficiency of 8 %). The main problem associated with this form of energy is not
its supply, but the development of devices that will allow
for its efficient and cost‐effective conversion into electric

Figure 2. Solar power systems installed in the areas defined
by the dark disks could provide a little more than the world's
current total primary energy demand (assuming a
conversion efficiency of 8 %). Colours in the map show the
local solar irradiance averaged over three years (Image
credit: http://www.ez2c.de/ml/solar_land_area/)

current. The second biggest problem is its storage and efficient transport. Areas that are mostly
irradiated are desert, therefore most of the time remote from main urban centres, so transporting this
energy where mainly needed becomes a challenge. Making solar energy a viable alternative to fossil
fuels therefore requires a series of advancements that most likely will be possible through fundamental
research into solar energy conversion, storage and transport.  A lot of these advancements are likely to
be enabled by nanotechnologies.

Photovoltaics
A photovoltaic (PV) device is a device which converts solar energy into electricity. In a conventional
photovoltaic cell there are two separate material layers, one with a reservoir of electrons that functions
as the negative pole of the cell, and the other having vacancies of electrons, the electron holes, that

Page 6 of 29



functions as the positive pole. When sun light or other light sources is absorbed by the cell, enough
energy is provided to the cell to drive the electrons from the negative to the positive pole, creating a
voltage difference between them. This way, the cell can serve as a source of electrical energy. The
efficiency of a PV depends on the type of semiconductor it is made of, and on its absorbing capacity. All
semiconductors adsorb only a precise ‘energy window’ (the ‘band gap’) which is just a fraction of the
entire solar energy available. Presently, maximum energy conversion efficiency (around 15‐20%) in a PV
cell is obtained when this is made of crystalline Silicon (Si). This in an excellent conduction material,
abundant and widely used in electronics, but has the main drawback of being very expensive to
produce, which is reflected in the high cost of current PVs. This has limited their use. Alternative,
cheaper materials, such as TiO2, can be used in PV technology. TiO2 is a well known non‐toxic
semiconducting material, but has the characteristic of adsorbing only the UV region of the solar
spectrum, which represents only about 5% of the total solar energy available. This material therefore
leads to cheaper PVs but with lower energy conversion efficiency.

As we will discuss here, nanotechnologies offer the possibility to introduce alternative materials and
fabrication methods to produce cells with tailored adsorption characteristics in order to adsorb a larger
portion of the solar energy spectrum. In order to meet the “energy challenge” through solar energy,
conversion efficiencies in the order of 45% are needed so the research in this area is very intense and
numerous different types of nanomaterials are being investigated. in order to reach this ambitious goal,
devices must be made of materials that absorb the visible part of the solar spectrum, which represents
about 46% of it.

There are basically two approaches being investigated:

1. Development of silicon nanocrystals engineered in a way to absorb more solar energy;

2. Biomimetic approaches, where the photovoltaic device is engineered to mimic the best known solar‐
conversion process ever made, the natural photosynthesis molecular machine.

Nanocrystals
The limitation of silicon is not only related to its processing cost. Due to its indirect band gap, silicon is
weak in adsorbing light‐only a fraction of the solar spectrum is absorbed. This is where nanoscience can
help: in sufficiently small nanocrystals the band gap becomes quasi‐direct, which gives rise to strong
light absorption. Thus the optical properties of silicon can be improved by adding nanocrystals. One

Page 7 of 29



such example is silicon‐based tandem solar cells, where the top cell is based on nanocrystals, while the
bottom cell is a standard silicon cell. Inside the solar cells the nanocrystals are used to increase the
generation of current.

Biomimetic approaches using nanotechnologies
Nature has developed an amazing “splendid molecular machine” that enables the conversion of solar
energy into chemical energy through a process called photosynthesis. In this process solar energy is
converted into stored chemical energy (in the form of carbohydrates). The process is an amazing
example of a natural nanotechnology which serves as an inspiration for creating biomimetic devices
capable converting solar energy into other forms of energy. In photovoltaics the aim is the conversion
into electricity, to be used for powering electrical appliances. In photosynthesis, light is “captured” by
light‐harvesting antennas (e.g., chlorophyll) in which photons are absorbed, exciting electrons to higher
energy states. The pigment in the “antenna” absorbs strongly in most of the visible region of the solar
spectrum. The energized electrons are transferred to a series of reaction centres which are called
Photosystem I and Photosystem II. In these reaction centres a series of photochemical electron transfer
reactions occur involving quinines. Eventually the energy is transferred to proton bonds to another
reaction centre where the energy is stored in the bonds of the ATP molecule, which reacts further to
form NADP+. In the final step of the process, hydrogen is taken from water (forming NADPH), releasing
oxygen as by‐product. The NADPH stores energy until it is used in the next step of the reaction to
provide energy for the formation of C‐C bonds, consuming carbon dioxide in the process. The end
product are carbohydrates. Therefore the overall process consumes water and carbon oxide, and
produces carbohydrates, which is the fixed‐form of carbon that is the base for all animal life.

Artificial photosynthesis
Some researchers have been able to extract from spinach the complex Photosynthesis I and use it to
power solid‐sate electronic devices. This represents an example of a biomimetic solid‐state
photosynthetic solar cell. Creating the interface is not trivial because in the plant the complex requires
salts and water to function, which obviously cannot be used in electronic devices, so surfactants are
used instead. The device is made of alternating layers of conducting material (gold), biological material,
semiconducting layer, and conducting layer on top. The conversion efficiency of the device is 12%.

Page 8 of 29



Dyesensitized solar cell
The second approach is an hybrid between conventional photovoltaics, which uses semiconducting
materials, and artificial photosynthesis. To date this seems the most promising approach to improve PV
efficiency. In this approach to the surface of the semiconductor (e.g., TiO2) are attached some other
strongly absorbing specie (‘dye’) which mimic the function of the chlorophyll. These type of cells, are
called dye‐sensitized cells, or “Gräztel cell” from the name of its inventor, or photoelectrochemical cells
(PEC). The complex dye molecules (called sensitizer) are attached to the surface of a mesoporous
titanium oxide. The difference from a classical thin‐film PV is that here light is absorbed in a
semiconductor layer, whereas in the Gräztel cell absorption occurs in the dye molecules.

The dye molecules act in some way like an antenna (mimicking the chlorophyll), meaning that more of
the light of a particular colour can be captured but also that a wider range of colours of light can be
absorbed compared to pure TiO2, this way
increasing the efficiency of the device (Figure 3).

In the Gräztel cell the anode is made of
mesoporous dye‐sensitised TiO2 and receives
electrons from the photo‐excited dye which is
thereby oxidised. The oxidised dye in turn
oxidised the mediator, a redox specie that is
dissolved in the electrolyte. The mediator is
regenerated by reduction at the cathode by the
electrons circulated through the external circuit.
The mesoporous nature of the titanium oxide
provides an enormous internal surface area,
Figure 3. Schematic of the operation of the dye‐
therefore reducing the amount of material sensitised electrochemical photovoltaic cell (Gräztel
needed in the cell. The titanium oxide films are cell). (Image credit: L Filipponi, iNANO, Aarhus
produced from a nanoparticle suspension (which University, own work).
is synthesised to form a stable porous material).
Specific synthetic dyes are under development to increase light absorption. These cells are extremely
promising because they are made of low‐cost materials and do not need elaborate apparatus to
manufacture. Current scale up of production utilizing polymer materials and roll to roll continuous
production has the potential to produce the large areas of solar cell required to capture significant

Page 9 of 29



amounts of solar energy. Some companies, such as DyeSol, are already producing and selling those types
of solar cells, with conversion efficiencies of about 12% (Figure 4).

Figure 4. A dye solar cell (DSC) commercialised by DyeSol. (Source:
www.dyesol.com)

Quantum dot sensitized solar cells
Another possibility is to use semiconductor nanocrystals (known as quantum dots, QDs) instead of the
photosensitive dyes used in the Gräztel cell. For example, CdS, CdSe, InP and InAs quantum dots have
been combined with mesoscopic networks of TiO2 nanoparticles to obtain quantum‐dot‐sensitized
solar cells (QDSSCs). In general, QDs offer several advantages compared to organic dyes such those
employed in a Grätzel cell: they provide the ability to match the solar spectrum better because their
adsorption spectrum can be tuned with particle size. An important nanotechnology discovery that has a
great potential to increase the efficiency of these types of solar cells was reported in May 2006 by a
team of the Los Alamos National Laboratory. Researchers from this group found that when
nanoparticles of less then 10 nm in diameter made of lead and selenium (PbSe nanoparticles) are
illuminated with light they adsorb one photon of light but produce up to three electrons5. When today’s
photovoltaic solar cells adsorb one photon of sunlight, the energy gets converted to one electron, and
the rest of the photon’s energy is lost in heat. Therefore PbSe nanoparticles produce at least twice the
electrons compared to conventional semiconductors, a process known as ‘carrier multiplication’. This
nanotechnology discovery could boost the efficiency from today’s solar cells of 20‐30% to 65%.

Lotusmimicking PV coatings
The Lotus leaf is characterized by being extremely water‐repellent, so much that water simply rolls off
its surface dragging dirt during the droplets motion. The consequence is the extreme cleanness of the
leaf, which in fact is a sign of purity in some Indian cultures. The super‐hydrophobic properties of the
Lotus leaf are a consequence of its micro‐ and nano‐topography, as well as its surface chemistry (see

Page 10 of 29



Chapter 2). Superhydrophobic surfaces are useful to improve the performance of solar cells. One of the
problems with this technology is that they are kept outdoors and therefore prone to become very dirt.
This layer of dirt “masks” the catalytic areas of the solar cells and therefore reduces its efficiency and
life‐time. Coating the solar panel with a superhydrophobic coating keeps the panel considerably cleaner.
Because of the nano‐surface roughness, the coating is transparent to UV light, a necessity for these
types of devices. The superhydrophobic coating is also durable, which further improves the solar panel
life‐time.

In one research PV cells have been coated with a nanostructured coating which increases the
absorption of light. The coating mimics the Lotus leaf so is super hydrophobic, with the effect of also
conferring self‐cleaning properties to the PV surface.

Solar energy storage
Storage of electrical power is critical for making solar energy a primary power source. The best place to
provide this storage is locally, near the point of use. Ideally every house, every business, every building
should have its own local electrical energy storage device, an uninterruptible power supply capable of
handling the entire needs of the owner for 24 hours. If this were done using today’s lead‐acid storage
batteries, such a unit for a typical house capable of storing 100 kilowatt hours of electrical energy would
take up a small room and cost over $10,000. Through advances in nanotechnology, it may be possible to
shrink an equivalent unit to the size of a washing machine, and drop the cost to less than $1,0001.

Solar heating
Solar energy can also be used as a heating source to produce hot water, and heat home and offices.
Current systems are able to convert 25‐40% of solar radiation into heat. The principle of solar heating is
straightforward, a material absorbs sunlight energy and releases in the form of heat directly to a water
source or to a heat exchange element (heat pump). Any material that can enhance surface area or have
improved absorption properties would improve this technique. Numerous nanomaterials do so. Since
the Sun is a variable source that produces a diffuse energy, controlling the incident solar radiation is
difficult because of its changing position. Nanotechnologies can be used to fabricate complex nano‐
structured mirrors and lenses to optimize solar thermal collection. Also aerogels with nanopores are
used as transparent and thermally isolating material for the cover material of solar collectors.

Page 11 of 29



Hydrogen Society
Hydrogen (H2) can, in principle, be a future environmentally friendly energy carrier when it is produced
from renewable energy. The ideal scheme would be
producing hydrogen by splitting water molecules using
solar light (as shown in Figure 5). H2 could then be then
used as energy carrier to provide electricity in our
homes, fuel our cars etc.

Figure 5. The ideal combination of photovoltaic and
hydropower.

The idea of a fuel cell was first conceived in 1839 by Sir William Grove who thought that electricity could
be produced by reversing the process of electrolysis, in which hydrogen and oxygen are produced by
the electrolysis of water.

Hydrogen fuel cells use hydrogen and oxygen as fuel to generate electricity. The fuel molecules in the
cell must be ionized to react. The ionization must be catalyzed by the electrodes, and an electrolyte
must conduct the formed ionic species so that they can react (Figure 6). The sub‐product of this reaction
is only water‐no CO2 is produced during the conversion of H2 to electricity. The result of the
electrochemical process is a maximum of 1.2 V and 1 W cm‐2 of power.

The three fundamental elements of a hydrogen fuel cell are
therefore: the fuel (H2 and O2), the catalyst and the electrolyte.
Presently, there are problems associated with each of these
elements, making the fabrication and operation of H2 fuel cells
technically challenging and very expensive. However, the technology
is developed enough and the worldwide research so intense that
consumer goods powered by fuel cells are likely on a large scale.

Figure 6. Schematic representation of a hydrogen fuel cell. (Image source: L. Filipponi, iNANO, Aarhus
University, Creative Commons Attribution Share Alike 3.0).

Page 12 of 29



Hydrogen production
The first problem is associated with the nature of the fuel, hydrogen. Although hydrogen is abundant in
nature it is not freely available, it needs to be extracted from a source, such as hydrocarbons (e.g.,
methane), which produce CO2 upon extraction, or water. Extraction of hydrogen from water is better.
Ideally H2 should be extracted using a renewable energy source (solar, wind, geothermal etc.). One of
the most promising methods of hydrogen generation is its photochemical extraction from water using
sunlight. The idea is to use sunlight to spit water in hydrogen and oxygen. This is accomplished regularly
and for over 3.5 billion years by photosynthetic organisms, but to do so artificially, it is a challenge!

Nanotechnologies for improving photoinduced water splitting
In principle, visible light at wavelengths shorter then 500nm has enough energy to split water in
hydrogen and oxygen. However, water is transparent to this visible range and does not adsorb this
energy. Therefore, the combination of a light harvesting system with a water splitting system is
necessary to implement the use of sunlight to split water.

As simple as the concept might sound, several technical challenges must be overcome before this
technology can become commercially viable. Table 2 compares the cost of producing hydrogen from a
series of sources, and shows how to date only the extraction from fossil fuels is economically viable.
Therefore fundamental research is necessary to overcome the limitations of photochemical water
decomposition to produce H2.

Source US$/GJ In 1972 A Fujishima and K Honda demonstrated the
H2 from coal/oil/natural gas 1‐5 photoelectrolysis of water with a TiO2 photoanode using
H2 from natural gas minus 8‐10 platinum as a counter electrode. Although the reaction is
CO2 possible, before it can become a viable source of hydrogen
H2 from coal minus CO2 10‐13 (which means economic and efficient at the same time) two
H2 from biomass 12‐18
main problems need to be solved.
H2 from nuclear energy 15‐20
H2 from wind energy (via 15‐25
land) Table 2. Comparison of the cost of different types of H2 sources.
H2 from wind energy (via 20‐30 For a sustainable economy to exist,  the price must be lower then
sea) 5 US$/GJ (Adapted from T.R. Jensen, Hydrogen Fuel Cells, Aktuel
H2 from solar cells 25‐50 Naturvidenskab 2004, www.ird.dk with permission from author).

Page 13 of 29



The first is the limited light adsorption in the visible of wide‐band gap semiconductors (such as TiO2).

This problem was already mentioned in the PV section as it applies to both technologies. Basically
photovoltaics and photoinduced water splitting use the same concept of using sunlight to excite
electrons but differ in how the excited electron (e‐h pairs) are used: to drive a current (in PVs) or to
drive a chemical redox reaction (in photoinduced water splitting).

As discussed in the previous section nanotechnology is leading the way in solving some of the problems
associated with solar energy conversion with the introduction of nanostructured materials that have
high solar energy adsorption rates. Along this approach, the group under the direction of Dr. Misra from
the University of Nevada has developed titanium dioxide (TiO2) nanotube arrays having a modified
band gap for generating hydrogen by splitting water using sunlight.

The second problem in the photoinduced water splitting is the fast electron‐hole recombination, which
lowers the efficiency of the process. In simple terms, photocatalysis involves harvesting solar photons in
a semiconductor (the TiO2 surface) and subsequent conversion of these photons to electronic
excitations, which then induce the desired water‐splitting reaction. The excited electron hole pair,
though, have a high tendency of recombine. Nanostructures offer the opportunity to minimize the
distanced (and thus the times) over which charges have to survive and be transported after excitation.
Deposition of small noble metal islands (<5nm) or metal nanoparticles enhance the photocatalytic
activity of systems that use TiO2 as the photocatalytic surface. This effect is due to the charge separation
across the metal‐semiconductor interface. More recent nanotechnology approaches include the use of
carbon‐doped titania nanotubes arrays, SWCNTs and nanostructured hematite films.

Page 14 of 29



Hydrogen storage

Figure 7. Volume of 4 kg of hydrogen compacted in
different ways, with size relative to the size of a
car. (Image credit: Reprinted by permission from
Macmillan Publishers Ltd: Nature (L. Schlapbach,
A. Züttel, ‘Hydrogen‐storage materials for mobile
applications’, Nature (2001) 414: 353‐358),
Copyright © 2001.

The combustion of hydrogen is straightforward with no detrimental by products: H2 + ½ O2→ H2O.
However, a problem exists that relate to its storage and transport which need to be both efficient and
safe. The problem is easily seen by comparing the energy to volume ratio for gaseous hydrogen
(3.0MJ/L) to that of conventional gasoline (32.0MJ/L). This means that, given the same volume, the
energy produced by hydrogen is about ten times lower than that from conventional gasoline. This
obviously represents a problem for storing hydrogen in a vehicle, for example: a big, heavy tank would
be required to store and transport the required amount of hydrogen (Figure 7). Some possible solutions
are to use liquid hydrogen (8.5MJ/L), to use compressed hydrogen or to store hydrogen in solid metallic
support such as metal complexes (hydrides).

The use of compressed hydrogen implies using liquid tanks that need to be made of a very strong yet
lightweight material. This material should also have outstanding insulating and pressurization
properties, in order to avoid hydrogen leakage. This problem can potentially be solved using
nanotechnology to develop new materials with exceptional properties in terms of strength and density.

Page 15 of 29



Solid metallic nanostructured supports
Solid metallic supports are probably the most
H2‐inhold Pressure/
Temperature viable option for hydrogen storage8. In this
Mass‐ Volume‐ p(H2) in bar approach hydrogen is ‘loaded’ to a solid
energy energy (1) support and extracted from it when needed.
density density The main challenges here are the material
(weight %) (g/L) loading capacity and the regeneration kinetics
Pressur 4.6 25 300
to re‐extract the hydrogen from the support
e tank
ca. 6 58 700 The best material would achieve an optimum
Metal Temperature compromise between having hydrogen too
hydride in ºC (2) weakly bonded to the storage material, which
MgH2 7.6 110 350 means a low storage capacity, and a too
LaNi5H6 1.4 121 ca. 50 strongly bonded to the storage material, which
TiFeH2 1.9 107 ca.50 would require high temperatures to release

hydrogen. Nanotechnology can contribute in
Comple
x metal this field by developing new molecules that
hydride allow high hydrogen loading capacity and
s acceptable regeneration kinetics. Researchers
LiBH4 18.5 121 380 aim at developing nanomaterials that are light
NaBH4 10.7 114 400 in weight, low in volume, have high loading
LiAlH4 10.6 87 >125 capacities, good regeneration kinetics and are
NaAlH4 7.5 94 210
low in cost.
Mg2FeH6 5.5 150 320

Table 3. Comparison between various hydrogen storing systems. Notes to table: (1) Hydrogen pressure in a gas
tank (700 bar is the target); (2) Temperature for H2 release at p(H2)=1 bar, without catalyser. (Adapted from
T.R. Jensen, Hydrogen Fuel Cells, Aktuel Naturvidenskab 2004, www.ird.dk)

Two candidate materials are complex metal hydrides, which have an intermediate bonding of hydrogen,
and nanostructured carbon‐based materials, such as carbon nanotubes. The properties of some complex
metal hydrides as H2 storage materials, such as LiBH4, NaBH4 and NaAlH4, are summarized in Table 3. In
Figure 4 the schematic representation of sodiumalluminiumhydride (NaAlH4) is shown. The structure can
be imagined as a salt made of sodium ions (Na+, yellow) and a complex ion of aluminium (Al, orange)

Page 16 of 29



and hydrogen (blue), AlH4‐ (other example of complex ions are the ion sulphate SO42‐ and the ion
phosphate PO43‐).

Figure 9. A schematic representation of
sodiumalluminiumhydride (NaAlH4), a promising complex
hydride for hydrogen storage. Image from: T.R. Jensen,
Hydrogen Fuel Cells, Aktuel Naturvidenskab 2004,
www.ird.dk, Naturvidenskab 2004, www.ird.dk)

The hydrogen fuel cell
In order for hydrogen fuel cells to become an economically viable alternative to combustion chambers,
two other main problems need to be addressed: the nature of the catalyst and that of the electrolyte in
the cell.

Currently, the electrodes in a fuel cell are made of a metal such as platinum (Pt), which is a rare,
expensive metal, also sensitive to the CO and sulphur species that are dispersed in the atmosphere.
These de‐activate the Pt surface (a phenomenon called ‘poisoning of the catalyst’). Fuel cells operate at
high temperatures (>70 °C) since the poisoning agents at these temperatures tend to de‐adsorb.
Nanotechnology is already actively involved in addressing some of the issues concerning fuel cell
catalyst. Improvements in this area through nanotechnology deal with (1) increase of material catalytic
activity; and (2) reduction of rare metal usage. Since the current generated at an electrode is
proportional to the active surface of the catalyst, fuel cells that have higher power density can be
formed from nanomaterials which have a higher surface area to volume ratio. Electrocatalytic material
properties are also proportional to particle size, so nanoparticles and nanomaterials have increased
catalytic activity compared to bulk materials. This characteristic can lead to a reduction of rare metal
usage, for example by using carbon nanomaterials as support for the dispersions of nano‐sized Pt,
therefore reducing the weight of Pt needed to produce the same surface area of active Pt catalyst.
Carbon nanomaterials are particularly suitable since they act both as support for the Pt nanomaterial
and as conductor. Suitable carbon nanomaterials are carbon foams containing nanopores, different
types of nanotubes and single walled nanohorns.

Page 17 of 29



Proton exchange membrane fuel cell
The electrolyte conventionally used in fuel cells is aqueous KOH operating at about 70 °C (liquid alkaline
cell). It leads to corrosion of the electrodes, reducing the cell lifetime, and operates at high
temperatures, decreasing the thermodynamic efficiency of the cell. A solid electrolyte is preferred,
therefore modern hydrogen fuel cells use a proton‐permeable membrane made of a polymer (e.g.,
Nafion®), which has a high proton conductivity due to the presence of water molecules in its structure.
In a Proton Exchange Membrane Fuel Cell (PEMFC) the proton ions generated at the platinum anode
pass through the proton conducting membrane to the platinum cathode, where they combine with
oxygen and form water (Figure 10 illustrates the operational principle of a PEMFC).

Figure 9. Diagram of a Proton
exchange membrane fuel cell.
(Image source: Wiki Commons,
Public image)

Page 18 of 29



Proton Exchange Membrane Fuel cells (PEMFC) are the most likely fuel cells to succeed
commercialization for automotive purposes thanks to their low operating temperatures and their
inherent properties of being lightweight, producing high current densities and contain no corrosive
materials9.

An area where improvement is highly needed, though, is the nature of the solid membrane. Nafion®, for
instance, is expensive, subject to degradation through dehydration at operation temperatures above
100 ºC, and is not fabricated with nanoscale control; therefore it has pores not uniform in size and
distribution, so that the active sites on the membrane surface (directly involved in proton binding) are
randomly exposed. Other 3‐D solid electrolytes have been investigated, but they have the problem of
either having very low conductivity (reducing the efficiency of the cell) or requiring high temperatures to
operate.

In this context, nanotechnologies can aid in the development of nano‐structured solid membranes to
increase proton conductivity, cell efficiency and durability. These include ceramic electrolyte
membranes (e.g. metal‐oxane membranes) and nano‐structured solid electrolytes or fillers fabricated
with nanoscale control. In addition, fuel cell assembly, durability and cost could be in principle improved
employing nanotechnology by fabricating sturdier cells able to withstand the large changes in
temperature required in some applications, such as automotive operation.

Thermoelectricity
Thermoelectric materials (TE) are functional materials that have the double property of being able to
convert heat to electricity, and vice versa. Thermoelectricity can be generated in all conductive
materials. When a temperature gradient is applied across a wire, electrons diffuse from the hot to the
cold part due to the larger thermal speed of the electrons in the hot region. Consequently, a charge
difference builds up between the hot and cold region, creating a voltage and producing an electric
current. Alternatively, a current can be applied to the wire to carry heat away from a hot section to
cooler areas.

Thermoelectric materials can therefore be used for either cooling or power generation. Although
current devices have a low conversion efficiency of around 10 per cent, they are strongly advantageous
as compared to conventional energy technologies, since the converters have no moving parts and are
therefore both reliable and durable. Also, they are scalable and hence ideal for miniature power

Page 19 of 29



generation, and no pollutants are released to the environment. If significantly improved thermoelectric
materials can be developed, thermoelectric devices may replace the traditional cooling system in
refrigerators. They could also make power generators in cars obsolete by utilizing heat from the exhaust
gasses, or they may possibly be used to convert huge amounts of industrial waste heat into electricity.

Despite their enormous potential, thermoelectric materials have so far failed to fulfil their huge
promise, and are currently employed only in niche applications, most notably by NASA to generate
electricity for spacecraft that are too far away from the sun for solar cells to operate. The problem is
that for the process to be efficient, the thermoelectric materials need to be a good electrical conductor
but a poor thermal conductor, so the temperature difference inside the material remains. More
specifically, thermoelectric materials are ranked by their figure of merit, ZT, which is defined as
ZT=S2σT/k, where S is the thermopower (or Seebeck coefficient), σ is the electrical conductivity, k is the
thermal conductivity and T is the absolute temperature. To be competitive with conventional
refrigerators and generators, one must develop thermoelectric materials with ZT>3. Yet in five decades
of research, the room‐temperature ZT of bulk semiconductors has increased only marginally, from 0.6 to
about 1.0. The challenge lies in the fact that S, s and k are interdependent: changing one alters the
others, making optimization extremely difficult.

However, in the last years, there have been reports of dramatic increases in the properties of TE
materials13. In all these cases, the material has been found to be nanostructured. Researchers are
studying in details these nanomaterials to understand weather this is a result of quantum confinement
or photon dynamics and transport. What is clear is that to have optimum properties, the material needs
to have high symmetry at the nanoscale level, and needs to incorporate heavy elements because of their
low thermal conductivity.

Some examples of nanostructured TE materials are half‐heuster alloys (ZrNiSn), Zn4Sb3, skutterudines,
and novel PbTe‐materials (e.g., LAST‐18, SALT‐20 and LASTT).

Figure 11. Clathrate crystals produced at iNANO are among the target
materials for NASA’s high‐temperature thermoelectric converters for
future Mars missions. Heat for the converters will be provided by
radioactive sources. (Image courtesy of iNANO, Aarhus University).

Page 20 of 29



Rechargeable Batteries
Rechargeable batteries are energy storage devices used
to power small electronic equipments such as cell
phones and personal computers, where high power and
light weight are important. These same attributes are
required for electric vehicles, hybrid electric vehicles,
power tool and backup power subsystems.
Simplistically, a battery is an electrochemical device that
generates DC through a coupled set of reduction‐
oxidation (‘redox’) reactions. The positive electrode is
reduced (‘captures electrons’) and the negative
electrode is oxidized (‘releases electrons’). The battery
Figure 12. Schematic representation of a
consists of a positive electrode facing a negative
lithium‐ion battery.
electrode divided by a porous separator that prevents
the electrodes from touching, and an ionic electrolyte, which is a conduction medium that ensures
movement of the ions from one electrode to the other. Intercalation‐based batteries using the small
lithium (Li+) ion are the most used. These batteries have at least one redox‐active electrode with an
open crystal structure with ‘holes’ capable of intercalating Li+. For example, oxidation of Co in LiCoO2
expels Li+ which is taken up in a graphite electrode. When the battery is charged, the Li+ moves from
the positive electrode to the negative one via the electrolyte. On discharge, the opposite occurs,
releasing energy in the process. Ideally, the structure of the redox‐active crystal should be capable of
reversibly intercalating the small Li+ ion.

Nanotechnologies to impact energy capacity, battery power, charge rate and lifetime
Current problems with lithium rechargeable batteries involve a number of issues, the first being the
battery energy capacity: in order to allow ions and electrons to move quickly into and out of the active
material (allowing fast charging and discharging) the material must be deposited as a thin film. This
limits the amount of active material that can be incorporated into the battery (energy capacity). For
high‐capacity batteries, thickness is increased in order to have more energy storage with the drawback
of slower charging.

The second issue concerns the battery power: an important attribute of large format batteries is their
capability of delivery power quickly. Power is restricted by the ion removal capability in lithium‐batteries
Page 21 of 29



which depend on the electrochemical properties of the battery. There is then the problem of charge
rate: batteries need to be recharged, and recharging times are now in the order of hours. The time of
charge is restricted by the incorporation rate capabilities of Li+ inside the graphite electrode.

Lithium‐batteries lifetime also needs to be improved: in current batteries, every time Li+ enters/exits
the graphite electrode, the pores of the electrode need to expand or shrink. This repeated expansion
and shrinkage fatigues the graphite particles, which as a result break apart, reducing battery
performance.

Nanomaterials as alternatives to conventional electrodes
Nanocrystalline composite materials and nanotubes can be used to replace the conventional graphite or
Li‐graphite electrode. These can be fabricated to have voids having same size as the lithium ions they
have to accommodate. This allows packing much more active material into an electrode, increasing
energy capacity. A nanostructured electrode with voids having the same size as the lithium ions
increases the battery life and also ensures high charge rates. Nanotechnology will also allow in the
future moving away from flat layers of electrode materials to positive and negative electrodes that
interpenetrate. This 3D nano‐architecture could improve the mobility of ions and electrons, thereby
increasing battery power.

In this context it is interesting the work reported in December 2007 by Yi Cui and colleagues from
Stanford University about the use of silicon nanowires as anode material. Bulk silicon has been
investigated in the past as an alternative material to graphite since it has a low discharge potential and
the highest theoretical charge capacity (more then 10 times that of existing graphite anodes). However,
silicon bulk anodes (containing silicon films or large silicon particles) have shown short battery lifetime
and capacity fading due to pulverization and loss of electrical contact between the active material and
the current collector. These problems arise from the fact that the volume of silicon anodes changes
about 400% during battery cycling which is a result of the anode swelling (battery charging) and
shrinking (battery discharging) as lithium ions enter and exit the anode.

The group at Standford University replaced a conventional bulk silicon anode with one formed of silicon
nanowires (SiNW), grown directly on the metallic current collector. This way they were able to achieve
the theoretical charge capacity of silicon anodes (10 times that of current ion‐lithium batteries) and to
maintain a discharge capacity close to 75% of this maximum. The work was patented and the discovery
has great potential for commercial high‐performance lithium batteries.

Page 22 of 29



“Paper battery”
Recently an exciting work was reported by scientists at Rensselaer Polytechnic Institute which uses a
composite material that combines high energy capacity and flexibility. The researchers found that they
could combine nanotubes (which are highly conductive) with a layer of cellulose, the material used to
make paper15. This way they were able to obtain ‘paper batteries’ which can be rolled or folded just like
paper without any loss of efficiency. This opens the opportunity to have batteries moulded to assume a
particular form. Like all batteries, the paper version comprises electrodes, electrolyte, and a separator.
The first electrode is formed by vertically aligned multiwalled carbon nanotubes, deposited on Si
substrates. Plant cellulose is cast on top of the layer, solidified, and dried to form the porous separator.
The middle paper layer is then impregnated with an ionic liquid which acts as the electrolyte and that
can be an organic salt that is liquid at room temperature. The ionic liquid contains no water, so there is
nothing in the batteries to freeze or evaporate. This increases the working temperature range of the
battery, which can withstand extreme temperatures from 195 K to 450 K. To make a battery, the second
electrode is formed by coating the paper side with lithium oxide. Interestingly the same material can be
used to make a supercapacitor simply by folding the paper in half, so that there is a carbon electrode at
both top and bottom. The team could also fabricate dual‐storage devices containing three electrodes
that act as both supercapacitors and batteries.

Battery operation range, lifetime and safety
Li‐batteries are now limited in their operation temperature range. Below 0 °C and above 50 °C the
batteries cannot be recharged, and above 130 °C they become unsafe due to thermal runaway. Thermal
runaway, which is due to reaction of the graphite with the electrolyte, can also occur due to battery
impurities. Finally, Li‐batteries are made of toxic metals and therefore are harmful for the environment.

The battery safety can be increased if the graphite electrode in a lithium‐battery is replaced with a
nanostructured material inert towards the electrolyte. Nanotechnology can also be employed to use
alternative active materials which are less expensive and non‐toxic to the environment. For example,
the non‐toxic magnetite (Fe3O4) has been employed as active material in a high‐capacity Cu nano‐
architectured electrode (Figure 13). Nanostructured lithium batteries are becoming a commercial
reality, such as the Altairano NanoSafe™ and 123 Systems Batteries.

Page 23 of 29



Figure 13. Cross‐sectional views of Cu‐nanostructured
current collector before (left) and after (right) Fe3O4
deposits. (Image credit: Reprinted by permission from
Macmillan Publishers Ltd: P. L. Taberna et al., ‘High
rate capabilities Fe3O4‐based Cu nano‐architectured
electrodes for lithium‐ion battery applications’ Nature
Materials (2006) 5:567‐573), copyright © 2006.

Supercapacitors
Supercapacitors are another way of storing electricity that can benefit from nanotechnology. They are
needed in those devices that require rapid storage and release of energy, for instance hybrid‐electric
and fuel‐cell powered vehicles. They are constructed by two electrodes immersed in an electrolyte, with
an ion permeable separator between them. Each electrode‐electrolyte interface represents a capacitor,
so the complete cell can be considered as two capacitors in series. The focus in the development of
these devices has been on achieving high surface‐area with low matrix resistivity. The most remarkable
property of a supercapacitor is its high power density, about 10 times that of secondary battery. The
maximum power density of a supercapacitor is proportional to the reciprocal of its internal resistance. A
number of sources contribute to the internal resistance and are collectively referred to as Equivalent
Series Resistance (ESR). Contributors to the ESR include the electronic resistance of the electrode
material and the interfacial resistance between the electrode and the current‐collector. Carbon, in its
various forms, is currently the most extensively used electrode material in supercapacitors. A typical
commercial supercapacitor can produce a power density of about 4 kW/kg. Nanotubes can be used to
increase the power density of supercapacitors, since the nanoscale tubular morphology of these
materials offers a unique combination of low electrical resistivity and high porosity in a readily
accessible structure. Single‐walled (SWNTs) and multi‐walled (MWNTs) nanotubes are under
investigation. Research has shown that the use of thin film electrodes with multi walled aligned
nanotubes increases the specific power density (laboratory results of 30 kW/Kg have been reported19),
thanks to reduction of ESR.

Page 24 of 29



Energy Saving
Energy saving can be achieved in numerous ways, such as improving insulation of residential homes and
offices; use more efficient lighting; and using lighter and stronger materials to built devices, which then
would require less energy to operate. Also, a large portion of energy is lost during its transport, so there
is a need for a more efficient electric grid to transport energy. Nanotechnologies can potentially be
applied to all of these energy saving materials and technologies.

Catalysis
Catalysis is of vital importance in our society and constitutes a cornerstone of life from biological
processes to large‐scale production of bulk chemicals. The availability of plentiful and inexpensive
chemicals relies on industrial catalytic processes and without them it would be impossible to maintain
the current living standard of the present human population. Other technologies also depend on
catalysis, including production of pharmaceuticals, means of environmental protection, and production
and distribution of sustainable energy. As already discussed in some of the previous sections, many
technological advanced required to render alternative energy carriers to fossil fuels an economically
viable option ‐such as sun light and hydrogen‐ rely on optimizing a catalytic process.

For instance, for water to be split into hydrogen and oxygen with sunlight to feed a fuel cell, researchers
need to improve the activity of the catalyst, for instance TiO2.

A typical heterogeneous catalyst consists of few nanometre wide catalytically active nanoparticles
dispersed on a highly porous support material which can have surface areas up to 250 m2 per gram. The
manufacturing of structures on the nanometre scale has been a central issue in catalysis research and
development for decades. This fact relates to the structure of a heterogeneous catalyst, which requires
control of materials ranging from macroscopic dimensions down to the nanoscale. Heterogeneous
catalysis therefore has in a sense always had a nanoscience component. Since catalytic action takes
place at a surface, and catalytic materials are often very expensive (as they use rare materials such as
Pt), the goal for chemists has always been to fabricate catalysts with as high surface‐to‐volume ratio as
possible, so to maximize the surface exposed to the reaction and minimize the amount of catalyst
required.

Page 25 of 29



Advanced materials
Nanotechnology can offer some indirect energy saving solutions by developing materials with better
properties. One example is materials with improved strength which make constructions leaner and thus
lighter, with an indirect energy saving, for instance in the transport sector (both on the road an in the
air). Since a large fraction of the fuel consumption in a car is weight‐related, making cars with lighter
materials would be a very efficient way of saving energy. Higher tensile strength can be exploited also as
higher possible loads, so that with the same amount of material, stronger components can be built. For
instance windmills could be able of sustain higher wind speeds if they were made of high‐strength
nanomaterials. Better creep resistance is an advantage in virtually any system for thermal power
generation due to the higher operating temperature which is allowed and the concurrent higher
efficiency. Nano‐coatings with improved corrosion properties have a longer service life in aggressive
environments and thus have potential for energy saving throughout their entire life‐cycle (e.g.,
extraction, production, machining, disposal and recycling).

Insulators and ‘smart’ coatings
Insulation is a very effective way of minimizing energy consumption, for instance in households and
offices. Nanotechnology offers the possibility of developing new materials with improved insulating
properties. One example is nanoporous aerogels to improve thermal insulation. A commercial example
is represented by Aspen Aerogels products. This company produces flexible aerogel nanoporous
insulation blankets (e.g., Cryogel™) designed for cryogenic applications (for instance, for insulating pipes
and tanker ships)25. These insulation blankets can be cut as normal textiles, installed faster than
traditional materials, and their low thermal conductivity allows for less material usage. Additionally, the
Aspen’s product are resistant to compression and inherently hydrophobic so they can be exposed to
water for long periods without damaging the product outstanding thermal properties. Nanotechnology
applied to indirect energy saving can be found in the form of ‘smart’ materials such as electrochromic
and photochromic coatings used for darkening window. They reduce indoor heating in summer, so less
air‐conditioning is required to keep the ambient cool, with consequent energy saving. Another example
of nanotechnology applied to smart coatings is the use of a family of wavelength‐selective films that is
used for manufacturing ‘heat mirrors’.

One of these materials is indium‐tin‐oxide (ITO), an infrared absorber. A 0.3 nm ITO coating on glass
provides more then 80% transmission for the wavelengths predominant in sunlight. The transmission
properties of the window can be varied by changing the thickness and material composition of the

Page 26 of 29



coating, so that a combination of materials could be used to produce smart windows that reflect solar
energy in summer but transmit solar energy in winter.

Energyharvesting materials
Numerous innovative electronic devices under development have nano‐scale components (see Chapter
4‐ NT and ICT).  Nanodevices don't use much energy, and if the little they do could be scavenged from
vibrations associated with foot steps, heart beats, noises and air flow, a whole range of applications in
personal electronics, sensing and defence technologies opens up. In order to be able to do so, an
“energy‐scavenger” having nano‐scale dimension need to be included in the device. Also, energy
gathering of this type requires a technology that works at low frequency range (below 10 Hz), ideally
based on soft, flexible materials. A group working at Georgia Institute of Technology has now come up
with a system that converts low‐frequency vibration/friction energy into electricity using piezoelectric
zinc oxide nanowires grown radially around textile fibres. A piezoelectric material makes uses of
piezoelectricity, which was discovered in 1883 by Pierre Curie and his brother Jacques. They showed
that electricity was produced when pressure was applied to selected crystallographic orientations.
Piezoelectricity is thus the induction of electrical polarization in
certain types of crystals due to mechanical stress. ZnO nanowires are
such type of piezoelectric nanomaterial. In the work mentioned
above, researchers have grown ZnO nanowires radially around a fibre
of Kevlar, which is a material known for its strength and stability. By
entangling two fibres and brushing their associated nanowires
together, and moving them by sliding them back and forth, a relative
“brushing motion” is created, which in turn produces an output
current.

Figure 14. Kevlar fibres coated with ZnO nanowires. (a) An SEM image of a Kevlar fibre covered with ZnO
nanowire arrays along the radial direction. (b) Higher magnification SEM image and a cross‐section image
(inset) of the fibre, showing the distribution of nanowires. (c) Diagram showing the cross sectional structure of
the TEOS‐enhanced fibre, designed for improved mechanical performance. (d) SEM image of a looped fibre,
showing the flexibility and strong binding of the nanowire layer. (e) Enlarged section of the looped fibre,
showing the distribution of the ZnO nanowires at the bending area. Reprinted by permission from Macmillan
Publishers Ltd.: Qin et al. “Microfibre‐nanowire hybrid structure for energy scavenging” (2008), 451, pp809‐
813, copyright ©2008.

Page 27 of 29



A mechanical energy (sliding motion) is converted into electricity via a coupled piezoelectric‐
semiconductor process. This work shows a potential method for creating fabrics which scavenge energy
from light winds and body movement. In the future these type of nano‐energy scavengers could be
incorporated in textiles to power personal electronics.

Efficient lighting
Another important application of nanotechnology in the area of energy saving is the production of more
efficient lighting devices. Conventional incandescent lights are not energy efficient, a large portion of
their energy being dispersed in heating. Solid state light devices in the form of light emitting diodes
(LEDs) are attracting serious attention now as low‐energy alternatives to conventional lamps. The need
is to engineer white‐light LEDs as a more efficient replacement for conventional lighting sources. One
proposed solution is to use a mixture of semiconductor nanocrystals as the intrinsic emitting layer for a
LED device. Simply mixing several colours of nanocrystals together to achieve white light is a possibility,
but this would result in an overall reduction of device efficiency through self‐adsorption between the
various sizes of the nanocrystal. An important result that can potentially resolves this problem came
recently from the work of some researchers from the Vanderbilt University. They found that crystals of
cadmium and selenium of certain size (called ‘magic sized’ CdSe) emit white light when excited by a UV
laser, a property that is the direct result of the extreme surface‐to‐volume ratio of the crystal. This
material could therefore be ideal for solid state lighting applications.

Organic light emitting diodes (OLEDs) represent a promising solution for lighting applications as well as
for low cost, full‐colour flat panel displays Quantum dots (QD) are another class of nanomaterials that
are under investigation for making more efficient displays and light sources (QD‐LEDs).. The structure
and properties of OLEDS and of QD‐LEDs is described in details in Chapter 4 of Module 2 “Applications
of Nanotechnologies: ICT”.

Efficient energy transport
One area where there is a large margin for improvement is in the transport of electric current. As the
worlds` power demand increases, the burden on the electricity infrastructure grows. This has been
recently shown in some nation‐wide blackouts like the one occurred in the US North‐east in 2003, or the
one occurred in Italy the same year. Therefore, a major challenge is to develop new transmission line
materials that are lighter and have less energy loss then copper. Single carbon nanotubes (CNT) have the
remarkable property of weighting one‐sixth of copper but have similar or even better conductivity then

Page 28 of 29



copper and negligible eddy current loss. Therefore this material has the potential to overcome some of
the limitations of current transmission materials. Before this can become a reality, though, some major
advancement in their production is needed. At present, scientists produce CNTs often less then 100 nm
in length and with widely varying electrical conduction properties. The challenge for the future is
therefore to produce nanotubes with controlled properties. Also, the manufacturing must be cost‐
effective and able to produce ropes of fibres with desired electrical properties. At present, thus, this
application is still a vision.

Page 29 of 29


Application of nanotechnologies: energy

More Related Content

What's hot (18)

Similar to Application of nanotechnologies: energy (20)