![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
A
10B
= (0.35 nm)-9
Furthermore, from the above equation the A is equal to
A = 10B(0.35 nm)-9
When the above two expressions for A/10B and A are substituted into the above expression for E0
(- 6.13 eV), the
following results
−6.13 eV = = −
A
A
10B
−1/ 9
+
B
A
10B
−10/ 9
= −
10B(0.35 nm)-9
(0.35 nm)-9
[ ]
−1/ 9
+
B
(0.35 nm)-9
[ ]
−10/ 9
= −
10B(0.35 nm)-9
0.35 nm
+
B
(0.35 nm)10
Or
−6.13 eV = = −
10B
(0.35 nm)10
+
B
(0.35 nm)10
= −
9B
(0.35 nm)10
Solving for B from this equation yields
B = 1.88 × 10-5 eV- nm10
Furthermore, the value of A is determined from one of the previous equations, as follows:
A = 10B(0.35 nm)-9 = (10)(1.88 × 10-5 eV- nm10)(0.35 nm)-9
= 2.39 eV- nm
Thus, Equations 2.8 and 2.9 become](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-18-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Density Computations
3.7 Iron has a BCC crystal structure, an atomic radius of 0.124 nm, and an atomic weight of 55.85 g/mol.
Compute and compare its theoretical density with the experimental value found inside the front cover.
Solution
This problem calls for a computation of the density of iron. According to Equation 3.5
ρ =
nAFe
VCNA
For BCC, n = 2 atoms/unit cell, and
VC =
4 R
3
3
Thus,
ρ =
nAFe
4 R
3
3
NA
=
(2 atoms/unit cell)(55.85 g/mol)
(4)(0.124 × 10-7 cm)/ 3[ ]
3
/(unit cell)(6.022 × 1023 atoms/mol)
= 7.90 g/cm3
The value given inside the front cover is 7.87 g/cm3.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-36-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.12 Using atomic weight, crystal structure, and atomic radius data tabulated inside the front cover,
compute the theoretical densities of lead, chromium, copper, and cobalt, and then compare these values with the
measured densities listed in this same table. The c/a ratio for cobalt is 1.623.
Solution
Since Pb has an FCC crystal structure, n = 4, and VC
= 16R3 2 (Equation 3.4). Also, R = 0.175 nm (1.75
× 10-8
cm) and APb
= 207.2 g/mol. Employment of Equation 3.5 yields
ρ =
nAPb
VC NA
=
(4 atoms/unit cell)(207.2 g/mol)
(16)(1.75 × 10-8 cm)3( 2)[ ]/(unit cell){ }(6.022 × 1023 atoms/mol)
= 11.35 g/cm3
The value given in the table inside the front cover is 11.35 g/cm3.
Chromium has a BCC crystal structure for which n = 2 and VC
= a3 =
4 R
3
3
(Equation 3.3); also ACr =
52.00g/mol and R = 0.125 nm. Therefore, employment of Equation 3.5 leads to
ρ =
(2 atoms/unit cell)(52.00 g/mol)
(4)(1.25 × 10-8 cm)
3
3
/(unit cell)
(6.022 × 1023 atoms/mol)
= 7.18 g/cm3
The value given in the table is 7.19 g/cm3.
Copper also has an FCC crystal structure and therefore
ρ =
(4 atoms/unit cell)(63.55 g/mol)
(2)(1.28 × 10-8 cm)( 2)[ ]
3
/(unit cell)
(6.022 × 1023 atoms/mol)
= 8.90 g/cm3](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-42-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.13 Rhodium has an atomic radius of 0.1345 nm and a density of 12.41 g/cm3
. Determine whether it has
an FCC or BCC crystal structure.
Solution
In order to determine whether Rh has an FCC or a BCC crystal structure, we need to compute its density
for each of the crystal structures. For FCC, n = 4, and a = 2R 2 (Equation 3.1). Also, from Figure 2.6, its atomic
weight is 102.91 g/mol. Thus, for FCC (employing Equation 3.5)
ρ =
nARh
a3NA
=
nARh
(2R 2)3NA
=
(4 atoms/unit cell)(102.91 g/mol)
(2)(1.345 × 10-8 cm)( 2)[ ]
3
/(unit cell)
(6.022 × 1023 atoms /mol)
= 12.41 g/cm3
which is the value provided in the problem statement. Therefore, Rh has the FCC crystal structure.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-44-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.14 Below are listed the atomic weight, density, and atomic radius for three hypothetical alloys. For
each determine whether its crystal structure is FCC, BCC, or simple cubic and then justify your determination. A
simple cubic unit cell is shown in Figure 3.24.
Alloy Atomic Weight Density Atomic Radius
(g/mol) (g/cm3
) (nm)
A 77.4 8.22 0.125
B 107.6 13.42 0.133
C 127.3 9.23 0.142
Solution
For each of these three alloys we need, by trial and error, to calculate the density using Equation 3.5, and
compare it to the value cited in the problem. For SC, BCC, and FCC crystal structures, the respective values of n
are 1, 2, and 4, whereas the expressions for a (since VC = a3) are 2R, 2 R 2 , and
4R
3
.
For alloy A, let us calculate ρ assuming a simple cubic crystal structure.
ρ =
nAA
VC NA
=
nAA
2R( )3
NA
=
(1 atom/unit cell)(77.4 g/mol)
(2)(1.25 × 10−8)[ ]
3
/(unit cell)
(6.022 × 1023 atoms/mol)
= 8.22 g/cm3
Therefore, its crystal structure is simple cubic.
For alloy B, let us calculate ρ assuming an FCC crystal structure.
ρ =
nAB
(2R 2)3 NA](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-45-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
=
(4 atoms/unit cell)(107.6 g/mol)
2 2( )(1.33 × 10-8 cm)[ ]
3
/(unit cell)
(6.022 × 1023 atoms/mol)
= 13.42 g/cm3
Therefore, its crystal structure is FCC.
For alloy C, let us calculate ρ assuming a simple cubic crystal structure.
=
nAC
2R( )3
NA
=
(1 atom/unit cell)(127.3 g/mol)
(2)(1.42 × 10-8 cm)[ ]
3
/(unit cell)
(6.022 × 1023 atoms/mol)
= 9.23 g/cm3
Therefore, its crystal structure is simple cubic.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-46-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.16 Iodine has an orthorhombic unit cell for which the a, b, and c lattice parameters are 0.479, 0.725,
and 0.978 nm, respectively.
(a) If the atomic packing factor and atomic radius are 0.547 and 0.177 nm, respectively, determine the
number of atoms in each unit cell.
(b) The atomic weight of iodine is 126.91 g/mol; compute its theoretical density.
Solution
(a) For indium, and from the definition of the APF
APF =
VS
VC
=
n
4
3
π R3
abc
we may solve for the number of atoms per unit cell, n, as
n =
(APF) abc
4
3
π R3
Incorporating values of the above parameters provided in the problem state leads to
=
(0.547)(4.79 × 10-8 cm)(7.25 × 10-8 cm)(9.78 × 10-8 cm)
4
3
π (1.77 × 10-8 cm)3
= 8.0 atoms/unit cell
(b) In order to compute the density, we just employ Equation 3.5 as
ρ =
nAI
abc NA
=
(8 atoms/unit cell)(126.91 g/mol)
(4.79 × 10-8 cm)(7.25 × 10-8 cm)(9.78 × 10-8 cm)[ ]/unit cell{ }(6.022 × 1023 atoms/mol)
= 4.96 g/cm3](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-48-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3. 17 Titanium has an HCP unit cell for which the ratio of the lattice parameters c/a is 1.58. If the radius
of the Ti atom is 0.1445 nm, (a) determine the unit cell volume, and (b) calculate the density of Ti and compare it
with the literature value.
Solution
(a) We are asked to calculate the unit cell volume for Ti. For HCP, from Equation 3.S1 (found in the
solution to Problem 3.6)
VC = 6 R2c 3
But for Ti, c = 1.58a, and a = 2R, or c = 3.16R, and
VC = (6)(3.16) R3 3
= (6) (3.16)( 3) 1.445 × 10-8 cm[ ]
3
= 9.91 × 10−23 cm3/unit cell
(b) The theoretical density of Ti is determined, using Equation 3.5, as follows:
ρ =
nATi
VC NA
For HCP, n = 6 atoms/unit cell, and for Ti, ATi = 47.87 g/mol (as noted inside the front cover). Thus,
ρ =
(6 atoms/unit cell)(47.87 g/mol)
(9.91 × 10-23 cm3/unit cell)(6.022 × 1023 atoms/mol)
= 4.81 g/cm3
The value given in the literature is 4.51 g/cm3.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-49-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.26 Using the Molecule Definition Utility found in both “Metallic Crystal Structures and
Crystallography” and “Ceramic Crystal Structures” modules of VMSE, located on the book’s web site
[www.wiley.com/college/Callister (Student Companion Site)], generate a three-dimensional unit cell for the
intermetallic compound AuCu3 given the following: (1) the unit cell is cubic with an edge length of 0.374 nm, (2)
gold atoms are situated at all cube corners, and (3) copper atoms are positioned at the centers of all unit cell faces.
Solution
First of all, open the “Molecular Definition Utility”; it may be found in either of “Metallic Crystal
Structures and Crystallography” or “Ceramic Crystal Structures” modules.
In the “Step 1” window, it is necessary to define the atom types, colors for the spheres (atoms), and specify
atom sizes. Let us enter “Au” as the name for the gold atoms (since “Au” the symbol for gold), and “Cu” as the
name for the copper atoms. Next it is necessary to choose a color for each atom type from the selections that appear
in the pull-down menu—for example, “Yellow” for Au and “Red” for Cu. In the “Atom Size” window, it is
necessary to enter an atom/ion size. In the instructions for this step, it is suggested that the atom/ion diameter in
nanometers be used. From the table found inside the front cover of the textbook, the atomic radii for gold and
copper are 0.144 nm and 0.128 nm, respectively, and, therefore, their ionic diameters are twice these values (i.e.,
0.288 nm and 0.256 nm); therefore, we enter the values “0.288” and “0.256” for the two atom types. Now click on
the “Register” button, followed by clicking on the “Go to Step 2” button.
In the “Step 2” window we specify positions for all of the atoms within the unit cell; their point
coordinates are specified in the problem statement. Let’s begin with gold. Click on the yellow sphere that is
located to the right of the “Molecule Definition Utility” box. Again, Au atoms are situated at all eight corners of the
cubic unit cell. One Au will be positioned at the origin of the coordinate system—i.e., its point coordinates are 000,
and, therefore, we enter a “0” (zero) in each of the “x”, “y”, and “z” atom position boxes. Next we click on the
“Register Atom Position” button. Now we enter the coordinates of another gold atom; let us arbitrarily select the
one that resides at the corner of the unit cell that is one unit-cell length along the x-axis (i.e., at the 100 point
coordinate). Inasmuch as it is located a distance of a units along the x-axis the value of “0.374” is entered in the “x”
atom position box (since this is the value of a given in the problem statement); zeros are entered in each of the “y”
and “z” position boxes. We repeat this procedure for the remaining six Au atoms.
After this step has been completed, it is necessary to specify positions for the copper atoms, which are
located at all six face-centered sites. To begin, we click on the red sphere that is located next to the “Molecule
Definition Utility” box. The point coordinates for some of the Cu atoms are fractional ones; in these instances, the a
unit cell length (i.e., 0.374) is multiplied by the fraction. For example, one Cu atom is located 1
1
2
1
2
coordinate.
Therefore, the x, y, and z atoms positions are (1)(0.374) = 0.374,
1
2
(0.374) = 0.187, and
1
2
(0.374) = 0.187,
respectively.
For the gold atoms, the x, y, and z atom position entries for all 8 sets of point coordinates are as follows:](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-58-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
[Note: Unfortunately, with this version of the Molecular Definition Utility, it is not possible to save either the data
or the image that you have generated. You may use screen capture (or screen shot) software to record and store
your image.]](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-60-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Crystallographic Directions
3.27 Draw an orthorhombic unit cell, and within that cell a [121 ] direction.
Solution
This problem calls for us to draw a [121 ] direction within an orthorhombic unit cell (a ≠ b ≠ c, α = β = γ =
90°). Such a unit cell with its origin positioned at point O is shown below. We first move along the +x-axis a units
(from point O to point A), then parallel to the +y-axis 2b units (from point A to point B). Finally, we proceed
parallel to the z-axis -c units (from point B to point C). The [121 ] direction is the vector from the origin (point O)
to point C as shown.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-61-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.28 Sketch a monoclinic unit cell, and within that cell a [011] direction.
Solution
This problem asks that a [011] direction be drawn within a monoclinic unit cell (a ≠ b ≠ c, and α = β =
90º ≠ γ). One such unit cell with its origin at point O is sketched below. For this direction, there is no projection
along the x-axis since the first index is zero; thus, the direction lies in the y-z plane. We next move from the origin
along the minus y-axis b units (from point O to point R). Since the final index is a one, move from point R parallel
to the z-axis, c units (to point P). Thus, the [011] direction corresponds to the vector passing from the origin (point
O) to point P, as indicated in the figure.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-62-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.29 What are the indices for the directions indicated by the two vectors in the sketch below?
Solution
For direction 1, the projection on the x-axis is zero (since it lies in the y-z plane), while projections on the
y- and z-axes, b/2 and c, respectively. This is a [012] direction as indicated in the summary below.
x y z
Projections 0a b/2 c
Projections in terms of a, b, and c 0 1/2 1
Reduction to integers 0 1 2
Enclosure [012]
Direction 2 is [112] as summarized below.
x y z
Projections a/2 b/2 -c
Projections in terms of a, b, and c 1/2 1/2 -1
Reduction to integers 1 1 -2
Enclosure [112]](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-63-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.30 Within a cubic unit cell, sketch the following directions:
(a) [110], (e) [111],
(b) [121], (f) [122],
(c) [012], (g) [123],
(d) [133], (h) [103].
Solution
The directions asked for are indicated in the cubic unit cells shown below.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-64-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.31 Determine the indices for the directions shown in the following cubic unit cell:
Solution
Direction A is a [01 1]direction, which determination is summarized as follows. We first of all position
the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system
x y z
Projections 0a –b –c
Projections in terms of a, b, and c 0 –1 –1
Reduction to integers not necessary
Enclosure [01 1]
Direction B is a [210] direction, which determination is summarized as follows. We first of all position
the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system
x y z
Projections –a
b
2
0c
Projections in terms of a, b, and c –1
1
2
0
Reduction to integers –2 1 0
Enclosure [210]
Direction C is a [112] direction, which determination is summarized as follows. We first of all position the
origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-65-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
x y z
Projections
a
2
b
2
c
Projections in terms of a, b, and c
1
2
1
2
1
Reduction to integers 1 1 2
Enclosure [112]
Direction D is a [112] direction, which determination is summarized as follows. We first of all position
the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system
x y z
Projections
a
2
b
2
–c
Projections in terms of a, b, and c
1
2
1
2
–1
Reduction to integers 1 1 –2
Enclosure [112]](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-66-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.32 Determine the indices for the directions shown in the following cubic unit cell:
Solution
Direction A is a [430] direction, which determination is summarized as follows. We first of all position
the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system
x y z
Projections –
2a
3
b
2
0c
Projections in terms of a, b, and c –
2
3
1
2
0
Reduction to integers –4 3 0
Enclosure [430]
Direction B is a [232] direction, which determination is summarized as follows. We first of all position
the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system
x y z
Projections
2a
3
–b
2c
3
Projections in terms of a, b, and c
2
3
–1
2
3
Reduction to integers 2 –3 2
Enclosure [232]
Direction C is a [133] direction, which determination is summarized as follows. We first of all position
the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-67-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
x y z
Projections
a
3
–b –c
Projections in terms of a, b, and c
1
3
–1 –1
Reduction to integers 1 –3 –3
Enclosure [133]
Direction D is a [136] direction, which determination is summarized as follows. We first of all position
the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system
x y z
Projections
a
6
b
2
–c
Projections in terms of a, b, and c
1
6
1
2
–1
Reduction to integers 1 3 –6
Enclosure [136]](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-68-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.33 For tetragonal crystals, cite the indices of directions that are equivalent to each of the following
directions:
(a) [001]
(b) [110]
(c) [010]
Solution
For tetragonal crystals a = b ≠ c and α = β = γ = 90°; therefore, projections along the x and y axes are
equivalent, which are not equivalent to projections along the z axis.
(a) Therefore, for the [001] direction, there is only one equivalent direction: [001].
(b) For the [110] direction, equivalent directions are as follows: [1 10], [110], and [110]
(b) Also, for the [010] direction, equivalent directions are the following: [010], [100], and [100].](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-69-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.34 Convert the [100] and [111] directions into the four-index Miller–Bravais scheme for hexagonal unit
cells.
Solution
For [100]
u' = 1,
v' = 0,
w' = 0
From Equations 3.6
u =
1
3
(2u' − v' ) =
1
3
[(2)(1) − 0] =
2
3
v =
1
3
(2vÕ− uÕ) =
1
3
[(2)(0) − 1] = −
1
3
t = − (u + v) = −
2
3
−
1
3
= −
1
3
w = w' = 0
It is necessary to multiply these numbers by 3 in order to reduce them to the lowest set of integers. Thus, the
direction is represented as [uvtw] = [21 10].
For [111], u' = 1, v' = 1, and w' = 1; therefore,
u =
1
3
[(2)(1) − 1] =
1
3
v =
1
3
[(2)(1) − 1] =
1
3
t = −
1
3
+
1
3
= −
2
3
w = 1](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-70-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
If we again multiply these numbers by 3, then u = 1, v = 1, t = -2, and w = 3. Thus, the direction is represented as
Thus, the direction is represented as [uvtw] = [1123].](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-71-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.35 Determine indices for the directions shown in the following hexagonal unit cells:
Solution
(a) For this direction, projections on the a1, a2, and z axes are a, a/2, and c/2, or, in terms of a and c the
projections are 1, 1/2, and 1/2, which when multiplied by the factor 2 become the smallest set of integers: 2, 1, and
1. This means that
u’ = 2
v’ = 1
w’ = 1
Now, from Equations 3.6, the u, v, t, and w indices become
u =
1
3
(2u' − v' ) =
1
3
(2)(2) − (1)[ ] =
3
3
= 1
v =
1
3
(2vÕ− uÕ) =
1
3
(2)(1) − (2)[ ] = 0
t = − (u + v) = − 1 + 0( ) = −1
w = w’ = 1
No reduction is necessary inasmuch as all of these indices are integers; therefore, this direction in the four-index
scheme is [1011]](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-72-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
(b) For this direction, projections on the a1, a2, and z axes are a/2, a, and 0c, or, in terms of a and c the
projections are 1/2, 1, and 0, which when multiplied by the factor 2 become the smallest set of integers: 1, 2, and 0
This means that
u’ = 1
v’ = 2
w’ = 0
Now, from Equations 3.6, the u, v, t, and w indices become
u =
1
3
(2u' − v) =
1
3
(2)(1) − 2[ ] = 0
v =
1
3
(2v' − u' ) =
1
3
(2)(2) − 1[ ] = 1
t = − (u+ v) = − 0 + 1( ) = −1
w = w' = 0
No reduction is necessary inasmuch as all of these indices are integers; therefore, this direction in the four-index
scheme is [0110].](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-73-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
(c) For this direction projections on the a1, a2, and z axes are −a, −a, and c/2, or, in terms of a and c the
projections are −1, −1, and 1/2, which when multiplied by the factor 2 become the smallest set of integers: −2, −2,
and 1. This means that
u’ = −2
v’ = −2
w’ = 1
Now, from Equations 3.6, the u, v, t, and w indices become
u =
1
3
(2u' − v) =
1
3
(2)(−2) − (−2)[ ] =−
2
3
v =
1
3
(2v' − u' ) =
1
3
(2)(−2) − (−2)[ ] = −
2
3
t = − (u+ v) = − −
2
3
−
2
3
=
4
3
w = w' = 1
Now, in order to get the lowest set of integers, it is necessary to multiply all indices by the factor 3, with the result
that this direction is a [2243] direction.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-74-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
(d) For this direction, projections on the a1, a2, and z axes are 0a, −a, and 0c, or, in terms of a and c the
projections are 0, -1, and 0. This means that
u’ = 0
v’ = −1
w’ = 0
Now, from Equations 3.6, the u, v, t, and w indices become
u =
1
3
(2u' − v' ) =
1
3
(2)(0) − (−1)[ ] =
1
3
v =
1
3
(2v'− u' ) =
1
3
(2)(−1) − 0[ ] =−
2
3
t = − (u+ v) = −
1
3
−
2
3
=
1
3
w = wÕ= 0
Now, in order to get the lowest set of integers, it is necessary to multiply all indices by the factor 3, with the result
that this is a [1210] direction.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-75-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.36 Sketch the [1123] and [1010] directions in a hexagonal unit cell.
Solution
The first portion of this problem asks that we plot the [1 123] within a hexagonal unit cell. Below is
shown this direction plotted within a hexagonal unit cell having a reduced-scale coordinate scheme.
For this direction, projections on the a1, a2, a3, and c axes are respectively, −1, −1, 2, and 3, respectively. In
plotting this direction, we begin at the origin of the coordinate system, point o. From here we proceed 1 unit
distance along the −a1 axis (to point p), from here 1 unit distance parallel to −a2 axis (to point q), then 2 unit
distances parallel (or along) the a3 axis (to point r), and finally, 3 unit distances parallel to the z axis (to point s).
Thus, the [1 123] direction is that vector that extends from point o to point s as shown.
Now we are asked to plot the [1010] within a hexagonal unit cell. In the figure below is plotted this
direction within a hexagonal unit cell having a reduced-scale coordinate scheme.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-76-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
For this direction, projections on the a1, a2, a3, and c axes are respectively, 1, 0, −1, and 0, respectively. In plotting
this direction, we begin at the origin of the coordinate system, point o. From here we proceed 1 unit distance along
the a1 axis (to point p). Since there is no projection on the a2 axis it is not necessary to move parallel to this axis.
Therefore, from point p we proceed 1 unit distance parallel to −a3 axis (to point q). And, finally, inasmuch as there
is no projection along the z axis, it is not necessary to move parallel to this axis. Thus, the [1010] direction is that
vector that extends from point o to point q as shown.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-77-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.37 Using Equations 3.6a, 3.6b, 3.6c, and 3.6d, derive expressions for each of the three primed indices
set (u′, v′, and w′) in terms of the four unprimed indices (u, v, t, and w).
Solution
It is first necessary to do an expansion of Equation 3.6a as
u =
1
3
(2u' − v) =
2u'
3
−
v'
3
And solving this expression for v’ yields
v' = 2u' − 3u
Now, substitution of this expression into Equation 3.6b gives
v =
1
3
(2vÕ− uÕ) =
1
3
(2)(2uÕ− 3u) − uÕ[ ] = uÕ− 2u
Or
u' = v + 2u
And, solving for v from Equation 3.6c leads to
v = − (u + t)
which, when substituted into the above expression for u’ yields
u' = v + 2u = − u − t + 2u = u − t
In solving for an expression for v’, we begin with the one of the above expressions for this parameter—i.e.,
v' = 2u' − 3u
Now, substitution of the above expression for u’ into this equation leads to
vÕ= 2uÕ− 3u = (2)(u − t) − 3u = − u −2t](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-78-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.44 Cite the indices of the direction that results from the intersection of each of the following pair of planes
within a cubic crystal: (a) (100) and (010) planes, (b) (111) and (111) planes, and (c) (101) and (001)
planes.
Solution
(a) In the figure below is shown (100) and (010) planes, and, as indicated, their intersection results in a [001],
or equivalently, a [001] direction.
(b) In the figure below is shown (111) and (111) planes, and, as indicated, their intersection results in a
[110], or equivalently, a [110] direction.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-87-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
(c) In the figure below is shown (101) and (001) planes, and, as indicated, their intersection results in a
[010], or equivalently, a [010] direction.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-88-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Furthermore, the (101) and (011) are equivalent to each other (but not to the other pair of planes); their atomic
arrangement is represented in the other drawing. Note: the 0.424 nm dimension in the left-most drawing comes
from the relationship (0.30 nm)2 + (0.30 nm)2
[ ]
1/ 2
. Likewise, the 0.500 nm dimension found in the right-most
drawing comes from (0.30 nm)2 + (0.40 nm)2
[ ]
1/ 2
.
(c) All of the (1 1 1), (111), (1 11), and (111) planes are equivalent, that is, have the same atomic
packing as illustrated in the following figure:](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-91-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.49 Convert the (010) and (101) planes into the four-index Miller–Bravais scheme for hexagonal unit
cells.
Solution
For (010), h = 0, k = 1, and l = 0, and, from Equation 3.7, the value of i is equal to
i = − (h + k) = − (0 + 1) = −1
Therefore, the (010) plane becomes (0110) .
Now for the (101) plane, h = 1, k = 0, and l = 1, and computation of i using Equation 3.7 leads to
i = − (h + k) = −[1 + 0] = −1
such that (101) becomes (1011).](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-96-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.50 Determine the indices for the planes shown in the hexagonal unit cells below:
Solution
(a) For this plane, intersections with the a1, a2, and z axes are ∞a, ∞a, and c/2 (the plane parallels both a1
and a2 axes). In terms of a and c these intersections are ∞, ∞, and ½, the respective reciprocals of which are 0, 0,
and 2. This means that
h = 0
k = 0
l = 2
Now, from Equation 3.7, the value of i is
i = − (h + k) = −[0 + 0] = 0
Hence, this is a (0002) plane.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-97-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Linear and Planar Densities
3.52 (a) Derive linear density expressions for FCC [100] and [111] directions in terms of the atomic
radius R.
(b) Compute and compare linear density values for these same two directions for silver.
Solution
(a) In the figure below is shown a [100] direction within an FCC unit cell.
For this [100] direction there is one atom at each of the two unit cell corners, and, thus, there is the equivalent of 1
atom that is centered on the direction vector. The length of this direction vector is just the unit cell edge length,
2R 2 (Equation 3.1). Therefore, the expression for the linear density of this plane is
LD100 =
number of atoms centered on [100] direction vector
length of [100] direction vector
=
1 atom
2R 2
=
1
2R 2
An FCC unit cell within which is drawn a [111] direction is shown below.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-102-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
For this [111] direction, the vector shown passes through only the centers of the single atom at each of its ends, and,
thus, there is the equivalence of 1 atom that is centered on the direction vector. The length of this direction vector is
denoted by z in this figure, which is equal to
z = x2 + y2
where x is the length of the bottom face diagonal, which is equal to 4R. Furthermore, y is the unit cell edge length,
which is equal to 2R 2 (Equation 3.1). Thus, using the above equation, the length z may be calculated as follows:
z = (4R)2 + (2 R 2)2 = 24 R2 = 2 R 6
Therefore, the expression for the linear density of this direction is
LD111 =
number of atoms centered on [111] direction vector
length of [111] direction vector
=
1 atom
2R 6
=
1
2R 6
(b) From the table inside the front cover, the atomic radius for silver is 0.144 nm. Therefore, the linear
density for the [100] direction is
LD100 (Ag) =
1
2R 2
=
1
(2)(0.144 nm) 2
= 2.46 nm−1 = 2.46 × 109 m−1
While for the [111] direction
LD111(Ag) =
1
2R 6
=
1
(2)(0.144 nm) 6
= 1.42 nm−1 = 1.42 × 109 m−1](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-103-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
3.53 (a) Derive linear density expressions for BCC [110] and [111] directions in terms of the atomic
radius R.
(b) Compute and compare linear density values for these same two directions for tungsten.
Solution
(a) In the figure below is shown a [110] direction within a BCC unit cell.
For this [110] direction there is one atom at each of the two unit cell corners, and, thus, there is the equivalence of 1
atom that is centered on the direction vector. The length of this direction vector is denoted by x in this figure, which
is equal to
x = z2 − y2
where y is the unit cell edge length, which, from Equation 3.3 is equal to
4 R
3
. Furthermore, z is the length of the
unit cell diagonal, which is equal to 4R Thus, using the above equation, the length x may be calculated as follows:
x = (4R)2 −
4R
3
2
=
32R2
3
= 4R
2
3
Therefore, the expression for the linear density of this direction is
LD110 =
number of atoms centered on [110] direction vector
length of [110] direction vector
=
1 atom
4 R
2
3
=
3
4 R 2](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-104-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
A BCC unit cell within which is drawn a [111] direction is shown below.
For although the [111] direction vector shown passes through the centers of three atoms, there is an equivalence of
only two atoms associated with this unit cell—one-half of each of the two atoms at the end of the vector, in addition
to the center atom belongs entirely to the unit cell. Furthermore, the length of the vector shown is equal to 4R, since
all of the atoms whose centers the vector passes through touch one another. Therefore, the linear density is equal to
LD111 =
number of atoms centered on [111] direction vector
length of [111] direction vector
=
2 atoms
4R
=
1
2R
(b) From the table inside the front cover, the atomic radius for tungsten is 0.137 nm. Therefore, the linear
density for the [110] direction is
LD110 (W) =
3
4 R 2
=
3
(4)(0.137 nm) 2
= 2.23 nm−1 = 2.23 × 109 m−1
While for the [111] direction
LD111(W) =
1
2 R
=
1
(2)(0.137 nm)
= 3.65 nm−1 = 3.65 × 109 m−1](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-105-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Or, in terms of the component elements 1 and 2
ρave =
m1 + m2
V1 + V2
[Note: here it is assumed that the total alloy volume is equal to the separate volumes of the individual components,
which is only an approximation; normally V will not be exactly equal to (V1
+ V2
)].
Each of V1
and V2
may be expressed in terms of its mass and density as,
V1 =
m1
ρ1
V2 =
m2
ρ2
When these expressions are substituted into the above equation, we get
ρave =
m1 + m2
m1
ρ1
+
m2
ρ2
Furthermore, from Equation 4.3
m1 =
C1 (m1 + m2)
100
m2 =
C2 (m1 + m2)
100
Which, when substituted into the above ρave expression yields
ρave =
m1 + m2
C1 (m1 + m2)
100
ρ1
+
C2 (m1 + m2)
100
ρ2
And, finally, this equation reduces to](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-136-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Interfacial Defects
4.27 For an FCC single crystal, would you expect the surface energy for a (100) plane to be greater or
less than that for a (111) plane? Why? (Note: You may want to consult the solution to Problem 3.54 at the end of
Chapter 3.)
Solution
The surface energy for a crystallographic plane will depend on its packing density [i.e., the planar density
(Section 3.11)]—that is, the higher the packing density, the greater the number of nearest-neighbor atoms, and the
more atomic bonds in that plane that are satisfied, and, consequently, the lower the surface energy. From the
solution to Problem 3.54, planar densities for FCC (100) and (111) planes are
1
4R2
and
1
2R2 3
, respectively—that
is
0.25
R2
and
0.29
R2
(where R is the atomic radius). Thus, since the planar density for (111) is greater, it will have the
lower surface energy.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-164-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
4.28 For a BCC single crystal, would you expect the surface energy for a (100) plane to be greater or less
than that for a (110) plane? Why? (Note: You may want to consult the solution to Problem 3.55 at the end of
Chapter 3.)
Solution
The surface energy for a crystallographic plane will depend on its packing density [i.e., the planar density
(Section 3.11)]—that is, the higher the packing density, the greater the number of nearest-neighbor atoms, and the
more atomic bonds in that plane that are satisfied, and, consequently, the lower the surface energy. From the
solution to Problem 3.55, the planar densities for BCC (100) and (110) are
3
16R2
and
3
8R2 2
, respectively—that
is
0.19
R2
and
0.27
R2
. Thus, since the planar density for (110) is greater, it will have the lower surface energy.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-165-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
5.9 When α-iron is subjected to an atmosphere of hydrogen gas, the concentration of hydrogen in the iron,
CH (in weight percent), is a function of hydrogen pressure, pH2
(in MPa), and absolute temperature (T) according
to
CH = 1.34 × 10−2 pH2
exp −
27.2 kJ /mol
RT
(5.14)
Furthermore, the values of D0 and Qd for this diffusion system are 1.4 × 10-7
m2
/s and 13,400 J/mol, respectively.
Consider a thin iron membrane 1 mm thick that is at 250°C. Compute the diffusion flux through this membrane if
the hydrogen pressure on one side of the membrane is 0.15 MPa (1.48 atm), and on the other side 7.5 MPa (74
atm).
Solution
Ultimately we will employ Equation 5.3 to solve this problem. However, it first becomes necessary to
determine the concentration of hydrogen at each face using Equation 5.14. At the low pressure (or B) side
CH(B) = (1.34 × 10-2) 0.15 MPa exp −
27,200 J/mol
(8.31 J/mol- K)(250 + 273 K)
9.93 × 10-6 wt%
Whereas, for the high pressure (or A) side
CH(A) = (1.34 × 10-2) 7.5 MPa exp −
27,200 J/mol
(8.31 J/mol- K)(250 + 273 K)
7.02 × 10-5 wt%
We now convert concentrations in weight percent to mass of nitrogen per unit volume of solid. At face B there are
9.93 × 10-6 g (or 9.93 × 10-9 kg) of hydrogen in 100 g of Fe, which is virtually pure iron. From the density of iron
(7.87 g/cm3), the volume iron in 100 g (VB) is just
VB =
100 g
7.87 g/cm3
= 12.7 cm3 = 1.27 × 10-5 m3
Therefore, the concentration of hydrogen at the B face in kilograms of H per cubic meter of alloy [ CH(B)
’’ ] is just](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-190-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
5.18 At what temperature will the diffusion coefficient for the diffusion of copper in nickel have a value of
6.5 × 10-17
m2
/s. Use the diffusion data in Table 5.2.
Solution
Solving for T from Equation 5.9a
T = −
Qd
R(ln D − ln D0)
and using the data from Table 5.2 for the diffusion of Cu in Ni (i.e., D0
= 2.7 × 10-5 m2/s and Qd = 256,000 J/mol) ,
we get
T = −
256,000 J/mol
(8.31 J/mol- K) ln (6.5 × 10-17 m2/s) − ln (2.7 × 10 -5 m2/s)[ ]
= 1152 K = 879°C
Note: this problem may also be solved using the “Diffusion” module in the VMSE software. Open the “Diffusion”
module, click on the “D vs 1/T Plot” submodule, and then do the following:
1. In the left-hand window that appears, there is a preset set of data for several diffusion systems. Click on
the box for which Cu is the diffusing species and Ni is the host metal. Next, at the bottom of this window, click the
“Add Curve” button.
2. A log D versus 1/T plot then appears, with a line for the temperature dependence of the diffusion
coefficient for Cu in Ni. At the top of this curve is a diamond-shaped cursor. Click-and-drag this cursor down the
line to the point at which the entry under the “Diff Coeff (D):” label reads 6.5 × 10-17 m2/s. The temperature at
which the diffusion coefficient has this value is given under the label “Temperature (T):”. For this problem, the
value is 1153 K.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-205-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
5.19 The preexponential and activation energy for the diffusion of iron in cobalt are 1.1 × 10-5
m2
/s and
253,300 J/mol, respectively. At what temperature will the diffusion coefficient have a value of 2.1 × 10-14
m2
/s?
Solution
For this problem we are given D0
(1.1 × 10-5
) and Qd (253,300 J/mol) for the diffusion of Fe in Co, and
asked to compute the temperature at which D = 2.1 × 10-14
m2
/s. Solving for T from Equation 5.9a yields
T =
Qd
R(ln D0 − ln D)
=
253,300 J/mol
(8.31 J/mol- K) ln (1.1 × 10-5 m2/s) - ln (2.1 × 10-14 m2/s)[ ]
= 1518 K = 1245°C
Note: this problem may also be solved using the “Diffusion” module in the VMSE software. Open the “Diffusion”
module, click on the “D vs 1/T Plot” submodule, and then do the following:
1. In the left-hand window that appears, click on the “Custom1” box.
2. In the column on the right-hand side of this window enter the data for this problem. In the window
under “D0” enter preexponential value—viz. “1.1e-5”. Next just below the “Qd” window enter the activation
energy value—viz. “253.3”. It is next necessary to specify a temperature range over which the data is to be plotted.
The temperature at which D has the stipulated value is probably between 1000ºC and 1500ºC, so enter “1000” in the
“T Min” box that is beside “C”; and similarly for the maximum temperature—enter “1500” in the box below “T
Max”.
3. Next, at the bottom of this window, click the “Add Curve” button.
4. A log D versus 1/T plot then appears, with a line for the temperature dependence of the diffusion
coefficient for Fe in Co. At the top of this curve is a diamond-shaped cursor. Click-and-drag this cursor down the
line to the point at which the entry under the “Diff Coeff (D):” label reads 2.1 × 10-14 m2/s. The temperature at
which the diffusion coefficient has this value is given under the label “Temperature (T):”. For this problem, the
value is 1519 K.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-206-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
5.21 The diffusion coefficients for iron in nickel are given at two temperatures:
T (K) D (m2
/s)
1273 9.4 × 10–16
1473 2.4 × 10–14
(a) Determine the values of D0 and the activation energy Qd.
(b) What is the magnitude of D at 1100ºC (1373 K)?
Solution
(a) Using Equation 5.9a, we set up two simultaneous equations with Qd and D0
as unknowns as follows:
ln D1 = lnD0 −
Qd
R
1
T1
ln D2 = lnD0 −
Qd
R
1
T2
Now, solving for Qd in terms of temperatures T1 and T2 (1273 K and 1473 K) and D1 and D2 (9.4 × 10-16
and 2.4 ×
10-14
m2
/s), we get
Qd = − R
ln D1 − ln D2
1
T1
−
1
T2
= − (8.31 J/mol- K)
ln (9.4 × 10 -16) − ln (2.4 × 10 -14)[ ]
1
1273 K
−
1
1473 K
= 252,400 J/mol
Now, solving for D0
from Equation 5.8 (and using the 1273 K value of D)
D0 = D1 exp
Qd
RT1
](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-208-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
5.22 The diffusion coefficients for silver in copper are given at two temperatures:
T (°C) D (m2
/s)
650 5.5 × 10–16
900 1.3 × 10–13
(a) Determine the values of D0 and Qd.
(b) What is the magnitude of D at 875°C?
Solution
(a) Using Equation 5.9a, we set up two simultaneous equations with Qd and D0
as unknowns as follows:
ln D1 = lnD0 −
Qd
R
1
T1
ln D2 = lnD0 −
Qd
R
1
T2
Solving for Qd in terms of temperatures T1 and T2 (923 K [650°C] and 1173 K [900°C]) and D1 and D2 (5.5 × 10-
16
and 1.3 × 10-13
m2
/s), we get
Qd = − R
ln D1 − ln D2
1
T1
−
1
T2
= −
(8.31 J/mol- K) ln (5.5 × 10 -16) − ln (1.3 × 10 -13)[ ]
1
923 K
−
1
1173 K
= 196,700 J/mol
Now, solving for D0
from Equation 5.8 (and using the 650°C value of D)
D0 = D1 exp
Qd
RT1
](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-210-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
= −
148,000 J/mol
(8.31 J/mol- K) ln (4.43 × 10-11 m2/s) − ln (2.3 × 10-5 m2/s)[ ]
= 1353 K = 1080°C](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-217-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
= 2.16 × 10-15 m2/s
We now need to find the T at which D has this value. This is accomplished by rearranging Equation 5.9a and
solving for T as
T =
Qd
R (lnD0 − lnD)
=
256,000 J/mol
(8.31 J/mol- K) ln (2.7 × 10-5 m2/s) − ln (2.16 × 10-15 m2/s)[ ]
= 1325 K = 1052°C](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-220-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
And since t = 49.5 h (178,200 s) and x = 4.0 mm (4.0 × 10-3
m), solving for D from the above equation yields
D =
x2
(4t)(0.9324 )2
=
(4.0 × 10−3 m)2
(4)(178,200 s)(0.869)
= 2.58 × 10-11 m2/s
Now, in order to determine the temperature at which D has the above value, we must employ Equation 5.9a;
solving this equation for T yields
T =
Qd
R (lnD0 − lnD)
From Table 5.2, D0 and Qd for the diffusion of C in FCC Fe are 2.3 × 10-5
m2
/s and 148,000 J/mol, respectively.
Therefore
T =
148,000 J/mol
(8.31 J/mol- K) ln (2.3 × 10-5 m2/s) - ln (2.58 × 10-11 m2/s)[ ]
= 1300 K = 1027°C](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-226-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Diffusion in Semiconducting Materials
5.32 Phosphorus atoms are to be diffused into a silicon wafer using both predeposition and drive-in heat
treatments; the background concentration of P in this silicon material is known to be 5 × 1019
atoms/m3
. The
predeposition treatment is to be conducted at 950°C for 45 minutes; the surface concentration of P is to be
maintained at a constant level of 1.5 × 1026
atoms/m3
. Drive-in diffusion will be carried out at 1200°C for a period
of 2.5 h. For the diffusion of P in Si, values of Qd and D0 are 3.40 eV and 1.1 × 10-4
m2
/s, respectively.
(a) Calculate the value of Q0.
(b) Determine the value of xj for the drive-in diffusion treatment.
(c) Also for the drive-in treatment, compute the position x at which the concentration of P atoms is 1024
m-
3
.
Solution
(a) For this portion of the problem we are asked to determine the value of Q0
. This is possible using
Equation 5.12. However, it is first necessary to determine the value of D for the predeposition treatment [Dp
at Tp
=
950°C (1223 K)] using Equation 5.8. Thus
Dp = D0 exp −
Qd
kTp
= (1.1 × 10−4 m2 /s) exp −
3.40 eV
(8.62 × 10−5 eV/atom− K)(1223 K)
= 1.08 × 10−18 m2 /s
The value of Q0
may be determined as follows:
Q0 = 2Cs
Dpt p
π
= (2)(1.5 × 1026 atoms /m3)
(1.08 × 10−18 m2 /s)(45 min)(60 s /min)
π
= 9.14 × 1018 atoms /m2
(b) Computation of the junction depth requires that we use Equation 5.13. However, before this is
possible it is necessary to calculate D at the temperature of the drive-in treatment [Dd
at 1200°C (1473 K)]. Thus,](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-227-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
5.33 Aluminum atoms are to be diffused into a silicon wafer using both predeposition and drive-in heat
treatments; the background concentration of Al in this silicon material is known to be 3 × 1019
atoms/m3
. The
drive-in diffusion treatment is to be carried out at 1050°C for a period of 4.0 h, which gives a junction depth xj of
3.0 µm. Compute the predeposition diffusion time at 950°C if the surface concentration is maintained at a constant
level of 2 × 1025
atoms/m3
. For the diffusion of Al in Si, values of Qd and D0 are 3.41 eV and 1.38 × 10-4
m2
/s,
respectively.`
Solution
This problem asks that we compute the time for the predeposition heat treatment for the diffusion of Al in
Si. In order to do this it is necessary to determine the value of Q0
from Equation 5.13. However, before doing this
we must first calculate Dd
, using Equation 5.8. Therefore
Dd = D0 exp −
Qd
kTd
= (1.38 × 10−4 m2 /s) exp −
3.41 eV
(8.62 × 10−5 eV/atom− K)(1050°C + 273 K)
= 1.43 × 10−17 m2 /s
Now, solving for Q0
in Equation 5.13 leads to
Q0 = CB πDdtd( )exp
x j
2
4Ddtd
In the problem statement we are given the following values:
CB
= 3 × 1019
atoms/m3
td
= 4 h (14,400 s)
xj
= 3.0 µm = 3.0 × 10-6
m
Therefore, incorporating these values into the above equation yields
Q0 = (3 × 1019 atoms /m3) (π)(1.43 × 10−17 m2 /s)(14,400 s)[ ]exp
(3.0 × 10−6 m)2
(4)(1.43 × 10−17 m2 /s)(14,400 s)
](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-230-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
τ =
V
A
For static equilibrium in the x' direction the following condition must be met:
F∑ x'
= 0
which means that
PÕ− P cos θ = 0
Or that
P' = P cos θ
Now it is possible to write an expression for the stress σ' in terms of P' and A' using the above expression and the
relationship between A and A' [Figure (a)]:
σ' =
PÕ
AÕ
=
P cosθ
A
cosθ
=
P
A
cos2θ
However, it is the case that P/A = σ; and, after making this substitution into the above expression, we have
Equation 6.4a--that is
σ' = σ cos
2
θ
Now, for static equilibrium in the y' direction, it is necessary that
FyÕ∑ = 0
= −VÕ+ Psinθ](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-243-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
6.12 As noted in Section 3.15, for single crystals of some substances, the physical properties are
anisotropic; that is, they are dependent on crystallographic direction. One such property is the modulus of
elasticity. For cubic single crystals, the modulus of elasticity in a general [uvw] direction, Euvw, is described by the
relationship
1
Euvw
=
1
E 100
− 3
1
E 100
−
1
E 111
α2β2 + β2γ2 + γ2α2
( )
where E 100 and E 111 are the moduli of elasticity in [100] and [111] directions, respectively; α, β, and γ are the
cosines of the angles between [uvw] and the respective [100], [010], and [001] directions. Verify that the E〈110〉
values for aluminum, copper, and iron in Table 3.3 are correct.
Solution
We are asked, using the equation given in the problem statement, to verify that the modulus of elasticity
values along [110] directions given in Table 3.3 for aluminum, copper, and iron are correct. The α, β, and γ
parameters in the equation correspond, respectively, to the cosines of the angles between the [110] direction and
[100], [010] and [001] directions. Since these angles are 45°, 45°, and 90°, the values of α, β, and γ are 0.707,
0.707, and 0, respectively. Thus, the given equation takes the form
1
E<110>
=
1
E<100>
− 3
1
E<100>
−
1
E<111>
(0.707)2(0.707)2 + (0.707)2 (0)2 + (0)2(0.707)2
[ ]
=
1
E<100>
− (0.75)
1
E<100>
−
1
E<111>
Utilizing the values of E<100>
and E<111>
from Table 3.3 for Al
1
E<110>
=
1
63.7 GPa
− (0.75)
1
63.7 GPa
−
1
76.1 GPa
Which leads to, E<110>
= 72.6 GPa, the value cited in the table.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-257-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
6.46 Find the toughness (or energy to cause fracture) for a metal that experiences both elastic and plastic
deformation. Assume Equation 6.5 for elastic deformation, that the modulus of elasticity is 172 GPa (25 × 106
psi),
and that elastic deformation terminates at a strain of 0.01. For plastic deformation, assume that the relationship
between stress and strain is described by Equation 6.19, in which the values for K and n are 6900 MPa (1 × 106
psi)
and 0.30, respectively. Furthermore, plastic deformation occurs between strain values of 0.01 and 0.75, at which
point fracture occurs.
Solution
This problem calls for us to compute the toughness (or energy to cause fracture). The easiest way to do
this is to integrate both elastic and plastic regions, and then add them together.
Toughness = σ dε∫
= Eεdε
0
0.01
∫ + Kεn dε
0.01
0.75
∫
=
Eε2
2 0
0.01
+
K
(n + 1)
ε(n+1)
0.01
0.75
=
172 × 109 N/m2
2
(0.01)2 +
6900 × 106 N/m2
(1.0 + 0.3)
(0.75)1.3 − (0.01)1.3
[ ]
= 3.65 × 109 J/m3 (5.29 × 105 in.-lbf/in.3)](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-305-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
6.47 For a tensile test, it can be demonstrated that necking begins when
dσT
dεT
= σT (6.26)
Using Equation 6.19, determine the value of the true strain at this onset of necking.
Solution
Let us take the derivative of Equation 6.19, set it equal to σT, and then solve for εT from the resulting
expression. Thus
d K (εT )n
[ ]
d εT
= Kn (εT )(n−1) = σT
However, from Equation 6.19, σT
= K(εT
)n
, which, when substituted into the above expression, yields
Kn (εT )(n - 1) = K (εT )n
Now solving for εT from this equation leads to
εT
= n
as the value of the true strain at the onset of necking.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-306-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Hardness
6.51 (a) A 10-mm-diameter Brinell hardness indenter produced an indentation 1.62 mm in diameter in a
steel alloy when a load of 500 kg was used. Compute the HB of this material.
(b) What will be the diameter of an indentation to yield a hardness of 450 HB when a 500 kg load is used?
Solution
(a) We are asked to compute the Brinell hardness for the given indentation. It is necessary to use the
equation in Table 6.5 for HB, where P = 500 kg, d = 1.62 mm, and D = 10 mm. Thus, the Brinell hardness is
computed as
HB =
2P
π D D − D2 − d2
[ ]
=
(2)(500 kg)
(π)(10 mm) 10 mm − (10 mm)2 − (1.62 mm)2
[ ]
= 241
(b) This part of the problem calls for us to determine the indentation diameter d which will yield a 450 HB
when P = 500 kg. Solving for d from the equation in Table 6.5 gives
d = D2 − D −
2P
(HB)π D
2
= (10mm)2 − 10 mm −
(2)(500 kg)
(450)(π)(10 mm)
2
= 1.19 mm](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-311-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
6.52 Estimate the Brinell and Rockwell hardnesses for the following:
(a) The naval brass for which the stress–strain behavior is shown in Figure 6.12.
(b) The steel alloy for which the stress–strain behavior is shown in Figure 6.21.
Solution
This problem calls for estimations of Brinell and Rockwell hardnesses.
(a) For the brass specimen, the stress-strain behavior for which is shown in Figure 6.12, the tensile
strength is 450 MPa (65,000 psi). From Figure 6.19, the hardness for brass corresponding to this tensile strength is
about 125 HB or 70 HRB.
(b) The steel alloy (Figure 6.21) has a tensile strength of about 515 MPa (74,700 psi) [Problem 6.25(d)].
This corresponds to a hardness of about 160 HB or ~90 HRB from the line for steels in Figure 6.19. Alternately,
using Equation 6.20a
HB =
TS(MPa)
3.45
=
515 MPa
3.45
= 149](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-312-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Slip in Single Crystals
7.11 Sometimes cos φ cos λ in Equation 7.2 is termed the Schmid factor. Determine the magnitude of the
Schmid factor for an FCC single crystal oriented with its [100] direction parallel to the loading axis.
Solution
We are asked to compute the Schmid factor for an FCC crystal oriented with its [100] direction parallel to
the loading axis. With this scheme, slip may occur on the (111) plane and in the [110] direction as noted in the
figure below.
The angle between the [100] and [110] directions, λ, may be determined using Equation 7.6
λ = cos−1 u1u2 + v1v2 + w1w2
u1
2 + v1
2 + w1
2
( )u2
2 + v2
2 + w2
2
( )
where (for [100]) u1
= 1, v1
= 0, w1
= 0, and (for [110]) u2
= 1, v2
= -1, w2
= 0. Therefore, λ is equal to
λ = cos−1 (1)(1) + (0)(−1) + (0)(0)
(1)2 + (0)2 + (0)2
[ ] (1)2 + (−1)2 + (0)2
[ ]
= cos−1 1
2
= 45°](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-337-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Now, the angle φ is equal to the angle between the normal to the (111) plane (which is the [111] direction), and the
[100] direction. Again from Equation 7.6, and for u1
= 1, v1
= 1, w1
= 1, and u2
= 1, v2
= 0, and w2
= 0, we have
φ = cos−1 (1)(1) + (1)(0) + (1)(0)
(1)2 + (1)2 + (1)2
[ ] (1)2 + (0)2 + (0)2
[ ]
= cos−1 1
3
= 54.7°
Therefore, the Schmid factor is equal to
cos λ cos φ = cos (45°) cos (54.7°) =
1
2
1
3
= 0.408](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-338-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
7.13 A single crystal of aluminum is oriented for a tensile test such that its slip plane normal makes an
angle of 28.1° with the tensile axis. Three possible slip directions make angles of 62.4°, 72.0°, and 81.1° with the
same tensile axis.
(a) Which of these three slip directions is most favored?
(b) If plastic deformation begins at a tensile stress of 1.95 MPa (280 psi), determine the critical resolved
shear stress for aluminum.
Solution
We are asked to compute the critical resolved shear stress for Al. As stipulated in the problem, φ = 28.1°,
while possible values for λ are 62.4°, 72.0°, and 81.1°.
(a) Slip will occur along that direction for which (cos φ cos λ) is a maximum, or, in this case, for the
largest cos λ. Cosines for the possible λ values are given below.
cos(62.4°) = 0.46
cos(72.0°) = 0.31
cos(81.1°) = 0.15
Thus, the slip direction is at an angle of 62.4° with the tensile axis.
(b) From Equation 7.4, the critical resolved shear stress is just
τcrss = σ y (cos φ cos λ)max
= (1.95 MPa) cos (28.1°) cos (62.4°)[ ]= 0.80 MPa (114 psi)](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-340-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
7.14 Consider a single crystal of silver oriented such that a tensile stress is applied along a [001]
direction. If slip occurs on a (111) plane and in a [101] direction, and is initiated at an applied tensile stress of 1.1
MPa (160 psi), compute the critical resolved shear stress.
Solution
This problem asks that we compute the critical resolved shear stress for silver. In order to do this, we must
employ Equation 7.4, but first it is necessary to solve for the angles λ and φ which are shown in the sketch below.
The angle λ is the angle between the tensile axis—i.e., along the [001] direction—and the slip direction—i.e.,
[101]. The angle λ may be determined using Equation 7.6 as
λ = cos−1 u1u2 + v1v2 + w1w2
u1
2 + v1
2 + w1
2
( )u2
2 + v2
2 + w2
2
( )
where (for [001]) u1
= 0, v1
= 0, w1
= 1, and (for [101]) u2
= –1, v2
= 0, w2
= 1. Therefore, λ is equal to
λ = cos−1 (0)(−1) + (0)(0) + (1)(1)
(0)2 + (0)2 + (1)2
[ ] (−1)2 + (0)2 + (1)2
[ ]
= cos−1 1
2
= 45°](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-341-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Furthermore, φ is the angle between the tensile axis—the [001] direction—and the normal to the slip plane—i.e., the
(111) plane; for this case this normal is along a [111] direction. Therefore, again using Equation 7.6
φ = cos−1 (0)(1) + (0)(1) + (1)(1)
(0)2 + (0)2 + (1)2
[ ] (1)2 + (1)2 + (1)2
[ ]
= cos−1 1
3
= 54.7°
And, finally, using Equation 7.4, the critical resolved shear stress is equal to
τcrss = σ y (cos φ cos λ)
= (1.1 MPa) cos(54.7°) cos(45°)[ ]= (1.1 MPa)
1
3
1
2
= 0.45 MPa (65.1 psi)](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-342-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
7.15 A single crystal of a metal that has the FCC crystal structure is oriented such that a tensile stress is
applied parallel to the [110] direction. If the critical resolved shear stress for this material is 1.75 MPa, calculate
the magnitude(s) of applied stress(es) necessary to cause slip to occur on the (111) plane in each of the [110],
[101] and [011] directions.
Solution
In order to solve this problem it is necessary to employ Equation 7.4, but first we need to solve for the for
λ and φ angles for the three slip systems.
For each of these three slip systems, the φ will be the same—i.e., the angle between the direction of the
applied stress, [110] and the normal to the (111) plane, that is, the [111] direction. The angle φ may be determined
using Equation 7.6 as
φ = cos−1 u1u2 + v1v2 + w1w2
u1
2 + v1
2 + w1
2
( )u2
2 + v2
2 + w2
2
( )
where (for [110]) u1
= 1, v1
= 1, w1
= 0, and (for [111]) u2
= 1, v2
= 1, w2
= 1. Therefore, φ is equal to
φ = cos−1 (1)(1) + (1)(1) + (0)(1)
(1)2 + (1)2 + (0)2
[ ] (1)2 + (1)2 + (1)2
[ ]
= cos−1 2
6
= 35.3°
Let us now determine λ for the [110 ] slip direction. Again, using Equation 7.6 where u1
= 1, v1
= 1, w1
= 0 (for
[110]), and u2
= 1, v2
= –1, w2
= 0 (for [110]. Therefore, λ is determined as
λ[110]−[110]
= cos−1 (1)(1) + (1)(−1) + (0)(0)
(1)2 + (1)2 + (0)2
[ ] (1)2 + (−1)2 + (0)2
[ ]
= cos−1 0 = 90°
Now, we solve for the yield strength for this (111)–[110] slip system using Equation 7.4 as](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-343-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
σ y =
τcrss
(cosφ cos λ)
=
1.75 MPa
cos (35.3°) cos (90°)
=
1.75 MPa
(0.816) (0)
= ∞
which means that slip will not occur on this (111)–[110] slip system.
Now, we must determine the value of λ for the (111)–[101] slip system—that is, the angle between the
[110] and [101] directions. Again using Equation 7.6
λ[110]−[101]
= cos−1 (1)(1) + (1)(0) + (0)(−1)
(1)2 + (1)2 + (0)2
[ ] (1)2 + (0)2 + (−1)2
[ ]
= cos−1 1
2
= 60°
Now, we solve for the yield strength for this (111)–[101] slip system using Equation 7.4 as
σ y =
τcrss
(cosφ cos λ)
=
1.75 MPa
cos (35.3°) cos (60°)
=
1.75 MPa
(0.816) (0.500)
= 4.29 MPa
And, finally, for the (111)–[011] slip system, λ is computed using Equation 7.6 as follows:
λ[110]−[011]
= cos−1 (1)(0) + (1)(1) + (0)(−1)
(1)2 + (1)2 + (0)2
[ ] (0)2 + (1)2 + (−1)2
[ ]
= cos−1 1
2
= 60°
Thus, since the values of φ and λ for this (110)–[011] slip system are the same as for (111)–[101], so also will σy
be the same—viz 4.29 MPa.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-344-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
7.16 (a) A single crystal of a metal that has the BCC crystal structure is oriented such that a tensile stress
is applied in the [010] direction. If the magnitude of this stress is 2.75 MPa, compute the resolved shear stress in the
[111] direction on each of the (110) and (101) planes.
(b) On the basis of these resolved shear stress values, which slip system(s) is (are) most favorably
oriented?
Solution
(a) This part of the problem asks, for a BCC metal, that we compute the resolved shear stress in the [111]
direction on each of the (110) and (101) planes. In order to solve this problem it is necessary to employ Equation
7.2, which means that we first need to solve for the for angles λ and φ for the three slip systems.
For each of these three slip systems, the λ will be the same—i.e., the angle between the direction of the
applied stress, [010] and the slip direction, [111]. This angle λ may be determined using Equation 7.6
λ = cos−1 u1u2 + v1v2 + w1w2
u1
2 + v1
2 + w1
2
( )u2
2 + v2
2 + w2
2
( )
where (for [010]) u1
= 0, v1
= 1, w1
= 0, and (for [111]) u2
= –1, v2
= 1, w2
= 1. Therefore, λ is determined as
λ = cos−1 (0)(−1) + (1)(1) + (0)(1)
(0)2 + (1)2 + (0)2
[ ] (−1)2 + (1)2 + (1)2
[ ]
= cos−1 1
3
= 54.7°
Let us now determine φ for the angle between the direction of the applied tensile stress—i.e., the [010] direction—
and the normal to the (110) slip plane—i.e., the [110] direction. Again, using Equation 7.6 where u1
= 0, v1
= 1, w1
= 0 (for [010]), and u2
= 1, v2
= 1, w2
= 0 (for [110]), φ is equal to
φ[010]−[110] = cos−1 (0)(1) + (1)(1) + (0)(0)
(0)2 + (1)2 + (0)2
[ ] (1)2 + (1)2 + (0)2
[ ]
= cos−1 1
2
= 45°](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-345-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Now, using Equation 7.2
τR = σ cosφ cos λ
we solve for the resolved shear stress for this slip system as
τR(110)−[111]
= (2.75 MPa) cos (54.7°) cos (45°)[ ] = (2.75 MPa) (0.578)(0.707) = 1.12 MPa
Now, we must determine the value of φ for the (101)–[111] slip system—that is, the angle between the
direction of the applied stress, [010], and the normal to the (101) plane—i.e., the [101] direction. Again using
Equation 7.6
λ[010]−[101] = cos−1 (0)(1) + (1)(0) + (0)(1)
(0)2 + (1)2 + (0)2
[ ] (1)2 + (0)2 + (1)2
[ ]
= cos−1 (0) = 90°
Thus, the resolved shear stress for this (101)–[111] slip system is
τR(101)−[111]
= = (2.75 MPa) cos (54.7°) cos (90°)[ ] = (2.75 MPa) (0.578)(0) = 0 MPa
(b) The most favored slip system(s) is (are) the one(s) that has (have) the largest τR
value. Therefore, the
(110)–[111] is the most favored since its τR (1.12 MPa) is greater than the τR value for (101) −[111] (viz., 0
MPa).](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-346-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
7.17 Consider a single crystal of some hypothetical metal that has the FCC crystal structure and is
oriented such that a tensile stress is applied along a [102] direction. If slip occurs on a (111) plane and in a [101]
direction, compute the stress at which the crystal yields if its critical resolved shear stress is 3.42 MPa.
Solution
This problem asks for us to determine the tensile stress at which a FCC metal yields when the stress is
applied along a [102] direction such that slip occurs on a (111) plane and in a [101] direction; the critical resolved
shear stress for this metal is 3.42 MPa. To solve this problem we use Equation 7.4; however it is first necessary to
determine the values of φ and λ. These determinations are possible using Equation 7.6. Now, λ is the angle
between [102] and [101] directions. Therefore, relative to Equation 7.6 let us take u1 = –1, v1 = 0, and w1 = 2, as
well as u2 = –1, v2 = 0, and w2 = 1. This leads to
λ = cos−1 u1u2 + v1v2 + w1w2
u1
2 + v1
2 + w1
2
( )u2
2 + v2
2 + w2
2
( )
= cos−1 (−1)(−1) + (0)(0) + (2)(1)
(−1)2 + (0)2 + (2)2
[ ] (−1)2 + (0)2 + (1)2
[ ]
= cos−1 3
10
= 18.4°
Now for the determination of φ, the normal to the (111) slip plane is the [111] direction. Again using Equation 7.6,
where we now take u1 = –1, v1 = 0, w1 = 2 (for [102]), and u2 = 1, v2 = 1, w2 = 1 (for [111]). Thus,
φ = cos−1 (−1)(1) + (0)(1) + (2)(1)
(−1)2 + (0)2 + (2)2
[ ] (1)2 + (1)2 + (1)2
[ ]
= cos−1 3
15
= 39.2°
It is now possible to compute the yield stress (using Equation 7.4) as](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-347-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
7.23 (a) From the plot of yield strength versus (grain diameter)–1/2
for a 70 Cu–30 Zn cartridge brass,
Figure 7.15, determine values for the constants σ0 and ky in Equation 7.7.
(b) Now predict the yield strength of this alloy when the average grain diameter is 1.0 × 10-3
mm.
Solution
(a) Perhaps the easiest way to solve for σ0 and ky in Equation 7.7 is to pick two values each of σy and d-1/2
from Figure 7.15, and then solve two simultaneous equations, which may be created. For example
d-1/2 (mm) -1/2 σy (MPa)
4 75
12 175
The two equations are thus
75 = σ0 + 4 ky
175 = σ0 + 12 ky
Solution of these equations yield the values of
ky = 12.5 MPa(mm)1/2 1810 psi(mm)1/2
[ ]
σ0 = 25 MPa (3630 psi)
(b) When d = 1.0 × 10-3 mm, d-1/2 = 31.6 mm-1/2, and, using Equation 7.7,
σ y = σ0 + kyd-1/2
= (25 MPa) + 12.5 MPa(mm)
1/2
(31.6 mm-1/2) = 420 MPa (61,000 psi)](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-354-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
7.24 The lower yield point for an iron that has an average grain diameter of 5 × 10-2
mm is 135 MPa
(19,500 psi). At a grain diameter of 8 × 10-3
mm, the yield point increases to 260 MPa (37,500 psi). At what grain
diameter will the lower yield point be 205 MPa (30,000 psi)?
Solution
The best way to solve this problem is to first establish two simultaneous expressions of Equation 7.7, solve
for σ0 and ky, and finally determine the value of d when σy = 205 MPa. The data pertaining to this problem may be
tabulated as follows:
σy d (mm) d-1/2 (mm)-1/2
135 MPa 5 × 10-2 4.47
260 MPa 8 × 10-3 11.18
The two equations thus become
135 MPa = σ0 + (4.47) k y
260 MPa = σ0 + (11.18) k y
Which yield the values, σ0 = 51.7 MPa and ky = 18.63 MPa(mm)1/2. At a yield strength of 205 MPa
205 MPa = 51.7 MPa + 18.63 MPa(mm)1/2
[ ]d-1/2
or d-1/2 = 8.23 (mm) -1/2, which gives d = 1.48 × 10-2 mm.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-355-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
7.31 (a) What is the approximate ductility (%EL) of a brass that has a yield strength of 275 MPa (40,000
psi)?
(b) What is the approximate Brinell hardness of a 1040 steel having a yield strength of 690 MPa (100,000
psi)?
Solution
(a) In order to solve this problem, it is necessary to consult Figures 7.19a and 7.19c. From Figure 7.19a, a
yield strength of 275 MPa for brass corresponds to 10%CW. A brass that has been cold-worked 10% will have a
ductility of about 43%EL [Figure 7.19c].
(b) This portion of the problem asks for the Brinell hardness of a 1040 steel having a yield strength of 690
MPa (100,000 psi). From Figure 7.19a, a yield strength of 690 MPa for a 1040 steel corresponds to about 10%CW.
A 1040 steel that has been cold worked 10% will have a tensile strength of about 780 MPa [Figure 7.19b]. Finally,
using Equation 6.20a
HB =
TS(MPa)
3.45
=
780 MPa
3.45
= 226](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-363-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
7.D5 A cylindrical rod of 1040 steel originally 15.2 mm (0.60 in.) in diameter is to be cold worked by
drawing; the circular cross section will be maintained during deformation. A cold-worked tensile strength in
excess of 840 MPa (122,000 psi) and a ductility of at least 12%EL are desired. Furthermore, the final diameter
must be 10 mm (0.40 in.). Explain how this may be accomplished.
Solution
First let us calculate the percent cold work and attendant tensile strength and ductility if the drawing is
carried out without interruption. From Equation 7.8
%CW =
π
d0
2
2
− π
dd
2
2
π
d0
2
2
× 100
=
π
15.2 mm
2
2
− π
10 mm
2
2
π
15.2 mm
2
2
× 100 = 56%CW
At 56%CW, the steel will have a tensile strength on the order of 920 MPa (133,000 psi) [Figure 7.19b], which is
adequate; however, the ductility will be less than 10%EL [Figure 7.19c], which is insufficient.
Instead of performing the drawing in a single operation, let us initially draw some fraction of the total
deformation, then anneal to recrystallize, and, finally, cold-work the material a second time in order to achieve the
final diameter, tensile strength, and ductility.
Reference to Figure 7.19b indicates that 20%CW is necessary to yield a tensile strength of 840 MPa
(122,000 psi). Similarly, a maximum of 21%CW is possible for 12%EL [Figure 7.19c]. The average of these
extremes is 20.5%CW. Again using Equation 7.8, if the final diameter after the first drawing is d 0
' , then
20.5%CW =
π
d 0
'
2
2
− π
10 mm
2
2
π
d 0
'
2
2
× 100
And, solving the above expression for d 0
' , yields](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-378-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
7.D6 A cylindrical rod of copper originally 16.0 mm (0.625 in.) in diameter is to be cold worked by
drawing; the circular cross section will be maintained during deformation. A cold-worked yield strength in excess
of 250 MPa (36,250 psi) and a ductility of at least 12%EL are desired. Furthermore, the final diameter must be
11.3 mm (0.445 in.). Explain how this may be accomplished.
Solution
Let us first calculate the percent cold work and attendant yield strength and ductility if the drawing is
carried out without interruption. From Equation 7.8
%CW =
π
d0
2
2
− π
dd
2
2
π
d0
2
2
× 100
=
π
16.0 mm
2
2
− π
11.3 mm
2
2
π
16.0 mm
2
2
× 100 = 50%CW
At 50%CW, the copper will have a yield strength on the order of 330 MPa (48,000 psi), Figure 7.19a, which is
adequate; however, the ductility will be about 4%EL, Figure 7.19c, which is insufficient.
Instead of performing the drawing in a single operation, let us initially draw some fraction of the total
deformation, then anneal to recrystallize, and, finally, cold work the material a second time in order to achieve the
final diameter, yield strength, and ductility.
Reference to Figure 7.19a indicates that 21%CW is necessary to give a yield strength of 250 MPa.
Similarly, a maximum of 23%CW is possible for 12%EL [Figure 7.19c]. The average of these two values is
22%CW, which we will use in the calculations. Thus, to achieve both the specified yield strength and ductility, the
copper must be deformed to 22%CW. If the final diameter after the first drawing is d 0
' , then, using Equation 7.8
22%CW =
π
d 0
'
2
2
− π
11.3 mm
2
2
π
d 0
'
2
2
× 100
And, solving for d 0
' from the above expression yields](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-380-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
8.18 The fatigue data for a brass alloy are given as follows:
Stress Amplitude (MPa) Cycles to Failure
310 2 × 105
223 1 × 106
191 3 × 106
168 1 × 107
153 3 × 107
143 1 × 108
134 3 × 108
127 1 × 109
(a) Make an S–N plot (stress amplitude versus logarithm cycles to failure) using these data.
(b) Determine the fatigue strength at 5 × 105
cycles.
(c) Determine the fatigue life for 200 MPa.
Solution
(a) The fatigue data for this alloy are plotted below.
(b) As indicated by the “A” set of dashed lines on the plot, the fatigue strength at 5 × 105 cycles [log (5 ×
105) = 5.7] is about 250 MPa.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-404-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
8.20 The fatigue data for a ductile cast iron are given as follows:
Stress Amplitude
[MPa (ksi)] Cycles to Failure
248 (36.0) 1 × 105
236 (34.2) 3 × 105
224 (32.5) 1 × 106
213 (30.9) 3 × 106
201 (29.1) 1 × 107
193 (28.0) 3 × 107
193 (28.0) 1 × 108
193 (28.0) 3 × 108
(a) Make an S–N plot (stress amplitude versus logarithm cycles to failure) using these data.
(b) What is the fatigue limit for this alloy?
(c) Determine fatigue lifetimes at stress amplitudes of 230 MPa (33,500 psi) and 175 MPa (25,000 psi).
(d) Estimate fatigue strengths at 2 × 105
and 6 × 106
cycles.
Solution
(a) The fatigue data for this alloy are plotted below.
(b) The fatigue limit is the stress level at which the curve becomes horizontal, which is 193 MPa (28,000
psi).](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-407-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
8.21 Suppose that the fatigue data for the cast iron in Problem 8.20 were taken for bending-rotating tests,
and that a rod of this alloy is to be used for an automobile axle that rotates at an average rotational velocity of 750
revolutions per minute. Give maximum lifetimes of continuous driving that are allowable for the following stress
levels: (a) 250 MPa (36,250 psi), (b) 215 MPa (31,000 psi), (c) 200 MPa (29,000 psi), and (d) 150 MPa (21,750
psi).
Solution
For each stress level, first read the corresponding lifetime from the above plot, then convert it into the
number of cycles.
(a) For a stress level of 250 MPa (36,250 psi), the fatigue lifetime is approximately 90,000 cycles. This
translates into (9 × 104 cycles)(1 min/750 cycles) = 120 min.
(b) For a stress level of 215 MPa (31,000 psi), the fatigue lifetime is approximately 2 × 106 cycles. This
translates into (2 × 106 cycles)(1 min/750 cycles) = 2670 min = 44.4 h.
(c) For a stress level of 200 MPa (29,000 psi), the fatigue lifetime is approximately 1 × 107 cycles. This
translates into (1 × 107 cycles)(1 min/750 cycles) = 1.33 × 104 min = 222 h.
(d) For a stress level of 150 MPa (21,750 psi), the fatigue lifetime is essentially infinite since we are below
the fatigue limit [193 MPa (28,000 psi)].](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-409-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Stress and Temperature Effects
8.28 A specimen 750 mm (30 in.) long of an S-590 alloy (Figure 8.31) is to be exposed to a tensile stress
of 80 MPa (11,600 psi) at 815°C (1500°F). Determine its elongation after 5000 h. Assume that the total of both
instantaneous and primary creep elongations is 1.5 mm (0.06 in.).
Solution
From the 815°C line in Figure 8.31, the steady state creep rate Ýεs is about 5.5 × 10-6 h-1 at 80 MPa. The
steady state creep strain, εs
, therefore, is just the product of Ýε s and time as
εs = Ýεs x (time)
= (5.5 × 10−6 h-1)(5,000 h) = 0.0275
Strain and elongation are related as in Equation 6.2; solving for the steady state elongation, ∆ls, leads to
∆ls = l0 εs = (750 mm)(0.0275) = 20.6 mm (0.81 in.)
Finally, the total elongation is just the sum of this ∆ls and the total of both instantaneous and primary creep
elongations [i.e., 1.5 mm (0.06 in.)]. Therefore, the total elongation is 20.6 mm + 1.5 mm = 22.1 mm (0.87 in.).](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-417-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
8.29 For a cylindrical S-590 alloy specimen (Figure 8.31) originally 10 mm (0.40 in.) in diameter and 500
mm (20 in.) long, what tensile load is necessary to produce a total elongation of 145 mm (5.7 in.) after 2,000 h at
730°C (1350°F)? Assume that the sum of instantaneous and primary creep elongations is 8.6 mm (0.34 in.).
Solution
It is first necessary to calculate the steady state creep rate so that we may utilize Figure 8.31 in order to
determine the tensile stress. The steady state elongation, ∆ls, is just the difference between the total elongation and
the sum of the instantaneous and primary creep elongations; that is,
∆ls = 145 mm − 8.6 mm = 136.4 mm (5.36 in.)
Now the steady state creep rate, Ýεs is just
ε
.
s =
∆ε
∆ t
=
∆ ls
l0
∆ t
=
136.4 mm
500 mm
2,000 h
= 1.36 × 10-4 h-1
Employing the 730°C line in Figure 8.31, a steady state creep rate of 1.36 × 10-4 h-1 corresponds to a stress σ of
about 200 MPa (or 29,000 psi) [since log (1.36 × 10-4) = -3.866]. From this we may compute the tensile load using
Equation 6.1 as
F = σA0 = σπ
d0
2
2
= (200 × 106 N/m2)(π)
10.0 × 10−3 m
2
2
= 15,700 N (3645 lbf)](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-418-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
8.32 From Equation 8.19, if the logarithm of Ýεs is plotted versus the logarithm of σ, then a straight line
should result, the slope of which is the stress exponent n. Using Figure 8.31, determine the value of n for the S-590
alloy at 925°C, and for the initial (i.e., lower-temperature) straight line segments at each of 650°C, 730°C, and
815°C.
Solution
The slope of the line from a log Ýεs versus log σ plot yields the value of n in Equation 8.19; that is
n =
∆ log Ýεs
∆ log σ
We are asked to determine the values of n for the creep data at the four temperatures in Figure 8.31 [i.e., at 925°C,
and for the initial (i.e., lower-temperature) straight line segments at each of 650°C, 730°C, and 815°C]. This is
accomplished by taking ratios of the differences between two log Ýε s and log σ values. (Note: Figure 8.31 plots log
σ versus log Ýεs; therefore, values of n are equal to the reciprocals of the slopes of the straight-line segments.)
Thus for 650°C
n =
∆ log Ýεs
∆ log σ
=
log (10−1) − log (10−5)
log (545 MPa) − log (240 MPa)
= 11.2
While for 730°C
n =
∆ log Ýεs
∆ log σ
=
log 1( ) − log (10−6)
log (430 MPa) − log (125 MPa)
= 11.2
And at 815°C
n =
∆ log Ýεs
∆ log σ
=
log 1( ) − log (10−6)
log (320 MPa) − log (65 MPa)
= 8.7
And, finally at 925°C
n =
∆ log Ýεs
∆ log σ
=
log 102
( )− log (10−5)
log (350 MPa) − log (44 MPa)
= 7.8](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-421-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
8.33 (a) Estimate the activation energy for creep (i.e., Qc in Equation 8.20) for the S-590 alloy having the
steady-state creep behavior shown in Figure 8.31. Use data taken at a stress level of 300 MPa (43,500 psi) and
temperatures of 650°C and 730°C . Assume that the stress exponent n is independent of temperature. (b) Estimate
Ýε s at 600°C (873 K) and 300 MPa.
Solution
(a) We are asked to estimate the activation energy for creep for the S-590 alloy having the steady-state
creep behavior shown in Figure 8.31, using data taken at σ = 300 MPa and temperatures of 650°C and 730°C.
Since σ is a constant, Equation 8.20 takes the form
Ýεs = K2σnexp −
Qc
RT
= K2
' exp −
Qc
RT
where K2
' is now a constant. (Note: the exponent n has about the same value at these two temperatures per
Problem 8.32.) Taking natural logarithms of the above expression
ln Ýεs = ln K2
' −
Qc
RT
For the case in which we have creep data at two temperatures (denoted as T1
and T2
) and their corresponding
steady-state creep rates ( Ýεs1
and Ýεs2
), it is possible to set up two simultaneous equations of the form as above, with
two unknowns, namely K2
' and Qc. Solving for Qc yields
Qc = −
R ln Ýεs1
− ln Ýεs2
1
T1
−
1
T2
Let us choose T1 as 650°C (923 K) and T2 as 730°C (1003 K); then from Figure 8.31, at σ = 300 MPa, Ýεs1
= 8.9 ×
10-5
h-1 and Ýεs2
= 1.3 × 10-2
h-1. Substitution of these values into the above equation leads to
Qc = −
(8.31 J /mol- K) ln (8.9 × 10−5) − ln (1.3 × 10−2)[ ]
1
923 K
−
1
1003 K
= 480,000 J/mol](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-422-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
8.34 Steady-state creep rate data are given below for nickel at 1000°C (1273 K):
Ýεs (s–1
) σ [MPa (psi)]
10–4
15 (2175)
10–6
4.5 (650)
If it is known that the activation energy for creep is 272,000 J/mol, compute the steady-state creep rate at a
temperature of 850°C (1123 K) and a stress level of 25 MPa (3625 psi).
Solution
Taking natural logarithms of both sides of Equation 8.20 yields
ln Ýεs = ln K2 + n ln σ −
Qc
RT
With the given data there are two unknowns in this equation--namely K2 and n. Using the data provided in the
problem statement we can set up two independent equations as follows:
ln 1 × 10−4 s−1
( )= ln K2 + n ln (15 MPa) −
272,000 J /mol
(8.31 J/mol- K)(1273 K)
ln 1 × 10−6 s−1
( )= ln K2 + n ln(4.5 MPa) −
272,000 J /mol
(8.31 J/mol- K)(1273 K)
Now, solving simultaneously for n and K2 leads to n = 3.825 and K2 = 466 s-1. Thus it is now possible to solve for
Ýεs at 25 MPa and 1123 K using Equation 8.20 as
Ýεs = K2σnexp −
Qc
RT
= 466 s−1
( )(25 MPa)3.825 exp −
272,000 J/mol
(8.31 J/mol- K)(1123 K)
2.28 × 10-5 s-1](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-424-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Principles of Fracture Mechanics
8.D2 (a) For the thin-walled spherical tank discussed in Design Example 8.1, on the basis of critical crack
size criterion [as addressed in part (a)], rank the following polymers from longest to shortest critical crack length:
nylon 6,6 (50% relative humidity), polycarbonate, poly(ethylene terephthalate), and poly(methyl methacrylate).
Comment on the magnitude range of the computed values used in the ranking relative to those tabulated for metal
alloys as provided in Table 8.3. For these computations, use data contained in Tables B.4 and B.5 in Appendix B.
(b) Now rank these same four polymers relative to maximum allowable pressure according to the leak-
before-break criterion, as described in the (b) portion of Design Example 8.1. As above, comment on these values
in relation to those for the metal alloys that are tabulated in Table 8.4.
Solution
(a) This portion of the problem calls for us to rank four polymers relative to critical crack length in the
wall of a spherical pressure vessel. In the development of Design Example 8.1, it was noted that critical crack
length is proportional to the square of the KIc–σy ratio. Values of KIc and σy as taken from Tables B.4 and B.5 are
tabulated below. (Note: when a range of σy or KIc values is given, the average value is used.)
Material KIc (MPa m ) σy (MPa)
Nylon 6,6 2.75 51.7
Polycarbonate 2.2 62.1
Poly(ethylene terephthlate) 5.0 59.3
Poly(methyl methacrylate) 1.2 63.5
On the basis of these values, the four polymers are ranked per the squares of the KIc–σy ratios as follows:
Material
KIc
σ y
2
(mm)
PET 7.11
Nylon 6,6 2.83
PC 1.26
PMMA 0.36](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-428-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Data Extrapolation Methods
8.D3 An S-590 alloy component (Figure 8.32) must have a creep rupture lifetime of at least 100 days at
500°C (773 K). Compute the maximum allowable stress level.
Solution
This problem asks that we compute the maximum allowable stress level to give a rupture lifetime of 100
days for an S-590 iron component at 773 K. It is first necessary to compute the value of the Larson-Miller
parameter as follows:
T (20 + log tr) = (773 K) 20 + log (100 days)(24 h/day)[ ]{ }
= 18.1 × 103
From the curve in Figure 8.32, this value of the Larson-Miller parameter corresponds to a stress level of about 530
MPa (77,000 psi).](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-430-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
8.D4 Consider an S-590 alloy component (Figure 8.32) that is subjected to a stress of 200 MPa (29,000
psi). At what temperature will the rupture lifetime be 500 h?
Solution
We are asked in this problem to calculate the temperature at which the rupture lifetime is 500 h when an S-
590 iron component is subjected to a stress of 200 MPa (29,000 psi). From the curve shown in Figure 8.32, at 200
MPa, the value of the Larson-Miller parameter is 22.5 × 103 (K-h). Thus,
22.5 × 103 (K - h) = T (20 + log tr )
= T 20 + log (500 h)[ ]
Or, solving for T yields T = 991 K (718°C).](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-431-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
8.D6 Consider an 18-8 Mo stainless steel component (Figure 8.35) that is exposed to a temperature of
500°C (773 K). What is the maximum allowable stress level for a rupture lifetime of 5 years? 20 years?
Solution
We are asked in this problem to calculate the stress levels at which the rupture lifetime will be 5 years and
20 years when an 18-8 Mo stainless steel component is subjected to a temperature of 500°C (773 K). It first
becomes necessary to calculate the value of the Larson-Miller parameter for each time. The values of tr
corresponding to 5 and 20 years are 4.38 × 104 h and 1.75 × 105 h, respectively. Hence, for a lifetime of 5 years
T (20 + log tr) = 773 20 + log (4.38 × 104 )[ ]= 19.05 × 103
And for tr = 20 years
T (20 + log tr) = 773 20 + log (1.75 × 105)[ ]= 19.51 × 103
Using the curve shown in Figure 8.35, the stress values corresponding to the five- and twenty-year
lifetimes are approximately 260 MPa (37,500 psi) and 225 MPa (32,600 psi), respectively.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-433-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
9.39 The room-temperature tensile strengths of pure lead and pure tin are 16.8 MPa and 14.5 MPa,
respectively.
(a) Make a schematic graph of the room-temperature tensile strength versus composition for all
compositions between pure lead and pure tin. (Hint: you may want to consult Sections 9.10 and 9.11, as well as
Equation 9.24 in Problem 9.64.)
(b) On this same graph schematically plot tensile strength versus composition at 150°C.
(c) Explain the shapes of these two curves, as well as any differences between them.
Solution
The (a) and (b) portions of the problem ask that we make schematic plots on the same graph for the tensile
strength versus composition for lead-tin alloys at both room temperature and 150°C; such a graph is shown below.
(c) Upon consultation of the Pb-Sn phase diagram (Figure 9.8) we note that, at room temperature (20°C),
about 1.5 wt% of Sn is soluble in Pb (within the α-phase region at the left extremity of the phase diagram).
Similarly, only about 1 wt% of Pb is soluble in Sn (within the β-phase region at the left extremity). Thus, there will
a solid-solution strengthening effect on both ends of the phase diagram—strength increases slightly with additions
of Sn to Pb [in the α phase region (left-hand side)] and with additions of Pb to Sn [in the β phase region (right-hand
side)]; these effects are noted in the above figure. This figure also shows that the tensile strength of pure lead is
greater than pure tin, which is in agreement with tensile strength values provided in the problem statement.
In addition, at room temperature, for compositions between about 1.5 wt% Sn and 99 wt% Sn, both α and
β phase will coexist, (Figure 9.8), Furthermore, for compositions within this range, tensile strength will depend
(approximately) on the tensile strengths of each of the α and β phases as well as their phase fractions in a manner
described by Equation 9.24 for the elastic modulus (Problem 9.64). That is, for this problem](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-497-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
from which we compute the number of stable nuclei at 300 K of supercooling as
n300
* = K1 exp −
∆G300
*
kT
n* = (5.62 × 1045 nuclei/m3)exp −
1.51 × 10−18 J
(1.38 × 10−23 J /atom− K)(1538 K − 300 K)
= 2.32 × 107 stable nuclei
(b) Relative to critical radius, r* for 300 K supercooling is slightly smaller that for 200 K (1.33 nm versus
2.00 nm). [From Problem 10.4, the value of r* at the homogeneous nucleation temperature (295 K) was 1.35 nm.]
More significant, however, are the values of n* at these two degrees of supercooling, which are dramatically
different—3.5 × 10-35 stable nuclei at ∆T = 200 K, versus 2.32 × 107 stable nuclei at ∆T = 300 K!](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-540-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
ln ln
1
1 − 0.20
= ln k + n ln(13.1 min)
ln ln
1
1 − 0.70
= ln k + n ln (29.1 min)
Solving these two expressions simultaneously for n and k yields n = 2.112 and k = 9.75 × 10-4.
Now it becomes necessary to solve for y when t = 22.8 min. Application of Equation 10.17 leads to
y = 1 − exp −ktn
( )
= 1 − exp − (9.75 × 10-4 )(22.8 min)2.112
[ ]= 0.51](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-550-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
11.29 Compare the effectiveness of quenching in moderately agitated water and oil by graphing, on a
single plot, radial hardness profiles for 65-mm (2
1
2
-in.) diameter cylindrical specimens of an 8630 steel that have
been quenched in both media.
Solution
We are asked to compare the effectiveness of quenching in moderately agitated water and oil by graphing,
on a single plot, hardness profiles for a 65 mm (2-1/2 in.) diameter cylindrical specimen of an 8630 steel that has
been quenched in both media.
For moderately agitated water, the equivalent distances and hardnesses for the several radial positions
[Figures 11.17a and 11.15] are tabulated below.
Radial Equivalent HRC
Position Distance, mm Hardness
Surface 2.5 52
3/4 R 7 43
Midradius 11 36
Center 13 33
While for moderately agitated oil, the equivalent distances and hardnesses for the several radial positions [Figures
11.17b and 11.15] are tabulated below.
Radial Equivalent HRC
Position Distance, mm Hardness
Surface 10 37
3/4 R 15 32
Midradius 18 29
Center 20 28
These data are plotted here.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-634-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
11.D4 A structural member 100 mm (4 in.) long must be able to support a load of 50,000 N (11,250 lbf)
without experiencing any plastic deformation. Given the following data for brass, steel, aluminum, and titanium,
rank them from least to greatest weight in accordance with these criteria.
Alloy
Yield Strength
[MPa (ksi)]
Density
(g/cm3
)
Brass 415 (60) 8.5
Steel 860 (125) 7.9
Aluminum 310 (45) 2.7
Titanium 550 (80) 4.5
Solution
This problem asks us to rank four alloys (brass, steel, titanium, and aluminum), from least to greatest
weight for a structural member to support a 50,000 N (11,250 lbf) load without experiencing plastic deformation.
From Equation 6.1, the cross-sectional area (A0) must necessarily carry the load (F) without exceeding the yield
strength (σy), as
A0 =
F
σ y
Now, given the length l, the volume of material required (V) is just
V = lA0 =
lF
σ y
Finally, the mass of the member (m) is
m = Vρ =
ρ lF
σ y
Here ρ is the density. Using the values given for these alloys
m (brass) =
(8.5 g/cm3)(10 cm)(50,000 N)
(415 × 106 N /m2) 1 m
102 cm
2
= 102 g](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-643-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Heat Treatment of Steels
11.D6 A cylindrical piece of steel 25 mm (1.0 in.) in diameter is to be quenched in moderately agitated oil.
Surface and center hardnesses must be at least 55 and 50 HRC, respectively. Which of the following alloys will
satisfy these requirements: 1040, 5140, 4340, 4140, and 8640? Justify your choice(s).
Solution
In moderately agitated oil, the equivalent distances from the quenched end for a one-inch diameter bar for
surface and center positions are 3 mm (1/8 in.) and 8 mm (11/32 in.), respectively [Figure 11.17b]. The hardnesses
at these two positions for the alloys cited (as determined using Figure 11.14) are given below.
Surface Center
Alloy Hardness (HRC) Hardness (HRC)
1040 50 30
5140 56 49
4340 57 57
4140 57 55
8640 57 53
Thus, alloys 4340, 4140, and 8640 will satisfy the criteria for both surface and center hardnesses.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-646-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
11.D7 A cylindrical piece of steel 75 mm (3 in.) in diameter is to be austenitized and quenched such that a
minimum hardness of 40 HRC is to be produced throughout the entire piece. Of the alloys 8660, 8640, 8630, and
8620, which will qualify if the quenching medium is (a) moderately agitated water, and (b) moderately agitated oil?
Justify your choice(s).
Solution
(a) This problem calls for us to decide which of 8660, 8640, 8630, and 8620 alloys may be fabricated into
a cylindrical piece 75 mm (3 in.) in diameter which, when quenched in mildly agitated water, will produce a
minimum hardness of 40 HRC throughout the entire piece.
The center of the steel cylinder will cool the slowest and therefore will be the softest. In moderately
agitated water the equivalent distance from the quenched end for a 75 mm diameter bar for the center position is
about 17 mm (11/16 in.) [Figure 11.17a]. The hardnesses at this position for the alloys cited (Figure 11.15) are
given below.
Center
Alloy Hardness (HRC)
8660 58
8640 42
8630 30
8620 22
Therefore, only 8660 and 8640 alloys will have a minimum of 40 HRC at the center, and therefore, throughout the
entire cylinder.
(b) This part of the problem asks us to do the same thing for moderately agitated oil. In moderately
agitated oil the equivalent distance from the quenched end for a 75 mm diameter bar at the center position is about
25.5 mm (1-1/32 in.) [Figure 11.17b]. The hardnesses at this position for the alloys cited (Figure 11.15) are given
below.
Center
Alloy Hardness (HRC)
8660 53
8640 37
8630 26
8620 < 20](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-647-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
11.D8 A cylindrical piece of steel 38 mm (1
1
2
in.) in diameter is to be austenitized and quenched such that
a microstructure consisting of at least 80% martensite will be produced throughout the entire piece. Of the alloys
4340, 4140, 8640, 5140, and 1040, which will qualify if the quenching medium is (a) moderately agitated oil and
(b) moderately agitated water? Justify your choice(s).
Solution
(a) Since the cooling rate is lowest at the center, we want a minimum of 80% martensite at the center
position. From Figure 11.17b, the cooling rate is equal to an equivalent distance from the quenched end of 12 mm
(1/2 in.). According to Figure 11.14, the hardness corresponding to 80% martensite for these alloys is 50 HRC.
Thus, all we need do is to determine which of the alloys have a 50 HRC hardness at an equivalent distance from the
quenched end of 12 mm (1/2 in.). At an equivalent distance of 12 mm (1/2 in.), the following hardnesses are
determined from Figure 11.14 for the various alloys.
Alloy Hardness (HRC)
4340 56
4140 53
8640 49
5140 43
1040 25
Thus, only alloys 4340 and 4140 will qualify.
(b) For moderately agitated water, the cooling rate at the center of a 38 mm diameter specimen is 7 mm
(5/16 in.) equivalent distance from the quenched end [Figure 11.17a]. At this position, the following hardnesses are
determined from Figure 11.14 for the several alloys.
Alloy Hardness (HRC)
4340 57
4140 55
8640 54
5140 51
1040 33
It is still necessary to have a hardness of 50 HRC or greater at the center; thus, alloys 4340, 4140, 8640, and 5140
qualify.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-649-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
11.D9 A cylindrical piece of steel 90 mm (3
1
2
in.) in diameter is to be quenched in moderately agitated
water. Surface and center hardnesses must be at least 55 and 40 HRC, respectively. Which of the following alloys
will satisfy these requirements: 1040, 5140, 4340, 4140, 8620, 8630, 8640, and 8660? Justify your choices.
Solution
A ninety-millimeter (three and one-half inch) diameter cylindrical steel specimen is to be quenched in
moderately agitated water. We are to decide which of eight different steels will have surface and center hardnesses
of at least 55 and 40 HRC, respectively.
In moderately agitated water, the equivalent distances from the quenched end for a 90 mm diameter bar for
surface and center positions are 3 mm (1/8 in.) and 22 mm (7/8 in.), respectively [Figure 11.17a]. The hardnesses at
these two positions for the alloys cited are given below. The hardnesses at these two positions for the alloys cited
are given below (as determined from Figures 11.14 and 11.15).
Surface Center
Alloy Hardness (HRC) Hardness (HRC)
1040 50 < 20
5140 56 34
4340 57 53
4140 57 45
8620 42 < 20
8630 51 28
8640 56 38
8660 64 55
Thus, alloys 4340, 4140, and 8660 will satisfy the criteria for both surface hardness (minimum 55 HRC) and center
hardness (minimum 40 HRC).](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-650-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
11.D15 A solution heat-treated 2014 aluminum alloy is to be precipitation hardened to have a minimum
tensile strength of 450 MPa (65,250 psi) and a ductility of at least 15%EL. Specify a practical precipitation heat
treatment in terms of temperature and time that would give these mechanical characteristics. Justify your answer.
Solution
We are asked to specify a practical heat treatment for a 2014 aluminum alloy that will produce a minimum
tensile strength of 450 MPa (65,250 psi), and a minimum ductility of 15%EL. From Figure 11.27a, the following
heat treating temperatures and time ranges are possible to the give the required tensile strength.
Temperature (°C) Time Range (h)
260 0.02-0.2
204 0.02-10
149 3-600
121 > 35-?
With regard to temperatures and times to give the desired ductility [Figure 11.27b]:
Temperature (°C) Time Range (h)
260 < 0.01, > 40
204 < 0.15
149 < 10
121 < 500
From these tabulations, the following may be concluded:
It is not possible to heat treat this alloy at 260°C so as to produce the desired set of properties— there is no
overlap of the two sets of time ranges.
At 204°C, the heat treating time would be between 0.02 and 0.15 h; times lying within this range are
impractically short.
At 149°C, the time would be between 3 and 10 h.
Finally, at 121°C, the time range is 35 to about 500 h.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-657-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
a =
2rA
2
There will also be an anion located at the corner, point F (not drawn), and the cube diagonal AEF will be related to
the ionic radii as
AEF = 2(rA + rC)
(The line AEF has not been drawn to avoid confusion.) From the triangle ABF
(AB)2 + (FB)2 = (AEF)2
But,
FB = a =
2rA
2
and
AB = 2rA
from above. Thus,
(2rA)2 +
2rA
2
2
= 2(rA + rC)[ ]
2
Solving for the rC/rA ratio leads to
rC
rA
=
6 − 2
2
= 0.225](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-661-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
12.3 Show that the minimum cation-to-anion radius ratio for a coordination number of 6 is 0.414. [Hint:
Use the NaCl crystal structure (Figure 12.2), and assume that anions and cations are just touching along cube
edges and across face diagonals.]
Solution
This problem asks us to show that the minimum cation-to-anion radius ratio for a coordination number of 6
is 0.414 (using the rock salt crystal structure). Below is shown one of the faces of the rock salt crystal structure in
which anions and cations just touch along the edges, and also the face diagonals.
From triangle FGH,
GF = 2rA
and
FH = GH = rA + rC
Since FGH is a right triangle
(GH)2 + (FH)2 = (FG)2
or
(rA + rC)2 + (rA + rC)2 = (2rA)2
which leads to](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-662-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
12.7 Compute the atomic packing factor for the rock salt crystal structure in which rC/rA = 0.414.
Solution
This problem asks that we compute the atomic packing factor for the rock salt crystal structure when rC/rA
= 0.414. From Equation 3.2
APF =
VS
VC
With regard to the sphere volume, VS, there are four cation and four anion spheres per unit cell. Thus,
VS = (4)
4
3
π rA
3
+ (4)
4
3
π rC
3
But, since rC/rA = 0.414
VS =
16
3
π rA
3 1 + (0.414)3
[ ]= (17.94) rA
3
Now, for rC/rA = 0.414 the corner anions in Table 12.2 just touch one another along the cubic unit cell edges such
that
VC = a3 = 2(rA + rC)[ ]
3
= 2(rA + 0.414rA)[ ]
3
= (22.62)rA
3
Thus
APF =
VS
VC
=
(17.94) rA
3
(22.62) rA
3
= 0.79](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-668-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
12.12 Using the Molecule Definition Utility found in both “Metallic Crystal Structures and
Crystallography” and “Ceramic Crystal Structures” modules of VMSE, located on the book’s web site
[www.wiley.com/college/callister (Student Companion Site)], generate (and print out) a three-dimensional unit cell
for titanium dioxide, TiO2, given the following: (1) The unit cell is tetragonal with a = 0.459 nm and c = 0.296 nm,
(2) oxygen atoms are located at the following point coordinates:
0.356 0.356 0 0.856 0.144
1
2
0.664 0.664 0 0.144 0.856
1
2
and (3) Ti atoms are located at the following point coordinates:
0 0 0 1 0 1
1 0 0 0 1 1
0 1 0 1 1 1
0 0 1
1
2
1
2
1
2
1 1 0
Solution
First of all, open the “Molecular Definition Utility”; it may be found in either of “Metallic Crystal
Structures and Crystallography” or “Ceramic Crystal Structures” modules.
In the “Step 1” window, it is necessary to define the atom types, colors for the spheres (atoms), and specify
atom sizes. Let us enter “O” as the name for the oxygen ions (since “O” the symbol for oxygen), and “Ti” as the
name for the titanium ions. Next it is necessary to choose a color for each atom type from the selections that appear
in the pull-down menu—for example, “Red” for O and “Light Cyan” for Ti. In the “Atom Size” window, it is
necessary to enter an atom/ion size. In the instructions for this step, it is suggested that the atom/ion diameter in
nanometers be used. From the table found inside the front cover of the textbook, the atomic radii for oxygen and
titanium are 0.140 nm and 0.068 nm, respectively, and, therefore, their ionic diameters are twice these values (i.e.,
0.280 nm and 0.136 nm); therefore, we enter the values “0.280” and “0.136” for the two atom types. Now click on
the “Register” button, followed by clicking on the “Go to Step 2” button.
In the “Step 2” window we specify positions for all of the atoms within the unit cell; their point
coordinates are specified in the problem statement. Let’s begin with oxygen. Click on the red sphere that is located
to the right of the “Molecule Definition Utility” box. Some of the point coordinates for the oxygen ions are
fractional ones; in these instances, the unit cell lattice parameters--a or c (i.e., 0.459 or 0.296) are multiplied by the
fraction. For example, one oxygen ion is located at the 0.856 0.144
1
2
coordinate. Therefore, the x, y, and z atoms
positions are (0.856)(0.459) = 0.393, (0.144)(0.459) = 0.066, and
1
2
(0.296) = 0.148, respectively. Thus, we enter
“0.393” in the “x” position box, “0.066” in the “y” position box, and “0.148” in the “z” position box. [Note: the](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-673-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
first two point coordinates relate to the a lattice parameter (0.459 nm), whereas the third applies to the c lattice
parameter (0.296 nm).] Next we click on the “Register Atom Position” button. Now we repeat the procedure for
the remaining oxygen ions
After this step has been completed, it is necessary to specify positions for the titanium ions. To begin, we
click on the light cyan sphere that is located next to the “Molecule Definition Utility” box. One Ti ion will be
positioned at the origin of the coordinate system—i.e., its point coordinates are 0 0 0, and, therefore, we enter a “0”
(zero) in each of the “x”, “y”, and “z” atom position boxes. Next we click on the “Register Atom Position” button.
And the enter the coordinate for all of the other titanium ions
For the oxygen ions, x, y, and z atom position entries for the 4 sets of point coordinates are as follows:
0.163, 0.163, 0
0.305, 0.305, 0
0.393, 0.066, 0.148
0.066, 0.393, 0.148
Now, for the titanium ions, the x, y, and z atom position entries for all 9 sets of point coordinates are as
follows:
0, 0, 0
0.459, 0, 0
0, 0.459, 0
0, 0, 0.296
0.459, 0.459, 0
0.459, 0, 0.296
0, 0.459, 0.296
0.459, 0.459, 0.296
0.230, 0.230, 0.148
In Step 3, we may specify which atoms are to be represented as being bonded to one another, and which
type of bond(s) to use (single solid, single dashed, double, and triple are possibilities), or we may elect to not
represent any bonds at all (in which case we are finished). If it is decided to show bonds, probably the best thing to
do is to represent unit cell edges as bonds. Your resulting image may be rotated by using mouse click-and-drag
Your image should appear as the following screen shot.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-674-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Here the darker spheres represent titanium ions, while oxygen ions are depicted by the lighter balls.
[Note: Unfortunately, with this version of the Molecular Definition Utility, it is not possible to save either the data
or the image that you have generated. You may use screen capture (or screen shot) software to record and store
your image.]](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-675-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
12.13 Calculate the density of FeO, given that it has the rock salt crystal structure.
Solution
We are asked to calculate the theoretical density of FeO. This density may be computed using Equation
(12.1) as
ρ =
′n AFe + AO( )
VC NA
Since the crystal structure is rock salt, n' = 4 formula units per unit cell. Using the ionic radii for Fe2+ and O2- from
Table 12.3, the unit cell volume is computed as follows:
VC = a3 = 2rFe2+ + 2rO2-( )
3
= 2 (0.077 nm) + 2 (0.140 nm)[ ]3
= 0.0817
nm3
unit cell
= 8.17 × 10-23 cm3
unit cell
Thus,
ρ =
(4 formula units/unit cell)(55.85 g/mol + 16.00 g/mol)
8.17 × 10-23 cm3/unit cell( )6.022 × 1023 formula units/mol( )
= 5.84 g/cm3](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-676-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
12.16 Compute the theoretical density of ZnS given that the Zn—S distance and bond angle are 0.234 nm
and 109.5°, respectively. How does this value compare with the measured density?
Solution
This problem asks that we compute the theoretical density of ZnS given that the Zn—S distance and bond
angle are 0.234 nm and 109.5°, respectively. The first thing we need do is to determine the unit cell volume from
the given Zn—S distance. From the previous problem, the unit cell volume VC is just a3, a being the unit cell edge
length, and
VC = (4y sin θ)3 = (4)(0.234 nm)(sin 35.25°)[ ]3
= 0.1576 nm3 = 1.576 × 10-22 cm3
Now we must utilize Equation 12.1 with n' = 4 formula units, and AZn and AS being 65.41 and 32.06 g/mol,
respectively. Thus
ρ =
n'Ê(AZn + AS)
VC NA
=
(4 formula units/unit cell)(65.41 g/mol + 32.06 g/mol)
(1.576 × 10-22 cm3/unit cell)(6.022 × 1023 formula units/mol)
= 4.11 g/cm3
The measured value of the density is 4.10 g/cm3.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-680-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
12.19 From the data in Table 12.3, compute the theoretical density of CaF2, which has the fluorite
structure.
Solution
A unit cell of the fluorite structure is shown in Figure 12.5. It may be seen that there are four CaF2 units
per unit cell (i.e., n' = 4 formula units/unit cell). Assume that for each of the eight small cubes in the unit cell
a =
2rCa2+ + 2rF−
3
and, from Table 12.3
a =
2(0.100 nm) + 2(0.133 nm)
3
= 0.269 nm = 2.69 × 10-8 cm
The volume of the unit cell is just
VC = (2a)3 = (2)(2.69 × 10-8 cm)[ ]
3
= 1.56 × 10−22 cm3
Thus, from Equation 12.1
ρ =
n'Ê(ACa + 2AF)
VC NA
=
(4 formula units/unit cell) 40.08 g/mol + (2)(19.00 g/mol)[ ]
(1.56 × 10-22 cm3/unit cell)( 6.022 × 1023 formula units/mol)
= 3.33 g/cm3
The measured density is 3.18 g/cm3.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-683-320.jpg)
(86.6 + 40.3) g/mol
= 1.00 formula units/unit cell
Of the three possible crystal structures, only cesium chloride has one formula unit per unit cell, and therefore, is the
only possibility.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-684-320.jpg)
(1)(24.31 g/mol) + (2)(55.85 g/mol) + (4)(16.00 g/mol)
= 8.0 formula units/unit cell
Thus, in each unit cell there are 8 Mg2+, 16 Fe3+, and 32 O2- ions. From Table 12.3, rMg2+ = 0.072 nm, rFe3+ =
0.069 nm, and rO2- = 0.140 nm. Thus, the total sphere volume in Equation 3.2 (which we denote as VS), is just
VS = (8)
4
3
π
(7.2 × 10−9 cm)3 + (16)
4
3
π
(6.9 × 10−9 cm)3
+ (32)
4
3
π
(1.40 × 10−8 cm)3
= 4.02 × 10-22 cm3
Now, the unit cell volume (VC) is just
VC = a3 = (8.36 × 10-8 cm)3 = 5.84 × 10−22 cm3
Finally, the atomic packing factor (APF) from Equation 3.2 is just
APF =
VS
VC
=
4.02 × 10-22 cm3
5.84 × 10-22 cm3
= 0.688](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-685-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
12.23 Compute the atomic packing factor for the diamond cubic crystal structure (Figure 12.15). Assume
that bonding atoms touch one another, that the angle between adjacent bonds is 109.5°, and that each atom internal
to the unit cell is positioned a/4 of the distance away from the two nearest cell faces (a is the unit cell edge length).
Solution
We are asked in this problem to compute the atomic packing factor for the diamond cubic crystal structure,
given that the angle between adjacent bonds is 109.5°. The first thing that we must do is to determine the unit cell
volume VC in terms of the atomic radius r. From Problem 12.15 the following relationship was developed
a = 4y sin θ
in which y = 2r and θ = 35.25°. Furthermore, since the unit cell is cubic, VC = a3; therefore
VC = (4y sin θ)3 = (4)(2r)(sin 35.25°)[ ]3
= 98.43 r3
Now, it is necessary to determine the sphere volume in the unit cell, VS, in terms of r. For this unit cell (Figure
12.15) there are 4 interior atoms, 6 face atoms, and 8 corner atoms. The entirety of the interior atoms, one-half of
each face atom, and one-eighth of each corner atom belong to the unit cell. Therefore, there are 8 equivalent atoms
per unit cell; hence
VS = (8)
4
3
π r3
= 33.51 r3
Finally, the atomic packing factor is just
APF =
VS
VC
=
33.51 r3
98.43 r3
= 0.340](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-688-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
12.24 Compute the atomic packing factor for cesium chloride using the ionic radii in Table 12.3 and
assuming that the ions touch along the cube diagonals.
Solution
We are asked in this problem to compute the atomic packing factor for the CsCl crystal structure. This
requires that we take the ratio of the sphere volume within the unit cell and the total unit cell volume. From Figure
12.3 there is the equivalence of one Cs and one Cl ion per unit cell; the ionic radii of these two ions are 0.170 nm
and 0.181 nm, respectively (Table 12.3). Thus, the sphere volume, VS, is just
VS =
4
3
(π) (0.170 nm)3 + (0.181 nm)3
[ ] = 0.0454 nm3
For CsCl the unit cell edge length, a, in terms of the atomic radii is just
a =
2r
Cs+ + 2r
Cl-
3
=
2(0.170 nm) + 2(0.181 nm)
3
= 0.405 nm
Since VC = a3
VC = (0.405 nm)3 = 0.0664 nm3
And, finally the atomic packing factor is just
APF =
VS
VC
=
0.0454 nm3
0.0664 nm3
= 0.684](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-689-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
12.38 When kaolinite clay [Al2(Si2O5)(OH)4] is heated to a sufficiently high temperature, chemical water
is driven off.
(a) Under these circumstances, what is the composition of the remaining product (in weight percent
Al2O3)?
(b) What are the liquidus and solidus temperatures of this material
Solution
(a) The chemical formula for kaolinite clay may also be written as Al2O3–2SiO2-2H2O. Thus, if we
remove the chemical water, the formula becomes Al2O3–2SiO2. The formula weight for Al2O3 is just (2)(26.98
g/mol) + (3)(16.00 g/mol) = 101.96 g/mol; and for SiO2 the formula weight is 28.09 g/mol + (2)(16.00 g/mol) =
60.09 g/mol. Thus, the composition of this product, in terms of the concentration of Al2O3, CAl2O3
, in weight
percent is just
CAl2O3
=
101.96 g /mol
101.96 g /mol + (2)(60.09 g /mol)
× 100 = 45.9 wt%
(b) The liquidus and solidus temperatures for this material as determined from the SiO2–Al2O3 phase
diagram, Figure 12.27, are 1825°C and 1587°C, respectively.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-707-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Miscellaneous Mechanical Considerations
12.47 The modulus of elasticity for beryllium oxide (BeO) having 5 vol% porosity is 310 GPa (45 × 106
psi).
(a) Compute the modulus of elasticity for the nonporous material.
(b) Compute the modulus of elasticity for 10 vol% porosity.
Solution
(a) This portion of the problem requests that we compute the modulus of elasticity for nonporous BeO
given that E = 310 GPa for a material having 5 vol% porosity. Thus, we solve Equation 12.9 for E0, using P = 0.05,
which gives
E0 =
E
1 − 1.9P + 0.9P2
=
310 GPa
1 − (1.9)(0.05) + (0.9)(0.05)2
= 342 GPa (49.6 × 106 psi)
(b) Now we are asked to determine the value of E at P = 10 vol% (i.e., 0.10). Using Equation 12.9 we get
E = E0(1 − 1.9P + 0.9P2)
= (342 GPa) 1 − (1.9)(0.10) + (0.9)(0.10)2
[ ]= 280 GPa (40.6 × 106 psi)](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-717-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
12.50 The flexural strength and associated volume fraction porosity for two specimens of the same ceramic
material are as follows:
σfs (MPa) P
100 0.05
50 0.20
(a) Compute the flexural strength for a completely nonporous specimen of this material.
(b) Compute the flexural strength for a 0.10 volume fraction porosity.
Solution
(a) Given the flexural strengths at two different volume fraction porosities, we are asked to determine the
flexural strength for a nonporous material. If the natural logarithm is taken of both sides of Equation 12.10, then
lnσ fs = lnσ0 − nP
Using the data provided in the problem statement, two simultaneous equations may be written as
ln (100 MPa) = ln σ0 − (0.05) n
ln (50 MPa) = ln σ0 − (0.20) n
Solving for n and σ0 leads to n = 4.62 and σ0 = 126 MPa. For the nonporous material, P = 0, and, from Equation
12.10, σ0 = σfs. Thus, σfs for P = 0 is 126 MPa.
(b) Now, we are asked for σfs at P = 0.10 for this same material. Utilizing Equation 12.10 yields
σ fs = σ0 exp (− nP)
= (126 MPa) exp − (4.62)(0.10)[ ]
= 79.4 MPa](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-720-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.17 Calculate the number-average molecular weight of a random nitrile rubber [poly(acrylonitrile-
butadiene) copolymer] in which the fraction of butadiene repeat units is 0.30; assume that this concentration
corresponds to a degree of polymerization of 2000.
Solution
This problem asks for us to calculate the number-average molecular weight of a random nitrile rubber
copolymer. For the acrylonitrile repeat unit there are three carbon, one nitrogen, and three hydrogen atoms. Thus,
its repeat unit molecular weight is
mAc = 3(AC) + (AN) + 3(AH)
= (3)(12.01 g/mol) + 14.01 g/mol + (3)(1.008 g/mol) = 53.06 g/mol
The butadiene repeat unit is composed of four carbon and six hydrogen atoms. Thus, its repeat unit molecular
weight is
mBu = 4(AC) + 6(AH)
= (4)(12.01 g/mol) + (6)(1.008 g/mol) = 54.09 g/mol
From Equation 14.7, the average repeat unit molecular weight is just
m = fAcmAc + fBumBu
= (0.70)(53.06 g/mol) + (0.30)(54.09 g/mol) = 53.37 g/mol
Since DP = 2000 (as stated in the problem), Mn may be computed using Equation 14.6 as
Mn = m (DP) = (53.37 g/mol)(2000) = 106,740 g/mol](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-775-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.21 A random poly(isobutylene-isoprene) copolymer has a number-average molecular weight of
200,000 g/mol and a degree of polymerization of 3000. Compute the fraction of isobutylene and isoprene repeat
units in this copolymer.
Solution
For a random poly(isobutylene-isoprene) copolymer in which Mn = 200,000 g/mol and DP = 3000, we are
asked to compute the fractions of isobutylene and isoprene repeat units.
From Table 14.5, the isobutylene repeat unit has four carbon and eight hydrogen atoms. Thus,
mib = (4)(12.01 g/mol) + (8)(1.008 g/mol) = 56.10 g/mol
Also, from Table 14.5, the isoprene repeat unit has five carbon and eight hydrogen atoms, and
mip = (5)(12.01 g/mol) + (8)(1.008 g/mol) = 68.11 g/mol
From Equation 14.7
m = fibmib + fipmip
Now, let x = fib, such that
m = 56.10x + (68.11)(1 − x)
since fib + fip = 1. Also, from Equation 14.6
DP =
Mn
m
Or
3000 =
200,000 g/mol
[56.10 x + 68.11(1 − x)] g/mol
Solving for x leads to x = fib = f(isobutylene) = 0.12. Also,
f(isoprene) = 1 – x = 1 – 0.12 = 0.88](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-781-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Diffusion in Polymeric Materials
14.27 Consider the diffusion of water vapor through a polypropylene (PP) sheet 2 mm thick. The
pressures of H2O at the two faces are 1 kPa and 10 kPa, which are maintained constant. Assuming conditions of
steady state, what is the diffusion flux [in [(cm3
STP)/cm2
-s] at 298 K?
Solution
This is a permeability problem in which we are asked to compute the diffusion flux of water vapor through
a 2-mm thick sheet of polypropylene. In order to solve this problem it is necessary to employ Equation 14.9. The
permeability coefficient of H2O through PP is given in Table 14.6 as 38 × 10-13 (cm3 STP)-cm/cm2-s-Pa. Thus,
from Equation 14.9
J = PM
∆P
∆x
= PM
P2 − P1
∆x
and taking P1 = 1 kPa (1,000 Pa) and P2 = 10 kPa (10,000 Pa) we get
= 38 × 10-13 (cm3 STP)(cm)
cm2 - s - Pa
10,000 Pa −1,000 Pa
0.2 cm
= 1.71 × 10-7 (cm3 STP)
cm2 - s](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-790-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
14.29 The permeability coefficient of a type of small gas molecule in a polymer is dependent on absolute
temperature according to the following equation:
PM = PM 0
exp −
Qp
RT
where PM0
and Qp are constants for a given gas-polymer pair. Consider the diffusion of hydrogen through a
poly(dimethyl siloxane) (PDMSO) sheet 20 mm thick. The hydrogen pressures at the two faces are 10 kPa and 1
kPa, which are maintained constant. Compute the diffusion flux [in (cm3
STP)/cm2
–s] at 350 K. For this diffusion
system
PM0
= 1.45 × 10−8 (cm3 STP)(cm)/cm2 - s - Pa
Qp = 13.7 kJ/mol
Also, assume a condition of steady state diffusion
Solution
This problem asks that we compute the diffusion flux at 350 K for hydrogen in poly(dimethyl siloxane)
(PDMSO). It is first necessary to compute the value of the permeability coefficient at 350 K. The temperature
dependence of PM is given in the problem statement, as follows:
PM = PM0
exp −
Qp
RT
And, incorporating values provided for the constants PM0
and Qp, we get
PM = 1.45 × 10-8 (cm3 STP)(cm)
cm2 - s - Pa
exp −
13,700 J/mol
(8.31 J/mol- K)(350 K)
= 1.31 × 10−10 (cm3 STP)(cm)
cm2 - s - Pa
And, using Equation 14.9, the diffusion flux is equal to
J = PM
∆P
∆x
= PM
P2 − P1
∆x
= 1.31 × 10-10 (cm3 STP)(cm)
cm2 - s - Pa
10,000 Pa -1,000 Pa
2.0 cm
](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-792-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
CHAPTER 15
CHARACTERISTICS, APPLICATIONS, AND PROCESSING OF POLYMERS
PROBLEM SOLUTIONS
Stress-Strain Behavior
15.1 From the stress–strain data for poly(methyl methacrylate) shown in Figure 15.3, determine the
modulus of elasticity and tensile strength at room temperature [20°C (68°F)], and compare these values with those
given in Table 15.1.
Solution
From Figure 15.3, the elastic modulus is the slope in the elastic linear region of the 20°C curve, which is
E =
∆ (stress)
∆ (strain)
=
30 MPa− 0 MPa
9 × 10−3 − 0
= 3.3 GPa (483,000 psi)
The value range cited in Table 15.1 is 2.24 to 3.24 GPa (325,000 to 470,000 psi). Thus, the plotted value is a little
on the high side.
The tensile strength corresponds to the stress at which the curve ends, which is 52 MPa (7500 psi). This
value lies within the range cited in Table 15.1—48.3 to 72.4 MPa (7000 to 10,500 psi).](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-794-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
15.22 For each of the following pairs of polymers, plot and label schematic stress–strain curves on the
same graph [i.e., make separate plots for parts (a), (b), and (c)].
(a) Isotactic and linear polypropylene having a weight-average molecular weight of 120,000 g/mol; atactic
and linear polypropylene having a weight-average molecular weight of 100,000 g/mol
(b) Branched poly(vinyl chloride) having a degree of polymerization of 2000; heavily crosslinked
poly(vinyl chloride) having a degree of polymerization of 2000
(c) Poly(styrene-butadiene) random copolymer having a number-average molecular weight of 100,000
g/mol and 10% of the available sites crosslinked and tested at 20°C; poly(styrene-butadiene) random copolymer
having a number-average molecular weight of 120,000 g/mol and 15% of the available sites crosslinked and tested
at -85°C. Hint: poly(styrene-butadiene) copolymers may exhibit elastomeric behavior.
Solution
(a) Shown below are the stress-strain curves for the two polypropylene materials. These materials will
display the stress-strain behavior of a normal plastic, curve B in Figure 15.1. However, the isotactic/linear will have
a higher degree of crystallinity (since isotactic are more likely to crystallize than atactic/linear), and therefore, will
have a higher tensile modulus and strength. Furthermore, the isotactic/linear also has a higher molecular weight
which also leads to an increase in strength.
(b) Shown below are the stress-strain curves for the two polyvinyl chloride materials. The branched PVC
will probably display the stress-strain behavior of a plastic, curve B in Figure 15.1. However, the heavily
crosslinked PVC will undoubtedly have a higher tensile modulus, and, also a higher strength, and will most likely
fail in a brittle manner--as curve A, Figure 15.1; these are the typical characteristics of a heavily crosslinked
polymer.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-817-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Factors That Influence Melting and Glass Transition Temperatures
15.33 For each of the following pairs of polymers, plot and label schematic specific volume versus
temperature curves on the same graph [i.e., make separate plots for parts (a), (b), and (c)].
(a) Spherulitic polypropylene, of 25% crystallinity, and having a weight-average molecular weight of
75,000 g/mol; spherulitic polystyrene, of 25% crystallinity, and having a weight-average molecular weight of
100,000 g/mol
(b) Graft poly(styrene-butadiene) copolymer with 10% of available sites crosslinked; random poly(styrene-
butadiene) copolymer with 15% of available sites crosslinked
(c) Polyethylene having a density of 0.985 g/cm3
and a degree of polymerization of 2500; polyethylene
having a density of 0.915 g/cm3
and a degree of polymerization of 2000
Solution
(a) Shown below are the specific volume-versus-temperature curves for the polypropylene and polystyrene
materials. Since both polymers are 25% crystalline, they will exhibit behavior similar to curve B in Figure 15.18.
However, polystyrene will have higher melting and glass transition temperatures due to the bulkier side group in its
repeat unit structure, and since it has a higher weight-average molecular weight.
(b) Shown below are the specific volume-versus-temperature curves for the graft and random poly(styrene-
butadiene) copolymers. Since these materials are graft and random copolymers, both will be highly noncrystalline,
and, thus, will display the behavior similar to curve A in Figure 15.18. However, since the random has the greater
degree of crosslinking, it will also have the higher glass transition temperature.](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-830-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
15.40 (a) How much ethylene glycol must be added to 47.3 kg of terephthalic acid to produce a linear
chain structure of poly(ethylene terephthalate) according to Equation 15.9?
(b) What is the mass of the resulting polymer?
Solution
(a) This problem asks that we determine how much ethylene glycol must be added to 47.3 kg of
terephthalic acid to produce a linear chain structure of poly(ethylene terephthalate) according to Equation 15.9.
Since the chemical formulas are provided in this equation we may calculate the molecular weights of each of these
materials as follows:
MW(ethylene glycol) = 2( AC) + 6( AH) + 2( AO)
= 2(12.01 g/mol) + 6(1.008 g/mol) + 2(16.00 g/mol) = 62.07 g/mol
MW(terephthalic acid) = 8(AC) + 6(AH) + 4(AO)
= 8 (12.01 g/mol) + 6(1.008 g/mol) + 4(16.00 g/mol) = 166.13 g/mol
The 47.3 kg mass of terephthalic acid equals 47,300 g or
47,300 g
166.13 g/mol
= 284.72 mol. Since, according to
Equation 15.9, each mole of terephthalic acid used requires one mole of ethylene glycol, which is equivalent to
(284.72 mol)(62.07 g/mol) = 17,673 g = 17.673 kg.
(b) Now we are asked for the mass of the resulting polymer. Inasmuch as one mole of water is given off
for every repeat unit produced, this corresponds to 284.72 moles or (284.72 mol)(18.02 g/mol) = 5130 g or 5.130 kg
since the molecular weight of water is 18.02 g/mol. The mass of poly(ethylene terephthalate) is just the sum of the
masses of the two reactant materials [as computed in part (a)] minus the mass of water released, or
mass [poly(ethylene terephthalate)] = 47.300 kg + 17.673 kg − 5.130 kg = 59.843 kg](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-838-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
15.41 Nylon 6,6 may be formed by means of a condensation polymerization reaction in which
hexamethylene diamine [NH2—(CH2)6—NH2] and adipic acid react with one another with the formation of water
as a byproduct. What masses of hexamethylene diamine and adipic acid are necessary to yield 37.5 kg of completely
linear nylon 6,6? (Note: the chemical equation for this reaction is the answer to Concept Check 15.12.)
Solution
This problem asks for us to calculate the masses of hexamethylene diamine and adipic acid necessary to
yield 37.5 kg of completely linear nylon 6,6. The chemical equation for this reaction is the answer to Concept
Check 15.12, which is as follows:
From this equation we may calculate the molecular weights of these molecules.
MW(adipic) = 6( AC) + 10( AH) + 4( AO)
= 6(12.01 g/mol) + 10(1.008 g/mol) + 4(16.00 g/mol) = 146.14 g/mol
MW(hexamethylene) = 6(AC) + 16(AH) + 2(AN)
= 6(12.01 g/mol) + 16(1.008 g/mol) + 2(14.01 g/mol) = 116.21 g/mol
MW(nylon) = 12( AC) + 22( AH) + 2( AN) + 2( AO)](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-839-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
16.3 A large-particle composite consisting of tungsten particles within a copper matrix is to be prepared.
If the volume fractions of tungsten and copper are 0.60 and 0.40, respectively, estimate the upper limit for the
specific stiffness of this composite given the data that follow.
Specific Gravity Modulus of Elasticity
(GPa)
Copper 8.9 110
Tungsten 19.3 407
Solution
Given the elastic moduli and specific gravities for copper and tungsten we are asked to estimate the upper
limit for specific stiffness when the volume fractions of tungsten and copper are 0.60 and 0.40, respectively. There
are two approaches that may be applied to solve this problem. The first is to estimate both the upper limits of elastic
modulus [Ec(u)] and specific gravity (ρc) for the composite, using expressions of the form of Equation 16.1, and
then take their ratio. Using this approach
Ec(u) = ECuVCu + EWVW
= (110 GPa)(0.40) + (407 GPa)(0.60)
= 288 GPa
And
ρc = ρCuVCu + ρWVW
= (8.9)(0.40) + (19.3)(0.60) = 15.14
Therefore
Specific Stiffness =
Ec(u)
ρc
=
288 GPa
15.14
= 19.0 GPa
With the alternate approach, the specific stiffness is calculated, again employing a modification of
Equation 16.1, but using the specific stiffness-volume fraction product for both metals, as follows:](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-851-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
Influence of Fiber Orientation and Concentration
16.8 A continuous and aligned fiber-reinforced composite is to be produced consisting of 30 vol% aramid
fibers and 70 vol% of a polycarbonate matrix; mechanical characteristics of these two materials are as follows:
Modulus of Elasticity
[GPa (psi)]
Tensile Strength [MPa
(psi)]
Aramid fiber
131 (19 × 106
) 3600 (520,000)
Polycarbonate
2.4 (3.5 × 105
) 65 (9425)
Also, the stress on the polycarbonate matrix when the aramid fibers fail is 45 MPa (6500 psi).
For this composite, compute
(a) the longitudinal tensile strength, and
(b) the longitudinal modulus of elasticity
Solution
This problem calls for us to compute the longitudinal tensile strength and elastic modulus of an aramid
fiber-reinforced polycarbonate composite.
(a) The longitudinal tensile strength is determined using Equation 16.17 as
σcl
∗ = σm
' (1 − Vf ) + σ f
∗ Vf
= (45 MPa)(0.70) + (3600)(0.30)
= 1100 MPa (160,000 psi)
(b) The longitudinal elastic modulus is computed using Equation 16.10a as
Ecl = EmVm + Ef Vf
= (2.4 GPa)(0.70) + (131 GPa)(0.30)
= 41 GPa (5.95 × 106 psi)](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-857-320.jpg)
![Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to
students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted
by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
16.12 In an aligned and continuous glass fiber-reinforced nylon 6,6 composite, the fibers are to carry
94% of a load applied in the longitudinal direction.
(a) Using the data provided, determine the volume fraction of fibers that will be required.
(b) What will be the tensile strength of this composite? Assume that the matrix stress at fiber failure is 30
MPa (4350 psi).
Modulus of Elasticity
[GPa (psi)]
Tensile Strength
[MPa (psi)]
Glass fiber 72.5 (10.5 × 106
) 3400 (490,000)
Nylon 6,6 3.0 (4.35 × 105
) 76 (11,000)
Solution
(a) Given some data for an aligned and continuous glass-fiber-reinforced nylon 6,6 composite, we are
asked to compute the volume fraction of fibers that are required such that the fibers carry 94% of a load applied in
the longitudinal direction. From Equation 16.11
Ff
Fm
=
Ef Vf
EmVm
=
Ef Vf
Em (1 − Vf )
Now, using values for Ff and Fm from the problem statement
Ff
Fm
=
0.94
0.06
= 15.67
And when we substitute the given values for Ef and Em into the first equation leads to
Ff
Fm
= 15.67 =
(72.5 GPa)Vf
(3.0 GPa)(1 − Vf )
And, solving for Vf yields, Vf = 0.393.
(b) We are now asked for the tensile strength of this composite. From Equation 16.17,
σcl
∗ = σm
' (1 − Vf ) + σ f
∗ Vf](https://image.slidesharecdn.com/callistermaterialsscienceengineeringintroduction8thsolutionmanual-150426191503-conversion-gate01/85/Callister-materials-science_engineering_introduction_8th_solution_manual-863-320.jpg)
Callister materials science_engineering_introduction_8th_solution_manual
- 1. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 2 ATOMIC STRUCTURE AND INTERATOMIC BONDING PROBLEM SOLUTIONS Fundamental Concepts Electrons in Atoms 2.1 Cite the difference between atomic mass and atomic weight. Solution Atomic mass is the mass of an individual atom, whereas atomic weight is the average (weighted) of the atomic masses of an atom's naturally occurring isotopes.
- 2. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.2 Chromium has four naturally-occurring isotopes: 4.34% of 50 Cr, with an atomic weight of 49.9460 amu, 83.79% of 52 Cr, with an atomic weight of 51.9405 amu, 9.50% of 53 Cr, with an atomic weight of 52.9407 amu, and 2.37% of 54 Cr, with an atomic weight of 53.9389 amu. On the basis of these data, confirm that the average atomic weight of Cr is 51.9963 amu. Solution The average atomic weight of silicon (ACr) is computed by adding fraction-of-occurrence/atomic weight products for the three isotopes. Thus ACr = f50Cr A50Cr + f52Cr A52Cr + f53Cr A53Cr + f54Cr A54Cr = (0.0434)(49.9460 amu) + (0.8379)(51.9405 amu) + (0.0950)(52.9407 amu) + (0.0237)(53.9389 amu) = 51.9963 amu
- 3. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.3 (a) How many grams are there in one amu of a material? (b) Mole, in the context of this book, is taken in units of gram-mole. On this basis, how many atoms are there in a pound-mole of a substance? Solution (a) In order to determine the number of grams in one amu of material, appropriate manipulation of the amu/atom, g/mol, and atom/mol relationships is all that is necessary, as # g/amu = 1 mol 6.022 × 1023 atoms 1 g/mol 1 amu /atom = 1.66 × 10-24 g/amu (b) Since there are 453.6 g/lbm , 1 lb- mol = (453.6 g/lbm) (6.022 × 10 23 atoms/g - mol) = 2.73 × 1026 atoms/lb-mol
- 4. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.4 (a) Cite two important quantum-mechanical concepts associated with the Bohr model of the atom. (b) Cite two important additional refinements that resulted from the wave-mechanical atomic model. Solution (a) Two important quantum-mechanical concepts associated with the Bohr model of the atom are (1) that electrons are particles moving in discrete orbitals, and (2) electron energy is quantized into shells. (b) Two important refinements resulting from the wave-mechanical atomic model are (1) that electron position is described in terms of a probability distribution, and (2) electron energy is quantized into both shells and subshells--each electron is characterized by four quantum numbers.
- 5. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.5 Relative to electrons and electron states, what does each of the four quantum numbers specify? Solution The n quantum number designates the electron shell. The l quantum number designates the electron subshell. The ml quantum number designates the number of electron states in each electron subshell. The ms quantum number designates the spin moment on each electron.
- 6. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.6 Allowed values for the quantum numbers of electrons are as follows: n = 1, 2, 3, . . . l = 0, 1, 2, 3, . . . , n –1 ml = 0, ±1, ±2, ±3, . . . , ±l ms = ± 1 2 The relationships between n and the shell designations are noted in Table 2.1. Relative to the subshells, l = 0 corresponds to an s subshell l = 1 corresponds to a p subshell l = 2 corresponds to a d subshell l = 3 corresponds to an f subshell For the K shell, the four quantum numbers for each of the two electrons in the 1s state, in the order of nlmlms, are 100( 1 2 ) and 100( − 1 2 ). Write the four quantum numbers for all of the electrons in the L and M shells, and note which correspond to the s, p, and d subshells. Solution For the L state, n = 2, and eight electron states are possible. Possible l values are 0 and 1, while possible ml values are 0 and ±1; and possible ms values are ± 1 2 . Therefore, for the s states, the quantum numbers are 200( 1 2 ) and 200(− 1 2 ). For the p states, the quantum numbers are 210( 1 2 ), 210(− 1 2 ), 211( 1 2 ), 211(− 1 2 ), 21(−1)( 1 2 ), and 21(−1)(− 1 2 ). For the M state, n = 3, and 18 states are possible. Possible l values are 0, 1, and 2; possible ml values are 0, ±1, and ±2; and possible ms values are ± 1 2 . Therefore, for the s states, the quantum numbers are 300( 1 2 ), 300(− 1 2 ), for the p states they are 310( 1 2 ), 310(− 1 2 ), 311( 1 2 ), 311(− 1 2 ), 31(−1)( 1 2 ), and 31(−1)(− 1 2 ); for the d states they are 320( 1 2 ), 320(− 1 2 ), 321( 1 2 ), 321(− 1 2 ), 32(−1)( 1 2 ), 32(−1)(− 1 2 ), 322( 1 2 ), 322(− 1 2 ), 32(−2)( 1 2 ), and 32(−2)(− 1 2 ).
- 7. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.7 Give the electron configurations for the following ions: Fe2+ , Al3+ , Cu+ , Ba2+ , Br- , and O2- . Solution The electron configurations for the ions are determined using Table 2.2 (and Figure 2.6). Fe2+ : From Table 2.2, the electron configuration for an atom of iron is 1s2 2s2 2p6 3s2 3p6 3d6 4s2 . In order to become an ion with a plus two charge, it must lose two electrons—in this case the two 4s. Thus, the electron configuration for an Fe2+ ion is 1s2 2s2 2p6 3s2 3p6 3d6 . Al3+ : From Table 2.2, the electron configuration for an atom of aluminum is 1s2 2s2 2p6 3s2 3p1 . In order to become an ion with a plus three charge, it must lose three electrons—in this case two 3s and the one 3p. Thus, the electron configuration for an Al3+ ion is 1s2 2s2 2p6 . Cu+ : From Table 2.2, the electron configuration for an atom of copper is 1s2 2s2 2p6 3s2 3p6 3d10 4s1 . In order to become an ion with a plus one charge, it must lose one electron—in this case the 4s. Thus, the electron configuration for a Cu+ ion is 1s2 2s2 2p6 3s2 3p6 3d10 . Ba2+ : The atomic number for barium is 56 (Figure 2.6), and inasmuch as it is not a transition element the electron configuration for one of its atoms is 1s2 2s2 2p6 3s2 3p6 3d10 4s2 4p6 4d10 5s2 5p6 6s2 . In order to become an ion with a plus two charge, it must lose two electrons—in this case two the 6s. Thus, the electron configuration for a Ba2+ ion is 1s2 2s2 2p6 3s2 3p6 3d10 4s2 4p6 4d10 5s2 5p6 . Br- : From Table 2.2, the electron configuration for an atom of bromine is 1s2 2s2 2p6 3s2 3p6 3d10 4s2 4p5 . In order to become an ion with a minus one charge, it must acquire one electron—in this case another 4p. Thus, the electron configuration for a Br- ion is 1s2 2s2 2p6 3s2 3p6 3d10 4s2 4p6 . O2- : From Table 2.2, the electron configuration for an atom of oxygen is 1s2 2s2 2p4 . In order to become an ion with a minus two charge, it must acquire two electrons—in this case another two 2p. Thus, the electron configuration for an O2- ion is 1s2 2s2 2p6 .
- 8. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.8 Sodium chloride (NaCl) exhibits predominantly ionic bonding. The Na+ and Cl- ions have electron structures that are identical to which two inert gases? Solution The Na + ion is just a sodium atom that has lost one electron; therefore, it has an electron configuration the same as neon (Figure 2.6). The Cl - ion is a chlorine atom that has acquired one extra electron; therefore, it has an electron configuration the same as argon.
- 9. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The Periodic Table 2.9 With regard to electron configuration, what do all the elements in Group VIIA of the periodic table have in common? Solution Each of the elements in Group VIIA has five p electrons.
- 10. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.10 To what group in the periodic table would an element with atomic number 114 belong? Solution From the periodic table (Figure 2.6) the element having atomic number 114 would belong to group IVA. According to Figure 2.6, Ds, having an atomic number of 110 lies below Pt in the periodic table and in the right- most column of group VIII. Moving four columns to the right puts element 114 under Pb and in group IVA.
- 11. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.11 Without consulting Figure 2.6 or Table 2.2, determine whether each of the electron configurations given below is an inert gas, a halogen, an alkali metal, an alkaline earth metal, or a transition metal. Justify your choices. (a) 1s2 2s2 2p6 3s2 3p6 3d7 4s2 (b) 1s2 2s2 2p6 3s2 3p6 (c) 1s2 2s2 2p5 (d) 1s2 2s2 2p6 3s2 (e) 1s2 2s2 2p6 3s2 3p6 3d2 4s2 (f) 1s2 2s2 2p6 3s2 3p6 4s1 Solution (a) The 1s2 2s2 2p6 3s2 3p6 3d7 4s2 electron configuration is that of a transition metal because of an incomplete d subshell. (b) The 1s2 2s2 2p6 3s2 3p6 electron configuration is that of an inert gas because of filled 3s and 3p subshells. (c) The 1s2 2s2 2p5 electron configuration is that of a halogen because it is one electron deficient from having a filled L shell. (d) The 1s2 2s2 2p6 3s2 electron configuration is that of an alkaline earth metal because of two s electrons. (e) The 1s2 2s2 2p6 3s2 3p6 3d2 4s2 electron configuration is that of a transition metal because of an incomplete d subshell. (f) The 1s2 2s2 2p6 3s2 3p6 4s1 electron configuration is that of an alkali metal because of a single s electron.
- 12. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.12 (a) What electron subshell is being filled for the rare earth series of elements on the periodic table? (b) What electron subshell is being filled for the actinide series? Solution (a) The 4f subshell is being filled for the rare earth series of elements. (b) The 5f subshell is being filled for the actinide series of elements.
- 13. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Bonding Forces and Energies 2.13 Calculate the force of attraction between a K+ and an O2- ion the centers of which are separated by a distance of 1.5 nm. Solution The attractive force between two ions FA is just the derivative with respect to the interatomic separation of the attractive energy expression, Equation 2.8, which is just FA = dEA dr = d − A r dr = A r2 The constant A in this expression is defined in footnote 3. Since the valences of the K+ and O2- ions (Z1 and Z2 ) are +1 and -2, respectively, Z1 = 1 and Z2 = 2, then FA = (Z1e) (Z2e) 4πε0r2 = (1)(2)(1.602 × 10−19 C)2 (4)(π) (8.85 × 10−12 F/m) (1.5 × 10−9 m)2 = 2.05 × 10-10 N
- 14. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.14 The net potential energy between two adjacent ions, EN, may be represented by the sum of Equations 2.8 and 2.9; that is, EN = − A r + B rn Calculate the bonding energy E0 in terms of the parameters A, B, and n using the following procedure: 1. Differentiate EN with respect to r, and then set the resulting expression equal to zero, since the curve of EN versus r is a minimum at E0. 2. Solve for r in terms of A, B, and n, which yields r0, the equilibrium interionic spacing. 3. Determine the expression for E0 by substitution of r0 into Equation 2.11. Solution (a) Differentiation of Equation 2.11 yields dEN dr = d − A r dr + d B rn dr = A r(1 + 1) − nB r(n + 1) = 0 (b) Now, solving for r (= r0 ) A r0 2 = nB r0 (n + 1) or r0 = A nB 1/(1 - n) (c) Substitution for r0 into Equation 2.11 and solving for E (= E0 ) E0 = − A r0 + B r0 n = − A A nB 1/(1 - n) + B A nB n/(1 - n)
- 15. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.15 For a K+ –Cl– ion pair, attractive and repulsive energies EA and ER , respectively, depend on the distance between the ions r, according to EA = − 1.436 r ER = 5.8 × 10−6 r9 For these expressions, energies are expressed in electron volts per K+ –Cl– pair, and r is the distance in nanometers. The net energy EN is just the sum of the two expressions above. (a) Superimpose on a single plot EN, ER, and EA versus r up to 1.0 nm. (b) On the basis of this plot, determine (i) the equilibrium spacing r0 between the K+ and Cl– ions, and (ii) the magnitude of the bonding energy E0 between the two ions. (c) Mathematically determine the r0 and E0 values using the solutions to Problem 2.14 and compare these with the graphical results from part (b). Solution (a) Curves of EA , ER , and EN are shown on the plot below. (b) From this plot r0 = 0.28 nm E0 = – 4.6 eV
- 16. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (c) From Equation 2.11 for EN A = 1.436 B = 5.86 × 10-6 n = 9 Thus, r0 = A nB 1/(1 - n) = 1.436 (8)(5.86 × 10-6) 1/(1 - 9) = 0.279 nm and E0 = − A A nB 1/(1 - n) + B A nB n/(1 - n) = − 1.436 1.436 (9)(5.86 × 10−6) 1/(1 − 9) + 5.86 × 10−6 1.436 (9)(5.86 × 10−6) 9/(1 − 9) = – 4.57 eV
- 17. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.16 Consider a hypothetical X+ -Y- ion pair for which the equilibrium interionic spacing and bonding energy values are 0.35 nm and -6.13 eV, respectively. If it is known that n in Equation 2.11 has a value of 10, using the results of Problem 2.14, determine explicit expressions for attractive and repulsive energies EA and ER of Equations 2.8 and 2.9. Solution This problem gives us, for a hypothetical X+-Y- ion pair, values for r0 (0.35 nm), E0 (– 6.13 eV), and n (10), and asks that we determine explicit expressions for attractive and repulsive energies of Equations 2.8 and 2.9. In essence, it is necessary to compute the values of A and B in these equations. Expressions for r0 and E0 in terms of n, A, and B were determined in Problem 2.14, which are as follows: r0 = A nB 1/(1 - n) E0 = − A A nB 1/(1 - n) + B A nB n/(1 - n) Thus, we have two simultaneous equations with two unknowns (viz. A and B). Upon substitution of values for r0 and E0 in terms of n, these equations take the forms 0.35 nm = A 10 B 1/(1 - 10) = A 10 B -1/9 and − 6.13 eV = − A A 10B 1/(1 − 10) + B A 10B 10/(1 − 10) = − A A 10B −1/ 9 + B A 10B −10/ 9 We now want to solve these two equations simultaneously for values of A and B. From the first of these two equations, solving for A/8B leads to
- 18. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. A 10B = (0.35 nm)-9 Furthermore, from the above equation the A is equal to A = 10B(0.35 nm)-9 When the above two expressions for A/10B and A are substituted into the above expression for E0 (- 6.13 eV), the following results −6.13 eV = = − A A 10B −1/ 9 + B A 10B −10/ 9 = − 10B(0.35 nm)-9 (0.35 nm)-9 [ ] −1/ 9 + B (0.35 nm)-9 [ ] −10/ 9 = − 10B(0.35 nm)-9 0.35 nm + B (0.35 nm)10 Or −6.13 eV = = − 10B (0.35 nm)10 + B (0.35 nm)10 = − 9B (0.35 nm)10 Solving for B from this equation yields B = 1.88 × 10-5 eV- nm10 Furthermore, the value of A is determined from one of the previous equations, as follows: A = 10B(0.35 nm)-9 = (10)(1.88 × 10-5 eV- nm10)(0.35 nm)-9 = 2.39 eV- nm Thus, Equations 2.8 and 2.9 become
- 19. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. EA = − 2.39 r ER = 1.88 × 10−5 r10 Of course these expressions are valid for r and E in units of nanometers and electron volts, respectively.
- 20. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.17 The net potential energy EN between two adjacent ions is sometimes represented by the expression EN = − C r + DÊexp − r ρ (2.12) in which r is the interionic separation and C, D, and ρ are constants whose values depend on the specific material. (a) Derive an expression for the bonding energy E0 in terms of the equilibrium interionic separation r0 and the constants D and ρ using the following procedure: 1. Differentiate EN with respect to r and set the resulting expression equal to zero. 2. Solve for C in terms of D, ρ, and r0. 3. Determine the expression for E0 by substitution for C in Equation 2.12. (b) Derive another expression for E0 in terms of r0, C, and ρ using a procedure analogous to the one outlined in part (a). Solution (a) Differentiating Equation 2.12 with respect to r yields dE dr = d − C r dr − d D exp − r ρ dr = C r2 − De−r /ρ ρ At r = r0 , dE/dr = 0, and C r0 2 = De−(r0/ρ) ρ (2.12b) Solving for C and substitution into Equation 2.12 yields an expression for E0 as E0 = De−(r0/ρ) 1 − r0 ρ (b) Now solving for D from Equation 2.12b above yields D = Cρ e (r0/ρ) r0 2
- 21. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Substitution of this expression for D into Equation 2.12 yields an expression for E0 as E0 = C r0 ρ r0 − 1
- 22. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Primary Interatomic Bonds 2.18 (a) Briefly cite the main differences between ionic, covalent, and metallic bonding. (b) State the Pauli exclusion principle. Solution (a) The main differences between the various forms of primary bonding are: Ionic--there is electrostatic attraction between oppositely charged ions. Covalent--there is electron sharing between two adjacent atoms such that each atom assumes a stable electron configuration. Metallic--the positively charged ion cores are shielded from one another, and also "glued" together by the sea of valence electrons. (b) The Pauli exclusion principle states that each electron state can hold no more than two electrons, which must have opposite spins.
- 23. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.19 Compute the percents ionic character of the interatomic bonds for the following compounds: TiO2, ZnTe, CsCl, InSb, and MgCl2. Solution The percent ionic character is a function of the electron negativities of the ions XA and XB according to Equation 2.10. The electronegativities of the elements are found in Figure 2.7. For TiO2 , XTi = 1.5 and XO = 3.5, and therefore, %IC = 1 − e(−0.25)(3.5−1.5)2 × 100 = 63.2% For ZnTe, XZn = 1.6 and XTe = 2.1, and therefore, %IC = 1 − e(−0.25)(2.1−1.6)2 × 100 = 6.1% For CsCl, XCs = 0.7 and XCl = 3.0, and therefore, %IC = 1 − e(−0.25)(3.0−0.7)2 × 100 = 73.4% For InSb, XIn = 1.7 and XSb = 1.9, and therefore, %IC = 1 − e(−0.25)(1.9−1.7)2 × 100 = 1.0% For MgCl2 , XMg = 1.2 and XCl = 3.0, and therefore, %IC = 1 − e(−0.25)(3.0−1.2)2 × 100 = 55.5%
- 24. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.20 Make a plot of bonding energy versus melting temperature for the metals listed in Table 2.3. Using this plot, approximate the bonding energy for copper, which has a melting temperature of 1084°C. Solution Below is plotted the bonding energy versus melting temperature for these four metals. From this plot, the bonding energy for copper (melting temperature of 1084°C) should be approximately 3.6 eV. The experimental value is 3.5 eV.
- 25. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.21 Using Table 2.2, determine the number of covalent bonds that are possible for atoms of the following elements: germanium, phosphorus, selenium, and chlorine. Solution For germanium, having the valence electron structure 4s24p2, N' = 4; thus, there are 8 – N' = 4 covalent bonds per atom. For phosphorus, having the valence electron structure 3s23p3, N' = 5; thus, there is 8 – N' = 3 covalent bonds per atom. For selenium, having the valence electron structure 4s24p4, N' = 6; thus, there are 8 – N' = 2 covalent bonds per atom. For chlorine, having the valence electron structure 3s23p5, N' = 7; thus, there are 8 – N' = 1 covalent bond per atom.
- 26. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.22 What type(s) of bonding would be expected for each of the following materials: brass (a copper-zinc alloy), rubber, barium sulfide (BaS), solid xenon, bronze, nylon, and aluminum phosphide (AlP)? Solution For brass, the bonding is metallic since it is a metal alloy. For rubber, the bonding is covalent with some van der Waals. (Rubber is composed primarily of carbon and hydrogen atoms.) For BaS, the bonding is predominantly ionic (but with some covalent character) on the basis of the relative positions of Ba and S in the periodic table. For solid xenon, the bonding is van der Waals since xenon is an inert gas. For bronze, the bonding is metallic since it is a metal alloy (composed of copper and tin). For nylon, the bonding is covalent with perhaps some van der Waals. (Nylon is composed primarily of carbon and hydrogen.) For AlP the bonding is predominantly covalent (but with some ionic character) on the basis of the relative positions of Al and P in the periodic table.
- 27. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Secondary Bonding or van der Waals Bonding 2.23 Explain why hydrogen fluoride (HF) has a higher boiling temperature than hydrogen chloride (HCl) (19.4 vs. –85°C), even though HF has a lower molecular weight. Solution The intermolecular bonding for HF is hydrogen, whereas for HCl, the intermolecular bonding is van der Waals. Since the hydrogen bond is stronger than van der Waals, HF will have a higher melting temperature.
- 28. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 3 THE STRUCTURE OF CRYSTALLINE SOLIDS PROBLEM SOLUTIONS Fundamental Concepts 3.1 What is the difference between atomic structure and crystal structure? Solution Atomic structure relates to the number of protons and neutrons in the nucleus of an atom, as well as the number and probability distributions of the constituent electrons. On the other hand, crystal structure pertains to the arrangement of atoms in the crystalline solid material.
- 29. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Unit Cells Metallic Crystal Structures 3.2 If the atomic radius of aluminum is 0.143 nm, calculate the volume of its unit cell in cubic meters. Solution For this problem, we are asked to calculate the volume of a unit cell of aluminum. Aluminum has an FCC crystal structure (Table 3.1). The FCC unit cell volume may be computed from Equation 3.4 as VC = 16R3 2 = (16)(0.143 × 10-9 m)3( 2) = 6.62 × 10-29 m3
- 30. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.3 Show for the body-centered cubic crystal structure that the unit cell edge length a and the atomic radius R are related through a =4R/ 3 . Solution Consider the BCC unit cell shown below Using the triangle NOP (NP)2 = a2 + a2 = 2a2 And then for triangle NPQ, (NQ)2 = (QP)2 + (NP)2 But NQ = 4R, R being the atomic radius. Also, QP = a. Therefore, (4R)2 = a2 + 2a2 or a = 4R 3
- 31. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.4 For the HCP crystal structure, show that the ideal c/a ratio is 1.633. Solution A sketch of one-third of an HCP unit cell is shown below. Consider the tetrahedron labeled as JKLM, which is reconstructed as The atom at point M is midway between the top and bottom faces of the unit cell--that is MH = c/2. And, since atoms at points J, K, and M, all touch one another, JM = JK = 2R = a where R is the atomic radius. Furthermore, from triangle JHM, (JM)2 = (JH)2 + (MH)2 or
- 32. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. a2 = (JH )2 + c 2 2 Now, we can determine the JH length by consideration of triangle JKL, which is an equilateral triangle, cos 30° = a /2 JH = 3 2 and JH = a 3 Substituting this value for JH in the above expression yields a2 = a 3 2 + c 2 2 = a2 3 + c2 4 and, solving for c/a c a = 8 3 = 1.633
- 33. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.5 Show that the atomic packing factor for BCC is 0.68. Solution The atomic packing factor is defined as the ratio of sphere volume to the total unit cell volume, or APF = VS VC Since there are two spheres associated with each unit cell for BCC VS = 2(sphere volume) = 2 4πR3 3 = 8πR3 3 Also, the unit cell has cubic symmetry, that is VC = a3. But a depends on R according to Equation 3.3, and VC = 4R 3 3 = 64R3 3 3 Thus, APF = VS VC = 8π R3 /3 64R3 /3 3 = 0.68
- 34. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.6 Show that the atomic packing factor for HCP is 0.74. Solution The APF is just the total sphere volume-unit cell volume ratio. For HCP, there are the equivalent of six spheres per unit cell, and thus VS = 6 4π R3 3 = 8π R3 Now, the unit cell volume is just the product of the base area times the cell height, c. This base area is just three times the area of the parallelepiped ACDE shown below. The area of ACDE is just the length of CD times the height BC . But CD is just a or 2R, and BC = 2R cos (30°) = 2 R 3 2 Thus, the base area is just AREA = (3)(CD)(BC) = (3)(2R) 2R 3 2 = 6R2 3 and since c = 1.633a = 2R(1.633) VC = (AREA)(c) = 6R2c 3 (3.S1)
- 35. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (6R2 3)(2)(1.633)R = 12 3 (1.633) R3 Thus, APF = VS VC = 8π R3 12 3 (1.633) R3 = 0.74
- 36. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Density Computations 3.7 Iron has a BCC crystal structure, an atomic radius of 0.124 nm, and an atomic weight of 55.85 g/mol. Compute and compare its theoretical density with the experimental value found inside the front cover. Solution This problem calls for a computation of the density of iron. According to Equation 3.5 ρ = nAFe VCNA For BCC, n = 2 atoms/unit cell, and VC = 4 R 3 3 Thus, ρ = nAFe 4 R 3 3 NA = (2 atoms/unit cell)(55.85 g/mol) (4)(0.124 × 10-7 cm)/ 3[ ] 3 /(unit cell)(6.022 × 1023 atoms/mol) = 7.90 g/cm3 The value given inside the front cover is 7.87 g/cm3.
- 37. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.8 Calculate the radius of an iridium atom, given that Ir has an FCC crystal structure, a density of 22.4 g/cm3 , and an atomic weight of 192.2 g/mol. Solution We are asked to determine the radius of an iridium atom, given that Ir has an FCC crystal structure. For FCC, n = 4 atoms/unit cell, and VC = 16R3 2 (Equation 3.4). Now, ρ = nAIr VC NA = nAIr (16R3 2)NA And solving for R from the above expression yields R = nAIr 16ρNA 2 1/3 = (4 atoms/unit cell) 192.2 g/mol( ) (16)(22.4 g/cm3)(6.022 × 1023 atoms/mol)( 2) 1/3 = 1.36 × 10-8 cm = 0.136 nm
- 38. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.9 Calculate the radius of a vanadium atom, given that V has a BCC crystal structure, a density of 5.96 g/cm3 , and an atomic weight of 50.9 g/mol. Solution This problem asks for us to calculate the radius of a vanadium atom. For BCC, n = 2 atoms/unit cell, and VC = 4R 3 3 = 64R3 3 3 Since, from Equation 3.5 ρ = nAV VC NA = nAV 64 R3 3 3 NA and solving for R the previous equation R = 3 3nAV 64ρ NA 1/3 and incorporating values of parameters given in the problem statement R = (3 3)(2 atoms/unit cell) (50.9 g/mol) (64)(5.96 g/cm3)(6.022 × 1023 atoms/mol) 1/3 = 1.32 × 10-8 cm = 0.132 nm
- 39. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.10 Some hypothetical metal has the simple cubic crystal structure shown in Figure 3.24. If its atomic weight is 70.4 g/mol and the atomic radius is 0.126 nm, compute its density. Solution For the simple cubic crystal structure, the value of n in Equation 3.5 is unity since there is only a single atom associated with each unit cell. Furthermore, for the unit cell edge length, a = 2R (Figure 3.24). Therefore, employment of Equation 3.5 yields ρ = nA VC NA = nA (2 R)3 NA and incorporating values of the other parameters provided in the problem statement leads to ρ = (1 atom/unit cell)(70.4 g/mol) (2)(1.26 × 10 -8 cm) 3 /(unit cell) (6.022 × 1023 atoms/mol) 7.31 g/cm3
- 40. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.11 Zirconium has an HCP crystal structure and a density of 6.51 g/cm3 . (a) What is the volume of its unit cell in cubic meters? (b) If the c/a ratio is 1.593, compute the values of c and a. Solution (a) The volume of the Zr unit cell may be computed using Equation 3.5 as VC = nAZr ρNA Now, for HCP, n = 6 atoms/unit cell, and for Zr, AZr = 91.22 g/mol. Thus, VC = (6 atoms/unit cell)(91.22 g/mol) (6.51 g/cm3)(6.022 × 1023 atoms/mol) = 1.396 × 10-22 cm3 /unit cell = 1.396 × 10-28 m3 /unit cell (b) From Equation 3.S1 of the solution to Problem 3.6, for HCP VC = 6R2c 3 But, since a = 2R, (i.e., R = a/2) then VC = 6 a 2 2 c 3 = 3 3 a2c 2 but, since c = 1.593a VC = 3 3 (1.593) a3 2 = 1.396 × 10-22 cm3/unit cell Now, solving for a a = (2)(1.396 × 10-22 cm3) (3)( 3)(1.593) 1/3
- 41. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = 3.23 × 10-8 cm = 0.323 nm And finally c = 1.593a = (1.593)(0.323 nm) = 0.515 nm
- 42. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.12 Using atomic weight, crystal structure, and atomic radius data tabulated inside the front cover, compute the theoretical densities of lead, chromium, copper, and cobalt, and then compare these values with the measured densities listed in this same table. The c/a ratio for cobalt is 1.623. Solution Since Pb has an FCC crystal structure, n = 4, and VC = 16R3 2 (Equation 3.4). Also, R = 0.175 nm (1.75 × 10-8 cm) and APb = 207.2 g/mol. Employment of Equation 3.5 yields ρ = nAPb VC NA = (4 atoms/unit cell)(207.2 g/mol) (16)(1.75 × 10-8 cm)3( 2)[ ]/(unit cell){ }(6.022 × 1023 atoms/mol) = 11.35 g/cm3 The value given in the table inside the front cover is 11.35 g/cm3. Chromium has a BCC crystal structure for which n = 2 and VC = a3 = 4 R 3 3 (Equation 3.3); also ACr = 52.00g/mol and R = 0.125 nm. Therefore, employment of Equation 3.5 leads to ρ = (2 atoms/unit cell)(52.00 g/mol) (4)(1.25 × 10-8 cm) 3 3 /(unit cell) (6.022 × 1023 atoms/mol) = 7.18 g/cm3 The value given in the table is 7.19 g/cm3. Copper also has an FCC crystal structure and therefore ρ = (4 atoms/unit cell)(63.55 g/mol) (2)(1.28 × 10-8 cm)( 2)[ ] 3 /(unit cell) (6.022 × 1023 atoms/mol) = 8.90 g/cm3
- 43. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The value given in the table is 8.90 g/cm3 . Cobalt has an HCP crystal structure, and from the solution to Problem 3.6 (Equation 3.S1), VC = 6R2c 3 and, since c = 1.623a and a = 2R, c = (1.623)(2R); hence VC = 6R2 (1.623)(2R) 3 = (19.48)( 3)R3 = (19.48)( 3)(1.25 × 10−8 cm)3 = 6.59 × 10−23 cm3/unit cell Also, there are 6 atoms/unit cell for HCP. Therefore the theoretical density is ρ = nACo VC NA = (6 atoms/unit cell)(58.93 g/mol) (6.59 × 10-23 cm3/unit cell)(6.022 × 1023 atoms/mol) = 8.91 g/cm3 The value given in the table is 8.9 g/cm3.
- 44. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.13 Rhodium has an atomic radius of 0.1345 nm and a density of 12.41 g/cm3 . Determine whether it has an FCC or BCC crystal structure. Solution In order to determine whether Rh has an FCC or a BCC crystal structure, we need to compute its density for each of the crystal structures. For FCC, n = 4, and a = 2R 2 (Equation 3.1). Also, from Figure 2.6, its atomic weight is 102.91 g/mol. Thus, for FCC (employing Equation 3.5) ρ = nARh a3NA = nARh (2R 2)3NA = (4 atoms/unit cell)(102.91 g/mol) (2)(1.345 × 10-8 cm)( 2)[ ] 3 /(unit cell) (6.022 × 1023 atoms /mol) = 12.41 g/cm3 which is the value provided in the problem statement. Therefore, Rh has the FCC crystal structure.
- 45. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.14 Below are listed the atomic weight, density, and atomic radius for three hypothetical alloys. For each determine whether its crystal structure is FCC, BCC, or simple cubic and then justify your determination. A simple cubic unit cell is shown in Figure 3.24. Alloy Atomic Weight Density Atomic Radius (g/mol) (g/cm3 ) (nm) A 77.4 8.22 0.125 B 107.6 13.42 0.133 C 127.3 9.23 0.142 Solution For each of these three alloys we need, by trial and error, to calculate the density using Equation 3.5, and compare it to the value cited in the problem. For SC, BCC, and FCC crystal structures, the respective values of n are 1, 2, and 4, whereas the expressions for a (since VC = a3) are 2R, 2 R 2 , and 4R 3 . For alloy A, let us calculate ρ assuming a simple cubic crystal structure. ρ = nAA VC NA = nAA 2R( )3 NA = (1 atom/unit cell)(77.4 g/mol) (2)(1.25 × 10−8)[ ] 3 /(unit cell) (6.022 × 1023 atoms/mol) = 8.22 g/cm3 Therefore, its crystal structure is simple cubic. For alloy B, let us calculate ρ assuming an FCC crystal structure. ρ = nAB (2R 2)3 NA
- 46. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (4 atoms/unit cell)(107.6 g/mol) 2 2( )(1.33 × 10-8 cm)[ ] 3 /(unit cell) (6.022 × 1023 atoms/mol) = 13.42 g/cm3 Therefore, its crystal structure is FCC. For alloy C, let us calculate ρ assuming a simple cubic crystal structure. = nAC 2R( )3 NA = (1 atom/unit cell)(127.3 g/mol) (2)(1.42 × 10-8 cm)[ ] 3 /(unit cell) (6.022 × 1023 atoms/mol) = 9.23 g/cm3 Therefore, its crystal structure is simple cubic.
- 47. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.15 The unit cell for tin has tetragonal symmetry, with a and b lattice parameters of 0.583 and 0.318 nm, respectively. If its density, atomic weight, and atomic radius are 7.30 g/cm3 , 118.69 g/mol, and 0.151 nm, respectively, compute the atomic packing factor. Solution In order to determine the APF for Sn, we need to compute both the unit cell volume (VC ) which is just the a2 c product, as well as the total sphere volume (VS ) which is just the product of the volume of a single sphere and the number of spheres in the unit cell (n). The value of n may be calculated from Equation 3.5 as n = ρVC NA ASn = (7.30 g/cm3)(5.83)2 (3.18)(× 10-24 cm3)(6.022 × 1023 atoms /mol) 118.69 g/mol = 4.00 atoms/unit cell Therefore APF = VS VC = (4) 4 3 π R3 (a)2 (c) = (4) 4 3 (π)(1.51 × 10-8 cm)3 (5.83 × 10-8 cm)2 (3.18 × 10-8 cm) = 0.534
- 48. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.16 Iodine has an orthorhombic unit cell for which the a, b, and c lattice parameters are 0.479, 0.725, and 0.978 nm, respectively. (a) If the atomic packing factor and atomic radius are 0.547 and 0.177 nm, respectively, determine the number of atoms in each unit cell. (b) The atomic weight of iodine is 126.91 g/mol; compute its theoretical density. Solution (a) For indium, and from the definition of the APF APF = VS VC = n 4 3 π R3 abc we may solve for the number of atoms per unit cell, n, as n = (APF) abc 4 3 π R3 Incorporating values of the above parameters provided in the problem state leads to = (0.547)(4.79 × 10-8 cm)(7.25 × 10-8 cm)(9.78 × 10-8 cm) 4 3 π (1.77 × 10-8 cm)3 = 8.0 atoms/unit cell (b) In order to compute the density, we just employ Equation 3.5 as ρ = nAI abc NA = (8 atoms/unit cell)(126.91 g/mol) (4.79 × 10-8 cm)(7.25 × 10-8 cm)(9.78 × 10-8 cm)[ ]/unit cell{ }(6.022 × 1023 atoms/mol) = 4.96 g/cm3
- 49. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3. 17 Titanium has an HCP unit cell for which the ratio of the lattice parameters c/a is 1.58. If the radius of the Ti atom is 0.1445 nm, (a) determine the unit cell volume, and (b) calculate the density of Ti and compare it with the literature value. Solution (a) We are asked to calculate the unit cell volume for Ti. For HCP, from Equation 3.S1 (found in the solution to Problem 3.6) VC = 6 R2c 3 But for Ti, c = 1.58a, and a = 2R, or c = 3.16R, and VC = (6)(3.16) R3 3 = (6) (3.16)( 3) 1.445 × 10-8 cm[ ] 3 = 9.91 × 10−23 cm3/unit cell (b) The theoretical density of Ti is determined, using Equation 3.5, as follows: ρ = nATi VC NA For HCP, n = 6 atoms/unit cell, and for Ti, ATi = 47.87 g/mol (as noted inside the front cover). Thus, ρ = (6 atoms/unit cell)(47.87 g/mol) (9.91 × 10-23 cm3/unit cell)(6.022 × 1023 atoms/mol) = 4.81 g/cm3 The value given in the literature is 4.51 g/cm3.
- 50. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.18 Zinc has an HCP crystal structure, a c/a ratio of 1.856, and a density of 7.13 g/cm3 . Compute the atomic radius for Zn. Solution In order to calculate the atomic radius for Zn, we must use Equation 3.5, as well as the expression which relates the atomic radius to the unit cell volume for HCP; Equation 3.S1 (from Problem 3.6) is as follows: VC = 6 R2c 3 In this case c = 1.856a, but, for HCP, a = 2R, which means that VC = 6R2 (1.856)(2R) 3 = (1.856)(12 3)R3 And from Equation 3.5, the density is equal to ρ = nAZn VC NA = nAZn (1.856)(12 3)R3NA And, solving for R from the above equation leads to the following: R = nAZn (1.856)(12 3) ρ NA 1/3 And incorporating appropriate values for the parameters in this equation leads to R = (6 atoms/unit cell) (65.41 g/mol) (1.856)(12 3)(7.13 g/cm3)(6.022 × 1023 atoms/mol) 1/3 = 1.33 × 10-8 cm = 0.133 nm
- 51. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.19 Rhenium has an HCP crystal structure, an atomic radius of 0.137 nm, and a c/a ratio of 1.615. Compute the volume of the unit cell for Re. Solution In order to compute the volume of the unit cell for Re, it is necessary to use Equation 3.S1 (found in Problem 3.6), that is VC = 6 R2c 3 The problem states that c = 1.615a, and a = 2R. Therefore VC = (1.615)(12 3) R3 = (1.615)(12 3)(1.37 × 10-8 cm)3 = 8.63 × 10-23 cm3 = 8.63 × 10-2 nm3
- 52. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Crystal Systems 3.20 Below is a unit cell for a hypothetical metal. (a) To which crystal system does this unit cell belong? (b) What would this crystal structure be called? (c) Calculate the density of the material, given that its atomic weight is 141 g/mol. Solution (a) The unit cell shown in the problem statement belongs to the tetragonal crystal system since a = b = 0.30 nm, c = 0.40 nm, and α = β = γ = 90°. (b) The crystal structure would be called body-centered tetragonal. (c) As with BCC, n = 2 atoms/unit cell. Also, for this unit cell VC = (3.0 × 10−8 cm)2(4.0 × 10−8 cm) = 3.60 × 10−23 cm3/unit cell Thus, using Equation 3.5, the density is equal to ρ = nA VC NA = (2 atoms/unit cell) (141 g/mol) (3.60 × 10-23 cm3/unit cell)(6.022 × 1023 atoms/mol) = 13.0 g/cm3
- 53. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.21 Sketch a unit cell for the body-centered orthorhombic crystal structure. Solution A unit cell for the body-centered orthorhombic crystal structure is presented below.
- 54. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Point Coordinates 3.22 List the point coordinates for all atoms that are associated with the FCC unit cell (Figure 3.1). Solution From Figure 3.1b, the atom located of the origin of the unit cell has the coordinates 000. Coordinates for other atoms in the bottom face are 100, 110, 010, and 1 2 1 2 0. (The z coordinate for all these points is zero.) For the top unit cell face, the coordinates are 001, 101, 111, 011, and 1 2 1 2 1. Coordinates for those atoms that are positioned at the centers of both side faces, and centers of both front and back faces need to be specified. For the front and back-center face atoms, the coordinates are 1 1 2 1 2 and 0 1 2 1 2 , respectively. While for the left and right side center-face atoms, the respective coordinates are 1 2 0 1 2 and 1 2 1 1 2 .
- 55. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.23 List the point coordinates of the titanium, barium, and oxygen ions for a unit cell of the perovskite crystal structure (Figure 12.6). Solution In Figure 12.6, the barium ions are situated at all corner positions. The point coordinates for these ions are as follows: 000, 100, 110, 010, 001, 101, 111, and 011. The oxygen ions are located at all face-centered positions; therefore, their coordinates are 1 2 1 2 0, 1 2 1 2 1, 1 1 2 1 2 , 0 1 2 1 2 , 1 2 0 1 2 , and 1 2 1 1 2 . And, finally, the titanium ion resides at the center of the cubic unit cell, with coordinates 1 2 1 2 1 2 .
- 56. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.24 List the point coordinates of all atoms that are associated with the diamond cubic unit cell (Figure 12.15). Solution First of all, one set of carbon atoms occupy all corner positions of the cubic unit cell; the coordinates of these atoms are as follows: 000, 100, 110, 010, 001, 101, 111, and 011. Another set of atoms reside on all of the face-centered positions, with the following coordinates: 1 2 1 2 0, 1 2 1 2 1, 1 1 2 1 2 , 0 1 2 1 2 , 1 2 0 1 2 , and 1 2 1 1 2 . The third set of carbon atoms are positioned within the interior of the unit cell. Using an x-y-z coordinate system oriented as in Figure 3.4, the coordinates of the atom that lies toward the lower-left-front of the unit cell has the coordinates 3 4 1 4 1 4 , whereas the atom situated toward the lower-right-back of the unit cell has coordinates of 1 4 3 4 1 4 . Also, the carbon atom that resides toward the upper-left-back of the unit cell has the 1 4 1 4 3 4 coordinates. And, the coordinates of the final atom, located toward the upper-right-front of the unit cell, are 3 4 3 4 3 4 .
- 57. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.25 Sketch a tetragonal unit cell , and within that cell indicate locations of the 1 2 1 1 2 and 1 4 1 2 3 4 point coordinates. Solution A tetragonal unit in which are shown the 1 2 1 1 2 and 1 4 1 2 3 4 point coordinates is presented below.
- 58. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.26 Using the Molecule Definition Utility found in both “Metallic Crystal Structures and Crystallography” and “Ceramic Crystal Structures” modules of VMSE, located on the book’s web site [www.wiley.com/college/Callister (Student Companion Site)], generate a three-dimensional unit cell for the intermetallic compound AuCu3 given the following: (1) the unit cell is cubic with an edge length of 0.374 nm, (2) gold atoms are situated at all cube corners, and (3) copper atoms are positioned at the centers of all unit cell faces. Solution First of all, open the “Molecular Definition Utility”; it may be found in either of “Metallic Crystal Structures and Crystallography” or “Ceramic Crystal Structures” modules. In the “Step 1” window, it is necessary to define the atom types, colors for the spheres (atoms), and specify atom sizes. Let us enter “Au” as the name for the gold atoms (since “Au” the symbol for gold), and “Cu” as the name for the copper atoms. Next it is necessary to choose a color for each atom type from the selections that appear in the pull-down menu—for example, “Yellow” for Au and “Red” for Cu. In the “Atom Size” window, it is necessary to enter an atom/ion size. In the instructions for this step, it is suggested that the atom/ion diameter in nanometers be used. From the table found inside the front cover of the textbook, the atomic radii for gold and copper are 0.144 nm and 0.128 nm, respectively, and, therefore, their ionic diameters are twice these values (i.e., 0.288 nm and 0.256 nm); therefore, we enter the values “0.288” and “0.256” for the two atom types. Now click on the “Register” button, followed by clicking on the “Go to Step 2” button. In the “Step 2” window we specify positions for all of the atoms within the unit cell; their point coordinates are specified in the problem statement. Let’s begin with gold. Click on the yellow sphere that is located to the right of the “Molecule Definition Utility” box. Again, Au atoms are situated at all eight corners of the cubic unit cell. One Au will be positioned at the origin of the coordinate system—i.e., its point coordinates are 000, and, therefore, we enter a “0” (zero) in each of the “x”, “y”, and “z” atom position boxes. Next we click on the “Register Atom Position” button. Now we enter the coordinates of another gold atom; let us arbitrarily select the one that resides at the corner of the unit cell that is one unit-cell length along the x-axis (i.e., at the 100 point coordinate). Inasmuch as it is located a distance of a units along the x-axis the value of “0.374” is entered in the “x” atom position box (since this is the value of a given in the problem statement); zeros are entered in each of the “y” and “z” position boxes. We repeat this procedure for the remaining six Au atoms. After this step has been completed, it is necessary to specify positions for the copper atoms, which are located at all six face-centered sites. To begin, we click on the red sphere that is located next to the “Molecule Definition Utility” box. The point coordinates for some of the Cu atoms are fractional ones; in these instances, the a unit cell length (i.e., 0.374) is multiplied by the fraction. For example, one Cu atom is located 1 1 2 1 2 coordinate. Therefore, the x, y, and z atoms positions are (1)(0.374) = 0.374, 1 2 (0.374) = 0.187, and 1 2 (0.374) = 0.187, respectively. For the gold atoms, the x, y, and z atom position entries for all 8 sets of point coordinates are as follows:
- 59. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 0, 0, and 0 0.374, 0, and 0 0, 0.374, and 0 0, 0, and 0.374 0, 0.374, 0.374 0.374, 0, 0.374 0.374, 0.374, 0 0.374, 0.374, 0.374 Now, for the copper atoms, the x, y, and z atom position entries for all 6 sets of point coordinates are as follows: 0.187, 0.187, 0 0.187, 0, 0.187 0, 0.187, 0.187 0.374, 0.187, 0.187 0.187, 0.374, 0.187 0.187, 0.187, 0.374 In Step 3, we may specify which atoms are to be represented as being bonded to one another, and which type of bond(s) to use (single solid, single dashed, double, and triple are possibilities), or we may elect to not represent any bonds at all (in which case we are finished). If it is decided to show bonds, probably the best thing to do is to represent unit cell edges as bonds. This image may be rotated by using mouse click-and-drag Your image should appear as the following screen shot. Here the gold atoms appear lighter than the copper atoms.
- 60. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. [Note: Unfortunately, with this version of the Molecular Definition Utility, it is not possible to save either the data or the image that you have generated. You may use screen capture (or screen shot) software to record and store your image.]
- 61. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Crystallographic Directions 3.27 Draw an orthorhombic unit cell, and within that cell a [121 ] direction. Solution This problem calls for us to draw a [121 ] direction within an orthorhombic unit cell (a ≠ b ≠ c, α = β = γ = 90°). Such a unit cell with its origin positioned at point O is shown below. We first move along the +x-axis a units (from point O to point A), then parallel to the +y-axis 2b units (from point A to point B). Finally, we proceed parallel to the z-axis -c units (from point B to point C). The [121 ] direction is the vector from the origin (point O) to point C as shown.
- 62. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.28 Sketch a monoclinic unit cell, and within that cell a [011] direction. Solution This problem asks that a [011] direction be drawn within a monoclinic unit cell (a ≠ b ≠ c, and α = β = 90º ≠ γ). One such unit cell with its origin at point O is sketched below. For this direction, there is no projection along the x-axis since the first index is zero; thus, the direction lies in the y-z plane. We next move from the origin along the minus y-axis b units (from point O to point R). Since the final index is a one, move from point R parallel to the z-axis, c units (to point P). Thus, the [011] direction corresponds to the vector passing from the origin (point O) to point P, as indicated in the figure.
- 63. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.29 What are the indices for the directions indicated by the two vectors in the sketch below? Solution For direction 1, the projection on the x-axis is zero (since it lies in the y-z plane), while projections on the y- and z-axes, b/2 and c, respectively. This is a [012] direction as indicated in the summary below. x y z Projections 0a b/2 c Projections in terms of a, b, and c 0 1/2 1 Reduction to integers 0 1 2 Enclosure [012] Direction 2 is [112] as summarized below. x y z Projections a/2 b/2 -c Projections in terms of a, b, and c 1/2 1/2 -1 Reduction to integers 1 1 -2 Enclosure [112]
- 64. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.30 Within a cubic unit cell, sketch the following directions: (a) [110], (e) [111], (b) [121], (f) [122], (c) [012], (g) [123], (d) [133], (h) [103]. Solution The directions asked for are indicated in the cubic unit cells shown below.
- 65. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.31 Determine the indices for the directions shown in the following cubic unit cell: Solution Direction A is a [01 1]direction, which determination is summarized as follows. We first of all position the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system x y z Projections 0a –b –c Projections in terms of a, b, and c 0 –1 –1 Reduction to integers not necessary Enclosure [01 1] Direction B is a [210] direction, which determination is summarized as follows. We first of all position the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system x y z Projections –a b 2 0c Projections in terms of a, b, and c –1 1 2 0 Reduction to integers –2 1 0 Enclosure [210] Direction C is a [112] direction, which determination is summarized as follows. We first of all position the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system
- 66. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. x y z Projections a 2 b 2 c Projections in terms of a, b, and c 1 2 1 2 1 Reduction to integers 1 1 2 Enclosure [112] Direction D is a [112] direction, which determination is summarized as follows. We first of all position the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system x y z Projections a 2 b 2 –c Projections in terms of a, b, and c 1 2 1 2 –1 Reduction to integers 1 1 –2 Enclosure [112]
- 67. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.32 Determine the indices for the directions shown in the following cubic unit cell: Solution Direction A is a [430] direction, which determination is summarized as follows. We first of all position the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system x y z Projections – 2a 3 b 2 0c Projections in terms of a, b, and c – 2 3 1 2 0 Reduction to integers –4 3 0 Enclosure [430] Direction B is a [232] direction, which determination is summarized as follows. We first of all position the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system x y z Projections 2a 3 –b 2c 3 Projections in terms of a, b, and c 2 3 –1 2 3 Reduction to integers 2 –3 2 Enclosure [232] Direction C is a [133] direction, which determination is summarized as follows. We first of all position the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system
- 68. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. x y z Projections a 3 –b –c Projections in terms of a, b, and c 1 3 –1 –1 Reduction to integers 1 –3 –3 Enclosure [133] Direction D is a [136] direction, which determination is summarized as follows. We first of all position the origin of the coordinate system at the tail of the direction vector; then in terms of this new coordinate system x y z Projections a 6 b 2 –c Projections in terms of a, b, and c 1 6 1 2 –1 Reduction to integers 1 3 –6 Enclosure [136]
- 69. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.33 For tetragonal crystals, cite the indices of directions that are equivalent to each of the following directions: (a) [001] (b) [110] (c) [010] Solution For tetragonal crystals a = b ≠ c and α = β = γ = 90°; therefore, projections along the x and y axes are equivalent, which are not equivalent to projections along the z axis. (a) Therefore, for the [001] direction, there is only one equivalent direction: [001]. (b) For the [110] direction, equivalent directions are as follows: [1 10], [110], and [110] (b) Also, for the [010] direction, equivalent directions are the following: [010], [100], and [100].
- 70. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.34 Convert the [100] and [111] directions into the four-index Miller–Bravais scheme for hexagonal unit cells. Solution For [100] u' = 1, v' = 0, w' = 0 From Equations 3.6 u = 1 3 (2u' − v' ) = 1 3 [(2)(1) − 0] = 2 3 v = 1 3 (2vÕ− uÕ) = 1 3 [(2)(0) − 1] = − 1 3 t = − (u + v) = − 2 3 − 1 3 = − 1 3 w = w' = 0 It is necessary to multiply these numbers by 3 in order to reduce them to the lowest set of integers. Thus, the direction is represented as [uvtw] = [21 10]. For [111], u' = 1, v' = 1, and w' = 1; therefore, u = 1 3 [(2)(1) − 1] = 1 3 v = 1 3 [(2)(1) − 1] = 1 3 t = − 1 3 + 1 3 = − 2 3 w = 1
- 71. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. If we again multiply these numbers by 3, then u = 1, v = 1, t = -2, and w = 3. Thus, the direction is represented as Thus, the direction is represented as [uvtw] = [1123].
- 72. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.35 Determine indices for the directions shown in the following hexagonal unit cells: Solution (a) For this direction, projections on the a1, a2, and z axes are a, a/2, and c/2, or, in terms of a and c the projections are 1, 1/2, and 1/2, which when multiplied by the factor 2 become the smallest set of integers: 2, 1, and 1. This means that u’ = 2 v’ = 1 w’ = 1 Now, from Equations 3.6, the u, v, t, and w indices become u = 1 3 (2u' − v' ) = 1 3 (2)(2) − (1)[ ] = 3 3 = 1 v = 1 3 (2vÕ− uÕ) = 1 3 (2)(1) − (2)[ ] = 0 t = − (u + v) = − 1 + 0( ) = −1 w = w’ = 1 No reduction is necessary inasmuch as all of these indices are integers; therefore, this direction in the four-index scheme is [1011]
- 73. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (b) For this direction, projections on the a1, a2, and z axes are a/2, a, and 0c, or, in terms of a and c the projections are 1/2, 1, and 0, which when multiplied by the factor 2 become the smallest set of integers: 1, 2, and 0 This means that u’ = 1 v’ = 2 w’ = 0 Now, from Equations 3.6, the u, v, t, and w indices become u = 1 3 (2u' − v) = 1 3 (2)(1) − 2[ ] = 0 v = 1 3 (2v' − u' ) = 1 3 (2)(2) − 1[ ] = 1 t = − (u+ v) = − 0 + 1( ) = −1 w = w' = 0 No reduction is necessary inasmuch as all of these indices are integers; therefore, this direction in the four-index scheme is [0110].
- 74. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (c) For this direction projections on the a1, a2, and z axes are −a, −a, and c/2, or, in terms of a and c the projections are −1, −1, and 1/2, which when multiplied by the factor 2 become the smallest set of integers: −2, −2, and 1. This means that u’ = −2 v’ = −2 w’ = 1 Now, from Equations 3.6, the u, v, t, and w indices become u = 1 3 (2u' − v) = 1 3 (2)(−2) − (−2)[ ] =− 2 3 v = 1 3 (2v' − u' ) = 1 3 (2)(−2) − (−2)[ ] = − 2 3 t = − (u+ v) = − − 2 3 − 2 3 = 4 3 w = w' = 1 Now, in order to get the lowest set of integers, it is necessary to multiply all indices by the factor 3, with the result that this direction is a [2243] direction.
- 75. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (d) For this direction, projections on the a1, a2, and z axes are 0a, −a, and 0c, or, in terms of a and c the projections are 0, -1, and 0. This means that u’ = 0 v’ = −1 w’ = 0 Now, from Equations 3.6, the u, v, t, and w indices become u = 1 3 (2u' − v' ) = 1 3 (2)(0) − (−1)[ ] = 1 3 v = 1 3 (2v'− u' ) = 1 3 (2)(−1) − 0[ ] =− 2 3 t = − (u+ v) = − 1 3 − 2 3 = 1 3 w = wÕ= 0 Now, in order to get the lowest set of integers, it is necessary to multiply all indices by the factor 3, with the result that this is a [1210] direction.
- 76. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.36 Sketch the [1123] and [1010] directions in a hexagonal unit cell. Solution The first portion of this problem asks that we plot the [1 123] within a hexagonal unit cell. Below is shown this direction plotted within a hexagonal unit cell having a reduced-scale coordinate scheme. For this direction, projections on the a1, a2, a3, and c axes are respectively, −1, −1, 2, and 3, respectively. In plotting this direction, we begin at the origin of the coordinate system, point o. From here we proceed 1 unit distance along the −a1 axis (to point p), from here 1 unit distance parallel to −a2 axis (to point q), then 2 unit distances parallel (or along) the a3 axis (to point r), and finally, 3 unit distances parallel to the z axis (to point s). Thus, the [1 123] direction is that vector that extends from point o to point s as shown. Now we are asked to plot the [1010] within a hexagonal unit cell. In the figure below is plotted this direction within a hexagonal unit cell having a reduced-scale coordinate scheme.
- 77. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. For this direction, projections on the a1, a2, a3, and c axes are respectively, 1, 0, −1, and 0, respectively. In plotting this direction, we begin at the origin of the coordinate system, point o. From here we proceed 1 unit distance along the a1 axis (to point p). Since there is no projection on the a2 axis it is not necessary to move parallel to this axis. Therefore, from point p we proceed 1 unit distance parallel to −a3 axis (to point q). And, finally, inasmuch as there is no projection along the z axis, it is not necessary to move parallel to this axis. Thus, the [1010] direction is that vector that extends from point o to point q as shown.
- 78. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.37 Using Equations 3.6a, 3.6b, 3.6c, and 3.6d, derive expressions for each of the three primed indices set (u′, v′, and w′) in terms of the four unprimed indices (u, v, t, and w). Solution It is first necessary to do an expansion of Equation 3.6a as u = 1 3 (2u' − v) = 2u' 3 − v' 3 And solving this expression for v’ yields v' = 2u' − 3u Now, substitution of this expression into Equation 3.6b gives v = 1 3 (2vÕ− uÕ) = 1 3 (2)(2uÕ− 3u) − uÕ[ ] = uÕ− 2u Or u' = v + 2u And, solving for v from Equation 3.6c leads to v = − (u + t) which, when substituted into the above expression for u’ yields u' = v + 2u = − u − t + 2u = u − t In solving for an expression for v’, we begin with the one of the above expressions for this parameter—i.e., v' = 2u' − 3u Now, substitution of the above expression for u’ into this equation leads to vÕ= 2uÕ− 3u = (2)(u − t) − 3u = − u −2t
- 79. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. And solving for u from Equation 3.6c gives u = − v − t which, when substituted in the previous equation results in the following expression for v’ vÕ= − u −2t = − (− v − t) − 2t = v − t And, of course from Equation 3.6d w’ = w
- 80. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Crystallographic Planes 3.38 (a) Draw an orthorhombic unit cell, and within that cell a (210) plane. (b) Draw a monoclinic unit cell, and within that cell a (002) plane. Solution (a) We are asked to draw a (210) plane within an orthorhombic unit cell. First remove the three indices from the parentheses, and take their reciprocals--i.e., 1/2, 1, and ∞. This means that the plane intercepts the x-axis at a/2, the y-axis at b, and parallels the z-axis. The plane that satisfies these requirements has been drawn within the orthorhombic unit cell below. (For orthorhombic, a ≠ b ≠ c, and α = β = γ = 90°.) (b) A (002) plane is drawn within the monoclinic cell shown below. We first remove the parentheses and take the reciprocals of the indices; this gives ∞, ∞, and 1/2. Thus, the (002) plane parallels both x- and y-axes, and intercepts the z-axis at a/2, as indicated in the drawing. (For monoclinic, a ≠ b ≠ c, and α = γ = 90° ≠ β.)
- 81. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
- 82. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.39 What are the indices for the two planes drawn in the sketch below? Solution Plane 1 is a (020) plane. The determination of its indices is summarized below. x y z Intercepts ∞a b/2 ∞c Intercepts in terms of a, b, and c ∞ 1/2 ∞ Reciprocals of intercepts 0 2 0 Enclosure (020) Plane 2 is a (221) plane, as summarized below. x y z Intercepts a/2 -b/2 c Intercepts in terms of a, b, and c 1/2 -1/2 1 Reciprocals of intercepts 2 -2 1 Enclosure (221)
- 83. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.40 Sketch within a cubic unit cell the following planes: (a) (011) , (e) (111) , (b) (112), (f) (122), (c) (102), (g) (123), (d) (131), (h) (013) Solution The planes called for are plotted in the cubic unit cells shown below.
- 84. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.41 Determine the Miller indices for the planes shown in the following unit cell: Solution For plane A we will leave the origin at the unit cell as shown; this is a (403) plane, as summarized below. x y z Intercepts a 2 ∞b 2c 3 Intercepts in terms of a, b, and c 1 2 ∞ 2 3 Reciprocals of intercepts 2 0 3 2 Reduction 4 0 3 Enclosure (403) For plane B we will move the origin of the unit cell one unit cell distance to the right along the y axis, and one unit cell distance parallel to the x axis; thus, this is a (1 12) plane, as summarized below. x y z Intercepts – a – b c 2 Intercepts in terms of a, b, and c – 1 – 1 1 2 Reciprocals of intercepts – 1 – 1 2 Reduction (not necessary) Enclosure (1 12)
- 85. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.42 Determine the Miller indices for the planes shown in the following unit cell: Solution For plane A we will move the origin of the coordinate system one unit cell distance to the upward along the z axis; thus, this is a (322) plane, as summarized below. x y z Intercepts a 3 b 2 – c 2 Intercepts in terms of a, b, and c 1 3 1 2 – 1 2 Reciprocals of intercepts 3 2 – 2 Reduction (not necessary) Enclosure (322) For plane B we will move the original of the coordinate system on unit cell distance along the x axis; thus, this is a (101) plane, as summarized below. x y z Intercepts – a 2 ∞b c 2 Intercepts in terms of a, b, and c – 1 2 ∞ 1 2 Reciprocals of intercepts – 2 0 2 Reduction – 1 0 1 Enclosure (101)
- 86. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.43 Determine the Miller indices for the planes shown in the following unit cell: Solution For plane A since the plane passes through the origin of the coordinate system as shown, we will move the origin of the coordinate system one unit cell distance to the right along the y axis; thus, this is a (324) plane, as summarized below. x y z Intercepts 2a 3 – b c 2 Intercepts in terms of a, b, and c 2 3 – 1 1 2 Reciprocals of intercepts 3 2 – 1 2 Reduction 3 – 2 4 Enclosure (324) For plane B we will leave the origin at the unit cell as shown; this is a (221) plane, as summarized below. x y z Intercepts a 2 b 2 c Intercepts in terms of a, b, and c 1 2 1 2 1 Reciprocals of intercepts 2 2 1 Reduction not necessary Enclosure (221)
- 87. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.44 Cite the indices of the direction that results from the intersection of each of the following pair of planes within a cubic crystal: (a) (100) and (010) planes, (b) (111) and (111) planes, and (c) (101) and (001) planes. Solution (a) In the figure below is shown (100) and (010) planes, and, as indicated, their intersection results in a [001], or equivalently, a [001] direction. (b) In the figure below is shown (111) and (111) planes, and, as indicated, their intersection results in a [110], or equivalently, a [110] direction.
- 88. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (c) In the figure below is shown (101) and (001) planes, and, as indicated, their intersection results in a [010], or equivalently, a [010] direction.
- 89. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.45 Sketch the atomic packing of (a) the (100) plane for the BCC crystal structure, and (b) the (201) plane for the FCC crystal structure (similar to Figures 3.10b and 3.11b). Solution (a) A BCC unit cell, its (100) plane, and the atomic packing of this plane are indicated below. Corresponding atom positions in the two drawings are indicated by letters W, X, Y, and Z. (b) An FCC unit cell, its (201) plane, and the atomic packing of this plane are indicated below. Corresponding atom positions in the two drawing are indicated by the letters A, B, and C.
- 90. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.46 Consider the reduced-sphere unit cell shown in Problem 3.20, having an origin of the coordinate system positioned at the atom labeled with an O. For the following sets of planes, determine which are equivalent: (a) (001), (010), and, (100) (b) (110), (101), (011), and (110) (c) (111), (111) , (111) , and (111) Solution (a) The unit cell in Problem 3.20 is body-centered tetragonal. Of the three planes given in the problem statement the (100) and (010) are equivalent—that is, have the same atomic packing. The atomic packing for these two planes as well as the (001) are shown in the figure below. (b) Of the four planes cited in the problem statement, (110) and (1 10) are equivalent to one another— have the same atomic packing. The atomic arrangement of these planes is shown in the left drawing below.
- 91. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Furthermore, the (101) and (011) are equivalent to each other (but not to the other pair of planes); their atomic arrangement is represented in the other drawing. Note: the 0.424 nm dimension in the left-most drawing comes from the relationship (0.30 nm)2 + (0.30 nm)2 [ ] 1/ 2 . Likewise, the 0.500 nm dimension found in the right-most drawing comes from (0.30 nm)2 + (0.40 nm)2 [ ] 1/ 2 . (c) All of the (1 1 1), (111), (1 11), and (111) planes are equivalent, that is, have the same atomic packing as illustrated in the following figure:
- 92. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.47 Here are shown the atomic packing schemes for several different crystallographic directions for some hypothetical metal. For each direction the circles represent only those atoms contained within a unit cell, which circles are reduced from their actual size. (a) To what crystal system does the unit cell belong? (b) What would this crystal structure be called? Solution Below is constructed a unit cell using the six crystallographic directions that were provided in the problem.
- 93. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (a) This unit cell belongs to the tetragonal system since a = b = 0.40 nm, c = 0.50 nm, and α = β = γ = 90°. (b) This crystal structure would be called face-centered tetragonal since the unit cell has tetragonal symmetry, and an atom is located at each of the corners, as well as at the centers of all six unit cell faces. In the figure above, atoms are only shown at the centers of three faces; however, atoms would also be situated at opposite faces.
- 94. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.48 Below are shown three different crystallographic planes for a unit cell of some hypothetical metal. The circles represent atoms: (a) To what crystal system does the unit cell belong? (b) What would this crystal structure be called? (c) If the density of this metal is 8.95 g/cm3 , determine its atomic weight. Solution The unit cells constructed below show the three crystallographic planes that were provided in the problem statement. (a) This unit cell belongs to the orthorhombic crystal system since a = 0.30 nm, b = 0.40 nm, c = 0.35 nm, and α = β = γ = 90°. (b) This crystal structure would be called body-centered orthorhombic since the unit cell has orthorhombic symmetry, and an atom is located at each of the corners, as well as at the cell center. (c) In order to compute its atomic weight, we employ Equation 3.5, with n = 2; thus A = ρVC NA n
- 95. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (8.95 g/cm3) (3.0)(4.0)(3.5) (× 10-24 cm3/unit cell)(6.022 × 10 23 atoms/mol) 2 atoms/unit cell = 113.2 g/mol
- 96. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.49 Convert the (010) and (101) planes into the four-index Miller–Bravais scheme for hexagonal unit cells. Solution For (010), h = 0, k = 1, and l = 0, and, from Equation 3.7, the value of i is equal to i = − (h + k) = − (0 + 1) = −1 Therefore, the (010) plane becomes (0110) . Now for the (101) plane, h = 1, k = 0, and l = 1, and computation of i using Equation 3.7 leads to i = − (h + k) = −[1 + 0] = −1 such that (101) becomes (1011).
- 97. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.50 Determine the indices for the planes shown in the hexagonal unit cells below: Solution (a) For this plane, intersections with the a1, a2, and z axes are ∞a, ∞a, and c/2 (the plane parallels both a1 and a2 axes). In terms of a and c these intersections are ∞, ∞, and ½, the respective reciprocals of which are 0, 0, and 2. This means that h = 0 k = 0 l = 2 Now, from Equation 3.7, the value of i is i = − (h + k) = −[0 + 0] = 0 Hence, this is a (0002) plane.
- 98. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (b) This plane passes through the origin of the coordinate axis system; therefore, we translate this plane one unit distance along the x axis, per the sketch shown below: At this point the plane intersects the a1, a2, and z axes at a, ∞a, and ∞c, respectively (the plane parallels both a2 and z axes). In terms of a and c these intersections are 1, ∞, and ∞, the respective reciprocals of which are 1, 0, and 0. This means that h = 1 k = 0 l = 0 Now, from Equation 3.7, the value of i is i = − (h + k) = − (1 + 0) = −1 Hence, this is a (1010) plane.
- 99. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (c) For this plane, intersections with the a1, a2, and z axes are –a, a, and c. In terms of a and c these intersections are –1, 1, and 1, the respective reciprocals of which are 0, 1, and 1. This means that h = –1 k = 1 l = 1 Now, from Equation 3.7, the value of i is i = − (h + k) = − (−1 + 1) = 0 Hence, this is a (1101) plane.
- 100. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (d) For this plane, intersections with the a1, a2, and z axes are –a/2, a, and c/2, respectively. In terms of a and c these intersections are –1/2, 1, and 1/2, the respective reciprocals of which are –2, 1, and 2. This means that h = –2 k = 1 l = 2 Now, from Equation 3.7, the value of i is i = − (h + k) = − (−2 + 1) = 1 Therefore, this is a (2112) plane.
- 101. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.51 Sketch the (1101) and (1120) planes in a hexagonal unit cell. Solution For (1101) the reciprocals of h, k, i, and l are, respectively, 1, –1, ∞, and 1; thus, this plane is parallel to the a3 axis, and intersects the a1 axis at a, the a2 axis at –a, and the z-axis at c. The plane having these intersections is shown in the figure below For (1120) the reciprocals of h, k, i, and l are, respectively, 1, 1, –1/2, and ∞; thus, this plane is parallel to the z axis, and intersects the a1 axis at a, the a2 axis at a, and the a3 axis at –a/2. The plane having these intersections is shown in the figure below.
- 102. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Linear and Planar Densities 3.52 (a) Derive linear density expressions for FCC [100] and [111] directions in terms of the atomic radius R. (b) Compute and compare linear density values for these same two directions for silver. Solution (a) In the figure below is shown a [100] direction within an FCC unit cell. For this [100] direction there is one atom at each of the two unit cell corners, and, thus, there is the equivalent of 1 atom that is centered on the direction vector. The length of this direction vector is just the unit cell edge length, 2R 2 (Equation 3.1). Therefore, the expression for the linear density of this plane is LD100 = number of atoms centered on [100] direction vector length of [100] direction vector = 1 atom 2R 2 = 1 2R 2 An FCC unit cell within which is drawn a [111] direction is shown below.
- 103. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. For this [111] direction, the vector shown passes through only the centers of the single atom at each of its ends, and, thus, there is the equivalence of 1 atom that is centered on the direction vector. The length of this direction vector is denoted by z in this figure, which is equal to z = x2 + y2 where x is the length of the bottom face diagonal, which is equal to 4R. Furthermore, y is the unit cell edge length, which is equal to 2R 2 (Equation 3.1). Thus, using the above equation, the length z may be calculated as follows: z = (4R)2 + (2 R 2)2 = 24 R2 = 2 R 6 Therefore, the expression for the linear density of this direction is LD111 = number of atoms centered on [111] direction vector length of [111] direction vector = 1 atom 2R 6 = 1 2R 6 (b) From the table inside the front cover, the atomic radius for silver is 0.144 nm. Therefore, the linear density for the [100] direction is LD100 (Ag) = 1 2R 2 = 1 (2)(0.144 nm) 2 = 2.46 nm−1 = 2.46 × 109 m−1 While for the [111] direction LD111(Ag) = 1 2R 6 = 1 (2)(0.144 nm) 6 = 1.42 nm−1 = 1.42 × 109 m−1
- 104. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.53 (a) Derive linear density expressions for BCC [110] and [111] directions in terms of the atomic radius R. (b) Compute and compare linear density values for these same two directions for tungsten. Solution (a) In the figure below is shown a [110] direction within a BCC unit cell. For this [110] direction there is one atom at each of the two unit cell corners, and, thus, there is the equivalence of 1 atom that is centered on the direction vector. The length of this direction vector is denoted by x in this figure, which is equal to x = z2 − y2 where y is the unit cell edge length, which, from Equation 3.3 is equal to 4 R 3 . Furthermore, z is the length of the unit cell diagonal, which is equal to 4R Thus, using the above equation, the length x may be calculated as follows: x = (4R)2 − 4R 3 2 = 32R2 3 = 4R 2 3 Therefore, the expression for the linear density of this direction is LD110 = number of atoms centered on [110] direction vector length of [110] direction vector = 1 atom 4 R 2 3 = 3 4 R 2
- 105. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. A BCC unit cell within which is drawn a [111] direction is shown below. For although the [111] direction vector shown passes through the centers of three atoms, there is an equivalence of only two atoms associated with this unit cell—one-half of each of the two atoms at the end of the vector, in addition to the center atom belongs entirely to the unit cell. Furthermore, the length of the vector shown is equal to 4R, since all of the atoms whose centers the vector passes through touch one another. Therefore, the linear density is equal to LD111 = number of atoms centered on [111] direction vector length of [111] direction vector = 2 atoms 4R = 1 2R (b) From the table inside the front cover, the atomic radius for tungsten is 0.137 nm. Therefore, the linear density for the [110] direction is LD110 (W) = 3 4 R 2 = 3 (4)(0.137 nm) 2 = 2.23 nm−1 = 2.23 × 109 m−1 While for the [111] direction LD111(W) = 1 2 R = 1 (2)(0.137 nm) = 3.65 nm−1 = 3.65 × 109 m−1
- 106. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.54 (a) Derive planar density expressions for FCC (100) and (111) planes in terms of the atomic radius R. (b) Compute and compare planar density values for these same two planes for nickel. Solution (a) In the figure below is shown a (100) plane for an FCC unit cell. For this (100) plane there is one atom at each of the four cube corners, each of which is shared with four adjacent unit cells, while the center atom lies entirely within the unit cell. Thus, there is the equivalence of 2 atoms associated with this FCC (100) plane. The planar section represented in the above figure is a square, wherein the side lengths are equal to the unit cell edge length, 2R 2 (Equation 3.1); and, thus, the area of this square is just (2R 2)2 = 8R2 . Hence, the planar density for this (100) plane is just PD100 = number of atoms centered on (100) plane area of (100) plane = 2 atoms 8R2 = 1 4R2 That portion of an FCC (111) plane contained within a unit cell is shown below.
- 107. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. There are six atoms whose centers lie on this plane, which are labeled A through F. One-sixth of each of atoms A, D, and F are associated with this plane (yielding an equivalence of one-half atom), with one-half of each of atoms B, C, and E (or an equivalence of one and one-half atoms) for a total equivalence of two atoms. Now, the area of the triangle shown in the above figure is equal to one-half of the product of the base length and the height, h. If we consider half of the triangle, then (2R)2 + h2 = (4R)2 which leads to h = 2R 3. Thus, the area is equal to Area = 4R(h) 2 = (4R)(2R 3) 2 = 4R2 3 And, thus, the planar density is PD111 = number of atoms centered on (111) plane area of (111) plane = 2 atoms 4R2 3 = 1 2R2 3 (b) From the table inside the front cover, the atomic radius for nickel is 0.125 nm. Therefore, the planar density for the (100) plane is PD100 (Ni) = 1 4 R2 = 1 4 (0.125 nm)2 = 16.00 nm−2 = 1.600 × 1019 m−2 While for the (111) plane PD111(Ni) = 1 2 R2 3 = 1 2 3 (0.125 nm)2 = 18.48 nm−2 = 1.848 × 1019 m−2
- 108. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.55 (a) Derive planar density expressions for BCC (100) and (110) planes in terms of the atomic radius R. (b) Compute and compare planar density values for these same two planes for vanadium. Solution (a) A BCC unit cell within which is drawn a (100) plane is shown below. For this (100) plane there is one atom at each of the four cube corners, each of which is shared with four adjacent unit cells. Thus, there is the equivalence of 1 atom associated with this BCC (100) plane. The planar section represented in the above figure is a square, wherein the side lengths are equal to the unit cell edge length, 4R 3 (Equation 3.3); and, thus, the area of this square is just 4R 3 2 = 16R2 3 . Hence, the planar density for this (100) plane is just PD100 = number of atoms centered on (100) plane area of (100) plane = 1 atom 16 R2 3 = 3 16 R2 A BCC unit cell within which is drawn a (110) plane is shown below.
- 109. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. For this (110) plane there is one atom at each of the four cube corners through which it passes, each of which is shared with four adjacent unit cells, while the center atom lies entirely within the unit cell. Thus, there is the equivalence of 2 atoms associated with this BCC (110) plane. The planar section represented in the above figure is a rectangle, as noted in the figure below. From this figure, the area of the rectangle is the product of x and y. The length x is just the unit cell edge length, which for BCC (Equation 3.3) is 4 R 3 . Now, the diagonal length z is equal to 4R. For the triangle bounded by the lengths x, y, and z y = z2 − x2 Or y = (4R)2 − 4R 3 2 = 4R 2 3 Thus, in terms of R, the area of this (110) plane is just
- 110. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Area(110) = xy = 4 R 3 4 R 2 3 = 16 R2 2 3 And, finally, the planar density for this (110) plane is just PD110 = number of atoms centered on (110) plane area of (110) plane = 2 atoms 16 R2 2 3 = 3 8 R2 2 (b) From the table inside the front cover, the atomic radius for vanadium is 0.132 nm. Therefore, the planar density for the (100) plane is PD100 (V) = 3 16R2 = 3 16(0.132 nm)2 = 10.76 nm−2 = 1.076 × 1019 m−2 While for the (110) plane PD110 (V) = 3 8R2 2 = 3 8(0.132 nm)2 2 = 15.22 nm−2 = 1.522 × 1019 m−2
- 111. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.56 (a) Derive the planar density expression for the HCP (0001) plane in terms of the atomic radius R. (b) Compute the planar density value for this same plane for magnesium. Solution (a) A (0001) plane for an HCP unit cell is show below. Each of the 6 perimeter atoms in this plane is shared with three other unit cells, whereas the center atom is shared with no other unit cells; this gives rise to three equivalent atoms belonging to this plane. In terms of the atomic radius R, the area of each of the 6 equilateral triangles that have been drawn is R2 3, or the total area of the plane shown is 6 R2 3. And the planar density for this (0001) plane is equal to PD0001 = number of atoms centered on (0001) plane area of (0001) plane = 3 atoms 6R2 3 = 1 2R2 3 (b) From the table inside the front cover, the atomic radius for magnesium is 0.160 nm. Therefore, the planar density for the (0001) plane is PD0001(Mg) = 1 2R2 3 = 1 2(0.160 nm)2 3 = 11.28 nm−2 = 1.128 × 1019 m−2
- 112. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Polycrystalline Materials 3.57 Explain why the properties of polycrystalline materials are most often isotropic. Solution Although each individual grain in a polycrystalline material may be anisotropic, if the grains have random orientations, then the solid aggregate of the many anisotropic grains will behave isotropically.
- 113. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. X-ray Diffraction: Determination of Crystal Structures 3.58 Using the data for molybdenum in Table 3.1, compute the interplanar spacing for the (111) set of planes. Solution From the Table 3.1, molybdenum has a BCC crystal structure and an atomic radius of 0.1363 nm. Using Equation (3.3), the lattice parameter a may be computed as a= 4 R 3 = (4)(0.1363 nm) 3 = 0.3148 nm Now, the interplanar spacing d111 maybe determined using Equation 3.14 as d111 = a (1)2 + (1)2 + (1)2 = 0.3148 nm 3 = 0.1817 nm
- 114. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.59 Determine the expected diffraction angle for the first-order reflection from the (113) set of planes for FCC platinum when monochromatic radiation of wavelength 0.1542 nm is used. Solution We first calculate the lattice parameter using Equation 3.1 and the value of R (0.1387 nm) cited in Table 3.1, as follows: a = 2 R 2 = (2)(0.1387 nm)( 2) = 0.3923 nm Next, the interplanar spacing for the (113) set of planes may be determined using Equation 3.14 according to d113 = a (1)2 + (1)2 + (3)2 = 0.3923 nm 11 = 0.1183 nm And finally, employment of Equation 3.13 yields the diffraction angle as sin θ = nλ 2d113 = (1)(0.1542 nm) (2)(0.1183 nm) = 0.652 Which leads to θ = sin-1(0.652) = 40.69° And, finally 2θ = (2)(40.69°) = 81.38°
- 115. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.60 Using the data for aluminum in Table 3.1, compute the interplanar spacings for the (110) and (221) sets of planes. Solution From the table, aluminum has an FCC crystal structure and an atomic radius of 0.1431 nm. Using Equation 3.1 the lattice parameter, a, may be computed as a = 2R 2 = (2) (0.1431 nm)( 2) = 0.4047 nm Now, the d110 interplanar spacing may be determined using Equation 3.14 as d110 = a (1)2 + (1)2 + (0)2 = 0.4047 nm 2 = 0.2862 nm And, similarly for d221 d221 = a (2)2 + (2)2 + (1)2 = 0.4047 nm 9 = 0.1349 nm
- 116. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.61 The metal iridium has an FCC crystal structure. If the angle of diffraction for the (220) set of planes occurs at 69.22° (first-order reflection) when monochromatic x-radiation having a wavelength of 0.1542 nm is used, compute (a) the interplanar spacing for this set of planes, and (b) the atomic radius for an iridium atom. Solution (a) From the data given in the problem, and realizing that 69.22° = 2θ, the interplanar spacing for the (220) set of planes for iridium may be computed using Equation 3.13 as d220 = nλ 2 sin θ = (1)(0.1542 nm) (2) sin 69.22° 2 = 0.1357 nm (b) In order to compute the atomic radius we must first determine the lattice parameter, a, using Equation 3.14, and then R from Equation 3.1 since Ir has an FCC crystal structure. Therefore, a = d220 (2)2 + (2)2 + (0)2 = (0.1357 nm)( 8) = 0.3838 nm And, from Equation 3.1 R = a 2 2 = 0.3838 nm 2 2 = 0.1357 nm
- 117. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.62 The metal rubidium has a BCC crystal structure. If the angle of diffraction for the (321) set of planes occurs at 27.00° (first-order reflection) when monochromatic x-radiation having a wavelength of 0.0711 nm is used, compute (a) the interplanar spacing for this set of planes, and (b) the atomic radius for the rubidium atom. Solution (a) From the data given in the problem, and realizing that 27.00° = 2θ, the interplanar spacing for the (321) set of planes for Rb may be computed using Equation 3.13 as follows: d321 = nλ 2 sin θ = (1)(0.0711 nm) (2) sin 27.00° 2 = 0.1523 nm (b) In order to compute the atomic radius we must first determine the lattice parameter, a, using Equation 3.14, and then R from Equation 3.3 since Rb has a BCC crystal structure. Therefore, a= d321 (3)2 + (2)2 + (1)2 = (0.1523 nm)( 14) = 0.5700 nm And, from Equation 3.3 R = a 3 4 = (0.5700 nm) 3 4 = 0.2468 nm
- 118. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.63 For which set of crystallographic planes will a first-order diffraction peak occur at a diffraction angle of 46.21° for BCC iron when monochromatic radiation having a wavelength of 0.0711 nm is used? Solution The first step to solve this problem is to compute the interplanar spacing using Equation 3.13. Thus, dhkl = nλ 2 sin θ = (1)(0.0711 nm) (2) sin 46.21° 2 = 0.0906 nm Now, employment of both Equations 3.14 and 3.3 (since Fe’s crystal structure is BCC), and the value of R for iron from Table 3.1 (0.1241 nm) leads to h2 + k 2 + l2 = a dhkl = 4R dhkl 3 = (4)(0.1241 nm) (0.0906 nm)( 3) = 3.163 This means that h2 + k 2 + l2 = (3.163)2 = 10.0 By trial and error, the only three integers having a sum that is even, and the sum of the squares of which equals 10.0 are 3, 1, and 0. Therefore, the set of planes responsible for this diffraction peak are the (310) ones.
- 119. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.64 Figure 3.22 shows an x-ray diffraction pattern for α-iron taken using a diffractometer and monochromatic x-radiation having a wavelength of 0.1542 nm; each diffraction peak on the pattern has been indexed. Compute the interplanar spacing for each set of planes indexed; also determine the lattice parameter of Fe for each of the peaks. Solution For each peak, in order to compute the interplanar spacing and the lattice parameter we must employ Equations 3.14 and 3.13, respectively. The first peak of Figure 3.22, which results from diffraction by the (110) set of planes, occurs at 2θ = 45.0°; the corresponding interplanar spacing for this set of planes, using Equation 3.13, is equal to d110 = nλ 2 sin θ = (1)(0.1542 nm) (2) sin 45.0° 2 = 0.2015 nm And, from Equation 3.14, the lattice parameter a is determined as a = dhkl (h)2 + (k)2 + (l)2 = d110 (1)2 + (1)2 + (0)2 = (0.2015 nm) 2 = 0.2850 nm Similar computations are made for the other peaks which results are tabulated below:
- 120. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Peak Index 2θ dhkl (nm) a (nm) 200 65.1 0.1433 0.2866 211 82.8 0.1166 0.2856
- 121. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.65 The diffraction peaks shown in Figure 3.22 are indexed according to the reflection rules for BCC (i.e., the sum h + k + l must be even). Cite the h, k, and l indices for the first four diffraction peaks for FCC crystals consistent with h, k, and l all being either odd or even. Solution The first four diffraction peaks that will occur for FCC consistent with h, k, and l all being odd or even are (111), (200), (220), and (311).
- 122. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 3.66 Figure 3.25 shows the first four peaks of the x-ray diffraction pattern for copper, which has an FCC crystal structure; monochromatic x-radiation having a wavelength of 0.1542 nm was used. (a) Index (i.e., give h, k, and l indices) for each of these peaks. (b) Determine the interplanar spacing for each of the peaks. (c) For each peak, determine the atomic radius for Cu and compare these with the value presented in Table 3.1. Solution (a) Since Cu has an FCC crystal structure, only those peaks for which h, k, and l are all either odd or even will appear. Therefore, the first peak results by diffraction from (111) planes. (b) For each peak, in order to calculate the interplanar spacing we must employ Equation 3.13. For the first peak which occurs at 43.8° d111 = nλ 2 sin θ = (1)(0.1542 nm) (2) sin 43.8° 2 = 0.2067 nm (c) Employment of Equations 3.14 and 3.1 is necessary for the computation of R for Cu as R = a 2 2 = (dhkl) (h)2 + (k)2 + (l)2 2 2 = (0.2067 nm) (1)2 + (1)2 + (1)2 2 2 = 0.1266 nm Similar computations are made for the other peaks which results are tabulated below:
- 123. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Peak Index 2θ dhkl (nm) R (nm) 200 50.8 0.1797 0.1271 220 74.4 0.1275 0.1275 311 90.4 0.1087 0.1274
- 124. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Noncrystalline Solids 3.67 Would you expect a material in which the atomic bonding is predominantly ionic in nature to be more or less likely to form a noncrystalline solid upon solidification than a covalent material? Why? (See Section 2.6.) Solution A material in which atomic bonding is predominantly ionic in nature is less likely to form a noncrystalline solid upon solidification than a covalent material because covalent bonds are directional whereas ionic bonds are nondirectional; it is more difficult for the atoms in a covalent material to assume positions giving rise to an ordered structure.
- 125. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 4 IMPERFECTIONS IN SOLIDS PROBLEM SOLUTIONS Vacancies and Self-Interstitials 4.1 Calculate the fraction of atom sites that are vacant for lead at its melting temperature of 327°C (600 K). Assume an energy for vacancy formation of 0.55 eV/atom. Solution In order to compute the fraction of atom sites that are vacant in lead at 600 K, we must employ Equation 4.1. As stated in the problem, Qv = 0.55 eV/atom. Thus, Nv N = exp − Qv kT = exp − 0.55 eV/atom (8.62 × 10−5 eV/atom- K)(600 K) = 2.41 × 10-5
- 126. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.2 Calculate the number of vacancies per cubic meter in iron at 850°C. The energy for vacancy formation is 1.08 eV/atom. Furthermore, the density and atomic weight for Fe are 7.65 g/cm3 and 55.85 g/mol, respectively. Solution Determination of the number of vacancies per cubic meter in iron at 850°C (1123 K) requires the utilization of Equations 4.1 and 4.2 as follows: Nv = N exp − Qv kT = NA ρFe AFe exp − Qv kT And incorporation of values of the parameters provided in the problem statement into the above equation leads to Nv = (6.022 × 1023atoms /mol)(7.65 g/cm3) 55.85 g/mol exp − 1.08 eV/atom (8.62 × 10−5 eV/atom− K)(850°C + 273 K) = 1.18 × 1018 cm-3 = 1.18 × 1024 m-3
- 127. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.3 Calculate the activation energy for vacancy formation in aluminum, given that the equilibrium number of vacancies at 500°C (773 K) is 7.57 × 1023 m-3 . The atomic weight and density (at 500°C) for aluminum are, respectively, 26.98 g/mol and 2.62 g/cm3 . Solution Upon examination of Equation 4.1, all parameters besides Qv are given except N, the total number of atomic sites. However, N is related to the density, (ρAl ), Avogadro's number (NA), and the atomic weight (AAl ) according to Equation 4.2 as N = NA ρAl AAl = (6.022 × 1023 atoms /mol)(2.62 g/cm3) 26.98 g/mol = 5.85 × 1022 atoms/cm3 = 5.85 × 1028 atoms/m3 Now, taking natural logarithms of both sides of Equation 4.1, ln Nv = ln N − Qv kT and, after some algebraic manipulation Qv = − kT ln Nv N = − (8.62 × 10-5 eV/atom- K)(500°C + 273 K) ln 7.57 × 1023 m−3 5.85 × 1028 m−3 = 0.75 eV/atom
- 128. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Impurities in Solids 4.4 Below, atomic radius, crystal structure, electronegativity, and the most common valence are tabulated, for several elements; for those that are nonmetals, only atomic radii are indicated. Element Atomic Radius (nm) Crystal Structure Electronegativity Valence Cu 0.1278 FCC 1.9 +2 C 0.071 H 0.046 O 0.060 Ag 0.1445 FCC 1.9 +1 Al 0.1431 FCC 1.5 +3 Co 0.1253 HCP 1.8 +2 Cr 0.1249 BCC 1.6 +3 Fe 0.1241 BCC 1.8 +2 Ni 0.1246 FCC 1.8 +2 Pd 0.1376 FCC 2.2 +2 Pt 0.1387 FCC 2.2 +2 Zn 0.1332 HCP 1.6 +2 Which of these elements would you expect to form the following with copper: (a) A substitutional solid solution having complete solubility (b) A substitutional solid solution of incomplete solubility (c) An interstitial solid solution Solution In this problem we are asked to cite which of the elements listed form with Cu the three possible solid solution types. For complete substitutional solubility the following criteria must be met: 1) the difference in atomic radii between Cu and the other element (∆R%) must be less than ±15%, 2) the crystal structures must be the same, 3) the electronegativities must be similar, and 4) the valences should be the same, or nearly the same. Below are tabulated, for the various elements, these criteria. Crystal ∆Electro- Element ∆R% Structure negativity Valence Cu FCC 2+ C –44
- 129. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. H –64 O –53 Ag +13 FCC 0 1+ Al +12 FCC -0.4 3+ Co -2 HCP -0.1 2+ Cr -2 BCC -0.3 3+ Fe -3 BCC -0.1 2+ Ni -3 FCC -0.1 2+ Pd +8 FCC +0.3 2+ Pt +9 FCC +0.3 2+ Zn +4 HCP -0.3 2+ (a) Ni, Pd, and Pt meet all of the criteria and thus form substitutional solid solutions having complete solubility. At elevated temperatures Co and Fe experience allotropic transformations to the FCC crystal structure, and thus display complete solid solubility at these temperatures. (b) Ag, Al, Co, Cr, Fe, and Zn form substitutional solid solutions of incomplete solubility. All these metals have either BCC or HCP crystal structures, and/or the difference between their atomic radii and that for Cu are greater than ±15%, and/or have a valence different than 2+. (c) C, H, and O form interstitial solid solutions. These elements have atomic radii that are significantly smaller than the atomic radius of Cu.
- 130. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.5 For both FCC and BCC crystal structures, there are two different types of interstitial sites. In each case, one site is larger than the other, and is normally occupied by impurity atoms. For FCC, this larger one is located at the center of each edge of the unit cell; it is termed an octahedral interstitial site. On the other hand, with BCC the larger site type is found at 0 1 2 1 4 positions—that is, lying on {100} faces, and situated midway between two unit cell edges on this face and one-quarter of the distance between the other two unit cell edges; it is termed a tetrahedral interstitial site. For both FCC and BCC crystal structures, compute the radius r of an impurity atom that will just fit into one of these sites in terms of the atomic radius R of the host atom. Solution In the drawing below is shown the atoms on the (100) face of an FCC unit cell; the interstitial site is at the center of the edge. The diameter of an atom that will just fit into this site (2r) is just the difference between that unit cell edge length (a) and the radii of the two host atoms that are located on either side of the site (R); that is 2r = a – 2R However, for FCC a is related to R according to Equation 3.1 as a = 2R 2 ; therefore, solving for r from the above equation gives r = a − 2 R 2 = 2 R 2 − 2 R 2 = 0.41R A (100) face of a BCC unit cell is shown below.
- 131. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The interstitial atom that just fits into this interstitial site is shown by the small circle. It is situated in the plane of this (100) face, midway between the two vertical unit cell edges, and one quarter of the distance between the bottom and top cell edges. From the right triangle that is defined by the three arrows we may write a 2 2 + a 4 2 = (R + r) 2 However, from Equation 3.3, a = 4R 3 , and, therefore, making this substitution, the above equation takes the form 4R 2 3 2 + 4R 4 3 2 = R2 + 2Rr + r2 After rearrangement the following quadratic equation results: r2 + 2Rr − 0.667R 2 = 0 And upon solving for r:
- 132. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. r = −(2R) ± (2R)2 − (4)(1)(−0.667R2) 2 = −2R± 2.582R 2 And, finally r(+) = −2R + 2.582R 2 = 0.291R r(−) = −2R − 2.582R 2 = − 2.291R Of course, only the r(+) root is possible, and, therefore, r = 0.291R. Thus, for a host atom of radius R, the size of an interstitial site for FCC is approximately 1.4 times that for BCC.
- 133. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Specification of Composition 4.6 Derive the following equations: (a) Equation 4.7a (b) Equation 4.9a (c) Equation 4.10a (d) Equation 4.11b Solution (a) This problem asks that we derive Equation 4.7a. To begin, C1 is defined according to Equation 4.3 as C1 = m1 m1 + m2 × 100 or, equivalently C1 = m1 ' m1 ' + m2 ' × 100 where the primed m's indicate masses in grams. From Equation 4.4 we may write m1 ' = nm1 A1 m 2 ' = nm2 A2 And, substitution into the C1 expression above C1 = nm1 A1 nm1 A1 + nm2 A2 × 100 From Equation 4.5 it is the case that nm1 = C1 ' (nm1 + nm2) 100
- 134. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. nm2 = C2 ' (nm1 + nm2) 100 And substitution of these expressions into the above equation leads to C1 = C1 ' A1 C1 ' A1 + C2 ' A2 × 100 which is just Equation 4.7a. (b) This problem asks that we derive Equation 4.9a. To begin, C1 " is defined as the mass of component 1 per unit volume of alloy, or C1 " = m1 V If we assume that the total alloy volume V is equal to the sum of the volumes of the two constituents--i.e., V = V1 + V2 --then C1 " = m1 V1 + V2 Furthermore, the volume of each constituent is related to its density and mass as V1 = m1 ρ1 V2 = m2 ρ2 This leads to C1 " = m1 m1 ρ1 + m2 ρ2 From Equation 4.3, m1 and m2 may be expressed as follows:
- 135. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. m1 = C1(m1 + m2) 100 m2 = C2 (m1 + m2) 100 Substitution of these equations into the preceding expression yields C1 " = C1 (m1 + m2) 100 C1 (m1 + m2) 100 ρ1 + C2 (m1 + m2) 100 ρ2 = C1 C1 ρ1 + C2 ρ2 If the densities ρ1 and ρ2 are given in units of g/cm3 , then conversion to units of kg/m3 requires that we multiply this equation by 103 , inasmuch as 1 g/cm3 = 103 kg/m3 Therefore, the previous equation takes the form C1 " = C1 C1 ρ1 + C2 ρ2 × 103 which is the desired expression. (c) Now we are asked to derive Equation 4.10a. The density of an alloy ρave is just the total alloy mass M divided by its volume V ρave = M V
- 136. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Or, in terms of the component elements 1 and 2 ρave = m1 + m2 V1 + V2 [Note: here it is assumed that the total alloy volume is equal to the separate volumes of the individual components, which is only an approximation; normally V will not be exactly equal to (V1 + V2 )]. Each of V1 and V2 may be expressed in terms of its mass and density as, V1 = m1 ρ1 V2 = m2 ρ2 When these expressions are substituted into the above equation, we get ρave = m1 + m2 m1 ρ1 + m2 ρ2 Furthermore, from Equation 4.3 m1 = C1 (m1 + m2) 100 m2 = C2 (m1 + m2) 100 Which, when substituted into the above ρave expression yields ρave = m1 + m2 C1 (m1 + m2) 100 ρ1 + C2 (m1 + m2) 100 ρ2 And, finally, this equation reduces to
- 137. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = 100 C1 ρ1 + C2 ρ2 (d) And, finally, the derivation of Equation 4.11b for Aave is requested. The alloy average molecular weight is just the ratio of total alloy mass in grams M’ and the total number of moles in the alloy Nm . That is Aave = MÕ Nm = m1 ' + m2 ' nm1 + nm2 But using Equation 4.4 we may write m1 ' = nm1 A1 m2 ' = nm2 A2 Which, when substituted into the above Aave expression yields Aave = M' Nm = nm1 A1 + nm2 A2 nm1 + nm2 Furthermore, from Equation 4.5 nm1 = C1 ' (nm1 + nm2) 100 nm2 = C2 ' (nm1 + nm2) 100 Thus, substitution of these expressions into the above equation for Aave yields Aave = C1 ' A1 (nm1 + nm2) 100 + C2 ' A2 (nm1 + nm2) 100 nm1 + nm2
- 138. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = C1 ' A1 + C2 ' A2 100 which is the desired result.
- 139. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.7 What is the composition, in atom percent, of an alloy that consists of 30 wt% Zn and 70 wt% Cu? Solution In order to compute composition, in atom percent, of a 30 wt% Zn-70 wt% Cu alloy, we employ Equation 4.6 as CZn ' = CZn ACu CZn ACu + CCu AZn × 100 = (30)(63.55 g/mol) (30)(63.55 g/mol) + (70)(65.41 g/mol) × 100 = 29.4 at% CCu ' = CCu AZn CZn ACu + CCu AZn × 100 = (70)(65.41 g /mol) (30)(63.55 g /mol) + (70)(65.41 g /mol) × 100 = 70.6 at%
- 140. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.8 What is the composition, in weight percent, of an alloy that consists of 6 at% Pb and 94 at% Sn? Solution In order to compute composition, in weight percent, of a 6 at% Pb-94 at% Sn alloy, we employ Equation 4.7 as CPb = CPb ' APb CPb ' APb + CSn ' ASn × 100 = (6)(207.2 g /mol) (6)(207.2 g /mol) + (94)(118.71 g /mol) × 100 = 10.0 wt% CSn = CSn ' ASn CPb ' APb + CSn ' ASn × 100 = (94)(118.71 g/mol) (6)(207.2 g/mol) + (94)(118.71 g/mol) × 100 = 90.0 wt%
- 141. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.9 Calculate the composition, in weight percent, of an alloy that contains 218.0 kg titanium, 14.6 kg of aluminum, and 9.7 kg of vanadium. Solution The concentration, in weight percent, of an element in an alloy may be computed using a modified form of Equation 4.3. For this alloy, the concentration of titanium (CTi ) is just CTi = mTi mTi + mAl + mV × 100 = 218 kg 218 kg + 14.6 kg + 9.7 kg × 100 = 89.97 wt% Similarly, for aluminum CAl = 14.6 kg 218 kg + 14.6 kg + 9.7 kg × 100 = 6.03 wt% And for vanadium CV = 9.7 kg 218 kg + 14.6 kg + 9.7 kg × 100 = 4.00 wt%
- 142. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.10 What is the composition, in atom percent, of an alloy that contains 98 g tin and 65 g of lead? Solution The concentration of an element in an alloy, in atom percent, may be computed using Equation 4.5. However, it first becomes necessary to compute the number of moles of both Sn and Pb, using Equation 4.4. Thus, the number of moles of Sn is just nmSn = mSn ' ASn = 98 g 118.71 g/mol = 0.826 mol Likewise, for Pb nmPb = 65 g 207.2 g /mol = 0.314 mol Now, use of Equation 4.5 yields CSn ' = nmSn nmSn + nmPb × 100 = 0.826 mol 0.826 mol + 0.314 mol × 100 = 72.5 at% Also, CPb ' = = 0.314 mol 0.826 mol + 0.314 mol × 100 = 27.5 at%
- 143. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.11 What is the composition, in atom percent, of an alloy that contains 99.7 lbm copper, 102 lbm zinc, and 2.1 lbm lead? Solution In this problem we are asked to determine the concentrations, in atom percent, of the Cu-Zn-Pb alloy. It is first necessary to convert the amounts of Cu, Zn, and Pb into grams. mCu ' = (99.7 lbm)(453.6 g/lbm) = 45,224 g mZn ' = (102 lbm)(453.6 g/lbm) = 46,267 g mPb ' = (2.1 lbm)(453.6 g/lbm) = 953 g These masses must next be converted into moles (Equation 4.4), as nmCu = mCu ' ACu = 45,224 g 63.55 g /mol = 711.6 mol nmZn = 46,267 g 65.41 g/mol = 707.3 mol nmPb = 953 g 207.2 g /mol = 4.6 mol Now, employment of a modified form of Equation 4.5, gives CCu ' = nmCu nmCu + nmZn + nmPb × 100 = 711.6 mol 711.6 mol + 707.3 mol + 4.6 mol × 100 = 50.0 at% CZn ' = 707.3 mol 711.6 mol + 707.3 mol + 4.6 mol × 100 = 49.7 at%
- 144. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CPb ' = 4.6 mol 711.6 mol + 707.3 mol + 4.6 mol × 100 = 0.3 at%
- 145. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.12 What is the composition, in atom percent, of an alloy that consists of 97 wt% Fe and 3 wt% Si? Solution We are asked to compute the composition of an Fe-Si alloy in atom percent. Employment of Equation 4.6 leads to CFe ' = CFe ASi CFe ASi + CSi AFe × 100 = 97(28.09 g/mol) 97(28.09 g/mol) + 3(55.85 g/mol) × 100 = 94.2 at% CSi ' = CSiAFe CSi AFe + CFe ASi × 100 = 3(55.85 g/mol) 3(55.85 g/mol) + 97(28.09 g/mol) × 100 = 5.8 at%
- 146. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.13 Convert the atom percent composition in Problem 4.11 to weight percent. Solution The composition in atom percent for Problem 4.11 is 50.0 at% Cu, 49.7 at% Zn, and 0.3 at% Pb. Modification of Equation 4.7 to take into account a three-component alloy leads to the following CCu = CCu ' ACu CCu ' ACu + CZn ' AZn + CPb ' APb × 100 = (50.0) (63.55 g/mol) (50.0) (63.55 g/mol) + (49.7) (65.41 g/mol) + (0.3) (207.2 g/mol) × 100 = 49.0 wt% CZn = CZn ' AZn CCu ' ACu + CZn ' AZn + CPb ' APb × 100 = (49.7) (65.41 g/mol) (50.0) (63.55 g/mol) + (49.7) (65.41 g/mol) + (0.3) (207.2 g/mol) × 100 = 50.1 wt% CPb = CPb ' APb CCu ' ACu + CZn ' AZn + CPb ' APb × 100 = (0.3) (207.2 g/mol) (50.0) (63.55 g/mol) + (49.7) (65.41 g/mol) + (0.3) (207.2 g/mol) × 100 = 1.0 wt%
- 147. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.14 Calculate the number of atoms per cubic meter in aluminum. Solution In order to solve this problem, one must employ Equation 4.2, N = NA ρAl AAl The density of Al (from the table inside of the front cover) is 2.71 g/cm3 , while its atomic weight is 26.98 g/mol. Thus, N = (6.022 × 1023 atoms /mol)(2.71 g/cm3) 26.98 g/mol = 6.05 × 1022 atoms/cm3 = 6.05 × 1028 atoms/m3
- 148. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.15 The concentration of carbon in an iron-carbon alloy is 0.15 wt%. What is the concentration in kilograms of carbon per cubic meter of alloy? Solution In order to compute the concentration in kg/m3 of C in a 0.15 wt% C-99.85 wt% Fe alloy we must employ Equation 4.9 as CC " = CC CC ρC + CFe ρFe × 103 From inside the front cover, densities for carbon and iron are 2.25 and 7.87 g/cm3 , respectively; and, therefore CC " = 0.15 0.15 2.25 g/cm3 + 99.85 7.87 g/cm3 × 103 = 11.8 kg/m3
- 149. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.16 Determine the approximate density of a high-leaded brass that has a composition of 64.5 wt% Cu, 33.5 wt% Zn, and 2.0 wt% Pb. Solution In order to solve this problem, Equation 4.10a is modified to take the following form: ρave = 100 CCu ρCu + CZn ρZn + CPb ρPb And, using the density values for Cu, Zn, and Pb—i.e., 8.94 g/cm3 , 7.13 g/cm3 , and 11.35 g/cm3 —(as taken from inside the front cover of the text), the density is computed as follows: ρave = 100 64.5 wt% 8.94 g /cm3 + 33.5 wt% 7.13 g/cm3 + 2.0 wt% 11.35 g/cm3 = 8.27 g/cm3
- 150. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.17 Calculate the unit cell edge length for an 85 wt% Fe-15 wt% V alloy. All of the vanadium is in solid solution, and, at room temperature the crystal structure for this alloy is BCC. Solution In order to solve this problem it is necessary to employ Equation 3.5; in this expression density and atomic weight will be averages for the alloy—that is ρave = nAave VC NA Inasmuch as the unit cell is cubic, then VC = a3, then ρave = nAave a3NA And solving this equation for the unit cell edge length, leads to a = nAave ρaveNA 1/3 Expressions for Aave and ρave are found in Equations 4.11a and 4.10a, respectively, which, when incorporated into the above expression yields a = n 100 CFe AFe + CV AV 100 CFe ρFe + CV ρV NA 1/ 3 Since the crystal structure is BCC, the value of n in the above expression is 2 atoms per unit cell. The atomic weights for Fe and V are 55.85 and 50.94 g/mol, respectively (Figure 2.6), whereas the densities for the Fe and V are 7.87 g/cm3 and 6.10 g/cm3 (from inside the front cover). Substitution of these, as well as the concentration values stipulated in the problem statement, into the above equation gives
- 151. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. a = (2 atoms/unit cell) 100 85 wt% 55.85 g/mol + 15 wt% 50.94 g/mol 100 85 wt% 7.87 g/cm3 + 15 wt% 6.10 g/cm3 6.022 × 1023 atoms/mol( ) 1/ 3 = 2.89 × 10-8 cm = 0.289 nm
- 152. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.18 Some hypothetical alloy is composed of 12.5 wt% of metal A and 87.5 wt% of metal B. If the densities of metals A and B are 4.27 and 6.35 g/cm3 , respectively, whereas their respective atomic weights are 61.4 and 125.7 g/mol, determine whether the crystal structure for this alloy is simple cubic, face-centered cubic, or body- centered cubic. Assume a unit cell edge length of 0.395 nm. Solution In order to solve this problem it is necessary to employ Equation 3.5; in this expression density and atomic weight will be averages for the alloy—that is ρave = nAave VC NA Inasmuch as for each of the possible crystal structures, the unit cell is cubic, then VC = a3, or ρave = nAave a3NA And, in order to determine the crystal structure it is necessary to solve for n, the number of atoms per unit cell. For n =1, the crystal structure is simple cubic, whereas for n values of 2 and 4, the crystal structure will be either BCC or FCC, respectively. When we solve the above expression for n the result is as follows: n = ρavea3NA Aave Expressions for Aave and ρave are found in Equations 4.11a and 4.10a, respectively, which, when incorporated into the above expression yields n = 100 CA ρA + CB ρB a3NA 100 CA AA + CB AB
- 153. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Substitution of the concentration values (i.e., CA = 12.5 wt% and CB = 87.5 wt%) as well as values for the other parameters given in the problem statement, into the above equation gives n = 100 12.5 wt% 4.27 g/cm3 + 87.5 wt% 6.35 g/cm3 (3.95 × 10-8 nm)3(6.022 × 1023 atoms/mol) 100 12.5 wt% 61.4 g/mol + 87.5 wt% 125.7 g/mol = 2.00 atoms/unit cell Therefore, on the basis of this value, the crystal structure is body-centered cubic.
- 154. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.19 For a solid solution consisting of two elements (designated as 1 and 2), sometimes it is desirable to determine the number of atoms per cubic centimeter of one element in a solid solution, N1, given the concentration of that element specified in weight percent, C1. This computation is possible using the following expression: N1 = NAC1 C1A1 ρ1 + A1 ρ2 100− C1( ) (4.18) where NA = Avogadro’s number ρ1 and ρ2 = densities of the two elements A1 = the atomic weight of element 1 Derive Equation 4.18 using Equation 4.2 and expressions contained in Section 4.4. Solution This problem asks that we derive Equation 4.18, using other equations given in the chapter. The concentration of component 1 in atom percent (C1 ' ) is just 100 c1 ' where c1 ' is the atom fraction of component 1. Furthermore, c1 ' is defined as c1 ' = N1/N where N1 and N are, respectively, the number of atoms of component 1 and total number of atoms per cubic centimeter. Thus, from the above discussion the following holds: N1 = C1 ' N 100 Substitution into this expression of the appropriate form of N from Equation 4.2 yields N1 = C1 ' NA ρave 100 Aave And, finally, substitution into this equation expressions for C1 ' (Equation 4.6a), ρave (Equation 4.10a), Aave (Equation 4.11a), and realizing that C2 = (C1 – 100), and after some algebraic manipulation we obtain the desired expression: N1 = NAC1 C1 A1 ρ1 + A1 ρ2 (100 − C1)
- 155. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.20 Gold forms a substitutional solid solution with silver. Compute the number of gold atoms per cubic centimeter for a silver-gold alloy that contains 10 wt% Au and 90 wt% Ag. The densities of pure gold and silver are 19.32 and 10.49 g/cm3 , respectively. Solution To solve this problem, employment of Equation 4.18 is necessary, using the following values: C1 = CAu = 10 wt% ρ1 = ρAu = 19.32 g/cm3 ρ2 = ρAg = 10.49 g/cm3 A1 = AAu = 196.97 g/mol Thus NAu = NACAu CAu AAu ρAu + AAu ρAg (100 − CAu) = (6.022 × 1023 atoms /mol) (10 wt%) (10 wt%)(196.97 g /mol) 19.32 g /cm3 + 196.97 g /mol 10.49 g /cm3 (100 − 10 wt%) = 3.36 × 1021 atoms/cm3
- 156. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.21 Germanium forms a substitutional solid solution with silicon. Compute the number of germanium atoms per cubic centimeter for a germanium-silicon alloy that contains 15 wt% Ge and 85 wt% Si. The densities of pure germanium and silicon are 5.32 and 2.33 g/cm3 , respectively. Solution To solve this problem, employment of Equation 4.18 is necessary, using the following values: C1 = CGe = 15 wt% ρ1 = ρGe = 5.32 g/cm3 ρ2 = ρSi = 2.33 g/cm3 A1 = AGe = 72.64 g/mol Thus NGe = NACGe CGe AGe ρGe + AGe ρSi (100 − CGe) = (6.022 × 1023 atoms /mol)(15 wt%) (15 wt%)(72.64 g/mol) 5.32 g/cm3 + 72.64 g/mol 2.33 g/cm3 (100 − 15 wt%) = 3.16 × 1021 atoms/cm3
- 157. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.22 Sometimes it is desirable to be able to determine the weight percent of one element, C1, that will produce a specified concentration in terms of the number of atoms per cubic centimeter, N1, for an alloy composed of two types of atoms. This computation is possible using the following expression: C1 = 100 1 + NAρ2 N1A1 − ρ2 ρ1 (4.19) where NA = Avogadro’s number ρ1 and ρ2 = densities of the two elements A1 and A2 = the atomic weights of the two elements Derive Equation 4.19 using Equation 4.2 and expressions contained in Section 4.4. Solution The number of atoms of component 1 per cubic centimeter is just equal to the atom fraction of component 1 (c1 ' ) times the total number of atoms per cubic centimeter in the alloy (N). Thus, using the equivalent of Equation 4.2, we may write N1 = c1 ' N = c1 ' NA ρave Aave Realizing that c1 ' = C1 ' 100 and C2 ' = 100 − C1 ' and substitution of the expressions for ρave and Aave, Equations 4.10b and 4.11b, respectively, leads to N1 = c1 ' NAρave Aave
- 158. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = NAC1 ' ρ1ρ2 C1 ' ρ2 A1 + (100 − C1 ' )ρ1A2 And, solving for C1 ' C1 ' = 100 N1ρ1 A2 NAρ1ρ2 − N1ρ2 A1 + N1ρ1 A2 Substitution of this expression for C1 ' into Equation 4.7a, which may be written in the following form C1 = C1 ' A1 C1 ' A1 + C2 ' A2 × 100 = C1 ' A1 C1 ' A1 + (100 − C1 ' )A2 × 100 yields C1 = 100 1 + NA ρ2 N1 A1 − ρ2 ρ1 the desired expression.
- 159. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.23 Molybdenum forms a substitutional solid solution with tungsten. Compute the weight percent of molybdenum that must be added to tungsten to yield an alloy that contains 1.0 × 1022 Mo atoms per cubic centimeter. The densities of pure Mo and W are 10.22 and 19.30 g/cm3 , respectively. Solution To solve this problem, employment of Equation 4.19 is necessary, using the following values: N1 = NMo = 1022 atoms/cm3 ρ1 = ρMo = 10.22 g/cm3 ρ2 = ρW = 19.30 g/cm3 A1 = AMo = 95.94 g/mol A2 = AW = 183.84 g/mol Thus CMo = 100 1 + NAρW NMo AMo − ρW ρMo = 100 1 + (6.022 × 1023 atoms /mol)(19.30 g /cm3) (1022 atoms /cm3)(95.94 g /mol) − 19.30 g /cm3 10.22 g /cm3 = 8.91 wt%
- 160. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.24 Niobium forms a substitutional solid solution with vanadium. Compute the weight percent of niobium that must be added to vanadium to yield an alloy that contains 1.55 × 1022 Nb atoms per cubic centimeter. The densities of pure Nb and V are 8.57 and 6.10 g/cm3 , respectively. Solution To solve this problem, employment of Equation 4.19 is necessary, using the following values: N1 = NNb = 1.55 × 1022 atoms/cm3 ρ1 = ρNb = 8.57 g/cm3 ρ2 = ρV = 6.10 g/cm3 A1 = ANb = 92.91 g/mol A2 = AV = 50.94 g/mol Thus CNb = 100 1 + NAρV NNb ANb − ρV ρNb = 100 1 + (6.022 × 1023 atoms /mol)(6.10 g /cm3) (1.55 × 1022 atoms /cm3)(92.91 g /mol) − 6.10 g /cm3 8.57 g /cm3 = 35.2 wt%
- 161. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.25 Silver and palladium both have the FCC crystal structure, and Pd forms a substitutional solid solution for all concentrations at room temperature. Compute the unit cell edge length for a 75 wt% Ag–25 wt% Pd alloy. The room-temperature density of Pd is 12.02 g/cm3 , and its atomic weight and atomic radius are 106.4 g/mol and 0.138 nm, respectively. Solution First of all, the atomic radii for Ag (using the table inside the front cover) and Pd are 0.144 and 0.138 nm, respectively. Also, using Equation 3.5 it is possible to compute the unit cell volume, and inasmuch as the unit cell is cubic, the unit cell edge length is just the cube root of the volume. However, it is first necessary to calculate the density and average atomic weight of this alloy using Equations 4.10a and 4.11a. Inasmuch as the densities of silver and palladium are 10.49 g/cm3 (as taken from inside the front cover) and 12.02 g/cm3, respectively, the average density is just ρave = 100 CAg ρAg + CPd ρPd = 100 75 wt% 10.49 g/cm3 + 25 wt% 12.02 g/cm3 = 10.83 g/cm3 And for the average atomic weight Aave = 100 CAg AAg + CPd APd = 100 75 wt% 107.9 g /mol + 25 wt% 106.4 g /mol = 107.5 g/mol Now, VC is determined from Equation 3.5 as
- 162. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. VC = nAave ρaveNA = (4 atoms /unit cell)(107.5 g/mol) (10.83 g/cm3)(6.022 × 1023 atoms /mol) = 6.59 × 10-23 cm3/unit cell And, finally a = (VC )1/3 = (6.59 × 10 −23cm3/unit cell)1/3 = 4.04 × 10-8 cm = 0.404 nm
- 163. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Dislocations—Linear Defects 4.26 Cite the relative Burgers vector–dislocation line orientations for edge, screw, and mixed dislocations. Solution The Burgers vector and dislocation line are perpendicular for edge dislocations, parallel for screw dislocations, and neither perpendicular nor parallel for mixed dislocations.
- 164. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Interfacial Defects 4.27 For an FCC single crystal, would you expect the surface energy for a (100) plane to be greater or less than that for a (111) plane? Why? (Note: You may want to consult the solution to Problem 3.54 at the end of Chapter 3.) Solution The surface energy for a crystallographic plane will depend on its packing density [i.e., the planar density (Section 3.11)]—that is, the higher the packing density, the greater the number of nearest-neighbor atoms, and the more atomic bonds in that plane that are satisfied, and, consequently, the lower the surface energy. From the solution to Problem 3.54, planar densities for FCC (100) and (111) planes are 1 4R2 and 1 2R2 3 , respectively—that is 0.25 R2 and 0.29 R2 (where R is the atomic radius). Thus, since the planar density for (111) is greater, it will have the lower surface energy.
- 165. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.28 For a BCC single crystal, would you expect the surface energy for a (100) plane to be greater or less than that for a (110) plane? Why? (Note: You may want to consult the solution to Problem 3.55 at the end of Chapter 3.) Solution The surface energy for a crystallographic plane will depend on its packing density [i.e., the planar density (Section 3.11)]—that is, the higher the packing density, the greater the number of nearest-neighbor atoms, and the more atomic bonds in that plane that are satisfied, and, consequently, the lower the surface energy. From the solution to Problem 3.55, the planar densities for BCC (100) and (110) are 3 16R2 and 3 8R2 2 , respectively—that is 0.19 R2 and 0.27 R2 . Thus, since the planar density for (110) is greater, it will have the lower surface energy.
- 166. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.29 (a) For a given material, would you expect the surface energy to be greater than, the same as, or less than the grain boundary energy? Why? (b) The grain boundary energy of a small-angle grain boundary is less than for a high-angle one. Why is this so? Solution (a) The surface energy will be greater than the grain boundary energy. For grain boundaries, some atoms on one side of a boundary will bond to atoms on the other side; such is not the case for surface atoms. Therefore, there will be fewer unsatisfied bonds along a grain boundary. (b) The small-angle grain boundary energy is lower than for a high-angle one because more atoms bond across the boundary for the small-angle, and, thus, there are fewer unsatisfied bonds.
- 167. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.30 (a) Briefly describe a twin and a twin boundary. (b) Cite the difference between mechanical and annealing twins. Solution (a) A twin boundary is an interface such that atoms on one side are located at mirror image positions of those atoms situated on the other boundary side. The region on one side of this boundary is called a twin. (b) Mechanical twins are produced as a result of mechanical deformation and generally occur in BCC and HCP metals. Annealing twins form during annealing heat treatments, most often in FCC metals.
- 168. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.31 For each of the following stacking sequences found in FCC metals, cite the type of planar defect that exists: (a) . . . A B C A B C B A C B A . . . (b) . . . A B C A B C B C A B C . . . Now, copy the stacking sequences and indicate the position(s) of planar defect(s) with a vertical dashed line. Solution (a) The interfacial defect that exists for this stacking sequence is a twin boundary, which occurs at the indicated position. The stacking sequence on one side of this position is mirrored on the other side. (b) The interfacial defect that exists within this FCC stacking sequence is a stacking fault, which occurs between the two lines. Within this region, the stacking sequence is HCP.
- 169. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Grain Size Determination 4.32 (a) Using the intercept method, determine the average grain size, in millimeters, of the specimen whose microstructure is shown in Figure 4.14(b); use at least seven straight-line segments. (b) Estimate the ASTM grain size number for this material. Solution (a) Below is shown the photomicrograph of Figure 4.14(b), on which seven straight line segments, each of which is 60 mm long has been constructed; these lines are labeled “1” through “7”. In order to determine the average grain diameter, it is necessary to count the number of grains intersected by each of these line segments. These data are tabulated below. Line Number No. Grains Intersected 1 11 2 10 3 9 4 8.5 5 7 6 10 7 8
- 170. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The average number of grain boundary intersections for these lines was 9.1. Therefore, the average line length intersected is just 60 mm 9.1 = 6.59 mm Hence, the average grain diameter, d, is d = ave. line length intersected magnification = 6.59 mm 100 = 6.59 × 10−2 mm (b) This portion of the problem calls for us to estimate the ASTM grain size number for this same material. The average grain size number, n, is related to the number of grains per square inch, N, at a magnification of 100× according to Equation 4.16. Inasmuch as the magnification is 100×, the value of N is measured directly from the micrograph. The photomicrograph on which has been constructed a square 1 in. on a side is shown below. The total number of complete grains within this square is approximately 10 (taking into account grain fractions). Now, in order to solve for n in Equation 4.16, it is first necessary to take logarithms as log N = (n − 1) log 2 From which n equals n = log N log 2 + 1
- 171. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = log 10 log 2 + 1 = 4.3
- 172. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.33 (a) Employing the intercept technique, determine the average grain size for the steel specimen whose microstructure is shown in Figure 9.25(a); use at least seven straight-line segments. (b) Estimate the ASTM grain size number for this material. Solution (a) Below is shown the photomicrograph of Figure 9.25(a), on which seven straight line segments, each of which is 60 mm long has been constructed; these lines are labeled “1” through “7”. In order to determine the average grain diameter, it is necessary to count the number of grains intersected by each of these line segments. These data are tabulated below. Line Number No. Grains Intersected 1 7 2 7 3 7 4 8 5 10 6 7 7 8 The average number of grain boundary intersections for these lines was 8.7. Therefore, the average line length intersected is just
- 173. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 60 mm 8.7 = 6.9 mm Hence, the average grain diameter, d, is d = ave. line length intersected magnification = 6.9 mm 90 = 0.077 mm (b) This portion of the problem calls for us to estimate the ASTM grain size number for this same material. The average grain size number, n, is related to the number of grains per square inch, N, at a magnification of 100× according to Equation 4.16. However, the magnification of this micrograph is not 100×, but rather 90×. Consequently, it is necessary to use Equation 4.17 NM M 100 2 = 2n−1 where NM = the number of grains per square inch at magnification M, and n is the ASTM grain size number. Taking logarithms of both sides of this equation leads to the following: log N M + 2 log M 100 = (n − 1) log 2 Solving this expression for n gives n = log N M + 2 log M 100 log 2 + 1 The photomicrograph on which has been constructed a square 1 in. on a side is shown below.
- 174. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. From Figure 9.25(a), NM is measured to be approximately 7, which leads to n = log 7 + 2 log 90 100 log 2 + 1 = 3.5
- 175. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.34 For an ASTM grain size of 8, approximately how many grains would there be per square inch at (a) a magnification of 100, and (b) without any magnification? Solution (a) This part of problem asks that we compute the number of grains per square inch for an ASTM grain size of 8 at a magnification of 100×. All we need do is solve for the parameter N in Equation 4.16, inasmuch as n = 8. Thus N = 2n−1 = 28−1 = 128 grains/in.2 (b) Now it is necessary to compute the value of N for no magnification. In order to solve this problem it is necessary to use Equation 4.17: N M M 100 2 = 2n−1 where NM = the number of grains per square inch at magnification M, and n is the ASTM grain size number. Without any magnification, M in the above equation is 1, and therefore, N1 1 100 2 = 28−1 = 128 And, solving for N1, N1 = 1,280,000 grains/in.2 .
- 176. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.35 Determine the ASTM grain size number if 25 grains per square inch are measured at a magnification of 600. Solution This problem asks that we determine the ASTM grain size number if 8 grains per square inch are measured at a magnification of 600. In order to solve this problem we make use of Equation 4.17: N M M 100 2 = 2 n −1 where NM = the number of grains per square inch at magnification M, and n is the ASTM grain size number. Solving the above equation for n, and realizing that NM = 8, while M = 600, we have n = log NM + 2 log M 100 log 2 + 1 = log 8 + 2 log 600 100 log 2 + 1 = 9.2
- 177. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.36 Determine the ASTM grain size number if 20 grains per square inch are measured at a magnification of 50. Solution This problem asks that we determine the ASTM grain size number if 20 grains per square inch are measured at a magnification of 50. In order to solve this problem we make use of Equation 4.17—viz. N M M 100 2 = 2n−1 where NM = the number of grains per square inch at magnification M, and n is the ASTM grain size number. Solving the above equation for n, and realizing that NM = 20, while M = 50, we have n = log N M + 2 log M 100 log 2 + 1 = log 20 + 2 log 50 100 log 2 + 1 = 3.3
- 178. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. DESIGN PROBLEMS Specification of Composition 4.D1 Aluminum–lithium alloys have been developed by the aircraft industry to reduce the weight and improve the performance of its aircraft. A commercial aircraft skin material having a density of 2.55 g/cm3 is desired. Compute the concentration of Li (in wt%) that is required. Solution Solution of this problem requires the use of Equation 4.10a, which takes the form ρave = 100 CLi ρLi + 100 − CLi ρAl inasmuch as CLi + CAl = 100. According to the table inside the front cover, the respective densities of Li and Al are 0.534 and 2.71 g/cm3 . Upon solving for CLi from the above equation, we get CLi = 100 ρLi (ρAl − ρave) ρave(ρAl − ρLi) And incorporating specified values into the above equation leads to CLi = (100)(0.534 g /cm3)(2.71 g /cm3 − 2.55 g /cm3) (2.55 g /cm3)(2.71 g /cm3 − 0.534 g /cm3) = 1.540 wt%
- 179. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 4.D2 Iron and vanadium both have the BCC crystal structure and V forms a substitutional solid solution in Fe for concentrations up to approximately 20 wt% V at room temperature. Determine the concentration in weight percent of V that must be added to iron to yield a unit cell edge length of 0.289 nm. Solution To begin, it is necessary to employ Equation 3.5, and solve for the unit cell volume, VC, as VC = nAave ρaveNA where Aave and ρave are the atomic weight and density, respectively, of the Fe-V alloy. Inasmuch as both of these materials have the BCC crystal structure, which has cubic symmetry, VC is just the cube of the unit cell length, a. That is VC = a3 = (0.289 nm)3 = (2.89 × 10−8 cm)3 = 2.414 × 10−23 cm3 It is now necessary to construct expressions for Aave and ρave in terms of the concentration of vanadium, CV, using Equations 4.11a and 4.10a. For Aave we have Aave = 100 CV AV + (100 − CV) AFe = 100 CV 50.94g/mol + (100 − CV) 55.85 g/mol whereas for ρave ρave = 100 CV ρV + (100 − CV) ρFe = 100 CV 6.10 g/cm3 + (100 − CV) 7.87 g/cm3
- 180. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Within the BCC unit cell there are 2 equivalent atoms, and thus, the value of n in Equation 3.5 is 2; hence, this expression may be written in terms of the concentration of V in weight percent as follows: VC = 2.414 × 10-23 cm3 = nAave ρ ave N A = (2 atoms /unit cell) 100 CV 50.94 g/mol + (100 − CV) 55.85 g/mol 100 CV 6.10 g/cm3 + (100 − CV) 7.87 g/cm3 (6.022 × 1023 atoms /mol) And solving this expression for CV leads to CV = 12.9 wt%.
- 181. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 5 DIFFUSION PROBLEM SOLUTIONS Introduction 5.1 Briefly explain the difference between self-diffusion and interdiffusion. Solution Self-diffusion is atomic migration in pure metals--i.e., when all atoms exchanging positions are of the same type. Interdiffusion is diffusion of atoms of one metal into another metal.
- 182. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.2 Self-diffusion involves the motion of atoms that are all of the same type; therefore it is not subject to observation by compositional changes, as with interdiffusion. Suggest one way in which self-diffusion may be monitored. Solution Self-diffusion may be monitored by using radioactive isotopes of the metal being studied. The motion of these isotopic atoms may be monitored by measurement of radioactivity level.
- 183. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Diffusion Mechanisms 5.3 (a) Compare interstitial and vacancy atomic mechanisms for diffusion. (b) Cite two reasons why interstitial diffusion is normally more rapid than vacancy diffusion. Solution (a) With vacancy diffusion, atomic motion is from one lattice site to an adjacent vacancy. Self-diffusion and the diffusion of substitutional impurities proceed via this mechanism. On the other hand, atomic motion is from interstitial site to adjacent interstitial site for the interstitial diffusion mechanism. (b) Interstitial diffusion is normally more rapid than vacancy diffusion because: (1) interstitial atoms, being smaller, are more mobile; and (2) the probability of an empty adjacent interstitial site is greater than for a vacancy adjacent to a host (or substitutional impurity) atom.
- 184. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Steady-State Diffusion 5.4 Briefly explain the concept of steady state as it applies to diffusion. Solution Steady-state diffusion is the situation wherein the rate of diffusion into a given system is just equal to the rate of diffusion out, such that there is no net accumulation or depletion of diffusing species--i.e., the diffusion flux is independent of time.
- 185. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.5 (a) Briefly explain the concept of a driving force. (b) What is the driving force for steady-state diffusion? Solution (a) The driving force is that which compels a reaction to occur. (b) The driving force for steady-state diffusion is the concentration gradient.
- 186. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.6 The purification of hydrogen gas by diffusion through a palladium sheet was discussed in Section 5.3. Compute the number of kilograms of hydrogen that pass per hour through a 5-mm-thick sheet of palladium having an area of 0.20 m2 at 500°C. Assume a diffusion coefficient of 1.0 × 10-8 m2 /s, that the concentrations at the high- and low-pressure sides of the plate are 2.4 and 0.6 kg of hydrogen per cubic meter of palladium, and that steady- state conditions have been attained. Solution This problem calls for the mass of hydrogen, per hour, that diffuses through a Pd sheet. It first becomes necessary to employ both Equations 5.1a and 5.3. Combining these expressions and solving for the mass yields M = JAt = − DAt ∆C ∆x = − (1.0 × 10-8 m2/s)(0.20 m2)(3600 s/h) 0.6 − 2.4 kg /m3 5 × 10−3 m = 2.6 × 10-3 kg/h
- 187. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.7 A sheet of steel 1.5 mm thick has nitrogen atmospheres on both sides at 1200°C and is permitted to achieve a steady-state diffusion condition. The diffusion coefficient for nitrogen in steel at this temperature is 6 × 10-11 m2 /s, and the diffusion flux is found to be 1.2 × 10-7 kg/m2 -s. Also, it is known that the concentration of nitrogen in the steel at the high-pressure surface is 4 kg/m3 . How far into the sheet from this high-pressure side will the concentration be 2.0 kg/m3 ? Assume a linear concentration profile. Solution This problem is solved by using Equation 5.3 in the form J = − D CA − CB xA − xB If we take CA to be the point at which the concentration of nitrogen is 4 kg/m3 , then it becomes necessary to solve for xB , as xB = xA + D CA − CB J Assume xA is zero at the surface, in which case xB = 0 + (6 × 10-11 m2/s) 4 kg /m3 − 2 kg /m3 1.2 × 10−7 kg /m2 - s = 1 × 10-3 m = 1 mm
- 188. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.8 A sheet of BCC iron 1 mm thick was exposed to a carburizing gas atmosphere on one side and a decarburizing atmosphere on the other side at 725°C. After having reached steady state, the iron was quickly cooled to room temperature. The carbon concentrations at the two surfaces of the sheet were determined to be 0.012 and 0.0075 wt%. Compute the diffusion coefficient if the diffusion flux is 1.4 × 10-8 kg/m2 -s. Hint: Use Equation 4.9 to convert the concentrations from weight percent to kilograms of carbon per cubic meter of iron. Solution Let us first convert the carbon concentrations from weight percent to kilograms carbon per meter cubed using Equation 4.9a. For 0.012 wt% C CC " = CC CC ρC + CFe ρFe × 103 = 0.012 0.012 2.25 g/cm3 + 99.988 7.87 g/cm3 × 103 0.944 kg C/m3 Similarly, for 0.0075 wt% C CC " = 0.0075 0.0075 2.25 g/cm3 + 99.9925 7.87 g/cm3 × 103 = 0.590 kg C/m3 Now, using a rearranged form of Equation 5.3 D = − J xA − xB CA − CB = − (1.40 × 10-8 kg/m2 - s) − 10−3 m 0.944 kg/m3 − 0.590 kg/m3
- 189. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = 3.95 × 10-11 m2 /s
- 190. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.9 When α-iron is subjected to an atmosphere of hydrogen gas, the concentration of hydrogen in the iron, CH (in weight percent), is a function of hydrogen pressure, pH2 (in MPa), and absolute temperature (T) according to CH = 1.34 × 10−2 pH2 exp − 27.2 kJ /mol RT (5.14) Furthermore, the values of D0 and Qd for this diffusion system are 1.4 × 10-7 m2 /s and 13,400 J/mol, respectively. Consider a thin iron membrane 1 mm thick that is at 250°C. Compute the diffusion flux through this membrane if the hydrogen pressure on one side of the membrane is 0.15 MPa (1.48 atm), and on the other side 7.5 MPa (74 atm). Solution Ultimately we will employ Equation 5.3 to solve this problem. However, it first becomes necessary to determine the concentration of hydrogen at each face using Equation 5.14. At the low pressure (or B) side CH(B) = (1.34 × 10-2) 0.15 MPa exp − 27,200 J/mol (8.31 J/mol- K)(250 + 273 K) 9.93 × 10-6 wt% Whereas, for the high pressure (or A) side CH(A) = (1.34 × 10-2) 7.5 MPa exp − 27,200 J/mol (8.31 J/mol- K)(250 + 273 K) 7.02 × 10-5 wt% We now convert concentrations in weight percent to mass of nitrogen per unit volume of solid. At face B there are 9.93 × 10-6 g (or 9.93 × 10-9 kg) of hydrogen in 100 g of Fe, which is virtually pure iron. From the density of iron (7.87 g/cm3), the volume iron in 100 g (VB) is just VB = 100 g 7.87 g/cm3 = 12.7 cm3 = 1.27 × 10-5 m3 Therefore, the concentration of hydrogen at the B face in kilograms of H per cubic meter of alloy [ CH(B) ’’ ] is just
- 191. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CH(B) '' = CH(B) VB = 9.93 × 10−9 kg 1.27 × 10−5 m3 = 7.82 × 10-4 kg/m3 At the A face the volume of iron in 100 g (VA) will also be 1.27 × 10-5 m3, and CH(A) '' = CH(A) VA = 7.02 × 10−8 kg 1.27 × 10−5 m3 = 5.53 × 10-3 kg/m3 Thus, the concentration gradient is just the difference between these concentrations of nitrogen divided by the thickness of the iron membrane; that is ∆C ∆x = CH(B) '' − CH(A) '' xB − xA = 7.82 × 10−4 kg /m3 − 5.53 × 10−3 kg /m3 10−3 m = − 4.75 kg/m4 At this time it becomes necessary to calculate the value of the diffusion coefficient at 250°C using Equation 5.8. Thus, D = D0 exp − Qd RT = (1.4 × 10−7 m2/s) exp − 13,400 J/mol (8.31 J/mol− K)(250 + 273 K) = 6.41 × 10-9 m2 /s And, finally, the diffusion flux is computed using Equation 5.3 by taking the negative product of this diffusion coefficient and the concentration gradient, as
- 192. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. J = − D ∆C ∆x = − (6.41 × 10-9 m2/s)(− 4.75 kg/m4 ) = 3.05 × 10-8 kg/m2 - s
- 193. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Nonsteady-State Diffusion 5.10 Show that Cx = B Dt exp − x2 4Dt is also a solution to Equation 5.4b. The parameter B is a constant, being independent of both x and t. Solution It can be shown that Cx = B Dt exp − x2 4Dt is a solution to ∂C ∂t = D ∂2C ∂x2 simply by taking appropriate derivatives of the Cx expression. When this is carried out, ∂C ∂t = D ∂2C ∂x2 = B 2D1/2t3/2 x2 2Dt − 1 exp − x2 4Dt
- 194. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.11 Determine the carburizing time necessary to achieve a carbon concentration of 0.45 wt% at a position 2 mm into an iron–carbon alloy that initially contains 0.20 wt% C. The surface concentration is to be maintained at 1.30 wt% C, and the treatment is to be conducted at 1000°C. Use the diffusion data for γ-Fe in Table 5.2. Solution In order to solve this problem it is first necessary to use Equation 5.5: Cx − C0 Cs − C0 = 1 − erf x 2 Dt wherein, Cx = 0.45, C0 = 0.20, Cs = 1.30, and x = 2 mm = 2 × 10-3 m. Thus, Cx − C0 Cs − C0 = 0.45 − 0.20 1.30 − 0.20 = 0.2273 = 1 − erf x 2 Dt or erf x 2 Dt = 1 − 0.2273 = 0.7727 By linear interpolation using data from Table 5.1 z erf(z) 0.85 0.7707 z 0.7727 0.90 0.7970 z − 0.850 0.900 − 0.850 = 0.7727 − 0.7707 0.7970 − 0.7707 From which z = 0.854 = x 2 Dt Now, from Table 5.2, at 1000°C (1273 K)
- 195. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. D = (2.3 × 10-5 m2/s) exp − 148,000 J/mol (8.31 J/mol- K)(1273 K) = 1.93 × 10-11 m2 /s Thus, 0.854 = 2 × 10−3 m (2) (1.93 × 10−11 m2/s)(t) Solving for t yields t = 7.1 × 104 s = 19.7 h
- 196. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.12 An FCC iron-carbon alloy initially containing 0.35 wt% C is exposed to an oxygen-rich and virtually carbon-free atmosphere at 1400 K (1127°C). Under these circumstances the carbon diffuses from the alloy and reacts at the surface with the oxygen in the atmosphere; that is, the carbon concentration at the surface position is maintained essentially at 0 wt% C. (This process of carbon depletion is termed decarburization.) At what position will the carbon concentration be 0.15 wt% after a 10-h treatment? The value of D at 1400 K is 6.9 × 10-11 m2 /s. Solution This problem asks that we determine the position at which the carbon concentration is 0.15 wt% after a 10- h heat treatment at 1325 K when C0 = 0.35 wt% C. From Equation 5.5 Cx − C0 Cs − C0 = 0.15 − 0.35 0 − 0.35 = 0.5714 = 1 − erf x 2 Dt Thus, erf x 2 Dt = 0.4286 Using data in Table 5.1 and linear interpolation z erf (z) 0.40 0.4284 z 0.4286 0.45 0.4755 z − 0.40 0.45 − 0.40 = 0.4286 − 0.4284 0.4755 − 0.4284 And, z = 0.4002 Which means that x 2 Dt = 0.4002 And, finally
- 197. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. x = 2(0.4002) Dt = (0.8004) (6.9 × 10−11 m2/s)(3.6 × 104 s) = 1.26 × 10-3 m = 1.26 mm Note: this problem may also be solved using the “Diffusion” module in the VMSE software. Open the “Diffusion” module, click on the “Diffusion Design” submodule, and then do the following: 1. Enter the given data in left-hand window that appears. In the window below the label “D Value” enter the value of the diffusion coefficient—viz. “6.9e-11”. 2. In the window just below the label “Initial, C0” enter the initial concentration—viz. “0.35”. 3. In the window the lies below “Surface, Cs” enter the surface concentration—viz. “0”. 4. Then in the “Diffusion Time t” window enter the time in seconds; in 10 h there are (60 s/min)(60 min/h)(10 h) = 36,000 s—so enter the value “3.6e4”. 5. Next, at the bottom of this window click on the button labeled “Add curve”. 6. On the right portion of the screen will appear a concentration profile for this particular diffusion situation. A diamond-shaped cursor will appear at the upper left-hand corner of the resulting curve. Click and drag this cursor down the curve to the point at which the number below “Concentration:” reads “0.15 wt%”. Then read the value under the “Distance:”. For this problem, this value (the solution to the problem) is ranges between 1.24 and 1.30 mm.
- 198. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.13 Nitrogen from a gaseous phase is to be diffused into pure iron at 700°C. If the surface concentration is maintained at 0.1 wt% N, what will be the concentration 1 mm from the surface after 10 h? The diffusion coefficient for nitrogen in iron at 700°C is 2.5 × 10-11 m2 /s. Solution This problem asks us to compute the nitrogen concentration (Cx ) at the 1 mm position after a 10 h diffusion time, when diffusion is nonsteady-state. From Equation 5.5 Cx − C0 Cs − C0 = Cx − 0 0.1 − 0 = 1 − erf x 2 Dt = 1 − erf 10−3 m (2) (2.5 × 10−11 m2/s)(10 h)(3600 s /h) = 1 – erf (0.527) Using data in Table 5.1 and linear interpolation z erf (z) 0.500 0.5205 0.527 y 0.550 0.5633 0.527 − 0.500 0.550 − 0.500 = y − 0.5205 0.5633 − 0.5205 from which y = erf (0.527) = 0.5436 Thus, Cx − 0 0.1 − 0 = 1.0 − 0.5436
- 199. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. This expression gives Cx = 0.046 wt% N Note: this problem may also be solved using the “Diffusion” module in the VMSE software. Open the “Diffusion” module, click on the “Diffusion Design” submodule, and then do the following: 1. Enter the given data in left-hand window that appears. In the window below the label “D Value” enter the value of the diffusion coefficient—viz. “2.5e-11”. 2. In the window just below the label “Initial, C0” enter the initial concentration—viz. “0”. 3. In the window the lies below “Surface, Cs” enter the surface concentration—viz. “0.1”. 4. Then in the “Diffusion Time t” window enter the time in seconds; in 10 h there are (60 s/min)(60 min/h)(10 h) = 36,000 s—so enter the value “3.6e4”. 5. Next, at the bottom of this window click on the button labeled “Add curve”. 6. On the right portion of the screen will appear a concentration profile for this particular diffusion situation. A diamond-shaped cursor will appear at the upper left-hand corner of the resulting curve. Click and drag this cursor down the curve to the point at which the number below “Distance:” reads “1.00 mm”. Then read the value under the “Concentration:”. For this problem, this value (the solution to the problem) is 0.05 wt%.
- 200. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.14 Consider a diffusion couple composed of two semi-infinite solids of the same metal, and that each side of the diffusion couple has a different concentration of the same elemental impurity; furthermore, assume each impurity level is constant throughout its side of the diffusion couple. For this situation, the solution to Fick’s second law (assuming that the diffusion coefficient for the impurity is independent of concentration), is as follows: Cx = C1 + C2 2 − C1 − C2 2 erf x 2 Dt (5.15) In this expression, when the x = 0 position is taken as the initial diffusion couple interface, then C1 is the impurity concentration for x < 0; likewise, C2 is the impurity content for x > 0. A diffusion couple composed of two silver-gold alloys is formed; these alloys have compositions of 98 wt% Ag–2 wt% Au and 95 wt% Ag–5 wt% Au. Determine the time this diffusion couple must be heated at 750ºC (1023 K) in order for the composition to be 2.5 wt% Au at the 50 mm position into the 2 wt% Au side of the diffusion couple. Preexponential and activation energy values for Au diffusion in Ag are 8.5 × 10–5 m2 /s and 202,100 J/mol, respectively. Solution For this platinum-gold diffusion couple for which C1 = 5 wt% Au and C2 = 2 wt% Au, we are asked to determine the diffusion time at 750°C that will give a composition of 2.5 wt% Au at the 50 µm position. Thus, for this problem, Equation 5.15 takes the form 2.5 = 5 + 2 2 − 5 − 2 2 erf 50 × 10−6 m 2 Dt It now becomes necessary to compute the diffusion coefficient at 750°C (1023 K) given that D0 = 8.5 × 10-5 m2 /s and Qd = 202,100 J/mol. From Equation 5.8 we have D = D0 exp − Qd RT = (8.5 × 10-5 m2/s) exp − 202,100 J/mol (8.31 J/mol− K)(1023 K) = 4.03 × 10-15 m2 /s Substitution of this value into the above equation leads to
- 201. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 2.5 = 5 + 2 2 − 5 − 2 2 erf 50 × 10−6 m 2 (4.03 × 10−15 m2 /s)(t) This expression reduces to the following form: 0.6667 = erf 393.8 s t Using data in Table 5.1, it is necessary to determine the value of z for which the error function is 0.6667 We use linear interpolation as follows: z erf (z) 0.650 0.6420 y 0.6667 0.700 0.6778 y − 0.650 0.700 − 0.650 = 0.6667 − 0.6420 0.6778 − 0.6420 from which y = 0.6844 = 393.8 s t And, solving for t gives t = 3.31 × 105 s = 92 h
- 202. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.15 For a steel alloy it has been determined that a carburizing heat treatment of 10-h duration will raise the carbon concentration to 0.45 wt% at a point 2.5 mm from the surface. Estimate the time necessary to achieve the same concentration at a 5.0-mm position for an identical steel and at the same carburizing temperature. Solution This problem calls for an estimate of the time necessary to achieve a carbon concentration of 0.45 wt% at a point 5.0 mm from the surface. From Equation 5.6b, x2 Dt = constant But since the temperature is constant, so also is D constant, and x2 t = constant or x1 2 t1 = x2 2 t2 Thus, (2.5 mm)2 10 h = (5.0 mm)2 t2 from which t2 = 40 h
- 203. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Factors That Influence Diffusion 5.16 Cite the values of the diffusion coefficients for the interdiffusion of carbon in both α-iron (BCC) and γ-iron (FCC) at 900°C. Which is larger? Explain why this is the case. Solution We are asked to compute the diffusion coefficients of C in both α and γ iron at 900°C. Using the data in Table 5.2, Dα = (6.2 × 10-7 m2/s) exp − 80,000 J/mol (8.31 J/mol- K)(1173 K) = 1.69 × 10-10 m2 /s Dγ = (2.3 × 10-5 m2/s) exp − 148,000 J/mol (8.31 J/mol- K)(1173 K) = 5.86 × 10-12 m2/s The D for diffusion of C in BCC α iron is larger, the reason being that the atomic packing factor is smaller than for FCC γ iron (0.68 versus 0.74—Section 3.4); this means that there is slightly more interstitial void space in the BCC Fe, and, therefore, the motion of the interstitial carbon atoms occurs more easily.
- 204. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.17 Using the data in Table 5.2, compute the value of D for the diffusion of zinc in copper at 650ºC. Solution Incorporating the appropriate data from Table 5.2 into Equation 5.8 leads to D = (2.4 × 10-5 m2/s) exp − 189,000 J/mol (8.31 J/mol- K)(650 + 273 K) = 4.8 × 10-16 m2/s Note: this problem may also be solved using the “Diffusion” module in the VMSE software. Open the “Diffusion” module, click on the “D vs 1/T Plot” submodule, and then do the following: 1. In the left-hand window that appears, click on the “Zn-Cu” pair under the “Diffusing Species”-“Host Metal” headings. 2. Next, at the bottom of this window, click the “Add Curve” button. 3. A log D versus 1/T plot then appears, with a line for the temperature dependence of the diffusion coefficient for Zn in Cu. Now under “Temp Range” in the boxes appearing below “T Max” change the temperature to either “650” C or “923” K. At the top of this curve is a diamond-shaped cursor. Click-and-drag this cursor down the line to the point at which the entry under the “Temperature (T):” label reads 923 K (inasmuch as this is the Kelvin equivalent of 650ºC). Finally, the diffusion coefficient value at this temperature is given under the label “Diff Coeff (D):”. For this problem, the value is 4.7 × 10-16 m2/s.
- 205. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.18 At what temperature will the diffusion coefficient for the diffusion of copper in nickel have a value of 6.5 × 10-17 m2 /s. Use the diffusion data in Table 5.2. Solution Solving for T from Equation 5.9a T = − Qd R(ln D − ln D0) and using the data from Table 5.2 for the diffusion of Cu in Ni (i.e., D0 = 2.7 × 10-5 m2/s and Qd = 256,000 J/mol) , we get T = − 256,000 J/mol (8.31 J/mol- K) ln (6.5 × 10-17 m2/s) − ln (2.7 × 10 -5 m2/s)[ ] = 1152 K = 879°C Note: this problem may also be solved using the “Diffusion” module in the VMSE software. Open the “Diffusion” module, click on the “D vs 1/T Plot” submodule, and then do the following: 1. In the left-hand window that appears, there is a preset set of data for several diffusion systems. Click on the box for which Cu is the diffusing species and Ni is the host metal. Next, at the bottom of this window, click the “Add Curve” button. 2. A log D versus 1/T plot then appears, with a line for the temperature dependence of the diffusion coefficient for Cu in Ni. At the top of this curve is a diamond-shaped cursor. Click-and-drag this cursor down the line to the point at which the entry under the “Diff Coeff (D):” label reads 6.5 × 10-17 m2/s. The temperature at which the diffusion coefficient has this value is given under the label “Temperature (T):”. For this problem, the value is 1153 K.
- 206. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.19 The preexponential and activation energy for the diffusion of iron in cobalt are 1.1 × 10-5 m2 /s and 253,300 J/mol, respectively. At what temperature will the diffusion coefficient have a value of 2.1 × 10-14 m2 /s? Solution For this problem we are given D0 (1.1 × 10-5 ) and Qd (253,300 J/mol) for the diffusion of Fe in Co, and asked to compute the temperature at which D = 2.1 × 10-14 m2 /s. Solving for T from Equation 5.9a yields T = Qd R(ln D0 − ln D) = 253,300 J/mol (8.31 J/mol- K) ln (1.1 × 10-5 m2/s) - ln (2.1 × 10-14 m2/s)[ ] = 1518 K = 1245°C Note: this problem may also be solved using the “Diffusion” module in the VMSE software. Open the “Diffusion” module, click on the “D vs 1/T Plot” submodule, and then do the following: 1. In the left-hand window that appears, click on the “Custom1” box. 2. In the column on the right-hand side of this window enter the data for this problem. In the window under “D0” enter preexponential value—viz. “1.1e-5”. Next just below the “Qd” window enter the activation energy value—viz. “253.3”. It is next necessary to specify a temperature range over which the data is to be plotted. The temperature at which D has the stipulated value is probably between 1000ºC and 1500ºC, so enter “1000” in the “T Min” box that is beside “C”; and similarly for the maximum temperature—enter “1500” in the box below “T Max”. 3. Next, at the bottom of this window, click the “Add Curve” button. 4. A log D versus 1/T plot then appears, with a line for the temperature dependence of the diffusion coefficient for Fe in Co. At the top of this curve is a diamond-shaped cursor. Click-and-drag this cursor down the line to the point at which the entry under the “Diff Coeff (D):” label reads 2.1 × 10-14 m2/s. The temperature at which the diffusion coefficient has this value is given under the label “Temperature (T):”. For this problem, the value is 1519 K.
- 207. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.20 The activation energy for the diffusion of carbon in chromium is 111,000 J/mol. Calculate the diffusion coefficient at 1100 K (827°C), given that D at 1400 K (1127°C) is 6.25 × 10-11 m2 /s. Solution To solve this problem it first becomes necessary to solve for D0 from Equation 5.8 as D0 = D exp Qd RT = (6.25 × 10 -11 m2/s)exp 111,000 J /mol (8.31 J/mol- K)(1400 K) = 8.7 × 10-7 m2/s Now, solving for D at 1100 K (again using Equation 5.8) gives D = (8.7 × 10-7 m2/s)exp − 111,000 J/mol (8.31 J/mol- K)(1100 K) = 4.6 × 10-12 m2 /s
- 208. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.21 The diffusion coefficients for iron in nickel are given at two temperatures: T (K) D (m2 /s) 1273 9.4 × 10–16 1473 2.4 × 10–14 (a) Determine the values of D0 and the activation energy Qd. (b) What is the magnitude of D at 1100ºC (1373 K)? Solution (a) Using Equation 5.9a, we set up two simultaneous equations with Qd and D0 as unknowns as follows: ln D1 = lnD0 − Qd R 1 T1 ln D2 = lnD0 − Qd R 1 T2 Now, solving for Qd in terms of temperatures T1 and T2 (1273 K and 1473 K) and D1 and D2 (9.4 × 10-16 and 2.4 × 10-14 m2 /s), we get Qd = − R ln D1 − ln D2 1 T1 − 1 T2 = − (8.31 J/mol- K) ln (9.4 × 10 -16) − ln (2.4 × 10 -14)[ ] 1 1273 K − 1 1473 K = 252,400 J/mol Now, solving for D0 from Equation 5.8 (and using the 1273 K value of D) D0 = D1 exp Qd RT1
- 209. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (9.4 × 10-16 m2/s)exp 252,400 J/mol (8.31 J/mol- K)(1273 K) = 2.2 × 10-5 m2/s (b) Using these values of D0 and Qd, D at 1373 K is just D = (2.2 × 10-5 m2/s)exp − 252,400 J/mol (8.31 J/mol- K)(1373 K) = 5.4 × 10-15 m2 /s Note: this problem may also be solved using the “Diffusion” module in the VMSE software. Open the “Diffusion” module, click on the “D0 and Qd from Experimental Data” submodule, and then do the following: 1. In the left-hand window that appears, enter the two temperatures from the table in the book (viz. “1273” and “1473”, in the first two boxes under the column labeled “T (K)”. Next, enter the corresponding diffusion coefficient values (viz. “9.4e-16” and “2.4e-14”). 3. Next, at the bottom of this window, click the “Plot data” button. 4. A log D versus 1/T plot then appears, with a line for the temperature dependence for this diffusion system. At the top of this window are give values for D0 and Qd; for this specific problem these values are 2.17 × 10-5 m2/s and 252 kJ/mol, respectively 5. To solve the (b) part of the problem we utilize the diamond-shaped cursor that is located at the top of the line on this plot. Click-and-drag this cursor down the line to the point at which the entry under the “Temperature (T):” label reads “1373”. The value of the diffusion coefficient at this temperature is given under the label “Diff Coeff (D):”. For our problem, this value is 5.4 × 10-15 m2/s.
- 210. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.22 The diffusion coefficients for silver in copper are given at two temperatures: T (°C) D (m2 /s) 650 5.5 × 10–16 900 1.3 × 10–13 (a) Determine the values of D0 and Qd. (b) What is the magnitude of D at 875°C? Solution (a) Using Equation 5.9a, we set up two simultaneous equations with Qd and D0 as unknowns as follows: ln D1 = lnD0 − Qd R 1 T1 ln D2 = lnD0 − Qd R 1 T2 Solving for Qd in terms of temperatures T1 and T2 (923 K [650°C] and 1173 K [900°C]) and D1 and D2 (5.5 × 10- 16 and 1.3 × 10-13 m2 /s), we get Qd = − R ln D1 − ln D2 1 T1 − 1 T2 = − (8.31 J/mol- K) ln (5.5 × 10 -16) − ln (1.3 × 10 -13)[ ] 1 923 K − 1 1173 K = 196,700 J/mol Now, solving for D0 from Equation 5.8 (and using the 650°C value of D) D0 = D1 exp Qd RT1
- 211. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (5.5 × 10-16 m2/s)exp 196,700 J/mol (8.31 J/mol- K)(923 K) = 7.5 × 10-5 m2/s (b) Using these values of D0 and Qd, D at 1148 K (875°C) is just D = (7.5 × 10-5 m2/s)exp − 196,700 J/mol (8.31 J/mol- K)(1148 K) = 8.3 × 10-14 m2/s Note: this problem may also be solved using the “Diffusion” module in the VMSE software. Open the “Diffusion” module, click on the “D0 and Qd from Experimental Data” submodule, and then do the following: 1. In the left-hand window that appears, enter the two temperatures from the table in the book (converted from degrees Celsius to Kelvins) (viz. “923” (650ºC) and “1173” (900ºC), in the first two boxes under the column labeled “T (K)”. Next, enter the corresponding diffusion coefficient values (viz. “5.5e-16” and “1.3e-13”). 3. Next, at the bottom of this window, click the “Plot data” button. 4. A log D versus 1/T plot then appears, with a line for the temperature dependence for this diffusion system. At the top of this window are give values for D0 and Qd; for this specific problem these values are 7.55 × 10-5 m2/s and 196 kJ/mol, respectively 5. To solve the (b) part of the problem we utilize the diamond-shaped cursor that is located at the top of the line on this plot. Click-and-drag this cursor down the line to the point at which the entry under the “Temperature (T):” label reads “1148” (i.e., 875ºC). The value of the diffusion coefficient at this temperature is given under the label “Diff Coeff (D):”. For our problem, this value is 8.9 × 10-14 m2/s.
- 212. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.23 Below is shown a plot of the logarithm (to the base 10) of the diffusion coefficient versus reciprocal of the absolute temperature, for the diffusion of iron in chromium. Determine values for the activation energy and preexponential. Solution This problem asks us to determine the values of Qd and D0 for the diffusion of Fe in Cr from the plot of log D versus 1/T. According to Equation 5.9b the slope of this plot is equal to − Qd 2.3R (rather than − Qd R since we are using log D rather than ln D) and the intercept at 1/T = 0 gives the value of log D0 . The slope is equal to slope = ∆ (log D) ∆ 1 T = log D1 − log D2 1 T1 − 1 T2 Taking 1/T1 and 1/T2 as 0.65 × 10-3 and 0.60 × 10-3 K-1 , respectively, then the corresponding values of D1 and D2 are 2.81 × 10-16 and 1.82 × 10-15 , as noted in the figure below.
- 213. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The values of log D1 and log D2 are –15.60 and –14.74, and therefore, Qd = − 2.3 R (slope) Qd = − 2.3 R log D1 − log D2 1 T1 − 1 T2 = − (2.3)(8.31 J/mol- K) −15.60 − (−14.74) (0.65 × 10−3 − 0.60 × 10−3) K−1 = 329,000 J/mol Rather than trying to make a graphical extrapolation to determine D0 , a more accurate value is obtained analytically using Equation 5.9b taking a specific value of both D and T (from 1/T) from the plot given in the problem; for example, D = 1.0 × 10-15 m2/s at T = 1626 K (1/T = 0.615 × 10-3 K-1 ). Therefore D0 = D exp Qd RT = (1.0 × 10-15 m2/s)exp 329,000 J/mol (8.31 J/mol- K)(1626 K) = 3.75 × 10-5 m2/s
- 214. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.24 Carbon is allowed to diffuse through a steel plate 15 mm thick. The concentrations of carbon at the two faces are 0.65 and 0.30 kg C/m3 Fe, which are maintained constant. If the preexponential and activation energy are 6.2 × 10-7 m2 /s and 80,000 J/mol, respectively, compute the temperature at which the diffusion flux is 1.43 × 10-9 kg/m2 -s. Solution Combining Equations 5.3 and 5.8 yields J = − D ∆C ∆x = − D0 ∆C ∆x exp − Qd RT Solving for T from this expression leads to T = Qd R 1 ln − D0∆C J ∆x And incorporation of values provided in the problem statement yields = 80,000 J/mol 8.31 J/mol- K 1 ln (6.2 × 10−7 m2 /s)(0.65 kg/m3 − 0.30 kg/m3) (1.43 × 10−9 kg/m2 - s)(15 × 10−3 m) = 1044 K = 771°C
- 215. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.25 The steady-state diffusion flux through a metal plate is 5.4 × 10-10 kg/m2 -s at a temperature of 727°C (1000 K) and when the concentration gradient is -350 kg/m4 . Calculate the diffusion flux at 1027°C (1300 K) for the same concentration gradient and assuming an activation energy for diffusion of 125,000 J/mol. Solution In order to solve this problem, we must first compute the value of D0 from the data given at 727°C (1000 K); this requires the combining of both Equations 5.3 and 5.8 as J = − D ∆C ∆x = − D0 ∆C ∆x exp − Qd RT Solving for D0 from the above expression gives D0 = − J ∆C ∆x exp Qd RT = − 5.4 × 10−10 kg/m2 - s − 350 kg /m4 exp 125,000 J/mol (8.31 J/mol- K)(1000 K) = 5.26 × 10-6 m2/s The value of the diffusion flux at 1300 K may be computed using these same two equations as follows: J = − D0 ∆C ∆ x exp − Qd RT = − (5.26 × 10-6 m2/s)(−350 kg/m4 )exp − 125,000 J/mol (8.31 J/mol- K)(1300 K) = 1.74 × 10-8 kg/m2-s
- 216. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.26 At approximately what temperature would a specimen of γ-iron have to be carburized for 2 h to produce the same diffusion result as at 900°C for 15 h? Solution To solve this problem it is necessary to employ Equation 5.7 Dt = constant Which, for this problem, takes the form D900t900 = DTtT At 900°C, and using the data from Table 5.2, for the diffusion of carbon in γ-iron—i.e., D0 = 2.3 × 10-5 m2/s Qd = 148,000 J/mol the diffusion coefficient is equal to D900 = (2.3 × 10-5 m2/s)exp − 148,000 J/mol (8.31 J/mol- K)(900 + 273 K) = 5.9 × 10-12 m2 /s Thus, from the above equation (5.9 × 10-12 m2/s)(15 h) = DT (2 h) And, solving for DT DT = (5.9 × 10-12 m2/s)(15 h) 2 h = 4.43 × 10 -11 m2/s Now, solving for T from Equation 5.9a gives T = − Qd R(ln DT − ln D0)
- 217. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = − 148,000 J/mol (8.31 J/mol- K) ln (4.43 × 10-11 m2/s) − ln (2.3 × 10-5 m2/s)[ ] = 1353 K = 1080°C
- 218. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.27 (a) Calculate the diffusion coefficient for copper in aluminum at 500ºC. (b) What time will be required at 600ºC to produce the same diffusion result (in terms of concentration at a specific point) as for 10 h at 500ºC? Solution (a) We are asked to calculate the diffusion coefficient for Cu in Al at 500°C. Using the data in Table 5.2 and Equation 5.8 D = D0 exp − Qd RT = (6.5 × 10-5 m2/s)exp − 136,000 J /mol (8.31 J/mol- K)(500 + 273 K) = 4.15 × 10-14 m2/s (b) This portion of the problem calls for the time required at 600°C to produce the same diffusion result as for 10 h at 500°C. Equation 5.7 is employed as D500t500 = D600t600 Now, from Equation 5.8 the value of the diffusion coefficient at 600°C is calculated as D600 = (6.5 × 10-5 m2/s)exp − 136,000 J/mol (8.31 J/mol- K)(600 + 273 K) = 4.69 × 10-13 m2/s Thus, t600 = D500t500 D600 = (4.15 × 10−14 m2 /s)(10 h) (4.69 × 10−13 m2 /s) = 0.88 h
- 219. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.28 A copper-nickel diffusion couple similar to that shown in Figure 5.1a is fashioned. After a 700-h heat treatment at 1100°C (1373 K) the concentration of Cu is 2.5 wt% at the 3.0-mm position within the nickel. At what temperature must the diffusion couple need to be heated to produce this same concentration (i.e., 2.5 wt% Cu) at a 2.0-mm position after 700 h? The preexponential and activation energy for the diffusion of Cu in Ni are given in Table 5.2. Solution In order to determine the temperature to which the diffusion couple must be heated so as to produce a concentration of 2.5 wt% Ni at the 2.0-mm position, we must first utilize Equation 5.6b with time t being a constant. That is x2 D = constant Or x1100 2 D1100 = xT 2 DT Now, solving for DT from this equation, yields DT = xT 2 D1100 x1100 2 and incorporating the temperature dependence of D1100 utilizing Equation (5.8), realizing that for the diffusion of Cu in Ni (Table 5.2) D0 = 2.7 × 10-5 m2 /s Qd = 256,000 J/mol then DT = xT 2 ( )D0 exp − Qd RT x1100 2 = (2 mm)2 (2.7 × 10−5 m2/s)exp − 256,000 J/mol (8.31 J/mol- K)(1373 K) (3 mm)2
- 220. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = 2.16 × 10-15 m2/s We now need to find the T at which D has this value. This is accomplished by rearranging Equation 5.9a and solving for T as T = Qd R (lnD0 − lnD) = 256,000 J/mol (8.31 J/mol- K) ln (2.7 × 10-5 m2/s) − ln (2.16 × 10-15 m2/s)[ ] = 1325 K = 1052°C
- 221. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.29 A diffusion couple similar to that shown in Figure 5.1a is prepared using two hypothetical metals A and B. After a 30-h heat treatment at 1000 K (and subsequently cooling to room temperature) the concentration of A in B is 3.2 wt% at the 15.5-mm position within metal B. If another heat treatment is conducted on an identical diffusion couple, only at 800 K for 30 h, at what position will the composition be 3.2 wt% A? Assume that the preexponential and activation energy for the diffusion coefficient are 1.8 × 10-5 m2 /s and 152,000 J/mol, respectively. Solution In order to determine the position within the diffusion couple at which the concentration of A in B is 3.2 wt%, we must employ Equation 5.6b with t constant. That is x2 D = constant Or x800 2 D800 = x1000 2 D1000 It is first necessary to compute values for both D800 and D1000; this is accomplished using Equation 5.8 as follows: D800 = (1.8 × 10-5 m2/s)exp − 152,000 J/mol (8.31 J/mol- K)(800K) = 2.12 × 10-15 m2/s D1000 = (1.8 × 10-5 m2/s)exp − 152,000 J/mol (8.31 J/mol- K)(1000 K) = 2.05 × 10-13 m2/s Now, solving the above expression for x800 yields x800 = x1000 D800 D1000
- 222. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (15.5 mm) 2.12 × 10−15 m2 /s 2.05 × 10−13 m2 /s = 1.6 mm
- 223. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.30 The outer surface of a steel gear is to be hardened by increasing its carbon content. The carbon is to be supplied from an external carbon-rich atmosphere, which is maintained at an elevated temperature. A diffusion heat treatment at 850°C (1123 K) for 10 min increases the carbon concentration to 0.90 wt% at a position 1.0 mm below the surface. Estimate the diffusion time required at 650°C (923 K) to achieve this same concentration also at a 1.0-mm position. Assume that the surface carbon content is the same for both heat treatments, which is maintained constant. Use the diffusion data in Table 5.2 for C diffusion in α-Fe. Solution In order to compute the diffusion time at 650°C to produce a carbon concentration of 0.90 wt% at a position 1.0 mm below the surface we must employ Equation 5.6b with position (x) constant; that is Dt = constant Or D850t850 = D650t650 In addition, it is necessary to compute values for both D850 and D650 using Equation 5.8. From Table 5.2, for the diffusion of C in α-Fe, Qd = 80,000 J/mol and D0 = 6.2 × 10-7 m2/s. Therefore, D850 = (6.2 × 10-7 m2/s)exp − 80,000 J/mol (8.31 J/mol- K)(850 + 273 K) = 1.17 × 10-10 m2/s D650 = (6.2 × 10-7 m2/s)exp − 80,000 J/mol (8.31 J/mol- K)(650 + 273 K) = 1.83 × 10-11 m2/s Now, solving the original equation for t650 gives t650 = D850t850 D650
- 224. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (1.17 × 10−10 m2/s)(10 min) 1.83 × 10−11 m2 /s = 63.9 min
- 225. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.31 An FCC iron-carbon alloy initially containing 0.20 wt% C is carburized at an elevated temperature and in an atmosphere wherein the surface carbon concentration is maintained at 1.0 wt%. If after 49.5 h the concentration of carbon is 0.35 wt% at a position 4.0 mm below the surface, determine the temperature at which the treatment was carried out. Solution This problem asks us to compute the temperature at which a nonsteady-state 49.5 h diffusion anneal was carried out in order to give a carbon concentration of 0.35 wt% C in FCC Fe at a position 4.0 mm below the surface. From Equation 5.5 Cx − C0 Cs − C0 = 0.35 − 0.20 1.0 − 0.20 = 0.1875 = 1 − erf x 2 Dt Or erf x 2 Dt = 0.8125 Now it becomes necessary, using the data in Table 5.1 and linear interpolation, to determine the value of x 2 Dt . Thus z erf (z) 0.90 0.7970 y 0.8125 0.95 0.8209 y − 0.90 0.95 − 0.90 = 0.8125 − 0.7970 0.8209 − 0.7970 From which y = 0.9324 Thus, x 2 Dt = 0.9324
- 226. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. And since t = 49.5 h (178,200 s) and x = 4.0 mm (4.0 × 10-3 m), solving for D from the above equation yields D = x2 (4t)(0.9324 )2 = (4.0 × 10−3 m)2 (4)(178,200 s)(0.869) = 2.58 × 10-11 m2/s Now, in order to determine the temperature at which D has the above value, we must employ Equation 5.9a; solving this equation for T yields T = Qd R (lnD0 − lnD) From Table 5.2, D0 and Qd for the diffusion of C in FCC Fe are 2.3 × 10-5 m2 /s and 148,000 J/mol, respectively. Therefore T = 148,000 J/mol (8.31 J/mol- K) ln (2.3 × 10-5 m2/s) - ln (2.58 × 10-11 m2/s)[ ] = 1300 K = 1027°C
- 227. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Diffusion in Semiconducting Materials 5.32 Phosphorus atoms are to be diffused into a silicon wafer using both predeposition and drive-in heat treatments; the background concentration of P in this silicon material is known to be 5 × 1019 atoms/m3 . The predeposition treatment is to be conducted at 950°C for 45 minutes; the surface concentration of P is to be maintained at a constant level of 1.5 × 1026 atoms/m3 . Drive-in diffusion will be carried out at 1200°C for a period of 2.5 h. For the diffusion of P in Si, values of Qd and D0 are 3.40 eV and 1.1 × 10-4 m2 /s, respectively. (a) Calculate the value of Q0. (b) Determine the value of xj for the drive-in diffusion treatment. (c) Also for the drive-in treatment, compute the position x at which the concentration of P atoms is 1024 m- 3 . Solution (a) For this portion of the problem we are asked to determine the value of Q0 . This is possible using Equation 5.12. However, it is first necessary to determine the value of D for the predeposition treatment [Dp at Tp = 950°C (1223 K)] using Equation 5.8. Thus Dp = D0 exp − Qd kTp = (1.1 × 10−4 m2 /s) exp − 3.40 eV (8.62 × 10−5 eV/atom− K)(1223 K) = 1.08 × 10−18 m2 /s The value of Q0 may be determined as follows: Q0 = 2Cs Dpt p π = (2)(1.5 × 1026 atoms /m3) (1.08 × 10−18 m2 /s)(45 min)(60 s /min) π = 9.14 × 1018 atoms /m2 (b) Computation of the junction depth requires that we use Equation 5.13. However, before this is possible it is necessary to calculate D at the temperature of the drive-in treatment [Dd at 1200°C (1473 K)]. Thus,
- 228. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Dd = (1.1 × 10−4 m2 /s) exp − 3.40 eV (8.62 × 10−5 eV/atom− K)(1473 K) = 2.58 × 10−16 m2 /s Now from Equation 5.13 x j = (4Ddtd ) ln Q0 CB πDdtd 1/ 2 = (4)(2.58 × 10−16 m2 /s)(9000 s) ln 9.14 × 1018 atoms /m2 (5 × 1019 atoms /m3) (π)(2.58 × 10−16 m2 /s)(9000 s) 1/ 2 = 1.21 × 10−5 m = 12.1 µm (c) For a concentration of 1024 P atoms/m3 for the drive-in treatment, we compute the value of x using Equation 5.11. However, it is first necessary to manipulate Equation 5.11 so that x is the dependent variable. Taking natural logarithms of both sides leads to lnC(x, t) = ln Q0 πDdtd − x2 4Ddtd Now, rearranging and solving for x leads to x = (4Ddtd ) ln Q0 C(x,t) πDdtd 1/ 2 Now, incorporating values for Q0 and Dd determined above and taking C(x,t) = 1024 P atoms/m3 yields x = (4)(2.58 × 10−16)(9000) ln 9.14 × 1018 (1024 ) (π)(2.58 × 10−16)(9000) 1/ 2
- 229. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = 3.36 × 10−6 m = 3.36 µm
- 230. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.33 Aluminum atoms are to be diffused into a silicon wafer using both predeposition and drive-in heat treatments; the background concentration of Al in this silicon material is known to be 3 × 1019 atoms/m3 . The drive-in diffusion treatment is to be carried out at 1050°C for a period of 4.0 h, which gives a junction depth xj of 3.0 µm. Compute the predeposition diffusion time at 950°C if the surface concentration is maintained at a constant level of 2 × 1025 atoms/m3 . For the diffusion of Al in Si, values of Qd and D0 are 3.41 eV and 1.38 × 10-4 m2 /s, respectively.` Solution This problem asks that we compute the time for the predeposition heat treatment for the diffusion of Al in Si. In order to do this it is necessary to determine the value of Q0 from Equation 5.13. However, before doing this we must first calculate Dd , using Equation 5.8. Therefore Dd = D0 exp − Qd kTd = (1.38 × 10−4 m2 /s) exp − 3.41 eV (8.62 × 10−5 eV/atom− K)(1050°C + 273 K) = 1.43 × 10−17 m2 /s Now, solving for Q0 in Equation 5.13 leads to Q0 = CB πDdtd( )exp x j 2 4Ddtd In the problem statement we are given the following values: CB = 3 × 1019 atoms/m3 td = 4 h (14,400 s) xj = 3.0 µm = 3.0 × 10-6 m Therefore, incorporating these values into the above equation yields Q0 = (3 × 1019 atoms /m3) (π)(1.43 × 10−17 m2 /s)(14,400 s)[ ]exp (3.0 × 10−6 m)2 (4)(1.43 × 10−17 m2 /s)(14,400 s)
- 231. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = 1.34 × 1018 atoms /m2 We may now compute the value of tp using Equation 5.12. However, before this is possible it is necessary to determine Dp (at 950°C) using Equation 5.8. Thus Dp = (1.38 × 10−4 m2 /s) exp − 3.41 eV (8.62 × 10−5 eV/atom− K)(950°C + 273 K) = 1.24 × 10−18 m2 /s Now, solving for tp in Equation 5.12 we get t p = πQ0 2 4Cs 2Dp And incorporating the value of Cs provided in the problem statement (2 × 1025 atoms/m3 ) as well as values for Q0 and Dp determined above, leads to t p = π 1.34 × 1018 atoms /m2 ( ) 2 (4) 2 × 1025 atoms /m3 ( ) 2 (1.24 × 10−18 m2 /s) = 2.84 × 103 s = 47.4 min
- 232. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. DESIGN PROBLEMS Steady-State Diffusion 5.D1 It is desired to enrich the partial pressure of hydrogen in a hydrogen-nitrogen gas mixture for which the partial pressures of both gases are 0.1013 MPa (1 atm). It has been proposed to accomplish this by passing both gases through a thin sheet of some metal at an elevated temperature; inasmuch as hydrogen diffuses through the plate at a higher rate than does nitrogen, the partial pressure of hydrogen will be higher on the exit side of the sheet. The design calls for partial pressures of 0.0709 MPa (0.7 atm) and 0.02026 MPa (0.2 atm), respectively, for hydrogen and nitrogen. The concentrations of hydrogen and nitrogen (CH and CN , in mol/m3 ) in this metal are functions of gas partial pressures (pH2 and pN2 , in MPa) and absolute temperature and are given by the following expressions: CH = 2.5 × 103 pH2 exp − 27.8 kJ/mol RT (5.16a) CN = 2.75 × 10−3 pN2 exp − 37.6 kJ/mol RT (5.16b) Furthermore, the diffusion coefficients for the diffusion of these gases in this metal are functions of the absolute temperature as follows: DH (m2/s) = 1.4 × 10−7 exp − 13.4 kJ/mol RT (5.17a) DN (m2/s) = 3.0 × 10−7 exp − 76.15 kJ/mol RT (5.17b) Is it possible to purify hydrogen gas in this manner? If so, specify a temperature at which the process may be carried out, and also the thickness of metal sheet that would be required. If this procedure is not possible, then state the reason(s) why. Solution This problem calls for us to ascertain whether or not a hydrogen-nitrogen gas mixture may be enriched with respect to hydrogen partial pressure by allowing the gases to diffuse through a metal sheet at an elevated temperature. If this is possible, the temperature and sheet thickness are to be specified; if such is not possible, then we are to state the reasons why. Since this situation involves steady-state diffusion, we employ Fick's first law, Equation 5.3. Inasmuch as the partial pressures on the high-pressure side of the sheet are the same, and the pressure of hydrogen on the low pressure side is 3.5 times that of nitrogen, and concentrations are proportional to the square
- 233. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. root of the partial pressure, the diffusion flux of hydrogen JH is the square root of 3.5 times the diffusion flux of nitrogen JN--i.e. JH = 3.5 JN Thus, equating the Fick's law expressions incorporating the given equations for the diffusion coefficients and concentrations in terms of partial pressures leads to the following JH = 1 ∆x × (2.5 × 103) 0.1013 MPa − 0.0709 MPa( )exp − 27.8 kJ RT (1.4 × 10−7 m2 /s)exp − 13.4 kJ RT = 3.5 JN = 3.5 ∆x × (2.75 × 103) 0.1013 MPa − 0.02026 MPa( )exp − 37.6 kJ RT (3.0 × 10−7 m2 /s)exp − 76.15 kJ RT The ∆x's cancel out, which means that the process is independent of sheet thickness. Now solving the above expression for the absolute temperature T gives T = 3237 K which value is extremely high (surely above the melting point of the metal). Thus, such a diffusion process is not possible.
- 234. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 5.D2 A gas mixture is found to contain two diatomic A and B species for which the partial pressures of both are 0.05065 MPa (0.5 atm). This mixture is to be enriched in the partial pressure of the A species by passing both gases through a thin sheet of some metal at an elevated temperature. The resulting enriched mixture is to have a partial pressure of 0.02026 MPa (0.2 atm) for gas A, and 0.01013 MPa (0.1 atm) for gas B. The concentrations of A and B (CA and CB, in mol/m3 ) are functions of gas partial pressures (pA2 and pB2 , in MPa) and absolute temperature according to the following expressions: CA = 200 pA2 exp − 25.0 kJ/mol RT (5.18a) CB = 1.0 × 10−3 pB2 exp − 30.0 kJ/mol RT (5.18b) Furthermore, the diffusion coefficients for the diffusion of these gases in the metal are functions of the absolute temperature as follows: DA (m2 /s) = 4.0 × 10−7 exp − 15.0 kJ/mol RT (5.19a) DB (m2 /s) = 2.5 × 10−6 exp − 24.0 kJ/mol RT (5.19b) Is it possible to purify the A gas in this manner? If so, specify a temperature at which the process may be carried out, and also the thickness of metal sheet that would be required. If this procedure is not possible, then state the reason(s) why. Solution This problem calls for us to ascertain whether or not an A2-B2 gas mixture may be enriched with respect to the A partial pressure by allowing the gases to diffuse through a metal sheet at an elevated temperature. If this is possible, the temperature and sheet thickness are to be specified; if such is not possible, then we are to state the reasons why. Since this situation involves steady-state diffusion, we employ Fick's first law, Equation 5.3. Inasmuch as the partial pressures on the high-pressure side of the sheet are the same, and the pressure of A2 on the low pressure side is 2.0 times that of B2, and concentrations are proportional to the square root of the partial pressure, the diffusion flux of A, JA, is the square root of 2.0 times the diffusion flux of nitrogen JB--i.e. JA = 2.0 JB Thus, equating the Fick's law expressions incorporating the given equations for the diffusion coefficients and concentrations in terms of partial pressures leads to the following
- 235. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. JA = 1 ∆x × (200) 0.05065 MPa − 0.02026 MPa( )exp − 25.0 kJ RT (4.0 × 10−7 m2 /s)exp − 15.0 kJ RT = 2.0 JB = 2.0 ∆x × (1.0 × 103) 0.05065 MPa − 0.01013 MPa( )exp − 30.0 kJ RT (2.5 × 10−6 m2 /s)exp − 24.0 kJ RT The ∆x's cancel out, which means that the process is independent of sheet thickness. Now solving the above expression for the absolute temperature T gives T = 401 K (128°C) Thus, it is possible to carry out this procedure at 401 K or 128°C.
- 236. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Nonsteady-State Diffusion 5.D3 The wear resistance of a steel shaft is to be improved by hardening its surface. This is to be accomplished by increasing the nitrogen content within an outer surface layer as a result of nitrogen diffusion into the steel. The nitrogen is to be supplied from an external nitrogen-rich gas at an elevated and constant temperature. The initial nitrogen content of the steel is 0.002 wt%, whereas the surface concentration is to be maintained at 0.50 wt%. For this treatment to be effective, a nitrogen content of 0.10 wt% must be established at a position 0.40 mm below the surface. Specify appropriate heat treatments in terms of temperature and time for temperatures between 475°C and 625°C. The preexponential and activation energy for the diffusion of nitrogen in iron are 3 × 10-7 m2 /s and 76,150 J/mol, respectively, over this temperature range. Solution This is a nonsteady-state diffusion situation; thus, it is necessary to employ Equation 5.5, utilizing the following values for the concentration parameters: C0 = 0.002 wt% N Cs = 0.50 wt% N Cx = 0.10 wt% N Therefore Cx − C0 Cs − C0 = 0.10 − 0.002 0.50 − 0.002 = 0.1968 = 1 − erf x 2 Dt And thus 1 − 0.1968 = 0.8032 = erf x 2 Dt Using linear interpolation and the data presented in Table 5.1
- 237. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. z erf (z) 0.9000 0.7970 y 0.8032 0.9500 0.8209 0.8032 − 0.7970 0.8209 − 0.7970 = y − 0.9000 0.9500 − 0.9000 From which y = x 2 Dt = 0.9130 The problem stipulates that x = 0.40 mm = 4.0 × 10-4 m. Therefore 4.0 × 10−4 m 2 Dt = 0.9130 Which leads to Dt = 4.80 × 10-8 m2 Furthermore, the diffusion coefficient depends on temperature according to Equation 5.8; and, as stipulated in the problem statement, D0 = 3 × 10-7 m2/s and Qd = 76,150 J/mol. Hence Dt = D0exp − Qd RT (t) = 4.80 × 10-8 m2 (3.0 × 10-7 m2/s)exp − 76,150 J/mol (8.31 J/mol- K)(T) (t) = 4.80 × 10−8 m2 And solving for the time t t (in s) = 0.160 exp − 9163.7 T
- 238. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Thus, the required diffusion time may be computed for some specified temperature (in K). Below are tabulated t values for three different temperatures that lie within the range stipulated in the problem. Temperature Time (°C) s h 500 22,500 6.3 550 11,000 3.1 600 5800 1.6
- 239. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Diffusion in Semiconducting Materials 5.D4 One integrated circuit design calls for the diffusion of arsenic into silicon wafers; the background concentration of As in Si is 2.5 × 1020 atoms/m3 . The predeposition heat treatment is to be conducted at 1000°C for 45 minutes, with a constant surface concentration of 8 × 1026 As atoms/m3 . At a drive-in treatment temperature of 1100°C, determine the diffusion time required for a junction depth of 1.2 µm. For this system, values of Qd and D0 are 4.10 eV and 2.29 × 10-3 m2 /s, respectively. Solution This problem asks that we compute the drive-in diffusion time for arsenic diffusion in silicon. It is first necessary to determine the value of Q0 using Equation 5.12. But before this is possible, the value of Dp at 1000°C must be computed with the aid of Equation 5.8. Thus, Dp = D0 exp − Qd kTp = (2.29 × 10−3 m2/s) exp − 4.10 eV (8.62 × 10−5 eV/atom− K)(1000°C + 273 K) = 1.36 × 10−19 m2/s Now for the computation of Q0 using Equation 5.12: Q0 = 2Cs Dpt p π = (2)(8 × 1026 atoms/m3) (1.36 × 10−19 m2/s)(45 min)(60 s/min) π = 1.73 × 1019 atoms/m2 We now desire to calculate td in Equation 5.13. Algebraic manipulation and rearrangement of this expression leads to
- 240. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. exp x j 2 4Ddtd = Q0 CB πDdtd At this point it is necessary to determine the value of Dd (at 1100°C). Thus Dd = (2.29 × 10−3 m2/s) exp − 4.10 eV (8.62 × 10−5 eV/atom− K)(1100°C + 273 K) = 2.06 × 10−18 m2/s And incorporation of values of all parameters except td in the above expression yields exp (1.2 × 10−6 m)2 (4)(2.06 × 10−18 m2/s)td = 1.73 × 1019 atoms/m2 (2.5 × 1020 atoms/m3) (π)(2.06 × 10−18 m2/s)td which expression reduces to exp 1.75 × 105 s td = 2.72 × 107 s1/ 2 td Solving for td is not a simple matter. One possibility is to use a graphing technique. Let us take the logarithm of both sides of the above equation, which gives 1.75 × 105 s td = ln 2.72 × 107 s1/ 2 td Now if we plot the terms on both left and right hand sides of this equation versus td , the value of td at the point of intersection of the two resulting curves is correct answer. Below is such a plot:
- 241. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. As noted, the two curves intersect at about 13,900 s, which corresponds to td = 3.86 h.
- 242. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 6 MECHANICAL PROPERTIES OF METALS PROBLEM SOLUTIONS Concepts of Stress and Strain 6.1 Using mechanics of materials principles (i.e., equations of mechanical equilibrium applied to a free- body diagram), derive Equations 6.4a and 6.4b. Solution This problem asks that we derive Equations 6.4a and 6.4b, using mechanics of materials principles. In Figure (a) below is shown a block element of material of cross-sectional area A that is subjected to a tensile force P. Also represented is a plane that is oriented at an angle θ referenced to the plane perpendicular to the tensile axis; the area of this plane is A' = A/cos θ. In addition, and the forces normal and parallel to this plane are labeled as P' and V', respectively. Furthermore, on the left-hand side of this block element are shown force components that are tangential and perpendicular to the inclined plane. In Figure (b) are shown the orientations of the applied stress σ, the normal stress to this plane σ', as well as the shear stress τ' taken parallel to this inclined plane. In addition, two coordinate axis systems in represented in Figure (c): the primed x and y axes are referenced to the inclined plane, whereas the unprimed x axis is taken parallel to the applied stress. Normal and shear stresses are defined by Equations 6.1 and 6.3, respectively. However, we now chose to express these stresses in terms (i.e., general terms) of normal and shear forces (P and V) as σ = P A
- 243. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. τ = V A For static equilibrium in the x' direction the following condition must be met: F∑ x' = 0 which means that PÕ− P cos θ = 0 Or that P' = P cos θ Now it is possible to write an expression for the stress σ' in terms of P' and A' using the above expression and the relationship between A and A' [Figure (a)]: σ' = PÕ AÕ = P cosθ A cosθ = P A cos2θ However, it is the case that P/A = σ; and, after making this substitution into the above expression, we have Equation 6.4a--that is σ' = σ cos 2 θ Now, for static equilibrium in the y' direction, it is necessary that FyÕ∑ = 0 = −VÕ+ Psinθ
- 244. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Or V' = Psinθ We now write an expression for τ' as τÕ= VÕ AÕ And, substitution of the above equation for V' and also the expression for A' gives τ' = VÕ AÕ = Psinθ A cosθ = P A sinθ cosθ = σ sinθ cosθ which is just Equation 6.4b.
- 245. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.2 (a) Equations 6.4a and 6.4b are expressions for normal (σ′) and shear (τ′) stresses, respectively, as a function of the applied tensile stress (σ) and the inclination angle of the plane on which these stresses are taken (θ of Figure 6.4). Make a plot on which is presented the orientation parameters of these expressions (i.e., cos2 θ and sin θ cos θ) versus θ. (b) From this plot, at what angle of inclination is the normal stress a maximum? (c) Also, at what inclination angle is the shear stress a maximum? Solution (a) Below are plotted curves of cos2θ (for σ') and sin θ cos θ (for τ') versus θ. (b) The maximum normal stress occurs at an inclination angle of 0°. (c) The maximum shear stress occurs at an inclination angle of 45°.
- 246. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Stress-Strain Behavior 6.3 A specimen of aluminum having a rectangular cross section 10 mm × 12.7 mm (0.4 in. × 0.5 in.) is pulled in tension with 35,500 N (8000 lbf) force, producing only elastic deformation. Calculate the resulting strain. Solution This problem calls for us to calculate the elastic strain that results for an aluminum specimen stressed in tension. The cross-sectional area is just (10 mm) × (12.7 mm) = 127 mm2 (= 1.27 × 10-4 m2 = 0.20 in.2); also, the elastic modulus for Al is given in Table 6.1 as 69 GPa (or 69 × 109 N/m2 ). Combining Equations 6.1 and 6.5 and solving for the strain yields ε = σ E = F A0E = 35,500 N (1.27 × 10−4 m2)(69 × 109 N/m2) = 4.1 × 10-3
- 247. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.4 A cylindrical specimen of a titanium alloy having an elastic modulus of 107 GPa (15.5 × 106 psi) and an original diameter of 3.8 mm (0.15 in.) will experience only elastic deformation when a tensile load of 2000 N (450 lbf) is applied. Compute the maximum length of the specimen before deformation if the maximum allowable elongation is 0.42 mm (0.0165 in.). Solution We are asked to compute the maximum length of a cylindrical titanium alloy specimen (before deformation) that is deformed elastically in tension. For a cylindrical specimen A0 = π d0 2 2 where d0 is the original diameter. Combining Equations 6.1, 6.2, and 6.5 and solving for l0 leads to l0 = ∆l ε = ∆l σ E Ê= ∆l E F A0 Ê= ∆l Eπ d0 2 2 F = ∆l Eπ d0 2 4F = (0.42 × 10−3 m)(107 × 109 N /m2) (π)(3.8 × 10−3 m)2 (4)(2000 N) = 0.255 m = 255 mm (10.0 in.)
- 248. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.5 A steel bar 100 mm (4.0 in.) long and having a square cross section 20 mm (0.8 in.) on an edge is pulled in tension with a load of 89,000 N (20,000 lbf), and experiences an elongation of 0.10 mm (4.0 × 10-3 in.). Assuming that the deformation is entirely elastic, calculate the elastic modulus of the steel. Solution This problem asks us to compute the elastic modulus of steel. For a square cross-section, A0 = b0 2, where b0 is the edge length. Combining Equations 6.1, 6.2, and 6.5 and solving for E, leads to E = σ ε = F A0 ∆l l0 = Fl0 b0 2 ∆ l = (89,000 N)(100 × 10−3 m) (20 × 10−3 m)2(0.10 × 10−3 m) = 223 × 109 N/m2 = 223 GPa (31.3 × 106 psi)
- 249. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.6 Consider a cylindrical titanium wire 3.0 mm (0.12 in.) in diameter and 2.5 × 104 mm (1000 in.) long. Calculate its elongation when a load of 500 N (112 lbf) is applied. Assume that the deformation is totally elastic. Solution In order to compute the elongation of the Ti wire when the 500 N load is applied we must employ Equations 6.1, 6.2, and 6.5. Solving for ∆l and realizing that for Ti, E = 107 GPa (15.5 × 106 psi) (Table 6.1), ∆l = l0ε = l0 σ E = l0F EA0 = l0F Eπ d0 2 2 = 4l0F Eπd0 2 = (4)(25 m)(500 N) (107 × 109 N/m2)(π )(3 × 10−3 m)2 = 0.0165 m = 16.5 mm (0.65 in.)
- 250. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.7 For a bronze alloy, the stress at which plastic deformation begins is 275 MPa (40,000 psi), and the modulus of elasticity is 115 GPa (16.7 × 106 psi). (a) What is the maximum load that may be applied to a specimen with a cross-sectional area of 325 mm2 (0.5 in.2 ) without plastic deformation? (b) If the original specimen length is 115 mm (4.5 in.), what is the maximum length to which it may be stretched without causing plastic deformation? Solution (a) This portion of the problem calls for a determination of the maximum load that can be applied without plastic deformation (Fy). Taking the yield strength to be 275 MPa, and employment of Equation 6.1 leads to Fy = σ y A0 = (275 × 106 N/m2)(325 × 10-6 m2) = 89,375 N (20,000 lbf) (b) The maximum length to which the sample may be deformed without plastic deformation is determined from Equations 6.2 and 6.5 as li = l0 1 + σ E = (115 mm) 1 + 275 MPa 115 × 103 MPa = 115.28 mm (4.51 in.)
- 251. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.8 A cylindrical rod of copper (E = 110 GPa, 16 × 106 psi) having a yield strength of 240 MPa (35,000 psi) is to be subjected to a load of 6660 N (1500 lbf). If the length of the rod is 380 mm (15.0 in.), what must be the diameter to allow an elongation of 0.50 mm (0.020 in.)? Solution This problem asks us to compute the diameter of a cylindrical specimen of copper in order to allow an elongation of 0.50 mm. Employing Equations 6.1, 6.2, and 6.5, assuming that deformation is entirely elastic σ = F A0 = F π d 0 2 4 = E ∆ l l0 Or, solving for d0 d0 = 4 l0F π E ∆l = (4)(380 × 10−3 m) (6660 N) (π)(110 × 109 N /m2)(0.50 × 10−3 m) = 7.65 × 10-3 m = 7.65 mm (0.30 in.)
- 252. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.9 Compute the elastic moduli for the following metal alloys, whose stress-strain behaviors may be observed in the “Tensile Tests” module of Virtual Materials Science and Engineering (VMSE): (a) titanium, (b) tempered steel, (c) aluminum, and (d) carbon steel. How do these values compare with those presented in Table 6.1 for the same metals? Solution The elastic modulus is the slope in the linear elastic region (Equation 6.10) as E = ∆σ ∆ε = σ2 − σ1 ε2 − ε1 Since stress-strain curves for all of the metals/alloys pass through the origin, we make take σ1 = 0 and ε1 = 0. Determinations of σ2 and ε2 are possible by moving the cursor to some arbitrary point in the linear region of the curve and then reading corresponding values in the “Stress” and “Strain” windows that are located below the plot. (a) For the titanium alloy, we selected σ2 = 404.2 MPa with its corresponding ε2 = 0.0038. Therefore, E = σ2 − σ1 ε2 − ε1 = 404.2 MPa − 0 MPa 0.0038 − 0 = 106,400 MPa = 106.4 GPa The elastic modulus for titanium given in Table 6.1 is 107 GPa, which is in very good agreement with this value. (b) For the tempered steel, we selected σ2 = 962.2 MPa with its corresponding ε2 = 0.0047. Therefore, E = σ2 − σ1 ε2 − ε1 = 962.2 MPa − 0 MPa 0.0047 − 0 = 204,700 MPa = 204.7 GPa
- 253. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The elastic modulus for steel given in Table 6.1 is 207 GPa, which is in reasonably good agreement with this value. (c) For the aluminum, we selected σ2 = 145.1 MPa with its corresponding ε2 = 0.0021. Therefore, E = σ2 − σ1 ε2 − ε1 = 145.1 MPa − 0 MPa 0.0021 − 0 = 69,100 MPa = 69.1 GPa The elastic modulus for aluminum given in Table 6.1 is 69 GPa, which is in excellent agreement with this value. (d) For the carbon steel, we selected σ2 = 129 MPa with its corresponding ε2 = 0.0006. Therefore, E = σ2 − σ1 ε2 − ε1 = 129 MPa − 0 MPa 0.0006 − 0 = 215,000 MPa = 215 GPa The elastic modulus for steel given in Table 6.1 is 207 GPa, which is in reasonable agreement with this value.
- 254. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.10 Consider a cylindrical specimen of a steel alloy (Figure 6.21) 10.0 mm (0.39 in.) in diameter and 75 mm (3.0 in.) long that is pulled in tension. Determine its elongation when a load of 20,000 N (4,500 lbf) is applied. Solution This problem asks that we calculate the elongation ∆l of a specimen of steel the stress-strain behavior of which is shown in Figure 6.21. First it becomes necessary to compute the stress when a load of 20,000 N is applied using Equation 6.1 as σ = F A0 = F π d0 2 2 = 20,000 N π 10.0 × 10−3 m 2 2 = 255 MPa (37,700 psi) Referring to Figure 6.21, at this stress level we are in the elastic region on the stress-strain curve, which corresponds to a strain of 0.0012. Now, utilization of Equation 6.2 to compute the value of ∆l ∆ l = εl0 = (0.0012)(75 mm) = 0.090 mm (0.0036 in.)
- 255. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.11 Figure 6.22 shows, for a gray cast iron, the tensile engineering stress–strain curve in the elastic region. Determine (a) the tangent modulus at 10.3 MPa (1500 psi), and (b) the secant modulus taken to 6.9 MPa (1000 psi). Solution (a) This portion of the problem asks that the tangent modulus be determined for the gray cast iron, the stress-strain behavior of which is shown in Figure 6.22. In the figure below is shown a tangent draw on the curve at a stress of 10.3 MPa (1500 psi). The slope of this line (i.e., ∆σ/∆ε), the tangent modulus, is computed as follows: ∆σ ∆ε = 15 MPa − 5 MPa 0.0074 − 0.0003 = 1410 MPa = 1.41 GPa (2.04 × 105 psi) (b) The secant modulus taken from the origin is calculated by taking the slope of a secant drawn from the origin through the stress-strain curve at 6.9 MPa (1,000 psi). This secant is drawn on the curve shown below:
- 256. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The slope of this line (i.e., ∆σ/∆ε), the secant modulus, is computed as follows: ∆σ ∆ε = 15 MPa − 0 MPa 0.0047 − 0 = 3190 MPa = 3.19 GPa (4.63 × 105 psi)
- 257. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.12 As noted in Section 3.15, for single crystals of some substances, the physical properties are anisotropic; that is, they are dependent on crystallographic direction. One such property is the modulus of elasticity. For cubic single crystals, the modulus of elasticity in a general [uvw] direction, Euvw, is described by the relationship 1 Euvw = 1 E 100 − 3 1 E 100 − 1 E 111 α2β2 + β2γ2 + γ2α2 ( ) where E 100 and E 111 are the moduli of elasticity in [100] and [111] directions, respectively; α, β, and γ are the cosines of the angles between [uvw] and the respective [100], [010], and [001] directions. Verify that the E〈110〉 values for aluminum, copper, and iron in Table 3.3 are correct. Solution We are asked, using the equation given in the problem statement, to verify that the modulus of elasticity values along [110] directions given in Table 3.3 for aluminum, copper, and iron are correct. The α, β, and γ parameters in the equation correspond, respectively, to the cosines of the angles between the [110] direction and [100], [010] and [001] directions. Since these angles are 45°, 45°, and 90°, the values of α, β, and γ are 0.707, 0.707, and 0, respectively. Thus, the given equation takes the form 1 E<110> = 1 E<100> − 3 1 E<100> − 1 E<111> (0.707)2(0.707)2 + (0.707)2 (0)2 + (0)2(0.707)2 [ ] = 1 E<100> − (0.75) 1 E<100> − 1 E<111> Utilizing the values of E<100> and E<111> from Table 3.3 for Al 1 E<110> = 1 63.7 GPa − (0.75) 1 63.7 GPa − 1 76.1 GPa Which leads to, E<110> = 72.6 GPa, the value cited in the table.
- 258. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. For Cu, 1 E<110> = 1 66.7 GPa − (0.75) 1 66.7 GPa − 1 191.1 GPa Thus, E<110> = 130.3 GPa, which is also the value cited in the table. Similarly, for Fe 1 E<110> = 1 125.0 GPa − (0.75) 1 125.0 GPa − 1 272.7 GPa And E<110> = 210.5 GPa, which is also the value given in the table.
- 259. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.13 In Section 2.6 it was noted that the net bonding energy EN between two isolated positive and negative ions is a function of interionic distance r as follows: EN = − A r + B rn (6.25) where A, B, and n are constants for the particular ion pair. Equation 6.25 is also valid for the bonding energy between adjacent ions in solid materials. The modulus of elasticity E is proportional to the slope of the interionic force–separation curve at the equilibrium interionic separation; that is, E ∝ dF dr ro Derive an expression for the dependence of the modulus of elasticity on these A, B, and n parameters (for the two- ion system) using the following procedure: 1. Establish a relationship for the force F as a function of r, realizing that F = dEN dr 2. Now take the derivative dF/dr. 3. Develop an expression for r0, the equilibrium separation. Since r0 corresponds to the value of r at the minimum of the EN-versus-r curve (Figure 2.8b), take the derivative dEN/dr, set it equal to zero, and solve for r, which corresponds to r0. 4. Finally, substitute this expression for r0 into the relationship obtained by taking dF/dr. Solution This problem asks that we derive an expression for the dependence of the modulus of elasticity, E, on the parameters A, B, and n in Equation 6.25. It is first necessary to take dEN/dr in order to obtain an expression for the force F; this is accomplished as follows: F = dEN dr = d − A r dr + d B rn dr = A r2 − nB r(n+1)
- 260. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The second step is to set this dEN /dr expression equal to zero and then solve for r (= r0). The algebra for this procedure is carried out in Problem 2.14, with the result that r0 = A nB 1/(1 − n) Next it becomes necessary to take the derivative of the force (dF/dr), which is accomplished as follows: dF dr = d A r2 dr + d − nB r(n+1) dr = − 2A r3 + (n)(n + 1)B r(n+2) Now, substitution of the above expression for r0 into this equation yields dF dr r0 = − 2A A nB 3/(1−n) + (n)(n + 1) B A nB (n+2)/(1−n) which is the expression to which the modulus of elasticity is proportional.
- 261. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.14 Using the solution to Problem 6.13, rank the magnitudes of the moduli of elasticity for the following hypothetical X, Y, and Z materials from the greatest to the least. The appropriate A, B, and n parameters (Equation 6.25) for these three materials are tabulated below; they yield EN in units of electron volts and r in nanometers: Material A B n X 2.5 2.0 × 10–5 8 Y 2.3 8.0 × 10–6 10.5 Z 3.0 1.5 × 10–5 9 Solution This problem asks that we rank the magnitudes of the moduli of elasticity of the three hypothetical metals X, Y, and Z. From Problem 6.13, it was shown for materials in which the bonding energy is dependent on the interatomic distance r according to Equation 6.25, that the modulus of elasticity E is proportional to E ∝ − 2A A nB 3/(1−n) + (n)(n + 1) B A nB (n+2)/(1−n) For metal X, A = 2.5, B = 2.0 × 10-5, and n = 8. Therefore, E ∝ − (2)(2.5) 2.5 (8)(2 × 10−5) 3/(1 − 8) + (8)(8 +1)(2 × 10−5) 2.5 (8)(2 × 10−5) (8 + 2)/(1 − 8) = 1097 For metal Y, A = 2.3, B = 8 × 10-6, and n = 10.5. Hence E ∝ − (2)(2.3) 2.3 (10.5)(8 × 10−6) 3/(1 − 10.5) + (10.5)(10.5 + 1)(8 × 10−6) 2.3 (10.5)(8 × 10−6) (10.5 + 2)/(1 − 10.5) = 551 And, for metal Z, A = 3.0, B = 1.5 × 10-5, and n = 9. Thus
- 262. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. E ∝ − (2)(3.0) 3.0 (9)(1.5 × 10−5) 3/(1 − 9) + (9)(9 + 1)(1.5 × 10−5) 3.0 (9)(1.5 × 10−5) (9 + 2)/(1 − 9) = 1024 Therefore, metal X has the highest modulus of elasticity.
- 263. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Elastic Properties of Materials 6.15 A cylindrical specimen of aluminum having a diameter of 19 mm (0.75 in.) and length of 200 mm (8.0 in.) is deformed elastically in tension with a force of 48,800 N (11,000 lbf). Using the data contained in Table 6.1, determine the following: (a) The amount by which this specimen will elongate in the direction of the applied stress. (b) The change in diameter of the specimen. Will the diameter increase or decrease? Solution (a) We are asked, in this portion of the problem, to determine the elongation of a cylindrical specimen of aluminum. Combining Equations 6.1, 6.2, and 6.5, leads to σ = Eε F π d0 2 4 = E ∆ l l0 Or, solving for ∆l (and realizing that E = 69 GPa, Table 6.1), yields ∆ l = 4F l0 π d0 2E = (4)(48,800 N)(200 × 10−3 m) (π)(19 × 10−3 m)2(69 × 109 N /m2) = 5 × 10-4 m = 0.50 mm (0.02 in.) (b) We are now called upon to determine the change in diameter, ∆d. Using Equation 6.8 ν = − εx εz = − ∆d /d0 ∆ l /l0 From Table 6.1, for aluminum, ν = 0.33. Now, solving the above expression for ∆d yields ∆d = − ν ∆l d0 l0 = − (0.33)(0.50 mm)(19 mm) 200 mm = –1.6 × 10-2 mm (–6.2 × 10-4 in.)
- 264. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The diameter will decrease.
- 265. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.16 A cylindrical bar of steel 10 mm (0.4 in.) in diameter is to be deformed elastically by application of a force along the bar axis. Using the data in Table 6.1, determine the force that will produce an elastic reduction of 3 × 10-3 mm (1.2 × 10-4 in.) in the diameter. Solution This problem asks that we calculate the force necessary to produce a reduction in diameter of 3 × 10-3 mm for a cylindrical bar of steel. For a cylindrical specimen, the cross-sectional area is equal to A0 = π d0 2 4 Now, combining Equations 6.1 and 6.5 leads to σ = F A0 = F πd0 2 4 = Eεz And, since from Equation 6.8 εz = − εx ν = − ∆d d0 ν = − ∆d νd0 Substitution of this equation into the above expression gives F πd0 2 4 = E − ∆d νd0 And, solving for F leads to F = − d0∆d π E 4ν From Table 6.1, for steel, ν = 0.30 and E = 207 GPa. Thus,
- 266. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. F = − (10 × 10−3 m)(− 3.0 × 10−6 m)(π)(207 × 109 N /m2) (4)(0.30) = 16,250 N (3770 lbf)
- 267. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.17 A cylindrical specimen of some alloy 8 mm (0.31 in.) in diameter is stressed elastically in tension. A force of 15,700 N (3530 lbf) produces a reduction in specimen diameter of 5 × 10-3 mm (2 × 10-4 in.). Compute Poisson's ratio for this material if its modulus of elasticity is 140 GPa (20.3 × 106 psi). Solution This problem asks that we compute Poisson's ratio for the metal alloy. From Equations 6.5 and 6.1 εz = σ E = F A0E = F π d0 2 2 E = 4F π d0 2 E Since the transverse strain εx is just εx = ∆d d0 and Poisson's ratio is defined by Equation 6.8, then ν = − εx εz = − ∆d /d0 4F π d0 2E = − d0∆d π E 4F = − (8 × 10−3 m)(−5 × 10−6 m) (π)(140 × 109 N /m2) (4)(15,700 N) = 0.280
- 268. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.18 A cylindrical specimen of a hypothetical metal alloy is stressed in compression. If its original and final diameters are 20.000 and 20.025 mm, respectively, and its final length is 74.96 mm, compute its original length if the deformation is totally elastic. The elastic and shear moduli for this alloy are 105 GPa and 39.7 GPa, respectively. Solution This problem asks that we compute the original length of a cylindrical specimen that is stressed in compression. It is first convenient to compute the lateral strain εx as εx = ∆d d0 = 20.025 mm− 20.000 mm 20.000 mm = 1.25 × 10-3 In order to determine the longitudinal strain εz we need Poisson's ratio, which may be computed using Equation 6.9; solving for ν yields ν = E 2G − 1 = 105 × 103 MPa (2)(39.7 × 103 MPa) − 1 = 0.322 Now εz may be computed from Equation 6.8 as εz = − εx ν = − 1.25 × 10−3 0.322 = − 3.88 × 10-3 Now solving for l0 using Equation 6.2 l0 = li 1 + εz = 74.96 mm 1 − 3.88 × 10−3 = 75.25 mm
- 269. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.19 Consider a cylindrical specimen of some hypothetical metal alloy that has a diameter of 8.0 mm (0.31 in.). A tensile force of 1000 N (225 lbf) produces an elastic reduction in diameter of 2.8 × 10-4 mm (1.10 × 10-5 in.). Compute the modulus of elasticity for this alloy, given that Poisson's ratio is 0.30. Solution This problem asks that we calculate the modulus of elasticity of a metal that is stressed in tension. Combining Equations 6.5 and 6.1 leads to E = σ εz = F A0εz = F εzπ d0 2 2 = 4F εzπ d0 2 From the definition of Poisson's ratio, (Equation 6.8) and realizing that for the transverse strain, εx= ∆d d0 εz = − εx ν = − ∆d d0ν Therefore, substitution of this expression for εz into the above equation yields E = 4F εzπ d0 2 = 4F ν π d0∆d = (4)(1000 N)(0.30) π (8 × 10−3 m)(2.8 × 10−7 m) =1.705 × 1011 Pa = 170.5 GPa (24.7 × 106 psi)
- 270. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.20 A brass alloy is known to have a yield strength of 275 MPa (40,000 psi), a tensile strength of 380 MPa (55,000 psi), and an elastic modulus of 103 GPa (15.0 × 106 psi). A cylindrical specimen of this alloy 12.7 mm (0.50 in.) in diameter and 250 mm (10.0 in.) long is stressed in tension and found to elongate 7.6 mm (0.30 in.). On the basis of the information given, is it possible to compute the magnitude of the load that is necessary to produce this change in length? If so, calculate the load. If not, explain why. Solution We are asked to ascertain whether or not it is possible to compute, for brass, the magnitude of the load necessary to produce an elongation of 7.6 mm (0.30 in.). It is first necessary to compute the strain at yielding from the yield strength and the elastic modulus, and then the strain experienced by the test specimen. Then, if ε(test) < ε(yield) deformation is elastic, and the load may be computed using Equations 6.1 and 6.5. However, if ε(test) > ε(yield) computation of the load is not possible inasmuch as deformation is plastic and we have neither a stress-strain plot nor a mathematical expression relating plastic stress and strain. We compute these two strain values as ε(test) = ∆l l0 = 7.6 mm 250 mm = 0.03 and ε(yield) = σ y E = 275 MPa 103 × 103 MPa = 0.0027 Therefore, computation of the load is not possible since ε(test) > ε(yield).
- 271. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.21 A cylindrical metal specimen 12.7 mm (0.5 in.) in diameter and 250 mm (10 in.) long is to be subjected to a tensile stress of 28 MPa (4000 psi); at this stress level the resulting deformation will be totally elastic. (a) If the elongation must be less than 0.080 mm (3.2 × 10-3 in.), which of the metals in Table 6.1 are suitable candidates? Why? (b) If, in addition, the maximum permissible diameter decrease is 1.2 × 10-3 mm (4.7 × 10-5 in.) when the tensile stress of 28 MPa is applied, which of the metals that satisfy the criterion in part (a) are suitable candidates? Why? Solution (a) This part of the problem asks that we ascertain which of the metals in Table 6.1 experience an elongation of less than 0.080 mm when subjected to a tensile stress of 28 MPa. The maximum strain that may be sustained, (using Equation 6.2) is just ε = ∆l l0 = 0.080 mm 250 mm = 3.2 × 10-4 Since the stress level is given (50 MPa), using Equation 6.5 it is possible to compute the minimum modulus of elasticity which is required to yield this minimum strain. Hence E = σ ε = 28 MPa 3.2 × 10−4 = 87.5 GPa Which means that those metals with moduli of elasticity greater than this value are acceptable candidates—namely, brass, Cu, Ni, steel, Ti and W. (b) This portion of the problem further stipulates that the maximum permissible diameter decrease is 1.2 × 10-3 mm when the tensile stress of 28 MPa is applied. This translates into a maximum lateral strain εx(max) as εx(max) = ∆d d0 = −1.2 × 10−3 mm 12.7 mm = − 9.45 × 10-5 But, since the specimen contracts in this lateral direction, and we are concerned that this strain be less than 9.45 × 10-5, then the criterion for this part of the problem may be stipulated as − ∆d d0 < 9.45 × 10-5. Now, Poisson’s ratio is defined by Equation 6.8 as
- 272. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. ν = − εx εz For each of the metal alloys let us consider a possible lateral strain, εx = ∆d d0 . Furthermore, since the deformation is elastic, then, from Equation 6.5, the longitudinal strain, εz is equal to εz = σ E Substituting these expressions for εx and εz into the definition of Poisson’s ratio we have ν = − εx εz =− ∆d d0 σ E which leads to the following: − ∆d d0 = νσ E Using values for ν and E found in Table 6.1 for the six metal alloys that satisfy the criterion for part (a), and for σ = 28 MPa, we are able to compute a − ∆d d0 for each alloy as follows: − ∆d d0 (brass) = (0.34)(28 × 106 N /m2) 97 × 109 N /m2 = 9.81 × 10−5 − ∆d d0 (copper) = (0.34)(28 × 106 N /m2) 110 × 109 N /m2 = 8.65 × 10−5 − ∆d d0 (titanium) = (0.34)(28 × 106 N /m2) 107 × 109 N /m2 = 8.90 × 10−5 − ∆d d0 (nickel) = (0.31)(28 × 106 N /m2) 207 × 109 N /m2 = 4.19 × 10−5 − ∆d d0 (steel) = (0.30)(28 × 106 N /m2) 207 × 109 N /m2 = 4.06 × 10−5
- 273. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. − ∆d d0 (tungsten) = (0.28)(28 × 106 N /m2) 407 × 109 N /m2 = 1.93 × 10−5 Thus, of the above six alloys, only brass will have a negative transverse strain that is greater than 9.45 × 10-5. This means that the following alloys satisfy the criteria for both parts (a) and (b) of the problem: copper, titanium, nickel, steel, and tungsten.
- 274. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.22 Consider the brass alloy for which the stress-strain behavior is shown in Figure 6.12. A cylindrical specimen of this material 6 mm (0.24 in.) in diameter and 50 mm (2 in.) long is pulled in tension with a force of 5000 N (1125 lbf). If it is known that this alloy has a Poisson's ratio of 0.30, compute: (a) the specimen elongation, and (b) the reduction in specimen diameter. Solution (a) This portion of the problem asks that we compute the elongation of the brass specimen. The first calculation necessary is that of the applied stress using Equation 6.1, as σ = F A0 = F π d0 2 2 = 5000 N π 6 × 10−3 m 2 2 = 177 × 106 N/m2 =177 MPa (25,000 psi) From the stress-strain plot in Figure 6.12, this stress corresponds to a strain of about 2.0 × 10-3. From the definition of strain, Equation 6.2 ∆l = εl0 = (2.0 × 10-3)(50 mm) = 0.10 mm (4 × 10-3 in.) (b) In order to determine the reduction in diameter ∆d, it is necessary to use Equation 6.8 and the definition of lateral strain (i.e., εx = ∆d/d0 ) as follows ∆d = d0εx = − d0νεz = − (6 mm)(0.30)(2.0 × 10-3) = –3.6 × 10-3 mm (–1.4 × 10-4 in.)
- 275. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.23 A cylindrical rod 100 mm long and having a diameter of 10.0 mm is to be deformed using a tensile load of 27,500 N. It must not experience either plastic deformation or a diameter reduction of more than 7.5 × 10-3 mm. Of the materials listed as follows, which are possible candidates? Justify your choice(s). Material Modulus of Elasticity (GPa) Yield Strength (MPa) Poisson’s Ratio Aluminum alloy 70 200 0.33 Brass alloy 101 300 0.34 Steel alloy 207 400 0.30 Titanium alloy 107 650 0.34 Solution This problem asks that we assess the four alloys relative to the two criteria presented. The first criterion is that the material not experience plastic deformation when the tensile load of 27,500 N is applied; this means that the stress corresponding to this load not exceed the yield strength of the material. Upon computing the stress σ = F A0 = F π d0 2 2 = 27,500 N π 10 × 10−3 m 2 2 = 350 × 106 N/m2 = 350 MPa Of the alloys listed, the Ti and steel alloys have yield strengths greater than 350 MPa. Relative to the second criterion (i.e., that ∆d be less than 7.5 × 10-3 mm), it is necessary to calculate the change in diameter ∆d for these three alloys. From Equation 6.8 ν = − εx εz = − ∆d d0 σ E = − E ∆d σ d0 Now, solving for ∆d from this expression, ∆d = − νσ d0 E For the steel alloy
- 276. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. ∆d = − (0.30)(350 MPa)(10 mm) 207 × 103 MPa = − 5.1 × 10-3 mm Therefore, the steel is a candidate. For the Ti alloy ∆d = − (0.34)(350 MPa)(10 mm) 107 × 103 MPa = −11.1 × 10-3 mm Hence, the titanium alloy is not a candidate.
- 277. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.24 A cylindrical rod 380 mm (15.0 in.) long, having a diameter of 10.0 mm (0.40 in.), is to be subjected to a tensile load. If the rod is to experience neither plastic deformation nor an elongation of more than 0.9 mm (0.035 in.) when the applied load is 24,500 N (5500 lbf), which of the four metals or alloys listed below are possible candidates? Justify your choice(s). Material Modulus of Elasticity (GPa) Yield Strength (MPa) Tensile Strength (MPa) Aluminum alloy 70 255 420 Brass alloy 100 345 420 Copper 110 250 290 Steel alloy 207 450 550 Solution This problem asks that we ascertain which of four metal alloys will not (1) experience plastic deformation, and (2) elongate more than 0.9 mm when a tensile load of 24,500 N is applied. It is first necessary to compute the stress using Equation 6.1; a material to be used for this application must necessarily have a yield strength greater than this value. Thus, σ = F A0 = 24,500 N π 10.0 × 10−3 m 2 2 = 312 MPa Of the metal alloys listed, only brass and steel have yield strengths greater than this stress. Next, we must compute the elongation produced in both brass and steel using Equations 6.2 and 6.5 in order to determine whether or not this elongation is less than 0.9 mm. For brass ∆l = σ l0 E = (312 MPa)(380 mm) 100 × 103 MPa = 1.19 mm Thus, brass is not a candidate. However, for steel ∆l = σ l0 E = (312 MPa)(380 mm) 207 × 103 MPa = 0.57 mm Therefore, of these four alloys, only steel satisfies the stipulated criteria.
- 278. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Tensile Properties 6.25 Figure 6.21 shows the tensile engineering stress–strain behavior for a steel alloy. (a) What is the modulus of elasticity? (b) What is the proportional limit? (c) What is the yield strength at a strain offset of 0.002? (d) What is the tensile strength? Solution Using the stress-strain plot for a steel alloy (Figure 6.21), we are asked to determine several of its mechanical characteristics. (a) The elastic modulus is just the slope of the initial linear portion of the curve; or, from the inset and using Equation 6.10 E = σ2 − σ1 ε2 − ε1 = (200 − 0) MPa (0.0010− 0) = 200 × 103 MPa = 200 GPa (29 × 106 psi) The value given in Table 6.1 is 207 GPa. (b) The proportional limit is the stress level at which linearity of the stress-strain curve ends, which is approximately 300 MPa (43,500 psi). (c) The 0.002 strain offset line intersects the stress-strain curve at approximately 400 MPa (58,000 psi). (d) The tensile strength (the maximum on the curve) is approximately 515 MPa (74,700 psi).
- 279. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.26 A cylindrical specimen of a brass alloy having a length of 60 mm (2.36 in.) must elongate only 10.8 mm (0.425 in.) when a tensile load of 50,000 N (11,240 lbf) is applied. Under these circumstances, what must be the radius of the specimen? Consider this brass alloy to have the stress-strain behavior shown in Figure 6.12. Solution We are asked to calculate the radius of a cylindrical brass specimen in order to produce an elongation of 10.8 mm when a load of 50,000 N is applied. It first becomes necessary to compute the strain corresponding to this elongation using Equation 6.2 as ε = ∆l l0 = 10.8 mm 60 mm = 0.18 From Figure 6.12, a stress of 420 MPa (61,000 psi) corresponds to this strain. Since for a cylindrical specimen, stress, force, and initial radius r0 are related as σ = F π r0 2 then r0 = F π σ = 50,000 N π (420 × 106 N /m2) = 0.0062 m = 6.2mm (0.24 in.)
- 280. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.27 A load of 85,000 N (19,100 lbf) is applied to a cylindrical specimen of a steel alloy (displaying the stress–strain behavior shown in Figure 6.21) that has a cross-sectional diameter of 15 mm (0.59 in.). (a) Will the specimen experience elastic and/or plastic deformation? Why? (b) If the original specimen length is 250 mm (10 in.), how much will it increase in length when this load is applied? Solution This problem asks us to determine the deformation characteristics of a steel specimen, the stress-strain behavior for which is shown in Figure 6.21. (a) In order to ascertain whether the deformation is elastic or plastic, we must first compute the stress, then locate it on the stress-strain curve, and, finally, note whether this point is on the elastic or plastic region. Thus, from Equation 6.1 σ = F A0 = 85,000 N π 15 × 10−3 m 2 2 = 481 × 106 N/m2 = 481 MPa (69,900 psi) The 481 MPa point is beyond the linear portion of the curve, and, therefore, the deformation will be both elastic and plastic. (b) This portion of the problem asks us to compute the increase in specimen length. From the stress-strain curve, the strain at 481 MPa is approximately 0.0135. Thus, from Equation 6.2 ∆l = εl0 = (0.0135)(250 mm) = 3.4 mm (0.135 in.)
- 281. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.28 A bar of a steel alloy that exhibits the stress-strain behavior shown in Figure 6.21 is subjected to a tensile load; the specimen is 300 mm (12 in.) long, and of square cross section 4.5 mm (0.175 in.) on a side. (a) Compute the magnitude of the load necessary to produce an elongation of 0.45 mm (0.018 in.). (b) What will be the deformation after the load has been released? Solution (a) We are asked to compute the magnitude of the load necessary to produce an elongation of 0.45 mm for the steel displaying the stress-strain behavior shown in Figure 6.21. First, calculate the strain, and then the corresponding stress from the plot. ε = ∆l l0 = 0.45 mm 300 mm =1.5 × 10−3 This is near the end of the elastic region; from the inset of Figure 6.21, this corresponds to a stress of about 300 MPa (43,500 psi). Now, from Equation 6.1 F = σA0 = σb2 in which b is the cross-section side length. Thus, F = (300 × 106 N/m2)(4.5 × 10-3 m)2 = 6075 N (1366 lbf ) (b) After the load is released there will be no deformation since the material was strained only elastically.
- 282. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.29 A cylindrical specimen of aluminum having a diameter of 0.505 in. (12.8 mm) and a gauge length of 2.000 in. (50.800 mm) is pulled in tension. Use the load–elongation characteristics tabulated below to complete parts (a) through (f). Load Length N lbf mm in. 0 0 50.800 2.000 7,330 1,650 50.851 2.002 15,100 3,400 50.902 2.004 23,100 5,200 50.952 2.006 30,400 6,850 51.003 2.008 34,400 7,750 51.054 2.010 38,400 8,650 51.308 2.020 41,300 9,300 51.816 2.040 44,800 10,100 52.832 2.080 46,200 10,400 53.848 2.120 47,300 10,650 54.864 2.160 47,500 10,700 55.880 2.200 46,100 10,400 56.896 2.240 44,800 10,100 57.658 2.270 42,600 9,600 58.420 2.300 36,400 8,200 59.182 2.330 Fracture (a) Plot the data as engineering stress versus engineering strain. (b) Compute the modulus of elasticity. (c) Determine the yield strength at a strain offset of 0.002. (d) Determine the tensile strength of this alloy. (e) What is the approximate ductility, in percent elongation? (f) Compute the modulus of resilience. Solution This problem calls for us to make a stress-strain plot for aluminum, given its tensile load-length data, and then to determine some of its mechanical characteristics.
- 283. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (a) The data are plotted below on two plots: the first corresponds to the entire stress-strain curve, while for the second, the curve extends to just beyond the elastic region of deformation. (b) The elastic modulus is the slope in the linear elastic region (Equation 6.10) as E = ∆σ ∆ε = 200 MPa − 0 MPa 0.0032 − 0 = 62.5 × 103 MPa = 62.5 GPa (9.1 × 106 psi)
- 284. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (c) For the yield strength, the 0.002 strain offset line is drawn dashed. It intersects the stress-strain curve at approximately 285 MPa (41,000 psi ). (d) The tensile strength is approximately 370 MPa (54,000 psi), corresponding to the maximum stress on the complete stress-strain plot. (e) The ductility, in percent elongation, is just the plastic strain at fracture, multiplied by one-hundred. The total fracture strain at fracture is 0.165; subtracting out the elastic strain (which is about 0.005) leaves a plastic strain of 0.160. Thus, the ductility is about 16%EL. (f) From Equation 6.14, the modulus of resilience is just Ur = σ y 2 2E which, using data computed above gives a value of Ur = (285 MPa)2 (2)(62.5 × 103 MPa) = 0.65 MN/m2 = 0.65 × 106 N/m2 = 6.5 × 105 J/m3 (93.8 in.- lbf/in.3)
- 285. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.30 A specimen of ductile cast iron having a rectangular cross section of dimensions 4.8 mm × 15.9 mm (3/16 in. × 5/8 in.) is deformed in tension. Using the load-elongation data tabulated below, complete problems (a) through (f). Load Length N lbf mm in. 0 0 75.000 2.953 4,740 1,065 75.025 2.954 9,140 2,055 75.050 2.955 12,920 2,900 75.075 2.956 16,540 3,720 75.113 2.957 18,300 4,110 75.150 2.959 20,170 4,530 75.225 2.962 22,900 5,145 75.375 2.968 25,070 5,635 75.525 2.973 26,800 6,025 75.750 2.982 28,640 6,440 76.500 3.012 30,240 6,800 78.000 3.071 31,100 7,000 79.500 3.130 31,280 7,030 81.000 3.189 30,820 6,930 82.500 3.248 29,180 6,560 84.000 3.307 27,190 6,110 85.500 3.366 24,140 5,430 87.000 3.425 18,970 4,265 88.725 3.493 Fracture (a) Plot the data as engineering stress versus engineering strain. (b) Compute the modulus of elasticity. (c) Determine the yield strength at a strain offset of 0.002. (d) Determine the tensile strength of this alloy. (e) Compute the modulus of resilience. (f) What is the ductility, in percent elongation? Solution
- 286. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. This problem calls for us to make a stress-strain plot for a ductile cast iron, given its tensile load-length data, and then to determine some of its mechanical characteristics. (a) The data are plotted below on two plots: the first corresponds to the entire stress-strain curve, while for the second, the curve extends just beyond the elastic region of deformation. (b) The elastic modulus is the slope in the linear elastic region (Equation 6.10) as
- 287. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. E = ∆σ ∆ε = 100 MPa − 0 MPa 0.0005 − 0 = 200 × 103 MPa = 200 GPa (29 × 106 psi) (c) For the yield strength, the 0.002 strain offset line is drawn dashed. It intersects the stress-strain curve at approximately 280 MPa (40,500 psi). (d) The tensile strength is approximately 410 MPa (59,500 psi), corresponding to the maximum stress on the complete stress-strain plot. (e) From Equation 6.14, the modulus of resilience is just Ur = σ y 2 2E which, using data computed above, yields a value of Ur = (280 × 106 N /m2)2 (2)(200 × 109 N /m2) = 1.96 × 105 J/m3 (28.3 in.- lbf/in.3) (f) The ductility, in percent elongation, is just the plastic strain at fracture, multiplied by one-hundred. The total fracture strain at fracture is 0.185; subtracting out the elastic strain (which is about 0.001) leaves a plastic strain of 0.184. Thus, the ductility is about 18.4%EL.
- 288. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.31 For the titanium alloy, whose stress strain behavior may be observed in the “Tensile Tests” module of Virtual Materials Science and Engineering (VMSE), determine the following: (a) the approximate yield strength (0.002 strain offset), (b) the tensile strength, and (c) the approximate ductility, in percent elongation. How do these values compare with those for the two Ti-6Al-4V alloys presented in Table B.4 of Appendix B? Solution (a) It is possible to do a screen capture and then print out the entire stress-strain curve for the Ti alloy. The intersection of a straight line parallel to the initial linear region of the curve and offset at a strain of 0.002 with this curve is at approximately 720 MPa. (b) The maximum reading in the stress window located below the plot as the curser point is dragged along the stress-strain curve is 1000 MPa, the value of the tensile strength. (c) The approximate percent elongation corresponds to the strain at fracture multiplied by 100 (i.e., 12%) minus the maximum elastic strain (i.e., value of strain at which the linearity of the curve ends multiplied by 100—in this case about 0.5%); this gives a value of about 11.5%EL. From Table B.4 in Appendix B, yield strength, tensile strength, and percent elongation values for the anneal Ti-6Al-4V are 830 MPa, 900 MPa, and 14%EL, while for the solution heat treated and aged alloy, the corresponding values are 1103 MPa, 1172 MPa, and 10%EL. Thus, tensile strength and percent elongation values for the VMSE alloy are slightly lower than for the annealed material in Table B.4 (720 vs 830 MPa, and 11.5 vs. 14 %EL), whereas the tensile strength is slightly higher (1000 vs. 900 MPa).
- 289. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.32 For the tempered steel alloy, whose stress strain behavior may be observed in the “Tensile Tests” module of Virtual Materials Science and Engineering (VMSE), determine the following: (a) the approximate yield strength (0.002 strain offset), (b) the tensile strength, and (c) the approximate ductility, in percent elongation. How do these values compare with those for the oil-quenched and tempered 4140 and 4340 steel alloys presented in Table B.4 of Appendix B? Solution (a) It is possible to do a screen capture and then print out the entire stress-strain curve for the tempered steel alloy. The intersection of a straight line parallel to the initial linear region of the curve and offset at a strain of 0.002 with this curve is at approximately 1430 MPa. (b) The maximum reading in the stress window located below the plot as the curser point is dragged along the stress-strain curve is 1656 MPa, the value of the tensile strength. (c) The approximate percent elongation corresponds to the strain at fracture multiplied by 100 (i.e., 14.8%) minus the maximum elastic strain (i.e., value of strain at which the linearity of the curve ends multiplied by 100—in this case about 0.8%); this gives a value of about 14.0%EL. For the oil-quenched and tempered 4140 and 4340 steel alloys, yield strength values presented in Table B.4 of Appendix B are 1570 MPa and 1620 MPa, respectively; these values are somewhat larger than the 1430 MPa for the tempered steel alloy of VMSE. Tensile strength values for these 4140 and 4340 alloys are, respectively 1720 MPa and 1760 MPa (compared to 1656 MPa for the VMSE steel). And, finally, the respective ductilities for the 4140 and 4340 alloys are 11.5%EL and 12%EL, which are slightly lower than the 14%EL value for the VMSE steel.
- 290. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.33 For the aluminum alloy, whose stress strain behavior may be observed in the “Tensile Tests” module of Virtual Materials Science and Engineering (VMSE), determine the following: (a) the approximate yield strength (0.002 strain offset), (b) the tensile strength, and (c) the approximate ductility, in percent elongation. How do these values compare with those for the 2024 aluminum alloy (T351 temper) presented in Table B.4 of Appendix B? Solution (a) It is possible to do a screen capture and then print out the entire stress-strain curve for the aluminum alloy. The intersection of a straight line parallel to the initial linear region of the curve and offset at a strain of 0.002 with this curve is at approximately 300 MPa. (b) The maximum reading in the stress window located below the plot as the curser point is dragged along the stress-strain curve is 484 MPa, the value of the tensile strength. (c) The approximate percent elongation corresponds to the strain at fracture multiplied by 100 (i.e., 22.4%) minus the maximum elastic strain (i.e., value of strain at which the linearity of the curve ends multiplied by 100—in this case about 0.5%); this gives a value of about 21.9%EL. For the 2024 aluminum alloy (T351 temper), the yield strength value presented in Table B.4 of Appendix B is 325, which is slightly larger than the 300 MPa for the aluminum alloy of VMSE. The tensile strength value for the 2024-T351 is 470 MPa (compared to 484 MPa for the VMSE alloy). And, finally, the ductility for 2024-T351 is 20%EL, which is about the same as for the VMSE aluminum (21.9%EL).
- 291. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.34 For the (plain) carbon steel alloy, whose stress strain behavior may be observed in the “Tensile Tests” module of Virtual Materials Science and Engineering (VMSE), determine the following: (a) the approximate yield strength, (b) the tensile strength, and (c) the approximate ductility, in percent elongation. Solution (a) It is possible to do a screen capture and then print out the entire stress-strain curve for the plain carbon steel alloy. Inasmuch as the stress-strain curve displays the yield point phenomenon, we take the yield strength as the lower yield point, which, for this steel, is about 225 MPa. (b) The maximum reading in the stress window located below the plot as the curser point is dragged along the stress-strain curve is 274 MPa, the value of the tensile strength. (c) The approximate percent elongation corresponds to the strain at fracture multiplied by 100 (i.e., 43.0%) minus the maximum elastic strain (i.e., value of strain at which the linearity of the curve ends multiplied by 100—in this case about 0.6%); this gives a value of about 42.4%EL.
- 292. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.35 A cylindrical metal specimen having an original diameter of 12.8 mm (0.505 in.) and gauge length of 50.80 mm (2.000 in.) is pulled in tension until fracture occurs. The diameter at the point of fracture is 6.60 mm (0.260 in.), and the fractured gauge length is 72.14 mm (2.840 in.). Calculate the ductility in terms of percent reduction in area and percent elongation. Solution This problem calls for the computation of ductility in both percent reduction in area and percent elongation. Percent reduction in area is computed using Equation 6.12 as %RA = π d0 2 2 − π df 2 2 π d0 2 2 × 100 in which d0 and df are, respectively, the original and fracture cross-sectional areas. Thus, %RA = π 12.8 mm 2 2 − π 6.60 mm 2 2 π 12.8 mm 2 2 × 100 = 73.4% While, for percent elongation, we use Equation 6.11 as %EL = lf − l0 l0 × 100 = 72.14 mm − 50.80 mm 50.80 mm × 100 = 42%
- 293. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.36 Calculate the moduli of resilience for the materials having the stress–strain behaviors shown in Figures 6.12 and 6.21. Solution This problem asks us to calculate the moduli of resilience for the materials having the stress-strain behaviors shown in Figures 6.12 and 6.21. According to Equation 6.14, the modulus of resilience Ur is a function of the yield strength and the modulus of elasticity as Ur = σ y 2 2E The values for σy and E for the brass in Figure 6.12 are determined in Example Problem 6.3 as 250 MPa (36,000 psi) and 93.8 GPa (13.6 × 106 psi), respectively. Thus Ur = (250 MPa)2 (2)(93.8 × 103 MPa) = 3.32 × 105 J/m3 (48.2 in.- lbf/in.3) Values of the corresponding parameters for the steel alloy (Figure 6.21) are determined in Problem 6.25 as 400 MPa (58,000 psi) and 200 GPa (29 × 106 psi), respectively, and therefore Ur = (400 MPa)2 (2)(200 × 103 MPa) = 4.0 × 105 J/m3 (58 in.- lbf/in.3)
- 294. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.37 Determine the modulus of resilience for each of the following alloys: Yield Strength Material MPa psi Steel alloy 550 80,000 Brass alloy 350 50,750 Aluminum alloy 250 36,250 Titanium alloy 800 116,000 Use modulus of elasticity values in Table 6.1. Solution The moduli of resilience of the alloys listed in the table may be determined using Equation 6.14. Yield strength values are provided in this table, whereas the elastic moduli are tabulated in Table 6.1. For steel Ur = σ y 2 2E = (550 × 106 N /m2)2 (2)(207 × 109 N /m2) = 7.31 × 105 J/m3 (107 in.- lbf/in.3) For the brass Ur = (350 × 106 N /m2)2 (2)(97 × 109 N /m2) = 6.31 × 105 J/m3 (92.0 in.- lbf/in.3) For the aluminum alloy Ur = (250 × 106 N /m2)2 (2)(69 × 109 N /m2) = 4.53 × 105 J/m3 (65.7 in.- lbf/in.3) And, for the titanium alloy Ur = (800 × 106 N /m2)2 (2)(107 × 109 N /m2) = 30.0× 105 J/m3 (434 in.- lbf/in.3)
- 295. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.38 A brass alloy to be used for a spring application must have a modulus of resilience of at least 0.75 MPa (110 psi). What must be its minimum yield strength? Solution The modulus of resilience, yield strength, and elastic modulus of elasticity are related to one another through Equation 6.14; the value of E for brass given in Table 6.1 is 97 GPa. Solving for σy from this expression yields σ y = 2UrE = (2) (0.75 MPa)(97 × 103 MPa) = 381 MPa (55,500 psi)
- 296. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. True Stress and Strain 6.39 Show that Equations 6.18a and 6.18b are valid when there is no volume change during deformation. Solution To show that Equation 6.18a is valid, we must first rearrange Equation 6.17 as Ai = A0 l0 li Substituting this expression into Equation 6.15 yields σT = F Ai = F A0 li l0 = σ li l0 But, from Equation 6.2 ε = li l0 − 1 Or li l0 = ε + 1 Thus, σT = σ li l0 = σ(ε + 1) For Equation 6.18b εT = ln (1 + ε) is valid since, from Equation 6.16
- 297. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. εT = ln li l0 and li l0 = ε + 1 from above.
- 298. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.40 Demonstrate that Equation 6.16, the expression defining true strain, may also be represented by ∈ T = ln A0 Ai when specimen volume remains constant during deformation. Which of these two expressions is more valid during necking? Why? Solution This problem asks us to demonstrate that true strain may also be represented by ∈ T = ln A0 Ai Rearrangement of Equation 6.17 leads to li l0 = A0 Ai Thus, Equation 6.16 takes the form ∈ T = ln li l0 = ln A0 Ai The expression ∈ T = ln A0 Ai is more valid during necking because Ai is taken as the area of the neck.
- 299. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.41 Using the data in Problem 6.28 and Equations 6.15, 6.16, and 6.18a, generate a true stress–true strain plot for aluminum. Equation 6.18a becomes invalid past the point at which necking begins; therefore, measured diameters are given below for the last four data points, which should be used in true stress computations. Load Length Diameter N lbf mm in. mm in. 46,100 10,400 56.896 2.240 11.71 0.461 42,400 10,100 57.658 2.270 10.95 0.431 42,600 9,600 58.420 2.300 10.62 0.418 36,400 8,200 59.182 2.330 9.40 0.370 Solution These true stress-strain data are plotted below.
- 300. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.42 A tensile test is performed on a metal specimen, and it is found that a true plastic strain of 0.20 is produced when a true stress of 575 MPa (83,500 psi) is applied; for the same metal, the value of K in Equation 6.19 is 860 MPa (125,000 psi). Calculate the true strain that results from the application of a true stress of 600 MPa (87,000 psi). Solution It first becomes necessary to solve for n in Equation 6.19. Taking logarithms of this expression and after rearrangement we have n = log σT − log K log εT And, incorporating values of the parameters provided in the problem statement leads to n = log (575 MPa) − log (860 MPa) log (0.20) = 0.250 Expressing εT as the dependent variable (Equation 6.19), and then solving for its value from the data stipulated in the problem statement, leads to εT = σT K 1/n = 600 MPa 860 MPa 1/0.250 = 0.237
- 301. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.43 For some metal alloy, a true stress of 415 MPa (60,175 psi) produces a plastic true strain of 0.475. How much will a specimen of this material elongate when a true stress of 325 MPa (46,125 psi) is applied if the original length is 300 mm (11.8 in.)? Assume a value of 0.25 for the strain-hardening exponent n. Solution Solution of this problem requires that we utilize Equation 6.19. It is first necessary to solve for K from the given true stress and strain. Rearrangement of this equation yields K = σT (εT )n = 415 MPa (0.475)0.25 = 500 MPa (72,500 psi) Next we must solve for the true strain produced when a true stress of 325 MPa is applied, also using Equation 6.19. Thus εT = σT K 1/n = 325 MPa 500 MPa 1/0.25 = 0.179 = ln li l0 Now, solving for li gives li = l0e0.179 = (300 mm) e0.179 = 358.8 mm (14.11 in.) And finally, the elongation ∆l is just ∆l = li − l0 = 358.8 mm− 300 mm = 58.8 mm (2.31 in.)
- 302. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.44 The following true stresses produce the corresponding true plastic strains for a brass alloy: True Stress (psi) True Strain 50,000 0.10 60,000 0.20 What true stress is necessary to produce a true plastic strain of 0.25? Solution For this problem, we are given two values of εT and σT, from which we are asked to calculate the true stress which produces a true plastic strain of 0.25. Employing Equation 6.19, we may set up two simultaneous equations with two unknowns (the unknowns being K and n), as log (50,000 psi) = log K + n log (0.10) log (60,000 psi) = log K + n log (0.20) Solving for n from these two expressions yields n = log (50,000) − log (60,000) log (0.10) − log (0.20) = 0.263 and for K log K = 4.96 or K = 104.96 = 91,623 psi Thus, for εT = 0.25 σT = K (εT )n = (91,623 psi)(0.25)0.263 = 63,700 psi (440 MPa)
- 303. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.45 For a brass alloy, the following engineering stresses produce the corresponding plastic engineering strains, prior to necking: Engineering Stress (MPa) Engineering Strain 235 0.194 250 0.296 On the basis of this information, compute the engineering stress necessary to produce an engineering strain of 0.25. Solution For this problem we first need to convert engineering stresses and strains to true stresses and strains so that the constants K and n in Equation 6.19 may be determined. Since σT = σ(1 + ε) then σT 1 = (235 MPa)(1 + 0.194) = 280 MPa σT 2 = (250 MPa)(1 + 0.296) = 324 MPa Similarly for strains, since εT = ln(1 + ε) then εT 1 = ln (1 + 0.194) = 0.177 εT 2 = ln (1 + 0.296) = 0.259 Taking logarithms of Equation 6.19, we get log σT = log K + n log εT which allows us to set up two simultaneous equations for the above pairs of true stresses and true strains, with K and n as unknowns. Thus log (280) = log K + n log (0.177) log (324) = log K + n log (0.259) Solving for these two expressions yields K = 543 MPa and n = 0.383.
- 304. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Now, converting ε = 0.25 to true strain εT = ln (1 + 0.25) = 0.223 The corresponding σT to give this value of εT (using Equation 6.19) is just σT = KεT n = (543 MPa)(0.223)0.383 = 306 MPa Now converting this value of σT to an engineering stress using Equation 6.18a gives σ = σT 1 + ε = 306 MPa 1 + 0.25 = 245 MPa
- 305. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.46 Find the toughness (or energy to cause fracture) for a metal that experiences both elastic and plastic deformation. Assume Equation 6.5 for elastic deformation, that the modulus of elasticity is 172 GPa (25 × 106 psi), and that elastic deformation terminates at a strain of 0.01. For plastic deformation, assume that the relationship between stress and strain is described by Equation 6.19, in which the values for K and n are 6900 MPa (1 × 106 psi) and 0.30, respectively. Furthermore, plastic deformation occurs between strain values of 0.01 and 0.75, at which point fracture occurs. Solution This problem calls for us to compute the toughness (or energy to cause fracture). The easiest way to do this is to integrate both elastic and plastic regions, and then add them together. Toughness = σ dε∫ = Eεdε 0 0.01 ∫ + Kεn dε 0.01 0.75 ∫ = Eε2 2 0 0.01 + K (n + 1) ε(n+1) 0.01 0.75 = 172 × 109 N/m2 2 (0.01)2 + 6900 × 106 N/m2 (1.0 + 0.3) (0.75)1.3 − (0.01)1.3 [ ] = 3.65 × 109 J/m3 (5.29 × 105 in.-lbf/in.3)
- 306. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.47 For a tensile test, it can be demonstrated that necking begins when dσT dεT = σT (6.26) Using Equation 6.19, determine the value of the true strain at this onset of necking. Solution Let us take the derivative of Equation 6.19, set it equal to σT, and then solve for εT from the resulting expression. Thus d K (εT )n [ ] d εT = Kn (εT )(n−1) = σT However, from Equation 6.19, σT = K(εT )n , which, when substituted into the above expression, yields Kn (εT )(n - 1) = K (εT )n Now solving for εT from this equation leads to εT = n as the value of the true strain at the onset of necking.
- 307. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.48 Taking the logarithm of both sides of Equation 6.19 yields log σT = log K + n log ∈ T (6.27) Thus, a plot of log σT versus log ∈ T in the plastic region to the point of necking should yield a straight line having a slope of n and an intercept (at log σT = 0) of log K. Using the appropriate data tabulated in Problem 6.29, make a plot of log σT versus log ∈ T and determine the values of n and K. It will be necessary to convert engineering stresses and strains to true stresses and strains using Equations 6.18a and 6.18b. Solution This problem calls for us to utilize the appropriate data from Problem 6.29 in order to determine the values of n and K for this material. From Equation 6.27 the slope and intercept of a log σT versus log εT plot will yield n and log K, respectively. However, Equation 6.19 is only valid in the region of plastic deformation to the point of necking; thus, only the 7th, 8th, 9th, and 10th data points may be utilized. The log-log plot with these data points is given below. The slope yields a value of 0.136 for n, whereas the intercept gives a value of 2.7497 for log K, and thus K = 102.7497 = 562 MPa.
- 308. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Elastic Recovery After Plastic Deformation 6.49 A cylindrical specimen of a brass alloy 7.5 mm (0.30 in.) in diameter and 90.0 mm (3.54 in.) long is pulled in tension with a force of 6000 N (1350 lbf); the force is subsequently released. (a) Compute the final length of the specimen at this time. The tensile stress–strain behavior for this alloy is shown in Figure 6.12. (b) Compute the final specimen length when the load is increased to 16,500 N (3700 lbf) and then released. Solution (a) In order to determine the final length of the brass specimen when the load is released, it first becomes necessary to compute the applied stress using Equation 6.1; thus σ = F A0 = F π d0 2 2 = 6000 N π 7.5 × 10−3 m 2 2 = 136 MPa (19,000 psi) Upon locating this point on the stress-strain curve (Figure 6.12), we note that it is in the linear, elastic region; therefore, when the load is released the specimen will return to its original length of 90 mm (3.54 in.). (b) In this portion of the problem we are asked to calculate the final length, after load release, when the load is increased to 16,500 N (3700 lbf). Again, computing the stress σ = 16,500 N π 7.5 × 10−3 m 2 2 = 373 MPa (52,300 psi) The point on the stress-strain curve corresponding to this stress is in the plastic region. We are able to estimate the amount of permanent strain by drawing a straight line parallel to the linear elastic region; this line intersects the strain axis at a strain of about 0.08 which is the amount of plastic strain. The final specimen length li may be determined from a rearranged form of Equation 6.2 as li = l0(1 + ε) = (90 mm)(1 + 0.08) = 97.20 mm (3.82 in.)
- 309. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.50 A steel alloy specimen having a rectangular cross section of dimensions 12.7 mm × 6.4 mm (0.5 in. × 0.25 in.) has the stress–strain behavior shown in Figure 6.21. If this specimen is subjected to a tensile force of 38,000 N (8540 lbf) then (a) Determine the elastic and plastic strain values. (b) If its original length is 460 mm (18.0 in.), what will be its final length after the load in part (a) is applied and then released? Solution (a) We are asked to determine both the elastic and plastic strain values when a tensile force of 38,000 N (8540 lbf) is applied to the steel specimen and then released. First it becomes necessary to determine the applied stress using Equation 6.1; thus σ = F A0 = F b0d0 where b0 and d0 are cross-sectional width and depth (12.7 mm and 6.4 mm, respectively). Thus σ = 38,000 N (12.7 × 10−3 m)(6.4 × 10−3 m) = 468 × 106 N /m2 = 468 MPa (68,300 psi) From Figure 6.21, this point is in the plastic region so the specimen will be both elastic and plastic strains. The total strain at this point, εt, is about 0.010. We are able to estimate the amount of permanent strain recovery εe from Hooke's law, Equation 6.5 as εe = σ E And, since E = 207 GPa for steel (Table 6.1) εe = 468 MPa 207 × 103 MPa = 0.00226 The value of the plastic strain, εp is just the difference between the total and elastic strains; that is εp = εt – εe = 0.010 – 0.00226 = 0.00774
- 310. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (b) If the initial length is 460 mm (18.0 in.) then the final specimen length li may be determined from a rearranged form of Equation 6.2 using the plastic strain value as li = l0(1 + εp) = (460 mm)(1 + 0.00774) = 463.6 mm (18.14 in.)
- 311. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Hardness 6.51 (a) A 10-mm-diameter Brinell hardness indenter produced an indentation 1.62 mm in diameter in a steel alloy when a load of 500 kg was used. Compute the HB of this material. (b) What will be the diameter of an indentation to yield a hardness of 450 HB when a 500 kg load is used? Solution (a) We are asked to compute the Brinell hardness for the given indentation. It is necessary to use the equation in Table 6.5 for HB, where P = 500 kg, d = 1.62 mm, and D = 10 mm. Thus, the Brinell hardness is computed as HB = 2P π D D − D2 − d2 [ ] = (2)(500 kg) (π)(10 mm) 10 mm − (10 mm)2 − (1.62 mm)2 [ ] = 241 (b) This part of the problem calls for us to determine the indentation diameter d which will yield a 450 HB when P = 500 kg. Solving for d from the equation in Table 6.5 gives d = D2 − D − 2P (HB)π D 2 = (10mm)2 − 10 mm − (2)(500 kg) (450)(π)(10 mm) 2 = 1.19 mm
- 312. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.52 Estimate the Brinell and Rockwell hardnesses for the following: (a) The naval brass for which the stress–strain behavior is shown in Figure 6.12. (b) The steel alloy for which the stress–strain behavior is shown in Figure 6.21. Solution This problem calls for estimations of Brinell and Rockwell hardnesses. (a) For the brass specimen, the stress-strain behavior for which is shown in Figure 6.12, the tensile strength is 450 MPa (65,000 psi). From Figure 6.19, the hardness for brass corresponding to this tensile strength is about 125 HB or 70 HRB. (b) The steel alloy (Figure 6.21) has a tensile strength of about 515 MPa (74,700 psi) [Problem 6.25(d)]. This corresponds to a hardness of about 160 HB or ~90 HRB from the line for steels in Figure 6.19. Alternately, using Equation 6.20a HB = TS(MPa) 3.45 = 515 MPa 3.45 = 149
- 313. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.53 Using the data represented in Figure 6.19, specify equations relating tensile strength and Brinell hardness for brass and nodular cast iron, similar to Equations 6.20a and 6.20b for steels. Solution These equations, for a straight line, are of the form TS = C + (E)(HB) where TS is the tensile strength, HB is the Brinell hardness, and C and E are constants, which need to be determined. One way to solve for C and E is analytically--establishing two equations using TS and HB data points on the plot, as (TS)1 = C + (E)(BH)1 (TS)2 = C + (E)(BH)2 Solving for E from these two expressions yields E = (TS)1 − (TS)2 (HB)2 − (HB)1 For nodular cast iron, if we make the arbitrary choice of (HB)1 and (HB)2 as 200 and 300, respectively, then, from Figure 6.19, (TS)1 and (TS)2 take on values of 600 MPa (87,000 psi) and 1100 MPa (160,000 psi), respectively. Substituting these values into the above expression and solving for E gives E = 600 MPa − 1100 MPa 200 HB − 300 HB = 5.0 MPa/HB (730 psi/HB) Now, solving for C yields C = (TS)1 – (E)(BH)1 = 600 MPa - (5.0 MPa/HB)(200 HB) = – 400 MPa (– 59,000 psi) Thus, for nodular cast iron, these two equations take the form
- 314. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. TS(MPa) = – 400 + 5.0 x HB TS(psi) = – 59,000 + 730 x HB Now for brass, we take (HB)1 and (HB)2 as 100 and 200, respectively, then, from Figure 7.31, (TS)1 and (TS)2 take on values of 370 MPa (54,000 psi) and 660 MPa (95,000 psi), respectively. Substituting these values into the above expression and solving for E gives E = 370 MPa − 660 MPa 100 HB − 200 HB = 2.9 MPa/HB (410 psi/HB) Now, solving for C yields C = (TS)1 – (E)(BH)1 = 370 MPa – (2.9 MPa/HB)(100 HB) = 80 MPa (13,000 psi) Thus, for brass these two equations take the form TS(MPa) = 80 + 2.9 x HB TS(psi) = 13,000 + 410 x HB
- 315. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Variability of Material Properties 6.54 Cite five factors that lead to scatter in measured material properties. Solution The five factors that lead to scatter in measured material properties are the following: (1) test method; (2) variation in specimen fabrication procedure; (3) operator bias; (4) apparatus calibration; and (5) material inhomogeneities and/or compositional differences.
- 316. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.55 Below are tabulated a number of Rockwell B hardness values that were measured on a single steel specimen. Compute average and standard deviation hardness values. 83.3 80.7 86.4 88.3 84.7 85.2 82.8 87.8 86.9 86.2 83.5 84.4 87.2 85.5 86.3 Solution The average of the given hardness values is calculated using Equation 6.21 as HRB = HRBi i=1 15 ∑ 15 = 83.3 + 88.3 + 82.8 . . . . + 86.3 15 = 85.3 And we compute the standard deviation using Equation 6.22 as follows: s = HRBi − HRB( ) 2 i=1 15 ∑ 15 − 1 = (83.3 − 85.3)2 + (88.3 − 85.3)2 + . . . . + (86.3 − 85.3)2 14 1/2 = 60.31 14 = 2.08
- 317. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Design/Safety Factors 6.56 Upon what three criteria are factors of safety based? Solution The criteria upon which factors of safety are based are (1) consequences of failure, (2) previous experience, (3) accuracy of measurement of mechanical forces and/or material properties, and (4) economics.
- 318. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.57 Determine working stresses for the two alloys that have the stress–strain behaviors shown in Figures 6.12 and 6.21. Solution The working stresses for the two alloys the stress-strain behaviors of which are shown in Figures 6.12 and 6.21 are calculated by dividing the yield strength by a factor of safety, which we will take to be 2. For the brass alloy (Figure 6.12), since σy = 250 MPa (36,000 psi), the working stress is 125 MPa (18,000 psi), whereas for the steel alloy (Figure 6.21), σy = 400 MPa (58,000 psi), and, therefore, σw = 200 MPa (29,000 psi).
- 319. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. DESIGN PROBLEMS 6.D1 A large tower is to be supported by a series of steel wires. It is estimated that the load on each wire will be 11,100 N (2500 lbf). Determine the minimum required wire diameter assuming a factor of safety of 2 and a yield strength of 1030 MPa (150,000 psi). Solution For this problem the working stress is computed using Equation 6.24 with N = 2, as σw = σ y 2 = 1030 MPa 2 = 515 MPa (75,000 psi ) Since the force is given, the area may be determined from Equation 6.1, and subsequently the original diameter d0 may be calculated as A0 = F σw = π d0 2 2 And d0 = 4F π σw = (4)(11,100 N) π (515 × 106 N /m2) = 5.23 × 10-3 m = 5.23 mm (0.206 in.)
- 320. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.D2 (a) Gaseous hydrogen at a constant pressure of 1.013 MPa (10 atm) is to flow within the inside of a thin-walled cylindrical tube of nickel that has a radius of 0.1 m. The temperature of the tube is to be 300°C and the pressure of hydrogen outside of the tube will be maintained at 0.01013 MPa (0.1 atm). Calculate the minimum wall thickness if the diffusion flux is to be no greater than 1 × 10-7 mol/m2 -s. The concentration of hydrogen in the nickel, CH (in moles hydrogen per m3 of Ni) is a function of hydrogen pressure, PH2 (in MPa) and absolute temperature (T) according to CH = 30.8 pH2 exp − 12.3 kJ/mol RT (6.28) Furthermore, the diffusion coefficient for the diffusion of H in Ni depends on temperature as DH = 4.76 × 10−7 exp − 39.56 kJ/mol RT (6.29) (b) For thin-walled cylindrical tubes that are pressurized, the circumferential stress is a function of the pressure difference across the wall (Δp), cylinder radius (r), and tube thickness (Δx) as σ = r ∆p 4 ∆x (6.30) Compute the circumferential stress to which the walls of this pressurized cylinder are exposed. (c) The room-temperature yield strength of Ni is 100 MPa (15,000 psi) and, furthermore, σy diminishes about 5 MPa for every 50°C rise in temperature. Would you expect the wall thickness computed in part (b) to be suitable for this Ni cylinder at 300°C? Why or why not? (d) If this thickness is found to be suitable, compute the minimum thickness that could be used without any deformation of the tube walls. How much would the diffusion flux increase with this reduction in thickness? On the other hand, if the thickness determined in part (c) is found to be unsuitable, then specify a minimum thickness that you would use. In this case, how much of a diminishment in diffusion flux would result? Solution (a) This portion of the problem asks for us to compute the wall thickness of a thin-walled cylindrical Ni tube at 300°C through which hydrogen gas diffuses. The inside and outside pressures are, respectively, 1.1013 and 0.01013 MPa, and the diffusion flux is to be no greater than 1 × 10-7 mol/m2-s. This is a steady-state diffusion problem, which necessitates that we employ Equation 5.3. The concentrations at the inside and outside wall faces may be determined using Equation 6.28, and, furthermore, the diffusion coefficient is computed using Equation 6.29. Solving for ∆x (using Equation 5.3) ∆x = − D ∆C J
- 321. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = − 1 1 × 10−7 mol/m2 − s × (4.76 × 10-7) exp − 39,560 J /mol (8.31 J/mol- K)(300 + 273 K) × (30.8) exp − 12,300 J/mol (8.31 J/mol- K)(300 + 273 K) 0.01013 MPa − 1.1013 MPa( ) = 0.0025 m = 2.5 mm (b) Now we are asked to determine the circumferential stress: σ = r ∆p 4 ∆x = (0.10 m)(1.013 MPa − 0.01013 MPa) (4)(0.0025 m) = 10.0 MPa (c) Now we are to compare this value of stress to the yield strength of Ni at 300°C, from which it is possible to determine whether or not the 2.5 mm wall thickness is suitable. From the information given in the problem, we may write an equation for the dependence of yield strength (σy) on temperature (T) as follows: σ y = 100 MPa − 5 MPa 50°C T − Tr( ) where Tr is room temperature and for temperature in degrees Celsius. Thus, at 300°C σ y = 100 MPa − (0.1 MPa/°C) (300°C − 20°C) = 72 MPa Inasmuch as the circumferential stress (10 MPa) is much less than the yield strength (72 MPa), this thickness is entirely suitable.
- 322. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (d) And, finally, this part of the problem asks that we specify how much this thickness may be reduced and still retain a safe design. Let us use a working stress by dividing the yield stress by a factor of safety, according to Equation 6.24. On the basis of our experience, let us use a value of 2.0 for N. Thus σw = σ y N = 72 MPa 2 = 36 MPa Using this value for σw and Equation 6.30, we now compute the tube thickness as ∆x = r ∆p 4σw = (0.10 m)(1.013 MPa − 0.01013 MPa) 4(36 MPa) = 0.00070 m = 0.70 mm Substitution of this value into Fick's first law we calculate the diffusion flux as follows: J = − D ∆C ∆x = − (4.76 × 10-7) exp − 39,560 J/mol (8.31 J/mol- K)(300 + 273 K) × (30.8) exp − 12,300 J /mol (8.31 J/mol- K)(300 + 273 K) 0.01013 MPa − 1.013 MPa( ) 0.0007 m = 3.53 × 10-7 mol/m2-s Thus, the flux increases by approximately a factor of 3.5, from 1 × 10-7 to 3.53 × 10-7 mol/m2-s with this reduction in thickness.
- 323. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 6.D3 Consider the steady-state diffusion of hydrogen through the walls of a cylindrical nickel tube as described in Problem 6.D2. One design calls for a diffusion flux of 5 × 10-8 mol/m2 -s, a tube radius of 0.125 m, and inside and outside pressures of 2.026 MPa (20 atm) and 0.0203 MPa (0.2 atm), respectively; the maximum allowable temperature is 450°C. Specify a suitable temperature and wall thickness to give this diffusion flux and yet ensure that the tube walls will not experience any permanent deformation. Solution This problem calls for the specification of a temperature and cylindrical tube wall thickness that will give a diffusion flux of 5 × 10-8 mol/m2-s for the diffusion of hydrogen in nickel; the tube radius is 0.125 m and the inside and outside pressures are 2.026 and 0.0203 MPa, respectively. There are probably several different approaches that may be used; and, of course, there is not one unique solution. Let us employ the following procedure to solve this problem: (1) assume some wall thickness, and, then, using Fick's first law for diffusion (which also employs Equations 5.3 and 6.29), compute the temperature at which the diffusion flux is that required; (2) compute the yield strength of the nickel at this temperature using the dependence of yield strength on temperature as stated in Problem 6.D2; (3) calculate the circumferential stress on the tube walls using Equation 6.30; and (4) compare the yield strength and circumferential stress values--the yield strength should probably be at least twice the stress in order to make certain that no permanent deformation occurs. If this condition is not met then another iteration of the procedure should be conducted with a more educated choice of wall thickness. As a starting point, let us arbitrarily choose a wall thickness of 2 mm (2 × 10-3 m). The steady-state diffusion equation, Equation 5.3, takes the form J = − D ∆C ∆x = 5 × 10-8 mol/m2-s = − (4.76 × 10-7)exp − 39,560 J/mol (8.31 J/mol- K)(T) × (30.8) exp − 12,300 J/mol (8.31 J/mol- K)(T) 0.0203 MPa − 2.026 MPa( ) 0.002 m Solving this expression for the temperature T gives T = 514 K = 241°C; this value is satisfactory inasmuch as it is less than the maximum allowable value (450°C). The next step is to compute the stress on the wall using Equation 6.30; thus
- 324. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. σ = r ∆p 4 ∆x = (0.125 m)(2.026 MPa − 0.0203 MPa) (4)(2 × 10−3 m) = 31.3 MPa Now, the yield strength (σy) of Ni at this temperature may be computed using the expression σ y = 100 MPa − 5 MPa 50°C T − Tr( ) where Tr is room temperature. Thus, σy = 100 MPa – (0.1 MPa/°C)(241°C – 20°C) = 77.9 MPa Inasmuch as this yield strength is greater than twice the circumferential stress, wall thickness and temperature values of 2 mm and 241°C are satisfactory design parameters.
- 325. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 7 DISLOCATIONS AND STRENGTHENING MECHANISMS PROBLEM SOLUTIONS Basic Concepts of Dislocations Characteristics of Dislocations 7.1 To provide some perspective on the dimensions of atomic defects, consider a metal specimen that has a dislocation density of 104 mm-2 . Suppose that all the dislocations in 1000 mm3 (1 cm3 ) were somehow removed and linked end to end. How far (in miles) would this chain extend? Now suppose that the density is increased to 1010 mm-2 by cold working. What would be the chain length of dislocations in 1000 mm3 of material? Solution The dislocation density is just the total dislocation length per unit volume of material (in this case per cubic millimeters). Thus, the total length in 1000 mm3 of material having a density of 104 mm-2 is just (104 mm-2)(1000 mm3) = 107 mm = 104 m = 6.2 mi Similarly, for a dislocation density of 1010 mm-2, the total length is (1010 mm-2)(1000 mm3) = 1013 mm = 1010 m = 6.2 × 106 mi
- 326. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.2 Consider two edge dislocations of opposite sign and having slip planes that are separated by several atomic distances as indicated in the diagram. Briefly describe the defect that results when these two dislocations become aligned with each other. Solution When the two edge dislocations become aligned, a planar region of vacancies will exist between the dislocations as:
- 327. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.3 Is it possible for two screw dislocations of opposite sign to annihilate each other? Explain your answer. Solution It is possible for two screw dislocations of opposite sign to annihilate one another if their dislocation lines are parallel. This is demonstrated in the figure below.
- 328. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.4 For each of edge, screw, and mixed dislocations, cite the relationship between the direction of the applied shear stress and the direction of dislocation line motion. Solution For the various dislocation types, the relationships between the direction of the applied shear stress and the direction of dislocation line motion are as follows: edge dislocation--parallel screw dislocation--perpendicular mixed dislocation--neither parallel nor perpendicular
- 329. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Slip Systems 7.5 (a) Define a slip system. (b) Do all metals have the same slip system? Why or why not? Solution (a) A slip system is a crystallographic plane, and, within that plane, a direction along which dislocation motion (or slip) occurs. (b) All metals do not have the same slip system. The reason for this is that for most metals, the slip system will consist of the most densely packed crystallographic plane, and within that plane the most closely packed direction. This plane and direction will vary from crystal structure to crystal structure.
- 330. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.6 (a) Compare planar densities (Section 3.11 and Problem 3.54) for the (100), (110), and (111) planes for FCC. (b) Compare planar densities (Problem 3.55) for the (100), (110), and (111) planes for BCC. Solution (a) For the FCC crystal structure, the planar density for the (110) plane is given in Equation 3.11 as PD110(FCC) = 1 4 R2 2 = 0.177 R2 Furthermore, the planar densities of the (100) and (111) planes are calculated in Homework Problem 3.54, which are as follows: PD100(FCC) = 1 4R2 = 0.25 R2 PD111(FCC) = 1 2R2 3 = 0.29 R2 (b) For the BCC crystal structure, the planar densities of the (100) and (110) planes were determined in Homework Problem 3.55, which are as follows: PD100(BCC) = 3 16R2 = 0.19 R2 PD110(BCC) = 3 8R2 2 = 0.27 R2 Below is a BCC unit cell, within which is shown a (111) plane.
- 331. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (a) The centers of the three corner atoms, denoted by A, B, and C lie on this plane. Furthermore, the (111) plane does not pass through the center of atom D, which is located at the unit cell center. The atomic packing of this plane is presented in the following figure; the corresponding atom positions from the Figure (a) are also noted. (b) Inasmuch as this plane does not pass through the center of atom D, it is not included in the atom count. One sixth of each of the three atoms labeled A, B, and C is associated with this plane, which gives an equivalence of one-half atom. In Figure (b) the triangle with A, B, and C at its corners is an equilateral triangle. And, from Figure (b), the area of this triangle is xy 2 . The triangle edge length, x, is equal to the length of a face diagonal, as indicated in Figure (a). And its length is related to the unit cell edge length, a, as
- 332. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. x2 = a2 + a2 = 2a2 or x = a 2 For BCC, a = 4R 3 (Equation 3.3), and, therefore, x = 4R 2 3 Also, from Figure (b), with respect to the length y we may write y2 + x 2 2 = x2 which leads to y = x 3 2 . And, substitution for the above expression for x yields y = x 3 2 = 4R 2 3 3 2 = 4R 2 2 Thus, the area of this triangle is equal to AREA = 1 2 x y = 1 2 4 R 2 3 4 R 2 2 = 8 R2 3 And, finally, the planar density for this (111) plane is PD111(BCC) = 0.5 atom 8R2 3 = 3 16R2 = 0.11 R2
- 333. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.7 One slip system for the BCC crystal structure is 110{ } 111 . In a manner similar to Figure 7.6b, sketch a 110{ }-type plane for the BCC structure, representing atom positions with circles. Now, using arrows, indicate two different 111 slip directions within this plane. Solution Below is shown the atomic packing for a BCC 110{ }-type plane. The arrows indicate two different 111 - type directions.
- 334. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.8 One slip system for the HCP crystal structure is 0001{ } 1120 . In a manner similar to Figure 7.6b, sketch a 0001{ }-type plane for the HCP structure and, using arrows, indicate three different 1120 slip directions within this plane. You might find Figure 3.8 helpful. Solution Below is shown the atomic packing for an HCP 0001{ }-type plane. The arrows indicate three different 1120 -type directions.
- 335. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.9 Equations 7.1a and 7.1b, expressions for Burgers vectors for FCC and BCC crystal structures, are of the form b = a 2 uvw where a is the unit cell edge length. Also, since the magnitudes of these Burgers vectors may be determined from the following equation: b = a 2 u2 + v2 + w2 ( ) 1/2 (7.10) determine values of |b| for aluminum and chromium. You may want to consult Table 3.1. Solution For Al, which has an FCC crystal structure, R = 0.1431 nm (Table 3.1) and a = 2R 2 = 0.4047 nm (Equation 3.1); also, from Equation 7.1a, the Burgers vector for FCC metals is b = a 2 〈110〉 Therefore, the values for u, v, and w in Equation 7.10 are 1, 1, and 0, respectively. Hence, the magnitude of the Burgers vector for Al is b = a 2 u2 + v2 + w2 = 0.4047 nm 2 (1 )2 + (1 )2 + (0)2 = 0.2862 nm For Cr which has a BCC crystal structure, R = 0.1249 nm (Table 3.1) and a = 4R 3 = 0.2884 nm (Equation 3.3); also, from Equation 7.1b, the Burgers vector for BCC metals is b = a 2 〈111〉 Therefore, the values for u, v, and w in Equation 7.10 are 1, 1, and 1, respectively. Hence, the magnitude of the Burgers vector for Cr is b = 0.2884 nm 2 (1)2 + (1)2 + (1)2 = 0.2498 nm
- 336. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.10 (a) In the manner of Equations 7.1a, 7.1b, and 7.1c, specify the Burgers vector for the simple cubic crystal structure. Its unit cell is shown in Figure 3.24. Also, simple cubic is the crystal structure for the edge dislocation of Figure 4.3, and for its motion as presented in Figure 7.1. You may also want to consult the answer to Concept Check 7.1. (b) On the basis of Equation 7.10, formulate an expression for the magnitude of the Burgers vector, |b|, for simple cubic. Solution (a) This part of the problem asks that we specify the Burgers vector for the simple cubic crystal structure (and suggests that we consult the answer to Concept Check 7.1). This Concept Check asks that we select the slip system for simple cubic from four possibilities. The correct answer is 100{ } 010 . Thus, the Burgers vector will lie in a 010 -type direction. Also, the unit slip distance is a (i.e., the unit cell edge length, Figures 4.3 and 7.1). Therefore, the Burgers vector for simple cubic is b = a 010 Or, equivalently b = a 100 (b) The magnitude of the Burgers vector, |b|, for simple cubic is b = a(12 + 02 + 02)1/ 2 = a
- 337. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Slip in Single Crystals 7.11 Sometimes cos φ cos λ in Equation 7.2 is termed the Schmid factor. Determine the magnitude of the Schmid factor for an FCC single crystal oriented with its [100] direction parallel to the loading axis. Solution We are asked to compute the Schmid factor for an FCC crystal oriented with its [100] direction parallel to the loading axis. With this scheme, slip may occur on the (111) plane and in the [110] direction as noted in the figure below. The angle between the [100] and [110] directions, λ, may be determined using Equation 7.6 λ = cos−1 u1u2 + v1v2 + w1w2 u1 2 + v1 2 + w1 2 ( )u2 2 + v2 2 + w2 2 ( ) where (for [100]) u1 = 1, v1 = 0, w1 = 0, and (for [110]) u2 = 1, v2 = -1, w2 = 0. Therefore, λ is equal to λ = cos−1 (1)(1) + (0)(−1) + (0)(0) (1)2 + (0)2 + (0)2 [ ] (1)2 + (−1)2 + (0)2 [ ] = cos−1 1 2 = 45°
- 338. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Now, the angle φ is equal to the angle between the normal to the (111) plane (which is the [111] direction), and the [100] direction. Again from Equation 7.6, and for u1 = 1, v1 = 1, w1 = 1, and u2 = 1, v2 = 0, and w2 = 0, we have φ = cos−1 (1)(1) + (1)(0) + (1)(0) (1)2 + (1)2 + (1)2 [ ] (1)2 + (0)2 + (0)2 [ ] = cos−1 1 3 = 54.7° Therefore, the Schmid factor is equal to cos λ cos φ = cos (45°) cos (54.7°) = 1 2 1 3 = 0.408
- 339. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.12 Consider a metal single crystal oriented such that the normal to the slip plane and the slip direction are at angles of 43.1° and 47.9°, respectively, with the tensile axis. If the critical resolved shear stress is 20.7 MPa (3000 psi), will an applied stress of 45 MPa (6500 psi) cause the single crystal to yield? If not, what stress will be necessary? Solution This problem calls for us to determine whether or not a metal single crystal having a specific orientation and of given critical resolved shear stress will yield. We are given that φ = 43.1°, λ = 47.9°, and that the values of the critical resolved shear stress and applied tensile stress are 20.7 MPa (3000 psi) and 45 MPa (6500 psi), respectively. From Equation 7.2 τR = σ cos φ cos λ = (45 MPa)(cos 43.1°)(cos 47.9°) = 22.0 MPa (3181 psi) Since the resolved shear stress (22 MPa) is greater than the critical resolved shear stress (20.7 MPa), the single crystal will yield.
- 340. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.13 A single crystal of aluminum is oriented for a tensile test such that its slip plane normal makes an angle of 28.1° with the tensile axis. Three possible slip directions make angles of 62.4°, 72.0°, and 81.1° with the same tensile axis. (a) Which of these three slip directions is most favored? (b) If plastic deformation begins at a tensile stress of 1.95 MPa (280 psi), determine the critical resolved shear stress for aluminum. Solution We are asked to compute the critical resolved shear stress for Al. As stipulated in the problem, φ = 28.1°, while possible values for λ are 62.4°, 72.0°, and 81.1°. (a) Slip will occur along that direction for which (cos φ cos λ) is a maximum, or, in this case, for the largest cos λ. Cosines for the possible λ values are given below. cos(62.4°) = 0.46 cos(72.0°) = 0.31 cos(81.1°) = 0.15 Thus, the slip direction is at an angle of 62.4° with the tensile axis. (b) From Equation 7.4, the critical resolved shear stress is just τcrss = σ y (cos φ cos λ)max = (1.95 MPa) cos (28.1°) cos (62.4°)[ ]= 0.80 MPa (114 psi)
- 341. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.14 Consider a single crystal of silver oriented such that a tensile stress is applied along a [001] direction. If slip occurs on a (111) plane and in a [101] direction, and is initiated at an applied tensile stress of 1.1 MPa (160 psi), compute the critical resolved shear stress. Solution This problem asks that we compute the critical resolved shear stress for silver. In order to do this, we must employ Equation 7.4, but first it is necessary to solve for the angles λ and φ which are shown in the sketch below. The angle λ is the angle between the tensile axis—i.e., along the [001] direction—and the slip direction—i.e., [101]. The angle λ may be determined using Equation 7.6 as λ = cos−1 u1u2 + v1v2 + w1w2 u1 2 + v1 2 + w1 2 ( )u2 2 + v2 2 + w2 2 ( ) where (for [001]) u1 = 0, v1 = 0, w1 = 1, and (for [101]) u2 = –1, v2 = 0, w2 = 1. Therefore, λ is equal to λ = cos−1 (0)(−1) + (0)(0) + (1)(1) (0)2 + (0)2 + (1)2 [ ] (−1)2 + (0)2 + (1)2 [ ] = cos−1 1 2 = 45°
- 342. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Furthermore, φ is the angle between the tensile axis—the [001] direction—and the normal to the slip plane—i.e., the (111) plane; for this case this normal is along a [111] direction. Therefore, again using Equation 7.6 φ = cos−1 (0)(1) + (0)(1) + (1)(1) (0)2 + (0)2 + (1)2 [ ] (1)2 + (1)2 + (1)2 [ ] = cos−1 1 3 = 54.7° And, finally, using Equation 7.4, the critical resolved shear stress is equal to τcrss = σ y (cos φ cos λ) = (1.1 MPa) cos(54.7°) cos(45°)[ ]= (1.1 MPa) 1 3 1 2 = 0.45 MPa (65.1 psi)
- 343. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.15 A single crystal of a metal that has the FCC crystal structure is oriented such that a tensile stress is applied parallel to the [110] direction. If the critical resolved shear stress for this material is 1.75 MPa, calculate the magnitude(s) of applied stress(es) necessary to cause slip to occur on the (111) plane in each of the [110], [101] and [011] directions. Solution In order to solve this problem it is necessary to employ Equation 7.4, but first we need to solve for the for λ and φ angles for the three slip systems. For each of these three slip systems, the φ will be the same—i.e., the angle between the direction of the applied stress, [110] and the normal to the (111) plane, that is, the [111] direction. The angle φ may be determined using Equation 7.6 as φ = cos−1 u1u2 + v1v2 + w1w2 u1 2 + v1 2 + w1 2 ( )u2 2 + v2 2 + w2 2 ( ) where (for [110]) u1 = 1, v1 = 1, w1 = 0, and (for [111]) u2 = 1, v2 = 1, w2 = 1. Therefore, φ is equal to φ = cos−1 (1)(1) + (1)(1) + (0)(1) (1)2 + (1)2 + (0)2 [ ] (1)2 + (1)2 + (1)2 [ ] = cos−1 2 6 = 35.3° Let us now determine λ for the [110 ] slip direction. Again, using Equation 7.6 where u1 = 1, v1 = 1, w1 = 0 (for [110]), and u2 = 1, v2 = –1, w2 = 0 (for [110]. Therefore, λ is determined as λ[110]−[110] = cos−1 (1)(1) + (1)(−1) + (0)(0) (1)2 + (1)2 + (0)2 [ ] (1)2 + (−1)2 + (0)2 [ ] = cos−1 0 = 90° Now, we solve for the yield strength for this (111)–[110] slip system using Equation 7.4 as
- 344. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. σ y = τcrss (cosφ cos λ) = 1.75 MPa cos (35.3°) cos (90°) = 1.75 MPa (0.816) (0) = ∞ which means that slip will not occur on this (111)–[110] slip system. Now, we must determine the value of λ for the (111)–[101] slip system—that is, the angle between the [110] and [101] directions. Again using Equation 7.6 λ[110]−[101] = cos−1 (1)(1) + (1)(0) + (0)(−1) (1)2 + (1)2 + (0)2 [ ] (1)2 + (0)2 + (−1)2 [ ] = cos−1 1 2 = 60° Now, we solve for the yield strength for this (111)–[101] slip system using Equation 7.4 as σ y = τcrss (cosφ cos λ) = 1.75 MPa cos (35.3°) cos (60°) = 1.75 MPa (0.816) (0.500) = 4.29 MPa And, finally, for the (111)–[011] slip system, λ is computed using Equation 7.6 as follows: λ[110]−[011] = cos−1 (1)(0) + (1)(1) + (0)(−1) (1)2 + (1)2 + (0)2 [ ] (0)2 + (1)2 + (−1)2 [ ] = cos−1 1 2 = 60° Thus, since the values of φ and λ for this (110)–[011] slip system are the same as for (111)–[101], so also will σy be the same—viz 4.29 MPa.
- 345. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.16 (a) A single crystal of a metal that has the BCC crystal structure is oriented such that a tensile stress is applied in the [010] direction. If the magnitude of this stress is 2.75 MPa, compute the resolved shear stress in the [111] direction on each of the (110) and (101) planes. (b) On the basis of these resolved shear stress values, which slip system(s) is (are) most favorably oriented? Solution (a) This part of the problem asks, for a BCC metal, that we compute the resolved shear stress in the [111] direction on each of the (110) and (101) planes. In order to solve this problem it is necessary to employ Equation 7.2, which means that we first need to solve for the for angles λ and φ for the three slip systems. For each of these three slip systems, the λ will be the same—i.e., the angle between the direction of the applied stress, [010] and the slip direction, [111]. This angle λ may be determined using Equation 7.6 λ = cos−1 u1u2 + v1v2 + w1w2 u1 2 + v1 2 + w1 2 ( )u2 2 + v2 2 + w2 2 ( ) where (for [010]) u1 = 0, v1 = 1, w1 = 0, and (for [111]) u2 = –1, v2 = 1, w2 = 1. Therefore, λ is determined as λ = cos−1 (0)(−1) + (1)(1) + (0)(1) (0)2 + (1)2 + (0)2 [ ] (−1)2 + (1)2 + (1)2 [ ] = cos−1 1 3 = 54.7° Let us now determine φ for the angle between the direction of the applied tensile stress—i.e., the [010] direction— and the normal to the (110) slip plane—i.e., the [110] direction. Again, using Equation 7.6 where u1 = 0, v1 = 1, w1 = 0 (for [010]), and u2 = 1, v2 = 1, w2 = 0 (for [110]), φ is equal to φ[010]−[110] = cos−1 (0)(1) + (1)(1) + (0)(0) (0)2 + (1)2 + (0)2 [ ] (1)2 + (1)2 + (0)2 [ ] = cos−1 1 2 = 45°
- 346. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Now, using Equation 7.2 τR = σ cosφ cos λ we solve for the resolved shear stress for this slip system as τR(110)−[111] = (2.75 MPa) cos (54.7°) cos (45°)[ ] = (2.75 MPa) (0.578)(0.707) = 1.12 MPa Now, we must determine the value of φ for the (101)–[111] slip system—that is, the angle between the direction of the applied stress, [010], and the normal to the (101) plane—i.e., the [101] direction. Again using Equation 7.6 λ[010]−[101] = cos−1 (0)(1) + (1)(0) + (0)(1) (0)2 + (1)2 + (0)2 [ ] (1)2 + (0)2 + (1)2 [ ] = cos−1 (0) = 90° Thus, the resolved shear stress for this (101)–[111] slip system is τR(101)−[111] = = (2.75 MPa) cos (54.7°) cos (90°)[ ] = (2.75 MPa) (0.578)(0) = 0 MPa (b) The most favored slip system(s) is (are) the one(s) that has (have) the largest τR value. Therefore, the (110)–[111] is the most favored since its τR (1.12 MPa) is greater than the τR value for (101) −[111] (viz., 0 MPa).
- 347. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.17 Consider a single crystal of some hypothetical metal that has the FCC crystal structure and is oriented such that a tensile stress is applied along a [102] direction. If slip occurs on a (111) plane and in a [101] direction, compute the stress at which the crystal yields if its critical resolved shear stress is 3.42 MPa. Solution This problem asks for us to determine the tensile stress at which a FCC metal yields when the stress is applied along a [102] direction such that slip occurs on a (111) plane and in a [101] direction; the critical resolved shear stress for this metal is 3.42 MPa. To solve this problem we use Equation 7.4; however it is first necessary to determine the values of φ and λ. These determinations are possible using Equation 7.6. Now, λ is the angle between [102] and [101] directions. Therefore, relative to Equation 7.6 let us take u1 = –1, v1 = 0, and w1 = 2, as well as u2 = –1, v2 = 0, and w2 = 1. This leads to λ = cos−1 u1u2 + v1v2 + w1w2 u1 2 + v1 2 + w1 2 ( )u2 2 + v2 2 + w2 2 ( ) = cos−1 (−1)(−1) + (0)(0) + (2)(1) (−1)2 + (0)2 + (2)2 [ ] (−1)2 + (0)2 + (1)2 [ ] = cos−1 3 10 = 18.4° Now for the determination of φ, the normal to the (111) slip plane is the [111] direction. Again using Equation 7.6, where we now take u1 = –1, v1 = 0, w1 = 2 (for [102]), and u2 = 1, v2 = 1, w2 = 1 (for [111]). Thus, φ = cos−1 (−1)(1) + (0)(1) + (2)(1) (−1)2 + (0)2 + (2)2 [ ] (1)2 + (1)2 + (1)2 [ ] = cos−1 3 15 = 39.2° It is now possible to compute the yield stress (using Equation 7.4) as
- 348. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. σ y = τcrss cosφ cos λ = 3.42 MPa 3 10 3 15 = 4.65 MPa
- 349. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.18 The critical resolved shear stress for iron is 27 MPa (4000 psi). Determine the maximum possible yield strength for a single crystal of Fe pulled in tension. Solution In order to determine the maximum possible yield strength for a single crystal of Fe pulled in tension, we simply employ Equation 7.5 as σ y = 2τcrss = (2)(27 MPa) = 54 MPa (8000 psi)
- 350. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Deformation by Twinning 7.19 List four major differences between deformation by twinning and deformation by slip relative to mechanism, conditions of occurrence, and final result. Solution Four major differences between deformation by twinning and deformation by slip are as follows: (1) with slip deformation there is no crystallographic reorientation, whereas with twinning there is a reorientation; (2) for slip, the atomic displacements occur in atomic spacing multiples, whereas for twinning, these displacements may be other than by atomic spacing multiples; (3) slip occurs in metals having many slip systems, whereas twinning occurs in metals having relatively few slip systems; and (4) normally slip results in relatively large deformations, whereas only small deformations result for twinning.
- 351. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Strengthening by Grain Size Reduction 7.20 Briefly explain why small-angle grain boundaries are not as effective in interfering with the slip process as are high-angle grain boundaries. Solution Small-angle grain boundaries are not as effective in interfering with the slip process as are high-angle grain boundaries because there is not as much crystallographic misalignment in the grain boundary region for small-angle, and therefore not as much change in slip direction.
- 352. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.21 Briefly explain why HCP metals are typically more brittle than FCC and BCC metals. Solution Hexagonal close packed metals are typically more brittle than FCC and BCC metals because there are fewer slip systems in HCP.
- 353. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.22 Describe in your own words the three strengthening mechanisms discussed in this chapter (i.e., grain size reduction, solid-solution strengthening, and strain hardening). Be sure to explain how dislocations are involved in each of the strengthening techniques. These three strengthening mechanisms are described in Sections 7.8, 7.9, and 7.10.
- 354. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.23 (a) From the plot of yield strength versus (grain diameter)–1/2 for a 70 Cu–30 Zn cartridge brass, Figure 7.15, determine values for the constants σ0 and ky in Equation 7.7. (b) Now predict the yield strength of this alloy when the average grain diameter is 1.0 × 10-3 mm. Solution (a) Perhaps the easiest way to solve for σ0 and ky in Equation 7.7 is to pick two values each of σy and d-1/2 from Figure 7.15, and then solve two simultaneous equations, which may be created. For example d-1/2 (mm) -1/2 σy (MPa) 4 75 12 175 The two equations are thus 75 = σ0 + 4 ky 175 = σ0 + 12 ky Solution of these equations yield the values of ky = 12.5 MPa(mm)1/2 1810 psi(mm)1/2 [ ] σ0 = 25 MPa (3630 psi) (b) When d = 1.0 × 10-3 mm, d-1/2 = 31.6 mm-1/2, and, using Equation 7.7, σ y = σ0 + kyd-1/2 = (25 MPa) + 12.5 MPa(mm) 1/2 (31.6 mm-1/2) = 420 MPa (61,000 psi)
- 355. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.24 The lower yield point for an iron that has an average grain diameter of 5 × 10-2 mm is 135 MPa (19,500 psi). At a grain diameter of 8 × 10-3 mm, the yield point increases to 260 MPa (37,500 psi). At what grain diameter will the lower yield point be 205 MPa (30,000 psi)? Solution The best way to solve this problem is to first establish two simultaneous expressions of Equation 7.7, solve for σ0 and ky, and finally determine the value of d when σy = 205 MPa. The data pertaining to this problem may be tabulated as follows: σy d (mm) d-1/2 (mm)-1/2 135 MPa 5 × 10-2 4.47 260 MPa 8 × 10-3 11.18 The two equations thus become 135 MPa = σ0 + (4.47) k y 260 MPa = σ0 + (11.18) k y Which yield the values, σ0 = 51.7 MPa and ky = 18.63 MPa(mm)1/2. At a yield strength of 205 MPa 205 MPa = 51.7 MPa + 18.63 MPa(mm)1/2 [ ]d-1/2 or d-1/2 = 8.23 (mm) -1/2, which gives d = 1.48 × 10-2 mm.
- 356. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.25 If it is assumed that the plot in Figure 7.15 is for noncold-worked brass, determine the grain size of the alloy in Figure 7.19; assume its composition is the same as the alloy in Figure 7.15. Solution This problem asks that we determine the grain size of the brass for which is the subject of Figure 7.19. From Figure 7.19a, the yield strength of brass at 0%CW is approximately 175 MPa (26,000 psi). This yield strength from Figure 7.15 corresponds to a d-1/2 value of approximately 12.0 (mm) -1/2. Thus, d = 6.9 × 10-3 mm.
- 357. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Solid-Solution Strengthening 7.26 In the manner of Figures 7.17b and 7.18b, indicate the location in the vicinity of an edge dislocation at which an interstitial impurity atom would be expected to be situated. Now briefly explain in terms of lattice strains why it would be situated at this position. Solution Below is shown an edge dislocation and where an interstitial impurity atom would be located. Compressive lattice strains are introduced by the impurity atom. There will be a net reduction in lattice strain energy when these lattice strains partially cancel tensile strains associated with the edge dislocation; such tensile strains exist just below the bottom of the extra half-plane of atoms (Figure 7.4).
- 358. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Strain Hardening 7.27 (a) Show, for a tensile test, that %CW = ε ε+1 ×100 if there is no change in specimen volume during the deformation process (i.e., A0l0 = Adld). (b) Using the result of part (a), compute the percent cold work experienced by naval brass (the stress- strain behavior of which is shown in Figure 6.12) when a stress of 400 MPa (58,000 psi) is applied. Solution (a) From Equation 7.8 %CW = A0 − Ad A0 × 100 = 1 − Ad A0 × 100 Which is also equal to 1 − l0 ld × 100 since Ad/A0 = l0/ld, the conservation of volume stipulation given in the problem statement. Now, from the definition of engineering strain (Equation 6.2) ε = ld − l0 l0 = ld l0 −1 Or, l0 ld = 1 ε + 1 Substitution for l0/ ld into the %CW expression above gives %CW = 1 − l0 ld × 100 = 1 − 1 ε + 1 × 100 = ε ε + 1 × 100
- 359. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (b) From Figure 6.12, a stress of 400 MPa (58,000 psi) corresponds to a strain of 0.13. Using the above expression %CW = ε ε + 1 × 100 = 0.13 0.13 + 1.00 × 100 = 11.5%CW
- 360. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.28 Two previously undeformed cylindrical specimens of an alloy are to be strain hardened by reducing their cross-sectional areas (while maintaining their circular cross sections). For one specimen, the initial and deformed radii are 16 mm and 11 mm, respectively. The second specimen, with an initial radius of 12 mm, must have the same deformed hardness as the first specimen; compute the second specimen's radius after deformation. Solution In order for these two cylindrical specimens to have the same deformed hardness, they must be deformed to the same percent cold work. For the first specimen %CW = A0 − Ad A0 × 100 = π r0 2 − π rd 2 π r0 2 × 100 = π (16 mm)2 − π (11 mm)2 π (16 mm)2 × 100 = 52.7%CW For the second specimen, the deformed radius is computed using the above equation and solving for rd as rd = r0 1 − %CW 100 = (12 mm) 1 − 52.7%CW 100 = 8.25 mm
- 361. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.29 Two previously undeformed specimens of the same metal are to be plastically deformed by reducing their cross-sectional areas. One has a circular cross section, and the other is rectangular; during deformation the circular cross section is to remain circular, and the rectangular is to remain as such. Their original and deformed dimensions are as follows: Circular (diameter, mm) Rectangular (mm) Original dimensions 15.2 125 × 175 Deformed dimensions 11.4 75 × 200 Which of these specimens will be the hardest after plastic deformation, and why? Solution The hardest specimen will be the one that has experienced the greatest degree of cold work. Therefore, all we need do is to compute the %CW for each specimen using Equation 7.8. For the circular one %CW = A0 − Ad A0 × 100 = π r 0 2 − π r d 2 π r 0 2 × 100 = π 15.2 mm 2 2 − π 11.4 mm 2 2 π 15.2 mm 2 2 × 100 = 43.8%CW For the rectangular one %CW = (125 mm)(175 mm) − (75 mm)(200 mm) (125 mm)(175 mm) × 100 = 31.4%CW Therefore, the deformed circular specimen will be harder.
- 362. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.30 A cylindrical specimen of cold-worked copper has a ductility (%EL) of 25%. If its cold-worked radius is 10 mm (0.40 in.), what was its radius before deformation? Solution This problem calls for us to calculate the precold-worked radius of a cylindrical specimen of copper that has a cold-worked ductility of 25%EL. From Figure 7.19c, copper that has a ductility of 25%EL will have experienced a deformation of about 11%CW. For a cylindrical specimen, Equation 7.8 becomes %CW = π r 0 2 − π r d 2 π r 0 2 × 100 Since rd = 10 mm (0.40 in.), solving for r0 yields r0 = rd 1 − %CW 100 = 10 mm 1 − 11.0 100 = 10.6 mm (0.424 in.)
- 363. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.31 (a) What is the approximate ductility (%EL) of a brass that has a yield strength of 275 MPa (40,000 psi)? (b) What is the approximate Brinell hardness of a 1040 steel having a yield strength of 690 MPa (100,000 psi)? Solution (a) In order to solve this problem, it is necessary to consult Figures 7.19a and 7.19c. From Figure 7.19a, a yield strength of 275 MPa for brass corresponds to 10%CW. A brass that has been cold-worked 10% will have a ductility of about 43%EL [Figure 7.19c]. (b) This portion of the problem asks for the Brinell hardness of a 1040 steel having a yield strength of 690 MPa (100,000 psi). From Figure 7.19a, a yield strength of 690 MPa for a 1040 steel corresponds to about 10%CW. A 1040 steel that has been cold worked 10% will have a tensile strength of about 780 MPa [Figure 7.19b]. Finally, using Equation 6.20a HB = TS(MPa) 3.45 = 780 MPa 3.45 = 226
- 364. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.32 Experimentally, it has been observed for single crystals of a number of metals that the critical resolved shear stress τcrss is a function of the dislocation density ρD as τcrss = τ0 + A ρD where τ0 and A are constants. For copper, the critical resolved shear stress is 2.10 MPa (305 psi) at a dislocation density of 105 mm-2 . If it is known that the value of A for copper is 6.35 × 10-3 MPa-mm (0.92 psi-mm), compute the τcrss at a dislocation density of 107 mm-2 . Solution We are asked in this problem to compute the critical resolved shear stress at a dislocation density of 107 mm-2. It is first necessary to compute the value of the constant τ0 (in the equation provided in the problem statement) from the one set of data as τ0 = τcrss − A ρD = 2.10 MPa − (6.35 × 10−3 MPa- mm) 105 mm−2 ( )= 0.092 MPa (13.3 psi) Now, the critical resolved shear stress may be determined at a dislocation density of 107 mm-2 as τcrss = τ0 + A ρD = (0.092 MPa) + (6.35 × 10-3 MPa- mm) 107 mm−2 = 20.2 MPa (2920 psi)
- 365. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Recovery Recrystallization Grain Growth 7.33 Briefly cite the differences between recovery and recrystallization processes. Solution For recovery, there is some relief of internal strain energy by dislocation motion; however, there are virtually no changes in either the grain structure or mechanical characteristics. During recrystallization, on the other hand, a new set of strain-free grains forms, and the material becomes softer and more ductile.
- 366. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.34 Estimate the fraction of recrystallization from the photomicrograph in Figure 7.21c. Solution Below is shown a square grid onto which is superimposed the recrystallized regions from the micrograph. Approximately 400 squares lie within the recrystallized areas, and since there are 672 total squares, the specimen is about 60% recrystallized.
- 367. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.35 Explain the differences in grain structure for a metal that has been cold worked and one that has been cold worked and then recrystallized. Solution During cold-working, the grain structure of the metal has been distorted to accommodate the deformation. Recrystallization produces grains that are equiaxed and smaller than the parent grains.
- 368. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.36 (a) What is the driving force for recrystallization? (b) For grain growth? Solution (a) The driving force for recrystallization is the difference in internal energy between the strained and unstrained material. (b) The driving force for grain growth is the reduction in grain boundary energy as the total grain boundary area decreases.
- 369. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.37 (a) From Figure 7.25, compute the length of time required for the average grain diameter to increase from 0.01 to 0.1 mm at 500°C for this brass material. (b) Repeat the calculation at 600°C. Solution (a) At 500°C, the time necessary for the average grain diameter to grow to increase from 0.01 to 0.1 mm is approximately 3500 min. (b) At 600°C the time required for this same grain size increase is approximately 150 min.
- 370. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.38 The average grain diameter for a brass material was measured as a function of time at 650°C, which is tabulated below at two different times: Time (min) Grain Diameter (mm) 30 3.9 × 10–2 90 6.6 × 10–2 (a) What was the original grain diameter? (b) What grain diameter would you predict after 150 min at 650°C? Solution (a) Using the data given and Equation 7.9 (taking n = 2), we may set up two simultaneous equations with d0 and K as unknowns; thus (3.9 × 10-2 mm)2 − d0 2 = (30 min)K (6.6 × 10-2 mm)2 − d0 2 = (90 min)K Solution of these expressions yields a value for d0, the original grain diameter, of d0 = 0.01 mm, and a value for K of 4.73 × 10-5 mm2/min (b) At 150 min, the diameter d is computed using a rearranged form of Equation 7.9 as d = d0 2 + Kt = (0.01 mm)2 + (4.73 × 10−5 mm2/min)(150 min) = 0.085 mm
- 371. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.39 An undeformed specimen of some alloy has an average grain diameter of 0.040 mm. You are asked to reduce its average grain diameter to 0.010 mm. Is this possible? If so, explain the procedures you would use and name the processes involved. If it is not possible, explain why. Solution Yes, it is possible to reduce the average grain diameter of an undeformed alloy specimen from 0.040 mm to 0.010 mm. In order to do this, plastically deform the material at room temperature (i.e., cold work it), and then anneal at an elevated temperature in order to allow recrystallization and some grain growth to occur until the average grain diameter is 0.010 mm.
- 372. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.40 Grain growth is strongly dependent on temperature (i.e., rate of grain growth increases with increasing temperature), yet temperature is not explicitly given as a part of Equation 7.9. (a) Into which of the parameters in this expression would you expect temperature to be included? (b) On the basis of your intuition, cite an explicit expression for this temperature dependence. Solution (a) The temperature dependence of grain growth is incorporated into the constant K in Equation 7.9. (b) The explicit expression for this temperature dependence is of the form K = K0 exp − Q RT in which K0 is a temperature-independent constant, the parameter Q is an activation energy, and R and T are the gas constant and absolute temperature, respectively.
- 373. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.41 An uncold-worked brass specimen of average grain size 0.008 mm has a yield strength of 160 MPa (23,500 psi). Estimate the yield strength of this alloy after it has been heated to 600°C for 1000 s, if it is known that the value of ky is 12.0 MPa-mm1/2 (1740 psi-mm1/2 ). Solution In order to solve this problem, it is first necessary to calculate the constant σ0 in Equation 7.7 as σ0 = σ y − kyd-1/2 = 160 MPa−(12.0 MPa− mm1/2)(0.008 mm)−1/ 2 = 25.8 MPa (4046 psi) Next, we must determine the average grain size after the heat treatment. From Figure 7.25 at 600°C after 1000 s (16.7 min) the average grain size of a brass material is about 0.20 mm. Therefore, calculating σy at this new grain size using Equation 7.7 we get σ y = σ0 + kyd-1/2 = 25.8 MPa + (12.0 MPa- mm1/2)(0.20 mm)-1/2 = 52.6 MPa (7940 psi)
- 374. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. DESIGN PROBLEMS Strain Hardening Recrystallization 7.D1 Determine whether or not it is possible to cold work steel so as to give a minimum Brinell hardness of 225, and at the same time have a ductility of at least 12%EL. Justify your decision. Solution The tensile strength corresponding to a Brinell hardness of 225 may be determined using Equation 6.20a as TS(MPa) = 3.45 × HB = (3.45)(225) = 776 MPa Furthermore, from Figure 7.19b, in order to achieve a tensile strength of 776 MPa, deformation of at least 9%CW is necessary. Finally, if we cold work the steel to 9%CW, then the ductility is 17%EL from Figure 7.19c. Therefore, it is possible to meet both of these criteria by plastically deforming the steel.
- 375. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.D2 Determine whether or not it is possible to cold work brass so as to give a minimum Brinell hardness of 120 and at the same time have a ductility of at least 20%EL. Justify your decision. Solution According to Figure 6.19, a Brinell hardness of 120 corresponds to a tensile strength of 440 MPa (63,500 psi.) Furthermore, from Figure 7.19b, in order to achieve a tensile strength of 440 MPa, deformation of at least 26%CW is necessary. Finally, if we are to achieve a ductility of at least 20%EL, then a maximum deformation of 23%CW is possible from Figure 7.19c. Therefore, it is not possible to meet both of these criteria by plastically deforming brass.
- 376. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.D3 A cylindrical specimen of cold-worked steel has a Brinell hardness of 250. (a) Estimate its ductility in percent elongation. (b) If the specimen remained cylindrical during deformation and its original radius was 5 mm (0.20 in.), determine its radius after deformation. Solution (a) From Figure 6.19, a Brinell hardness of 250 corresponds to a tensile strength of 860 MPa (125,000 psi), which, from Figure 7.19b, requires a deformation of 25%CW. Furthermore, 25%CW yields a ductility of about 11%EL for steel, Figure 7.19c. (b) We are now asked to determine the radius after deformation if the uncold-worked radius is 5 mm (0.20 in.). From Equation 7.8 and for a cylindrical specimen %CW = π r0 2 − π r d 2 π r0 2 × 100 Now, solving for rd from this expression, we get rd = r0 1 − %CW 100 = (5 mm) 1 − 25 100 = 4.33 mm (0.173 in.)
- 377. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.D4 It is necessary to select a metal alloy for an application that requires a yield strength of at least 345 MPa (50,000 psi) while maintaining a minimum ductility (%EL) of 20%. If the metal may be cold worked, decide which of the following are candidates: copper, brass, and a 1040 steel. Why? Solution For each of these alloys, the minimum cold work necessary to achieve the yield strength may be determined from Figure 7.19a, while the maximum possible cold work for the ductility is found in Figure 7.19c. These data are tabulated below. Yield Strength Ductility (> 345 MPa) (> 20%EL) Steel Any %CW < 5%CW Brass > 20%CW < 23%CW Copper > 54%CW < 15%CW Thus, both the 1040 steel and brass are possible candidates since for these alloys there is an overlap of percents coldwork to give the required minimum yield strength and ductility values.
- 378. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.D5 A cylindrical rod of 1040 steel originally 15.2 mm (0.60 in.) in diameter is to be cold worked by drawing; the circular cross section will be maintained during deformation. A cold-worked tensile strength in excess of 840 MPa (122,000 psi) and a ductility of at least 12%EL are desired. Furthermore, the final diameter must be 10 mm (0.40 in.). Explain how this may be accomplished. Solution First let us calculate the percent cold work and attendant tensile strength and ductility if the drawing is carried out without interruption. From Equation 7.8 %CW = π d0 2 2 − π dd 2 2 π d0 2 2 × 100 = π 15.2 mm 2 2 − π 10 mm 2 2 π 15.2 mm 2 2 × 100 = 56%CW At 56%CW, the steel will have a tensile strength on the order of 920 MPa (133,000 psi) [Figure 7.19b], which is adequate; however, the ductility will be less than 10%EL [Figure 7.19c], which is insufficient. Instead of performing the drawing in a single operation, let us initially draw some fraction of the total deformation, then anneal to recrystallize, and, finally, cold-work the material a second time in order to achieve the final diameter, tensile strength, and ductility. Reference to Figure 7.19b indicates that 20%CW is necessary to yield a tensile strength of 840 MPa (122,000 psi). Similarly, a maximum of 21%CW is possible for 12%EL [Figure 7.19c]. The average of these extremes is 20.5%CW. Again using Equation 7.8, if the final diameter after the first drawing is d 0 ' , then 20.5%CW = π d 0 ' 2 2 − π 10 mm 2 2 π d 0 ' 2 2 × 100 And, solving the above expression for d 0 ' , yields
- 379. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. d 0 ' = 10 mm 1 − 20.5%CW 100 = 11.2 mm (0.45 in.)
- 380. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.D6 A cylindrical rod of copper originally 16.0 mm (0.625 in.) in diameter is to be cold worked by drawing; the circular cross section will be maintained during deformation. A cold-worked yield strength in excess of 250 MPa (36,250 psi) and a ductility of at least 12%EL are desired. Furthermore, the final diameter must be 11.3 mm (0.445 in.). Explain how this may be accomplished. Solution Let us first calculate the percent cold work and attendant yield strength and ductility if the drawing is carried out without interruption. From Equation 7.8 %CW = π d0 2 2 − π dd 2 2 π d0 2 2 × 100 = π 16.0 mm 2 2 − π 11.3 mm 2 2 π 16.0 mm 2 2 × 100 = 50%CW At 50%CW, the copper will have a yield strength on the order of 330 MPa (48,000 psi), Figure 7.19a, which is adequate; however, the ductility will be about 4%EL, Figure 7.19c, which is insufficient. Instead of performing the drawing in a single operation, let us initially draw some fraction of the total deformation, then anneal to recrystallize, and, finally, cold work the material a second time in order to achieve the final diameter, yield strength, and ductility. Reference to Figure 7.19a indicates that 21%CW is necessary to give a yield strength of 250 MPa. Similarly, a maximum of 23%CW is possible for 12%EL [Figure 7.19c]. The average of these two values is 22%CW, which we will use in the calculations. Thus, to achieve both the specified yield strength and ductility, the copper must be deformed to 22%CW. If the final diameter after the first drawing is d 0 ' , then, using Equation 7.8 22%CW = π d 0 ' 2 2 − π 11.3 mm 2 2 π d 0 ' 2 2 × 100 And, solving for d 0 ' from the above expression yields
- 381. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. d 0 ' = 11.3 mm 1 − 22%CW 100 = 12.8 mm (0.50 in.)
- 382. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 7.D7 A cylindrical 1040 steel rod having a minimum tensile strength of 865 MPa (125,000 psi), a ductility of at least 10%EL, and a final diameter of 6.0 mm (0.25 in.) is desired. Some 7.94 mm (0.313 in.) diameter 1040 steel stock, which has been cold worked 20% is available. Describe the procedure you would follow to obtain this material. Assume that 1040 steel experiences cracking at 40%CW. Solution This problem calls for us to cold work some 1040 steel stock that has been previously cold worked in order to achieve minimum tensile strength and ductility values of 865 MPa (125,000 psi) and 10%EL, respectively, while the final diameter must be 6.0 mm (0.25 in.). Furthermore, the material may not be deformed beyond 40%CW. Let us start by deciding what percent coldwork is necessary for the minimum tensile strength and ductility values, assuming that a recrystallization heat treatment is possible. From Figure 7.19b, at least 25%CW is required for a tensile strength of 865 MPa. Furthermore, according to Figure 7.19c, 10%EL corresponds a maximum of 30%CW. Let us take the average of these two values (i.e., 27.5%CW), and determine what previous specimen diameter is required to yield a final diameter of 6.0 mm. For cylindrical specimens, Equation 7.8 takes the form %CW = π d0 2 2 − π dd 2 2 π d0 2 2 × 100 Solving for the original diameter d0 yields d0 = dd 1 − %CW 100 = 6.0 mm 1 − 27.5%CW 100 = 7.05 mm (0.278 in.) Now, let us determine its undeformed diameter realizing that a diameter of 7.94 mm corresponds to 20%CW. Again solving for d0 using the above equation and assuming dd = 7.94 mm yields d0 = dd 1 − %CW 100 = 7.94 mm 1 − 20%CW 100 = 8.88 mm (0.350 in.) At this point let us see if it is possible to deform the material from 8.88 mm to 7.05 mm without exceeding the 40%CW limit. Again employing Equation 7.8
- 383. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. %CW = π 8.88 mm 2 2 − π 7.05 mm 2 2 π 8.88 mm 2 2 × 100 = 37%CW In summary, the procedure which can be used to produce the desired material would be as follows: cold work the as-received stock to 7.05 mm (0.278 in.), heat treat it to achieve complete recrystallization, and then cold work the material again to 6.0 mm (0.25 in.), which will give the desired tensile strength and ductility.
- 384. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 8 FAILURE PROBLEM SOLUTIONS Principles of Fracture Mechanics 8.1 What is the magnitude of the maximum stress that exists at the tip of an internal crack having a radius of curvature of 2.5 × 10-4 mm (10-5 in.) and a crack length of 2.5 × 10-2 mm (10-3 in.) when a tensile stress of 170 MPa (25,000 psi) is applied? Solution This problem asks that we compute the magnitude of the maximum stress that exists at the tip of an internal crack. Equation 8.1 is employed to solve this problem, as σm = 2σ0 a ρt 1/ 2 = (2)(170 MPa) 2.5 × 10−2 mm 2 2.5 × 10−4 mm 1/2 = 2404 MPa (354,000 psi)
- 385. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.2 Estimate the theoretical fracture strength of a brittle material if it is known that fracture occurs by the propagation of an elliptically shaped surface crack of length 0.25 mm (0.01 in.) and having a tip radius of curvature of 1.2 × 10-3 mm (4.7 × 10-5 in.) when a stress of 1200 MPa (174,000 psi) is applied. Solution In order to estimate the theoretical fracture strength of this material it is necessary to calculate σm using Equation 8.1 given that σ0 = 1200 MPa, a = 0.25 mm, and ρt = 1.2 × 10-3 mm. Thus, σm = 2σ0 a ρt 1/ 2 = (2)(1200 MPa) 0.25 mm 1.2 × 10−3 mm 1/2 = 3.5 × 104 MPa = 35 GPa (5.1 × 106 psi)
- 386. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.3 If the specific surface energy for soda-lime glass is 0.30 J/m2 , using data contained in Table 12.5, compute the critical stress required for the propagation of a surface crack of length 0.05 mm. Solution We may determine the critical stress required for the propagation of an surface crack in soda-lime glass using Equation 8.3; taking the value of 69 GPa (Table 12.5) as the modulus of elasticity, we get σc = 2E γs π a 1/ 2 = (2)(69 × 109 N /m2)(0.30 N/m) (π) 0.05 × 10−3 m( ) 1/ 2 = 16.2 × 106 N/m2 = 16.2 MPa
- 387. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.4 A polystyrene component must not fail when a tensile stress of 1.25 MPa (180 psi) is applied. Determine the maximum allowable surface crack length if the surface energy of polystyrene is 0.50 J/m2 (2.86 × 10-3 in.-lbf/in.2 ). Assume a modulus of elasticity of 3.0 GPa (0.435 × 106 psi). Solution The maximum allowable surface crack length for polystyrene may be determined using Equation 8.3; taking 3.0 GPa as the modulus of elasticity, and solving for a, leads to a = 2E γs π σc 2 = (2)(3 × 109 N/m2)(0.50 N/m) (π)(1.25 × 106 N/m2) 2 = 6.1 × 10-4 m = 0.61 mm (0.024 in.)
- 388. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.5 A specimen of a 4340 steel alloy having a plane strain fracture toughness of 45 MPa m ( 41 ksi in. ) is exposed to a stress of 1000 MPa (145,000 psi). Will this specimen experience fracture if it is known that the largest surface crack is 0.75 mm (0.03 in.) long? Why or why not? Assume that the parameter Y has a value of 1.0. Solution This problem asks us to determine whether or not the 4340 steel alloy specimen will fracture when exposed to a stress of 1000 MPa, given the values of KIc, Y, and the largest value of a in the material. This requires that we solve for σc from Equation 8.6. Thus σc = KIc Y π a = 45 MPa m (1.0) (π)(0.75 × 10−3 m) = 927 MPa (133,500 psi) Therefore, fracture will most likely occur because this specimen will tolerate a stress of 927 MPa (133,500 psi) before fracture, which is less than the applied stress of 1000 MPa (145,000 psi).
- 389. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.6 Some aircraft component is fabricated from an aluminum alloy that has a plane strain fracture toughness of 35 MPa m (31.9 ksi in.). It has been determined that fracture results at a stress of 250 MPa (36,250 psi) when the maximum (or critical) internal crack length is 2.0 mm (0.08 in.). For this same component and alloy, will fracture occur at a stress level of 325 MPa (47,125 psi) when the maximum internal crack length is 1.0 mm (0.04 in.)? Why or why not? Solution We are asked to determine if an aircraft component will fracture for a given fracture toughness (35 MPa m), stress level (325 MPa), and maximum internal crack length (1.0 mm), given that fracture occurs for the same component using the same alloy for another stress level and internal crack length. It first becomes necessary to solve for the parameter Y, using Equation 8.5, for the conditions under which fracture occurred (i.e., σ = 250 MPa and 2a = 2.0 mm). Therefore, Y = KIc σ π a = 35 MPa m (250 MPa) (π) 2 × 10−3 m 2 = 2.50 Now we will solve for the product Y σ πa for the other set of conditions, so as to ascertain whether or not this value is greater than the KIc for the alloy. Thus, Y σ π a = (2.50)(325 MPa) (π) 1 × 10−3 m 2 = 32.2 MPa m (29.5 ksi in.) Therefore, fracture will not occur since this value (32.3 MPa m ) is less than the KIc of the material, 35 MPa m.
- 390. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.7 Suppose that a wing component on an aircraft is fabricated from an aluminum alloy that has a plane strain fracture toughness of 40 MPa m (36.4 ksi in.). It has been determined that fracture results at a stress of 365 MPa (53,000 psi) when the maximum internal crack length is 2.5 mm (0.10 in.). For this same component and alloy, compute the stress level at which fracture will occur for a critical internal crack length of 4.0 mm (0.16 in.). Solution This problem asks us to determine the stress level at which an a wing component on an aircraft will fracture for a given fracture toughness (40 MPa m ) and maximum internal crack length (4.0 mm), given that fracture occurs for the same component using the same alloy at one stress level (365 MPa) and another internal crack length (2.5 mm). It first becomes necessary to solve for the parameter Y for the conditions under which fracture occurred using Equation 8.5. Therefore, Y = KIc σ πa = 40 MPa m (365 MPa) (π) 2.5 × 10−3 m 2 = 1.75 Now we will solve for σc using Equation 8.6 as σc = KIc Y πa = 40 MPa m (1.75) (π) 4 × 10−3 m 2 = 288 MPa (41,500 psi)
- 391. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.8 A large plate is fabricated from a steel alloy that has a plane strain fracture toughness of 55 MPa m (50 ksi in.). If, during service use, the plate is exposed to a tensile stress of 200 MPa (29,000 psi), determine the minimum length of a surface crack that will lead to fracture. Assume a value of 1.0 for Y. Solution For this problem, we are given values of KIc (55 MPa m ), σ (200 MPa), and Y (1.0) for a large plate and are asked to determine the minimum length of a surface crack that will lead to fracture. All we need do is to solve for ac using Equation 8.7; therefore ac = 1 π KIc Y σ 2 = 1 π 55 MPa m (1.0)(200 MPa) 2 = 0.024 m = 24 mm (0.95 in.)
- 392. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.9 Calculate the maximum internal crack length allowable for a 7075-T651 aluminum alloy (Table 8.1) component that is loaded to a stress one half of its yield strength. Assume that the value of Y is 1.35. Solution This problem asks us to calculate the maximum internal crack length allowable for the 7075-T651 aluminum alloy in Table 8.1 given that it is loaded to a stress level equal to one-half of its yield strength. For this alloy, KIc = 24 MPa m (22 ksi in.); also, σ = σy/2 = (495 MPa)/2 = 248 MPa (36,000 psi). Now solving for 2ac using Equation 8.7 yields 2ac = 2 π KIc Yσ 2 = 2 π 24 MPa m (1.35)(248 MPa) 2 = 0.0033 m = 3.3 mm (0.13 in.)
- 393. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.10 A structural component in the form of a wide plate is to be fabricated from a steel alloy that has a plane strain fracture toughness of 77.0 MPa m (70.1 ksi in.) and a yield strength of 1400 MPa (205,000 psi). The flaw size resolution limit of the flaw detection apparatus is 4.0 mm (0.16 in.). If the design stress is one half of the yield strength and the value of Y is 1.0, determine whether or not a critical flaw for this plate is subject to detection. Solution This problem asks that we determine whether or not a critical flaw in a wide plate is subject to detection given the limit of the flaw detection apparatus (4.0 mm), the value of KIc (77 MPa m ), the design stress (σy/2 in which σ y = 1400 MPa), and Y = 1.0. We first need to compute the value of ac using Equation 8.7; thus ac = 1 π KIc Yσ 2 = 1 π 77 MPa m (1.0) 1400 MPa 2 2 = 0.0039 m = 3.9 mm (0.15 in.) Therefore, the critical flaw is not subject to detection since this value of ac (3.9 mm) is less than the 4.0 mm resolution limit.
- 394. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.11 After consultation of other references, write a brief report on one or two nondestructive test techniques that are used to detect and measure internal and/or surface flaws in metal alloys. The student should do this problem on his/her own.
- 395. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Impact Fracture Testing 8.12 Following is tabulated data that were gathered from a series of Charpy impact tests on a ductile cast iron. Temperature (°C) Impact Energy (J) –25 124 –50 123 –75 115 –85 100 –100 73 –110 52 –125 26 –150 9 –175 6 (a) Plot the data as impact energy versus temperature. (b) Determine a ductile-to-brittle transition temperature as that temperature corresponding to the average of the maximum and minimum impact energies. (c) Determine a ductile-to-brittle transition temperature as that temperature at which the impact energy is 80 J. Solution (a) The plot of impact energy versus temperature is shown below.
- 396. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (b) The average of the maximum and minimum impact energies from the data is Average = 124 J + 6 J 2 = 65 J As indicated on the plot by the one set of dashed lines, the ductile-to-brittle transition temperature according to this criterion is about –105°C. (c) Also, as noted on the plot by the other set of dashed lines, the ductile-to-brittle transition temperature for an impact energy of 80 J is about –95°C.
- 397. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.13 Following is tabulated data that were gathered from a series of Charpy impact tests on a tempered 4140 steel alloy. Temperature (°C) Impact Energy (J) 100 89.3 75 88.6 50 87.6 25 85.4 0 82.9 –25 78.9 –50 73.1 –65 66.0 –75 59.3 –85 47.9 –100 34.3 –125 29.3 –150 27.1 –175 25.0 (a) Plot the data as impact energy versus temperature. (b) Determine a ductile-to-brittle transition temperature as that temperature corresponding to the average of the maximum and minimum impact energies. (c) Determine a ductile-to-brittle transition temperature as that temperature at which the impact energy is 70 J. Solution The plot of impact energy versus temperature is shown below.
- 398. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (b) The average of the maximum and minimum impact energies from the data is Average = 89.3 J + 25 J 2 = 57.2 J As indicated on the plot by the one set of dashed lines, the ductile-to-brittle transition temperature according to this criterion is about –75°C. (c) Also, as noted on the plot by the other set of dashed lines, the ductile-to-brittle transition temperature for an impact energy of 70 J is about –55°C.
- 399. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Cyclic Stresses (Fatigue) The S-N Curve 8.14 A fatigue test was conducted in which the mean stress was 50 MPa (7250 psi) and the stress amplitude was 225 MPa (32,625 psi). (a) Compute the maximum and minimum stress levels. (b) Compute the stress ratio. (c) Compute the magnitude of the stress range. Solution (a) Given the values of σm (50 MPa) and σa (225 MPa) we are asked to compute σmax and σmin. From Equation 8.14 σm = σmax + σmin 2 = 50 MPa Or, σmax + σmin = 100 MPa Furthermore, utilization of Equation 8.16 yields σa = σmax − σmin 2 = 225 MPa Or, σmax – σmin = 450 MPa Simultaneously solving these two expressions leads to σmax = 275 MPa (40,000 psi) σmin = −175 MPa (−25,500 psi) (b) Using Equation 8.17 the stress ratio R is determined as follows: R = σmin σmax = −175 MPa 275 MPa = − 0.64
- 400. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (c) The magnitude of the stress range σr is determined using Equation 8.15 as σr = σmax − σmin = 275 MPa − (−175 MPa) = 450 MPa (65,500 psi)
- 401. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.15 A cylindrical 1045 steel bar (Figure 8.34) is subjected to repeated compression-tension stress cycling along its axis. If the load amplitude is 22,000 N (4950 lbf), compute the minimum allowable bar diameter to ensure that fatigue failure will not occur. Assume a factor of safety of 2.0. Solution From Figure 8.34, the fatigue limit stress amplitude for this alloy is 310 MPa (45,000 psi). Stress is defined in Equation 6.1 as σ = F A0 . For a cylindrical bar A0 = π d0 2 2 Substitution for A0 into the Equation 6.1 leads to σ = F A0 = F π d0 2 2 = 4F πd0 2 We now solve for d0, taking stress as the fatigue limit divided by the factor of safety. Thus d0 = 4F π σ N = (4)(22,000 N) (π) 310 × 106 N /m2 2 = 13.4 × 10−3 m = 13.4 mm (0.53 in.)
- 402. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.16 An 8.0 mm (0.31 in.) diameter cylindrical rod fabricated from a red brass alloy (Figure 8.34) is subjected to reversed tension-compression load cycling along its axis. If the maximum tensile and compressive loads are +7500 N (1700 lbf) and -7500 N (-1700 lbf), respectively, determine its fatigue life. Assume that the stress plotted in Figure 8.34 is stress amplitude. Solution We are asked to determine the fatigue life for a cylindrical red brass rod given its diameter (8.0 mm) and the maximum tensile and compressive loads (+7500 N and -7500 N, respectively). The first thing that is necessary is to calculate values of σmax and σmin using Equation 6.1. Thus σmax = Fmax A0 = Fmax π d0 2 2 = 7500 N (π) 8.0 × 10−3 m 2 2 = 150 × 106 N/m2 = 150 MPa (22,500 psi) σmin = Fmin π d0 2 2 = −7500 N (π) 8.0 × 10−3 m 2 2 = −150 × 106 N/m2 = −150 MPa (−22,500 psi) Now it becomes necessary to compute the stress amplitude using Equation 8.16 as σa = σmax − σmin 2 = 150 MPa − (−150 MPa) 2 = 150 MPa (22,500 psi) From Figure 8.34, f for the red brass, the number of cycles to failure at this stress amplitude is about 1 × 105 cycles.
- 403. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.17 A 12.5 mm (0.50 in.) diameter cylindrical rod fabricated from a 2014-T6 alloy (Figure 8.34) is subjected to a repeated tension-compression load cycling along its axis. Compute the maximum and minimum loads that will be applied to yield a fatigue life of 1.0 × 107 cycles. Assume that the stress plotted on the vertical axis is stress amplitude, and data were taken for a mean stress of 50 MPa (7250 psi). Solution This problem asks that we compute the maximum and minimum loads to which a 12.5 mm (0.50 in.) diameter 2014-T6 aluminum alloy specimen may be subjected in order to yield a fatigue life of 1.0 × 107 cycles; Figure 8.34 is to be used assuming that data were taken for a mean stress of 50 MPa (7250 psi). Upon consultation of Figure 8.34, a fatigue life of 1.0 × 107 cycles corresponds to a stress amplitude of 160 MPa (23,200 psi). Or, from Equation 8.16 σmax − σmin = 2σa = (2)(160 MPa) = 320 MPa (46,400 psi) Since σm = 50 MPa, then from Equation 8.14 σmax + σmin = 2σm = (2)(50 MPa) = 100 MPa (14,500 psi) Simultaneous solution of these two expressions for σmax and σmin yields σmax = +210 MPa (+30,400 psi) σmin = –110 MPa (–16,000 psi) Now, inasmuch as σ = F A0 (Equation 6.1), and A0 = π d0 2 2 then Fmax = σmaxπ d 0 2 4 = (210 × 106 N /m2) (π)(12.5 × 10−3 m)2 4 = 25,800 N (6000 lbf) Fmin = σminπ d 0 2 4 = (−110 × 106 N /m2) (π)(12.5 × 10−3 m)2 4 = −13,500 N (−3140 lbf)
- 404. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.18 The fatigue data for a brass alloy are given as follows: Stress Amplitude (MPa) Cycles to Failure 310 2 × 105 223 1 × 106 191 3 × 106 168 1 × 107 153 3 × 107 143 1 × 108 134 3 × 108 127 1 × 109 (a) Make an S–N plot (stress amplitude versus logarithm cycles to failure) using these data. (b) Determine the fatigue strength at 5 × 105 cycles. (c) Determine the fatigue life for 200 MPa. Solution (a) The fatigue data for this alloy are plotted below. (b) As indicated by the “A” set of dashed lines on the plot, the fatigue strength at 5 × 105 cycles [log (5 × 105) = 5.7] is about 250 MPa.
- 405. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (c) As noted by the “B” set of dashed lines, the fatigue life for 200 MPa is about 2 × 106 cycles (i.e., the log of the lifetime is about 6.3).
- 406. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.19 Suppose that the fatigue data for the brass alloy in Problem 8.18 were taken from torsional tests, and that a shaft of this alloy is to be used for a coupling that is attached to an electric motor operating at 1500 rpm. Give the maximum torsional stress amplitude possible for each of the following lifetimes of the coupling: (a) 1 year, (b) 1 month, (c) 1 day, and (d) 2 hours. Solution For each lifetime, first compute the number of cycles, and then read the corresponding fatigue strength from the above plot. (a) Fatigue lifetime = (1 yr)(365 days/yr)(24 h/day)(60 min/h)(1500 cycles/min) = 7.9 × 108 cycles. The stress amplitude corresponding to this lifetime is about 130 MPa. (b) Fatigue lifetime = (30 days)(24 h/day)(60 min/h)(1500 cycles/min) = 6.5 × 107 cycles. The stress amplitude corresponding to this lifetime is about 145 MPa. (c) Fatigue lifetime = (24 h)(60 min/h)(1500 cycles/min) = 2.2 × 106 cycles. The stress amplitude corresponding to this lifetime is about 195 MPa. (d) Fatigue lifetime = (2 h)(60 min/h)(1500 cycles/min) = 1.8 × 105 cycles. The stress amplitude corresponding to this lifetime is about 315 MPa.
- 407. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.20 The fatigue data for a ductile cast iron are given as follows: Stress Amplitude [MPa (ksi)] Cycles to Failure 248 (36.0) 1 × 105 236 (34.2) 3 × 105 224 (32.5) 1 × 106 213 (30.9) 3 × 106 201 (29.1) 1 × 107 193 (28.0) 3 × 107 193 (28.0) 1 × 108 193 (28.0) 3 × 108 (a) Make an S–N plot (stress amplitude versus logarithm cycles to failure) using these data. (b) What is the fatigue limit for this alloy? (c) Determine fatigue lifetimes at stress amplitudes of 230 MPa (33,500 psi) and 175 MPa (25,000 psi). (d) Estimate fatigue strengths at 2 × 105 and 6 × 106 cycles. Solution (a) The fatigue data for this alloy are plotted below. (b) The fatigue limit is the stress level at which the curve becomes horizontal, which is 193 MPa (28,000 psi).
- 408. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (c) As noted by the “A” set of dashed lines, the fatigue lifetime at a stress amplitude of 230 MPa is about 5 × 105 cycles (log N = 5.7). From the plot, the fatigue lifetime at a stress amplitude of 230 MPa (33,500 psi) is about 50,000 cycles (log N = 4.7). At 175 MPa (25,000 psi) the fatigue lifetime is essentially an infinite number of cycles since this stress amplitude is below the fatigue limit. (d) As noted by the “B” set of dashed lines, the fatigue strength at 2 × 105 cycles (log N = 5.3) is about 240 MPa (35,000 psi); and according to the “C” set of dashed lines, the fatigue strength at 6 × 106 cycles (log N = 6.78) is about 205 MPa (30,000 psi).
- 409. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.21 Suppose that the fatigue data for the cast iron in Problem 8.20 were taken for bending-rotating tests, and that a rod of this alloy is to be used for an automobile axle that rotates at an average rotational velocity of 750 revolutions per minute. Give maximum lifetimes of continuous driving that are allowable for the following stress levels: (a) 250 MPa (36,250 psi), (b) 215 MPa (31,000 psi), (c) 200 MPa (29,000 psi), and (d) 150 MPa (21,750 psi). Solution For each stress level, first read the corresponding lifetime from the above plot, then convert it into the number of cycles. (a) For a stress level of 250 MPa (36,250 psi), the fatigue lifetime is approximately 90,000 cycles. This translates into (9 × 104 cycles)(1 min/750 cycles) = 120 min. (b) For a stress level of 215 MPa (31,000 psi), the fatigue lifetime is approximately 2 × 106 cycles. This translates into (2 × 106 cycles)(1 min/750 cycles) = 2670 min = 44.4 h. (c) For a stress level of 200 MPa (29,000 psi), the fatigue lifetime is approximately 1 × 107 cycles. This translates into (1 × 107 cycles)(1 min/750 cycles) = 1.33 × 104 min = 222 h. (d) For a stress level of 150 MPa (21,750 psi), the fatigue lifetime is essentially infinite since we are below the fatigue limit [193 MPa (28,000 psi)].
- 410. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.22 Three identical fatigue specimens (denoted A, B, and C) are fabricated from a nonferrous alloy. Each is subjected to one of the maximum-minimum stress cycles listed below; the frequency is the same for all three tests. Specimen σmax (MPa) σmin (MPa) A +450 –350 B +400 –300 C +340 –340 (a) Rank the fatigue lifetimes of these three specimens from the longest to the shortest. (b) Now justify this ranking using a schematic S–N plot. Solution In order to solve this problem, it is necessary to compute both the mean stress and stress amplitude for each specimen. Since from Equation 8.14, mean stresses are the specimens are determined as follows: σm = σmax + σmin 2 σm (A) = 450 MPa + (−350 MPa) 2 = 50 MPa σm (B) = 400 MPa + (−300 MPa) 2 = 50 MPa σm (C) = 340 MPa + (−340 MPa) 2 = 0 MPa Furthermore, using Equation 8.16, stress amplitudes are computed as σa = σmax − σmin 2 σa (A) = 450 MPa − (−350 MPa) 2 = 400 MPa σa (B) = 400 MPa − (−300 MPa) 2 = 350 MPa σa (C) = 340 MPa − (−340 MPa) 2 = 340 MPa On the basis of these results, the fatigue lifetime for specimen C will be greater than specimen B, which in turn will be greater than specimen A. This conclusion is based upon the following S-N plot on which curves are plotted for two σm values.
- 411. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
- 412. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.23 Cite five factors that may lead to scatter in fatigue life data. Solution Five factors that lead to scatter in fatigue life data are (1) specimen fabrication and surface preparation, (2) metallurgical variables, (3) specimen alignment in the test apparatus, (4) variation in mean stress, and (5) variation in test cycle frequency.
- 413. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Crack Initiation and Propagation Factors That Affect Fatigue Life 8.24 Briefly explain the difference between fatigue striations and beachmarks both in terms of (a) size and (b) origin. Solution (a) With regard to size, beachmarks are normally of macroscopic dimensions and may be observed with the naked eye; fatigue striations are of microscopic size and it is necessary to observe them using electron microscopy. (b) With regard to origin, beachmarks result from interruptions in the stress cycles; each fatigue striation is corresponds to the advance of a fatigue crack during a single load cycle.
- 414. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.25 List four measures that may be taken to increase the resistance to fatigue of a metal alloy. Solution Four measures that may be taken to increase the fatigue resistance of a metal alloy are: (1) Polish the surface to remove stress amplification sites. (2) Reduce the number of internal defects (pores, etc.) by means of altering processing and fabrication techniques. (3) Modify the design to eliminate notches and sudden contour changes. (4) Harden the outer surface of the structure by case hardening (carburizing, nitriding) or shot peening.
- 415. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Generalized Creep Behavior 8.26 Give the approximate temperature at which creep deformation becomes an important consideration for each of the following metals: nickel, copper, iron, tungsten, lead, and aluminum. Solution Creep becomes important at about 0.4Tm, Tm being the absolute melting temperature of the metal. (The melting temperatures in degrees Celsius are found inside the front cover of the book.) For Ni, 0.4Tm = (0.4)(1455 + 273) = 691 K or 418°C (785°F) For Cu, 0.4Tm = (0.4)(1085 + 273) = 543 K or 270°C (518°F) For Fe, 0.4Tm = (0.4)(1538 + 273) = 725 K or 450°C (845°F) For W, 0.4Tm = (0.4)(3410 + 273) = 1473 K or 1200°C (2190°F) For Pb, 0.4Tm = (0.4)(327 + 273) = 240 K or −33°C (−27°F) For Al, 0.4Tm = (0.4)(660 + 273) = 373 K or 100°C (212°F)
- 416. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.27 The following creep data were taken on an aluminum alloy at 400°C (750°F) and a constant stress of 25 MPa (3660 psi). Plot the data as strain versus time, then determine the steady-state or minimum creep rate. Note: The initial and instantaneous strain is not included. Time (min) Strain Time (min) Strain 0 0.000 16 0.135 2 0.025 18 0.153 4 0.043 20 0.172 6 0.065 22 0.193 8 0.078 24 0.218 10 0.092 26 0.255 12 0.109 28 0.307 14 0.120 30 0.368 Solution These creep data are plotted below The steady-state creep rate (∆ε/∆t) is the slope of the linear region (i.e., the straight line that has been superimposed on the curve) as ∆ε ∆t = 0.230 − 0.09 30 min − 10 min = 7.0 × 10-3 min-1
- 417. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Stress and Temperature Effects 8.28 A specimen 750 mm (30 in.) long of an S-590 alloy (Figure 8.31) is to be exposed to a tensile stress of 80 MPa (11,600 psi) at 815°C (1500°F). Determine its elongation after 5000 h. Assume that the total of both instantaneous and primary creep elongations is 1.5 mm (0.06 in.). Solution From the 815°C line in Figure 8.31, the steady state creep rate Ýεs is about 5.5 × 10-6 h-1 at 80 MPa. The steady state creep strain, εs , therefore, is just the product of Ýε s and time as εs = Ýεs x (time) = (5.5 × 10−6 h-1)(5,000 h) = 0.0275 Strain and elongation are related as in Equation 6.2; solving for the steady state elongation, ∆ls, leads to ∆ls = l0 εs = (750 mm)(0.0275) = 20.6 mm (0.81 in.) Finally, the total elongation is just the sum of this ∆ls and the total of both instantaneous and primary creep elongations [i.e., 1.5 mm (0.06 in.)]. Therefore, the total elongation is 20.6 mm + 1.5 mm = 22.1 mm (0.87 in.).
- 418. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.29 For a cylindrical S-590 alloy specimen (Figure 8.31) originally 10 mm (0.40 in.) in diameter and 500 mm (20 in.) long, what tensile load is necessary to produce a total elongation of 145 mm (5.7 in.) after 2,000 h at 730°C (1350°F)? Assume that the sum of instantaneous and primary creep elongations is 8.6 mm (0.34 in.). Solution It is first necessary to calculate the steady state creep rate so that we may utilize Figure 8.31 in order to determine the tensile stress. The steady state elongation, ∆ls, is just the difference between the total elongation and the sum of the instantaneous and primary creep elongations; that is, ∆ls = 145 mm − 8.6 mm = 136.4 mm (5.36 in.) Now the steady state creep rate, Ýεs is just ε . s = ∆ε ∆ t = ∆ ls l0 ∆ t = 136.4 mm 500 mm 2,000 h = 1.36 × 10-4 h-1 Employing the 730°C line in Figure 8.31, a steady state creep rate of 1.36 × 10-4 h-1 corresponds to a stress σ of about 200 MPa (or 29,000 psi) [since log (1.36 × 10-4) = -3.866]. From this we may compute the tensile load using Equation 6.1 as F = σA0 = σπ d0 2 2 = (200 × 106 N/m2)(π) 10.0 × 10−3 m 2 2 = 15,700 N (3645 lbf)
- 419. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.30 If a component fabricated from an S-590 alloy (Figure 8.30) is to be exposed to a tensile stress of 300 MPa (43,500 psi) at 650°C (1200°F), estimate its rupture lifetime. Solution This problem asks us to calculate the rupture lifetime of a component fabricated from an S-590 alloy exposed to a tensile stress of 300 MPa at 650°C. All that we need do is read from the 650°C line in Figure 8.30 the rupture lifetime at 300 MPa; this value is about 600 h.
- 420. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.31 A cylindrical component constructed from an S-590 alloy (Figure 8.30) has a diameter of 12 mm (0.50 in.). Determine the maximum load that may be applied for it to survive 500 h at 925°C (1700°F). Solution We are asked in this problem to determine the maximum load that may be applied to a cylindrical S-590 alloy component that must survive 500 h at 925°C. From Figure 8.30, the stress corresponding to 500 h is about 50 MPa (7,250 psi). Since stress is defined in Equation 6.1 as σ = F/A0, and for a cylindrical specimen, A0 = π d0 2 2 , then F = σA0 = σπ d0 2 2 = (50 × 106 N/m2)(π) 12 × 10−3 m 2 2 = 5655 N (1424 lbf)
- 421. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.32 From Equation 8.19, if the logarithm of Ýεs is plotted versus the logarithm of σ, then a straight line should result, the slope of which is the stress exponent n. Using Figure 8.31, determine the value of n for the S-590 alloy at 925°C, and for the initial (i.e., lower-temperature) straight line segments at each of 650°C, 730°C, and 815°C. Solution The slope of the line from a log Ýεs versus log σ plot yields the value of n in Equation 8.19; that is n = ∆ log Ýεs ∆ log σ We are asked to determine the values of n for the creep data at the four temperatures in Figure 8.31 [i.e., at 925°C, and for the initial (i.e., lower-temperature) straight line segments at each of 650°C, 730°C, and 815°C]. This is accomplished by taking ratios of the differences between two log Ýε s and log σ values. (Note: Figure 8.31 plots log σ versus log Ýεs; therefore, values of n are equal to the reciprocals of the slopes of the straight-line segments.) Thus for 650°C n = ∆ log Ýεs ∆ log σ = log (10−1) − log (10−5) log (545 MPa) − log (240 MPa) = 11.2 While for 730°C n = ∆ log Ýεs ∆ log σ = log 1( ) − log (10−6) log (430 MPa) − log (125 MPa) = 11.2 And at 815°C n = ∆ log Ýεs ∆ log σ = log 1( ) − log (10−6) log (320 MPa) − log (65 MPa) = 8.7 And, finally at 925°C n = ∆ log Ýεs ∆ log σ = log 102 ( )− log (10−5) log (350 MPa) − log (44 MPa) = 7.8
- 422. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.33 (a) Estimate the activation energy for creep (i.e., Qc in Equation 8.20) for the S-590 alloy having the steady-state creep behavior shown in Figure 8.31. Use data taken at a stress level of 300 MPa (43,500 psi) and temperatures of 650°C and 730°C . Assume that the stress exponent n is independent of temperature. (b) Estimate Ýε s at 600°C (873 K) and 300 MPa. Solution (a) We are asked to estimate the activation energy for creep for the S-590 alloy having the steady-state creep behavior shown in Figure 8.31, using data taken at σ = 300 MPa and temperatures of 650°C and 730°C. Since σ is a constant, Equation 8.20 takes the form Ýεs = K2σnexp − Qc RT = K2 ' exp − Qc RT where K2 ' is now a constant. (Note: the exponent n has about the same value at these two temperatures per Problem 8.32.) Taking natural logarithms of the above expression ln Ýεs = ln K2 ' − Qc RT For the case in which we have creep data at two temperatures (denoted as T1 and T2 ) and their corresponding steady-state creep rates ( Ýεs1 and Ýεs2 ), it is possible to set up two simultaneous equations of the form as above, with two unknowns, namely K2 ' and Qc. Solving for Qc yields Qc = − R ln Ýεs1 − ln Ýεs2 1 T1 − 1 T2 Let us choose T1 as 650°C (923 K) and T2 as 730°C (1003 K); then from Figure 8.31, at σ = 300 MPa, Ýεs1 = 8.9 × 10-5 h-1 and Ýεs2 = 1.3 × 10-2 h-1. Substitution of these values into the above equation leads to Qc = − (8.31 J /mol- K) ln (8.9 × 10−5) − ln (1.3 × 10−2)[ ] 1 923 K − 1 1003 K = 480,000 J/mol
- 423. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (b) We are now asked to estimate Ýεs at 600°C (873 K) and 300 MPa. It is first necessary to determine the value of K2 ' , which is accomplished using the first expression above, the value of Qc, and one value each of Ýεs and T (say Ýεs1 and T1). Thus, K2 ' = Ýεs1 exp Qc RT1 = 8.9 × 10−5 h−1 ( )exp 480,000 J /mol (8.31 J /mol- K)(923 K) = 1.34 × 1023 h-1 Now it is possible to calculate Ýεs at 600°C (873 K) and 300 MPa as follows: Ýεs = K2 ' exp − Qc RT = 1.34 × 1023 h−1 ( )exp − 480,000 J/mol (8.31 J/mol- K)(873 K) = 2.47 × 10-6 h-1
- 424. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.34 Steady-state creep rate data are given below for nickel at 1000°C (1273 K): Ýεs (s–1 ) σ [MPa (psi)] 10–4 15 (2175) 10–6 4.5 (650) If it is known that the activation energy for creep is 272,000 J/mol, compute the steady-state creep rate at a temperature of 850°C (1123 K) and a stress level of 25 MPa (3625 psi). Solution Taking natural logarithms of both sides of Equation 8.20 yields ln Ýεs = ln K2 + n ln σ − Qc RT With the given data there are two unknowns in this equation--namely K2 and n. Using the data provided in the problem statement we can set up two independent equations as follows: ln 1 × 10−4 s−1 ( )= ln K2 + n ln (15 MPa) − 272,000 J /mol (8.31 J/mol- K)(1273 K) ln 1 × 10−6 s−1 ( )= ln K2 + n ln(4.5 MPa) − 272,000 J /mol (8.31 J/mol- K)(1273 K) Now, solving simultaneously for n and K2 leads to n = 3.825 and K2 = 466 s-1. Thus it is now possible to solve for Ýεs at 25 MPa and 1123 K using Equation 8.20 as Ýεs = K2σnexp − Qc RT = 466 s−1 ( )(25 MPa)3.825 exp − 272,000 J/mol (8.31 J/mol- K)(1123 K) 2.28 × 10-5 s-1
- 425. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.35 Steady-state creep data taken for a stainless steel at a stress level of 70 MPa (10,000 psi) are given as follows: Ýεs (s–1 ) T (K) 1.0 × 10–5 977 2.5 × 10–3 1089 If it is known that the value of the stress exponent n for this alloy is 7.0, compute the steady-state creep rate at 1250 K and a stress level of 50 MPa (7250 psi). Solution Taking natural logarithms of both sides of Equation 8.20 yields ln Ýεs = lnK2 + n lnσ − Qc RT With the given data there are two unknowns in this equation--namely K2 and Qc. Using the data provided in the problem statement we can set up two independent equations as follows: ln 1.0 × 10−5 s−1 ( )= ln K2 + (7.0) ln(70 MPa) − Qc (8.31 J/mol- K)(977 K) ln 2.5 × 10−3 s−1 ( )= ln K2 + (7.0) ln(70 MPa) − Qc (8.31 J/mol- K)(1089 K) Now, solving simultaneously for K2 and Qc leads to K2 = 2.55 × 105 s-1 and Qc = 436,000 J/mol. Thus, it is now possible to solve for Ýεs at 50 MPa and 1250 K using Equation 8.20 as Ýεs = K2σnexp − Qc RT = 2.55 × 105 s−1 ( )(50 MPa)7.0 exp − 436,000 J/mol (8.31 J/mol- K)(1250 K) 0.118 s-1
- 426. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Alloys for High-Temperature Use 8.36 Cite three metallurgical/processing techniques that are employed to enhance the creep resistance of metal alloys. Solution Three metallurgical/processing techniques that are employed to enhance the creep resistance of metal alloys are (1) solid solution alloying, (2) dispersion strengthening by using an insoluble second phase, and (3) increasing the grain size or producing a grain structure with a preferred orientation.
- 427. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. DESIGN PROBLEMS 8.D1 Each student (or group of students) is to obtain an object/structure/component that has failed. It may come from your home, an automobile repair shop, a machine shop, etc. Conduct an investigation to determine the cause and type of failure (i.e., simple fracture, fatigue, creep). In addition, propose measures that can be taken to prevent future incidents of this type of failure. Finally, submit a report that addresses the above issues. Each student or group of students is to submit their own report on a failure analysis investigation that was conducted.
- 428. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Principles of Fracture Mechanics 8.D2 (a) For the thin-walled spherical tank discussed in Design Example 8.1, on the basis of critical crack size criterion [as addressed in part (a)], rank the following polymers from longest to shortest critical crack length: nylon 6,6 (50% relative humidity), polycarbonate, poly(ethylene terephthalate), and poly(methyl methacrylate). Comment on the magnitude range of the computed values used in the ranking relative to those tabulated for metal alloys as provided in Table 8.3. For these computations, use data contained in Tables B.4 and B.5 in Appendix B. (b) Now rank these same four polymers relative to maximum allowable pressure according to the leak- before-break criterion, as described in the (b) portion of Design Example 8.1. As above, comment on these values in relation to those for the metal alloys that are tabulated in Table 8.4. Solution (a) This portion of the problem calls for us to rank four polymers relative to critical crack length in the wall of a spherical pressure vessel. In the development of Design Example 8.1, it was noted that critical crack length is proportional to the square of the KIc–σy ratio. Values of KIc and σy as taken from Tables B.4 and B.5 are tabulated below. (Note: when a range of σy or KIc values is given, the average value is used.) Material KIc (MPa m ) σy (MPa) Nylon 6,6 2.75 51.7 Polycarbonate 2.2 62.1 Poly(ethylene terephthlate) 5.0 59.3 Poly(methyl methacrylate) 1.2 63.5 On the basis of these values, the four polymers are ranked per the squares of the KIc–σy ratios as follows: Material KIc σ y 2 (mm) PET 7.11 Nylon 6,6 2.83 PC 1.26 PMMA 0.36
- 429. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. These values are smaller than those for the metal alloys given in Table 8.3, which range from 0.93 to 43.1 mm. (b) Relative to the leak-before-break criterion, the KIc 2 - σ y ratio is used. The four polymers are ranked according to values of this ratio as follows: Material KIc 2 σ y (MPa - m) PET 0.422 Nylon 6,6 0.146 PC 0.078 PMMA 0.023 These values are all smaller than those for the metal alloys given in Table 8.4, which values range from 1.2 to 11.2 MPa-m.
- 430. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Data Extrapolation Methods 8.D3 An S-590 alloy component (Figure 8.32) must have a creep rupture lifetime of at least 100 days at 500°C (773 K). Compute the maximum allowable stress level. Solution This problem asks that we compute the maximum allowable stress level to give a rupture lifetime of 100 days for an S-590 iron component at 773 K. It is first necessary to compute the value of the Larson-Miller parameter as follows: T (20 + log tr) = (773 K) 20 + log (100 days)(24 h/day)[ ]{ } = 18.1 × 103 From the curve in Figure 8.32, this value of the Larson-Miller parameter corresponds to a stress level of about 530 MPa (77,000 psi).
- 431. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.D4 Consider an S-590 alloy component (Figure 8.32) that is subjected to a stress of 200 MPa (29,000 psi). At what temperature will the rupture lifetime be 500 h? Solution We are asked in this problem to calculate the temperature at which the rupture lifetime is 500 h when an S- 590 iron component is subjected to a stress of 200 MPa (29,000 psi). From the curve shown in Figure 8.32, at 200 MPa, the value of the Larson-Miller parameter is 22.5 × 103 (K-h). Thus, 22.5 × 103 (K - h) = T (20 + log tr ) = T 20 + log (500 h)[ ] Or, solving for T yields T = 991 K (718°C).
- 432. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.D5 For an 18-8 Mo stainless steel (Figure 8.35), predict the time to rupture for a component that is subjected to a stress of 80 MPa (11,600 psi) at 700°C (973 K). Solution This problem asks that we determine, for an 18-8 Mo stainless steel, the time to rupture for a component that is subjected to a stress of 80 MPa (11,600 psi) at 700°C (973 K). From Figure 8.35, the value of the Larson- Miller parameter at 80 MPa is about 23.5 × 103, for T in K and tr in h. Therefore, 23.5 × 103 = T (20 + log tr) = 973(20 + log tr) And, solving for tr 24.15 = 20 + log tr which leads to tr = 1.42 × 104 h = 1.6 yr.
- 433. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 8.D6 Consider an 18-8 Mo stainless steel component (Figure 8.35) that is exposed to a temperature of 500°C (773 K). What is the maximum allowable stress level for a rupture lifetime of 5 years? 20 years? Solution We are asked in this problem to calculate the stress levels at which the rupture lifetime will be 5 years and 20 years when an 18-8 Mo stainless steel component is subjected to a temperature of 500°C (773 K). It first becomes necessary to calculate the value of the Larson-Miller parameter for each time. The values of tr corresponding to 5 and 20 years are 4.38 × 104 h and 1.75 × 105 h, respectively. Hence, for a lifetime of 5 years T (20 + log tr) = 773 20 + log (4.38 × 104 )[ ]= 19.05 × 103 And for tr = 20 years T (20 + log tr) = 773 20 + log (1.75 × 105)[ ]= 19.51 × 103 Using the curve shown in Figure 8.35, the stress values corresponding to the five- and twenty-year lifetimes are approximately 260 MPa (37,500 psi) and 225 MPa (32,600 psi), respectively.
- 434. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 9 PHASE DIAGRAMS PROBLEM SOLUTIONS Solubility Limit 9.1 Consider the sugar–water phase diagram of Figure 9.1. (a) How much sugar will dissolve in 1500 g water at 90°C (194°F)? (b) If the saturated liquid solution in part (a) is cooled to 20°C (68°F), some of the sugar will precipitate out as a solid. What will be the composition of the saturated liquid solution (in wt% sugar) at 20°C? (c) How much of the solid sugar will come out of solution upon cooling to 20°C? Solution (a) We are asked to determine how much sugar will dissolve in 1000 g of water at 90°C. From the solubility limit curve in Figure 9.1, at 90°C the maximum concentration of sugar in the syrup is about 77 wt%. It is now possible to calculate the mass of sugar using Equation 4.3 as Csugar (wt%) = msugar msugar + mwater × 100 77 wt% = msugar msugar + 1500 g × 100 Solving for msugar yields msugar = 5022 g (b) Again using this same plot, at 20°C the solubility limit (or the concentration of the saturated solution) is about 64 wt% sugar. (c) The mass of sugar in this saturated solution at 20°C (m'sugar ) may also be calculated using Equation 4.3 as follows: 64 wt% = m'sugar m'sugar + 1500 g × 100
- 435. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. which yields a value for m'sugar of 2667 g. Subtracting the latter from the former of these sugar concentrations yields the amount of sugar that precipitated out of the solution upon cooling m"sugar ; that is m"sugar = msugar − mÕsugar = 5022 g − 2667 g = 2355 g
- 436. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.2 At 500°C (930°F), what is the maximum solubility (a) of Cu in Ag? (b) Of Ag in Cu? Solution (a) From Figure 9.7, the maximum solubility of Cu in Ag at 500°C corresponds to the position of the β–(α + β) phase boundary at this temperature, or to about 2 wt% Cu. (b) From this same figure, the maximum solubility of Ag in Cu corresponds to the position of the α–(α + β) phase boundary at this temperature, or about 1.5 wt% Ag.
- 437. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Microstructure 9.3 Cite three variables that determine the microstructure of an alloy. Solution Three variables that determine the microstructure of an alloy are (1) the alloying elements present, (2) the concentrations of these alloying elements, and (3) the heat treatment of the alloy.
- 438. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Phase Equilibria 9.4 What thermodynamic condition must be met for a state of equilibrium to exist? Solution In order for a system to exist in a state of equilibrium the free energy must be a minimum for some specified combination of temperature, pressure, and composition.
- 439. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. One-Component (or Unary) Phase Diagrams 9.5 Consider a specimen of ice that is at 210°C and 1 atm pressure. Using Figure 9.2, the pressure– temperature phase diagram for H2O, determine the pressure to which the specimen must be raised or lowered to cause it (a) to melt, and (b) to sublime. Solution The figure below shows the pressure-temperature phase diagram for H2 O, Figure 10.2; a vertical line has been constructed at -10°C, and the location on this line at 1 atm pressure (point B) is also noted. (a) Melting occurs, (by changing pressure) as, moving vertically (upward) at this temperature, we cross the Ice-Liquid phase boundary. This occurs at approximately 570 atm; thus, the pressure of the specimen must be raised from 1 to 570 atm. (b) In order to determine the pressure at which sublimation occurs at this temperature, we move vertically downward from 1 atm until we cross the Ice-Vapor phase boundary. This intersection occurs at approximately 0.0023 atm.
- 440. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.6 At a pressure of 0.01 atm, determine (a) the melting temperature for ice, and (b) the boiling temperature for water. Solution The melting temperature for ice and the boiling temperature for water at a pressure of 0.01 atm may be determined from the pressure-temperature diagram for this system, Figure 10.2, which is shown below; a horizontal line has been constructed across this diagram at a pressure of 0.01 atm. The melting and boiling temperatures for ice at a pressure of 0.01 atm may be determined by moving horizontally across the pressure-temperature diagram at this pressure. The temperature corresponding to the intersection of the Ice-Liquid phase boundary is the melting temperature, which is approximately 1°C. On the other hand, the boiling temperature is at the intersection of the horizontal line with the Liquid-Vapor phase boundary--approximately 16°C.
- 441. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Binary Isomorphous Systems 9.7 Given here are the solidus and liquidus temperatures for the germanium-silicon system. Construct the phase diagram for this system and label each region. Composition (wt% Si) Solidus Temperature (°C) Liquidus Temperature (°C) 0 938 938 10 1005 1147 20 1065 1226 30 1123 1278 40 1178 1315 50 1232 1346 60 1282 1367 70 1326 1385 80 1359 1397 90 1390 1408 100 1414 1414 Solution The germanium-silicon phase diagram is constructed below.
- 442. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Interpretation of Phase Diagrams 9.8 Cite the phases that are present and the phase compositions for the following alloys: (a) 90 wt% Zn-10 wt% Cu at 400°C (750°F) (b) 75 wt% Sn-25 wt% Pb at 175°C (345°F) (c) 55 wt% Ag-45 wt% Cu at 900°C (1650°F) (d) 30 wt% Pb-70 wt% Mg at 425°C (795°F) (e) 2.12 kg Zn and 1.88 kg Cu at 500°C (930°F) (f) 37 lbm Pb and 6.5 lbm Mg at 400°C (750°F) (g) 8.2 mol Ni and 4.3 mol Cu at 1250°C (2280°F) (h) 4.5 mol Sn and 0.45 mol Pb at 200°C (390°F) Solution This problem asks that we cite the phase or phases present for several alloys at specified temperatures. (a) That portion of the Cu-Zn phase diagram (Figure 9.19) that pertains to this problem is shown below; the point labeled “A” represents the 90 wt% Zn-10 wt% Cu composition at 400°C. As may be noted, point A lies within the ε and η phase field. A tie line has been constructed at 400°C; its intersection with the ε−ε + η phase boundary is at 87 wt% Zn, which corresponds to the composition of the ε phase. Similarly, the tie-line intersection with the ε + η−η phase boundary occurs at 97 wt% Zn, which is the composition of the η phase. Thus, the phase compositions are as follows:
- 443. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Cε = 87 wt% Zn-13 wt% Cu Cη = 97 wt% Zn-3 wt% Cu (b) That portion of the Pb-Sn phase diagram (Figure 9.8) that pertains to this problem is shown below; the point labeled “B” represents the 75 wt% Sn-25 wt% Pb composition at 175°C. As may be noted, point B lies within the α + β phase field. A tie line has been constructed at 175°C; its intersection with the α−α + β phase boundary is at 16 wt% Sn, which corresponds to the composition of the α phase. Similarly, the tie-line intersection with the α + β−β phase boundary occurs at 97 wt% Sn, which is the composition of the β phase. Thus, the phase compositions are as follows: Cα = 16 wt% Sn-84 wt% Pb Cβ = 97 wt% Sn-3 wt% Pb (c) The Ag-Cu phase diagram (Figure 9.7) is shown below; the point labeled “C” represents the 55 wt% Ag-45 wt% Cu composition at 900°C.
- 444. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. As may be noted, point C lies within the Liquid phase field. Therefore, only the liquid phase is present; its composition is 55 wt% Ag-45 wt% Cu. (d) The Mg-Pb phase diagram (Figure 9.20) is shown below; the point labeled “D” represents the 30 wt% Pb-70 wt% Mg composition at 425°C.
- 445. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. As may be noted, point D lies within the α phase field. Therefore, only the α phase is present; its composition is 30 wt% Pb-70 wt% Mg. (e) For an alloy composed of 2.12 kg Zn and 1.88 kg Cu and at 500°C, we must first determine the Zn and Cu concentrations, as CZn = 2.12 kg 2.12 kg + 1.88 kg × 100 = 53 wt% CCu = 1.88 kg 2.12 kg + 1.88 kg × 100 = 47 wt% That portion of the Cu-Zn phase diagram (Figure 9.19) that pertains to this problem is shown below; the point labeled “E” represents the 53 wt% Zn-47 wt% Cu composition at 500°C.
- 446. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. As may be noted, point E lies within the β + γ phase field. A tie line has been constructed at 500°C; its intersection with the β−β + γ phase boundary is at 49 wt% Zn, which corresponds to the composition of the β phase. Similarly, the tie-line intersection with the β + γ−γ phase boundary occurs at 58 wt% Zn, which is the composition of the γ phase. Thus, the phase compositions are as follows: Cβ = 49 wt% Zn-51 wt% Cu Cγ = 58 wt% Zn-42 wt% Cu (f) For an alloy composed of 37 lbm Pb and 6.5 lbm Mg and at 400°C, we must first determine the Pb and Mg concentrations, as CPb = 37 lbm 37 lbm + 6.5 lbm × 100 = 85 wt% CMg = 6.5 lbm 37 lbm + 6.5 lbm × 100 = 15 wt% That portion of the Mg-Pb phase diagram (Figure 9.20) that pertains to this problem is shown below; the point labeled “F” represents the 85 wt% Pb-15 wt% Mg composition at 400°C.
- 447. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. As may be noted, point F lies within the L + Mg2Pb phase field. A tie line has been constructed at 400°C; it intersects the vertical line at 81 wt% Pb, which corresponds to the composition of Mg2Pb. Furthermore, the tie line intersection with the L + Mg2Pb-L phase boundary is at 93 wt% Pb, which is the composition of the liquid phase. Thus, the phase compositions are as follows: CMg2Pb = 81 wt% Pb-19 wt% Mg CL = 93 wt% Pb-7 wt% Mg (g) For an alloy composed of 8.2 mol Ni and 4.3 mol Cu and at 1250°C, it is first necessary to determine the Ni and Cu concentrations, which we will do in wt% as follows: nNi ' = nmNi ANi = (8.2 mol)(58.69 g/mol) = 481.3 g nCu ' = nmCu ACu = (4.3 mol)(63.55 g/mol) = 273.3 g CNi = 481.3 g 481.3 g + 273.3 g × 100 = 63.8 wt% CCu = 273.3 g 481.3 g + 273.3 g × 100 = 36.2 wt% The Cu-Ni phase diagram (Figure 9.3a) is shown below; the point labeled “G” represents the 63.8 wt% Ni-36.2 wt% Cu composition at 1250°C.
- 448. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. As may be noted, point G lies within the α phase field. Therefore, only the α phase is present; its composition is 63.8 wt% Ni-36.2 wt% Cu. (h) For an alloy composed of 4.5 mol Sn and 0.45 mol Pb and at 200°C, it is first necessary to determine the Sn and Pb concentrations, which we will do in weight percent as follows: nSn ’ = nmSn ASn = (4.5 mol)(118.71 g/mol) = 534.2 g nPb ' = nmPb APb = (0.45 mol)(207.2 g/mol) = 93.2 g CSn = 534.2 g 534.2 g + 93.2 g × 100 = 85.1 wt% CPb = 93.2 g 534.2 g + 93.2 g × 100 = 14.9 wt% That portion of the Pb-Sn phase diagram (Figure 9.8) that pertains to this problem is shown below; the point labeled “H” represents the 85.1 wt% Sn-14.9 wt% Pb composition at 200°C.
- 449. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. As may be noted, point H lies within the β + L phase field. A tie line has been constructed at 200°C; its intersection with the L−β + L phase boundary is at 74 wt% Sn, which corresponds to the composition of the L phase. Similarly, the tie-line intersection with the β + L−β phase boundary occurs at 97.5 wt% Sn, which is the composition of the β phase. Thus, the phase compositions are as follows: Cβ = 97.5 wt% Sn-2.5 wt% Pb CL = 74 wt% Sn-26 wt% Pb
- 450. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.9 Is it possible to have a copper–nickel alloy that, at equilibrium, consists of a liquid phase of composition 20 wt% Ni–80 wt% Cu and also an α phase of composition 37 wt% Ni–63 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why. Solution It is not possible to have a Cu-Ni alloy, which at equilibrium, consists of a liquid phase of composition 20 wt% Ni-80 wt% Cu and an α phase of composition 37 wt% Ni-63 wt% Cu. From Figure 9.3a, a single tie line does not exist within the α + L region that intersects the phase boundaries at the given compositions. At 20 wt% Ni, the L-(α + L) phase boundary is at about 1200°C, whereas at 37 wt% Ni the (L + α)-α phase boundary is at about 1230°C.
- 451. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.10 Is it possible to have a copper-zinc alloy that, at equilibrium, consists of an ε phase of composition 80 wt% Zn-20 wt% Cu, and also a liquid phase of composition 95 wt% Zn-5 wt% Cu? If so, what will be the approximate temperature of the alloy? If this is not possible, explain why. Solution It is not possible to have a Cu-Zn alloy, which at equilibrium consists of an ε phase of composition 80 wt% Zn-20 wt% Cu and also a liquid phase of composition 95 wt% Zn-5 wt% Cu. From Figure 9.19 a single tie line does not exist within the ε + L region which intersects the phase boundaries at the given compositions. At 80 wt% Zn, the ε-(ε + L) phase boundary is at about 575°C, whereas at 95 wt% Zn the (ε + L)-L phase boundary is at about 490°C.
- 452. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.11 A copper-nickel alloy of composition 70 wt% Ni-30 wt% Cu is slowly heated from a temperature of 1300°C (2370°F). (a) At what temperature does the first liquid phase form? (b) What is the composition of this liquid phase? (c) At what temperature does complete melting of the alloy occur? (d) What is the composition of the last solid remaining prior to complete melting? Solution Shown below is the Cu-Ni phase diagram (Figure 9.3a) and a vertical line constructed at a composition of 70 wt% Ni-30 wt% Cu. (a) Upon heating from 1300°C, the first liquid phase forms at the temperature at which this vertical line intersects the α-(α + L) phase boundary--i.e., about 1345°C. (b) The composition of this liquid phase corresponds to the intersection with the (α + L)-L phase boundary, of a tie line constructed across the α + L phase region at 1345°C--i.e., 59 wt% Ni; (c) Complete melting of the alloy occurs at the intersection of this same vertical line at 70 wt% Ni with the (α + L)-L phase boundary--i.e., about 1380°C;
- 453. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (d) The composition of the last solid remaining prior to complete melting corresponds to the intersection with α-(α + L) phase boundary, of the tie line constructed across the α + L phase region at 1380°C--i.e., about 79 wt% Ni.
- 454. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.12 A 50 wt% Pb-50 wt% Mg alloy is slowly cooled from 700°C (1290°F) to 400°C (750°F). (a) At what temperature does the first solid phase form? (b) What is the composition of this solid phase? (c) At what temperature does the liquid solidify? (d) What is the composition of this last remaining liquid phase? Solution Shown below is the Mg-Pb phase diagram (Figure 9.20) and a vertical line constructed at a composition of 50 wt% Pb-50 wt% Mg. (a) Upon cooling from 700°C, the first solid phase forms at the temperature at which a vertical line at this composition intersects the L-(α + L) phase boundary--i.e., about 560°C; (b) The composition of this solid phase corresponds to the intersection with the α-(α + L) phase boundary, of a tie line constructed across the α + L phase region at 560°C--i.e., 21 wt% Pb-79 wt% Mg; (c) Complete solidification of the alloy occurs at the intersection of this same vertical line at 50 wt% Pb with the eutectic isotherm--i.e., about 465°C;
- 455. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (d) The composition of the last liquid phase remaining prior to complete solidification corresponds to the eutectic composition--i.e., about 67 wt% Pb-33 wt% Mg.
- 456. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.13 For an alloy of composition 74 wt% Zn-26 wt% Cu, cite the phases present and their compositions at the following temperatures: 850°C, 750°C, 680°C, 600°C, and 500°C. Solution This problem asks us to determine the phases present and their concentrations at several temperatures, for an alloy of composition 74 wt% Zn-26 wt% Cu. From Figure 9.19 (the Cu-Zn phase diagram), which is shown below with a vertical line constructed at the specified composition: At 850°C, a liquid phase is present; CL = 74 wt% Zn-26 wt% Cu At 750°C, γ and liquid phases are present; Cγ = 67 wt% Zn-33 wt% Cu; CL = 77 wt% Zn-23 wt% Cu At 680°C, δ and liquid phases are present; Cδ = 73 wt% Zn-27 wt% Cu; CL = 82 wt% Zn-18 wt% Cu At 600°C, the δ phase is present; Cδ = 74 wt% Zn-26 wt% Cu At 500°C, γ and ε phases are present; Cγ = 69 wt% Zn-31 wt% Cu; Cε = 78 wt% Zn-22 wt% Cu
- 457. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.14 Determine the relative amounts (in terms of mass fractions) of the phases for the alloys and temperatures given in Problem 9.8. Solution This problem asks that we determine the phase mass fractions for the alloys and temperatures in Problem 9.8. (a) From Problem 9.8a, ε and η phases are present for a 90 wt% Zn-10 wt% Cu alloy at 400°C, as represented in the portion of the Cu-Zn phase diagram shown below (at point A). Furthermore, the compositions of the phases, as determined from the tie line are Cε = 87 wt% Zn-13 wt% Cu Cη = 97 wt% Zn-3 wt% Cu Inasmuch as the composition of the alloy C0 = 90 wt% Zn, application of the appropriate lever rule expressions (for compositions in weight percent zinc) leads to Wε = Cη − C0 Cη − Cε = 97 − 90 97 − 87 = 0.70 Wη = C0 − Cε Cη − Cε = 90 − 87 97 − 87 = 0.30
- 458. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (b) From Problem 9.8b, α and β phases are present for a 75 wt% Sn-25 wt% Pb alloy at 175°C, as represented in the portion of the Pb-Sn phase diagram shown below (at point B). Furthermore, the compositions of the phases, as determined from the tie line are Cα = 16 wt% Sn-84 wt% Pb Cβ = 97 wt% Sn-3 wt% Pb Inasmuch as the composition of the alloy C0 = 75 wt% Sn, application of the appropriate lever rule expressions (for compositions in weight percent tin) leads to Wα = Cβ − C0 Cβ − Cα = 97 − 75 97 − 16 = 0.27 Wβ = C0 − Cα Cβ − Cα = 75 − 16 97 − 16 = 0.73 (c) From Problem 9.8c, just the liquid phase is present for a 55 wt% Ag-45 wt% Cu alloy at 900°C, as may be noted in the Ag-Cu phase diagram shown below (at point C)—i.e., WL = 1.0
- 459. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (d) From Problem 9.8d, just the α phase is present for a 30 wt% Pb-70 wt% Mg alloy at 425°C, as may be noted in the Mg-Pb phase diagram shown below (at point D)—i.e., Wα = 1.0
- 460. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (e) From Problem 9.8e, β and γ phases are present for an alloy composed of 2.12 kg Zn and 1.88 kg Cu (i.e., of composition 53 wt% Zn-47 wt% Cu) at 500°C. This is represented in the portion of the Cu-Zn phase diagram shown below (at point E). Furthermore, the compositions of the phases, as determined from the tie line are Cβ = 49 wt% Zn-51 wt% Cu Cγ = 58 wt% Zn-42 wt% Cu Inasmuch as the composition of the alloy C0 = 53 wt% Zn and application of the appropriate lever rule expressions (for compositions in weight percent zinc) leads to Wβ = Cγ − C0 Cγ − Cβ = 58 − 53 58 − 49 = 0.56 Wγ = C0 − Cβ Cγ − Cβ = 53 − 49 58 − 49 = 0.44 (f) From Problem 9.8f, L and Mg2Pb phases are present for an alloy composed of 37 lbm Pb and 6.5 lbm Mg (85 wt% Pb-15 wt% Mg) at 400°C. This is represented in the portion of the Pb-Mg phase diagram shown below (at point F).
- 461. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Furthermore, the compositions of the phases, as determined from the tie line are CMg2Pb = 81 wt% Pb-19 wt% Mg CL = 93 wt% Pb-7 wt% Mg Inasmuch as the composition of the alloy C0 = 85 wt% Pb and application of the appropriate lever rule expressions (for compositions in weight percent lead) leads to WMg2Pb = CL − C0 CL − CMg2Pb = 93 − 85 93 − 81 = 0.67 WL = C0 − CMg2Pb CL − CMg2Pb = 85 − 81 93 − 81 = 0.33 (g) From Problem 9.8g, just the α phase is present (i.e., Wα = 1.0) for an alloy composed of 8.2 mol Ni and 4.3 mol Cu (i.e., 63.8 wt% Ni-36.2 wt% Cu) at 1250°C; such may be noted (as point G) in the Cu-Ni phase diagram shown below.
- 462. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (h) From Problem 9.8h, β and L phases are present for an alloy composed of 4.5 mol Sn and 0.45 mol Pb (85.1 wt% Sn-14.9 wt% Pb ) and at 200°C. This is represented in the portion of the Pb-Sn phase diagram shown below (at point H). Furthermore, the compositions of the phases, as determined from the tie line are
- 463. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Cβ = 97.5 wt% Sn-2.5 wt% Pb CL = 74 wt% Sn-26 wt% Pb Inasmuch as the composition of the alloy C0 = 85.1 wt% Sn, application of the appropriate lever rule expressions (for compositions in weight percent lead) leads to Wβ = C0 − CL Cβ − CL = 85.1 − 74 97.5 − 74 = 0.47 WL = Cβ − C0 Cβ − CL = 97.5 − 85.1 97.5 − 74 = 0.53
- 464. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.15 A 1.5-kg specimen of a 90 wt% Pb–10 wt% Sn alloy is heated to 250°C (480°F); at this temperature it is entirely an α-phase solid solution (Figure 9.8). The alloy is to be melted to the extent that 50% of the specimen is liquid, the remainder being the α phase. This may be accomplished either by heating the alloy or changing its composition while holding the temperature constant. (a) To what temperature must the specimen be heated? (b) How much tin must be added to the 1.5-kg specimen at 250°C to achieve this state? Solution (a) Probably the easiest way to solve this part of the problem is by trial and error--that is, on the Pb-Sn phase diagram (Figure 9.8), moving vertically at the given composition, through the α + L region until the tie-line lengths on both sides of the given composition are the same. This occurs at approximately 295°C (560°F). (b) We can also produce a 50% liquid solution at 250°C, by adding Sn to the alloy. At 250°C and within the α + L phase region Cα = 14 wt% Sn-86 wt% Pb CL = 34 wt% Sn-66 wt% Pb Let C0 be the new alloy composition to give Wα = WL = 0.5. Then, Wα = 0.5 = CL − C0 CL − Cα = 34 − C0 34 − 14 And solving for C0 gives 24 wt% Sn. Now, let mSn be the mass of Sn added to the alloy to achieve this new composition. The amount of Sn in the original alloy is (0.10)(1.5 kg) = 0.15 kg Then, using a modified form of Equation 4.3 0.15 kg + mSn 1.5 kg + mSn ×100 = 24 And, solving for mSn (the mass of tin to be added), yields mSn = 0.276 kg.
- 465. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.16 A magnesium-lead alloy of mass 5.5 kg consists of a solid α phase that has a composition that is just slightly below the solubility limit at 200°C (390°F). (a) What mass of lead is in the alloy? (b) If the alloy is heated to 350°C (660°F), how much more lead may be dissolved in the α phase without exceeding the solubility limit of this phase? Solution (a) This portion of the problem asks that we calculate, for a Pb-Mg alloy, the mass of lead in 5.5 kg of the solid α phase at 200°C just below the solubility limit. From Figure 9.20, the solubility limit for the α phase at 200°C corresponds to the position (composition) of the α-α + Mg2Pb phase boundary at this temperature, which is about 5 wt% Pb. Therefore, the mass of Pb in the alloy is just (0.05)(5.5 kg) = 0.28 kg. (b) At 350°C, the solubility limit of the α phase increases to approximately 25 wt% Pb. In order to determine the additional amount of Pb that may be added (mPb), we utilize a modified form of Equation 4.3 as CPb = 25 wt% = 0.28 kg + mPb 5.5 kg + mPb × 100 Solving for mPb yields mPb = 1.46 kg.
- 466. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.17 A 90 wt% Ag-10 wt% Cu alloy is heated to a temperature within the β + liquid phase region. If the composition of the liquid phase is 85 wt% Ag, determine: (a) The temperature of the alloy (b) The composition of the β phase (c) The mass fractions of both phases Solution (a) In order to determine the temperature of a 90 wt% Ag-10 wt% Cu alloy for which β and liquid phases are present with the liquid phase of composition 85 wt% Ag, we need to construct a tie line across the β + L phase region of Figure 9.7 that intersects the liquidus line at 85 wt% Ag; this is possible at about 850°C. (b) The composition of the β phase at this temperature is determined from the intersection of this same tie line with solidus line, which corresponds to about 95 wt% Ag. (c) The mass fractions of the two phases are determined using the lever rule, Equations 9.1 and 9.2 with C0 = 90 wt% Ag, CL = 85 wt% Ag, and Cβ = 95 wt% Ag, as Wβ = C0 − CL Cβ − CL = 90 − 85 95 − 85 = 0.50 WL = Cβ − C0 Cβ − CL = 95 − 90 95 − 85 = 0.50
- 467. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.18 A 30 wt% Sn-70 wt% Pb alloy is heated to a temperature within the α + liquid phase region. If the mass fraction of each phase is 0.5, estimate: (a) The temperature of the alloy (b) The compositions of the two phases Solution (a) We are given that the mass fractions of α and liquid phases are both 0.5 for a 30 wt% Sn-70 wt% Pb alloy and asked to estimate the temperature of the alloy. Using the appropriate phase diagram, Figure 9.8, by trial and error with a ruler, a tie line within the α + L phase region that is divided in half for an alloy of this composition exists at about 230°C. (b) We are now asked to determine the compositions of the two phases. This is accomplished by noting the intersections of this tie line with both the solidus and liquidus lines. From these intersections, Cα = 15 wt% Sn, and CL = 43 wt% Sn.
- 468. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.19 For alloys of two hypothetical metals A and B, there exist an α, A-rich phase and a β, B-rich phase. From the mass fractions of both phases for two different alloys provided in the table below, (which are at the same temperature), determine the composition of the phase boundary (or solubility limit) for both α and β phases at this temperature. Alloy Composition Fraction α Phase Fraction β Phase 60 wt% A–40 wt% B 0.57 0.43 30 wt% A–70 wt% B 0.14 0.86 Solution The problem is to solve for compositions at the phase boundaries for both α and β phases (i.e., Cα and Cβ). We may set up two independent lever rule expressions, one for each composition, in terms of Cα and Cβ as follows: Wα1 = 0.57 = Cβ − C01 Cβ − Cα = Cβ − 60 Cβ − Cα Wα2 = 0.14 = Cβ − C02 Cβ − Cα = Cβ − 30 Cβ − Cα In these expressions, compositions are given in wt% of A. Solving for Cα and Cβ from these equations, yield Cα = 90 (or 90 wt% A-10 wt% B) Cβ = 20.2 (or 20.2 wt% A-79.8 wt% B)
- 469. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.20 A hypothetical A–B alloy of composition 55 wt% B–45 wt% A at some temperature is found to consist of mass fractions of 0.5 for both α and β phases. If the composition of the β phase is 90 wt% B–10 wt% A, what is the composition of the α phase? Solution For this problem, we are asked to determine the composition of the β phase given that C0 = 55 (or 55 wt% B-45 wt% A) Cβ = 90 (or 90 wt% B-10 wt% A) Wα = Wβ = 0.5 If we set up the lever rule for Wα Wα = 0.5 = Cβ − C0 Cβ − Cα = 90 − 55 90 − Cα And solving for Cα Cα = 20 (or 20 wt% B-80 wt% A)
- 470. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.21 Is it possible to have a copper-silver alloy of composition 50 wt% Ag-50 wt% Cu, which, at equilibrium, consists of α and β phases having mass fractions Wα = 0.60 and Wβ = 0.40? If so, what will be the approximate temperature of the alloy? If such an alloy is not possible, explain why. Solution It is not possible to have a Cu-Ag alloy of composition 50 wt% Ag-50 wt% Cu which consists of mass fractions Wα = 0.60 and Wβ = 0.40. Using the appropriate phase diagram, Figure 9.7, and, using Equations 9.1 and 9.2 let us determine Wα and Wβ at just below the eutectic temperature and also at room temperature. At just below the eutectic, Cα = 8.0 wt% Ag and Cβ = 91.2 wt% Ag; thus, Wα = Cβ − C0 Cβ − Cα = 91.2 − 50 91.2 − 8 = 0.50 Wβ =1.00 − Wα =1.00 − 0.50 = 0.50 Furthermore, at room temperature, Cα = 0 wt% Ag and Cβ = 100 wt% Ag; employment of Equations 9.1 and 9.2 yields Wα = Cβ − C0 Cβ − Cα = 100 − 50 100 − 0 = 0.50 And, Wβ = 0.50. Thus, the mass fractions of the α and β phases, upon cooling through the α + β phase region will remain approximately constant at about 0.5, and will never have values of Wα = 0.60 and Wβ = 0.40 as called for in the problem.
- 471. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.22 For 11.20 kg of a magnesium-lead alloy of composition 30 wt% Pb-70 wt% Mg, is it possible, at equilibrium, to have α and Mg2Pb phases having respective masses of 7.39 kg and 3.81 kg? If so, what will be the approximate temperature of the alloy? If such an alloy is not possible, explain why. Solution Yes, it is possible to have a 30 wt% Pb-70 wt% Mg alloy which has masses of 7.39 kg and 3.81 kg for the α and Mg2Pb phases, respectively. In order to demonstrate this, it is first necessary to determine the mass fraction of each phase as follows: Wα = mα mα + mMg2Pb = 7.39 kg 7.39 kg + 3.81 kg = 0.66 WMg2Pb = 1.00 − 0.66 = 0.34 Now, if we apply the lever rule expression for Wα Wα = CMg2Pb − C0 CMg2Pb − Cα Since the Mg2Pb phase exists only at 81 wt% Pb, and C0 = 30 wt% Pb Wα = 0.66 = 81 − 30 81 − Cα Solving for Cα from this expression yields Cα = 3.7 wt% Pb. The position along the α−(α + Mg2Pb) phase boundary of Figure 9.20 corresponding to this composition is approximately 190°C.
- 472. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.23 Derive Equations 9.6a and 9.7a, which may be used to convert mass fraction to volume fraction, and vice versa. Solution This portion of the problem asks that we derive Equation 9.6a, which is used to convert from phase weight fraction to phase volume fraction. Volume fraction of phase α, Vα, is defined by Equation 9.5 as Vα = vα vα + vβ (9.S1) where vα and vβ are the volumes of the respective phases in the alloy. Furthermore, the density of each phase is equal to the ratio of its mass and volume, or upon rearrangement vα = mα ρα (9.S2a) vβ = mβ ρβ (9.S2b) Substitution of these expressions into Equation 9.S1 leads to Vα = mα ρα mα ρα + mβ ρβ (9.S3) in which m's and ρ's denote masses and densities, respectively. Now, the mass fractions of the α and β phases (i.e., Wα and Wβ) are defined in terms of the phase masses as Wα = mα mα + mβ (9.S4a) Wβ = mβ mα + mβ (9.S4b) Which, upon rearrangement yield
- 473. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. mα = Wα (mα + mβ) (9.S5a) mβ = Wβ (mα + mβ) (9.S5b) Incorporation of these relationships into Equation 9.S3 leads to Vα = Wα (mα + mβ) ρα Wα (mα + mβ) ρα + Wβ (mα + mβ) ρβ Vα = Wα ρα Wα ρα + Wβ ρβ (9.S6) which is the desired equation. For this portion of the problem we are asked to derive Equation 9.7a, which is used to convert from phase volume fraction to mass fraction. Mass fraction of the α phase is defined as Wα = mα mα + mβ (9.S7) From Equations 9.S2a and 9.S2b mα = vαρα (9.S8a) mβ = vβρβ (9.S8b) Substitution of these expressions into Equation 9.S7 yields Wα = vαρα vαρα + vβρβ (9.S9)
- 474. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. From Equation 9.5 and its equivalent for Vβ the following may be written: vα = Vα(vα + vβ) (9.S10a) vβ = Vβ(vα + vβ) (9.S10b) Substitution of Equations 9.S10a and 9.S10b into Equation 9.S9 yields Wα = Vα(vα + vβ)ρα Vα(vα + vβ)ρα + Vβ(vα + vβ)ρβ Wα = Vαρα Vαρα + Vβρβ (9.S11) which is the desired expression.
- 475. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.24 Determine the relative amounts (in terms of volume fractions) of the phases for the alloys and temperatures given in Problem 9.8a, b, and c. Below are given the approximate densities of the various metals at the alloy temperatures: Metal Temperature (°C) Density (g/cm3 ) Ag 900 9.97 Cu 400 8.77 Cu 900 8.56 Pb 175 11.20 Sn 175 7.22 Zn 400 6.83 Solution This problem asks that we determine the phase volume fractions for the alloys and temperatures in Problems 9.8a, b, and c. This is accomplished by using the technique illustrated in Example Problem 9.3, and also the results of Problems 9.8 and 9.14. (a) This is a Cu-Zn alloy at 400°C, wherein Cε = 87 wt% Zn-13 wt% Cu Cη = 97 wt% Zn-3 wt% Cu Wε = 0.70 Wη = 0.30 ρCu = 8.77 g/cm3 ρZn = 6.83 g/cm3 Using these data it is first necessary to compute the densities of the ε and η phases using Equation 4.10a. Thus ρε = 100 CZn(ε) ρZn + CCu(ε) ρCu
- 476. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = 100 87 6.83 g/cm3 + 13 8.77 g/cm3 = 7.03 g/cm3 ρη = 100 CZn(η) ρZn + CCu(η) ρCu = 100 97 6.83 g/cm3 + 3 8.77 g/cm3 = 6.88 g/cm3 Now we may determine the Vε and Vη values using Equation 9.6. Thus, Vε = Wε ρε Wε ρε + Wη ρη = 0.70 7.03 g/cm3 0.70 7.03 g/cm3 + 0.30 6.88 g/cm3 = 0.70 Vη = Wη ρη Wε ρε + Wη ρη = 0.30 6.88 g/cm3 0.70 7.03 g/cm3 + 0.30 6.88 g/cm3 = 0.30 (b) This is a Pb-Sn alloy at 175°C, wherein Cα = 16 wt% Sn-84 wt% Pb Cβ = 97 wt% Sn-3 wt% Pb
- 477. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Wα = 0.27 Wβ = 0.73 ρSn = 7.22 g/cm3 ρPb = 11.20 g/cm3 Using this data it is first necessary to compute the densities of the α and β phases. Thus ρα = 100 CSn(α) ρSn + CPb(α) ρPb = 100 16 7.22 g/cm3 + 84 11.20 g/cm3 = 10.29 g/cm3 ρβ = 100 CSn(β) ρSn + CPb(β) ρPb = 100 97 7.22 g/cm3 + 3 11.20 g/cm3 = 7.30 g/cm3 Now we may determine the Vα and Vβ values using Equation 9.6. Thus, Vα = Wα ρα Wα ρα + Wβ ρβ = 0.27 10.29 g/cm3 0.27 10.29 g/cm3 + 0.73 7.30 g/cm3 = 0.21 Vβ = Wβ ρβ Wα ρα + Wβ ρβ
- 478. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = 0.73 7.30 g/cm3 0.27 10.29 g/cm3 + 0.73 7.30 g/cm3 = 0.79 (c) This is a Ag-Cu alloy at 900°C, wherein only the liquid phase is present. Therefore, VL = 1.0.
- 479. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Development of Microstructure in Isomorphous Alloys 9.25 (a) Briefly describe the phenomenon of coring and why it occurs. (b) Cite one undesirable consequence of coring. Solution (a) Coring is the phenomenon whereby concentration gradients exist across grains in polycrystalline alloys, with higher concentrations of the component having the lower melting temperature at the grain boundaries. It occurs, during solidification, as a consequence of cooling rates that are too rapid to allow for the maintenance of the equilibrium composition of the solid phase. (b) One undesirable consequence of a cored structure is that, upon heating, the grain boundary regions will melt first and at a temperature below the equilibrium phase boundary from the phase diagram; this melting results in a loss in mechanical integrity of the alloy.
- 480. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Mechanical Properties of Isomorphous Alloys 9.26 It is desirable to produce a copper-nickel alloy that has a minimum noncold-worked tensile strength of 350 MPa (50,750 psi) and a ductility of at least 48%EL. Is such an alloy possible? If so, what must be its composition? If this is not possible, then explain why. Solution From Figure 9.6a, a tensile strength greater than 350 MPa (50,750 psi) is possible for compositions between about 22.5 and 98 wt% Ni. On the other hand, according to Figure 9.6b, ductilities greater than 48%EL exist for compositions less than about 8 wt% and greater than about 98 wt% Ni. Therefore, the stipulated criteria are met only at a composition of 98 wt% Ni.
- 481. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Binary Eutectic Systems 9.27 A 45 wt% Pb–55 wt% Mg alloy is rapidly quenched to room temperature from an elevated temperature in such a way that the high-temperature microstructure is preserved. This microstructure is found to consist of the α phase and Mg2Pb, having respective mass fractions of 0.65 and 0.35. Determine the approximate temperature from which the alloy was quenched. Solution We are asked to determine the approximate temperature from which a 45 wt% Pb-55 wt% Mg alloy was quenched, given the mass fractions of α and Mg2Pb phases. We can write a lever-rule expression for the mass fraction of the α phase as Wα = 0.65 = CMg2Pb − C0 CMg2Pb − Cα The value of C0 is stated as 45 wt% Pb-55 wt% Mg, and CMg2Pb is 81 wt% Pb-19 wt% Mg, which is independent of temperature (Figure 9.20); thus, 0.65 = 81 − 45 81 − Cα which yields Cα = 25.6 wt% Pb The temperature at which the α–(α + Mg2Pb) phase boundary (Figure 9.20) has a value of 25.6 wt% Pb is about 360°C (680°F).
- 482. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Development of Microstructure in Eutectic Alloys 9.28 Briefly explain why, upon solidification, an alloy of eutectic composition forms a microstructure consisting of alternating layers of the two solid phases. Solution Upon solidification, an alloy of eutectic composition forms a microstructure consisting of alternating layers of the two solid phases because during the solidification atomic diffusion must occur, and with this layered configuration the diffusion path length for the atoms is a minimum.
- 483. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.29 What is the difference between a phase and a microconstituent? Solution A “phase” is a homogeneous portion of the system having uniform physical and chemical characteristics, whereas a “microconstituent” is an identifiable element of the microstructure (that may consist of more than one phase).
- 484. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.30 Is it possible to have a copper-silver alloy in which the mass fractions of primary β and total β are 0.68 and 0.925, respectively, at 775°C (1425°F)? Why or why not? Solution This problem asks if it is possible to have a Cu-Ag alloy for which the mass fractions of primary β and total β are 0.68 and 0.925, respectively at 775°C. In order to make this determination we need to set up the appropriate lever rule expression for each of these quantities. From Figure 9.7 and at 775°C, Cα = 8.0 wt% Ag, Cβ = 91.2 wt% Ag, and Ceutectic = 71.9 wt% Ag. For primary β Wβ’ = C0 − Ceutectic Cβ Ê− Ceutectic = C0 − 71.9 91.2 − 71.9 = 0.68 Solving for C0 gives C0 = 85 wt% Ag. Now the analogous expression for total β Wβ = C0 − Cα Cβ − Cα = C0 − 8.0 91.2 − 8.0 = 0.925 And this value of C0 is 85 wt% Ag. Therefore, since these two C0 values are the same (85 wt% Ag), this alloy is possible.
- 485. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.31 For 6.70 kg of a magnesium-lead alloy, is it possible to have the masses of primary α and total α of 4.23 kg and 6.00 kg, respectively, at 460°C (860°F)? Why or why not? Solution This problem asks if it is possible to have a Mg-Pb alloy for which the masses of primary α and total α are 4.23 kg and 6.00 kg, respectively in 6.70 kg total of the alloy at 460°C. In order to make this determination we first need to convert these masses to mass fractions. Thus, Wα' = 4.23 kg 6.70 kg = 0.631 Wα = 6.00 kg 6.70 kg = 0.896 Next it is necessary to set up the appropriate lever rule expression for each of these quantities. From Figure 9.20 and at 460°C, Cα = 41 wt% Pb, CMg2 Pb = 81 wt% Pb, and Ceutectic = 66 wt% Pb For primary α Wα' = Ceutectic − C0 Ceutectic − Cα = 66 − C0 66 − 41 = 0.631 And solving for C0 gives C0 = 50.2 wt% Pb. Now the analogous expression for total α Wα = CMg2Pb − C0 CMg2Pb − Cα = 81 − C0 81 − 41 = 0.896 And this value of C0 is 45.2 wt% Pb. Therefore, since these two C0 values are different, this alloy is not possible.
- 486. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.32 For a copper-silver alloy of composition 25 wt% Ag-75 wt% Cu and at 775°C (1425°F) do the following: (a) Determine the mass fractions of α and β phases. (b) Determine the mass fractions of primary α and eutectic microconstituents. (c) Determine the mass fraction of eutectic α. Solution (a) This portion of the problem asks that we determine the mass fractions of α and β phases for an 25 wt% Ag-75 wt% Cu alloy (at 775°C). In order to do this it is necessary to employ the lever rule using a tie line that extends entirely across the α + β phase field. From Figure 9.7 and at 775°C, Cα = 8.0 wt% Ag, Cβ = 91.2 wt% Ag, and Ceutectic = 71.9 wt% Sn. Therefore, the two lever-rule expressions are as follows: Wα = Cβ − C0 Cβ − Cα = 91.2 − 25 91.2 − 8.0 = 0.796 Wβ = C0 − Cα Cβ − Cα = 25 − 8.0 91.2 − 8.0 = 0.204 (b) Now it is necessary to determine the mass fractions of primary α and eutectic microconstituents for this same alloy. This requires us to utilize the lever rule and a tie line that extends from the maximum solubility of Ag in the α phase at 775°C (i.e., 8.0 wt% Ag) to the eutectic composition (71.9 wt% Ag). Thus Wα' = Ceutectic Ê− C0 Ceutectic Ê− Cα = 71.9 − 25 71.9 − 8.0 = 0.734 We = C0 − Cα Ceutectic − Cα = 25 − 8.0 71.9 − 8.0 = 0.266 (c) And, finally, we are asked to compute the mass fraction of eutectic α, Weα. This quantity is simply the difference between the mass fractions of total α and primary α as Weα = Wα – Wα' = 0.796 – 0.734 = 0.062
- 487. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.33 The microstructure of a lead-tin alloy at 180°C (355°F) consists of primary β and eutectic structures. If the mass fractions of these two microconstituents are 0.57 and 0.43, respectively, determine the composition of the alloy. Solution Since there is a primary β microconstituent present, then we know that the alloy composition, C0 is between 61.9 and 97.8 wt% Sn (Figure 9.8). Furthermore, this figure also indicates that Cβ = 97.8 wt% Sn and Ceutectic = 61.9 wt% Sn. Applying the appropriate lever rule expression for Wβ' Wβ' = C0 − Ceutectic Cβ Ê− Ceutectic = C0 − 61.9 97.8 − 61.9 = 0.57 and solving for C0 yields C0 = 82.4 wt% Sn.
- 488. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.34 Consider the hypothetical eutectic phase diagram for metals A and B, which is similar to that for the lead-tin system, Figure 9.8. Assume that (1) α and β phases exist at the A and B extremities of the phase diagram, respectively; (2) the eutectic composition is 47 wt% B-53 wt% A; and (3) the composition of the β phase at the eutectic temperature is 92.6 wt% B-7.4 wt% A. Determine the composition of an alloy that will yield primary α and total α mass fractions of 0.356 and 0.693, respectively. Solution We are given a hypothetical eutectic phase diagram for which Ceutectic = 47 wt% B, Cβ = 92.6 wt% B at the eutectic temperature, and also that Wα' = 0.356 and Wα = 0.693; from this we are asked to determine the composition of the alloy. Let us write lever rule expressions for Wα' and Wα Wα = Cβ Ê− C0 Cβ − Cα = 92.6 − C0 92.6 − Cα = 0.693 Wα' = Ceutectic Ê− C0 Ceutectic Ê− Cα = 47 − C0 47 − Cα = 0.356 Thus, we have two simultaneous equations with C0 and Cα as unknowns. Solving them for C0 gives C0 = 32.6 wt% B.
- 489. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.35 For an 85 wt% Pb-15 wt% Mg alloy, make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: 600°C (1110°F), 500°C (930°F), 270°C (520°F), and 200°C (390°F). Label all phases and indicate their approximate compositions. Solution The illustration below is the Mg-Pb phase diagram (Figure 9.20). A vertical line at a composition of 85 wt% Pb-15 wt% Mg has been drawn, and, in addition, horizontal arrows at the four temperatures called for in the problem statement (i.e., 600°C, 500°C, 270°C, and 200°C). On the basis of the locations of the four temperature-composition points, schematic sketches of the four respective microstructures along with phase compositions are represented as follows:
- 490. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
- 491. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.36 For a 68 wt% Zn-32 wt% Cu alloy, make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: 1000°C (1830°F), 760°C (1400°F), 600°C (1110°F), and 400°C (750°F). Label all phases and indicate their approximate compositions. Solution The illustration below is the Cu-Zn phase diagram (Figure 9.19). A vertical line at a composition of 68 wt% Zn-32 wt% Cu has been drawn, and, in addition, horizontal arrows at the four temperatures called for in the problem statement (i.e., 1000°C, 760°C, 600°C, and 400°C). On the basis of the locations of the four temperature-composition points, schematic sketches of the four respective microstructures along with phase compositions are represented as follows:
- 492. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
- 493. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.37 For a 30 wt% Zn-70 wt% Cu alloy, make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: 1100°C (2010°F), 950°C (1740°F), 900°C (1650°F), and 700°C (1290°F). Label all phases and indicate their approximate compositions. Solution The illustration below is the Cu-Zn phase diagram (Figure 9.19). A vertical line at a composition of 30 wt% Zn-70 wt% Cu has been drawn, and, in addition, horizontal arrows at the four temperatures called for in the problem statement (i.e., 1100°C, 950°C, 900°C, and 700°C). On the basis of the locations of the four temperature-composition points, schematic sketches of the four respective microstructures along with phase compositions are represented as follows:
- 494. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
- 495. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.38 On the basis of the photomicrograph (i.e., the relative amounts of the microconstituents) for the lead– tin alloy shown in Figure 9.17 and the Pb–Sn phase diagram (Figure 9.8), estimate the composition of the alloy, and then compare this estimate with the composition given in the figure legend of Figure 9.17. Make the following assumptions: (1) the area fraction of each phase and microconstituent in the photomicrograph is equal to its volume fraction; (2) the densities of the α and β phases as well as the eutectic structure are 11.2, 7.3, and 8.7 g/cm3 , respectively; and (3) this photomicrograph represents the equilibrium microstructure at 180°C (355°F). Solution Below is shown the micrograph of the Pb-Sn alloy, Figure 9.17: Primary α and eutectic microconstituents are present in the photomicrograph, and it is given that their densities are 11.2 and 8.7 g/cm3, respectively. Below is shown a square grid network onto which is superimposed outlines of the primary α phase areas.
- 496. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The area fraction of this primary α phase may be determined by counting squares. There are a total of 644 squares, and of these, approximately 104 lie within the primary α phase particles. Thus, the area fraction of primary α is 104/644 = 0.16, which is also assumed to be the volume fraction. We now want to convert the volume fractions into mass fractions in order to employ the lever rule to the Pb-Sn phase diagram. To do this, it is necessary to utilize Equations 9.7a and 9.7b as follows: Wα' = Vα' ρα' Vα' ρα' + Veutectic ρeutectic = (0.16)(11.2 g /cm3) (0.16)(11.2 g /cm3) + (0.84)(8.7 g /cm3) = 0.197 Weutectic = Veutectic ρeutectic VαÕραÕ+ Veutectic ρeutectic = (0.84)(8.7 g/cm3) (0.16)(11.2 g/cm3) + (0.84)(8.7 g/cm3) = 0.803 From Figure 9.8, we want to use the lever rule and a tie-line that extends from the eutectic composition (61.9 wt% Sn) to the α–(α + β) phase boundary at 180°C (about 18.3 wt% Sn). Accordingly Wα' = 0.197 = 61.9 − C0 61.9 − 18.3 wherein C0 is the alloy composition (in wt% Sn). Solving for C0 yields C0 = 53.3 wt% Sn. This value is in good agreement with the actual composition—viz. 50 wt% Sn.
- 497. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.39 The room-temperature tensile strengths of pure lead and pure tin are 16.8 MPa and 14.5 MPa, respectively. (a) Make a schematic graph of the room-temperature tensile strength versus composition for all compositions between pure lead and pure tin. (Hint: you may want to consult Sections 9.10 and 9.11, as well as Equation 9.24 in Problem 9.64.) (b) On this same graph schematically plot tensile strength versus composition at 150°C. (c) Explain the shapes of these two curves, as well as any differences between them. Solution The (a) and (b) portions of the problem ask that we make schematic plots on the same graph for the tensile strength versus composition for lead-tin alloys at both room temperature and 150°C; such a graph is shown below. (c) Upon consultation of the Pb-Sn phase diagram (Figure 9.8) we note that, at room temperature (20°C), about 1.5 wt% of Sn is soluble in Pb (within the α-phase region at the left extremity of the phase diagram). Similarly, only about 1 wt% of Pb is soluble in Sn (within the β-phase region at the left extremity). Thus, there will a solid-solution strengthening effect on both ends of the phase diagram—strength increases slightly with additions of Sn to Pb [in the α phase region (left-hand side)] and with additions of Pb to Sn [in the β phase region (right-hand side)]; these effects are noted in the above figure. This figure also shows that the tensile strength of pure lead is greater than pure tin, which is in agreement with tensile strength values provided in the problem statement. In addition, at room temperature, for compositions between about 1.5 wt% Sn and 99 wt% Sn, both α and β phase will coexist, (Figure 9.8), Furthermore, for compositions within this range, tensile strength will depend (approximately) on the tensile strengths of each of the α and β phases as well as their phase fractions in a manner described by Equation 9.24 for the elastic modulus (Problem 9.64). That is, for this problem
- 498. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (TS)alloy ≅ (TS)αVα + (TS)βVβ in which TS and V denote tensile strength and volume fraction, respectively, and the subscripts represent the alloy/phases. Also, mass fractions of the α and β phases change linearly with changing composition (according to the lever rule). Furthermore, although there is some disparity between the densities of Pb and Sn (11.35 versus 7.27 g/cm3), weight and volume fractions of the α and β phases will also be similar (see Equation 9.6). At 150°C, the curve will be shifted to significantly lower tensile strengths inasmuch as tensile strength diminishes with increasing temperature (Section 6.6, Figure 6.14). In addition, according to Figure 9.8, solubility limits for both α and β phases increase—for the α phase from 1.5 to 10 wt% Sn, and for the β phase from 1 to about 2 wt% Pb. Thus, the compositional ranges over which solid-solution strengthening occurs increase somewhat from the room-temperature ranges; these effects are also noted on the 150°C curve above. Furthermore, at 150°C, it would be expected that the tensile strength of lead will be greater than that of tin; and for compositions over which both α and β phases coexist, strength will decrease approximately linearly with increasing Sn content.
- 499. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Equilibrium Diagrams Having Intermediate Phases or Compounds 9.40 Two intermetallic compounds, AB and AB2, exist for elements A and B. If the compositions for AB and AB2 are 34.3 wt% A–65.7 wt% B and 20.7 wt% A–79.3 wt% B, respectively, and element A is potassium, identify element B. Solution This problem gives us the compositions in weight percent for the two intermetallic compounds AB and AB2, and then asks us to identify element B if element A is potassium. Probably the easiest way to solve this problem is to first compute the ratio of the atomic weights of these two elements using Equation 4.6a; then, since we know the atomic weight of potassium (39.10 g/mol, per inside the front cover), it is possible to determine the atomic weight of element B, from which an identification may be made. First of all, consider the AB intermetallic compound; inasmuch as it contains the same numbers of A and B atoms, its composition in atomic percent is 50 at% A-50 at% B. Equation 4.6a may be written in the form: CB ' = CB AA CA AB + CB AA × 100 where AA and AB are the atomic weights for elements A and B, and CA and CB are their compositions in weight percent. For this AB compound, and making the appropriate substitutions in the above equation leads to 50 at% B = (65.7 wt% B)(AA) (34.3 wt% A)(AB) + (65.7 wt% B)(AA) × 100 Now, solving this expression yields, AB = 1.916 AA Since potassium is element A and it has an atomic weight of 39.10 g/mol, the atomic weight of element B is just AB = (1.916)(39.10 g/mol) = 74.92 g/mol Upon consultation of the period table of the elements (Figure 2.6) we note the element that has an atomic weight closest to this value is arsenic (74.92 g/mol). Therefore, element B is arsenic, and the two intermetallic compounds are KAs and KAs2.
- 500. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Congruent Phase Transformations Eutectoid and Peritectic Reactions 9.41 What is the principal difference between congruent and incongruent phase transformations? Solution The principal difference between congruent and incongruent phase transformations is that for congruent no compositional changes occur with any of the phases that are involved in the transformation. For incongruent there will be compositional alterations of the phases.
- 501. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.42 Figure 9.36 is the aluminum-neodymium phase diagram, for which only single-phase regions are labeled. Specify temperature-composition points at which all eutectics, eutectoids, peritectics, and congruent phase transformations occur. Also, for each, write the reaction upon cooling. Solution Below is shown the aluminum-neodymium phase diagram (Figure 9.36). There are two eutectics on this phase diagram. One exists at 12 wt% Nd-88 wt% Al and 632°C. The reaction upon cooling is L → Al + Al11Nd3 The other eutectic exists at about 97 wt% Nd-3 wt% Al and 635°C. This reaction upon cooling is L → AlNd3 + Nd There are four peritectics. One exists at 59 wt% Nd-41 wt% Al and 1235°C. Its reaction upon cooling is as follows:
- 502. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. L + Al2Nd → Al11Nd3 The second peritectic exists at 84 wt% Nd-16 wt% Al and 940°C. This reaction upon cooling is L + Al2Nd → AlNd The third peritectic exists at 91 wt% Nd-9 wt% Al and 795°C. This reaction upon cooling is L + AlNd → AlNd2 The fourth peritectic exists at 94 wt% Nd-6 wt% Al and 675°C. This reaction upon cooling is L + AlNd2 → AlNd3 There is one congruent melting point at about 73 wt% Nd-27 wt% Al and 1460°C. Its reaction upon cooling is L → Al2Nd No eutectoids are present.
- 503. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.43 Figure 9.37 is a portion of the titanium-copper phase diagram for which only single-phase regions are labeled. Specify all temperature-composition points at which eutectics, eutectoids, peritectics, and congruent phase transformations occur. Also, for each, write the reaction upon cooling. Solution Below is shown the titanium-copper phase diagram (Figure 9.37). There is one eutectic on this phase diagram, which exists at about 51 wt% Cu-49 wt% Ti and 960°C. Its reaction upon cooling is L → Ti2Cu + TiCu There is one eutectoid for this system. It exists at about 7.5 wt% Cu-92.5 wt% Ti and 790°C. This reaction upon cooling is β → α + Ti2Cu There is one peritectic on this phase diagram. It exists at about 40 wt% Cu-60 wt% Ti and 1005°C. The reaction upon cooling is
- 504. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. β + L → Ti2Cu There is a single congruent melting point that exists at about 57.5 wt% Cu-42.5 wt% Ti and 982°C. The reaction upon cooling is L → TiCu
- 505. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.44 Construct the hypothetical phase diagram for metals A and B between temperatures of 600°C and 1000°C given the following information: ● The melting temperature of metal A is 940°C. ● The solubility of B in A is negligible at all temperatures. ● The melting temperature of metal B is 830°C. ● The maximum solubility of A in B is 12 wt% A, which occurs at 700°C. ● At 600°C, the solubility of A in B is 8 wt% A. ● One eutectic occurs at 700°C and 75 wt% B–25 wt% A. ● A second eutectic occurs at 730°C and 60 wt% B–40 wt% A. ● A third eutectic occurs at 755°C and 40 wt% B–60 wt% A. ● One congruent melting point occurs at 780°C and 51 wt% B–49 wt% A. ● A second congruent melting point occurs at 755°C and 67 wt% B–33 wt% A. ● The intermetallic compound AB exists at 51 wt% B–49 wt% A. ● The intermetallic compound AB2 exists at 67 wt% B–33 wt% A. Solution Below is shown the phase diagram for these two A and B metals.
- 506. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The Gibbs Phase Rule 9.45 In Figure 9.38 is shown the pressure–temperature phase diagram for H2O. Apply the Gibbs phase rule at points A, B, and C; that is, specify the number of degrees of freedom at each of the points—that is, the number of externally controllable variables that need be specified to completely define the system. Solution We are asked to specify the value of F for Gibbs phase rule at points A, B, and C on the pressure- temperature diagram for H2O, Figure 9.38, which is shown below. Gibbs phase rule in general form is P + F = C + N For this system, the number of components, C, is 1, whereas N, the number of noncompositional variables, is 2--viz. temperature and pressure. Thus, the phase rule now becomes P + F = 1 + 2 = 3 Or F = 3 – P where P is the number of phases present at equilibrium.
- 507. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. At point A, three phases are present (viz. ice I, ice III, and liquid) and P = 3; thus, the number of degrees of freedom is zero since F = 3 – P = 3 – 3 = 0 Thus, point A is an invariant point (in this case a triple point), and we have no choice in the selection of externally controllable variables in order to define the system. At point B on the figure, only a single (vapor) phase is present (i.e., P = 1), or F = 3 – P = 3 – 1 = 2 which means that specification of both temperature and pressure are necessary to define the system. And, finally, at point C which is on the phase boundary between liquid and ice I phases, two phases are in equilibrium (P = 2); hence F = 3 – P = 3 – 2 = 1 Or that we need to specify the value of either temperature or pressure, which determines the value of the other parameter (pressure or temperature).
- 508. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The Iron-Iron Carbide (Fe-Fe3C) Phase Diagram Development of Microstructure in Iron-Carbon Alloys 9.46 Compute the mass fractions of α ferrite and cementite in pearlite. Solution This problem asks that we compute the mass fractions of α ferrite and cementite in pearlite. The lever-rule expression for ferrite is Wα = CFe3C − C0 CFe3C − Cα and, since CFe3C = 6.70 wt% C, C0 = 0.76 wt% C, and Cα = 0.022 wt% C Wα = 6.70 − 0.76 6.70 − 0.022 = 0.89 Similarly, for cementite WFe3C = C0 − Cα CFe3C − Cα = 0.76 − 0.022 6.70 − 0.022 = 0.11
- 509. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.47 (a) What is the distinction between hypoeutectoid and hypereutectoid steels? (b) In a hypoeutectoid steel, both eutectoid and proeutectoid ferrite exist. Explain the difference between them. What will be the carbon concentration in each? Solution (a) A “hypoeutectoid” steel has a carbon concentration less than the eutectoid; on the other hand, a “hypereutectoid” steel has a carbon content greater than the eutectoid. (b) For a hypoeutectoid steel, the proeutectoid ferrite is a microconstituent that formed above the eutectoid temperature. The eutectoid ferrite is one of the constituents of pearlite that formed at a temperature below the eutectoid. The carbon concentration for both ferrites is 0.022 wt% C.
- 510. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.48 What is the carbon concentration of an iron–carbon alloy for which the fraction of total ferrite is 0.94? Solution This problem asks that we compute the carbon concentration of an iron-carbon alloy for which the fraction of total ferrite is 0.94. Application of the lever rule (of the form of Equation 9.12) yields Wα = 0.94 = CFe3C − C0 ' CFe3C − Cα = 6.70 − C0 ' 6.70 − 0.022 and solving for C0 ' C0 ' = 0.42 wt% C
- 511. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.49 What is the proeutectoid phase for an iron–carbon alloy in which the mass fractions of total ferrite and total cementite are 0.92 and 0.08, respectively? Why? Solution In this problem we are given values of Wα and WFe3C (0.92 and 0.08, respectively) for an iron-carbon alloy and then are asked to specify the proeutectoid phase. Employment of the lever rule for total α leads to Wα = 0.92 = CFe3C − C0 CFe3C − Cα = 6.70 − C0 6.70 − 0.022 Now, solving for C0, the alloy composition, leads to C0 = 0.56 wt% C. Therefore, the proeutectoid phase is α- ferrite since C0 is less than 0.76 wt% C.
- 512. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.50 Consider 1.0 kg of austenite containing 1.15 wt% C, cooled to below 727°C (1341°F). (a) What is the proeutectoid phase? (b) How many kilograms each of total ferrite and cementite form? (c) How many kilograms each of pearlite and the proeutectoid phase form? (d) Schematically sketch and label the resulting microstructure. Solution (a) The proeutectoid phase will be Fe3C since 1.15 wt% C is greater than the eutectoid composition (0.76 wt% C). (b) For this portion of the problem, we are asked to determine how much total ferrite and cementite form. Application of the appropriate lever rule expression yields Wα = CFe3C − C0 CFe3C − Cα = 6.70 − 1.15 6.70 − 0.022 = 0.83 which, when multiplied by the total mass of the alloy (1.0 kg), gives 0.83 kg of total ferrite. Similarly, for total cementite, WFe3C = C0 − Cα CFe3C − Cα = 1.15 − 0.022 6.70 − 0.022 = 0.17 And the mass of total cementite that forms is (0.17)(1.0 kg) = 0.17 kg. (c) Now we are asked to calculate how much pearlite and the proeutectoid phase (cementite) form. Applying Equation 9.22, in which C1 ' = 1.15 wt% C Wp = 6.70 − C 1 ' 6.70 − 0.76 = 6.70 − 1.15 6.70 − 0.76 = 0.93 which corresponds to a mass of 0.93 kg. Likewise, from Equation 9.23 WFe3C' = C1 ' − 0.76 5.94 = 1.15 − 0.76 5.94 = 0.07 which is equivalent to 0.07 kg of the total 1.0 kg mass. (d) Schematically, the microstructure would appear as:
- 513. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
- 514. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.51 Consider 2.5 kg of austenite containing 0.65 wt% C, cooled to below 727°C (1341°F). (a) What is the proeutectoid phase? (b) How many kilograms each of total ferrite and cementite form? (c) How many kilograms each of pearlite and the proeutectoid phase form? (d) Schematically sketch and label the resulting microstructure. Solution (a) Ferrite is the proeutectoid phase since 0.65 wt% C is less than 0.76 wt% C. (b) For this portion of the problem, we are asked to determine how much total ferrite and cementite form. For ferrite, application of the appropriate lever rule expression yields Wα = CFe3C − C0 CFe3C − Cα = 6.70 − 0.65 6.70 − 0.022 = 0.91 which corresponds to (0.91)(2.5 kg) = 2.27 kg of total ferrite. Similarly, for total cementite, WFe3C = C0 − Cα CFe3C − Cα = 0.65 − 0.022 6.70 − 0.022 = 0.09 Or (0.09)(2.5 kg) = 0.23 kg of total cementite form. (c) Now consider the amounts of pearlite and proeutectoid ferrite. Using Equation 9.20 Wp = C 0 ' − 0.022 0.74 = 0.65 − 0.022 0.74 = 0.85 This corresponds to (0.85)(2.5 kg) = 2.12 kg of pearlite. Also, from Equation 9.21, Wα' = 0.76 − 0.65 0.74 = 0.15 Or, there are (0.15)(2.5 kg) = 0.38 kg of proeutectoid ferrite. (d) Schematically, the microstructure would appear as:
- 515. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
- 516. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.52 Compute the mass fractions of proeutectoid ferrite and pearlite that form in an iron–carbon alloy containing 0.25 wt% C. Solution The mass fractions of proeutectoid ferrite and pearlite that form in a 0.25 wt% C iron-carbon alloy are considered in this problem. From Equation 9.20 Wp = C0 ' − 0.022 0.74 = 0.25 − 0.022 0.74 = 0.31 And, from Equation 9.21 (for proeutectoid ferrite) Wα' = 0.76 − C0 ' 0.74 = 0.76 − 0.25 0.74 = 0.69
- 517. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.53 The microstructure of an iron–carbon alloy consists of proeutectoid ferrite and pearlite; the mass fractions of these two microconstituents are 0.286 and 0.714, respectively. Determine the concentration of carbon in this alloy. Solution This problem asks that we determine the carbon concentration in an iron-carbon alloy, given the mass fractions of proeutectoid ferrite and pearlite. From Equation 9.20 Wp = 0.714 = C0 ' − 0.022 0.74 which yields C0 ' = 0.55 wt% C.
- 518. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.54 The mass fractions of total ferrite and total cementite in an iron-carbon alloy are 0.88 and 0.12, respectively. Is this a hypoeutectoid or hypereutectoid alloy? Why? Solution In this problem we are given values of Wα and WFe3C for an iron-carbon alloy (0.88 and 0.12, respectively), and then are asked to specify whether the alloy is hypoeutectoid or hypereutectoid. Employment of the lever rule for total α leads to Wα = 0.88 = CFe3C − C0 CFe3C − Cα = 6.70 − C0 6.70 − 0.022 Now, solving for C0, the alloy composition, leads to C0 = 0.82 wt% C. Therefore, the alloy is hypereutectoid since C0 is greater than 0.76 wt% C.
- 519. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.55 The microstructure of an iron-carbon alloy consists of proeutectoid ferrite and pearlite; the mass fractions of these microconstituents are 0.20 and 0.80, respectively. Determine the concentration of carbon in this alloy. Solution We are asked in this problem to determine the concentration of carbon in an alloy for which Wα' = 0.20 and Wp = 0.80. If we let C0 ' equal the carbon concentration in the alloy, employment of the appropriate lever rule expression, Equation 9.20, leads to Wp = C0 ' − 0.022 0.74 = 0.80 Solving for C0 ' yields C0 ' = 0.61 wt% C.
- 520. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.56 Consider 2.0 kg of a 99.6 wt% Fe–0.4 wt% C alloy that is cooled to a temperature just below the eutectoid. (a) How many kilograms of proeutectoid ferrite form? (b) How many kilograms of eutectoid ferrite form? (c) How many kilograms of cementite form? Solution In this problem we are asked to consider 2.0 kg of a 99.6 wt% Fe-0.4 wt% C alloy that is cooled to a temperature below the eutectoid. (a) Equation 9.21 must be used in computing the amount of proeutectoid ferrite that forms. Thus, Wα' = 0.76 − C0 ' 0.74 = 0.76 − 0.40 0.74 = 0.49 Or, (0.49)(2.0 kg) = 0.98 kg of proeutectoid ferrite forms. (b) In order to determine the amount of eutectoid ferrite, it first becomes necessary to compute the amount of total ferrite using the lever rule applied entirely across the α + Fe3 C phase field, as Wα = CFe3C − C0 Õ CFe3C − Cα = 6.70 − 0.40 6.70 − 0.022 = 0.94 which corresponds to (0.94)(2.0 kg) = 1.88 kg. Now, the amount of eutectoid ferrite is just the difference between total and proeutectoid ferrites, or 1.88 kg – 0.98 kg = 0.90 kg (c) With regard to the amount of cementite that forms, again application of the lever rule across the entirety of the α + Fe3C phase field, leads to WFe3C = C0 Õ − Cα CFe3C − Cα = 0.40 − 0.022 6.70 − 0.022 = 0.057 which amounts to (0.057)(2.0 kg) = 0.114 kg cementite in the alloy.
- 521. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.57 Compute the maximum mass fraction of proeutectoid cementite possible for a hypereutectoid iron– carbon alloy. Solution This problem asks that we compute the maximum mass fraction of proeutectoid cementite possible for a hypereutectoid iron-carbon alloy. This requires that we utilize Equation 9.23 with C1 ' = 2.14 wt% C, the maximum solubility of carbon in austenite. Thus, WFe3C' = C1 ' − 0.76 5.94 = 2.14 − 0.76 5.94 = 0.232
- 522. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.58 Is it possible to have an iron-carbon alloy for which the mass fractions of total ferrite and proeutectoid cementite are 0.846 and 0.049, respectively? Why or why not? Solution This problem asks if it is possible to have an iron-carbon alloy for which Wα = 0.846 and WFe3 ′C = 0.049. In order to make this determination, it is necessary to set up lever rule expressions for these two mass fractions in terms of the alloy composition, then to solve for the alloy composition of each; if both alloy composition values are equal, then such an alloy is possible. The expression for the mass fraction of total ferrite is Wα = CFe3C − C0 CFe3C − Cα = 6.70 − C0 6.70 − 0.022 = 0.846 Solving for this C0 yields C0 = 1.05 wt% C. Now for WFe3 ′C we utilize Equation 9.23 as WFe3C' = C1 ' − 0.76 5.94 = 0.049 This expression leads to C1 ' = 1.05 wt% C. And, since C0 = C1 ' , this alloy is possible.
- 523. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.59 Is it possible to have an iron-carbon alloy for which the mass fractions of total cementite and pearlite are 0.039 and 0.417, respectively? Why or why not? Solution This problem asks if it is possible to have an iron-carbon alloy for which WFe3C = 0.039 and Wp = 0.417. In order to make this determination, it is necessary to set up lever rule expressions for these two mass fractions in terms of the alloy composition, then to solve for the alloy composition of each; if both alloy composition values are equal, then such an alloy is possible. The expression for the mass fraction of total cementite is WFe3C = C0 − Cα CFe3C − Cα = C0 − 0.022 6.70 − 0.022 = 0.039 Solving for this C0 yields C0 = 0.28 wt% C. Therefore, this alloy is hypoeutectoid since C0 is less than the eutectoid composition (0.76 wt% ). Thus, it is necessary to use Equation 9.20 for Wp as Wp = C 0 ' − 0.022 0.74 = 0.417 This expression leads to C 0 ' = 0.33 wt% C. Since C0 and C 0 ' are different, this alloy is not possible.
- 524. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.60 Compute the mass fraction of eutectoid ferrite in an iron-carbon alloy that contains 0.43 wt% C. Solution In order to solve this problem it is necessary to compute mass fractions of total and proeutectoid ferrites, and then to subtract the latter from the former. To calculate the mass fraction of total ferrite, it is necessary to use the lever rule and a tie line that extends across the entire α + Fe3C phase field as Wα = CFe3C − C0 CFe3C − Cα = 6.70 − 0.43 6.70 − 0.022 = 0.939 Now, for the mass fraction of proeutectoid ferrite we use Equation 9.21 as Wα' = 0.76 − C0 ' − 0.74 = 0.76 − 0.43 0.74 = 0.446 And, finally, the mass fraction of eutectoid ferrite Wα'' is just Wα'' = Wα – Wα' = 0.939 –0.446 = 0.493
- 525. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.61 The mass fraction of eutectoid cementite in an iron-carbon alloy is 0.104. On the basis of this information, is it possible to determine the composition of the alloy? If so, what is its composition? If this is not possible, explain why. Solution This problem asks whether or not it is possible to determine the composition of an iron-carbon alloy for which the mass fraction of eutectoid cementite is 0.104; and if so, to calculate the composition. Yes, it is possible to determine the alloy composition; and, in fact, there are two possible answers. For the first, the eutectoid cementite exists in addition to proeutectoid cementite. For this case the mass fraction of eutectoid cementite (WFe3C'') is just the difference between total cementite and proeutectoid cementite mass fractions; that is WFe3C'' = WFe3C – WFe3C' Now, it is possible to write expressions for WFe3C (of the form of Equation 9.12) and WFe3C' (Equation 9.23) in terms of C0, the alloy composition. Thus, WFe3C" = C0 − Cα CFe3C − Cα − C0 − 0.76 5.94 = C0 − 0.022 6.70 − 0.022 − C0 − 0.76 5.94 = 0.104 And, solving for C0 yields C0 = 1.11 wt% C. For the second possibility, we have a hypoeutectoid alloy wherein all of the cementite is eutectoid cementite. Thus, it is necessary to set up a lever rule expression wherein the mass fraction of total cementite is 0.104. Therefore, WFe3C = C0 − Cα CFe3C − Cα = C0 − 0.022 6.70 − 0.022 = 0.104 And, solving for C0 yields C0 = 0.72 wt% C.
- 526. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.62 The mass fraction of eutectoid ferrite in an iron-carbon alloy is 0.82. On the basis of this information, is it possible to determine the composition of the alloy? If so, what is its composition? If this is not possible, explain why. Solution This problem asks whether or not it is possible to determine the composition of an iron-carbon alloy for which the mass fraction of eutectoid ferrite is 0.82; and if so, to calculate the composition. Yes, it is possible to determine the alloy composition; and, in fact, there are two possible answers. For the first, the eutectoid ferrite exists in addition to proeutectoid ferrite. For this case the mass fraction of eutectoid ferrite (Wα'') is just the difference between total ferrite and proeutectoid ferrite mass fractions; that is Wα'' = Wα – Wα' Now, it is possible to write expressions for Wα (of the form of Equation 9.12) and Wα' (Equation 9.21) in terms of C0, the alloy composition. Thus, Wα" = CFe3C − C0 CFe3C − Cα − 0.76 − C0 0.74 = 6.70 − C0 6.70 − 0.022 − 0.76 − C0 0.74 = 0.82 And, solving for C0 yields C0 = 0.70 wt% C. For the second possibility, we have a hypereutectoid alloy wherein all of the ferrite is eutectoid ferrite. Thus, it is necessary to set up a lever rule expression wherein the mass fraction of total ferrite is 0.82. Therefore, Wα = CFe3C − C0 CFe3C − Cα = 6.70 − C0 6.70 − 0.022 = 0.82 And, solving for C0 yields C0 = 1.22 wt% C.
- 527. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.63 For an iron-carbon alloy of composition 5 wt% C-95 wt% Fe, make schematic sketches of the microstructure that would be observed for conditions of very slow cooling at the following temperatures: 1175°C (2150°F), 1145°C (2095°F), and 700°C (1290°F). Label the phases and indicate their compositions (approximate). Solution Below is shown the Fe-Fe3C phase diagram (Figure 9.24). A vertical line at a composition of 5 wt% C-95 wt% Fe has been drawn, and, in addition, horizontal arrows at the three temperatures called for in the problem statement (i.e., 1175°C, 1145°C, and 700°C). On the basis of the locations of the three temperature-composition points, schematic sketches of the respective microstructures along with phase compositions are represented as follows:
- 528. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
- 529. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.64 Often, the properties of multiphase alloys may be approximated by the relationship E (alloy) = EαVα + EβVβ (9.24) where E represents a specific property (modulus of elasticity, hardness, etc.), and V is the volume fraction. The subscripts α and β denote the existing phases or microconstituents. Employ the relationship above to determine the approximate Brinell hardness of a 99.80 wt% Fe–0.20 wt% C alloy. Assume Brinell hardnesses of 80 and 280 for ferrite and pearlite, respectively, and that volume fractions may be approximated by mass fractions. Solution This problem asks that we determine the approximate Brinell hardness of a 99.80 wt% Fe-0.20 wt% C alloy, using a relationship similar to Equation 9.24. First, we compute the mass fractions of pearlite and proeutectoid ferrite using Equations 9.20 and 9.21, as Wp = C 0 ' − 0.022 0.74 = 0.20 − 0.022 0.74 = 0.24 Wα' = 0.76 − C 0 ' 0.74 = 0.76 − 0.20 0.74 = 0.76 Now, we compute the Brinell hardness of the alloy using a modified form of Equation 9.24 as HBalloy = HBα'Wα' + HBpWp = (80)(0.76) + (280)(0.24) = 128
- 530. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The Influence of Other Alloying Elements 9.65 A steel alloy contains 97.5 wt% Fe, 2.0 wt% Mo, and 0.5 wt% C. (a) What is the eutectoid temperature of this alloy? (b) What is the eutectoid composition? (c) What is the proeutectoid phase? Assume that there are no changes in the positions of other phase boundaries with the addition of Mo. Solution (a) From Figure 9.34, the eutectoid temperature for 2.0 wt% Mo is approximately 850°C. (b) From Figure 9.35, the eutectoid composition is approximately 0.22 wt% C. (c) Since the carbon concentration of the alloy (0.5 wt%) is greater than the eutectoid (0.22 wt% C), cementite is the proeutectoid phase.
- 531. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 9.66 A steel alloy is known to contain 93.8 wt% Fe, 6.0 wt% Ni, and 0.2 wt% C. (a) What is the approximate eutectoid temperature of this alloy? (b) What is the proeutectoid phase when this alloy is cooled to a temperature just below the eutectoid? (c) Compute the relative amounts of the proeutectoid phase and pearlite. Assume that there are no alterations in the positions of other phase boundaries with the addition of Ni. Solution (a) From Figure 9.34, the eutectoid temperature for 6.0 wt% Ni is approximately 650°C (1200°F). (b) From Figure 9.35, the eutectoid composition is approximately 0.62 wt% C. Since the carbon concentration in the alloy (0.2 wt%) is less than the eutectoid (0.62 wt% C), the proeutectoid phase is ferrite. (c) Assume that the α–(α + Fe3C) phase boundary is at a negligible carbon concentration. Modifying Equation 9.21 leads to Wα' = 0.62 − C0 ' 0.62 − 0 = 0.62 − 0.20 0.62 = 0.68 Likewise, using a modified Equation 9.20 Wp = C0 ' − 0 0.62 − 0 = 0.20 0.62 = 0.32
- 532. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 10 PHASE TRANSFORMATIONS IN METALS PROBLEM SOLUTIONS The Kinetics of Phase Transformations 10.1 Name the two stages involved in the formation of particles of a new phase. Briefly describe each. Solution The two stages involved in the formation of particles of a new phase are nucleation and growth. The nucleation process involves the formation of normally very small particles of the new phase(s) which are stable and capable of continued growth. The growth stage is simply the increase in size of the new phase particles.
- 533. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.2 (a) Rewrite the expression for the total free energy change for nucleation (Equation 10.1) for the case of a cubic nucleus of edge length a (instead of a sphere of radius r). Now differentiate this expression with respect to a (per Equation 10.2) and solve for both the critical cube edge length, a*, and also ΔG*. (b) Is ΔG* greater for a cube or a sphere? Why? Solution (a) This problem first asks that we rewrite the expression for the total free energy change for nucleation (analogous to Equation 10.1) for the case of a cubic nucleus of edge length a. The volume of such a cubic radius is a3, whereas the total surface area is 6a2 (since there are six faces each of which has an area of a2). Thus, the expression for ∆G is as follows: ∆G = a3∆Gv + 6a2γ Differentiation of this expression with respect to a is as d ∆G da = d(a3∆Gv) da + d(6a2γ) da = 3a2∆Gv + 12aγ If we set this expression equal to zero as 3a2∆Gv + 12a γ = 0 and then solve for a (= a*), we have a* = − 4γ ∆Gv Substitution of this expression for a in the above expression for ∆G yields an equation for ∆G* as ∆G * = (a*)3∆Gv + 6(a*)2γ = − 4γ ∆Gv 3 ∆Gv + 6γ − 4γ ∆Gv 2
- 534. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = 32γ3 (∆Gv)2 (b) ∆Gv for a cube—i.e., (32) γ3 (∆Gv)2 —is greater that for a sphere—i.e., 16π 3 γ3 (∆Gv)2 = (16.8) γ3 (∆Gv)2 . The reason for this is that surface-to-volume ratio of a cube is greater than for a sphere.
- 535. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.3 If copper (which has a melting point of 1085°C) homogeneously nucleates at 849°C, calculate the critical radius given values of –1.77 × 109 J/m3 and 0.200 J/m2 , respectively, for the latent heat of fusion and the surface free energy. Solution This problem states that copper homogeneously nucleates at 849°C, and that we are to calculate the critical radius given the latent heat of fusion (–1.77 × 109 J/m3) and the surface free energy (0.200 J/m2). Solution to this problem requires the utilization of Equation 10.6 as r * = − 2γTm ∆H f 1 Tm − T = − (2)(0.200 J /m2)(1085 + 273 K) −1.77 × 109 J /m3 1 1085°C − 849°C = 1.30 × 10−9 m = 1.30 nm
- 536. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.4 (a) For the solidification of iron, calculate the critical radius r* and the activation free energy ΔG* if nucleation is homogeneous. Values for the latent heat of fusion and surface free energy are –1.85 × 109 J/m3 and 0.204 J/m2 , respectively. Use the supercooling value found in Table 10.1. (b) Now calculate the number of atoms found in a nucleus of critical size. Assume a lattice parameter of 0.292 nm for solid iron at its melting temperature. Solution (a) This portion of the problem asks that we compute r* and ∆G* for the homogeneous nucleation of the solidification of Fe. First of all, Equation 10.6 is used to compute the critical radius. The melting temperature for iron, found inside the front cover is 1538°C; also values of ∆Hf (–1.85 × 109 J/m3 ) and γ (0.204 J/m2) are given in the problem statement, and the supercooling value found in Table 10.1 is 295°C (or 295 K). Thus, from Equation 10.6 we have r * = − 2γTm ∆H f 1 Tm − T = − (2)(0.204 J /m2)(1538 + 273 K) −1.85 × 109 J /m3 1 295 K = 1.35 × 10−9 m = 1.35 nm For computation of the activation free energy, Equation 10.7 is employed. Thus ∆G * = 16π γ3Tm 2 3∆H f 2 1 (Tm − T)2 = (16)(π)(0.204 J /m2) 3 (1538 + 273 K)2 (3)(−1.85 × 109 J /m3)2 1 (295 K)2 = 1.57 × 10−18 J (b) In order to compute the number of atoms in a nucleus of critical size (assuming a spherical nucleus of radius r*), it is first necessary to determine the number of unit cells, which we then multiply by the number of atoms per unit cell. The number of unit cells found in this critical nucleus is just the ratio of critical nucleus and unit cell volumes. Inasmuch as iron has the BCC crystal structure, its unit cell volume is just a3 where a is the unit cell
- 537. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. length (i.e., the lattice parameter); this value is 0.292 nm, as cited in the problem statement. Therefore, the number of unit cells found in a radius of critical size is just # unit cells/particle = 4 3 πr *3 a3 = 4 3 (π)(1.35 nm)3 (0.292 nm)3 = 414 unit cells Inasmuch as 2 atoms are associated with each BCC unit cell, the total number of atoms per critical nucleus is just (414 unit cells/critical nucleus)(2 atoms /unit cell) = 828 atoms /critical nucleus
- 538. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.5 (a) Assume for the solidification of iron (Problem 10.4) that nucleation is homogeneous, and the number of stable nuclei is 106 nuclei per cubic meter. Calculate the critical radius and the number of stable nuclei that exist at the following degrees of supercooling: 200 K and 300 K. (b) What is significant about the magnitudes of these critical radii and the numbers of stable nuclei? Solution (a) For this part of the problem we are asked to calculate the critical radius for the solidification of iron (per Problem 10.4), for 200 K and 300 K degrees of supercooling, and assuming that the there are 106 nuclei per meter cubed for homogeneous nucleation. In order to calculate the critical radii, we replace the Tm – T term in Equation 10.6 by the degree of supercooling (denoted as ∆T) cited in the problem. For 200 K supercooling, r200 * = − 2γTm ∆H f 1 ∆T = − (2)(0.204 J /m2)(1538 + 273 K) −1.85 × 10 9 J /m3 1 200 K = 2.00 × 10-9 m = 2.00 nm And, for 300 K supercooling, r300 * = − (2)(0.204 J /m2)(1538 + 273 K) −1.85 × 10 9 J /m3 1 300 K = 1.33 × 10-9 m = 1.33 nm In order to compute the number of stable nuclei that exist at 200 K and 300 K degrees of supercooling, it is necessary to use Equation 10.8. However, we must first determine the value of K1 in Equation 10.8, which in turn requires that we calculate ∆G* at the homogeneous nucleation temperature using Equation 10.7; this was done in Problem 10.4, and yielded a value of ∆G* = 1.57 × 10-18 J. Now for the computation of K1, using the value of n* for at the homogenous nucleation temperature (106 nuclei/m3): K1 = n* exp − ∆G * kT
- 539. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = 106 nuclei/m3 exp − 1.57 × 10−18 J (1.38 × 10−23 J /atom− K)(1538°C − 295°C) = 5.62 × 1045 nuclei/m3 Now for 200 K supercooling, it is first necessary to recalculate the value ∆G* of using Equation 10.7, where, again, the Tm – T term is replaced by the number of degrees of supercooling, denoted as ∆T, which in this case is 200 K. Thus ∆G200 * = 16π γ3Tm 2 3∆H f 2 1 (∆T)2 = (16)(π)(0.204 J /m2)3 (1538 + 273 K)2 (3)(−1.85 × 109 J /m3)2 1 (200 K)2 = 3.41 × 10-18 J And, from Equation 10.8, the value of n* is n200 * = K1 exp − ∆G200 * kT = (5.62 × 1045 nuclei/m3)exp − 3.41 × 10−18 J (1.38 × 10−23 J /atom− K)(1538 K − 200 K) = 3.5 × 10-35 stable nuclei Now, for 300 K supercooling the value of ∆G* is equal to ∆G300 * = (16)(π)(0.204 J /m2)3 (1538 + 273 K)2 (3)(−1.85 × 109 J /m3)2 1 (300 K)2 = 1.51 × 10-18 J
- 540. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. from which we compute the number of stable nuclei at 300 K of supercooling as n300 * = K1 exp − ∆G300 * kT n* = (5.62 × 1045 nuclei/m3)exp − 1.51 × 10−18 J (1.38 × 10−23 J /atom− K)(1538 K − 300 K) = 2.32 × 107 stable nuclei (b) Relative to critical radius, r* for 300 K supercooling is slightly smaller that for 200 K (1.33 nm versus 2.00 nm). [From Problem 10.4, the value of r* at the homogeneous nucleation temperature (295 K) was 1.35 nm.] More significant, however, are the values of n* at these two degrees of supercooling, which are dramatically different—3.5 × 10-35 stable nuclei at ∆T = 200 K, versus 2.32 × 107 stable nuclei at ∆T = 300 K!
- 541. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.6 For some transformation having kinetics that obey the Avrami equation (Equation 10.17), the parameter n is known to have a value of 1.7. If, after 100 s, the reaction is 50% complete, how long (total time) will it take the transformation to go to 99% completion? Solution This problem calls for us to compute the length of time required for a reaction to go to 99% completion. It first becomes necessary to solve for the parameter k in Equation 10.17. In order to do this it is best manipulate the equation such that k is the dependent variable. We first rearrange Equation 10.17 as exp(− ktn) = 1 − y and then take natural logarithms of both sides: − ktn = ln(1 − y) Now solving for k gives k = − ln (1 − y) tn And, from the problem statement, for y = 0.50 when t = 100 s and given that n = 1.7, the value of k is equal to k = − ln (1 − 0.5) (100 s)1.7 = 2.76 × 10-4 We now want to manipulate Equation 10.17 such that t is the dependent variable. The above equation may be written in the form: tn = − ln (1 − y) k And solving this expression for t leads to t = − ln (1 − y) k 1/n
- 542. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Now, using this equation and the value of k determined above, the time to 99% transformation completion is equal to t = − ln (1 − 0.99) 2.76 × 10−4 1/1.7 = 305 s
- 543. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.7 Compute the rate of some reaction that obeys Avrami kinetics, assuming that the constants n and k have values of 3.0 and 7 × 10-3 , respectively, for time expressed in seconds. Solution This problem asks that we compute the rate of some reaction given the values of n and k in Equation 10.17. Since the reaction rate is defined by Equation 10.18, it is first necessary to determine t0.5, or the time necessary for the reaction to reach y = 0.5. We must first manipulate Equation 10.17 such that t is the dependent variable. We first rearrange Equation 10.17 as exp(− ktn) = 1 − y and then take natural logarithms of both sides: − ktn = ln(1 − y) which my be rearranged so as to read tn = − ln (1 − y) k Now, solving for t from this expression leads to t = − ln (1 − y) k 1/n For t0.5 this equation takes the form t0.5 = − ln (1 − 0.5) k 1/n And, incorporation of values for n and k given in the problem statement (3.0 and 7 × 10-3, respectively), then t0.5 = − ln (1 − 0.5) 7 × 10−3 1/3.0 = 4.63 s Now, the rate is computed using Equation 10.18 as
- 544. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. rate = 1 t0.5 = 1 4.63 s = 0.216 s-1
- 545. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.8 It is known that the kinetics of recrystallization for some alloy obey the Avrami equation and that the value of n in the exponential is 2.5. If, at some temperature, the fraction recrystallized is 0.40 after 200 min, determine the rate of recrystallization at this temperature. Solution This problem gives us the value of y (0.40) at some time t (200 min), and also the value of n (2.5) for the recrystallization of an alloy at some temperature, and then asks that we determine the rate of recrystallization at this same temperature. It is first necessary to calculate the value of k. We first rearrange Equation 10.17 as exp(− ktn) = 1 − y and then take natural logarithms of both sides: − ktn = ln(1 − y) Now solving for k gives k = − ln (1 − y) tn which, using the values cited above for y, n, and t yields k = − ln (1 − 0.40) (200 min)2.5 = 9.0 × 10-7 At this point we want to compute t0.5, the value of t for y = 0.5, which means that it is necessary to establish a form of Equation 10.17 in which t is the dependent variable. From one of the above equations tn = − ln (1 − y) k And solving this expression for t leads to t = − ln (1 − y) k 1/n
- 546. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. For t0.5, this equation takes the form t0.5 = − ln (1 − 0.5) k 1/n and incorporation of the value of k determined above, as well as the value of n cited in the problem statement (2.5), then t0.5 is equal to t0.5 = − ln (1 − 0.5) 9.0 × 10−7 1/2.5 = 226.3 min Therefore, from Equation 10.18, the rate is just rate = 1 t0.5 = 1 226.3 min = 4.42 × 10-3 (min)-1
- 547. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.9 The kinetics of the austenite-to-pearlite transformation obey the Avrami relationship. Using the fraction transformed–time data given here, determine the total time required for 95% of the austenite to transform to pearlite: Fraction Transformed Time (s) 0.2 12.6 0.8 28.2 Solution The first thing necessary is to set up two expressions of the form of Equation 10.17, and then to solve simultaneously for the values of n and k. In order to expedite this process, we will rearrange and do some algebraic manipulation of Equation 10.17. First of all, we rearrange as follows: 1 − y = exp − ktn ( ) Now taking natural logarithms ln (1 − y) = − ktn Or − ln (1 − y) = ktn which may also be expressed as ln 1 1 − y = ktn Now taking natural logarithms again, leads to ln ln 1 1 − y = ln k + n lnt
- 548. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. which is the form of the equation that we will now use. Using values cited in the problem statement, the two equations are thus ln ln 1 1 − 0.2 = ln k + n ln(12.6 s) ln ln 1 1 − 0.8 = ln k + n ln(28.2 s) Solving these two expressions simultaneously for n and k yields n = 2.453 and k = 4.46 × 10-4. Now it becomes necessary to solve for the value of t at which y = 0.95. One of the above equations—viz − ln (1 − y) = ktn may be rewritten as tn = − ln (1 − y) k And solving for t leads to t = − ln (1 − y) k 1/n Now incorporating into this expression values for n and k determined above, the time required for 95% austenite transformation is equal to t = − ln (1 − 0.95) 4.64 × 10−4 1/2.453 = 35.7 s
- 549. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.10 The fraction recrystallized–time data for the recrystallization at 600°C of a previously deformed steel are tabulated here. Assuming that the kinetics of this process obey the Avrami relationship, determine the fraction recrystallized after a total time of 22.8 min. Fraction Recrystallized Time (min) 0.20 13.1 0.70 29.1 Solution The first thing necessary is to set up two expressions of the form of Equation 10.17, and then to solve simultaneously for the values of n and k. In order to expedite this process, we will rearrange and do some algebraic manipulation of Equation 10.17. First of all, we rearrange as follows: 1 − y = exp − ktn ( ) Now taking natural logarithms ln (1 − y) = − ktn Or − ln (1 − y) = ktn which may also be expressed as ln 1 1 − y = ktn Now taking natural logarithms again, leads to ln ln 1 1 − y = ln k + n lnt which is the form of the equation that we will now use. The two equations are thus
- 550. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. ln ln 1 1 − 0.20 = ln k + n ln(13.1 min) ln ln 1 1 − 0.70 = ln k + n ln (29.1 min) Solving these two expressions simultaneously for n and k yields n = 2.112 and k = 9.75 × 10-4. Now it becomes necessary to solve for y when t = 22.8 min. Application of Equation 10.17 leads to y = 1 − exp −ktn ( ) = 1 − exp − (9.75 × 10-4 )(22.8 min)2.112 [ ]= 0.51
- 551. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.11 (a) From the curves shown in Figure 10.11 and using Equation 10.18, determine the rate of recrystallization for pure copper at the several temperatures. (b) Make a plot of ln(rate) versus the reciprocal of temperature (in K–1 ), and determine the activation energy for this recrystallization process. (See Section 5.5.) (c) By extrapolation, estimate the length of time required for 50% recrystallization at room temperature, 20°C (293 K). Solution This problem asks us to consider the percent recrystallized versus logarithm of time curves for copper shown in Figure 10.11. (a) The rates at the different temperatures are determined using Equation 10.18, which rates are tabulated below: Temperature (°C) Rate (min)-1 135 0.105 119 4.4 × 10-2 113 2.9 × 10-2 102 1.25 × 10-2 88 4.2 × 10-3 43 3.8 × 10-5 (b) These data are plotted below.
- 552. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The activation energy, Q, is related to the slope of the line drawn through the data points as Q = − Slope (R) where R is the gas constant. The slope of this line is equal to Slope = ∆ ln rate ∆ 1 T = ln rate1 − ln rate2 1 T1 − 1 T2 Let us take 1/T1 = 0.0025 K-1 and 1/T2 = 0.0031 K-1; the corresponding ln rate values are ln rate1 = -2.6 and ln rate2 = -9.4. Thus, using these values, the slope is equal to Slope = −2.6 − (−9.4) 0.0025 K-1 − 0.0031 K-1 = −1.133 × 104 K And, finally the activation energy is Q = − (Slope)(R) = − (−1.133 × 104 K-1)(8.31 J/mol- K) = 94,150 J/mol (c) At room temperature (20°C), 1/T = 1/(20 + 273 K) = 3.41 × 10-3 K-1. Extrapolation of the data in the plot to this 1/T value gives ln (rate) ≅ −12.8 which leads to rate ≅ exp (−12.8) = 2.76 × 10-6 (min)-1 But since rate = 1 t0.5
- 553. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. t0.5 = 1 rate = 1 2.76 × 10−6 (min)−1 = 3.62 × 105 min = 250 days
- 554. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.12 Determine values for the constants n and k (Equation 10.17) for the recrystallization of copper (Figure 10.11) at 102°C. Solution In this problem we are asked to determine, from Figure 10.11, the values of the constants n and k (Equation 10.17) for the recrystallization of copper at 102°C. One way to solve this problem is to take two values of percent recrystallization (which is just 100y, Equation 10.17) and their corresponding time values, then set up two simultaneous equations, from which n and k may be determined. In order to expedite this process, we will rearrange and do some algebraic manipulation of Equation 10.17. First of all, we rearrange as follows: 1 − y = exp − ktn ( ) Now taking natural logarithms ln (1 − y) = − ktn Or − ln (1 − y) = ktn which may also be expressed as ln 1 1 − y = ktn Now taking natural logarithms again, leads to ln ln 1 1 − y = ln k + n lnt which is the form of the equation that we will now use. From the 102°C curve of Figure 10.11, let us arbitrarily choose two percent recrystallized values, 20% and 80% (i.e., y1 = 0.20 and y2 = 0.80). Their corresponding time values are t1 = 50 min and t2 = 100 min (realizing that the time axis is scaled logarithmically). Thus, our two simultaneous equations become
- 555. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. ln ln 1 1 − 0.2 = ln k + n ln (50) ln ln 1 1 − 0.8 = ln k + n ln (100) from which we obtain the values n = 2.85 and k = 3.21 × 10-6.
- 556. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Metastable Versus Equilibrium States 10.13 In terms of heat treatment and the development of microstructure, what are two major limitations of the iron–iron carbide phase diagram? Solution Two limitations of the iron-iron carbide phase diagram are: (1) The nonequilibrium martensite does not appear on the diagram; and (2) The diagram provides no indication as to the time-temperature relationships for the formation of pearlite, bainite, and spheroidite, all of which are composed of the equilibrium ferrite and cementite phases.
- 557. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.14 (a) Briefly describe the phenomena of superheating and supercooling. (b) Why do these phenomena occur? Solution (a) Superheating and supercooling correspond, respectively, to heating or cooling above or below a phase transition temperature without the occurrence of the transformation. (b) These phenomena occur because right at the phase transition temperature, the driving force is not sufficient to cause the transformation to occur. The driving force is enhanced during superheating or supercooling.
- 558. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Isothermal Transformation Diagrams 10.15 Suppose that a steel of eutectoid composition is cooled to 550°C (1020°F) from 760°C (1400°F) in less than 0.5 s and held at this temperature. (a) How long will it take for the austenite-to-pearlite reaction to go to 50% completion? To 100% completion? (b) Estimate the hardness of the alloy that has completely transformed to pearlite. Solution We are called upon to consider the isothermal transformation of an iron-carbon alloy of eutectoid composition. (a) From Figure 10.22, a horizontal line at 550°C intersects the 50% and reaction completion curves at about 2.5 and 6 seconds, respectively; these are the times asked for in the problem statement. (b) The pearlite formed will be fine pearlite. From Figure 10.30a, the hardness of an alloy of composition 0.76 wt% C that consists of fine pearlite is about 265 HB (27 HRC).
- 559. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.16 Briefly cite the differences between pearlite, bainite, and spheroidite relative to microstructure and mechanical properties. Solution The microstructures of pearlite, bainite, and spheroidite all consist of α-ferrite and cementite phases. For pearlite, the two phases exist as layers which alternate with one another. Bainite consists of very fine and parallel needle-shaped particles of cementite that are surrounded an α-ferrite matrix. For spheroidite, the matrix is ferrite, and the cementite phase is in the shape of sphere-shaped particles. Bainite is harder and stronger than pearlite, which, in turn, is harder and stronger than spheroidite.
- 560. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.17 What is the driving force for the formation of spheroidite? Solution The driving force for the formation of spheroidite is the net reduction in ferrite-cementite phase boundary area.
- 561. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.18 Using the isothermal transformation diagram for an iron–carbon alloy of eutectoid composition (Figure 10.22), specify the nature of the final microstructure (in terms of microconstituents present and approximate percentages of each) of a small specimen that has been subjected to the following time–temperature treatments. In each case assume that the specimen begins at 760°C (1400°F) and that it has been held at this temperature long enough to have achieved a complete and homogeneous austenitic structure. (a) Cool rapidly to 700°C (1290°F), hold for 104 s, then quench to room temperature. Solution Below is Figure 10.22 upon which is superimposed the above heat treatment. After cooling and holding at 700°C for 104 s, approximately 50% of the specimen has transformed to coarse pearlite. Upon cooling to room temperature, the remaining 50% transforms to martensite. Hence, the final microstructure consists of about 50% coarse pearlite and 50% martensite. (b) Reheat the specimen in part (a) to 700°C (1290°F) for 20 h. Solution
- 562. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Heating to 700°C for 20 h the specimen in part (a) will transform the coarse pearlite and martensite to spheroidite. (c) Rapidly cool to 600°C (1110°F), hold for 4 s, rapidly cool to 450°C (840°F), hold for 10 s, then quench to room temperature. Solution Below is Figure 10.22 upon which is superimposed the above heat treatment. After cooling to and holding at 600°C for 4 s, approximately 50% of the specimen has transformed to pearlite (medium). During the rapid cooling to 450°C no transformations occur. At 450°C we start timing again at zero time; while holding at 450°C for 10 s, approximately 50 percent of the remaining unreacted 50% (or 25% of the original specimen) will transform to bainite. And upon cooling to room temperature, the remaining 25% of the original specimen transforms to martensite. Hence, the final microstructure consists of about 50% pearlite (medium), 25% bainite, and 25% martensite. (d) Cool rapidly to 400°C (750°F), hold for 2 s, then quench to room temperature.
- 563. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Solution Below is Figure 10.22 upon which is superimposed the above heat treatment. After cooling to and holding at 400°C for 2 s, no of the transformation begin lines have been crossed, and therefore, the specimen is 100% austenite. Upon cooling rapidly to room temperature, all of the specimen transforms to martensite, such that the final microstructure is 100% martensite. (e) Cool rapidly to 400°C (750°F), hold for 20 s, then quench to room temperature. Solution Below is Figure 10.22 upon which is superimposed the above heat treatment.
- 564. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. After cooling and holding at 400°C for 20 s, approximately 40% of the specimen has transformed to bainite. Upon cooling to room temperature, the remaining 60% transforms to martensite. Hence, the final microstructure consists of about 40% bainite and 60% martensite. (f) Cool rapidly to 400°C (750°F), hold for 200 s, then quench to room temperature. Solution Below is Figure 10.22 upon which is superimposed the above heat treatment.
- 565. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. After cooling and holding at 400°C for 200 s, the entire specimen has transformed to bainite. Therefore, during the cooling to room temperature no additional transformations will occur. Hence, the final microstructure consists of 100% bainite. (g) Rapidly cool to 575°C (1065°F), hold for 20 s, rapidly cool to 350°C (660°F), hold for 100 s, then quench to room temperature. Solution Below is Figure 10.22 upon which is superimposed the above heat treatment.
- 566. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. After cooling and holding at 575°C for 20 s, the entire specimen has transformed to fine pearlite. Therefore, during the second heat treatment at 350°C no additional transformations will occur. Hence, the final microstructure consists of 100% fine pearlite. (h) Rapidly cool to 250°C (480°F), hold for 100 s, then quench to room temperature in water. Reheat to 315°C (600°F) for 1 h and slowly cool to room temperature. Solution Below is Figure 10.22 upon which is superimposed the above heat treatment.
- 567. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. After cooling and holding at 250°C for 100 s, no transformations will have occurred—at this point, the entire specimen is still austenite. Upon rapidly cooling to room temperature in water, the specimen will completely transform to martensite. The second heat treatment (at 315°C for 1 h)—not shown on the above plot—will transform the material to tempered martensite. Hence, the final microstructure is 100% tempered martensite.
- 568. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.19 Make a copy of the isothermal transformation diagram for an iron–carbon alloy of eutectoid composition (Figure 10.22) and then sketch and label time–temperature paths on this diagram to produce the following microstructures: (a) 100% fine pearlite (b) 100% tempered martensite (c) 50% coarse pearlite, 25% bainite, and 25% martensite Solution Below is shown the isothermal transformation diagram for a eutectoid iron-carbon alloy, with time- temperature paths that will yield (a) 100% fine pearlite; (b) 100% tempered martensite; and (c) 50% coarse pearlite, 25% bainite, and 25% martensite.
- 569. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.20 Using the isothermal transformation diagram for a 0.45 wt% C steel alloy (Figure 10.39), determine the final microstructure (in terms of just the microconstituents present) of a small specimen that has been subjected to the following time-temperature treatments. In each case assume that the specimen begins at 845°C (1550°F), and that it has been held at this temperature long enough to have achieved a complete and homogeneous austenitic structure. (a) Rapidly cool to 250°C (480°F), hold for 103 s, then quench to room temperature. Solution Below is Figure 10.39 upon which is superimposed the above heat treatment. While rapidly cooling to 250°C about 80% of the specimen transforms to martensite; during the 1000 s isothermal treatment at 250°C no additional transformations occur. During the final cooling to room temperature, the untransformed austenite also transforms to martensite. Hence, the final microstructure consists of 100% martensite. (b) Rapidly cool to 700°C (1290°F), hold for 30 s, then quench to room temperature. Solution Below is Figure 10.39 upon which is superimposed the above heat treatment.
- 570. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. After cooling to and holding at 700°C for 30 s, a portion of specimen has transformed to proeutectoid ferrite. While cooling to room temperature, the remainder of the specimen transforms to martensite. Hence, the final microstructure consists proeutectoid ferrite and martensite. (c) Rapidly cool to 400°C (750°F), hold for 500 s, then quench to room temperature. Solution Below is Figure 10.39 upon which is superimposed the above heat treatment.
- 571. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. After cooling to and holding at 400°C for 500 s, all of the specimen has transformed to bainite. Hence, the final microstructure consists of 100% bainite. (d) Rapidly cool to 700°C (1290°F), hold at this temperature for 105 s, then quench to room temperature. Solution Below is Figure 10.39 upon which is superimposed the above heat treatment.
- 572. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. After cooling to and while holding at 700°C the specimen first transforms to proeutectoid ferrite and coarse pearlite. Continued heat treating at 700°C for 105 s results in a further transformation into spheroidite. Hence, the final microstructure consists of 100% spheroidite. (e) Rapidly cool to 650°C (1200°F), hold at this temperature for 3 s, rapidly cool to 400°C (750°F), hold for 10 s, then quench to room temperature. Solution Below is Figure 10.39 upon which is superimposed the above heat treatment.
- 573. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. After cooling to and holding at 650°C for 3 s, some of the specimen first transformers to proeutectoid ferrite and then to pearlite (medium). During the second stage of the heat treatment at 400°C, some (but not all) of the remaining unreacted austenite transforms to bainite. As a result of the final quenching, all of the remaining austenite transforms to martensite. Hence, the final microstructure consists of ferrite, pearlite (medium), bainite, and martensite. (f) Rapidly cool to 450°C (840°F), hold for 10 s, then quench to room temperature. Solution Below is Figure 10.39 upon which is superimposed the above heat treatment.
- 574. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. After cooling to and holding at 450°C for 10 s, a portion of the specimen first transformers to bainite. During the quenching to room temperature, the remainder of the specimen transforms to martensite. Hence, the final microstructure consists of bainite and martensite. (g) Rapidly cool to 625°C (1155°F), hold for 1 s, then quench to room temperature. Solution Below is Figure 10.39 upon which is superimposed the above heat treatment.
- 575. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. After cooling to and holding at 625°C for 1 s, a portion of the specimen first transformers to proeutectoid ferrite and pearlite. During the quenching to room temperature, the remainder of the specimen transforms to martensite. Hence, the final microstructure consists of ferrite, pearlite, and martensite. (h) Rapidly cool to 625°C (1155°F), hold at this temperature for 10 s, rapidly cool to 400°C (750°F), hold at this temperature for 5 s, then quench to room temperature. Solution Below is Figure 10.39 upon which is superimposed the above heat treatment.
- 576. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. After cooling to and holding at 625°C for 10 s, all of the specimen transformers to proeutectoid ferrite and pearlite. During the second part of the heat treatment at 400°C no additional transformation will occur. Hence, the final microstructure consists of ferrite and pearlite.
- 577. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.21 For parts (a), (c), (d), (f), and (h) of Problem 10.20, determine the approximate percentages of the microconstituents that form. Solution (a) From Problem 10.20(a) the microstructure consists of 100% martensite. (c) From Problem 10.20(c) the microstructure consists of 100% bainite. (d) From Problem 10.20(d) the microstructure consists of 100% spheroidite. (f) Figure 10.39 onto which the heat treatment for Problem 10.20(f) has been constructed is shown below. From this diagram, for the isothermal heat treatment at 450°C, the horizontal line constructed at this temperature and that ends at the 10 s point spans approximately 70% of the distance between the bainite reaction start and reaction completion curves. Therefore, the final microstructure consists of about 70% bainite and 30% martensite (the martensite forms while cooling to room temperature after 10 s at 450°C). (h) Figure 10.39 onto which the heat treatment for Problem 10.20(h) has been constructed is shown below.
- 578. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. After holding for 10 s at 625°C, the specimen has completely transformed to proeutectoid ferrite and fine pearlite; no further reaction will occur at 400°C. Therefore, we can calculate the mass fractions using the appropriate lever rule expressions, Equations 9.20 and 9.21, as follows: Wp = C0 ’ − 0.022 0.74 = 0.45 − 0.022 0.74 = 0.58 or 58% Wα' = 0.76 − C0 ’ 0.74 = 0.76 − 0.45 0.74 = 0.42 or 42%
- 579. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.22 Make a copy of the isothermal transformation diagram for a 0.45 wt% C iron-carbon alloy (Figure 10.39), and then sketch and label on this diagram the time-temperature paths to produce the following microstructures: (a) 42% proeutectoid ferrite and 58% coarse pearlite (b) 50% fine pearlite and 50% bainite (c) 100% martensite (d) 50% martensite and 50% austenite Solution Below is shown an isothermal transformation diagram for a 0.45 wt% C iron-carbon alloy, with time- temperature paths that will produce (a) 42% proeutectoid ferrite and 58% coarse pearlite; (b) 50% fine pearlite and 50% bainite; (c) 100% martensite; and (d) 50% martensite and 50% austenite.
- 580. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Continuous Cooling Transformation Diagrams 10.23 Name the microstructural products of eutectoid iron–carbon alloy (0.76 wt% C) specimens that are first completely transformed to austenite, then cooled to room temperature at the following rates: (a) 200°C/s, (b) 100°C/s, and (c) 20°C/s. Solution We are called upon to name the microstructural products that form for specimens of an iron-carbon alloy of eutectoid composition that are continuously cooled to room temperature at a variety of rates. Figure 10.27 is used in these determinations. (a) At a rate of 200°C/s, only martensite forms. (b) At a rate of 100°C/s, both martensite and pearlite form. (c) At a rate of 20°C/s, only fine pearlite forms.
- 581. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.24 Figure 10.40 shows the continuous cooling transformation diagram for a 1.13 wt% C iron-carbon alloy. Make a copy of this figure and then sketch and label continuous cooling curves to yield the following microstructures: (a) Fine pearlite and proeutectoid cementite (b) Martensite (c) Martensite and proeutectoid cementite (d) Coarse pearlite and proeutectoid cementite (e) Martensite, fine pearlite, and proeutectoid cementite Solution Below is shown a continuous cooling transformation diagram for a 1.13 wt% C iron-carbon alloy, with continuous cooling paths that will produce (a) fine pearlite and proeutectoid cementite; (b) martensite; (c) martensite and proeutectoid cementite; (d) coarse pearlite and proeutectoid cementite; and (e) martensite, fine pearlite, and proeutectoid cementite.
- 582. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.25 Cite two important differences between continuous cooling transformation diagrams for plain carbon and alloy steels. Solution Two important differences between continuous cooling transformation diagrams for plain carbon and alloy steels are: (1) for an alloy steel, a bainite nose will be present, which nose will be absent for plain carbon alloys; and (2) the pearlite-proeutectoid noses for plain carbon steel alloys are positioned at shorter times than for the alloy steels.
- 583. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.26 Briefly explain why there is no bainite transformation region on the continuous cooling transformation diagram for an iron–carbon alloy of eutectoid composition. Solution There is no bainite transformation region on the continuous cooling transformation diagram for an iron- carbon alloy of eutectoid composition (Figure 10.25) because by the time a cooling curve has passed into the bainite region, the entirety of the alloy specimen will have transformed to pearlite.
- 584. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.27 Name the microstructural products of 4340 alloy steel specimens that are first completely transformed to austenite, then cooled to room temperature at the following rates: (a) 10°C/s, (b) 1°C/s, (c) 0.1°C/s, and (d) 0.01°C/s. Solution This problem asks for the microstructural products that form when specimens of a 4340 steel are continuously cooled to room temperature at several rates. Figure 10.28 is used for these determinations. (a) At a cooling rate of 10°C/s, only martensite forms. (b) At a cooling rate of 1°C/s, both martensite and bainite form. (c) At a cooling rate of 0.1°C/s, martensite, proeutectoid ferrite, and bainite form. (d) At a cooling rate of 0.01°C/s, martensite, proeutectoid ferrite, pearlite, and bainite form.
- 585. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.28 Briefly describe the simplest continuous cooling heat treatment procedure that would be used in converting a 4340 steel from one microstructure to another. (a) (Martensite + bainite) to (ferrite + pearlite) (b) (Martensite + bainite) to spheroidite (c) (Martensite + bainite) to (martensite + bainite + ferrite) Solution This problem asks that we briefly describe the simplest continuous cooling heat treatment procedure that would be used in converting a 4340 steel from one microstructure to another. Solutions to this problem require the use of Figure 10.28. (a) In order to convert from (martensite + bainite) to (ferrite + pearlite) it is necessary to heat above about 720°C, allow complete austenitization, then cool to room temperature at a rate slower than 0.006°C/s. (b) To convert from (martensite + bainite) to spheroidite the alloy must be heated to about 700°C for several hours. (c) In order to convert from (martensite + bainite) to (martensite + bainite + ferrite) it is necessary to heat to above about 720°C, allow complete austenitization, then cool to room temperature at a rate between 0.3°C/s and 0.02°C/s.
- 586. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.29 On the basis of diffusion considerations, explain why fine pearlite forms for the moderate cooling of austenite through the eutectoid temperature, whereas coarse pearlite is the product for relatively slow cooling rates. Solution For moderately rapid cooling, the time allowed for carbon diffusion is not as great as for slower cooling rates. Therefore, the diffusion distance is shorter, and thinner layers of ferrite and cementite form (i.e., fine pearlite forms).
- 587. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Mechanical Behavior of Iron-Carbon Alloys Tempered Martensite 10.30 Briefly explain why fine pearlite is harder and stronger than coarse pearlite, which in turn is harder and stronger than spheroidite. Solution The hardness and strength of iron-carbon alloys that have microstructures consisting of α-ferrite and cementite phases depend on the boundary area between the two phases. The greater this area, the harder and stronger the alloy inasmuch as (1) these boundaries impede the motion of dislocations, and (2) the cementite phase restricts the deformation of the ferrite phase in regions adjacent to the phase boundaries. Fine pearlite is harder and stronger than coarse pearlite because the alternating ferrite-cementite layers are thinner for fine, and therefore, there is more phase boundary area. The phase boundary area between the sphere-like cementite particles and the ferrite matrix is less in spheroidite than for the alternating layered microstructure found in coarse pearlite.
- 588. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.31 Cite two reasons why martensite is so hard and brittle. Solution Two reasons why martensite is so hard and brittle are: (1) there are relatively few operable slip systems for the body-centered tetragonal crystal structure, and (2) virtually all of the carbon is in solid solution, which produces a solid-solution hardening effect.
- 589. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.32 Rank the following iron–carbon alloys and associated microstructures from the highest to the lowest tensile strength: (a) 0.25 wt%C with spheroidite, (b) 0.25 wt%C with coarse pearlite, (c) 0.60 wt%C with fine pearlite, and (d) 0.60 wt%C with coarse pearlite. Justify this ranking. Solution This problem asks us to rank four iron-carbon alloys of specified composition and microstructure according to hardness. This ranking is as follows: 0.60 wt% C, fine pearlite 0.60 wt% C, coarse pearlite 0.25 wt% C, coarse pearlite 0.25 wt% C, spheroidite The 0.25 wt% C, coarse pearlite is stronger than the 0.25 wt% C, spheroidite since coarse pearlite is stronger than spheroidite; the composition of the alloys is the same. The 0.60 wt% C, coarse pearlite is stronger than the 0.25 wt% C, coarse pearlite, since increasing the carbon content increases the strength. Finally, the 0.60 wt% C, fine pearlite is stronger than the 0.60 wt% C, coarse pearlite inasmuch as the strength of fine pearlite is greater than coarse pearlite because of the many more ferrite-cementite phase boundaries in fine pearlite.
- 590. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.33 Briefly explain why the hardness of tempered martensite diminishes with tempering time (at constant temperature) and with increasing temperature (at constant tempering time). Solution This question asks for an explanation as to why the hardness of tempered martensite diminishes with tempering time (at constant temperature) and with increasing temperature (at constant tempering time). The hardness of tempered martensite depends on the ferrite-cementite phase boundary area; since these phase boundaries are barriers to dislocation motion, the greater the area the harder the alloy. The microstructure of tempered martensite consists of small sphere-like particles of cementite embedded within a ferrite matrix. As the size of the cementite particles increases, the phase boundary area diminishes, and the alloy becomes softer. Therefore, with increasing tempering time, the cementite particles grow, the phase boundary area decreases, and the hardness diminishes. As the tempering temperature is increased, the rate of cementite particle growth also increases, and the alloy softens, again, because of the decrease in phase boundary area.
- 591. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.34 Briefly describe the simplest heat treatment procedure that would be used in converting a 0.76 wt% C steel from one microstructure to the other, as follows: (a) Spheroidite to tempered martensite (b) Tempered martensite to pearlite (c) Bainite to martensite (d) Martensite to pearlite (e) Pearlite to tempered martensite (f) Tempered martensite to pearlite (g) Bainite to tempered martensite (h) Tempered martensite to spheroidite Solution In this problem we are asked to describe the simplest heat treatment that would be required to convert a eutectoid steel from one microstructure to another. Figure 10.27 is used to solve the several parts of this problem. (a) For spheroidite to tempered martensite, austenitize at a temperature of about 760°C, quench to room temperature at a rate greater than about 140°C/s, then isothermally heat at a temperature between 250 and 650°C. (b) For tempered martensite to pearlite, austenitize at a temperature of about 760°C, then cool to room temperature at a rate less than about 35°C/s. (c) For bainite to martensite, first austenitize at a temperature of about 760°C, then quench to room temperature at a rate greater than about 140°C/s. (d) For martensite to pearlite, first austenitize at a temperature of about 760°C, then cool to room temperature at a rate less than about 35°C/s. (e) For pearlite to tempered martensite, first austenitize at a temperature of about 760°C, then rapidly quench to room temperature at a rate greater than about 140°C/s, then isothermally heat treat (temper) at a temperature between 250 and 650°C. (f) For tempered martensite to pearlite, first austenitize at a temperature of about 760°C, then cool to room temperature at a rate less than about 35°C/s. (g) For bainite to tempered martensite, first austenitize at a temperature of about 760°C, then rapidly quench to room temperature at a rate greater than about 140°C/s, then isothermally heat treat (temper) at a temperature between 250 and 650°C. (h) For tempered martensite to spheroidite simply heat at about 700°C for approximately 20 h.
- 592. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.35 (a) Briefly describe the microstructural difference between spheroidite and tempered martensite. (b) Explain why tempered martensite is much harder and stronger. Solution (a) Both tempered martensite and spheroidite have sphere-like cementite particles within a ferrite matrix; however, these particles are much larger for spheroidite. (b) Tempered martensite is harder and stronger inasmuch as there is much more ferrite-cementite phase boundary area for the smaller particles; thus, there is greater reinforcement of the ferrite phase, and more phase boundary barriers to dislocation motion.
- 593. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.36 Estimate the Rockwell hardnesses for specimens of an iron–carbon alloy of eutectoid composition that have been subjected to the heat treatments described in parts (b), (d), (f), (g), and (h) of Problem 10.18. Solution This problem asks for estimates of Rockwell hardness values for specimens of an iron-carbon alloy of eutectoid composition that have been subjected to some of the heat treatments described in Problem 10.18. (b) The microstructural product of this heat treatment is 100% spheroidite. According to Figure 10.30a, the hardness of a 0.76 wt% C alloy with spheroidite is about 87 HRB. (d) The microstructural product of this heat treatment is 100% martensite. According to Figure 10.32, the hardness of a 0.76 wt% C alloy consisting of martensite is about 64 HRC. (f) The microstructural product of this heat treatment is 100% bainite. From Figure 10.31, the hardness of a 0.76 wt% C alloy consisting of bainite is about 385 HB. And, conversion from Brinell to Rockwell hardness using Figure 6.18 leads to a hardness of 36 HRC. (g) The microstructural product of this heat treatment is 100% fine pearlite. According to Figure 10.30a, the hardness of a 0.76 wt% C alloy consisting of fine pearlite is about 27 HRC. (h) The microstructural product of this heat treatment is 100% tempered martensite. According to Figure 10.35, the hardness of a water-quenched eutectoid alloy that was tempered at 315°C for one hour is about 57 HRC.
- 594. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.37 Estimate the Brinell hardnesses for specimens of a 0.45 wt% C iron-carbon alloy that have been subjected to the heat treatments described in parts (a), (d), and (h) of Problem 10.20. Solution This problem asks for estimates of Brinell hardness values for specimens of an iron-carbon alloy of composition 0.45 wt% C that have been subjected to some of the heat treatments described in Problem 10.20. (a) The microstructural product of this heat treatment is 100% martensite. According to Figure 10.32, the hardness of a 0.45 wt% C alloy consisting of martensite is about 630 HB. (d) The microstructural product of this heat treatment is 100% spheroidite. According to Figure 10.30a the hardness of a 0.45 wt% C alloy with spheroidite is about 150 HB. (h) The microstructural product of this heat treatment is proeutectoid ferrite and fine pearlite. According to Figure 10.30a, the hardness of a 0.45 wt% C alloy consisting of fine pearlite is about 200 HB.
- 595. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.38 Determine the approximate tensile strengths for specimens of a eutectoid iron–carbon alloy that have experienced the heat treatments described in parts (a) and (c) of Problem 10.23. Solution This problem asks for estimates of tensile strength values for specimens of an iron-carbon alloy of eutectoid composition that have been subjected to some of the heat treatments described in Problem 10.23. (a) The microstructural product of this heat treatment is 100% martensite. According to Figure 10.32, the hardness of a 0.76 wt% C alloy is about 690 HB. For steel alloys, hardness and tensile strength are related through Equation 6.20a, and therefore TS (MPa) = 3.45 × HB = (3.45)(690 HB) = 2380 MPa (345,000 psi) (c) The microstructural product of this heat treatment is 100% fine pearlite. According to Figure 10.30a, the hardness of a 0.76 wt% C alloy consisting of fine pearlite is about 265 HB. Therefore, the tensile strength is TS (MPa) = 3.45 × HB = (3.45)(265 HB) = 915 MPa (132,500 psi)
- 596. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.39 For a eutectoid steel, describe isothermal heat treatments that would be required to yield specimens having the following Rockwell hardnesses: (a) 93 HRB, (b) 40 HRC, and (c) 27 HRC. Solution For this problem we are asked to describe isothermal heat treatments required to yield specimens having several Brinell hardnesses. (a) From Figure 10.30a, in order for a 0.76 wt% C alloy to have a Rockwell hardness of 93 HRB, the microstructure must be coarse pearlite. Thus, utilizing the isothermal transformation diagram for this alloy, Figure 10.22, we must rapidly cool to a temperature at which coarse pearlite forms (i.e., to about 675°C), allow the specimen to isothermally and completely transform to coarse pearlite. At this temperature an isothermal heat treatment for at least 200 s is required. (b) This portion of the problem asks for a hardness of 40 HRC the microstructure could consist of either (1) about 75% fine pearlite and 25% martensite (Figure 10.32), or (2) tempered martensite (Figure 10.35). For case (1), after austenitizing, rapidly cool to about 580°C (Figure 10.22), hold at this temperature for about 4 s (to obtain 75% fine pearlite), and then rapidly quench to room temperature. For case (2), after austenitizing, rapidly cool to room temperature in order to achieve 100% martensite. Then temper this martensite for about 2000 s at 535°C (Figure 10.35). (c) From Figure 10.30a, in order for a 0.76 wt% C alloy to have a Rockwell hardness of 27 HRC, the microstructure must be fine pearlite. Thus, utilizing the isothermal transformation diagram for this alloy, Figure 10.22, we must rapidly cool to a temperature at which fine pearlite forms (i.e., at about 580°C), allow the specimen to isothermally and completely transform to fine pearlite. At this temperature an isothermal heat treatment for at least 7 s is required.
- 597. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. DESIGN PROBLEMS Continuous Cooling Transformation Diagrams Mechanical Behavior of Iron-Carbon Alloys 10.D1 Is it possible to produce an iron-carbon alloy of eutectoid composition that has a minimum hardness of 90 HRB and a minimum ductility of 35%RA? If so, describe the continuous cooling heat treatment to which the alloy would be subjected to achieve these properties. If it is not possible, explain why. Solution This problem inquires as to the possibility of producing an iron-carbon alloy of eutectoid composition that has a minimum hardness of 90 HRB and a minimum ductility of 35%RA. If the alloy is possible, then the continuous cooling heat treatment is to be stipulated. According to Figures 10.30a and b, the following is a tabulation of Rockwell B hardnesses and percents area reduction for fine and coarse pearlites and spheroidite for a 0.76 wt% C alloy. Microstructure HRB %RA Fine pearlite > 100 20 Coarse pearlite 93 28 Spheroidite 88 67 Therefore, none of the microstructures meets both of these criteria. Both fine and coarse pearlites are hard enough, but lack the required ductility. Spheroidite is sufficiently ductile, but does not meet the hardness criterion.
- 598. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.D2 Is it possible to produce an iron-carbon alloy that has a minimum tensile strength of 690 MPa (100,000 psi) and a minimum ductility of 40%RA? If so, what will be its composition and microstructure (coarse and fine pearlites and spheroidite are alternatives)? If this is not possible, explain why. Solution This problem asks if it is possible to produce an iron-carbon alloy that has a minimum tensile strength of 690 MPa (100,000 psi) and a minimum ductility of 40%RA. If such an alloy is possible, its composition and microstructure are to be stipulated. From Equation 6.20a, this tensile strength corresponds to a Brinell hardness of HB = TS (MPa) 3.45 = 690 MPa 3.45 = 200 According to Figures 10.30a and b, the following is a tabulation of the composition ranges for fine and coarse pearlites and spheroidite that meet the stipulated criteria. Compositions for Compositions for Microstructure HB ≥ 200 %RA ≥ 40% Fine pearlite > 0.45 %C < 0.47 %C Coarse pearlite > 0.7 %C < 0.54 %C Spheroidite not possible 0-1.0 %C Therefore, only fine pearlite has a composition range overlap for both of the hardness and ductility restrictions; the fine pearlite would necessarily have to have a carbon content between 0.45 and 0.47 wt% C.
- 599. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.D3 It is desired to produce an iron-carbon alloy that has a minimum hardness of 175 HB and a minimum ductility of 52%RA. Is such an alloy possible? If so, what will be its composition and microstructure (coarse and fine pearlites and spheroidite are alternatives)? If this is not possible, explain why. Solution This problem inquires as to the possibility of producing a iron-carbon alloy having a minimum hardness of 175 HB and a minimum ductility of 52%RA. The composition and microstructure are to be specified; possible microstructures include fine and coarse pearlites and spheroidite. To solve this problem, we must consult Figures 10.30a and b. The following is a tabulation of the composition ranges for fine and coarse pearlites and spheroidite that meet the stipulated criteria. Compositions for Compositions for Microstructure HB ≥ 175 %RA ≥ 52% Fine pearlite > 0.36 %C < 0.33 %C Coarse pearlite > 0.43 %C < 0.40 %C Spheroidite > 0.70 <0-1.0 %C Thus, only spheroidite has a composition overlap for both of hardness and ductility restrictions; the spheroidite would necessarily have to have a carbon content greater than 0.70 wt% C.
- 600. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Tempered Martensite 10.D4 (a) For a 1080 steel that has been water quenched, estimate the tempering time at 425°C (800°F) to achieve a hardness of 50 HRC. (b) What will be the tempering time at 315°C (600°F) necessary to attain the same hardness? Solution This problem asks us to consider the tempering of a water-quenched 1080 steel to achieve a hardness of 50 HRC. It is necessary to use Figure 10.35. (a) The time necessary at 425°C is about 500 s. (b) At 315°C, the time required (by extrapolation) is approximately 4 × 106 s (about 50 days).
- 601. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.D5 An alloy steel (4340) is to be used in an application requiring a minimum tensile strength of 1380 MPa (200,000 psi) and a minimum ductility of 43%RA. Oil quenching followed by tempering is to be used. Briefly describe the tempering heat treatment. Solution We are to consider the tempering of an oil-quenched 4340 steel. From Figure 10.34, for a minimum tensile strength of 1380 MPa (200,000 psi) a tempering temperature of less than 450°C (840°F) is required. Also, for a minimum ductility of 43%RA, tempering must be carried out at a temperature greater than about 400°C (750°F). Therefore, tempering must occur at between 400 and 450°C (750 and 840°F) for 1 h.
- 602. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 10.D6 Is it possible to produce an oil-quenched and tempered 4340 steel that has a minimum yield strength of 1400 MPa (203,000 psi) and a ductility of at least 42%RA? If this is possible, describe the tempering heat treatment. If it is not possible, explain why. Solution This problem asks if it is possible to produce an oil-quenched and tempered 4340 steel that has a minimum yield strength of 1400 MPa (203,000 psi) and a minimum ductility of 42%RA, and, if possible, to describe the tempering heat treatment. In Figure 10.34 is shown the tempering characteristics of this alloy. According to this figure, in order to achieve a minimum yield strength of 1400 MPa a tempering temperature of less that about 410°C is required. On the other hand, tempering must be carried out at greater than about 360°C for a minimum ductility of 42%RA. Therefore, an oil-quenched and tempered 4340 alloy possessing these characteristics is possible; tempering would be carried out at between 360°C and 410°C for 1 h.
- 603. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 11 APPLICATIONS AND PROCESSING OF METAL ALLOYS PROBLEM SOLUTIONS Ferrous Alloys 11.1 (a) List the four classifications of steels. (b) For each, briefly describe the properties and typical applications. Solution This question asks that we list four classifications of steels, and, for each, to describe properties and cite typical applications. Low Carbon Steels Properties: nonresponsive to heat treatments; relatively soft and weak; machinable and weldable. Typical applications: automobile bodies, structural shapes, pipelines, buildings, bridges, and tin cans. Medium Carbon Steels Properties: heat treatable, relatively large combinations of mechanical characteristics. Typical applications: railway wheels and tracks, gears, crankshafts, and machine parts. High Carbon Steels Properties: hard, strong, and relatively brittle. Typical applications: chisels, hammers, knives, and hacksaw blades. High Alloy Steels (Stainless and Tool) Properties: hard and wear resistant; resistant to corrosion in a large variety of environments. Typical applications: cutting tools, drills, cutlery, food processing, and surgical tools.
- 604. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.2 (a) Cite three reasons why ferrous alloys are used so extensively. (b) Cite three characteristics of ferrous alloys that limit their utilization. Solution (a) Ferrous alloys are used extensively because: (1) Iron ores exist in abundant quantities. (2) Economical extraction, refining, and fabrication techniques are available. (3) The alloys may be tailored to have a wide range of properties. (b) Disadvantages of ferrous alloys are: (1) They are susceptible to corrosion. (2) They have a relatively high density. (3) They have relatively low electrical conductivities.
- 605. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.3 What is the function of alloying elements in tool steels? Solution The alloying elements in tool steels (e.g., Cr, V, W, and Mo) combine with the carbon to form very hard and wear-resistant carbide compounds.
- 606. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.4 Compute the volume percent of graphite VGr in a 3.5 wt% C cast iron, assuming that all the carbon exists as the graphite phase. Assume densities of 7.9 and 2.3 g/cm3 for ferrite and graphite, respectively. Solution We are asked to compute the volume percent graphite in a 3.5 wt% C cast iron. It first becomes necessary to compute mass fractions using the lever rule. From the iron-carbon phase diagram (Figure 11.2), the tie-line in the α and graphite phase field extends from essentially 0 wt% C to 100 wt% C. Thus, for a 3.5 wt% C cast iron Wα = CGr − C0 CGr − Cα = 100 − 3.5 100 − 0 = 0.965 WGr = C0 − Cα CGr − Cα = 3.5 − 0 100 − 0 = 0.035 Conversion from weight fraction to volume fraction of graphite is possible using Equation 9.6a as VGr = WGr ρGr Wα ρα + WGr ρGr = 0.035 2.3 g/cm3 0.965 7.9 g/cm3 + 0.035 2.3 g/cm3 = 0.111 or 11.1 vol%
- 607. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.5 On the basis of microstructure, briefly explain why gray iron is brittle and weak in tension. Solution Gray iron is weak and brittle in tension because the tips of the graphite flakes act as points of stress concentration.
- 608. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.6 Compare gray and malleable cast irons with respect to (a) composition and heat treatment, (b) microstructure, and (c) mechanical characteristics. Solution This question asks us to compare various aspects of gray and malleable cast irons. (a) With respect to composition and heat treatment: Gray iron--2.5 to 4.0 wt% C and 1.0 to 3.0 wt% Si. For most gray irons there is no heat treatment after solidification. Malleable iron--2.5 to 4.0 wt% C and less than 1.0 wt% Si. White iron is heated in a nonoxidizing atmosphere and at a temperature between 800 and 900°C for an extended time period. (b) With respect to microstructure: Gray iron--Graphite flakes are embedded in a ferrite or pearlite matrix. Malleable iron--Graphite clusters are embedded in a ferrite or pearlite matrix. (c) With respect to mechanical characteristics: Gray iron--Relatively weak and brittle in tension; good capacity for damping vibrations. Malleable iron--Moderate strength and ductility.
- 609. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.7 Compare white and nodular cast irons with respect to (a) composition and heat treatment, (b) microstructure, and (c) mechanical characteristics. Solution This question asks us to compare white and nodular cast irons. (a) With regard to composition and heat treatment: White iron--2.5 to 4.0 wt% C and less than 1.0 wt% Si. No heat treatment; however, cooling is rapid during solidification. Nodular cast iron--2.5 to 4.0 wt% C, 1.0 to 3.0 wt% Si, and a small amount of Mg or Ce. A heat treatment at about 700°C may be necessary to produce a ferritic matrix. (b) With regard to microstructure: White iron--There are regions of cementite interspersed within pearlite. Nodular cast iron--Nodules of graphite are embedded in a ferrite or pearlite matrix. (c) With respect to mechanical characteristics: White iron--Extremely hard and brittle. Nodular cast iron--Moderate strength and ductility.
- 610. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.8 Is it possible to produce malleable cast iron in pieces having large cross-sectional dimensions? Why or why not? Solution It is not possible to produce malleable iron in pieces having large cross-sectional dimensions. White cast iron is the precursor of malleable iron, and a rapid cooling rate is necessary for the formation of white iron, which may not be accomplished at interior regions of thick cross-sections.
- 611. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Nonferrous Alloys 11.9 What is the principal difference between wrought and cast alloys? Solution The principal difference between wrought and cast alloys is as follows: wrought alloys are ductile enough so as to be hot or cold worked during fabrication, whereas cast alloys are brittle to the degree that shaping by deformation is not possible and they must be fabricated by casting.
- 612. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.10 Why must rivets of a 2017 aluminum alloy be refrigerated before they are used? Solution Rivets of a 2017 aluminum alloy must be refrigerated before they are used because, after being solution heat treated, they precipitation harden at room temperature. Once precipitation hardened, they are too strong and brittle to be driven.
- 613. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.11 What is the chief difference between heat-treatable and non-heat-treatable alloys? Solution The chief difference between heat-treatable and nonheat-treatable alloys is that heat-treatable alloys may be strengthened by a heat treatment wherein a precipitate phase is formed (precipitation hardening) or a martensitic transformation occurs. Nonheat-treatable alloys are not amenable to strengthening by such treatments.
- 614. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.12 Give the distinctive features, limitations, and applications of the following alloy groups: titanium alloys, refractory metals, superalloys, and noble metals. Solution Titanium Alloys Distinctive features: relatively low density, high melting temperatures, and high strengths are possible. Limitation: because of chemical reactivity with other materials at elevated temperatures, these alloys are expensive to refine. Applications: aircraft structures, space vehicles, and in chemical and petroleum industries. Refractory Metals Distinctive features: extremely high melting temperatures; large elastic moduli, hardnesses, and strengths. Limitation: some experience rapid oxidation at elevated temperatures. Applications: extrusion dies, structural parts in space vehicles, incandescent light filaments, x-ray tubes, and welding electrodes. Superalloys Distinctive features: able to withstand high temperatures and oxidizing atmospheres for long time periods. Applications: aircraft turbines, nuclear reactors, and petrochemical equipment. Noble Metals Distinctive features: highly resistant to oxidation, especially at elevated temperatures; soft and ductile. Limitation: expensive. Applications: jewelry, dental restoration materials, coins, catalysts, and thermocouples.
- 615. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Forming Operations 11.13 Cite advantages and disadvantages of hot working and cold working. Solution The advantages of cold working are: (1) A high quality surface finish. (2) The mechanical properties may be varied. (3) Close dimensional tolerances. The disadvantages of cold working are: (1) High deformation energy requirements. (2) Large deformations must be accomplished in steps, which may be expensive. (3) A loss of ductility. The advantages of hot working are: (1) Large deformations are possible, which may be repeated. (2) Deformation energy requirements are relatively low. The disadvantages of hot working are: (1) A poor surface finish. (2) A variety of mechanical properties is not possible.
- 616. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.14 (a) Cite advantages of forming metals by extrusion as opposed to rolling. (b) Cite some disadvantages. Solution (a) The advantages of extrusion as opposed to rolling are as follows: (1) Pieces having more complicated cross-sectional geometries may be formed. (2) Seamless tubing may be produced. (b) The disadvantages of extrusion over rolling are as follows: (1) Nonuniform deformation over the cross-section. (2) A variation in properties may result over a cross-section of an extruded piece.
- 617. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Casting 11.15 List four situations in which casting is the preferred fabrication technique. Solution Four situations in which casting is the preferred fabrication technique are: (1) For large pieces and/or complicated shapes. (2) When mechanical strength is not an important consideration. (3) For alloys having low ductilities. (4) When it is the most economical fabrication technique.
- 618. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.16 Compare sand, die, investment, lost foam, and continuous casting techniques. Solution For sand casting, sand is the mold material, a two-piece mold is used, ordinarily the surface finish is not an important consideration, the sand may be reused (but the mold may not), casting rates are low, and large pieces are usually cast. For die casting, a permanent mold is used, casting rates are high, the molten metal is forced into the mold under pressure, a two-piece mold is used, and small pieces are normally cast. For investment casting, a single-piece mold is used, which is not reusable; it results in high dimensional accuracy, good reproduction of detail, and a fine surface finish; and casting rates are low. For lost foam casting, the pattern is polystyrene foam, whereas the mold material is sand. Complex geometries and tight tolerances are possible. Casting rates are higher than for investment, and there are few environmental wastes. For continuous casting, at the conclusion of the extraction process, the molten metal is cast into a continuous strand having either a rectangular or circular cross-section; these shapes are desirable for subsequent secondary metal-forming operations. The chemical composition and mechanical properties are relatively uniform throughout the cross-section.
- 619. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Miscellaneous Techniques 11.17 If it is assumed that, for steel alloys, the average cooling rate of the heat-affected zone in the vicinity of a weld is 10°C/s, compare the microstructures and associated properties that will result for 1080 (eutectoid) and 4340 alloys in their HAZs. Solution This problem asks that we specify and compare the microstructures and mechanical properties in the heat- affected weld zones for 1080 and 4340 alloys assuming that the average cooling rate is 10°C/s. Figure 10.27 shows the continuous cooling transformation diagram for an iron-carbon alloy of eutectoid composition (1080), and, in addition, cooling curves that delineate changes in microstructure. For a cooling rate of 10°C/s (which is less than 35°C/s) the resulting microstructure will be totally pearlite--probably a reasonably fine pearlite. On the other hand, in Figure 10.28 is shown the CCT diagram for a 4340 steel. From this diagram it may be noted that a cooling rate of 10°C/s produces a totally martensitic structure. Pearlite is softer and more ductile than martensite, and, therefore, is most likely more desirable.
- 620. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.18 Describe one problem that might exist with a steel weld that was cooled very rapidly. Solution If a steel weld is cooled very rapidly, martensite may form, which is very brittle. In some situations, cracks may form in the weld region as it cools.
- 621. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Annealing Processes 11.19 In your own words describe the following heat treatment procedures for steels and, for each, the intended final microstructure: full annealing, normalizing, quenching, and tempering. Solution Full annealing--Heat to about 50°C above the A3 line, Figure 11.10 (if the concentration of carbon is less than the eutectoid) or above the A1 line (if the concentration of carbon is greater than the eutectoid) until the alloy comes to equilibrium; then furnace cool to room temperature. The final microstructure is coarse pearlite. Normalizing--Heat to at least 55°C above the A3 line Figure 11.10 (if the concentration of carbon is less than the eutectoid) or above the Acm line (if the concentration of carbon is greater than the eutectoid) until the alloy completely transforms to austenite, then cool in air. The final microstructure is fine pearlite. Quenching--Heat to a temperature within the austenite phase region and allow the specimen to fully austenitize, then quench to room temperature in oil or water. The final microstructure is martensite. Tempering--Heat a quenched (martensitic) specimen, to a temperature between 450 and 650°C, for the time necessary to achieve the desired hardness. The final microstructure is tempered martensite.
- 622. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.20 Cite three sources of internal residual stresses in metal components. What are two possible adverse consequences of these stresses? Solution Three sources of residual stresses in metal components are plastic deformation processes, nonuniform cooling of a piece that was cooled from an elevated temperature, and a phase transformation in which parent and product phases have different densities. Two adverse consequences of these stresses are distortion (or warpage) and fracture.
- 623. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.21 Give the approximate minimum temperature at which it is possible to austenitize each of the following iron–carbon alloys during a normalizing heat treatment: (a) 0.20 wt% C, (b) 0.76 wt% C, and (c) 0.95 wt% C. Solution (a) For 0.20 wt% C, heat to at least 905°C (1660°F) since the A3 temperature is 850°C (1560°F). (b) For 0.76 wt% C, heat to at least 782°C (1440°F) since the A3 temperature is 727°C (1340°F). (c) For 0.95 wt% C, heat to at least 840°C (1545°F) since the Acm temperature is 785°C (1445°F).
- 624. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.22 Give the approximate temperature at which it is desirable to heat each of the following iron–carbon alloys during a full anneal heat treatment: (a) 0.25 wt% C, (b) 0.45 wt% C, (c) 0.85 wt% C, and (d) 1.10 wt% C. Solution (a) For 0.25 wt% C, heat to about 880°C (1510°F) since the A3 temperature is 830°C (1420°F). (b) For 0.45 wt% C, heat to about 830°C (1525°F) since the A3 temperature is 780°C (1435°F). (c) For 0.85 wt% C, heat to about 777°C (1430°F) since the A1 temperature is 727°C (1340°F). (d) For 1.10 wt% C, heat to about 777°C (1430°F) since the A1 temperature is 727°C (1340°F).
- 625. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.23 What is the purpose of a spheroidizing heat treatment? On what classes of alloys is it normally used? Solution The purpose of a spheroidizing heat treatment is to produce a very soft and ductile steel alloy having a spheroiditic microstructure. It is normally used on medium- and high-carbon steels, which, by virtue of carbon content, are relatively hard and strong.
- 626. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Heat Treatment of Steels 11.24 Briefly explain the difference between hardness and hardenability. Solution Hardness is a measure of a material's resistance to localized surface deformation, whereas hardenability is a measure of the depth to which a ferrous alloy may be hardened by the formation of martensite. Hardenability is determined from hardness tests.
- 627. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.25 What influence does the presence of alloying elements (other than carbon) have on the shape of a hardenability curve? Briefly explain this effect. Solution The presence of alloying elements (other than carbon) causes a much more gradual decrease in hardness with position from the quenched end for a hardenability curve. The reason for this effect is that alloying elements retard the formation of pearlitic and bainitic structures which are not as hard as martensite.
- 628. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.26 How would you expect a decrease in the austenite grain size to affect the hardenability of a steel alloy? Why? Solution A decrease of austenite grain size will decrease the hardenability. Pearlite normally nucleates at grain boundaries, and the smaller the grain size, the greater the grain boundary area, and, consequently, the easier it is for pearlite to form.
- 629. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.27 Name two thermal properties of a liquid medium that will influence its quenching effectiveness. Solution The two thermal properties of a liquid medium that influence its quenching effectiveness are thermal conductivity and heat capacity.
- 630. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.28 Construct radial hardness profiles for the following: (a) A 50-mm (2-in.) diameter cylindrical specimen of an 8640 steel alloy that has been quenched in moderately agitated oil Solution In the manner of Example Problem 11.1, the equivalent distances and hardnesses tabulated below were determined from Figures 11.14 and 11.17b. Radial Equivalent HRC Position Distance, mm Hardness Surface 7 54 3/4 R 11 50 Midradius 14 45 Center 16 44 The resulting hardness profile is plotted below. (b) A 75-mm (3-in.) diameter cylindrical specimen of a 5140 steel alloy that has been quenched in moderately agitated oil Solution In the manner of Example Problem 11.1, the equivalent distances and hardnesses tabulated below were determined from Figures 11.14 and 11.17b.
- 631. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Radial Equivalent HRC Position Distance, mm Hardness Surface 13 41 3/4 R 17.5 37 Midradius 22 33 Center 25 32 The resulting hardness profile is plotted below. (c) A 65-mm (2 1 2 -in.) diameter cylindrical specimen of an 8620 steel alloy that has been quenched in moderately agitated water Solution In the manner of Example Problem 11.1, the equivalent distances and hardnesses tabulated below were determined from Figures 11.15 and 11.17a. Radial Equivalent HRC Position Distance, mm Hardness Surface 2.5 42 3/4 R 7 31 Midradius 11 25 Center 13 24
- 632. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. The resulting hardness profile is plotted below. (d) A 70-mm (2 3 4 -in.) diameter cylindrical specimen of a 1040 steel alloy that has been quenched in moderately agitated water. Solution In the manner of Example Problem 11.1, the equivalent distances and hardnesses tabulated below were determined from Figures 11.14 and 11.17a. Radial Equivalent HRC Position Distance, mm Hardness Surface 3 48 3/4 R 8 30 Midradius 13 23 Center 15 22 The resulting hardness profile is plotted below.
- 633. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
- 634. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.29 Compare the effectiveness of quenching in moderately agitated water and oil by graphing, on a single plot, radial hardness profiles for 65-mm (2 1 2 -in.) diameter cylindrical specimens of an 8630 steel that have been quenched in both media. Solution We are asked to compare the effectiveness of quenching in moderately agitated water and oil by graphing, on a single plot, hardness profiles for a 65 mm (2-1/2 in.) diameter cylindrical specimen of an 8630 steel that has been quenched in both media. For moderately agitated water, the equivalent distances and hardnesses for the several radial positions [Figures 11.17a and 11.15] are tabulated below. Radial Equivalent HRC Position Distance, mm Hardness Surface 2.5 52 3/4 R 7 43 Midradius 11 36 Center 13 33 While for moderately agitated oil, the equivalent distances and hardnesses for the several radial positions [Figures 11.17b and 11.15] are tabulated below. Radial Equivalent HRC Position Distance, mm Hardness Surface 10 37 3/4 R 15 32 Midradius 18 29 Center 20 28 These data are plotted here.
- 635. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
- 636. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Precipitation Hardening 11.30 Compare precipitation hardening (Section 11.9) and the hardening of steel by quenching and tempering (Sections 10.5, 10.6, and 10.8) with regard to (a) The total heat treatment procedure (b) The microstructures that develop (c) How the mechanical properties change during the several heat treatment stages Solution (a) With regard to the total heat treatment procedure, the steps for the hardening of steel are as follows: (1) Austenitize above the upper critical temperature. (2) Quench to a relatively low temperature. (3) Temper at a temperature below the eutectoid. (4) Cool to room temperature. With regard to precipitation hardening, the steps are as follows: (1) Solution heat treat by heating into the solid solution phase region. (2) Quench to a relatively low temperature. (3) Precipitation harden by heating to a temperature that is within the solid two-phase region. (4) Cool to room temperature. (b) For the hardening of steel, the microstructures that form at the various heat treating stages in part (a) are: (1) Austenite (2) Martensite (3) Tempered martensite (4) Tempered martensite For precipitation hardening, the microstructures that form at the various heat treating stages in part (a) are: (1) Single phase (2) Single phase--supersaturated (3) Small plate-like particles of a new phase within a matrix of the original phase. (4) Same as (3) (c) For the hardening of steel, the mechanical characteristics for the various steps in part (a) are as follows: (1) Not important (2) The steel becomes hard and brittle upon quenching. (3) During tempering, the alloy softens slightly and becomes more ductile. (4) No significant changes upon cooling to or maintaining at room temperature.
- 637. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. For precipitation hardening, the mechanical characteristics for the various steps in part (a) are as follows: (1) Not important (2) The alloy is relatively soft. (3) The alloy hardens with increasing time (initially), and becomes more brittle; it may soften with overaging. (4) The alloy may continue to harden or overage at room temperature.
- 638. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.31 What is the principal difference between natural and artificial aging processes? Solution For precipitation hardening, natural aging is allowing the precipitation process to occur at the ambient temperature; artificial aging is carried out at an elevated temperature.
- 639. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. DESIGN PROBLEMS Ferrous Alloys Nonferrous Alloys 11.D1 Below is a list of metals and alloys: Plain carbon steel Magnesium Brass Zinc Gray cast iron Tool steel Platinum Aluminum Stainless steel Tungsten Titanium alloy Select from this list the one metal or alloy that is best suited for each of the following applications, and cite at least one reason for your choice: (a) The block of an internal combustion engine (b) Condensing heat exchanger for steam (c) Jet engine turbofan blades (d) Drill bit (e) Cryogenic (i.e., very low temperature) container (f) As a pyrotechnic (i.e., in flares and fireworks) (g) High-temperature furnace elements to be used in oxidizing atmospheres Solution (a) Gray cast iron would be the best choice for an engine block because it is relatively easy to cast, is wear resistant, has good vibration damping characteristics, and is relatively inexpensive. (b) Stainless steel would be the best choice for a heat exchanger to condense steam because it is corrosion resistant to the steam and condensate. (c) Titanium alloys are the best choice for high-speed aircraft jet engine turbofan blades because they are light weight, strong, and easily fabricated very resistant to corrosion. However, one drawback is their cost. (d) A tool steel would be the best choice for a drill bit because it is very hard retains its hardness at high temperature and is wear resistant, and, thus, will retain a sharp cutting edge. (e) For a cryogenic (low-temperature) container, an aluminum alloy would be the best choice; aluminum alloys have an FCC crystal structure, and therefore, are ductile at very low temperatures. (f) As a pyrotechnic in flares and fireworks, magnesium is the best choice because it ignites easily and burns
- 640. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. readily in air with a very bright flame. (g) Platinum is the best choice for high-temperature furnace elements to be used in oxidizing atmospheres because it is very ductile, has a relatively very high melting temperature, and is highly resistant to oxidation.
- 641. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D2 A group of new materials are the metallic glasses (or amorphous metals). Write an essay about these materials in which you address the following issues: (1) compositions of some of the common metallic glasses, (2) characteristics of these materials that make them technologically attractive, (3) characteristics that limit their utilization, (4) current and potential uses, and (5) at least one technique that is used to produce metallic glasses. Solution (a) Compositionally, the metallic glass materials are rather complex; several compositions are as follows: Fe80B20, Fe72Cr8P13C7, Fe67Co18B14Si, Pd77.5Cu6.0Si16.5, and Fe40Ni38Mo4B18. (b) These materials are exceptionally strong and tough, extremely corrosion resistant, and are easily magnetized. (c) Principal drawbacks for these materials are 1) complicated and exotic fabrication techniques are required; and 2) inasmuch as very rapid cooling rates are required, at least one dimension of the material must be small--i.e., they are normally produced in ribbon form. (d) Potential uses include transformer cores, magnetic amplifiers, heads for magnetic tape players, reinforcements for pressure vessels and tires, shields for electromagnetic interference, security tapes for library books. (e) Production techniques include centrifuge melt spinning, planar-flow casting, rapid pressure application, arc melt spinning.
- 642. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D3 Of the following alloys, pick the one(s) that may be strengthened by heat treatment, cold work, or both: R50500 titanium, AZ31B magnesium, 6061 aluminum, C51000 phosphor bronze, lead, 6150 steel, 304 stainless steel, and C17200 beryllium copper. Solution This question provides us with a list of several metal alloys, and then asks us to pick those that may be strengthened by heat treatment, by cold work, or both. Those alloys that may be heat treated are either those noted as "heat treatable" (Tables 11.6 through 11.9), or as martensitic stainless steels (Table 11.4). Alloys that may be strengthened by cold working must not be exceptionally brittle, and, furthermore, must have recrystallization temperatures above room temperature (which immediately eliminates lead). The alloys that fall within the three classifications are as follows: Heat Treatable Cold Workable Both 6150 steel 6150 steel 6150 steel C17200 Be-Cu C17200 Be-Cu C17200 Be-Cu 6061 Al 6061 Al 6061 Al 304 stainless steel R50500 Ti C51000 phosphor bronze AZ31B Mg
- 643. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D4 A structural member 100 mm (4 in.) long must be able to support a load of 50,000 N (11,250 lbf) without experiencing any plastic deformation. Given the following data for brass, steel, aluminum, and titanium, rank them from least to greatest weight in accordance with these criteria. Alloy Yield Strength [MPa (ksi)] Density (g/cm3 ) Brass 415 (60) 8.5 Steel 860 (125) 7.9 Aluminum 310 (45) 2.7 Titanium 550 (80) 4.5 Solution This problem asks us to rank four alloys (brass, steel, titanium, and aluminum), from least to greatest weight for a structural member to support a 50,000 N (11,250 lbf) load without experiencing plastic deformation. From Equation 6.1, the cross-sectional area (A0) must necessarily carry the load (F) without exceeding the yield strength (σy), as A0 = F σ y Now, given the length l, the volume of material required (V) is just V = lA0 = lF σ y Finally, the mass of the member (m) is m = Vρ = ρ lF σ y Here ρ is the density. Using the values given for these alloys m (brass) = (8.5 g/cm3)(10 cm)(50,000 N) (415 × 106 N /m2) 1 m 102 cm 2 = 102 g
- 644. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. m (steel) = (7.9 g/cm3)(10 cm)(50,000 N) (860 × 106 N /m2) 1 m 102 cm 2 = 46 g m (aluminum) = (2.7 g/cm3)(10 cm)(50,000 N) (310 × 106 N /m2) 1 m 102 cm 2 = 43.5 g m (titanium) = (4.5 g/cm3)(10 cm)(50,000 N) (550 × 106 N /m2) 1 m 102 cm 2 = 40.9 g Thus, titanium would have the minimum weight (or mass), followed by aluminum, steel, and brass.
- 645. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D5 Discuss whether it would be advisable to hot work or cold work the following metals and alloys on the basis of melting temperature, oxidation resistance, yield strength, and degree of brittleness: tin, tungsten, aluminum alloys, magnesium alloys, and a 4140 steel. Solution Tin would almost always be hot-worked. Even deformation at room temperature would be considered hot- working inasmuch as its recrystallization temperature is below room temperature (Table 7.2). Tungsten is hard and strong at room temperature, has a high recrystallization temperature, and experiences oxidation at elevated temperatures. Cold-working is difficult because of its strength, and hot-working is not practical because of oxidation problems. Most tungsten articles are fabricated by powder metallurgy, or by using cold-working followed by annealing cycles. Most aluminum alloys may be cold-worked since they are ductile and have relatively low yield strengths. Magnesium alloys are normally hot-worked inasmuch as they are quite brittle at room temperature. Also, magnesium alloys have relatively low recrystallization temperatures. A 4140 steel could be cold-worked in an over-tempered state which leaves it soft and relatively ductile, after which quenching and tempering heat treatments may be employed to strengthen and harden it. This steel would probably have a relatively high recrystallization temperature, and hot-working may cause oxidation.
- 646. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Heat Treatment of Steels 11.D6 A cylindrical piece of steel 25 mm (1.0 in.) in diameter is to be quenched in moderately agitated oil. Surface and center hardnesses must be at least 55 and 50 HRC, respectively. Which of the following alloys will satisfy these requirements: 1040, 5140, 4340, 4140, and 8640? Justify your choice(s). Solution In moderately agitated oil, the equivalent distances from the quenched end for a one-inch diameter bar for surface and center positions are 3 mm (1/8 in.) and 8 mm (11/32 in.), respectively [Figure 11.17b]. The hardnesses at these two positions for the alloys cited (as determined using Figure 11.14) are given below. Surface Center Alloy Hardness (HRC) Hardness (HRC) 1040 50 30 5140 56 49 4340 57 57 4140 57 55 8640 57 53 Thus, alloys 4340, 4140, and 8640 will satisfy the criteria for both surface and center hardnesses.
- 647. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D7 A cylindrical piece of steel 75 mm (3 in.) in diameter is to be austenitized and quenched such that a minimum hardness of 40 HRC is to be produced throughout the entire piece. Of the alloys 8660, 8640, 8630, and 8620, which will qualify if the quenching medium is (a) moderately agitated water, and (b) moderately agitated oil? Justify your choice(s). Solution (a) This problem calls for us to decide which of 8660, 8640, 8630, and 8620 alloys may be fabricated into a cylindrical piece 75 mm (3 in.) in diameter which, when quenched in mildly agitated water, will produce a minimum hardness of 40 HRC throughout the entire piece. The center of the steel cylinder will cool the slowest and therefore will be the softest. In moderately agitated water the equivalent distance from the quenched end for a 75 mm diameter bar for the center position is about 17 mm (11/16 in.) [Figure 11.17a]. The hardnesses at this position for the alloys cited (Figure 11.15) are given below. Center Alloy Hardness (HRC) 8660 58 8640 42 8630 30 8620 22 Therefore, only 8660 and 8640 alloys will have a minimum of 40 HRC at the center, and therefore, throughout the entire cylinder. (b) This part of the problem asks us to do the same thing for moderately agitated oil. In moderately agitated oil the equivalent distance from the quenched end for a 75 mm diameter bar at the center position is about 25.5 mm (1-1/32 in.) [Figure 11.17b]. The hardnesses at this position for the alloys cited (Figure 11.15) are given below. Center Alloy Hardness (HRC) 8660 53 8640 37 8630 26 8620 < 20
- 648. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Therefore, only the 8660 alloy will have a minimum of 40 HRC at the center, and therefore, throughout the entire cylinder.
- 649. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D8 A cylindrical piece of steel 38 mm (1 1 2 in.) in diameter is to be austenitized and quenched such that a microstructure consisting of at least 80% martensite will be produced throughout the entire piece. Of the alloys 4340, 4140, 8640, 5140, and 1040, which will qualify if the quenching medium is (a) moderately agitated oil and (b) moderately agitated water? Justify your choice(s). Solution (a) Since the cooling rate is lowest at the center, we want a minimum of 80% martensite at the center position. From Figure 11.17b, the cooling rate is equal to an equivalent distance from the quenched end of 12 mm (1/2 in.). According to Figure 11.14, the hardness corresponding to 80% martensite for these alloys is 50 HRC. Thus, all we need do is to determine which of the alloys have a 50 HRC hardness at an equivalent distance from the quenched end of 12 mm (1/2 in.). At an equivalent distance of 12 mm (1/2 in.), the following hardnesses are determined from Figure 11.14 for the various alloys. Alloy Hardness (HRC) 4340 56 4140 53 8640 49 5140 43 1040 25 Thus, only alloys 4340 and 4140 will qualify. (b) For moderately agitated water, the cooling rate at the center of a 38 mm diameter specimen is 7 mm (5/16 in.) equivalent distance from the quenched end [Figure 11.17a]. At this position, the following hardnesses are determined from Figure 11.14 for the several alloys. Alloy Hardness (HRC) 4340 57 4140 55 8640 54 5140 51 1040 33 It is still necessary to have a hardness of 50 HRC or greater at the center; thus, alloys 4340, 4140, 8640, and 5140 qualify.
- 650. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D9 A cylindrical piece of steel 90 mm (3 1 2 in.) in diameter is to be quenched in moderately agitated water. Surface and center hardnesses must be at least 55 and 40 HRC, respectively. Which of the following alloys will satisfy these requirements: 1040, 5140, 4340, 4140, 8620, 8630, 8640, and 8660? Justify your choices. Solution A ninety-millimeter (three and one-half inch) diameter cylindrical steel specimen is to be quenched in moderately agitated water. We are to decide which of eight different steels will have surface and center hardnesses of at least 55 and 40 HRC, respectively. In moderately agitated water, the equivalent distances from the quenched end for a 90 mm diameter bar for surface and center positions are 3 mm (1/8 in.) and 22 mm (7/8 in.), respectively [Figure 11.17a]. The hardnesses at these two positions for the alloys cited are given below. The hardnesses at these two positions for the alloys cited are given below (as determined from Figures 11.14 and 11.15). Surface Center Alloy Hardness (HRC) Hardness (HRC) 1040 50 < 20 5140 56 34 4340 57 53 4140 57 45 8620 42 < 20 8630 51 28 8640 56 38 8660 64 55 Thus, alloys 4340, 4140, and 8660 will satisfy the criteria for both surface hardness (minimum 55 HRC) and center hardness (minimum 40 HRC).
- 651. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D10 A cylindrical piece of 4140 steel is to be austenitized and quenched in moderately agitated oil. If the microstructure is to consist of at least 50% martensite throughout the entire piece, what is the maximum allowable diameter? Justify your answer. Solution From Figure 11.14, the equivalent distance from the quenched end of a 4140 steel to give 50% martensite (or a 42.5 HRC hardness) is 27 mm (1-1/8 in.). Thus, the quenching rate at the center of the specimen should correspond to this equivalent distance. Using Figure 11.17b, the center specimen curve takes on a value of 27 mm (1-1/8 in.) equivalent distance at a diameter of about 83 mm (3.3 in.).
- 652. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D11 A cylindrical piece of 8640 steel is to be austenitized and quenched in moderately agitated oil. If the hardness at the surface of the piece must be at least 49 HRC, what is the maximum allowable diameter? Justify your answer. Solution We are to determine, for a cylindrical piece of 8640 steel, the minimum allowable diameter possible in order yield a surface hardness of 49 HRC, when the quenching is carried out in moderately agitated oil. From Figure 11.15, the equivalent distance from the quenched end of an 8640 steel to give a hardness of 49 HRC is about 12 mm (15/32 in.). Thus, the quenching rate at the surface of the specimen should correspond to this equivalent distance. Using Figure 11.17b, the surface specimen curve takes on a value of 12 mm equivalent distance at a diameter of about 75 mm (3 in.).
- 653. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D12 Is it possible to temper an oil-quenched 4140 steel cylindrical shaft 100 mm (4 in.) in diameter so as to give a minimum tensile strength of 850 MPa (125,000 psi) and a minimum ductility of 21%EL? If so, specify a tempering temperature. If this is not possible, then explain why. Solution This problem asks if it is possible to temper an oil-quenched 4140 steel cylindrical shaft 100 mm (4 in.) in diameter so as to give a minimum tensile strength of 850 MPa (125,000 psi) and a minimum ductility of 21%EL. In order to solve this problem it is necessary to use Figures 11.20a and 11.20c, which plot, respectively, tensile strength and ductility versus tempering temperature. For the 100 mm diameter line of Figure 11.20a, tempering temperatures less than about 560°C are required to give a tensile strength of at least 850 MPa. Furthermore, from Figure 11.20c, for the 100 mm diameter line, tempering temperatures greater than about 585°C will give ductilities greater than 21%EL. Hence, it is not possible to temper this alloy to produce the stipulated minimum tensile strength and ductility. To meet the tensile strength minimum, T(tempering) < 560°C, whereas for ductility minimum, T(tempering) > 585°C; thus, there is no overlap of these tempering temperature ranges.
- 654. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D13 Is it possible to temper an oil-quenched 4140 steel cylindrical shaft 12.5 mm (0.5 in.) in diameter so as to give a minimum yield strength of 1000 MPa (145,000 psi) and a minimum ductility of 16%EL? If so, specify a tempering temperature. If this is not possible, then explain why. Solution This problem asks if it is possible to temper an oil-quenched 4140 steel cylindrical shaft 12.5 mm (0.5 in.) in diameter so as to give a minimum yield strength of 1000 MPa (145,000 psi) and a minimum ductility of 16%EL. In order to solve this problem it is necessary to use Figures 11.20b and 11.20c, which plot, respectively, yield strength and ductility versus tempering temperature. For the 12.5 mm diameter line of Figure 11.20b, tempering temperatures less than about 600°C are required to give a yield strength of at least 1000 MPa. Furthermore, from Figure 11.20c, for the 12.5 mm diameter line, tempering temperatures greater than about 550°C will give ductilities greater than 17%EL. Hence, it is possible to temper this alloy to produce the stipulated minimum yield strength and ductility; the tempering temperature will lie between 550°C and 600°C.
- 655. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Precipitation Hardening 11.D14 Copper-rich copper–beryllium alloys are precipitation hardenable. After consulting the portion of the phase diagram (Figure 11.30), do the following: (a) Specify the range of compositions over which these alloys may be precipitation hardened. (b) Briefly describe the heat-treatment procedures (in terms of temperatures) that would be used to precipitation harden an alloy having a composition of your choosing, yet lying within the range given for part (a). Solution This problem is concerned with the precipitation-hardening of copper-rich Cu-Be alloys. It is necessary for us to use the Cu-Be phase diagram (Figure 11.30), which is shown below. (a) The range of compositions over which these alloys may be precipitation hardened is between approximately 0.2 wt% Be (the maximum solubility of Be in Cu at about 300°C) and 2.7 wt% Be (the maximum solubility of Be in Cu at 866°C). (b) The heat treatment procedure, of course, will depend on the composition chosen. First of all, the solution heat treatment must be carried out at a temperature within the α phase region, after which, the specimen is quenched to room temperature. Finally, the precipitation heat treatment is conducted at a temperature within the α + γ2 phase region. For example, for a 1.5 wt% Be-98.5 wt% Cu alloy, the solution heat treating temperature must be between about 600°C (1110°F) and 900°C (1650°F), while the precipitation heat treatment would be below 600°C (1110°F),
- 656. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. and probably above 300°C (570°F). Below 300°C, diffusion rates are low, and heat treatment times would be relatively long.
- 657. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D15 A solution heat-treated 2014 aluminum alloy is to be precipitation hardened to have a minimum tensile strength of 450 MPa (65,250 psi) and a ductility of at least 15%EL. Specify a practical precipitation heat treatment in terms of temperature and time that would give these mechanical characteristics. Justify your answer. Solution We are asked to specify a practical heat treatment for a 2014 aluminum alloy that will produce a minimum tensile strength of 450 MPa (65,250 psi), and a minimum ductility of 15%EL. From Figure 11.27a, the following heat treating temperatures and time ranges are possible to the give the required tensile strength. Temperature (°C) Time Range (h) 260 0.02-0.2 204 0.02-10 149 3-600 121 > 35-? With regard to temperatures and times to give the desired ductility [Figure 11.27b]: Temperature (°C) Time Range (h) 260 < 0.01, > 40 204 < 0.15 149 < 10 121 < 500 From these tabulations, the following may be concluded: It is not possible to heat treat this alloy at 260°C so as to produce the desired set of properties— there is no overlap of the two sets of time ranges. At 204°C, the heat treating time would be between 0.02 and 0.15 h; times lying within this range are impractically short. At 149°C, the time would be between 3 and 10 h. Finally, at 121°C, the time range is 35 to about 500 h.
- 658. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 11.D16 Is it possible to produce a precipitation-hardened 2014 aluminum alloy having a minimum tensile strength of 425 MPa (61,625 psi) and a ductility of at least 12%EL? If so, specify the precipitation heat treatment. If it is not possible, explain why. Solution This problem inquires as to the possibility of producing a precipitation-hardened 2014 aluminum alloy having a minimum tensile strength of 425 MPa (61,625 psi) and a ductility of at least 12%EL. In order to solve this problem it is necessary to consult Figures 11.27a and 11.27b. Below are tabulated the times required at the various temperatures to achieve the stipulated tensile strength. Temperature (°C) Time Range (h) 260 < 0.5 204 < 15 149 1-1000 121 > 35-? With regard to temperatures and times to give the desired ductility: Temperature (°C) Time Range (h) 260 < 0.02, > 10 204 < 0.4, > 350 149 < 20 121 < 1000 From these tabulations, the following may be concluded: At 260°C, the heat treating time would need to be less than 0.02 h (1.2 min), which is impractically short. At 204°C, the heat treatment would need to be less than 0.4 h (24 min), which is a little on the short side. At 149°C, the time range would be between 1 and 20 h. Finally, at 121°C, this property combination is possible for virtually all times less than about 1000 h.
- 659. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 12 STRUCTURES AND PROPERTIES OF CERAMICS PROBLEM SOLUTIONS Crystal Structures 12.1 For a ceramic compound, what are the two characteristics of the component ions that determine the crystal structure? Solution The two characteristics of component ions that determine the crystal structure of a ceramic compound are: 1) the magnitude of the electrical charge on each ion, and 2) the relative sizes of the cations and anions.
- 660. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.2 Show that the minimum cation-to-anion radius ratio for a coordination number of 4 is 0.225. Solution In this problem we are asked to show that the minimum cation-to-anion radius ratio for a coordination number of four is 0.225. If lines are drawn from the centers of the anions, then a tetrahedron is formed. The tetrahedron may be inscribed within a cube as shown below. The spheres at the apexes of the tetrahedron are drawn at the corners of the cube, and designated as positions A, B, C, and D. (These are reduced in size for the sake of clarity.) The cation resides at the center of the cube, which is designated as point E. Let us now express the cation and anion radii in terms of the cube edge length, designated as a. The spheres located at positions A and B touch each other along the bottom face diagonal. Thus, AB = 2rA But (AB)2 = a2 + a2 = 2a2 or AB = a 2 = 2rA And
- 661. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. a = 2rA 2 There will also be an anion located at the corner, point F (not drawn), and the cube diagonal AEF will be related to the ionic radii as AEF = 2(rA + rC) (The line AEF has not been drawn to avoid confusion.) From the triangle ABF (AB)2 + (FB)2 = (AEF)2 But, FB = a = 2rA 2 and AB = 2rA from above. Thus, (2rA)2 + 2rA 2 2 = 2(rA + rC)[ ] 2 Solving for the rC/rA ratio leads to rC rA = 6 − 2 2 = 0.225
- 662. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.3 Show that the minimum cation-to-anion radius ratio for a coordination number of 6 is 0.414. [Hint: Use the NaCl crystal structure (Figure 12.2), and assume that anions and cations are just touching along cube edges and across face diagonals.] Solution This problem asks us to show that the minimum cation-to-anion radius ratio for a coordination number of 6 is 0.414 (using the rock salt crystal structure). Below is shown one of the faces of the rock salt crystal structure in which anions and cations just touch along the edges, and also the face diagonals. From triangle FGH, GF = 2rA and FH = GH = rA + rC Since FGH is a right triangle (GH)2 + (FH)2 = (FG)2 or (rA + rC)2 + (rA + rC)2 = (2rA)2 which leads to
- 663. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. rA + rC = 2rA 2 Or, solving for rC/rA rC rA = 2 2 − 1 = 0.414
- 664. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.4 Demonstrate that the minimum cation-to-anion radius ratio for a coordination number of 8 is 0.732. Solution This problem asks us to show that the minimum cation-to-anion radius ratio for a coordination number of 8 is 0.732. From the cubic unit cell shown below the unit cell edge length is 2rA, and from the base of the unit cell x2 = (2rA)2 + (2rA)2 = 8rA 2 Or x = 2rA 2 Now from the triangle that involves x, y, and the unit cell edge x2 + (2rA)2 = y2 = (2rA + 2rC )2 (2rA 2)2 + 4rA 2 = (2rA + 2rC)2 Which reduces to 2rA( 3 − 1) = 2rC Or
- 665. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. rC rA = 3 − 1 = 0.732
- 666. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.5 On the basis of ionic charge and ionic radii given in Table 12.3, predict crystal structures for the following materials: (a) CsI, (b) NiO, (c) KI, and (d) NiS. Justify your selections. Solution This problem calls for us to predict crystal structures for several ceramic materials on the basis of ionic charge and ionic radii. (a) For CsI, using data from Table 12.3 rCs+ rI− = 0.170 nm 0.220 nm = 0.773 Now, from Table 12.2, the coordination number for each cation (Cs+) is eight, and, using Table 12.4, the predicted crystal structure is cesium chloride. (b) For NiO, using data from Table 12.3 rNi2+ rO2− = 0.069 nm 0.140 nm = 0.493 The coordination number is six (Table 12.2), and the predicted crystal structure is sodium chloride (Table 12.4). (c) For KI, using data from Table 12.3 rK + rI− = 0.138 nm 0.220 nm = 0.627 The coordination number is six (Table 12.2), and the predicted crystal structure is sodium chloride (Table 12.4). (d) For NiS, using data from Table 12.3 rNi2+ rS2− = 0.069 nm 0.184 nm = 0.375 The coordination number is four (Table 12.2), and the predicted crystal structure is zinc blende (Table 12.4).
- 667. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.6 Which of the cations in Table 12.3 would you predict to form iodides having the cesium chloride crystal structure? Justify your choices. Solution We are asked to cite the cations in Table 12.3 which would form iodides having the cesium chloride crystal structure. First of all, the possibilities would include only the monovalent cations Cs+, K+, and Na+. Furthermore, the coordination number for each cation must be 8, which means that 0.732 < rC/rA < 1.0 (Table 12.2). From Table 12.3 the rC/rA ratios for these three cations and the I- ion are as follows: rCs+ rI− = 0.170 nm 0.220 nm = 0.77 rK + rI− = 0.138 nm 0.220 nm = 0.63 rNa+ rI− = 0.102 nm 0.220 nm = 0.46 Thus, only cesium will form the CsCl crystal structure with iodine.
- 668. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.7 Compute the atomic packing factor for the rock salt crystal structure in which rC/rA = 0.414. Solution This problem asks that we compute the atomic packing factor for the rock salt crystal structure when rC/rA = 0.414. From Equation 3.2 APF = VS VC With regard to the sphere volume, VS, there are four cation and four anion spheres per unit cell. Thus, VS = (4) 4 3 π rA 3 + (4) 4 3 π rC 3 But, since rC/rA = 0.414 VS = 16 3 π rA 3 1 + (0.414)3 [ ]= (17.94) rA 3 Now, for rC/rA = 0.414 the corner anions in Table 12.2 just touch one another along the cubic unit cell edges such that VC = a3 = 2(rA + rC)[ ] 3 = 2(rA + 0.414rA)[ ] 3 = (22.62)rA 3 Thus APF = VS VC = (17.94) rA 3 (22.62) rA 3 = 0.79
- 669. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.8 The zinc blende crystal structure is one that may be generated from close-packed planes of anions. (a) Will the stacking sequence for this structure be FCC or HCP? Why? (b) Will cations fill tetrahedral or octahedral positions? Why? (c) What fraction of the positions will be occupied? Solution This question is concerned with the zinc blende crystal structure in terms of close-packed planes of anions. (a) The stacking sequence of close-packed planes of anions for the zinc blende crystal structure will be the same as FCC (and not HCP) because the anion packing is FCC (Table 12.4). (b) The cations will fill tetrahedral positions since the coordination number for cations is four (Table 12.4). (c) Only one-half of the tetrahedral positions will be occupied because there are two tetrahedral sites per anion, and yet only one cation per anion.
- 670. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.9 The corundum crystal structure, found for Al2O3, consists of an HCP arrangement of O2- ions; the Al3+ ions occupy octahedral positions. (a) What fraction of the available octahedral positions are filled with Al3+ ions? (b) Sketch two close-packed O2– planes stacked in an AB sequence, and note octahedral positions that will be filled with the Al3+ ions. Solution This question is concerned with the corundum crystal structure in terms of close-packed planes of anions. (a) For this crystal structure, two-thirds of the octahedral positions will be filled with Al3+ ions since there is one octahedral site per O2- ion, and the ratio of Al3+ to O2- ions is two-to-three. (b) Two close-packed O2- planes and the octahedral positions between these planes that will be filled with Al3+ ions are sketched below.
- 671. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.10 Iron sulfide (FeS) may form a crystal structure that consists of an HCP arrangement of S2- ions. (a) Which type of interstitial site will the Fe2+ ions occupy? (b) What fraction of these available interstitial sites will be occupied by Fe2+ ions? Solution (a) This portion of the problem asks that we specify which type of interstitial site the Fe2+ ions will occupy in FeS if the S2- ions form an HCP arrangement. Since, from Table 12.3, rS2- = 0.184 nm and rFe2+= 0.077 nm, then rFe2+ rS2− = 0.077 nm 0.184 nm = 0.418 Inasmuch as rC/rA is between 0.414 and 0.732, the coordination number for Fe2+ is 6 (Table 12.2); therefore, tetrahedral octahedral positions are occupied. (b) We are now asked what fraction of these available interstitial sites are occupied by Fe2+ ions. Since there is 1 octahedral site per S2- ion, and the ratio of Fe2+ to S2- is 1:1, all of these sites are occupied with Fe2+ ions.
- 672. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.11 Magnesium silicate, Mg2SiO4, forms in the olivine crystal structure that consists of an HCP arrangement of O2- ions. (a) Which type of interstitial site will the Mg2+ ions occupy? Why? (b) Which type of interstitial site will the Si4+ ions occupy? Why? (c) What fraction of the total tetrahedral sites will be occupied? (d) What fraction of the total octahedral sites will be occupied? Solution (a) We are first of all asked to cite, for Mg2SiO4, which type of interstitial site the Mg2+ ions will occupy. From Table 12.3, the cation-anion radius ratio is rMg2+ rO2− = 0.072 nm 0.140 nm = 0.514 Since this ratio is between 0.414 and 0.732, the Mg2+ ions will occupy octahedral sites (Table 12.2). (b) Similarly, for the Si4+ ions rSi4+ rO2− = 0.040 nm 0.140 nm = 0.286 Since this ratio is between 0.225 and 0.414, the Si4+ ions will occupy tetrahedral sites. (c) For each Mg2SiO4 formula unit, there are four O2- ions, and, therefore, eight tetrahedral sites; furthermore, since there is one Si4+ ion per four O2- ions (eight tetrahedral sites), one-eighth of the tetrahedral sites will be occupied. (d) Also, inasmuch as the Mg2+ to O2- ratio is 1:2, and there is one octahedral site per O2- ion, one-half of these sites will be filled.
- 673. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.12 Using the Molecule Definition Utility found in both “Metallic Crystal Structures and Crystallography” and “Ceramic Crystal Structures” modules of VMSE, located on the book’s web site [www.wiley.com/college/callister (Student Companion Site)], generate (and print out) a three-dimensional unit cell for titanium dioxide, TiO2, given the following: (1) The unit cell is tetragonal with a = 0.459 nm and c = 0.296 nm, (2) oxygen atoms are located at the following point coordinates: 0.356 0.356 0 0.856 0.144 1 2 0.664 0.664 0 0.144 0.856 1 2 and (3) Ti atoms are located at the following point coordinates: 0 0 0 1 0 1 1 0 0 0 1 1 0 1 0 1 1 1 0 0 1 1 2 1 2 1 2 1 1 0 Solution First of all, open the “Molecular Definition Utility”; it may be found in either of “Metallic Crystal Structures and Crystallography” or “Ceramic Crystal Structures” modules. In the “Step 1” window, it is necessary to define the atom types, colors for the spheres (atoms), and specify atom sizes. Let us enter “O” as the name for the oxygen ions (since “O” the symbol for oxygen), and “Ti” as the name for the titanium ions. Next it is necessary to choose a color for each atom type from the selections that appear in the pull-down menu—for example, “Red” for O and “Light Cyan” for Ti. In the “Atom Size” window, it is necessary to enter an atom/ion size. In the instructions for this step, it is suggested that the atom/ion diameter in nanometers be used. From the table found inside the front cover of the textbook, the atomic radii for oxygen and titanium are 0.140 nm and 0.068 nm, respectively, and, therefore, their ionic diameters are twice these values (i.e., 0.280 nm and 0.136 nm); therefore, we enter the values “0.280” and “0.136” for the two atom types. Now click on the “Register” button, followed by clicking on the “Go to Step 2” button. In the “Step 2” window we specify positions for all of the atoms within the unit cell; their point coordinates are specified in the problem statement. Let’s begin with oxygen. Click on the red sphere that is located to the right of the “Molecule Definition Utility” box. Some of the point coordinates for the oxygen ions are fractional ones; in these instances, the unit cell lattice parameters--a or c (i.e., 0.459 or 0.296) are multiplied by the fraction. For example, one oxygen ion is located at the 0.856 0.144 1 2 coordinate. Therefore, the x, y, and z atoms positions are (0.856)(0.459) = 0.393, (0.144)(0.459) = 0.066, and 1 2 (0.296) = 0.148, respectively. Thus, we enter “0.393” in the “x” position box, “0.066” in the “y” position box, and “0.148” in the “z” position box. [Note: the
- 674. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. first two point coordinates relate to the a lattice parameter (0.459 nm), whereas the third applies to the c lattice parameter (0.296 nm).] Next we click on the “Register Atom Position” button. Now we repeat the procedure for the remaining oxygen ions After this step has been completed, it is necessary to specify positions for the titanium ions. To begin, we click on the light cyan sphere that is located next to the “Molecule Definition Utility” box. One Ti ion will be positioned at the origin of the coordinate system—i.e., its point coordinates are 0 0 0, and, therefore, we enter a “0” (zero) in each of the “x”, “y”, and “z” atom position boxes. Next we click on the “Register Atom Position” button. And the enter the coordinate for all of the other titanium ions For the oxygen ions, x, y, and z atom position entries for the 4 sets of point coordinates are as follows: 0.163, 0.163, 0 0.305, 0.305, 0 0.393, 0.066, 0.148 0.066, 0.393, 0.148 Now, for the titanium ions, the x, y, and z atom position entries for all 9 sets of point coordinates are as follows: 0, 0, 0 0.459, 0, 0 0, 0.459, 0 0, 0, 0.296 0.459, 0.459, 0 0.459, 0, 0.296 0, 0.459, 0.296 0.459, 0.459, 0.296 0.230, 0.230, 0.148 In Step 3, we may specify which atoms are to be represented as being bonded to one another, and which type of bond(s) to use (single solid, single dashed, double, and triple are possibilities), or we may elect to not represent any bonds at all (in which case we are finished). If it is decided to show bonds, probably the best thing to do is to represent unit cell edges as bonds. Your resulting image may be rotated by using mouse click-and-drag Your image should appear as the following screen shot.
- 675. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Here the darker spheres represent titanium ions, while oxygen ions are depicted by the lighter balls. [Note: Unfortunately, with this version of the Molecular Definition Utility, it is not possible to save either the data or the image that you have generated. You may use screen capture (or screen shot) software to record and store your image.]
- 676. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.13 Calculate the density of FeO, given that it has the rock salt crystal structure. Solution We are asked to calculate the theoretical density of FeO. This density may be computed using Equation (12.1) as ρ = ′n AFe + AO( ) VC NA Since the crystal structure is rock salt, n' = 4 formula units per unit cell. Using the ionic radii for Fe2+ and O2- from Table 12.3, the unit cell volume is computed as follows: VC = a3 = 2rFe2+ + 2rO2-( ) 3 = 2 (0.077 nm) + 2 (0.140 nm)[ ]3 = 0.0817 nm3 unit cell = 8.17 × 10-23 cm3 unit cell Thus, ρ = (4 formula units/unit cell)(55.85 g/mol + 16.00 g/mol) 8.17 × 10-23 cm3/unit cell( )6.022 × 1023 formula units/mol( ) = 5.84 g/cm3
- 677. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.14 Magnesium oxide has the rock salt crystal structure and a density of 3.58 g/cm3 . (a) Determine the unit cell edge length. (b) How does this result compare with the edge length as determined from the radii in Table 12.3, assuming that the Mg2+ and O2- ions just touch each other along the edges? Solution (a) This part of the problem calls for us to determine the unit cell edge length for MgO. The density of MgO is 3.58 g/cm3 and the crystal structure is rock salt. From Equation 12.1 ρ = ′n (AMg + AO) VC NA = ′n (AMg + AO) a3 NA Or, solving for a a = ′n (AMg + AO) ρ NA 1/ 3 Inasmuch as there are 4 formula units per unit cell for the rock salt crystal structure, and the atomic weights of magnesium and oxygen are 24.31 and 16.00 g/mol, respectively, when we solve for a from the above equation a = (4 formula units/unit cell)(24.31 g/mol + 16.00 g/mol) (3.58 g/cm3)(6.022 × 1023 formula units/mol) 1/ 3 = 4.21 × 10 -8 cm = 0.421 nm (b) The edge length is determined from the Mg2+ and O2- radii for this portion of the problem. Now for the rock salt crystal structure a = 2rMg2+ + 2rO2- From Table 12.3 a = 2(0.072 nm) + 2(0.140 nm) = 0.424 nm
- 678. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.15 Compute the theoretical density of diamond given that the C—C distance and bond angle are 0.154 nm and 109.5°, respectively. How does this value compare with the measured density? Solution This problem asks that we compute the theoretical density of diamond given that the C—C distance and bond angle are 0.154 nm and 109.5°, respectively. The first thing we need do is to determine the unit cell edge length from the given C—C distance. The drawing below shows the cubic unit cell with those carbon atoms that bond to one another in one-quarter of the unit cell. From this figure, φ is one-half of the bond angle or φ = 109.5°/2 = 54.75°, which means that θ = 90°− 54.75° = 35.25° since the triangle shown is a right triangle. Also, y = 0.154 nm, the carbon-carbon bond distance. Furthermore, x = a/4, and therefore, x = a 4 = y sin θ Or a = 4y sin θ = (4)(0.154 nm)(sin 35.25°) = 0.356 nm = 3.56 × 10-8 cm The unit cell volume, VC is just a3, that is VC = a3 = (3.56 × 10-8 cm)3 = 4.51 × 10−23 cm3
- 679. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. We must now utilize a modified Equation 12.1 since there is only one atom type. There are 8 equivalent atoms per unit cell, and therefore ρ = nÕAC VC NA = (8 atoms/unit cell)(12.01 g/g - atom) (4.51 × 10-23 cm3/unit cell)(6.022 × 1023 atoms/g - atom) = 3.54 g/cm3 The measured density is 3.51 g/cm3.
- 680. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.16 Compute the theoretical density of ZnS given that the Zn—S distance and bond angle are 0.234 nm and 109.5°, respectively. How does this value compare with the measured density? Solution This problem asks that we compute the theoretical density of ZnS given that the Zn—S distance and bond angle are 0.234 nm and 109.5°, respectively. The first thing we need do is to determine the unit cell volume from the given Zn—S distance. From the previous problem, the unit cell volume VC is just a3, a being the unit cell edge length, and VC = (4y sin θ)3 = (4)(0.234 nm)(sin 35.25°)[ ]3 = 0.1576 nm3 = 1.576 × 10-22 cm3 Now we must utilize Equation 12.1 with n' = 4 formula units, and AZn and AS being 65.41 and 32.06 g/mol, respectively. Thus ρ = n'Ê(AZn + AS) VC NA = (4 formula units/unit cell)(65.41 g/mol + 32.06 g/mol) (1.576 × 10-22 cm3/unit cell)(6.022 × 1023 formula units/mol) = 4.11 g/cm3 The measured value of the density is 4.10 g/cm3.
- 681. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.17 Cadmium sulfide (CdS) has a cubic unit cell, and from x-ray diffraction data it is known that the cell edge length is 0.582 nm. If the measured density is 4.82 g/cm3 , how many Cd2+ and S2- ions are there per unit cell? Solution We are asked to determine the number of Cd2+ and S2- ions per unit cell for cadmium sulfide (CdS). For CdS, a = 0.582 nm and ρ = 4.82 g/cm3. Solving for n' from Equation 12.1, we get ′n = ρVCNA ACd + AS = ρa3NA ACd + AS = (4.82 g/cm3)(5.82 × 10−8 cm)3(6.022 × 1023 formula units /mol) (112.41 g/mol + 32.06 g/mol) = 3.96 or almost 4 Therefore, there are four Cd2+ and four S2- per unit cell.
- 682. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.18 (a) Using the ionic radii in Table 12.3, compute the theoretical density of CsCl. (Hint: Use a modification of the result of Problem 3.3.) (b) The measured density is 3.99 g/cm3 . How do you explain the slight discrepancy between your calculated value and the measured one? Solution (a) We are asked to compute the density of CsCl. Modifying the result of Problem 3.3, we get a = 2rCs+ + 2rCl− 3 = 2(0.170 nm) + 2(0.181 nm) 3 = 0.405 nm = 4.05 × 10-8 cm From Equation 12.1 ρ = ′n (ACs + ACl) VC NA = ′n (ACs + ACl) a3 NA For the CsCl crystal structure, n' = 1 formula unit/unit cell, and thus ρ = (1 formula unit/unit cell)(132.91 g/mol + 35.45 g/mol) (4.05 × 10-8 cm)3/unit cell(6.022 × 1023 formula units/mol) = 4.21 g/cm3 (b) This value of the density is greater than the measured density (3.99 g/cm3). The reason for this discrepancy is that the ionic radii in Table 12.3, used for this computation, were for a coordination number of six, when, in fact, the coordination number of both Cs+ and Cl- is eight. The ionic radii should be slightly greater, leading to a larger VC value, and a lower density.
- 683. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.19 From the data in Table 12.3, compute the theoretical density of CaF2, which has the fluorite structure. Solution A unit cell of the fluorite structure is shown in Figure 12.5. It may be seen that there are four CaF2 units per unit cell (i.e., n' = 4 formula units/unit cell). Assume that for each of the eight small cubes in the unit cell a = 2rCa2+ + 2rF− 3 and, from Table 12.3 a = 2(0.100 nm) + 2(0.133 nm) 3 = 0.269 nm = 2.69 × 10-8 cm The volume of the unit cell is just VC = (2a)3 = (2)(2.69 × 10-8 cm)[ ] 3 = 1.56 × 10−22 cm3 Thus, from Equation 12.1 ρ = n'Ê(ACa + 2AF) VC NA = (4 formula units/unit cell) 40.08 g/mol + (2)(19.00 g/mol)[ ] (1.56 × 10-22 cm3/unit cell)( 6.022 × 1023 formula units/mol) = 3.33 g/cm3 The measured density is 3.18 g/cm3.
- 684. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.20 A hypothetical AX type of ceramic material is known to have a density of 2.65 g/cm3 and a unit cell of cubic symmetry with a cell edge length of 0.43 nm. The atomic weights of the A and X elements are 86.6 and 40.3 g/mol, respectively. On the basis of this information, which of the following crystal structures is (are) possible for this material: rock salt, cesium chloride, or zinc blende? Justify your choice(s). Solution We are asked to specify possible crystal structures for an AX type of ceramic material given its density (2.65 g/cm3), that the unit cell has cubic symmetry with edge length of 0.43 nm (4.3 × 10-8 cm), and the atomic weights of the A and X elements (86.6 and 40.3 g/mol, respectively). Using Equation 12.1 and solving for n' yields n' = ρVC NA AC + AA∑∑ = (2.65 g/cm3) (4.30 × 10-8 cm)3/unit cell[ ](6.022 × 1023 formula units/mol) (86.6 + 40.3) g/mol = 1.00 formula units/unit cell Of the three possible crystal structures, only cesium chloride has one formula unit per unit cell, and therefore, is the only possibility.
- 685. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.21 The unit cell for MgFe2O4 (MgO-Fe2O3) has cubic symmetry with a unit cell edge length of 0.836 nm. If the density of this material is 4.52 g/cm3 , compute its atomic packing factor. For this computation, you will need to use ionic radii listed in Table 12.3. Solution This problem asks us to compute the atomic packing factor for MgFe2O4 given its density and unit cell edge length. It is first necessary to determine the number of formula units in the unit cell in order to calculate the sphere volume. Solving for n' from Equation 12.1 leads to n' = ρVC NA AC + AA∑∑ = (4.52 g/cm3) (8.36 × 10-8 cm)3/unit cell[ ](6.022 × 1023 formula units/mol) (1)(24.31 g/mol) + (2)(55.85 g/mol) + (4)(16.00 g/mol) = 8.0 formula units/unit cell Thus, in each unit cell there are 8 Mg2+, 16 Fe3+, and 32 O2- ions. From Table 12.3, rMg2+ = 0.072 nm, rFe3+ = 0.069 nm, and rO2- = 0.140 nm. Thus, the total sphere volume in Equation 3.2 (which we denote as VS), is just VS = (8) 4 3 π (7.2 × 10−9 cm)3 + (16) 4 3 π (6.9 × 10−9 cm)3 + (32) 4 3 π (1.40 × 10−8 cm)3 = 4.02 × 10-22 cm3 Now, the unit cell volume (VC) is just VC = a3 = (8.36 × 10-8 cm)3 = 5.84 × 10−22 cm3 Finally, the atomic packing factor (APF) from Equation 3.2 is just APF = VS VC = 4.02 × 10-22 cm3 5.84 × 10-22 cm3 = 0.688
- 686. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.22 The unit cell for Cr2O3 has hexagonal symmetry with lattice parameters a = 0.4961 nm and c = 1.360 nm. If the density of this material is 5.22 g/cm3 , calculate its atomic packing factor. For this computation assume ionic radii of 0.062 nm and 0.140 nm, respectively for Cr3+ and O2- . Solution This problem asks for us to calculate the atomic packing factor for chromium oxide given values for the a and c lattice parameters, and the density. It first becomes necessary to determine the value of n' in Equation 12.1. This necessitates that we calculate the value of VC, the unit cell volume. In Problem 3.6 it was shown that the area of the hexagonal base (AREA) is related to a as AREA = 6R2 3 = 6 a 2 2 3 = 1.5a2 3 inasmuch as, for HCP, a = 2R (where R is the atomic radius). Now, incorporating the value of a provided in the problem statement into the above expression leads to AREA = (1.5)(4.961 × 10-8 cm)2( 3) = 6.39 × 10−15 cm2 The unit cell volume now is just VC = (AREA)(c) = (6.39 × 10-15 cm2)(1.360 × 10-7 cm) = 8.70 × 10-22 cm3 Now, solving for n' (Equation 12.1) yields n' = ρNAVC AC + AA∑∑ = (5.22 g/cm3)(6.022 × 1023 formula units/mol)(8.70 × 10-22 cm3/unit cell) (2)(52.00 g/mol) + (3)(16.00g/mol) = 18.0 formula units/unit cell
- 687. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Or, there are 18 Cr2O3 units per unit cell, or 36 Cr3+ ions and 54 O2- ions. As given in the problem statement, the radii of these two ion types are 0.062 and 0.140 nm, respectively. Thus, the total sphere volume in Equation 3.2 (which we denote as VS), is just VS = (36) 4 3 π (rCr3+ )3 + (54) 4 3 π (rO2− )3 = (36) 4 3 π (6.2 × 10−9 cm)3 + (54) 4 3 π (1.4 × 10−8 cm)3 = 6.57 × 10-22 cm3 Finally, the APF is just APF = VS VC = 6.57 × 10 -22 cm3 8.70 × 10 -22 cm3 = 0.755
- 688. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.23 Compute the atomic packing factor for the diamond cubic crystal structure (Figure 12.15). Assume that bonding atoms touch one another, that the angle between adjacent bonds is 109.5°, and that each atom internal to the unit cell is positioned a/4 of the distance away from the two nearest cell faces (a is the unit cell edge length). Solution We are asked in this problem to compute the atomic packing factor for the diamond cubic crystal structure, given that the angle between adjacent bonds is 109.5°. The first thing that we must do is to determine the unit cell volume VC in terms of the atomic radius r. From Problem 12.15 the following relationship was developed a = 4y sin θ in which y = 2r and θ = 35.25°. Furthermore, since the unit cell is cubic, VC = a3; therefore VC = (4y sin θ)3 = (4)(2r)(sin 35.25°)[ ]3 = 98.43 r3 Now, it is necessary to determine the sphere volume in the unit cell, VS, in terms of r. For this unit cell (Figure 12.15) there are 4 interior atoms, 6 face atoms, and 8 corner atoms. The entirety of the interior atoms, one-half of each face atom, and one-eighth of each corner atom belong to the unit cell. Therefore, there are 8 equivalent atoms per unit cell; hence VS = (8) 4 3 π r3 = 33.51 r3 Finally, the atomic packing factor is just APF = VS VC = 33.51 r3 98.43 r3 = 0.340
- 689. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.24 Compute the atomic packing factor for cesium chloride using the ionic radii in Table 12.3 and assuming that the ions touch along the cube diagonals. Solution We are asked in this problem to compute the atomic packing factor for the CsCl crystal structure. This requires that we take the ratio of the sphere volume within the unit cell and the total unit cell volume. From Figure 12.3 there is the equivalence of one Cs and one Cl ion per unit cell; the ionic radii of these two ions are 0.170 nm and 0.181 nm, respectively (Table 12.3). Thus, the sphere volume, VS, is just VS = 4 3 (π) (0.170 nm)3 + (0.181 nm)3 [ ] = 0.0454 nm3 For CsCl the unit cell edge length, a, in terms of the atomic radii is just a = 2r Cs+ + 2r Cl- 3 = 2(0.170 nm) + 2(0.181 nm) 3 = 0.405 nm Since VC = a3 VC = (0.405 nm)3 = 0.0664 nm3 And, finally the atomic packing factor is just APF = VS VC = 0.0454 nm3 0.0664 nm3 = 0.684
- 690. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.25 For each of the following crystal structures, represent the indicated plane in the manner of Figures 3.11 and 3.12, showing both anions and cations: (a) (100) plane for the rock salt crystal structure, (b) (110) plane for the cesium chloride crystal structure, (c) (111) plane for the zinc blende crystal structure, and (d) (110) plane for the perovskite crystal structure. Solution (a) A (100) plane for the rock salt crystal structure would appear as (b) A (110) plane for the cesium chloride crystal structure would appear as (c) A (111) plane for the zinc blende crystal structure would appear as
- 691. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (d) A (110) plane for the perovskite crystal structure would appear as
- 692. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Silicate Ceramics 12.26 In terms of bonding, explain why silicate materials have relatively low densities. Solution The silicate materials have relatively low densities because the atomic bonds are primarily covalent in nature (Table 12.1), and, therefore, directional. This limits the packing efficiency of the atoms, and therefore, the magnitude of the density.
- 693. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.27 Determine the angle between covalent bonds in an SiO4 4− tetrahedron. Solution This problem asks for us to determine the angle between covalent bonds in the SiO4 4− tetrahedron. Below is shown one such tetrahedron situated within a cube. Now if we extend the base diagonal from one corner to the other, it is the case that (2y)2 = a2 + a2 = 2a2 or y = a 2 2 Furthermore, x = a/2, and tan θ = x y = a/2 a 2 /2 = 1 2 From which θ = tan-1 1 2 = 35.26° Now, solving for the angle φ φ = 180° − 90° − 35.26° = 54.74° Finally, the bond angle is just 2φ, or 2φ = (2)(54.74°) = 109.48°.
- 694. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Imperfections in Ceramics 12.28 Would you expect Frenkel defects for anions to exist in ionic ceramics in relatively large concentrations? Why or why not? Solution Frenkel defects for anions would not exist in appreciable concentrations because the anion is quite large and is highly unlikely to exist as an interstitial.
- 695. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.29 Calculate the fraction of lattice sites that are Schottky defects for sodium chloride at its melting temperature (801°C). Assume an energy for defect formation of 2.3 eV. Solution We are asked in this problem to calculate the fraction of lattice sites that are Schottky defects for NaCl at its melting temperature (801°C), assuming that the energy for defect formation is 2.3 eV. In order to solve this problem it is necessary to use Equation 12.3 and solve for the Ns/N ratio. Rearrangement of this expression and substituting values for the several parameters leads to Ns N = exp − Qs 2kT = exp − 2.3 eV (2)(8.62 ×10-5 eV/K)(801 + 273 K) = 4.03 × 10-6
- 696. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.30 Calculate the number of Frenkel defects per cubic meter in zinc oxide at 1000°C. The energy for defect formation is 2.51 eV, while the density for ZnO is 5.55 g/cm3 at (1000°C). Solution This problem asks that we compute the number of Frenkel defects per cubic meter in zinc oxide at 1000°C. Solution of this problem is possible using Equation 12.2. However, we must first determine the value of N, the number of lattice sites per cubic meter, which is possible using a modified form of Equation 4.2; thus N = NAρ AZn + AO = (6.022 × 1023 atoms/mol)(5.55 g/cm3)(106 cm3/m3) 65.41 g/mol + 16.00 g/mol = 4.11 × 1028 lattice sites/m3 And, finally the value of Nfr is computed using Equation 12.2 as N fr = N exp − Qfr 2kT = (4.11 × 1028 lattice sites/m3) exp - 2.51 eV (2)(8.62 × 10-5 eV/K)(1000 + 273 K) = 4.43 × 1023 defects/m3
- 697. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.31 Using the data given below that relate to the formation of Schottky defects in some oxide ceramic (having the chemical formula MO), determine the following: (a) The energy for defect formation (in eV), (b) The equilibrium number of Schottky defects per cubic meter at 1000°C, and (c) The identity of the oxide (i.e., what is the metal M?) T (°C) ρ (g/cm3 ) Ns (m–3 ) 750 5.50 9.21 × 1019 1000 5.44 ? 1250 5.37 5.0 × 1022 Solution This problem provides for some oxide ceramic, at temperatures of 750°C and 1250°C, values for density and the number of Schottky defects per cubic meter. The (a) portion of the problem asks that we compute the energy for defect formation. To begin, let us combine a modified form of Equation 4.2 and Equation 12.3 as Ns = N exp − Qs 2kT = NAρ AM + AO exp − Qs 2kT Inasmuch as this is a hypothetical oxide material, we don't know the atomic weight of metal M, nor the value of Qs in the above equation. Therefore, let us write equations of the above form for two temperatures, T1 and T2. These are as follows: Ns1 = NAρ1 AM + AO exp − Qs 2kT1 (12.S1a) Ns2 = NAρ2 AM + AO exp − Qs 2kT2 (12.S1b) Dividing the first of these equations by the second leads to
- 698. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Ns1 Ns2 = NAρ1 AM + AO exp − Qs 2kT1 NAρ2 AM + AO exp − Qs 2kT2 which, after some algebraic manipulation, reduces to the form Ns1 Ns2 = ρ1 ρ2 exp − Qs 2k 1 T1 − 1 T2 (12.S2) Now, taking natural logarithms of both sides of this equation gives ln Ns1 Ns2 = ln ρ1 ρ2 − Qs 2k 1 T1 − 1 T2 and solving for Qs leads to the expression Qs = −2k ln Ns1 Ns2 − ln ρ1 ρ2 1 T1 − 1 T2 Let us take T1 = 750°C and T2 = 1250°C, and we may compute the value of Qs as Qs = −(2)(8.62 × 10-5 eV/K) ln 9.2 × 1019 m-3 5.0 × 1022 m-3 − ln 5.50 g/cm3 5.37 g/cm3 1 750 + 273 K − 1 1250 + 273 K = 3.40 eV (b) It is now possible to solve for Ns at 1000°C using Equation 12.S2 above. This time let's take T1 = 1000°C and T2 = 750°C. Thus, solving for Ns1, substituting values provided in the problem statement and Qs determined above yields Ns1 = Ns2 ρ1 ρ2 exp − Qs 2k 1 T1 − 1 T2
- 699. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (9.2 × 1019 m-3)( 5.44 g/cm3) 5.50 g/cm3 exp − 3.40 eV (2)(8.62 × 10-5 eV/K) 1 1000 + 273 K − 1 750 + 273 K = 4.0 x 1021 m-3 (c) And, finally, we want to determine the identity of metal M. This is possible by computing the atomic weight of M (AM) from Equation 12.S1a. Rearrangement of this expression leads to NAρ1 AM + AO = Ns1exp Qs 2kT1 And, after further algebraic manipulation NAρ1 Ns1exp Qs 2kT1 = AM + AO And, solving this expression for AM gives AM = NAρ1 Ns1exp Qs 2kT1 − AO Now, assuming that T1 = 750°C, the value of AM is AM = (6.022 × 1023 ions/mol)( 5.50 g/cm3)(106 cm3 /m3) (9.2 × 1019 ions/m3) exp 3.40 eV (2)(8.62 × 10-5 eV/K)(750 + 273 K) − 16.00 g/mol = 136.7 g/mol Upon consultation of the periodic table in Figure 2.6, the divalent metal (i.e., that forms M2+ ions) that has an atomic weight closest to 136.7 g/mol is barium. Thus, this metal oxide is BaO.
- 700. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.32 In your own words, briefly define the term “stoichiometric.” Solution Stoichiometric means having exactly the ratio of anions to cations as specified by the chemical formula for the compound.
- 701. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.33 If cupric oxide (CuO) is exposed to reducing atmospheres at elevated temperatures, some of the Cu2+ ions will become Cu+ . (a) Under these conditions, name one crystalline defect that you would expect to form in order to maintain charge neutrality. (b) How many Cu+ ions are required for the creation of each defect? (c) How would you express the chemical formula for this nonstoichiometric material? Solution (a) For a Cu2+O2- compound in which a small fraction of the copper ions exist as Cu+, for each Cu+ formed there is one less positive charge introduced (or one more negative charge). In order to maintain charge neutrality, we must either add an additional positive charge or subtract a negative charge. This may be accomplished be either creating Cu2+ interstitials or O2- vacancies. (b) There will be two Cu+ ions required for each of these defects. (c) The chemical formula for this nonstoichiometric material is Cu1+xO or CuO1-x, where x is some small fraction.
- 702. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.34 (a) Suppose that Li2O is added as an impurity to CaO. If the Li+ substitutes for Ca2+ , what kind of vacancies would you expect to form? How many of these vacancies are created for every Li+ added? (b) Suppose that CaCl2 is added as an impurity to CaO. If the Cl- substitutes for O2- , what kind of vacancies would you expect to form? How many of the vacancies are created for every Cl- added? Solution (a) For Li+ substituting for Ca2+ in CaO, oxygen vacancies would be created. For each Li+ substituting for Ca2+, one positive charge is removed; in order to maintain charge neutrality, a single negative charge may be removed. Negative charges are eliminated by creating oxygen vacancies, and for every two Li+ ions added, a single oxygen vacancy is formed. (b) For Cl- substituting for O2- in CaO, calcium vacancies would be created. For each Cl- substituting for an O2-, one negative charge is removed; in order to maintain charge neutrality, two Cl- ions will lead to the formation of one calcium vacancy.
- 703. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.35 What point defects are possible for Al2O3 as an impurity in MgO? How many Al3+ ions must be added to form each of these defects? Solution For every Al3+ ion that substitutes for Mg2+ in MgO, a single positive charge is added. Thus, in order to maintain charge neutrality, either a positive charge must be removed or a negative charge must be added. Negative charges are added by forming O2- interstitials, which are not likely to form. Positive charges may be removed by forming Mg2+ vacancies, and one magnesium vacancy would be formed for every two Al3+ ions added.
- 704. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Ceramic Phase Diagrams 12.36 For the ZrO2–CaO system (Figure 12.26), write all eutectic and eutectoid reactions for cooling. Solution There is only one eutectic for the portion of the ZrO2-CaO system shown in Figure 12.26. It occurs at approximately 2250°C and 23.5 wt% CaO, and, upon cooling, the reaction is Liquid → cubic ZrO2 + CaZrO3 There are two eutectoids. One occurs at about 1000°C and about 2 wt% CaO; its reaction upon cooling is as follows: tetragonal → monoclinic ZrO2 + cubic ZrO2 The second eutectoid occurs at about 850°C and 7 wt% CaO. This reaction is cubic → monoclinic ZrO2 + CaZr4O9
- 705. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.37 From Figure 12.25, the phase diagram for the MgO–Al2O3 system, it may be noted that the spinel solid solution exists over a range of compositions, which means that it is nonstoichiometric at compositions other than 50 mol% MgO–50 mol% Al2O3. (a) The maximum nonstoichiometry on the Al2O3-rich side of the spinel phase field exists at about 2000°C (3630°F) corresponding to approximately 82 mol% (92 wt%) Al2O3. Determine the type of vacancy defect that is produced and the percentage of vacancies that exist at this composition. (b) The maximum nonstoichiometry on the MgO-rich side of the spinel phase field exists at about 2000°C (3630°F) corresponding to approximately 39 mol% (62 wt%) Al2O3. Determine the type of vacancy defect that is produced and the percentage of vacancies that exist at this composition. Solution (a) For this portion of the problem we are to determine the type of vacancy defect that is produced on the Al2O3-rich side of the spinel phase field (Figure 12.25) and the percentage of these vacancies at the maximum nonstoichiometry (82 mol% Al2O3). On the alumina-rich side of this phase field, there is an excess of Al3+ ions, which means that some of the Al3+ ions substitute for Mg2+ ions. In order to maintain charge neutrality, Mg2+ vacancies are formed, and for every Mg2+ vacancy formed, two Al3+ ions substitute for three Mg2+ ions. Now, we will calculate the percentage of Mg2+ vacancies that exist at 82 mol% Al2O3. Let us arbitrarily choose as our basis 50 MgO-Al2O3 units of the stoichiometric material, which consists of 50 Mg2+ ions and 100 Al3+ ions. Furthermore, let us designate the number of Mg2+ vacancies as x, which means that 2x Al3+ ions have been added and 3x Mg2+ ions have been removed (two of which are filled with Al3+ ions). Using our 50 MgO- Al2O3 unit basis, the number of moles of Al2O3 in the nonstoichiometric material is (100 + 2x)/2; similarly the number of moles of MgO is (50 – 3x). Thus, the expression for the mol% of Al2O3 is just mol% Al2O3 = 100 + 2x 2 100 + 2x 2 + (50 − 3x) × 100 If we solve for x when the mol% of Al2O3 = 82, then x = 12.1. Thus, adding 2x or (2)(12.1) = 24.2 Al3+ ions to the original material consisting of 100 Al3+ and 50 Mg2+ ions will produce 12.1 Mg2+ vacancies. Therefore, the percentage of vacancies is just % vacancies = 12.1 100 + 50 × 100 = 8.1%
- 706. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (b) Now, we are asked to make the same determinations for the MgO-rich side of the spinel phase field, for 39 mol% Al2O3. In this case, Mg2+ ions are substituting for Al3+ ions. Since the Mg2+ ion has a lower charge than the Al3+ ion, in order to maintain charge neutrality, negative charges must be eliminated, which may be accomplished by introducing O2- vacancies. For every 2 Mg2+ ions that substitute for 2 Al3+ ions, one O2- vacancy is formed. Now, we will calculate the percentage of O2- vacancies that exist at 39 mol% Al2O3. Let us arbitrarily choose as our basis 50 MgO-Al2O3 units of the stoichiometric material which consists of 50 Mg2+ ions 100 Al3+ ions. Furthermore, let us designate the number of O2- vacancies as y, which means that 2y Mg2+ ions have been added and 2y Al3+ ions have been removed. Using our 50 MgO-Al2O3 unit basis, the number of moles of Al2O3 in the nonstoichiometric material is (100 – 2y)/2; similarly the number of moles of MgO is (50 + 2y). Thus, the expression for the mol% of Al2O3 is just mol% Al2O3 = 100 − 2y 2 100 − 2y 2 + (50 + 2y) × 100 If we solve for y when the mol% of Al2O3 = 39, then y = 7.91. Thus, 7.91 O2- vacancies are produced in the original material that had 200 O2- ions. Therefore, the percentage of vacancies is just % vacancies = 7.91 200 × 100 = 3.96%
- 707. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.38 When kaolinite clay [Al2(Si2O5)(OH)4] is heated to a sufficiently high temperature, chemical water is driven off. (a) Under these circumstances, what is the composition of the remaining product (in weight percent Al2O3)? (b) What are the liquidus and solidus temperatures of this material Solution (a) The chemical formula for kaolinite clay may also be written as Al2O3–2SiO2-2H2O. Thus, if we remove the chemical water, the formula becomes Al2O3–2SiO2. The formula weight for Al2O3 is just (2)(26.98 g/mol) + (3)(16.00 g/mol) = 101.96 g/mol; and for SiO2 the formula weight is 28.09 g/mol + (2)(16.00 g/mol) = 60.09 g/mol. Thus, the composition of this product, in terms of the concentration of Al2O3, CAl2O3 , in weight percent is just CAl2O3 = 101.96 g /mol 101.96 g /mol + (2)(60.09 g /mol) × 100 = 45.9 wt% (b) The liquidus and solidus temperatures for this material as determined from the SiO2–Al2O3 phase diagram, Figure 12.27, are 1825°C and 1587°C, respectively.
- 708. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Brittle Fracture of Ceramics 12.39 Briefly explain (a) why there may be significant scatter in the fracture strength for some given ceramic material, and (b) why fracture strength increases with decreasing specimen size. Solution (a) There may be significant scatter in the fracture strength for some given ceramic material because the fracture strength depends on the probability of the existence of a flaw that is capable of initiating a crack; this probability varies from specimen to specimen of the same material. (b) The fracture strength increases with decreasing specimen size because as specimen size decreases, the probably of the existence of a flaw of that is capable of initiating a crack diminishes.
- 709. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.40 The tensile strength of brittle materials may be determined using a variation of Equation 8.1. Compute the critical crack tip radius for an Al2O3 specimen that experiences tensile fracture at an applied stress of 275 MPa (40,000 psi). Assume a critical surface crack length of 2 × 10-3 mm and a theoretical fracture strength of E/10, where E is the modulus of elasticity. Solution We are asked for the critical crack tip radius for an Al2O3 material. From Equation 8.1 σm = 2σ0 a ρt 1/2 Fracture will occur when σm reaches the fracture strength of the material, which is given as E/10; thus E 10 = 2σ0 a ρt 1/2 Or, solving for ρt ρt = 400 aσ0 2 E2 From Table 12.5, E = 393 GPa, and thus, ρt = (400)(2 × 10−3 mm)(275 MPa)2 (393 × 103 MPa) 2 = 3.9 × 10-7 mm = 0.39 nm
- 710. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.41 The fracture strength of glass may be increased by etching away a thin surface layer. It is believed that the etching may alter surface crack geometry (i.e., reduce crack length and increase the tip radius). Compute the ratio of the original and etched crack tip radii for an eightfold increase in fracture strength if two-thirds of the crack length is removed. Solution This problem asks that we compute the crack tip radius ratio before and after etching. Let ρt = original crack tip radius, and ρt ' = etched crack tip radius Also, σ f ' = σ f a' = a 3 σ0 ' = 8σ0 Solving for ρt ' ρt from the following σ f = 2σ0 a ρt 1/2 = σ f ' = 2σ0 ' a' ρt ' 1/2 yields ρt ' ρt = σ0 ' σ0 2 a' a = 8σ0 σ0 2 a/ 3 a = 21.3
- 711. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Stress-Strain Behavior 12.42 A three-point bending test is performed on a glass specimen having a rectangular cross section of height d = 5 mm (0.2 in.) and width b = 10 mm (0.4 in.); the distance between support points is 45 mm (1.75 in.). (a) Compute the flexural strength if the load at fracture is 290 N (65 lbf). (b) The point of maximum deflection Δy occurs at the center of the specimen and is described by ∆y = FL3 48EI where E is the modulus of elasticity and I is the cross-sectional moment of inertia. Compute ∆y at a load of 266 N (60 lbf). Solution (a) For this portion of the problem we are asked to compute the flexural strength for a glass specimen that is subjected to a three-point bending test. The flexural strength (Equation 12.7a) is just σ fs = 3Ff L 2bd2 for a rectangular cross-section. Using the values given in the problem statement, σ fs = (3)(290 N)(45 × 10−3 m) (2)(10 × 10−3 m)(5 × 10−3 m)2 = 7.83 × 107 N/m2 = 78.3 MPa (10,660 psi) (b) We are now asked to compute the maximum deflection. From Table 12.5, the elastic modulus (E) for glass is 69 GPa (10 × 106 psi). Also, the moment of inertia for a rectangular cross section (Figure 12.32) is just I = bd3 12 Thus, ∆y = FL3 48E bd3 12 = FL3 4Ebd3
- 712. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (266 N)(45 × 10−3 m)3 (4)(69 × 109 N/m2)(10 × 10−3 m)(5 × 10−3 m)3 = 7.0 × 10-5 m = 7.0 × 10-2 mm (2.5 × 10-3 in.)
- 713. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.43 A circular specimen of MgO is loaded using a three-point bending mode. Compute the minimum possible radius of the specimen without fracture, given that the applied load is 425 N (95.5 lbf), the flexural strength is 105 MPa (15,000 psi), and the separation between load points is 50 mm (2.0 in.). Solution We are asked to calculate the maximum radius of a circular specimen of MgO that is loaded using three- point bending. Solving for R from Equation 12.7b R = Ff L σ fsπ 1/3 which, when substituting the parameters stipulated in the problem statement, yields R = (425 N)(50 × 10−3 m) (105 × 106 N /m2)(π) 1/3 = 4.0 × 10-3 m = 4.0 mm (0.16 in.)
- 714. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.44 A three-point bending test was performed on an aluminum oxide specimen having a circular cross section of radius 3.5 mm (0.14 in.); the specimen fractured at a load of 950 N (215 lbf) when the distance between the support points was 50 mm (2.0 in.). Another test is to be performed on a specimen of this same material, but one that has a square cross section of 12 mm (0.47 in.) length on each edge. At what load would you expect this specimen to fracture if the support point separation is 40 mm (1.6 in.)? Solution For this problem, the load is given at which a circular specimen of aluminum oxide fractures when subjected to a three-point bending test; we are then are asked to determine the load at which a specimen of the same material having a square cross-section fractures. It is first necessary to compute the flexural strength of the aluminum oxide, Equation 12.7b, and then, using this value, we may calculate the value of Ff in Equation 12.7a. From Equation 12.7b σ fs = Ff L πR3 = (950 N)(50 × 10−3 m) (π)(3.5 × 10−3 m)3 = 352 × 106 N/m2 = 352 MPa (50,000 psi) Now, solving for Ff from Equation 12.7a, realizing that b = d = 12 mm, yields Ff = 2σ fsd3 3L = (2)(352 × 106 N /m2)(12 × 10−3 m)3 (3)(40 × 10−3 m) = 10,100 N (2165 lbf )
- 715. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.45 (a) A three-point transverse bending test is conducted on a cylindrical specimen of aluminum oxide having a reported flexural strength of 390 MPa (56,600 psi). If the specimen radius is 2.5 mm (0.10 in.) and the support point separation distance is 30 mm (1.2 in.), predict whether or not you would expect the specimen to fracture when a load of 620 N (140 lbf) is applied. Justify your prediction. (b) Would you be 100% certain of the prediction in part (a)? Why or why not? Solution (a) This portion of the problem asks that we determine whether or not a cylindrical specimen of aluminum oxide having a flexural strength of 390 MPa (56,600 psi) and a radius of 2.5 mm will fracture when subjected to a load of 620 N in a three-point bending test; the support point separation is given as 30 mm. Using Equation 12.7b we will calculate the value of σ; if this value is greater than σfs (390 MPa), then fracture is expected to occur. Employment of Equation 12.7b yields σ = FL πR3 = (620 N)(30 × 10−3 m) (π)(2.5 × 10−3 m)3 = 379 × 106 N/m2 = 379 MPa (53,500 psi) Since this value is less than the given value of σfs (390 MPa), then fracture is not predicted. (b) The certainty of this prediction is not 100% because there is always some variability in the flexural strength for ceramic materials, and since this value of σ (379 MPa) is relatively close to σfs (390 MPa) then there is some chance that fracture will occur.
- 716. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Mechanisms of Plastic Deformation 12.46 Cite one reason why ceramic materials are, in general, harder yet more brittle than metals. Solution Crystalline ceramics are harder yet more brittle than metals because they (ceramics) have fewer slip systems, and, therefore, dislocation motion is highly restricted.
- 717. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Miscellaneous Mechanical Considerations 12.47 The modulus of elasticity for beryllium oxide (BeO) having 5 vol% porosity is 310 GPa (45 × 106 psi). (a) Compute the modulus of elasticity for the nonporous material. (b) Compute the modulus of elasticity for 10 vol% porosity. Solution (a) This portion of the problem requests that we compute the modulus of elasticity for nonporous BeO given that E = 310 GPa for a material having 5 vol% porosity. Thus, we solve Equation 12.9 for E0, using P = 0.05, which gives E0 = E 1 − 1.9P + 0.9P2 = 310 GPa 1 − (1.9)(0.05) + (0.9)(0.05)2 = 342 GPa (49.6 × 106 psi) (b) Now we are asked to determine the value of E at P = 10 vol% (i.e., 0.10). Using Equation 12.9 we get E = E0(1 − 1.9P + 0.9P2) = (342 GPa) 1 − (1.9)(0.10) + (0.9)(0.10)2 [ ]= 280 GPa (40.6 × 106 psi)
- 718. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.48 The modulus of elasticity for boron carbide (B4C) having 5 vol% porosity is 290 GPa (42 × 106 psi). (a) Compute the modulus of elasticity for the nonporous material. (b) At what volume percent porosity will the modulus of elasticity be 235 GPa (34 × 106 psi)? Solution (a) This portion of the problem requests that we compute the modulus of elasticity for nonporous B4C given that E = 290 GPa (42 × 106 psi) for a material having 5 vol% porosity. Thus, we solve Equation 12.9 for E0, using P = 0.05, which gives E0 = E 1 − 1.9P + 0.9P2 = 290 GPa 1 − (1.9)(0.05) + (0.9)(0.05)2 = 320 GPa (46.3 × 106 psi) (b) Now we are asked to compute the volume percent porosity at which the elastic modulus of B4C is 235 MPa (34 × 106 psi). Since from part (a), E0 = 320 GPa, and using Equation 12.9 we get E E0 = 235 MPa 320 MPa = 0.734 = 1 − 1.9P + 0.9P2 Or 0.9P2 − 1.9P + 0.266 = 0 Now, solving for the value of P using the quadratic equation solution yields P = 1.9 ± (−1.9)2 − (4)(0.9)(0.266) (2)(0.9) The positive and negative roots are P+ = 1.96 P- = 0.151 Obviously, only the negative root is physically meaningful, and therefore the value of the porosity to give the desired modulus of elasticity is 15.1 vol%.
- 719. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.49 Using the data in Table 12.5, do the following: (a) Determine the flexural strength for nonporous MgO assuming a value of 3.75 for n in Equation 12.10. (b) Compute the volume fraction porosity at which the flexural strength for MgO is 62 MPa (9000 psi). Solution (a) This part of the problem asks us to determine the flexural strength of nonporous MgO assuming that the value of n in Equation 12.10 is 3.75. Taking natural logarithms of both sides of Equation 12.10 yields ln σ fs = lnσ0 − nP In Table 12.5 it is noted that for P = 0.05, σfs = 105 MPa. For the nonporous material P = 0 and, ln σ0 = ln σfffsss. Solving for ln σ0 from the above equation and using these data gives lnσ0 = lnσ fs + nP = ln (105 MPa) + (3.75)(0.05) = 4.841 or σ0 = e4.841 = 127 MPa (18,100 psi) (b) Now we are asked to compute the volume percent porosity to yield a σfs of 62 MPa (9000 psi). Taking the natural logarithm of Equation 12.10 and solving for P leads to P = ln σ0 − ln σ fs n = ln (127 MPa) − ln (62 MPa) 3.75 = 0.19 or 19 vol%
- 720. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 12.50 The flexural strength and associated volume fraction porosity for two specimens of the same ceramic material are as follows: σfs (MPa) P 100 0.05 50 0.20 (a) Compute the flexural strength for a completely nonporous specimen of this material. (b) Compute the flexural strength for a 0.10 volume fraction porosity. Solution (a) Given the flexural strengths at two different volume fraction porosities, we are asked to determine the flexural strength for a nonporous material. If the natural logarithm is taken of both sides of Equation 12.10, then lnσ fs = lnσ0 − nP Using the data provided in the problem statement, two simultaneous equations may be written as ln (100 MPa) = ln σ0 − (0.05) n ln (50 MPa) = ln σ0 − (0.20) n Solving for n and σ0 leads to n = 4.62 and σ0 = 126 MPa. For the nonporous material, P = 0, and, from Equation 12.10, σ0 = σfs. Thus, σfs for P = 0 is 126 MPa. (b) Now, we are asked for σfs at P = 0.10 for this same material. Utilizing Equation 12.10 yields σ fs = σ0 exp (− nP) = (126 MPa) exp − (4.62)(0.10)[ ] = 79.4 MPa
- 721. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. DESIGN PROBLEMS Crystal Structures 12.D1 Gallium arsenide (GaAs) and gallium phosphide (GaP) both have the zinc blende crystal structure and are soluble in one another at all concentrations. Determine the concentration in weight percent of GaP that must be added to GaAs to yield a unit cell edge length of 0.5570 nm. The densities of GaAs and GaP are 5.316 and 4.130 g/cm3 , respectively. Solution This problem asks that we determine the concentration (in weight percent) of GaP that must be added to GaAs to yield a unit cell edge length of 0.5570 nm. The densities of GaAs and GaP were given in the problem as 5.307 and 4.130 g/cm3, respectively. To begin, it is necessary to employ Equation (13.1), and solve for the unit cell volume, VC, for the GaP-GaAs alloy as VC = n' Aave ρaveNA where Aave and ρave are the atomic weight and density, respectively, of the InAs-GaAs alloy. Inasmuch as both of these materials have the zinc blende crystal structure, which has cubic symmetry, VC is just the cube of the unit cell length, a. That is VC = a3 = (0.5570 nm)3 = (5.570 × 10−8 cm)3 = 1.728 × 10−22 cm3 It is now necessary to construct expressions for Aave and ρave in terms of the concentration of indium arsenide, CInAs using Equations 4.11a and 4.10a. For Aave we have Aave = 100 CGaP AGaP + (100 − C GaP ) AGaAs = 100 C GaP 100.69 g/mol + (100 − C GaP ) 144.64 g/mol
- 722. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. whereas for ρave ρave = 100 CGaP ρGaP + (100 − CGaP ) ρGaAs = 100 CGaP 4.130 g/cm3 + (100 − CGaP ) 5.316 g/cm3 Within the zinc blende unit cell there are four formula units, and thus, the value of n' in Equation 12.1 is 4; hence, this expression may be written in terms of the concentration of GaP in weight percent as follows: VC = 1.728 × 10-22 cm3 = n' Aave ρaveNA = (4 formula units/unit cell) 100 CGaP 100.69 g/mol + (100 − CGaP ) 144.64 g/mol 100 CGaP 4.130 g/cm3 + (100 − CGaP ) 5.316 g/cm3 (6.022 × 1023 formula units/mol) And solving this expression for CGaP leads to CGaP = 33.7 wt%.
- 723. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Stress-Strain Behavior 12.D2 It is necessary to select a ceramic material to be stressed using a three-point loading scheme (Figure 12.32). The specimen must have a circular cross section and a radius of 2.5 mm (0.10 in.), and must not experience fracture or a deflection of more than 6.2 × 10-2 mm (2.4 × 10-3 in.) at its center when a load of 275 N (62 lbf) is applied. If the distance between support points is 45 mm (1.77 in.), which of the materials in Table 12.5 are candidates? The magnitude of the centerpoint deflection may be computed using the equation supplied in Problem 12.42. Solution This problem asks for us to determine which of the ceramic materials in Table 12.5, when fabricated into cylindrical specimens and stressed in three-point loading, will not fracture when a load of 275 N (62 lbf) is applied, and also will not experience a center-point deflection of more than 6.2 × 10-2 mm (2.4 × 10-3 in.). The first of these criteria is met by those materials that have flexural strengths greater than the stress calculated using Equation 12.7b. According to this expression σ fs = FL π R3 = (275 N)(45 × 10−3 m) (π)(2.5 × 10−3 m)3 = 252 × 106 N /m2 = 252 MPa (35,000 psi) Of the materials in Table 12.5, the following have flexural strengths greater than this value: Si3N4, ZrO2, SiC, and Al2O3 For the second criterion we must solve for the magnitude of the modulus of elasticity, E, from the equation given in Problem 12.42 where the expression for the cross-sectional moment of inertia appears in Figure 12.32; that is, for a circular cross-section I = π R4 4 . Solving for E from these two expressions E = FL3 12π R4∆y = (275 N)(45 × 10−3 m)3 (12)(π)(2.5 × 10−3 m)4 (6.2 × 10−5 m) = 274 × 109 N/m2 = 274 GPa (38 × 106 psi)
- 724. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Of those materials that satisfy the first criterion, only Al2O3, Si3N4, and SiC have moduli of elasticity greater than this value (Table 12.5), and, therefore, are possible candidates.
- 725. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 13 APPLICATIONS AND PROCESSING OF CERAMICS PROBLEM SOLUTIONS Glasses Glass-Ceramics 13.1 Cite the two desirable characteristics of glasses. Solution Two desirable characteristics of glasses are optical transparency and ease of fabrication.
- 726. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.2 (a) What is crystallization? (b) Cite two properties that may be improved by crystallization. Solution (a) Crystallization is the process whereby a glass material is caused to transform to a crystalline solid, usually as a result of a heat treatment. (b) Two properties that may be improved by crystallization are (1) a lower coefficient of thermal expansion, and (2) higher strength.
- 727. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Refractories 13.3 For refractory ceramic materials, cite three characteristics that improve with and two characteristics that are adversely affected by increasing porosity. Solution For refractory ceramic materials, three characteristics that improve with increasing porosity are (1) decreased thermal expansion and contraction upon thermal cycling, (2) improved thermal insulation, and (3) improved resistance to thermal shock. Two characteristics that are adversely affected are (1) load-bearing capacity and (2) resistance to attack by corrosive materials.
- 728. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.4 Find the maximum temperature to which the following two magnesia–alumina refractory materials may be heated before a liquid phase will appear. (a) A spinel-bonded alumina material of composition 95 wt% Al2O3-5 wt% MgO. (b) A magnesia-alumina spinel of composition 65 wt% Al2O3-35 wt% MgO. Consult Figure 12.25. Solution (a) From Figure 12.25, for a spinel-bonded magnesia material (95 wt% Al2O3-5 wt% MgO), the maximum temperature without a liquid phase corresponds to the temperature of the eutectic isotherm on the Al2O3-rich side of the phase diagram, which is approximately 2000°C (3630°F). (b) The maximum temperature without the formation of a liquid phase for a magnesia-alumina spinel (65 wt% Al2O3-35 wt% MgO) lies at the phase boundary between MgAl2O4(ss)-MgAl2O4 + Liquid phase fields (just slightly to the left of the congruent melting point at which the two phase boundaries become tangent); this temperature is approximately 2030°C (3685°F).
- 729. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.5 Upon consideration of the SiO2–Al2O3 phase diagram, Figure 12.27, for each pair of the following list of compositions, which would you judge to be the more desirable refractory? Justify your choices. (a) 20 wt% Al2O3-80 wt% SiO2 and 25 wt% Al2O3-75 wt% SiO2 (b) 70 wt% Al2O3-30 wt% SiO2 and 80 wt% Al2O3-20 wt% SiO2 Solution (a) The 25 wt% Al2O3-75 wt% SiO2 will be more desirable because the liquidus temperature will be greater for this composition; therefore, at any temperature within the mullite + liquid region on the phase diagram, there will be a lower fraction of the liquid phase present than for the 20 wt% Al2O3-80 wt% SiO2 composition, and, thus, the mechanical integrity will be greater. (b) The 80 wt% Al2O3-20 wt% SiO2 composition will be more desirable because, for this composition, a liquid phase does not form until about 1890°C, whereas, for the 70 wt% Al2O3-30 wt% SiO2 material, a liquid phase forms at a much lower temperature--1587°C.
- 730. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.6 Compute the mass fractions of liquid in the following refractory materials at 1600°C (2910°F): (a) 6 wt% Al2O3-94 wt% SiO2 (b) 10 wt% Al2O3-90 wt% SiO2 (c) 30 wt% Al2O3-70 wt% SiO2 (d) 80 wt% Al2O3-20 wt% SiO2 Solution This problem calls for us to compute the mass fractions of liquid for two fireclay refractory materials at 1600°C. In order to solve this problem it is necessary that we use the SiO2-Al2O3 phase diagram (Figure 12.27) in conjunction with tie-lines and the lever rule at 1600°C. (a) For the 6 wt% Al2O3-94 wt% SiO2 composition, the appropriate lever-rule expression is WL = C0 − CSiO2 CL − CSiO2 For a tie-line constructed across the SiO2-Liquid phase field at 1600°C CL= 7 wt% Al2O3 CSiO2 = 0 wt% Al2O3 And, inasmuch as C0 = 6 wt% Al2O3 the mass fraction of liquid using the above lever-rule expression is WL = 6 − 0 7 − 0 = 0.86 (b) For the 10 wt% Al2O3-90 wt% SiO2 composition, the appropriate lever-rule expression is WL = Cmullite − C0 Cmullite − CL For a tie-line constructed across the Mullite (ss)-Liquid phase field at 1600°C Cmullite = 72 wt% Al2O3 CL = 8 wt% Al2O3 And, inasmuch as C0 = 10 wt% Al2O3 the mass fraction of liquid using the above lever-rule expression is WL = 72 − 10 72 − 8 = 0.97
- 731. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (c) For the 30 wt% Al2O3-70 wt% SiO2 composition, the appropriate lever-rule expression is WL = Cmullite − C0 Cmullite − CL For a tie-line constructed across the Mullite (ss)-Liquid phase field at 1600°C Cmullite = 72 wt% Al2O3 CL = 8 wt% Al2O3 And, inasmuch as C0 = 30 wt% Al2O3 the mass fraction of liquid using the above lever-rule expression is WL = 72 − 30 72 − 8 = 0.66 (d) For the 80 wt% Al2O3-20 wt% SiO2 composition at 1600°C, only alumina and mullite phases are present; thus WL = 0.
- 732. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.7 For the MgO–Al2O3 system, what is the maximum temperature that is possible without the formation of a liquid phase? At what composition or over what range of compositions will this maximum temperature be achieved? Solution This problem asks that we specify, for the MgO-Al2O3 system, Figure 12.25, the maximum temperature without the formation of a liquid phase; it is approximately 2800°C which is possible for pure MgO.
- 733. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Cements 13.8 Compare the manner in which the aggregate particles become bonded together in clay-based mixtures during firing and in cements during setting. Solution For clay-based aggregates, a liquid phase forms during firing, which infiltrates the pores between the unmelted particles; upon cooling, this liquid becomes a glass, that serves as the bonding phase. With cements, the bonding process is a chemical, hydration reaction between the water that has been added and the various cement constituents. The cement particles are bonded together by reactions that occur at the particle surfaces.
- 734. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Fabrication and Processing of Glasses and Glass-Ceramics 13.9 Soda and lime are added to a glass batch in the form of soda ash (Na2CO3) and limestone (CaCO3). During heating, these two ingredients decompose to give off carbon dioxide (CO2), the resulting products being soda and lime. Compute the weight of soda ash and limestone that must be added to 100 lbm of quartz (SiO2) to yield a glass of composition 75 wt% SiO2, 15 wt% Na2O, and 10 wt% CaO. Solution We are asked to compute the weight of soda ash and limestone that must be added to 100 lbm of SiO2 to yield a glass composition of 75 wt% SiO2, 15 wt% Na2O, and 10 wt% CaO. Let x equal the weight of Na2O and y equal the weight of CaO. Then, employment of a modified form Equation 4.3, we may write the following expressions for the concentrations of Na2O (CNa2O) and CaO (CCaO): CNa2O = 15 wt% = x 100 + x + y × 100 CCaO = 10 wt% = y 100 + x + y × 100 Solving for x and y from these two expressions yields x = 20.0 lbm Na2O and y = 13.3 lbm CaO. Now, in order to compute the weights of Na2CO3 and CaCO3, we must employ molecular weights. The molecular weights of Na2CO3 (MWNa2CO3 ) and Na2O (MWNa2O) are as follows: MWNa2CO3 = 2(ANa) + AC + 3(AO) = 2(22.99 g/mol) + 12.01 g/mol + 3(16.00g/mol) = 105.99 g/mol MWNa2O = 2(ANa) + AO = 2(22.99 g/mol) + 16.00 g/mol = 61.98 g/mol And, finally, the mass of Na2CO3 (mNa2CO3 ) is equal to mNa2CO3 = (20.0 lbm) MWNa2CO3 MWNa2O
- 735. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (20.0 lbm) 105.99 g/mol 61.98 g/mol = 34.2 lbm Likewise, the molecular weights of CaCO3 (MWCaCO3 ) and CaO (MWCaO) are as follows: MWCaCO3 = ACa + AC + 3(AO ) = 40.08 g/mol + 12.01 g/mol + (3)(16.00 g/mol) = 100.09 g/mol MWCaO = ACa + AO = 40.08 g/mol + 16.00 g/mol = 56.08 g/mol Such that the mass of CaCO3 (mCaCO3 ) is equal to mCaCO3 = (13.3 lbm) MWCaCO3 MWCaO = (13.3 lbm) 100.09 g/mol 56.08 g/mol = 23.7 lbm
- 736. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.10 What is the distinction between glass transition temperature and melting temperature? Solution The glass transition temperature is, for a noncrystalline ceramic, that temperature at which there is a change of slope for the specific volume versus temperature curve (Figure 13.6). The melting temperature is, for a crystalline material and upon cooling, that temperature at which there is a sudden and discontinuous decrease in the specific-volume-versus-temperature curve.
- 737. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.11 Compare the temperatures at which soda–lime, borosilicate, 96% silica, and fused silica may be annealed. Solution The annealing point is that temperature at which the viscosity of the glass is 1012 Pa-s (1013 P). From Figure 13.7, these temperatures for the several glasses are as follows: Glass Annealing Temperature Soda-lime 500°C (930°F) Borosilicate 565°C (1050°F) 96% Silica 930°C (1705°F) Fused silica 1170°C (2140°F)
- 738. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.12 Compare the softening points for 96% silica, borosilicate, and soda–lime glasses. Solution The softening point of a glass is that temperature at which the viscosity is 4 × 106 Pa-s; from Figure 13.7, these temperatures for the 96% silica, borosilicate, and soda-lime glasses are 1540°C (2800°F), 830°C (1525°F), and 700°C (1290°F), respectively.
- 739. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.13 The viscosity η of a glass varies with temperature according to the relationship η= A exp Qvis RT where Qvis is the energy of activation for viscous flow, A is a temperature-independent constant, and R and T are, respectively, the gas constant and the absolute temperature. A plot of ln η versus l/T should be nearly linear, and with a slope of Qvis/R. Using the data in Figure 13.7, (a) make such a plot for the borosilicate glass, and (b) determine the activation energy between temperatures of 500 and 900°C. Solution (a) Below is shown the logarithm viscosity versus reciprocal of temperature plot for the borosilicate glass, using the data in Figure 13.7. The dashed line has been drawn through the data points corresponding to temperatures between 500 and 900ºC (as stipulated in the problem statement). (b) The activation energy, Qvis, may be computed according to
- 740. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Qvis = R ∆ ln η ∆ 1 T = R ln η1 − ln η2 1 T1 − 1 T2 where R is the gas constant, and ∆ ln η ∆ 1 T is the slope of the dashed line that has been constructed. Taking 1/T1 and 1/T2 as 0.8 × 10-3 and 1.3 × 10-3 K-1, respectively, then the corresponding values of ln η1 and ln η2 are 10.59 and 32.50. Therefore, Qvis = R lnη1 − lnη2 1 T1 − 1 T2 = (8.31 J/mol− K) 10.59 − 32.50 0.8 × 10−3 K−1 − 1.3 × 10−3 K−1 = 364,000 J/mol
- 741. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.14 For many viscous materials, the viscosity η may be defined in terms of the expression η = σ dε/dt where σ and dε/dt are, respectively, the tensile stress and the strain rate. A cylindrical specimen of a soda-lime glass of diameter 5 mm (0.2 in.) and length 100 mm (4 in.) is subjected to a tensile force of 1 N (0.224 lbf) along its axis. If its deformation is to be less than 1 mm (0.04 in.) over a week’s time, using Figure 13.7, determine the maximum temperature to which the specimen may be heated. Solution This problem calls for us to determine the maximum temperature to which a cylindrical specimen of soda- lime glass may be heated in order that its deformation be less than 1 mm over a week's time. According to Equation 6.1 σ = F A0 = 1 N π 5 × 10−3 m 2 2 = 5.09 × 104 Pa Also, dε dt = d ∆l l0 dt = 1 mm/100 mm (1 wk)(7 days /week)(24 h /day)(3600 s /h) = 1.653 × 10-8 s-1 Thus, η = σ dε/dt = 5.09 × 104 Pa 1.653 × 10−8 s−1 = 3.1 × 1012 Pa- s From Figure 13.7, the temperature at which the viscosity of the soda-lime glass is 3.1 × 1012 Pa-s is about 500°C (930°F).
- 742. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.15 (a) Explain why residual thermal stresses are introduced into a glass piece when it is cooled. (b) Are thermal stresses introduced upon heating? Why or why not? Solution (a) Residual thermal stresses are introduced into a glass piece when it is cooled because surface and interior regions cool at different rates, and, therefore, contract different amounts; since the material will experience very little, if any deformation, stresses are established. (b) Yes, thermal stresses will be introduced because of thermal expansion upon heating for the same reason as for thermal contraction upon cooling.
- 743. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.16 Borosilicate glasses and fused silica are resistant to thermal shock. Why is this so? Solution Borosilicate glasses and fused silica are resistant to thermal shock because they have relatively low coefficients of thermal expansion; therefore, upon heating or cooling, the difference in the degree of expansion or contraction across a cross-section of a ware that is constructed from these materials will be relatively low.
- 744. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.17 In your own words, briefly describe what happens as a glass piece is thermally tempered. Thermal tempering of glasses is described in Section 13.9.
- 745. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.18 Glass pieces may also be strengthened by chemical tempering. With this procedure, the glass surface is put in a state of compression by exchanging some of the cations near the surface with other cations having a larger diameter. Suggest one type of cation that, by replacing Na+ , will induce chemical tempering in a soda–lime glass. Solution Chemical tempering will be accomplished by substitution, for Na+, another monovalent cation with a slightly larger diameter. From Table 12.3, both K+ and Cs+ fill these criteria, having ionic radii of 0.138 and 0.170 nm, respectively, which are larger than the ionic radius of Na+ (0.102 nm). In fact, soda-lime glasses are tempered by a K+-Na+ ion exchange.
- 746. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Fabrication and Processing of Clay Products 13.19 Cite the two desirable characteristics of clay minerals relative to fabrication processes. Solution Two desirable characteristics of clay minerals relative to fabrication processes are (1) they become hydroplastic (and therefore formable) when mixed with water; and (2) during firing, clays melt over a range of temperatures, which allows some fusion and bonding of the ware without complete melting and a loss of mechanical integrity and shape.
- 747. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.20 From a molecular perspective, briefly explain the mechanism by which clay minerals become hydroplastic when water is added. Solution Clays become hydroplastic when water is added because the water molecules occupy regions between the layered molecular sheets; these water molecules essentially eliminate the secondary molecular bonds between adjacent sheets, and also form a thin film around the clay particles. The net result is that the clay particles are relatively free to move past one another, which is manifested as the hydroplasticity phenomenon.
- 748. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.21 (a) What are the three main components of a whiteware ceramic such as porcelain? (b) What role does each component play in the forming and firing procedures? Solution (a) The three components of a whiteware ceramic are clay, quartz, and a flux. (b) With regard to the role that each component plays: Quartz acts as a filler material. Clay facilitates the forming operation since, when mixed with water, the mass may be made to become either hydroplastic or form a slip. Also, since clays melt over a range of temperatures, the shape of the piece being fired will be maintained. The flux facilitates the formation of a glass having a relatively low melting temperature.
- 749. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.22 (a) Why is it so important to control the rate of drying of a ceramic body that has been hydroplastically formed or slip cast? (b) Cite three factors that influence the rate of drying, and explain how each affects the rate. Solution (a) It is important to control the rate of drying inasmuch as if the rate of drying is too rapid, there will be nonuniform shrinkage between surface and interior regions, such that warping and/or cracking of the ceramic ware may result. (b) Three factors that affect the rate of drying are temperature, humidity, and rate of air flow. The rate of drying is enhanced by increasing both the temperature and rate of air flow, and by decreasing the humidity of the air.
- 750. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.23 Cite one reason why drying shrinkage is greater for slip cast or hydroplastic products that have smaller clay particles. Solution The reason that drying shrinkage is greater for products having smaller clay particles is because there is more particle surface area, and, consequently, more water will surround a given volume of particles. The drying shrinkage will thus be greater as this water is removed, and as the interparticle separation decreases.
- 751. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 13.24 (a) Name three factors that influence the degree to which vitrification occurs in clay-based ceramic wares. (b) Explain how density, firing distortion, strength, corrosion resistance, and thermal conductivity are affected by the extent of vitrification. Solution (a) Three factors that influence the degree to which vitrification occurs in clay-based ceramic wares are: (1) composition (especially the concentration of flux present); (2) the temperature of firing; and (3) the time at the firing temperature. (b) Density will increase with degree of vitrification since the total remaining pore volume decreases. Firing distortion will increase with degree of vitrification since more liquid phase will be present at the firing temperature. Strength will also increase with degree of vitrification inasmuch as more of the liquid phase forms, which fills in a greater fraction of pore volume. Upon cooling, the liquid forms a glass matrix of relatively high strength. Corrosion resistance normally increases also, especially at service temperatures below that at which the glass phase begins to soften. The rate of corrosion is dependent on the amount of surface area exposed to the corrosive medium; hence, decreasing the total surface area by filling in some of the surface pores, diminishes the corrosion rate. Thermal conductivity will increase with degree of vitrification. The glass phase has a higher conductivity than the pores that it has filled.
- 752. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Powder Pressing 13.25 Some ceramic materials are fabricated by hot isostatic pressing. Cite some of the limitations and difficulties associated with this technique. Solution The principal disadvantage of hot-isostatic pressing is that it is expensive. The pressure is applied on a pre-formed green piece by a gas. Thus, the process is slow, and the equipment required to supply the gas and withstand the elevated temperature and pressure is costly.
- 753. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. DESIGN PROBLEM 13.D1 Some of our modern kitchen cookware is made of ceramic materials. (a) List at least three important characteristics required of a material to be used for this application. (b) Make a comparison of three ceramic materials as to their relative properties and, in addition, to cost. (c) On the basis of this comparison, select the material most suitable for the cookware. Solution (a) Important characteristics that are required of a ceramic material to be used for kitchen cookware are: (1) it must have a high resistance to thermal shock (Section 19.5) in order to withstand relatively rapid changes in temperature; (2) it must have a relatively high thermal conductivity; 3) it must be relatively strong and tough in order to endure normal kitchen use; and 4) it must be nontoxic. (b) Possible materials worth considering are a common soda-lime glass, a borosilicate (Pyrex) glass, and a glass ceramic. These materials and some of their characteristics are discussed in this chapter. Using Equation 17.9 a comparison of the resistance to thermal shock may be made. The student will need to obtain cost information. (c) It is left to the student to make this determination and justify the decision.
- 754. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 14 POLYMER STRUCTURES PROBLEM SOLUTIONS Hydrocarbon Molecules Polymer Molecules The Chemistry of Polymer Molecules 14.1 On the basis of the structures presented in this chapter, sketch repeat unit structures for the following polymers: (a) polychlorotrifluoroethylene, and (b) poly(vinyl alcohol). Solution The repeat unit structures called for are sketched below. (a) Polychlorotrifluoroethylene (b) Poly(vinyl alcohol)
- 755. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Molecular Weight 14.2 Compute repeat unit molecular weights for the following: (a) poly(vinyl chloride), (b) poly(ethylene terephthalate), (c) polycarbonate, and (d) polydimethylsiloxane. Solution (a) For poly(vinyl chloride), each repeat unit consists of two carbons, three hydrogens, and one chlorine (Table 14.3). If AC, AH and ACl represent the atomic weights of carbon, hydrogen, and chlorine, respectively, then m = 2(AC) + 3(AH) + (ACl) = (2)(12.01 g/mol) + (3)(1.008 g/mol) + 35.45 g/mol = 62.49 g/mol (b) For poly(ethylene terephthalate), from Table 14.3, each repeat unit has ten carbons, eight hydrogens, and four oxygens. Thus, m = 10(AC) + 8(AH) + 4(AO) = (10)(12.01 g/mol) + (8)(1.008 g/mol) + (4)(16.00 g/mol) = 192.16 g/mol (c) For polycarbonate, from Table 14.3, each repeat unit has sixteen carbons, fourteen hydrogens, and three oxygens. Thus, m = 16(AC) + 14(AH) + 3(AO) = (16)(12.01 g/mol) + (14)(1.008 g/mol) + (3)(16.00 g/mol) = 254.27 g/mol (d) For polydimethylsiloxane, from Table 14.5, each repeat unit has two carbons, six hydrogens, one silicon and one oxygen. Thus, m = 2(AC) + 6(AH) + (ASi) + (AO) = (2)(12.01 g/mol) + (6)(1.008 g/mol) + (28.09 g/mol) + (16.00 g/mol) = 74.16 g/mol
- 756. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.3 The number-average molecular weight of a polypropylene is 1,000,000 g/mol. Compute the degree of polymerization. Solution We are asked to compute the degree of polymerization for polypropylene, given that the number-average molecular weight is 1,000,000 g/mol. The repeat unit molecular weight of polypropylene is just m = 3(AC) + 6(AH) = (3)(12.01 g/mol) + (6)(1.008 g/mol) = 42.08 g/mol Now it is possible to compute the degree of polymerization using Equation 14.6 as DP = Mn m = 1,000,000 g/mol 42.08 g/mol = 23,760
- 757. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.4 (a) Compute the repeat unit molecular weight of polystyrene. (b) Compute the number-average molecular weight for a polystyrene for which the degree of polymerization is 25,000. Solution (a) The repeat unit molecular weight of polystyrene is called for in this portion of the problem. For polystyrene, from Table 14.3, each repeat unit has eight carbons and eight hydrogens. Thus, m = 8(AC) + 8(AH) = (8)(12.01 g/mol) + (8)(1.008 g/mol) = 104.14 g/mol (b) We are now asked to compute the number-average molecular weight. Since the degree of polymerization is 25,000, using Equation 14.6 Mn = (DP)m = (25,000)(104.14 g/mol) = 2.60 × 106 g/mol
- 758. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.5 Below, molecular weight data for a polypropylene material are tabulated. Compute (a) the number- average molecular weight, (b) the weight-average molecular weight, and (c) the degree of polymerization. Molecular Weight Range (g/mol) xi wi 8,000–16,000 0.05 0.02 16,000–24,000 0.16 0.10 24,000–32,000 0.24 0.20 32,000–40,000 0.28 0.30 40,000–48,000 0.20 0.27 48,000–56,000 0.07 0.11 Solution (a) From the tabulated data, we are asked to compute Mn, the number-average molecular weight. This is carried out below. Molecular wt Range Mean Mi xi xiMi 8,000-16,000 12,000 0.05 600 16,000-24,000 20,000 0.16 3200 24,000-32,000 28,000 0.24 6720 32,000-40,000 36,000 0.28 10,080 40,000-48,000 44,000 0.20 8800 48,000-56,000 52,000 0.07 3640 ____________________________ Mn = xiMi∑ = 33,040 g/mol (b) From the tabulated data, we are asked to compute Mw, the weight-average molecular weight. Molecular wt. Range Mean Mi wi wiMi 8,000-16,000 12,000 0.02 240 16,000-24,000 20,000 0.10 2000 24,000-32,000 28,000 0.20 5600
- 759. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 32,000-40,000 36,000 0.30 10,800 40,000-48,000 44,000 0.27 11,880 48,000-56,000 52,000 0.11 5720 ___________________________ Mw = wiMi∑ = 36,240 g/mol (c) Now we are asked to compute the degree of polymerization, which is possible using Equation 14.6. For polypropylene, the repeat unit molecular weight is just m = 3(AC) + 6(AH) = (3)(12.01 g/mol) + (6)(1.008 g/mol) = 42.08 g/mol And DP = Mn m = 33,040 g/mol 42.08 g/mol = 785
- 760. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.6 Molecular weight data for some polymer are tabulated here. Compute (a) the number-average molecular weight, and (b) the weight-average molecular weight. (c) If it is known that this material's degree of polymerization is 710, which one of the polymers listed in Table 14.3 is this polymer? Why? Molecular Weight Range g/mol xi wi 15,000–30,000 0.04 0.01 30,000–45,000 0.07 0.04 45,000–60,000 0.16 0.11 60,000–75,000 0.26 0.24 75,000–90,000 0.24 0.27 90,000–105,000 0.12 0.16 105,000–120,000 0.08 0.12 120,000–135,000 0.03 0.05 Solution (a) From the tabulated data, we are asked to compute Mn, the number-average molecular weight. This is carried out below. Molecular wt. Range Mean Mi xi xiMi 15,000-30,000 22,500 0.04 900 30,000-45,000 37,500 0.07 2625 45,000-60,000 52,500 0.16 8400 60,000-75,000 67,500 0.26 17,550 75,000-90,000 82,500 0.24 19,800 90,000-105,000 97,500 0.12 11,700 105,000-120,000 112,500 0.08 9000 120,000-135,000 127,500 0.03 3825 _________________________ Mn = xiMi∑ = 73,800 g/mol
- 761. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (b) From the tabulated data, we are asked to compute Mw, the weight-average molecular weight. This determination is performed as follows: Molecular wt. Range Mean Mi wi wiMi 15,000-30,000 22,500 0.01 225 30,000-45,000 37,500 0.04 1500 45,000-60,000 52,500 0.11 5775 60,000-75,000 67,500 0.24 16,200 75,000-90,000 82,500 0.27 22,275 90,000-105,000 97,500 0.16 15,600 105,000-120,000 112,500 0.12 13,500 120,000-135,000 127,500 0.05 6375 _________________________ Mw = wiMi∑ = 81,450 g/mol (c) We are now asked if the degree of polymerization is 710, which of the polymers in Table 14.3 is this material? It is necessary to compute m in Equation 14.6 as m = Mn DP = 73,800 g/mol 710 = 103.94 g/mol The repeat unit molecular weights of the polymers listed in Table 14.3 are as follows: Polyethylene--28.05 g/mol Poly(vinyl chloride)--62.49 g/mol Polytetrafluoroethylene--100.02 g/mol Polypropylene--42.08 g/mol Polystyrene--104.14 g/mol Poly(methyl methacrylate)--100.11 g/mol Phenol-formaldehyde--133.16 g/mol Nylon 6,6--226.32 g/mol PET--192.16 g/mol Polycarbonate--254.27 g/mol Therefore, polystyrene is the material since its repeat unit molecular weight is closest to that calculated above.
- 762. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.7 Is it possible to have a poly(methyl methacrylate) homopolymer with the following molecular weight data and a of polymerization of 527? Why or why not? Molecular Weight Range (g/mol) wi xi 8,000–20,000 0.02 0.05 20,000–32,000 0.08 0.15 32,000–44,000 0.17 0.21 44,000–56,000 0.29 0.28 56,000–68,000 0.23 0.18 68,000–80,000 0.16 0.10 80,000–92,000 0.05 0.03 Solution This problem asks if it is possible to have a poly(methyl methacrylate) homopolymer with the given molecular weight data and a degree of polymerization of 527. The appropriate data are given below along with a computation of the number-average molecular weight. Molecular wt. Range Mean Mi xi xiMi 8,000-20,000 14,000 0.05 700 20,000-32,000 26,000 0.15 3900 32,000-44,000 38,000 0.21 7980 44,000-56,000 50,000 0.28 14,000 56,000-68,000 62,000 0.18 11,160 68,000-80,000 74,000 0.10 7400 80,000-92,000 86,000 0.03 2580 _________________________ Mn = xiMi∑ = 47,720 g/mol For PMMA, from Table 14.3, each repeat unit has five carbons, eight hydrogens, and two oxygens. Thus, m = 5(AC) + 8(AH) + 2(AO)
- 763. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (5)(12.01 g/mol) + (8)(1.008 g/mol) + (2)(16.00 g/mol) = 100.11 g/mol Now, we will compute the degree of polymerization using Equation 14.6 as DP = M n m = 47,720 g/mol 100.11 g/mol = 477 Thus, such a homopolymer is not possible since the calculated degree of polymerization is 477 (and not 527).
- 764. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.8 High-density polyethylene may be chlorinated by inducing the random substitution of chlorine atoms for hydrogen. (a) Determine the concentration of Cl (in wt%) that must be added if this substitution occurs for 5% of all the original hydrogen atoms. (b) In what ways does this chlorinated polyethylene differ from poly(vinyl chloride)? Solution (a) For chlorinated polyethylene, we are asked to determine the weight percent of chlorine added for 5% Cl substitution of all original hydrogen atoms. Consider 50 carbon atoms; there are 100 possible side-bonding sites. Ninety-five are occupied by hydrogen and five are occupied by Cl. Thus, the mass of these 50 carbon atoms, mC, is just mC = 50(AC) = (50)(12.01 g/mol) = 600.5 g Likewise, for hydrogen and chlorine, mH = 95(AH) = (95)(1.008 g/mol) = 95.76 g mCl = 5(ACl) = (5)(35.45 g/mol) = 177.25 g Thus, the concentration of chlorine, CCl, is determined using a modified form of Equation 4.3 as CCl = mCl mC + mH + mCl x 100 = 177.25 g 600.5 g + 95.76 g + 177.25 g × 100 = 20.3 wt% (b) Chlorinated polyethylene differs from poly(vinyl chloride), in that, for PVC, (1) 25% of the side- bonding sites are substituted with Cl, and (2) the substitution is probably much less random.
- 765. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Molecular Shape 14.9 For a linear polymer molecule, the total chain length L depends on the bond length between chain atoms d, the total number of bonds in the molecule N, and the angle between adjacent backbone chain atoms θ, as follows: L = Nd sin θ 2 (14.11) Furthermore, the average end-to-end distance for a series of polymer molecules r in Figure 14.6 is equal to r = d N (14.12) A linear polytetrafluoroethylene has a number-average molecular weight of 500,000 g/mol; compute average values of L and r for this material. Solution This problem first of all asks for us to calculate, using Equation 14.11, the average total chain length, L, for a linear polytetrafluoroethylene polymer having a number-average molecular weight of 500,000 g/mol. It is necessary to calculate the degree of polymerization, DP, using Equation 14.6. For polytetrafluoroethylene, from Table 14.3, each repeat unit has two carbons and four flourines. Thus, m = 2(AC) + 4(AF) = (2)(12.01 g/mol) + (4)(19.00 g/mol) = 100.02 g/mol and DP = Mn m = 500,000 g/mol 100.02 g/mol = 5000 which is the number of repeat units along an average chain. Since there are two carbon atoms per repeat unit, there are two C—C chain bonds per repeat unit, which means that the total number of chain bonds in the molecule, N, is just (2)(5000) = 10,000 bonds. Furthermore, assume that for single carbon-carbon bonds, d = 0.154 nm and θ = 109° (Section 14.4); therefore, from Equation 14.11 L = Nd sin θ 2
- 766. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (10,000)(0.154 nm) sin 109° 2 = 1254 nm It is now possible to calculate the average chain end-to-end distance, r, using Equation 14.12 as r = d N = (0.154 nm) 10,000 = 15.4 nm
- 767. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.10 Using the definitions for total chain molecule length, L (Equation 14.11) and average chain end-to- end distance r (Equation 14.12), for a linear polyethylene determine: (a) the number-average molecular weight for L = 2500 nm; (b) the number-average molecular weight for r = 20 nm. Solution (a) This portion of the problem asks for us to calculate the number-average molecular weight for a linear polyethylene for which L in Equation 14.11 is 2500 nm. It is first necessary to compute the value of N using this equation, where, for the C—C chain bond, d = 0.154 nm, and θ = 109°. Thus N = L d sin θ 2 = 2500 nm (0.154 nm) sin 109° 2 = 19,940 Since there are two C—C bonds per polyethylene repeat unit, there is an average of N/2 or 19,940/2 = 9970 repeat units per chain, which is also the degree of polymerization, DP. In order to compute the value of Mn using Equation 14.6, we must first determine m for polyethylene. Each polyethylene repeat unit consists of two carbon and four hydrogen atoms, thus m = 2(AC) + 4(AH) = (2)(12.01 g/mol) + (4)(1.008 g/mol) = 28.05 g/mol Therefore Mn = (DP)m = (9970)(28.05 g/mol) = 280,000 g/mol (b) Next, we are to determine the number-average molecular weight for r = 20 nm. Solving for N from Equation 14.12 leads to N = r2 d2 = (20 nm)2 (0.154 nm)2 = 16,900
- 768. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. which is the total number of bonds per average molecule. Since there are two C—C bonds per repeat unit, then DP = N/2 = 16,900/2 = 8450. Now, from Equation 14.6 Mn = (DP)m = (8450)(28.05 g/mol) = 237,000 g/mol
- 769. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Molecular Configurations 14.11 Sketch portions of a linear polystyrene molecule that are (a) syndiotactic, (b) atactic, and (c) isotactic. Use two-dimensional schematics per footnote 8 of this chapter. Solution We are asked to sketch portions of a linear polystyrene molecule for different configurations (using two- dimensional schematic sketches). (a) Syndiotactic polystyrene (b) Atactic polystyrene (c) Isotactic polystyrene
- 770. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.12 Sketch cis and trans structures for (a) butadiene, and (b) chloroprene. Use two-dimensional schematics per footnote 11 of this chapter. Solution This problem asks for us to sketch cis and trans structures for butadiene and chloroprene. (a) The structure for cis polybutadiene (Table 14.5) is The structure of trans butadiene is (b) The structure of cis chloroprene (Table 14.5) is The structure of trans chloroprene is
- 771. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Thermoplastic and Thermosetting Polymers 14.13 Make comparisons of thermoplastic and thermosetting polymers (a) on the basis of mechanical characteristics upon heating, and (b) according to possible molecular structures. Solution (a) Thermoplastic polymers soften when heated and harden when cooled, whereas thermosetting polymers, harden upon heating, while further heating will not lead to softening. (b) Thermoplastic polymers have linear and branched structures, while for thermosetting polymers, the structures will normally be network or crosslinked.
- 772. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.14 (a) Is it possible to grind up and reuse phenol-formaldehyde? Why or why not? (b) Is it possible to grind up and reuse polypropylene? Why or why not? Solution (a) It is not possible to grind up and reuse phenol-formaldehyde because it is a network thermoset polymer and, therefore, is not amenable to remolding. (b) Yes, it is possible to grind up and reuse polypropylene since it is a thermoplastic polymer, will soften when reheated, and, thus, may be remolded.
- 773. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Copolymers 14.15 Sketch the repeat structure for each of the following alternating copolymers: (a) poly(butadiene- chloroprene), (b) poly(styrene-methyl methacrylate), and (c) poly(acrylonitrile-vinyl chloride). Solution This problem asks for sketches of the repeat unit structures for several alternating copolymers. (a) For poly(butadiene-chloroprene) (b) For poly(styrene-methyl methacrylate) (c) For poly(acrylonitrile-vinyl chloride)
- 774. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.16 The number-average molecular weight of a poly(styrene-butadiene) alternating copolymer is 1,350,000 g/mol; determine the average number of styrene and butadiene repeat units per molecule. Solution Since it is an alternating copolymer, the number of both types of repeat units will be the same. Therefore, consider them as a single repeat unit, and determine the number-average degree of polymerization. For the styrene repeat unit, there are eight carbon atoms and eight hydrogen atoms, while the butadiene repeat consists of four carbon atoms and six hydrogen atoms. Therefore, the styrene-butadiene combined repeat unit weight is just m = 12(AC) + 14(AH) = (12)(12.01 g/mol) + (14)(1.008 g/mol) = 158.23 g/mol From Equation 14.6, the degree of polymerization is just DP = Mn m = 1,350,000 g/mol 158.23 g/mol = 8530 Thus, there is an average of 8530 of both repeat unit types per molecule.
- 775. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.17 Calculate the number-average molecular weight of a random nitrile rubber [poly(acrylonitrile- butadiene) copolymer] in which the fraction of butadiene repeat units is 0.30; assume that this concentration corresponds to a degree of polymerization of 2000. Solution This problem asks for us to calculate the number-average molecular weight of a random nitrile rubber copolymer. For the acrylonitrile repeat unit there are three carbon, one nitrogen, and three hydrogen atoms. Thus, its repeat unit molecular weight is mAc = 3(AC) + (AN) + 3(AH) = (3)(12.01 g/mol) + 14.01 g/mol + (3)(1.008 g/mol) = 53.06 g/mol The butadiene repeat unit is composed of four carbon and six hydrogen atoms. Thus, its repeat unit molecular weight is mBu = 4(AC) + 6(AH) = (4)(12.01 g/mol) + (6)(1.008 g/mol) = 54.09 g/mol From Equation 14.7, the average repeat unit molecular weight is just m = fAcmAc + fBumBu = (0.70)(53.06 g/mol) + (0.30)(54.09 g/mol) = 53.37 g/mol Since DP = 2000 (as stated in the problem), Mn may be computed using Equation 14.6 as Mn = m (DP) = (53.37 g/mol)(2000) = 106,740 g/mol
- 776. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.18 An alternating copolymer is known to have a number-average molecular weight of 250,000 g/mol and a degree of polymerization of 3420. If one of the repeat units is styrene, which of ethylene, propylene, tetrafluoroethylene, and vinyl chloride is the other repeat unit? Why? Solution For an alternating copolymer which has a number-average molecular weight of 250,000 g/mol and a degree of polymerization of 3420, we are to determine one of the repeat unit types if the other is styrene. It is first necessary to calculate m using Equation 14.6 as m = Mn DP = 250,000 g/mol 3420 = 73.10 g/mol Since this is an alternating copolymer we know that chain fraction of each repeat unit type is 0.5; that is fs = fx = 0.5, fs and fx being, respectively, the chain fractions of the styrene and unknown repeat units. Also, the repeat unit molecular weight for styrene is ms = 8(AC) + 8(AH) = 8(12.01 g/mol) + 8(1.008 g/mol) = 104.14 g/mol Now, using Equation 14.7, it is possible to calculate the repeat unit weight of the unknown repeat unit type, mx. Thus mx = m − fsms fx = 73.10 g/mol - (0.5)(104.14 g/mol) 0.5 = 42.06 g/mol Finally, it is necessary to calculate the repeat unit molecular weights for each of the possible other repeat unit types. These are calculated below: methylene = 2(AC) + 4(AH) = 2(12.01 g/mol) + 4(1.008 g/mol) = 28.05 g/mol mpropylene = 3(AC) + 6(AH) = 3(12.01 g/mol) + 6(1.008 g/mol) = 42.08 g/mol mTFE = 2(AC) + 4(AF) = 2(12.01 g/mol) + 4(19.00 g/mol) = 100.02 g/mol mVC = 2(AC) + 3(AH) + (ACl) = 2(12.01 g/mol) + 3(1.008 g/mol) + 35.45 g/mol = 62.49 g/mol Therefore, propylene is the other repeat unit type since its m value is almost the same as the calculated mx.
- 777. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.19 (a) Determine the ratio of butadiene to styrene repeat units in a copolymer having a number- average molecular weight of 350,000 g/mol and degree of polymerization of 4425. (b) Which type(s) of copolymer(s) will this copolymer be, considering the following possibilities: random, alternating, graft, and block? Why? Solution (a) This portion of the problem asks us to determine the ratio of butadiene to styrene repeat units in a copolymer having a weight-average molecular weight of 350,000 g/mol and a degree of polymerization of 4425. It first becomes necessary to calculate the average repeat unit molecular weight of the copolymer, m , using Equation 14.6 as m = Mn DP = 350,000 g/mol 4425 = 79.10 g/mol If we designate fb as the chain fraction of butadiene repeat units, since the copolymer consists of only two repeat unit types, the chain fraction of styrene repeat units fs is just 1 – fb. Now, Equation 14.7 for this copolymer may be written in the form m = fbmb + fsms = fbmb + (1 − fb)ms in which mb and ms are the repeat unit molecular weights for butadiene and styrene, respectively. These values are calculated as follows: mb = 4(AC) + 6(AH) = 4(12.01 g/mol) + 6(1.008 g/mol) = 54.09 g/mol ms = 8(AC) + 8(AH) = 8(12.01 g/mol) + 8(1.008 g/mol) = 104.14 g/mol Solving for fb in the above expression yields fb = m − ms mb − ms = 79.10 g/mol − 104.14 g/mol 54.09 g/mol − 104.14 g/mol = 0.50 Furthermore, fs = 1 – fb = 1 – 0.50 = 0.50; or the ratio is just
- 778. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. fb fs = 0.50 0.50 = 1.0 (b) Of the possible copolymers, the only one for which there is a restriction on the ratio of repeat unit types is alternating; the ratio must be 1:1. Therefore, on the basis of the result in part (a), the possibilities for this copolymer are not only alternating, but also random, graft, and block.
- 779. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.20 Crosslinked copolymers consisting of 60 wt% ethylene and 40 wt% propylene may have elastic properties similar to those for natural rubber. For a copolymer of this composition, determine the fraction of both repeat unit types. Solution For a copolymer consisting of 60 wt% ethylene and 40 wt% propylene, we are asked to determine the fraction of both repeat unit types. In 100 g of this material, there are 60 g of ethylene and 40 g of propylene. The ethylene (C2H4) molecular weight is m(ethylene) = 2(AC) + 4(AH) = (2)(12.01 g/mol) + (4)(1.008 g/mol) = 28.05 g/mol The propylene (C3H6) molecular weight is m(propylene) = 3(AC) + 6(AH) = (3)(12.01 g/mol) + (6)(1.008 g/mol) = 42.08 g/mol Therefore, in 100 g of this material, there are 60 g 28.05 g/mol = 2.14 mol of ethylene and 40 g 42.08 g/mol = 0.95 mol of propylene Thus, the fraction of the ethylene repeat unit, f(ethylene), is just f (ethylene) = 2.14 mol 2.14 mol + 0.95 mol = 0.69 Likewise,
- 780. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. f (propylene) = 0.95 mol 2.14 mol + 0.95 mol = 0.31
- 781. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.21 A random poly(isobutylene-isoprene) copolymer has a number-average molecular weight of 200,000 g/mol and a degree of polymerization of 3000. Compute the fraction of isobutylene and isoprene repeat units in this copolymer. Solution For a random poly(isobutylene-isoprene) copolymer in which Mn = 200,000 g/mol and DP = 3000, we are asked to compute the fractions of isobutylene and isoprene repeat units. From Table 14.5, the isobutylene repeat unit has four carbon and eight hydrogen atoms. Thus, mib = (4)(12.01 g/mol) + (8)(1.008 g/mol) = 56.10 g/mol Also, from Table 14.5, the isoprene repeat unit has five carbon and eight hydrogen atoms, and mip = (5)(12.01 g/mol) + (8)(1.008 g/mol) = 68.11 g/mol From Equation 14.7 m = fibmib + fipmip Now, let x = fib, such that m = 56.10x + (68.11)(1 − x) since fib + fip = 1. Also, from Equation 14.6 DP = Mn m Or 3000 = 200,000 g/mol [56.10 x + 68.11(1 − x)] g/mol Solving for x leads to x = fib = f(isobutylene) = 0.12. Also, f(isoprene) = 1 – x = 1 – 0.12 = 0.88
- 782. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Polymer Crystallinity 14.22 Explain briefly why the tendency of a polymer to crystallize decreases with increasing molecular weight. Solution The tendency of a polymer to crystallize decreases with increasing molecular weight because as the chains become longer it is more difficult for all regions along adjacent chains to align so as to produce the ordered atomic array.
- 783. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.23 For each of the following pairs of polymers, do the following: (1) state whether or not it is possible to determine whether one polymer is more likely to crystallize than the other; (2) if it is possible, note which is the more likely and then cite reason(s) for your choice; and (3) if it is not possible to decide, then state why. (a) Linear and syndiotactic poly(vinyl chloride); linear and isotactic polystyrene. (b) Network phenol-formaldehyde; linear and heavily crosslinked cis-isoprene. (c) Linear polyethylene; lightly branched isotactic polypropylene. (d) Alternating poly(styrene-ethylene) copolymer; random poly(vinyl chloride-tetrafluoroethylene) copolymer. Solution (a) Yes, for these two polymers it is possible to decide. The linear and syndiotactic poly(vinyl chloride) is more likely to crystallize; the phenyl side-group for polystyrene is bulkier than the Cl side-group for poly(vinyl chloride). Syndiotactic and isotactic isomers are equally likely to crystallize. (b) No, it is not possible to decide for these two polymers. Both heavily crosslinked and network polymers are not likely to crystallize. (c) Yes, it is possible to decide for these two polymers. The linear polyethylene is more likely to crystallize. The repeat unit structure for polypropylene is chemically more complicated than is the repeat unit structure for polyethylene. Furthermore, branched structures are less likely to crystallize than are linear structures. (d) Yes, it is possible to decide for these two copolymers. The alternating poly(styrene-ethylene) copolymer is more likely to crystallize. Alternating copolymers crystallize more easily than do random copolymers.
- 784. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.24 The density of totally crystalline polypropylene at room temperature is 0.946 g/cm3 . Also, at room temperature the unit cell for this material is monoclinic with lattice parameters a = 0.666 nm α = 90° b = 2.078 nm β = 99.62° c = 0.650 nm γ = 90° If the volume of a monoclinic unit cell, Vmono, is a function of these lattice parameters as Vmono = abc sin β determine the number of repeat units per unit cell. Solution For this problem we are given the density of polypropylene (0.946 g/cm3), an expression for the volume of its unit cell, and the lattice parameters, and are asked to determine the number of repeat units per unit cell. This computation necessitates the use of Equation 3.5, in which we solve for n. Before this can be carried out we must first calculate VC, the unit cell volume, and A the repeat unit molecular weight. For VC VC = abc sin β = (0.666 nm)(2.078 nm)(0.650 nm) sin (99.62°) = 0.8869 nm3 = 8.869 × 10-22 cm3 The repeat unit for polypropylene is shown in Table 14.3, from which the value of A may be determined as follows: A = 3(AC) + 6(AH) = 3(12.01 g/mol) + 6(1.008 g/mol) = 42.08 g/mol Finally, solving for n from Equation 3.5 leads to
- 785. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. n = ρVC NA A = (0.946 g/cm3)(8.869 × 10 -22 cm3/unit cell)(6.022 × 1023 repeat units/mol) 42.08 g/mol = 12.0 repeat unit/unit cell
- 786. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.25 The density and associated percent crystallinity for two polytetrafluoroethylene materials are as follows: ρ (g/cm3 ) crystallinity (%) 2.144 51.3 2.215 74.2 (a) Compute the densities of totally crystalline and totally amorphous polytetrafluoroethylene. (b) Determine the percent crystallinity of a specimen having a density of 2.26 g/cm3 . Solution (a) We are asked to compute the densities of totally crystalline and totally amorphous polytetrafluoroethylene (ρc and ρa from Equation 14.8). From Equation 14.8 let C = % crystallinity 100 , such that C = ρc (ρs − ρa) ρs (ρc − ρa) Rearrangement of this expression leads to ρc (C ρs − ρs) + ρcρa − Cρs ρa = 0 in which ρc and ρa are the variables for which solutions are to be found. Since two values of ρs and C are specified in the problem statement, two equations may be constructed as follows: ρc (C1 ρs1 − ρs1) + ρcρa − C1 ρs1 ρa = 0 ρc (C2 ρs2 − ρs2 ) + ρcρa − C2 ρs2 ρa = 0 In which ρs1 = 2.144 g/cm3, ρs2 = 2.215 g/cm3, C1 = 0.513, and C2 = 0.742. Solving the above two equations for ρa and ρc leads to ρa = ρs1 ρs2 (C1 − C2) C1 ρs1 − C2 ρs2
- 787. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (2.144 g/cm3)(2.215 g/cm3)(0.513 − 0.742) (0.513)(2.144 g/cm3) − (0.742)(2.215 g/cm3) = 2.000 g/cm3 And ρc = ρs1ρs2 (C2 − C1) ρs2 (C2 − 1) − ρs1 (C1 − 1) = (2.144 g/cm3)(2.215 g/cm3)(0.742 − 0.513) (2.215 g/cm3)(0.742 − 1) − (2.144 g/cm3)(0.513 − 1) = 2.301 g/cm3 (b) Now we are to determine the % crystallinity for ρs = 2.26 g/cm3. Again, using Equation 14.8 % crystallinity = ρc (ρs − ρa) ρs (ρc − ρa) × 100 = (2.301 g/cm3)(2.260 g/cm3 − 2.000 g/cm3) (2.260 g/cm3)(2.301 g/cm3 − 2.000 g/cm3) × 100 = 87.9%
- 788. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.26 The density and associated percent crystallinity for two nylon 6,6 materials are as follows: ρ (g/cm3 ) crystallinity (%) 1.188 67.3 1.152 43.7 (a) Compute the densities of totally crystalline and totally amorphous nylon 6,6. (b) Determine the density of a specimen having 55.4% crystallinity. Solution (a) We are asked to compute the densities of totally crystalline and totally amorphous nylon 6,6 (ρc and ρa from Equation 14.8). From Equation 14.8 let C = % crystallinity 100 , such that C = ρc (ρs − ρa) ρs (ρc − ρa) Rearrangement of this expression leads to ρc (C ρs − ρs) + ρcρa − C ρsρa = 0 in which ρc and ρa are the variables for which solutions are to be found. Since two values of ρs and C are specified in the problem, two equations may be constructed as follows: ρc (C1 ρs1 − ρs1) + ρcρa − C1ρs1ρa = 0 ρc (C2 ρs2 − ρs2) + ρcρa − C2ρs2ρa = 0 In which ρs1 = 1.188 g/cm3, ρs2 = 1.152 g/cm3, C1 = 0.673, and C2 = 0.437. Solving the above two equations for ρa and ρc leads to ρa = ρs1 ρs2 (C1 − C2) C1 ρs1 − C2 ρs2
- 789. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (1.188 g/cm3)(1.152 g/cm3)(0.673− 0.437) (0.673)(1.188 g/cm3)− (0.437)(1.152 g/cm3) = 1.091 g/cm3 And ρc = ρs1 ρs2 (C2 − C1) ρs2 (C2 − 1) − ρs1(C1 − 1) = (1.188 g/cm3)(1.152 g/cm3)(0.437− 0.673) (1.152 g/cm3)(0.437−1) − (1.188 g/cm3)(0.673−1) = 1.242 g/cm3 (b) Now we are asked to determine the density of a specimen having 55.4% crystallinity. Solving for ρs from Equation 14.8 and substitution for ρa and ρc which were computed in part (a) yields ρs = −ρc ρa C (ρc − ρa) − ρc = −(1.242 g/cm3)(1.091 g/cm3) (0.554)(1.242 g/cm3 − 1.091 g/cm3)− 1.242 g/cm3 = 1.170 g/cm3
- 790. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Diffusion in Polymeric Materials 14.27 Consider the diffusion of water vapor through a polypropylene (PP) sheet 2 mm thick. The pressures of H2O at the two faces are 1 kPa and 10 kPa, which are maintained constant. Assuming conditions of steady state, what is the diffusion flux [in [(cm3 STP)/cm2 -s] at 298 K? Solution This is a permeability problem in which we are asked to compute the diffusion flux of water vapor through a 2-mm thick sheet of polypropylene. In order to solve this problem it is necessary to employ Equation 14.9. The permeability coefficient of H2O through PP is given in Table 14.6 as 38 × 10-13 (cm3 STP)-cm/cm2-s-Pa. Thus, from Equation 14.9 J = PM ∆P ∆x = PM P2 − P1 ∆x and taking P1 = 1 kPa (1,000 Pa) and P2 = 10 kPa (10,000 Pa) we get = 38 × 10-13 (cm3 STP)(cm) cm2 - s - Pa 10,000 Pa −1,000 Pa 0.2 cm = 1.71 × 10-7 (cm3 STP) cm2 - s
- 791. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.28 Argon diffuses through a high density polyethylene (HDPE) sheet 40 mm thick at a rate of 4.0 × 10–7 (cm3 STP)/cm2 -s at 325 K. The pressures of argon at the two faces are 5000 kPa and 1500 kPa, which are maintained constant. Assuming conditions of steady state, what is the permeability coefficient at 325 K? Solution This problem asks us to compute the permeability coefficient for argon through high density polyethylene at 325 K given a steady-state permeability situation. It is necessary for us to Equation 14.9 in order to solve this problem. Rearranging this expression and solving for the permeability coefficient gives PM = J ∆x ∆P = J ∆x P2 − P1 Taking P1 = 1500 kPa (1,500,000 Pa) and P2 = 5000 kPa (5,000,000 Pa), the permeability coefficient of Ar through HDPE is equal to PM = 4.0 × 10-7 (cm3 STP) cm2 - s (4 cm) (5,000,000 Pa - 1,500,000 Pa) = 4.57 × 10-13 (cm3 STP)(cm) cm2 - s - Pa
- 792. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 14.29 The permeability coefficient of a type of small gas molecule in a polymer is dependent on absolute temperature according to the following equation: PM = PM 0 exp − Qp RT where PM0 and Qp are constants for a given gas-polymer pair. Consider the diffusion of hydrogen through a poly(dimethyl siloxane) (PDMSO) sheet 20 mm thick. The hydrogen pressures at the two faces are 10 kPa and 1 kPa, which are maintained constant. Compute the diffusion flux [in (cm3 STP)/cm2 –s] at 350 K. For this diffusion system PM0 = 1.45 × 10−8 (cm3 STP)(cm)/cm2 - s - Pa Qp = 13.7 kJ/mol Also, assume a condition of steady state diffusion Solution This problem asks that we compute the diffusion flux at 350 K for hydrogen in poly(dimethyl siloxane) (PDMSO). It is first necessary to compute the value of the permeability coefficient at 350 K. The temperature dependence of PM is given in the problem statement, as follows: PM = PM0 exp − Qp RT And, incorporating values provided for the constants PM0 and Qp, we get PM = 1.45 × 10-8 (cm3 STP)(cm) cm2 - s - Pa exp − 13,700 J/mol (8.31 J/mol- K)(350 K) = 1.31 × 10−10 (cm3 STP)(cm) cm2 - s - Pa And, using Equation 14.9, the diffusion flux is equal to J = PM ∆P ∆x = PM P2 − P1 ∆x = 1.31 × 10-10 (cm3 STP)(cm) cm2 - s - Pa 10,000 Pa -1,000 Pa 2.0 cm
- 793. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = 5.90 × 10-7 (cm3 STP) cm2 - s
- 794. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 15 CHARACTERISTICS, APPLICATIONS, AND PROCESSING OF POLYMERS PROBLEM SOLUTIONS Stress-Strain Behavior 15.1 From the stress–strain data for poly(methyl methacrylate) shown in Figure 15.3, determine the modulus of elasticity and tensile strength at room temperature [20°C (68°F)], and compare these values with those given in Table 15.1. Solution From Figure 15.3, the elastic modulus is the slope in the elastic linear region of the 20°C curve, which is E = ∆ (stress) ∆ (strain) = 30 MPa− 0 MPa 9 × 10−3 − 0 = 3.3 GPa (483,000 psi) The value range cited in Table 15.1 is 2.24 to 3.24 GPa (325,000 to 470,000 psi). Thus, the plotted value is a little on the high side. The tensile strength corresponds to the stress at which the curve ends, which is 52 MPa (7500 psi). This value lies within the range cited in Table 15.1—48.3 to 72.4 MPa (7000 to 10,500 psi).
- 795. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.2 Compute the elastic moduli for the following polymers, whose stress-strain behaviors may be observed in the “Tensile Tests” module of Virtual Materials Science and Engineering (VMSE): (a) high-density polyethylene, (b) nylon, and (c) phenol-formaldehyde (bakelite). How do these values compare with those presented in Table 15.1 for the same polymers? Solution The elastic modulus is the slope in the linear elastic region (Equation 6.10) as E = ∆σ ∆ε = σ2 − σ1 ε2 − ε1 Since all the stress-strain curves pass through the origin, we make take σ1 = 0 and ε1 = 0. Determinations of σ2 and ε2 are possible by moving the cursor to some arbitrary point in the linear region of the curve and then reading corresponding values in the “Stress” and “Strain” windows that are located below the plot. (a) For high-density polyethylene, we selected σ2 = 6.0 MPa with its corresponding ε2 = 0.0152. Therefore, E = σ2 − σ1 ε2 − ε1 = 6.0 MPa − 0 MPa 0.0152 − 0 = 395 MPa = 0.395 GPa The elastic modulus (average) for high-density polyethylene given in Table 15.1 is 1.08 GPa, which is significantly higher than this value. (b) For nylon, we selected σ2 = 24.3 MPa with its corresponding ε2 = 0.0085. Therefore, E = σ2 − σ1 ε2 − ε1 = 24.3 MPa − 0 MPa 0.0085 − 0 = 2860 MPa = 2.86 GPa The elastic modulus range for nylon 6,6 given in Table 15.1 is 1.58 GPa to 3.80 GPa; therefore, the value for the VMSE nylon lies within this range.
- 796. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (c) For phenol-formaldehyde (bakelite), we selected σ2 = 33.0 MPa with its corresponding ε2 = 0.0068. Therefore, E = σ2 − σ1 ε2 − ε1 = 33.0 MPa − 0 MPa 0.0068 − 0 = 4850 MPa = 4.85 GPa The elastic modulus range for the phenol-formaldehyde given in Table 15.1 is 2.76 GPa to 4.83 GPa; therefore, this value for the VMSE phenol-formaldehyde lies just above the maximum value for this range.
- 797. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.3 For the nylon polymer, whose stress strain behavior may be observed in the “Tensile Tests” module of Virtual Materials Science and Engineering (VMSE), determine the following: (a) the yield strength, and (b) the approximate ductility, in percent elongation. How do these values compare with those for the nylon material presented in Table 15.1? Solution (a) The yield strength corresponds to the first maximum (just beyond the initial linear-elastic region) of the stress-strain curve. This reading in the stress window located below the plot as the curser point is dragged along the stress-strain curve is 84 MPa. (b) The approximate percent elongation corresponds to the strain at fracture multiplied by 100 (i.e., 44.5%) minus the maximum elastic strain (i.e., value of strain at which the linearity of the curve ends multiplied by 100—in this case about 4%); this gives a value of about 40%EL. For nylon 6,6, the range of values of yield strength presented in Table 15.1 is 44.8 MPa to 82.8 MPa; therefore, the value for the VMSE nylon lies slightly above the upper value. The ductility range for nylon 6,6 is 15%EL to 300%EL; therefore, our value (40%EL) lies within this range.
- 798. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.4 For the phenol-formaldehyde (Bakelite) polymer, whose stress strain behavior may be observed in the “Tensile Tests” module of Virtual Materials Science and Engineering (VMSE), determine the following: (a) the tensile strength, and (b) the approximate ductility, in percent elongation. How do these values compare with those for the phenol-formaldehyde material presented in Table 15.1? Solution (a) The tensile strength corresponds to the stress at which fracture occurs. This reading in the stress window located below the plot as the curser point is dragged along the stress-strain curve is 52 MPa. (b) The approximate percent elongation corresponds to the strain at fracture multiplied by 100 (i.e., 1.29%) minus the maximum elastic strain (i.e., value of strain at which the linearity of the curve ends multiplied by 100—in this case about 1%); this gives a value of about 0.3%EL. For phenol-formaldehyde, the range of values of tensile strength presented in Table 15.1 is 34.5 MPa to 62.1 MPa; therefore, the value for the VMSE material (52 MPa) lies within this range. The ductility range for phenol-formaldehyde is 1.5%EL to 2.0%EL; therefore, our value (0.3%EL) lies below the lower limit.
- 799. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Viscoelastic Deformation 15.5 In your own words, briefly describe the phenomenon of viscoelasticity. The explanation of viscoelasticity is given in Section 15.4.
- 800. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.6 For some viscoelastic polymers that are subjected to stress relaxation tests, the stress decays with time according to σ(t) = σ(0) exp − t τ (15.10) where σ(t) and σ(0) represent the time-dependent and initial (i.e., time = 0) stresses, respectively, and t and τ denote elapsed time and the relaxation time; τ is a time-independent constant characteristic of the material. A specimen of some viscoelastic polymer the stress relaxation of which obeys Equation 15.10 was suddenly pulled in tension to a measured strain of 0.6; the stress necessary to maintain this constant strain was measured as a function of time. Determine Er(10) for this material if the initial stress level was 2.76 MPa (400 psi), which dropped to 1.72 MPa (250 psi) after 60 s. Solution This problem asks for a determination of the relaxation modulus of a viscoelastic material, which behavior is according to Equation 15.10--i.e., σ(t) = σ(0) exp − t τ We want to determine σ(10), but it is first necessary to compute τ from the data provided in the problem statement. Thus, solving for τ from the above expression, τ = − t ln σ(t) σ(0) = − 60 s ln 1.72 MPa 2.76 MPa = 127 s Therefore, σ(10) = (2.76 MPa) exp − 10 s 127 s = 2.55 MPa Now, using Equation 15.1 Er (10) = σ (10) ε0 = 2.55 MPa 0.6 = 4.25 MPa (616 psi)
- 801. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.7 In Figure 15.28, the logarithm of Er(t) versus the logarithm of time is plotted for polyisobutylene at a variety of temperatures. Make a plot of Er(10) versus temperature and then estimate its Tg. Solution Below is plotted the logarithm of Er(10) versus temperature. The glass-transition temperature is that temperature corresponding to the abrupt decrease in log Er(10), which for this polyisobutylene material is about -60°C.
- 802. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.8 On the basis of the curves in Figure 15.5, sketch schematic strain–time plots for the following polystyrene materials at the specified temperatures: (a) Amorphous at 120°C (b) Crosslinked at 150°C (c) Crystalline at 230°C (d) Crosslinked at 50°C Solution (a) Amorphous polystyrene at 120°C behaves a rubbery material (Figure 15.8, curve C); therefore, the strain-time behavior would be as Figure 15.5c. (b) Crosslinked polystyrene at 150°C behaves as a viscoelastic material (Figure 15.8, curve B); therefore, the strain-time behavior will be as Figure 15.5c. (c) Crystalline polystyrene at 230°C behaves as a viscous liquid (Figure 15.8, curve A); therefore, the strain-time behavior will be as Figure 15.5d. (d) Crosslinked polystyrene at 50°C behaves in a glassy manner (Figure 15.8, curve B); therefore, the strain-time behavior will be as Figure 15.5b.
- 803. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.9 (a) Contrast the manner in which stress relaxation and viscoelastic creep tests are conducted. (b) For each of these tests, cite the experimental parameter of interest and how it is determined. Solution (a) Stress relaxation tests are conducted by rapidly straining the material elastically in tension, holding the strain level constant, and then measuring the stress as a function of time. For viscoelastic creep tests, a stress (usually tensile) is applied instantaneously and maintained constant while strain is measured as a function of time. (b) The experimental parameters of interest from the stress relaxation and viscoelastic creep tests are the relaxation modulus and creep modulus (or creep compliance), respectively. The relaxation modulus is the ratio of stress measured after 10 s and strain (Equation 15.1); creep modulus is the ratio of stress and strain taken at a specific time (Equation 15.2).
- 804. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.10 Make two schematic plots of the logarithm of relaxation modulus versus temperature for an amorphous polymer (curve C in Figure 15.8). (a) On one of these plots demonstrate how the behavior changes with increasing molecular weight. (b) On the other plot, indicate the change in behavior with increasing crosslinking. Solution (a) This portion of the problem calls for a plot of log Er(10) versus temperature demonstrating how the behavior changes with increased molecular weight. Such a plot is given below. Increasing molecular weight increases both glass-transition and melting temperatures. (b) We are now called upon to make a plot of log Er(10) versus temperature demonstrating how the behavior changes with increased crosslinking. Such a plot is given below. Increasing the degree of crosslinking will increase the modulus in both glassy and rubbery regions.
- 805. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful.
- 806. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Fracture of Polymers Miscellaneous Mechanical Considerations 15.11 For thermoplastic polymers, cite five factors that favor brittle fracture. Solution For thermoplastic polymers, five factors that favor brittle fracture are as follows: (1) a reduction in temperature, (2) an increase in strain rate, (3) the presence of a sharp notch, (4) increased specimen thickness, and (5) modifications of the polymer structure.
- 807. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.12 (a) Compare the fatigue limits for polystyrene (Figure 15.11) and the cast iron for which fatigue data are given in Problem 8.20. (b) Compare the fatigue strengths at 106 cycles for poly(ethylene terephthalate) (PET, Figure 15.11) and red brass (Figure 8.34). Solution (a) The fatigue limits for polystyrene and the cast iron are 10.5 MPa (1500 psi) and 193 MPa (28,000 psi), respectively. (b) At 106 cycles, the fatigue strengths of PET and red brass are 15 MPa (2175 psi) and 115 MPa (16,700 psi ), respectively.
- 808. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Deformation of Semicrystalline Polymers 15.13 In your own words, describe the mechanisms by which semicrystalline polymers (a) elastically deform and (b) plastically deform, and (c) by which elastomers elastically deform. (a) and (b) The mechanisms by which semicrystalline polymers elastically and plastically deform are described in Section 15.7. (c) The explanation of the mechanism by which elastomers elastically deform is provided in Section 15.9.
- 809. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Factors That Influence the Mechanical Properties of Semicrystalline Polymers Deformation of Elastomers 15.14 Briefly explain how each of the following influences the tensile modulus of a semicrystalline polymer and why: (a) Molecular weight (b) Degree of crystallinity (c) Deformation by drawing (d) Annealing of an undeformed material (f) Annealing of a drawn material Solution (a) The tensile modulus is not directly influenced by a polymer's molecular weight. (b) Tensile modulus increases with increasing degree of crystallinity for semicrystalline polymers. This is due to enhanced secondary interchain bonding which results from adjacent aligned chain segments as percent crystallinity increases. This enhanced interchain bonding inhibits relative interchain motion. (c) Deformation by drawing also increases the tensile modulus. The reason for this is that drawing produces a highly oriented molecular structure, and a relatively high degree of interchain secondary bonding. (d) When an undeformed semicrystalline polymer is annealed below its melting temperature, the tensile modulus increases. (e) A drawn semicrystalline polymer that is annealed experiences a decrease in tensile modulus as a result of a reduction in chain-induced crystallinity, and a reduction in interchain bonding forces.
- 810. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.15 Briefly explain how each of the following influences the tensile or yield strength of a semicrystalline polymer and why: (a) Molecular weight (b) Degree of crystallinity (c) Deformation by drawing (d) Annealing of an undeformed material Solution (a) The tensile strength of a semicrystalline polymer increases with increasing molecular weight. This effect is explained by increased chain entanglements at higher molecular weights. (b) Increasing the degree of crystallinity of a semicrystalline polymer leads to an enhancement of the tensile strength. Again, this is due to enhanced interchain bonding and forces; in response to applied stresses, interchain motions are thus inhibited. (c) Deformation by drawing increases the tensile strength of a semicrystalline polymer. This effect is due to the highly oriented chain structure that is produced by drawing, which gives rise to higher interchain secondary bonding forces. (d) Annealing an undeformed semicrystalline polymer produces an increase in its tensile strength.
- 811. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.16 Normal butane and isobutane have boiling temperatures of –0.5 and –12.3°C (31.1 and 9.9°F), respectively. Briefly explain this behavior on the basis of their molecular structures, as presented in Section 14.2. Solution Normal butane has a higher melting temperature as a result of its molecular structure (Section 14.2). There is more of an opportunity for van der Waals bonds to form between two molecules in close proximity to one another than for isobutane because of the linear nature of each normal butane molecule.
- 812. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.17 The tensile strength and number-average molecular weight for two poly(methyl methacrylate) materials are as follows: Tensile Strength (MPa) Number-Average Molecular Weight (g/mol) 107 40,000 170 60,000 Estimate the tensile strength at a number-average molecular weight of 30,000 g/mol. Solution This problem gives us the tensile strengths and associated number-average molecular weights for two poly(methyl methacrylate) materials and then asks that we estimate the tensile strength for Mn = 30,000 g/mol. Equation 15.3 cites the dependence of the tensile strength on Mn. Thus, using the data provided in the problem statement, we may set up two simultaneous equations from which it is possible to solve for the two constants TS∞ and A. These equations are as follows: 107 MPa = TS∞ − A 40,000 g /mol 170 MPa = TS∞ − A 60,000 g /mol Thus, the values of the two constants are: TS∞ = 296 MPa and A = 7.56 × 106 MPa-g/mol. Substituting these values into Equation 15.3 for Mn = 30,000 g/mol leads to TS = TS∞ − A 30,000 g /mol = 296 MPa − 7.56 × 106 MPa - g/mol 30,000 g/mol = 44 MPa
- 813. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.18 The tensile strength and number-average molecular weight for two polyethylene materials are as follows: Tensile Strength (MPa) Number-Average Molecular Weight (g/mol) 85 12,700 150 28,500 Estimate the number-average molecular weight that is required to give a tensile strength of 195 MPa. Solution This problem gives us the tensile strengths and associated number-average molecular weights for two polyethylene materials and then asks that we estimate the Mn that is required for a tensile strength of 195 MPa. Equation 15.3 cites the dependence of the tensile strength on Mn. Thus, using the data provided in the problem statement, we may set up two simultaneous equations from which it is possible to solve for the two constants TS∞ and A. These equations are as follows: 85 MPa = TS∞ − A 12,700 g /mol 150 MPa = TS∞ − A 28,500 g/mol Thus, the values of the two constants are: TS∞ = 202 MPa and A = 1.489 × 106 MPa-g/mol. Solving for Mn in Equation 15.3 and substituting TS = 195 MPa as well as the above values for TS∞ and A leads to Mn = A TS∞ − TS = 1.489 × 106 MPa- g /mol 202 MPa − 195 MPa = 213,000 g/mol
- 814. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.19 For each of the following pairs of polymers, do the following: (1) state whether or not it is possible to decide whether one polymer has a higher tensile modulus than the other; (2) if this is possible, note which has the higher tensile modulus and then cite the reason(s) for your choice; and (3) if it is not possible to decide, then state why. (a) Random acrylonitrile-butadiene copolymer with 10% of possible sites crosslinked; alternating acrylonitrile-butadiene copolymer with 5% of possible sites crosslinked (b) Branched and syndiotactic polypropylene with a degree of polymerization of 5000; linear and isotactic polypropylene with a degree of polymerization of 3000 (c) Branched polyethylene with a number-average molecular weight of 250,000 g/mol; linear and isotactic poly(vinyl chloride) with a number-average molecular weight of 200,000 g/mol Solution For each of four pairs of polymers, we are to do the following: (1) determine whether or not it is possible to decide which has the higher tensile modulus; (2) if so, note which has the higher tensile modulus and then state the reasons for this choice; and (3) if it is not possible to decide, then state why. (a) No, it is not possible. The random acrylonitrile-butadiene copolymer will tend to a lower degree of crystallinity than the alternating acrylonitrile-butadiene copolymer inasmuch as random copolymers don’t normally crystallize. On this basis only, the alternating material would have a higher modulus inasmuch as tensile modulus increases with degree of crystallinity. On the other hand, the random copolymer has a higher degree of crosslinking (10% versus 5% for the alternating copolymer), and, on this basis only would have the higher tensile modulus—an increase in crosslinking leads to an increase in E. Thus, this determination is not possible; with regard to degree of crystallinity the alternating material has the higher E, whereas the random copolymer would have a higher E value on the basis of degree of crosslinking. (b) Yes, it is possible. The linear and isotactic polypropylene will have a greater tensile modulus. Linear polymers are more likely to crystallize that branched ones. The likelihood of crystallization for both syndiotactic and isotactic polypropylene is about the same, and, therefore, degree is crystallization is not a factor. Furthermore, tensile modulus is relatively insensitive to degree of polymerization (i.e., molecular weight)—the fact that branched PP has the higher molecular weight is not important. (c) No, it is not possible. Linear polymers have higher degrees of crystallization (and higher tensile moduli) than branched polymers—on this basis, the PVC material should have the higher value of E. On the other hand, PVC has a more complex repeat unit structure than does polyethylene, which means that, on this basis, the PE would have a higher degree of crystallinity and also a greater tensile modulus. Also, tensile modulus is relatively independent of number-average molecular weight. Therefore, this determination is not possible since it is not possible to determine which of the two materials has the greater degree of crystallinity.
- 815. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.20 For each of the following pairs of polymers, do the following: (1) state whether or not it is possible to decide whether one polymer has a higher tensile strength than the other; (2) if this is possible, note which has the higher tensile strength and then cite the reason(s) for your choice; and (3) if it is not possible to decide, then state why. (a) Syndiotactic polystyrene having a number-average molecular weight of 600,000 g/mol; atactic polystyrene having a number-average molecular weight of 500,000 g/mol (b) Random acrylonitrile-butadiene copolymer with 10% of possible sites crosslinked; block acrylonitrile- butadiene copolymer with 5% of possible sites crosslinked (c) Network polyester; lightly branched polypropylene Solution For each of three pairs of polymers, we are to do the following: (1) determine whether or not it is possible to decide which has the higher tensile strength; (2) if it is possible, then note which has the higher tensile strength and then state the reasons for this choice; and (3) if it is not possible to decide, to state why. (a) Yes it is possible. The syndiotactic polystyrene has the higher tensile strength. Syndiotactic polymers are more likely to crystallize than atactic ones; the greater the crystallinity, the higher the tensile strength. Furthermore, the syndiotactic also has a higher molecular weight; increasing molecular weight also enhances the strength. (b) No it is not possible. The random acrylonitrile-butadiene copolymer has more crosslinking; increased crosslinking leads to an increase in strength. However, the block copolymeric material will most likely have a higher degree of crystallinity; and increasing crystallinity improves the strength. (c) Yes it is possible. The network polyester will display a greater tensile strength. Relative chain motion is much more restricted than for the lightly branched polypropylene since there are many more of the strong covalent bonds for the network structure.
- 816. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.21 Would you expect the tensile strength of polychlorotrifluoroethylene to be greater than, the same as, or less than that of a polytetrafluoroethylene specimen having the same molecular weight and degree of crystallinity? Why? Solution The strength of a polychlorotrifluoroethylene having the repeat unit structure will be greater than for a polytetrafluoroethylene having the same molecular weight and degree of crystallinity. The replacement of one fluorine atom within the PTFE repeat unit with a chlorine atom leads to a higher interchain attraction, and, thus, a stronger polymer. Furthermore, poly(vinyl chloride) is stronger than polyethylene (Table 15.1) for the same reason.
- 817. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.22 For each of the following pairs of polymers, plot and label schematic stress–strain curves on the same graph [i.e., make separate plots for parts (a), (b), and (c)]. (a) Isotactic and linear polypropylene having a weight-average molecular weight of 120,000 g/mol; atactic and linear polypropylene having a weight-average molecular weight of 100,000 g/mol (b) Branched poly(vinyl chloride) having a degree of polymerization of 2000; heavily crosslinked poly(vinyl chloride) having a degree of polymerization of 2000 (c) Poly(styrene-butadiene) random copolymer having a number-average molecular weight of 100,000 g/mol and 10% of the available sites crosslinked and tested at 20°C; poly(styrene-butadiene) random copolymer having a number-average molecular weight of 120,000 g/mol and 15% of the available sites crosslinked and tested at -85°C. Hint: poly(styrene-butadiene) copolymers may exhibit elastomeric behavior. Solution (a) Shown below are the stress-strain curves for the two polypropylene materials. These materials will display the stress-strain behavior of a normal plastic, curve B in Figure 15.1. However, the isotactic/linear will have a higher degree of crystallinity (since isotactic are more likely to crystallize than atactic/linear), and therefore, will have a higher tensile modulus and strength. Furthermore, the isotactic/linear also has a higher molecular weight which also leads to an increase in strength. (b) Shown below are the stress-strain curves for the two polyvinyl chloride materials. The branched PVC will probably display the stress-strain behavior of a plastic, curve B in Figure 15.1. However, the heavily crosslinked PVC will undoubtedly have a higher tensile modulus, and, also a higher strength, and will most likely fail in a brittle manner--as curve A, Figure 15.1; these are the typical characteristics of a heavily crosslinked polymer.
- 818. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (c) Shown below are the stress-strain curves for the two poly(styrene-butadiene) random copolymers. The copolymer tested at 20°C will display elastomeric behavior (curve C of Figure 15.1) inasmuch as it is a random copolymer that is lightly crosslinked; furthermore, the temperature of testing is above its glass transition temperature. On the other hand, since -85°C is below the glass transition temperature of the poly(styrene- butadiene) copolymer, the stress-strain behavior under these conditions is as curve A of Figure 15.1.
- 819. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.23 List the two molecular characteristics that are essential for elastomers. Solution Two molecular characteristics essential for elastomers are: (1) they must be amorphous, having chains that are extensively coiled and kinked in the unstressed state; and (2) there must be some crosslinking.
- 820. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.24 Which of the following would you expect to be elastomers and which thermosetting polymers at room temperature? Justify each choice. (a) Epoxy having a network structure (b) Lightly crosslinked poly(styrene-butadiene) random copolymer that has a glass-transition temperature of -50°C (c) Lightly branched and semicrystalline polytetrafluoroethylene that has a glass-transition temperature of -100°C (d) Heavily crosslinked poly(ethylene-propylene) random copolymer that has a glass-transition temperature of 0°C (e) Thermoplastic elastomer that has a glass-transition temperature of 75°C Solution This question asks us to choose from a list of materials those that would be expected to be elastomers and those that would be thermosetting polymers. (a) Epoxy having a network structure will be a thermoset polymer since it has a network structure. It would not be an elastomer since it does not have a crosslinked chain structure. (b) A lightly crosslinked poly(styrene-butadiene) random copolymer that has a glass-transition temperature of -50°C will be an elastomer since it 1) is a random copolymer, 2) is lightly crosslinked, and 3) is being used at a temperature above its glass transition. All three of these criteria are requisites for an elastomer. (c) Lightly branched and semicrystalline PTFE would be neither an elastomer nor a thermoset. It is not crosslinked nor does it have a network structure. (d) A heavily crosslinked poly(ethylene-propylene) random copolymer would be a thermoset inasmuch as it is heavily crosslinked. (e) A thermoplastic elastomer that has a glass-transition temperature of 75°C is neither an elastomer nor a thermoset. Since it is a thermoplastic it is not a thermoset. Furthermore, room temperature is below its glass- transition temperature, and, therefore, it will not display elastomeric behavior.
- 821. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.25 Ten kilogram of polybutadiene is vulcanized with 4.8 kg sulfur. What fraction of the possible crosslink sites is bonded to sulfur crosslinks, assuming that, on the average, 4.5 sulfur atoms participate in each crosslink? Solution This problem asks that we compute the fraction of possible crosslink sites in 10 kg of polybutadiene when 4.8 kg of S is added, assuming that, on the average, 4.5 sulfur atoms participate in each crosslink bond. Given the butadiene repeat unit in Table 14.5, we may calculate its molecular weight as follows: A(butadiene) = 4(AC ) + 6(AH ) = (4)(12.01 g/mol) + 6(1.008 g/mol) = 54.09 g/mol Which means that in 10 kg of butadiene there are 10,000 g 54.09 g/mol = 184.9 mol = nbuta. For the vulcanization polybutadiene, there are two possible crosslink sites per repeat unit--one for each of the two carbon atoms that are doubly bonded. Furthermore, each of these crosslinks forms a bridge between two repeat units. Therefore, we can say that there is the equivalent of one crosslink per repeat unit. Let us now calculate the number of moles of sulfur (nsulfur ) that react with the butadiene, by taking the mole ratio of sulfur to butadiene, and then dividing this ratio by 4.5 atoms per crosslink; this yields the fraction of possible sites that are crosslinked. Thus nsulfur = 4800 g 32.06 g /mol = 149.7 mol And fraction sites crosslinked = nsulfur nbuta 4.5 = 149.7 mol 184.9 mol 4.5 = 0.180
- 822. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.26 Compute the weight percent sulfur that must be added to completely crosslink an alternating chloroprene-acrylonitrile copolymer, assuming that five sulfur atoms participate in each crosslink. Solution For an alternating chloroprene-acrylonitrile copolymer, we are asked to compute the weight percent sulfur necessary for complete crosslinking, assuming that, on the average, five sulfur atoms participate in each crosslink. The chloroprene and acrylonitrile repeat units are shown in Table 14.5, from which it may be noted that there are two possible crosslink sites on each chloroprene repeat unit (one site at each of the two carbon atoms that are doubly bonded), and no possible sites for acrylonitrile; also, since it is an alternating copolymer, the ratio of chloroprene to acrylonitrile repeat units is 1:1. Thus, for each pair of combined chloroprene-acrylonitrile repeat units that crosslink, ten sulfur atoms are required, or, for complete crosslinking, the sulfur-to-(chloroprene- acrylonitrile) ratio is 5:1. Now, let us consider as our basis, one mole of the combined chloroprene-acrylonitrile repeat unit. In order for complete crosslinking, five moles of sulfur are required. Thus, for us to convert this composition to weight percent, it is necessary to convert moles to mass. The acrylonitrile repeat unit consists of three carbon atoms, three hydrogen atoms, and one nitrogen atom; the chloroprene repeat unit is composed of four carbons, five hydrogens, and one chlorine. This gives a molecular weight for the combined repeat unit of m(chloroprene-acrylonitrile) = 3(A C ) + 3(AH ) + AN + 4(AC ) + 5(AH ) + ACl = 7(12.01 g/mol) + 8(1.008 g/mol) + 14.007 g/mol + 35.45 g/mol = 141.59 g/mol Or, in one mole of this combined repeat unit, there are 141.59 g. Furthermore, for complete crosslinking 5.0 mol of sulfur is required, which amounts to (5.0 mol)(32.06 g/mol) = 160.3 g. Thus, the concentration of S in weight percent CS is just CS = 160.3 g 160.3 g + 141.59 g × 100 = 53.1 wt%
- 823. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.27 The vulcanization of polyisoprene is accomplished with sulfur atoms according to Equation 15.4. If 57 wt% sulfur is combined with polyisoprene, how many crosslinks will be associated with each isoprene repeat unit if it is assumed that, on the average, six sulfur atoms participate in each crosslink? Solution This problem asks for us to determine how many crosslinks form per isoprene repeat unit when 57 wt% sulfur is added. If we arbitrarily consider 100 g of the vulcanized material, 57 g will be sulfur and 43 g will be polyisoprene. Next, let us find how many moles of sulfur and isoprene correspond to these masses. The atomic weight of sulfur is 32.06 g/mol, and thus, # moles S = 57 g 32.06 g /mol = 1.78 mol Now, in each isoprene repeat unit there are five carbon atoms and eight hydrogen atoms. Thus, the molecular weight of a mole of isoprene units is (5)(12.01 g/mol) + (8)(1.008 g/mol) = 68.11 g/mol Or, in 43 g of polyisoprene, the number of moles is equal to # moles isoprene = 43 g 68.11 g /mol = 0.631 mol Therefore, the ratio of moles of S to the number of moles of polyisoprene is 1.78 mol 0.631 mol :1 = 2.82 :1 When all possible sites are crosslinked, the ratio of the number of moles of sulfur to the number of moles of isoprene is 6:1; this is because there are two crosslink sites per repeat unit and each crosslink is shared between repeat units on adjacent chains, and there are 6 sulfur atoms per crosslink. Finally, to determine the fraction of sites that are crosslinked, we just divide the actual crosslinked sulfur/isoprene ratio by the completely crosslinked ratio. Or, fraction of repeat unit sites crosslinked = 2.82 /1 6 /1 = 0.470
- 824. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.28 For the vulcanization of polyisoprene, compute the weight percent of sulfur that must be added to ensure that 8% of possible sites will be crosslinked; assume that, on the average, three sulfur atoms are associated with each crosslink. Solution We are asked what weight percent of sulfur must be added to polyisoprene in order to ensure that 8% of possible sites are crosslinked, assuming that, on the average, three sulfur atoms are associated with each crosslink. Table 14.5 shows the repeat unit for cis-isoprene. For each of these units there are two possible crosslink sites; one site is associated with each of the two carbon atoms that are involved in the chain double bond. Since 8% of the possible sites are crosslinked, for each 100 isoprene repeat units 8 of them are crosslinked; actually there are two crosslink sites per repeat unit, but each crosslink is shared by two chains. Furthermore, on the average we assume that each crosslink is composed of 3 sulfur atoms; thus, there must be 3 × 8 or 24 sulfur atoms added for every 100 isoprene repeat units. In terms of moles, it is necessary to add 24 moles of sulfur to 100 moles of isoprene. The atomic weight of sulfur is 32.06 g/mol, while the molecular weight of isoprene is A(isoprene) = 5(A C ) + 8(AH ) = (5)(12.01 g/mol) + (8)(1.008 g/mol) = 68.11 g/mol The mass of sulfur added (mS) is mS = (24 mol)(32.06 g/mol) = 769.4 g While for isoprene mip = (100 mol)(68.11 g/mol) = 6811 g Or, the concentration of sulfur in weight percent (Equation 4.3) is just CS = mS mS + mip × 100 = 769.4 g 769.4 g + 6811 g × 100 = 10.1 wt%
- 825. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.29 Demonstrate, in a manner similar to Equation 15.4, how vulcanization may occur in a butadiene rubber. Solution The reaction by which a butadiene rubber may become vulcanized is as follows:
- 826. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Crystallization 15.30 Determine values for the constants n and k (Equation 10.17) for the crystallization of polypropylene (Figure 15.17) at 160°C. Solution In this problem we are asked to determine the values of the constants n and k (Equation 10.17) for the crystallization of polypropylene at 160°C (Figure 15.17). One way to solve this problem is to take two values of percent recrystallization (which is just 100y, Equation 10.17) and their corresponding time values, then set up two simultaneous equations, from which n and k may be determined. In order to expedite this process, we will rearrange and do some algebraic manipulation of Equation 10.17. First of all, we rearrange as follows: 1 − y = exp − ktn ( ) Now taking natural logarithms ln (1 − y) = − ktn Or − ln (1 − y) = ktn which may also be expressed as ln 1 1 − y = ktn Now taking natural logarithms again, leads to ln ln 1 1 − y = ln k + n lnt which is the form of the equation that we will now use. From the 160°C curve of Figure 15.17, let us arbitrarily choose two percent crystallized values of 20% and 80% (i.e., y1 = 0.20 and y2 = 0.80). The corresponding time
- 827. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. values are t1 = 3400 min and t2 = 6700 min (realizing that the time axis is scaled logarithmically). Thus, our two simultaneous equations become ln ln 1 1 − 0.20 = ln k + n ln (3400) ln ln 1 1 − 0.80 = ln k + n ln (6700) from which we obtain the values n = 2.91 and k = 1.182 × 10-11.
- 828. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Melting and Glass Transition Temperatures 15.31 Name the following polymer(s) that would be suitable for the fabrication of cups to contain hot coffee: polyethylene, polypropylene, poly(vinyl chloride), PET polyester, and polycarbonate. Why? Solution This question asks us to name which, of several polymers, would be suitable for the fabrication of cups to contain hot coffee. At its glass transition temperature, an amorphous polymer begins to soften. The maximum temperature of hot coffee is probably slightly below 100°C (212°F). Of the polymers listed, only polystyrene and polycarbonate have glass transition temperatures of 100°C or above (Table 15.2), and would be suitable for this application.
- 829. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.32 Of those polymers listed in Table 15.2, which polymer(s) would be best suited for use as ice cube trays? Why? Solution In order for a polymer to be suited for use as an ice cube tray it must have a glass-transition temperature below 0°C. Of those polymers listed in Table 15.2 only low-density and high-density polyethylene, PTFE, and polypropylene satisfy this criterion.
- 830. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Factors That Influence Melting and Glass Transition Temperatures 15.33 For each of the following pairs of polymers, plot and label schematic specific volume versus temperature curves on the same graph [i.e., make separate plots for parts (a), (b), and (c)]. (a) Spherulitic polypropylene, of 25% crystallinity, and having a weight-average molecular weight of 75,000 g/mol; spherulitic polystyrene, of 25% crystallinity, and having a weight-average molecular weight of 100,000 g/mol (b) Graft poly(styrene-butadiene) copolymer with 10% of available sites crosslinked; random poly(styrene- butadiene) copolymer with 15% of available sites crosslinked (c) Polyethylene having a density of 0.985 g/cm3 and a degree of polymerization of 2500; polyethylene having a density of 0.915 g/cm3 and a degree of polymerization of 2000 Solution (a) Shown below are the specific volume-versus-temperature curves for the polypropylene and polystyrene materials. Since both polymers are 25% crystalline, they will exhibit behavior similar to curve B in Figure 15.18. However, polystyrene will have higher melting and glass transition temperatures due to the bulkier side group in its repeat unit structure, and since it has a higher weight-average molecular weight. (b) Shown below are the specific volume-versus-temperature curves for the graft and random poly(styrene- butadiene) copolymers. Since these materials are graft and random copolymers, both will be highly noncrystalline, and, thus, will display the behavior similar to curve A in Figure 15.18. However, since the random has the greater degree of crosslinking, it will also have the higher glass transition temperature.
- 831. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. (c) Shown below are the specific volume-versus-temperature curves for the two polyethylene materials. The polyethylene having a density of 0.985 g/cm3 will be highly crystalline, and, thus, will exhibit a behavior similar to curve C in Figure 15.18. On the other hand, the other material, of lower density will have some branching and also be semicrystalline; thus, its behavior will be similar to curve B of Figure 15.18. In addition, the melting temperature of the higher density material will be greater since it has less branching and a higher degree of polymerization.
- 832. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.34 For each of the following pairs of polymers, do the following: (1) state whether or not it is possible to determine whether one polymer has a higher melting temperature than the other; (2) if it is possible, note which has the higher melting temperature and then cite reason(s) for your choice; and (3) if it is not possible to decide, then state why. (a) Isotactic polystyrene that has a density of 1.12 g/cm3 and a weight-average molecular weight of 150,000 g/mol; syndiotactic polystyrene that has a density of 1.10 g/cm3 and a weight-average molecular weight of 125,000 g/mol (b) Linear polyethylene that has a degree of polymerization of 5,000; linear and isotactic polypropylene that has a degree of polymerization of 6,500 (c) Branched and isotactic polystyrene that has a degree of polymerization of 4,000; linear and isotactic polypropylene that has a degree of polymerization of 7,500 Solution (a) Yes, it is possible to determine which of the two polystyrenes has the higher Tm. The isotactic polystyrene will have the higher melting temperature because it has a higher density (i.e., less branching) and also the greater weight-average molecular weight. (b) Yes, it is possible to determine which polymer has the higher melting temperature. The polypropylene will have the higher Tm because it has a bulky phenyl side group in its repeat unit structure, which is absent in the polyethylene. Furthermore, the polypropylene has a higher degree of polymerization. (c) No, it is not possible to determine which of the two polymers has the higher melting temperature. The polystyrene has a bulkier side group than the polypropylene; on the basis of this effect alone, the polystyrene should have the greater Tm. However, the polystyrene has more branching and a lower degree of polymerization; both of these factors lead to a lowering of the melting temperature.
- 833. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.35 Make a schematic plot showing how the modulus of elasticity of an amorphous polymer depends on the glass transition temperature. Assume that molecular weight is held constant. Solution For an amorphous polymer, the elastic modulus may be enhanced by increasing the number of crosslinks (while maintaining the molecular weight constant); this will also enhance the glass transition temperature. Thus, the modulus-glass transition temperature behavior would appear as
- 834. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Elastomers Fibers Miscellaneous Applications 15.36 Briefly explain the difference in molecular chemistry between silicone polymers and other polymeric materials. Solution The backbone chain of most polymers consists of carbon atoms that are linked together. For the silicone polymers, this backbone chain is composed of silicon and oxygen atoms that alternate positions.
- 835. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.37 List two important characteristics for polymers that are to be used in fiber applications. Solution Two important characteristics for polymers that are to be used in fiber applications are: (1) they must have high molecular weights, and (2) they must have chain configurations/structures that will allow for high degrees of crystallinity.
- 836. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.38 Cite five important characteristics for polymers that are to be used in thin-film applications. Solution Five important characteristics for polymers that are to be used in thin-film applications are: (1) low density; (2) high flexibility; (3) high tensile and tear strengths; (4) resistance to moisture/chemical attack; and (5) low gas permeability.
- 837. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Polymerization 15.39 Cite the primary differences between addition and condensation polymerization techniques. Solution For addition polymerization, the reactant species have the same chemical composition as the monomer species in the molecular chain. This is not the case for condensation polymerization, wherein there is a chemical reaction between two or more monomer species, producing the repeating unit. There is often a low molecular weight by-product for condensation polymerization; such is not found for addition polymerization.
- 838. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.40 (a) How much ethylene glycol must be added to 47.3 kg of terephthalic acid to produce a linear chain structure of poly(ethylene terephthalate) according to Equation 15.9? (b) What is the mass of the resulting polymer? Solution (a) This problem asks that we determine how much ethylene glycol must be added to 47.3 kg of terephthalic acid to produce a linear chain structure of poly(ethylene terephthalate) according to Equation 15.9. Since the chemical formulas are provided in this equation we may calculate the molecular weights of each of these materials as follows: MW(ethylene glycol) = 2( AC) + 6( AH) + 2( AO) = 2(12.01 g/mol) + 6(1.008 g/mol) + 2(16.00 g/mol) = 62.07 g/mol MW(terephthalic acid) = 8(AC) + 6(AH) + 4(AO) = 8 (12.01 g/mol) + 6(1.008 g/mol) + 4(16.00 g/mol) = 166.13 g/mol The 47.3 kg mass of terephthalic acid equals 47,300 g or 47,300 g 166.13 g/mol = 284.72 mol. Since, according to Equation 15.9, each mole of terephthalic acid used requires one mole of ethylene glycol, which is equivalent to (284.72 mol)(62.07 g/mol) = 17,673 g = 17.673 kg. (b) Now we are asked for the mass of the resulting polymer. Inasmuch as one mole of water is given off for every repeat unit produced, this corresponds to 284.72 moles or (284.72 mol)(18.02 g/mol) = 5130 g or 5.130 kg since the molecular weight of water is 18.02 g/mol. The mass of poly(ethylene terephthalate) is just the sum of the masses of the two reactant materials [as computed in part (a)] minus the mass of water released, or mass [poly(ethylene terephthalate)] = 47.300 kg + 17.673 kg − 5.130 kg = 59.843 kg
- 839. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.41 Nylon 6,6 may be formed by means of a condensation polymerization reaction in which hexamethylene diamine [NH2—(CH2)6—NH2] and adipic acid react with one another with the formation of water as a byproduct. What masses of hexamethylene diamine and adipic acid are necessary to yield 37.5 kg of completely linear nylon 6,6? (Note: the chemical equation for this reaction is the answer to Concept Check 15.12.) Solution This problem asks for us to calculate the masses of hexamethylene diamine and adipic acid necessary to yield 37.5 kg of completely linear nylon 6,6. The chemical equation for this reaction is the answer to Concept Check 15.12, which is as follows: From this equation we may calculate the molecular weights of these molecules. MW(adipic) = 6( AC) + 10( AH) + 4( AO) = 6(12.01 g/mol) + 10(1.008 g/mol) + 4(16.00 g/mol) = 146.14 g/mol MW(hexamethylene) = 6(AC) + 16(AH) + 2(AN) = 6(12.01 g/mol) + 16(1.008 g/mol) + 2(14.01 g/mol) = 116.21 g/mol MW(nylon) = 12( AC) + 22( AH) + 2( AN) + 2( AO)
- 840. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = 12(12.01 g/mol) + 22(1.008 g/mol) + 2(14.01 g/mol) + 2(16.00 g/mol) = 226.32 g/mol The mass of 37.5 kg of nylon 6,6 equals 37,500 g or m(nylon) = 37,500 g 226.32 g/mol = 165.7 mol Since, according to the chemical equation given above, each mole of nylon 6,6 that is produced requires one mole each of adipic acid and hexamethylene diamine, with two moles of water as the by-product. The masses corresponding to 165.7 moles of adipic acid and hexamethylene diamine are as follows: m(adipic) = (165.7 mol)(146.14 g/mol) = 24,215 g = 24.215 kg m(hexamethylene) = (165.7 mol)(116.21 g/mol) = 19,256 g = 19.256 kg
- 841. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Polymer Additives 15.42 What is the distinction between dye and pigment colorants? Solution The distinction between dye and pigment colorants is that a dye dissolves within and becomes a part of the polymer structure, whereas a pigment does not dissolve, but remains as a separate phase.
- 842. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Forming Techniques for Plastics 15.43 Cite four factors that determine what fabrication technique is used to form polymeric materials. Solution Four factors that determine what fabrication technique is used to form polymeric materials are: (1) whether the polymer is thermoplastic or thermosetting; (2) if thermoplastic, the softening temperature; (3) atmospheric stability; and (4) the geometry and size of the finished product.
- 843. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.44 Contrast compression, injection, and transfer molding techniques that are used to form plastic materials. Solution This question requests that we compare polymer molding techniques. For compression molding, both heat and pressure are applied after the polymer and necessary additives are situated between the mold members. For transfer molding, the solid materials (normally thermosetting in nature) are first melted in the transfer chamber prior to being forced into the die. And, for injection molding (normally used for thermoplastic materials), the raw materials are impelled by a ram through a heating chamber, and finally into the die cavity.
- 844. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Fabrication of Fibers and Films 15.45 Why must fiber materials that are melt spun and then drawn be thermoplastic? Cite two reasons. Solution Fiber materials that are melt spun must be thermoplastic because: (1) In order to be melt spun, they must be capable of forming a viscous liquid when heated, which is not possible for thermosets. (2) During drawing, mechanical elongation must be possible; inasmuch as thermosetting materials are, in general, hard and relatively brittle, they are not easily elongated.
- 845. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.46 Which of the following polyethylene thin films would have the better mechanical characteristics: (1) formed by blowing, or (2) formed by extrusion and then rolled? Why? Solution Of the two polymers cited, the one that was formed by extrusion and then rolled would have the higher strength. Both blown and extruded materials would have roughly comparable strengths; however the rolling operation would further serve to enhance the strength of the extruded material.
- 846. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. DESIGN QUESTIONS 15.D1 (a) List several advantages and disadvantages of using transparent polymeric materials for eyeglass lenses. (b) Cite four properties (in addition to being transparent) that are important for this application. (c) Note three polymers that may be candidates for eyeglass lenses, and then tabulate values of the properties noted in part (b) for these three materials. Solution (a) Several advantages of using transparent polymeric materials for eyeglass lenses are: they have relatively low densities, and, therefore, are light in weight; they are relatively easy to grind to have the desired contours; they are less likely to shatter than are glass lenses; wraparound lenses for protection during sports activities are possible; and they filter out more ultraviolet radiation than do glass lenses. The principal disadvantage of these types of lenses is that some are relatively soft and are easily scratched (although antiscratch coatings may be applied). Plastic lenses are not as mechanically stable as glass, and, therefore, are not as precise optically. (b) Some of the properties that are important for polymer lens materials are: they should be relatively hard in order to resist scratching; they must be impact resistant; they should be shatter resistant; they must have a relatively high index of refraction such that thin lenses may be ground for very nearsighted people; and they should absorb significant proportions of all types of ultraviolet radiation, which radiation can do damage to the eye tissues. (c) Of those polymers discussed in this chapter and Chapter 14, likely lens candidates are polystyrene, poly(methyl methacrylate), and polycarbonate; these three materials are not easily crystallized, and, therefore, are normally transparent. Upon consultation of their fracture toughnesses (Table B.5 in Appendix B), polycarbonate is the most superior of the three. Commercially, the two plastic lens materials of choice are polycarbonate and allyl diglycol carbonate (having the trade name CR-39). Polycarbonate is very impact resistant, but not as hard as CR-39. Furthermore, PC comes in both normal and high refractive-index grades.
- 847. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.D2 Write an essay on polymeric materials that are used in the packaging of food products and drinks. Include a list of the general requisite characteristics of materials that are used for these applications. Now cite a specific material that is utilized for each of three different container types and the rationale for each choice. Solution There are three primary requirements for polymeric materials that are utilized in the packaging of food products and drinks; these are: (1) sufficient strength, to include tensile, tear, and impact strengths; (2) barrier protection--that is, being resistant to permeation by oxygen, water vapor, and carbon dioxide; and (3) being nonreactive with the food/drink contents--such reactions can compromise the integrity of the packaging material, or they can produce toxic by-products. With regard to strength, poly(ethylene terephthalate) (PET or PETE) and oriented polypropylene (OPP) have high tensile strengths, linear low-density polyethylene (LLDPE) and low-density polyethylene (LDPE) have high tear strengths, while those polymers having the best impact strengths are PET and poly(vinyl chloride) (PVC). Relative to barrier characteristics, ethylene vinyl alcohol (EVOH) and poly(vinylidene chloride) (PVDC) copolymers are relatively impermeable to oxygen and carbon dioxide, whereas high-density polyethylene (HDPE), PVDC, polypropylene, and LDPE are impervious to water vapor. Most common polymers are relatively nonreactive with food products, and are considered safe; exceptions are acrylonitrile and plasticizers used in PVC materials. The aesthetics of packaging polymers are also important in the marketing of food and drink products. Some will be colored, many are adorned with printing, others need to be transparent and clear, and many need to be resistant to scuffing. On the basis of the preceding discussion, examples of polymers that are used for specific applications are as follows: PET(E) for soda pop containers; PVC for beer containers; LDPE and HDPE films for packaging bread and bakery products.
- 848. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 15.D3 Write an essay on the replacement of metallic automobile components by polymers and composite materials. Address the following issues: (1) Which automotive components (e.g., crankshaft) now use polymers and/or composites? (2) Specifically what materials (e.g., high-density polyethylene) are now being used? (3) What are the reasons for these replacements? Solution The primary reasons that the automotive industry has replaced metallic automobile components with polymer and composite materials are: polymers/composites (1) have lower densities, and afford higher fuel efficiencies; (2) may be produced at lower costs but with comparable mechanical characteristics; (3) are in many environments more corrosion resistant; (4) reduce noise, and (5) are thermally insulating and thus reduce the transference of heat. These replacements are many and varied. Several are as follows: Bumper fascia are molded from an elastomer-modified polypropylene. Overhead consoles are made of poly(phenylene oxide) and recycled polycarbonate. Rocker arm covers are injection molded of a glass- and mineral-reinforced nylon 6,6 composite. Torque converter reactors, water outlets, pulleys, and brake pistons, are made from phenolic thermoset composites that are reinforced with glass fibers. Air intake manifolds are made of a glass-reinforced nylon 6,6.
- 849. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. CHAPTER 16 COMPOSITES PROBLEM SOLUTIONS Large-Particle Composites 16.1 The mechanical properties of aluminum may be improved by incorporating fine particles of aluminum oxide (Al2O3). Given that the moduli of elasticity of these materials are, respectively, 69 GPa (10 × 106 psi) and 393 GPa (57 × 106 psi), plot modulus of elasticity versus the volume percent of Al2O3 in Al from 0 to 100 vol%, using both upper- and lower-bound expressions. Solution The elastic modulus versus the volume percent of Al2O3 is shown below, on which is included both upper and lower bound curves; these curves were generated using Equations 16.1 and 16.2, respectively, and using the moduli of elasticity for aluminum and Al2O3 that were given in the problem statement.
- 850. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 16.2 Estimate the maximum and minimum thermal conductivity values for a cermet that contains 85 vol% titanium carbide (TiC) particles in a cobalt matrix. Assume thermal conductivities of 27 and 69 W/m-K for TiC and Co, respectively. Solution This problem asks for the maximum and minimum thermal conductivity values for a TiC-Co cermet. Using a modified form of Equation 16.1 the maximum thermal conductivity kmax is calculated as kmax = kmVm + kpVp = kCoVCo + kTiCVTiC = (69 W/m- K)(0.15) + (27 W/m- K)(0.85) = 33.3 W/m- K Using a modified form of Equation 16.2, the minimum thermal conductivity kmin will be kmin = kCokTiC VCokTiC + VTiCkCo = (69 W/m- K)(27 W/m- K) (0.15)(27 W/m- K) + (0.85)(69 W/m- K) = 29.7 W/m-K
- 851. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 16.3 A large-particle composite consisting of tungsten particles within a copper matrix is to be prepared. If the volume fractions of tungsten and copper are 0.60 and 0.40, respectively, estimate the upper limit for the specific stiffness of this composite given the data that follow. Specific Gravity Modulus of Elasticity (GPa) Copper 8.9 110 Tungsten 19.3 407 Solution Given the elastic moduli and specific gravities for copper and tungsten we are asked to estimate the upper limit for specific stiffness when the volume fractions of tungsten and copper are 0.60 and 0.40, respectively. There are two approaches that may be applied to solve this problem. The first is to estimate both the upper limits of elastic modulus [Ec(u)] and specific gravity (ρc) for the composite, using expressions of the form of Equation 16.1, and then take their ratio. Using this approach Ec(u) = ECuVCu + EWVW = (110 GPa)(0.40) + (407 GPa)(0.60) = 288 GPa And ρc = ρCuVCu + ρWVW = (8.9)(0.40) + (19.3)(0.60) = 15.14 Therefore Specific Stiffness = Ec(u) ρc = 288 GPa 15.14 = 19.0 GPa With the alternate approach, the specific stiffness is calculated, again employing a modification of Equation 16.1, but using the specific stiffness-volume fraction product for both metals, as follows:
- 852. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Specific Stiffness = ECu ρCu VCu + EW ρW VW = 110 GPa 8.9 (0.40) + 407 GPa 19.3 (0.60) = 17.6 GPa
- 853. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 16.4 (a) What is the distinction between cement and concrete? (b) Cite three important limitations that restrict the use of concrete as a structural material. (c) Briefly explain three techniques that are utilized to strengthen concrete by reinforcement. Solution (a) Concrete consists of an aggregate of particles that are bonded together by a cement. (b) Three limitations of concrete are: (1) it is a relatively weak and brittle material; (2) it experiences relatively large thermal expansions (contractions) with changes in temperature; and (3) it may crack when exposed to freeze-thaw cycles. (c) Three reinforcement strengthening techniques are: (1) reinforcement with steel wires, rods, etc.; (2) reinforcement with fine fibers of a high modulus material; and (3) introduction of residual compressive stresses by prestressing or posttensioning.
- 854. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Dispersion-Strengthened Composites 16.5 Cite one similarity and two differences between precipitation hardening and dispersion strengthening. Solution The similarity between precipitation hardening and dispersion strengthening is the strengthening mechanism--i.e., the precipitates/particles effectively hinder dislocation motion. The two differences are: (1) the hardening/strengthening effect is not retained at elevated temperatures for precipitation hardening--however, it is retained for dispersion strengthening; and (2) the strength is developed by a heat treatment for precipitation hardening--such is not the case for dispersion strengthening.
- 855. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Influence of Fiber Length 16.6 For some glass fiber-epoxy matrix combination, the critical fiber length-fiber diameter ratio is 50. Using the data in Table 16.4, determine the fiber-matrix bond strength. Solution This problem asks that, for a glass fiber-epoxy matrix combination, to determine the fiber-matrix bond strength if the critical fiber length-fiber diameter ratio is 50. Thus, we are to solve for τc in Equation 16.3. Since we are given that σ f ∗ = 3.45 GPa from Table 16.4, and that lc d = 50, then τc = σ f ∗ d 2 lc = (3.45 × 103 MPa) 1 2 1 50 = 34.5 MPa
- 856. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 16.7 (a) For a fiber-reinforced composite, the efficiency of reinforcement η is dependent on fiber length l according to η= l − 2x l where x represents the length of the fiber at each end that does not contribute to the load transfer. Make a plot of η versus l to l = 40 mm (1.6 in.) assuming that x = 0.75 mm (0.03 in.). (b) What length is required for a 0.80 efficiency of reinforcement? Solution (a) The plot of reinforcement efficiency versus fiber length is given below. (b) This portion of the problem asks for the length required for a 0.80 efficiency of reinforcement. Solving for l from the given expression l = 2x 1 − η Or, when x = 0.75 mm (0.03 in.) and η = 0.80, then l = (2)(0.75 mm) 1 − 0.80 = 7.5 mm (0.30 in.)
- 857. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Influence of Fiber Orientation and Concentration 16.8 A continuous and aligned fiber-reinforced composite is to be produced consisting of 30 vol% aramid fibers and 70 vol% of a polycarbonate matrix; mechanical characteristics of these two materials are as follows: Modulus of Elasticity [GPa (psi)] Tensile Strength [MPa (psi)] Aramid fiber 131 (19 × 106 ) 3600 (520,000) Polycarbonate 2.4 (3.5 × 105 ) 65 (9425) Also, the stress on the polycarbonate matrix when the aramid fibers fail is 45 MPa (6500 psi). For this composite, compute (a) the longitudinal tensile strength, and (b) the longitudinal modulus of elasticity Solution This problem calls for us to compute the longitudinal tensile strength and elastic modulus of an aramid fiber-reinforced polycarbonate composite. (a) The longitudinal tensile strength is determined using Equation 16.17 as σcl ∗ = σm ' (1 − Vf ) + σ f ∗ Vf = (45 MPa)(0.70) + (3600)(0.30) = 1100 MPa (160,000 psi) (b) The longitudinal elastic modulus is computed using Equation 16.10a as Ecl = EmVm + Ef Vf = (2.4 GPa)(0.70) + (131 GPa)(0.30) = 41 GPa (5.95 × 106 psi)
- 858. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 16.9 Is it possible to produce a continuous and oriented aramid fiber-epoxy matrix composite having longitudinal and transverse moduli of elasticity of 57.1 GPa (8.28 × 106 psi) and 4.12 GPa (6 × 105 psi), respectively? Why or why not? Assume that the modulus of elasticity of the epoxy is 2.4 GPa (3.50 × 105 psi). Solution This problem asks for us to determine if it is possible to produce a continuous and oriented aramid fiber- epoxy matrix composite having longitudinal and transverse moduli of elasticity of 57.1 GPa and 4.12 GPa, respectively, given that the modulus of elasticity for the epoxy is 2.4 GPa. Also, from Table 16.4 the value of E for aramid fibers is 131 GPa. The approach to solving this problem is to calculate values of Vf for both longitudinal and transverse cases using the data and Equations 16.10b and 16.16; if the two Vf values are the same then this composite is possible. For the longitudinal modulus Ecl (using Equation 16.10b), Ecl = Em(1 − Vfl) + Ef Vfl 57.1 GPa = (2.4 GPa)(1 − Vfl) + (131 GPa)Vfl Solving this expression for Vfl (i.e., the volume fraction of fibers for the longitudinal case) yields Vfl = 0.425. Now, repeating this procedure for the transverse modulus Ect (using Equation 16.16) Ect = EmEf (1 − Vft)Ef + VftEm 4.12 GPa = (2.4 GPa)(131 GPa) (1 − Vft)(131 GPa) + Vft (2.4 GPa) Solving this expression for Vft (i.e., the volume fraction of fibers for the transverse case), leads to Vft = 0.425. Thus, since Vfl and Vft are equal, the proposed composite is possible.
- 859. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 16.10 For a continuous and oriented fiber-reinforced composite, the moduli of elasticity in the longitudinal and transverse directions are 19.7 and 3.66 GPa (2.8 × 106 and 5.3 × 105 psi), respectively. If the volume fraction of fibers is 0.25, determine the moduli of elasticity of fiber and matrix phases. Solution This problem asks for us to compute the elastic moduli of fiber and matrix phases for a continuous and oriented fiber-reinforced composite. We can write expressions for the longitudinal and transverse elastic moduli using Equations 16.10b and 16.16, as Ecl = Em(1 − Vf ) + Ef Vf 19.7 GPa = Em (1 − 0.25) + Ef (0.25) And Ect = EmEf (1 − Vf )Ef +Vf Em 3.66 GPa = EmEf (1 − 0.25)Ef + 0.25Em Solving these two expressions simultaneously for Em and Ef leads to Em = 2.79 GPa (4.04 × 105 psi) Ef = 70.4 GPa (10.2 × 106 psi)
- 860. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 16.11 (a) Verify that Equation 16.11, the expression for the fiber load–matrix load ratio (Ff/Fm), is valid. (b) What is the Ff/Fc ratio in terms of Ef, Em, and Vf? Solution (a) In order to show that the relationship in Equation 16.11 is valid, we begin with Equation 16.4—i.e., Fc = Fm + Ff which may be manipulated to the form Fc Fm = 1 + Ff Fm or Ff Fm = Fc Fm − 1 For elastic deformation, combining Equations 6.1 and 6.5 σ = F A = εE or F = AεE We may write expressions for Fc and Fm of the above form as Fc = AcεEc Fm = AmεEm which, when substituted into the above expression for Ff/Fm, gives Ff Fm = AcεEc AmεEm − 1
- 861. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. But, Vm = Am/Ac, which, upon rearrangement gives Ac Am = 1 Vm which, when substituted into the previous expression leads to Ff Fm = Ec EmVm − 1 Also, from Equation 16.10a, Ec = EmVm + EfVf, which, when substituted for Ec into the previous expression, yields Ff Fm = EmVm + Ef Vf EmVm − 1 = EmVm + Ef Vf − EmVm EmVm = Ef Vf EmVm the desired result. (b) This portion of the problem asks that we establish an expression for Ff/Fc. We determine this ratio in a similar manner. Now Fc = Ff + Fm (Equation 16.4), or division by Fc leads to 1 = Ff Fc + Fm Fc which, upon rearrangement, gives Ff Fc = 1 − Fm Fc Now, substitution of the expressions in part (a) for Fm and Fc that resulted from combining Equations 6.1 and 6.5 results in Ff Fc = 1 − AmεEm AcεEc = 1 − AmEm AcEc
- 862. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. Since the volume fraction of fibers is equal to Vm = Am/Ac, then the above equation may be written in the form Ff Fc = 1 − VmEm Ec And, finally substitution of Equation 16.10(a) for Ec into the above equation leads to the desired result as follows: Ff Fc = 1 − VmEm VmEm + Vf Ef = VmEm + Vf Ef − VmEm VmEm + Vf Ef = Vf Ef VmEm + Vf Ef = Vf Ef (1 − Vf )Em + Vf Ef
- 863. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 16.12 In an aligned and continuous glass fiber-reinforced nylon 6,6 composite, the fibers are to carry 94% of a load applied in the longitudinal direction. (a) Using the data provided, determine the volume fraction of fibers that will be required. (b) What will be the tensile strength of this composite? Assume that the matrix stress at fiber failure is 30 MPa (4350 psi). Modulus of Elasticity [GPa (psi)] Tensile Strength [MPa (psi)] Glass fiber 72.5 (10.5 × 106 ) 3400 (490,000) Nylon 6,6 3.0 (4.35 × 105 ) 76 (11,000) Solution (a) Given some data for an aligned and continuous glass-fiber-reinforced nylon 6,6 composite, we are asked to compute the volume fraction of fibers that are required such that the fibers carry 94% of a load applied in the longitudinal direction. From Equation 16.11 Ff Fm = Ef Vf EmVm = Ef Vf Em (1 − Vf ) Now, using values for Ff and Fm from the problem statement Ff Fm = 0.94 0.06 = 15.67 And when we substitute the given values for Ef and Em into the first equation leads to Ff Fm = 15.67 = (72.5 GPa)Vf (3.0 GPa)(1 − Vf ) And, solving for Vf yields, Vf = 0.393. (b) We are now asked for the tensile strength of this composite. From Equation 16.17, σcl ∗ = σm ' (1 − Vf ) + σ f ∗ Vf
- 864. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. = (30 MPa)(1 − 0.393) + (3400 MPa)(0.393) = 1354 MPa (196,400 psi) since values for σ f ∗ (3400 MPa) and σm ' (30 MPa) are given in the problem statement.
- 865. Excerpts from this work may be reproduced by instructors for distribution on a not-for-profit basis for testing or instructional purposes only to students enrolled in courses for which the textbook has been adopted. Any other reproduction or translation of this work beyond that permitted by Sections 107 or 108 of the 1976 United States Copyright Act without the permission of the copyright owner is unlawful. 16.13 Assume that the composite described in Problem 16.8 has a cross-sectional area of 320 mm2 (0.50 in.2 ) and is subjected to a longitudinal load of 44,500 N (10,000 lbf). (a) Calculate the fiber–matrix load ratio. (b) Calculate the actual loads carried by both fiber and matrix phases. (c) Compute the magnitude of the stress on each of the fiber and matrix phases. (d) What strain is experienced by the composite? Solution The problem stipulates that the cross-sectional area of a composite, Ac, is 320 mm2 (0.50 in.2), and the longitudinal load, Fc, is 44,500 N (10,000 lbf) for the composite described in Problem 16.8. Also, for this composite Vf = 0.3 Vm = 0.7 Ef = 131 GPa Em = 2.4 GPa (a) First, we are asked to calculate the Ff/Fm ratio. According to Equation 16.11 Ff Fm = Ef Vf