Chapter 03

1
Stress and Strain:
0 0
0.177 0.00005
0.336 0.00010
0.584 0.000167
0.725 0.000217
0.902 0.000283
1.061 0.000333
1.220 0.000375
1.362 0.000417
1.645 0.000517
1.768 0.000583
1.874 0.000625
Modulus of Elasticity: From the stress–strain diagram
Ans.Eapprox =
1.31 - 0
0.0004 - 0
= 3.275A103
B ksi
e =
dL
L
(in./in.)s =
P
A
(ksi)
•3–1. A concrete cylinder having a diameter of 6.00 in. and
gauge length of 12 in. is tested in compression.The results of
the test are reported in the table as load versus contraction.
Draw the stress–strain diagram using scales of
and From the diagram, determine
approximately the modulus of elasticity.
1 in. = 0.2110-3
2 in.>in.
1 in. = 0.5 ksi
© 2010 Pearson Education, Inc., Upper Saddle River, NJ. All rights reserved.This material is protected under all copyright laws as they currently
exist. No portion of this material may be reproduced, in any form or by any means, without permission in writing from the publisher.
0
5.0
9.5
16.5
20.5
25.5
30.0
34.5
38.5
46.5
50.0
53.0
0
0.0006
0.0012
0.0020
0.0026
0.0034
0.0040
0.0045
0.0050
0.0062
0.0070
0.0075
Load (kip) Contraction (in.)
03 Solutions 46060 5/7/10 8:45 AM Page 1

Modulus of Toughness: The modulus of toughness is equal to the area under the
stress–strain diagram (shown shaded).
Ans.= 85.0
in # lb
in3
+
1
2
(12.3)A103
B ¢
lb
in2 ≤(0.0004)¢
in.
in.
≤
+
1
2
(7.90)A103
B ¢
lb
in2 ≤(0.0012)¢
in.
in.
≤
+ 45.5A103
B ¢
lb
in2 ≤(0.0012)¢
in.
in.
≤
(ut)approx =
1
2
(33.2)A103
B ¢
lb
in2 ≤(0.0004 + 0.0010)¢
in.
in.
≤
3–3. Data taken from a stress–strain test for a ceramic are
given in the table. The curve is linear between the origin
and the first point. Plot the diagram, and determine
approximately the modulus of toughness.The rupture stress
is sr = 53.4 ksi.
0
33.2
45.5
49.4
51.5
53.4
0
0.0006
0.0010
0.0014
0.0018
0.0022
S (ksi) P (in./in.)
2
Ans.
Modulus of Resilience: The modulus of resilience is equal to the area under the
linear portion of the stress–strain diagram (shown shaded).
Ans.ut =
1
2
(33.2)A103
B ¢
lb
in2 ≤ ¢0.0006
in.
in.
≤ = 9.96
in # lb
in3
E =
33.2 - 0
0.0006 - 0
= 55.3A103
B ksi
3–2. Data taken from a stress–strain test for a ceramic are
given in the table.The curve is linear between the origin and
the first point. Plot the diagram, and determine the modulus
of elasticity and the modulus of resilience.
0
33.2
45.5
49.4
51.5
53.4
0
0.0006
0.0010
0.0014
0.0018
0.0022
S (ksi) P (in./in.)

3
Stress and Strain:
0 0
90.45 0.00035
259.9 0.00120
308.0 0.00204
333.3 0.00330
355.3 0.00498
435.1 0.02032
507.7 0.06096
525.6 0.12700
507.7 0.17780
479.1 0.23876
Ans.
Ultimate and Fracture Stress: From the stress–strain diagram
Ans.
Ans.(sf)approx = 479 MPa
(sm)approx = 528 MPa
(E)approx =
228.75(106
) - 0
0.001 - 0
= 229 GPa
e =
dL
L
(mm/mm)s =
P
A
(MPa)
*3–4. A tension test was performed on a specimen having
an original diameter of 12.5 mm and a gauge length of
50 mm.The data are listed in the table. Plot the stress–strain
diagram, and determine approximately the modulus of
elasticity, the ultimate stress, and the fracture stress. Use a
scale of and
Redraw the linear-elastic region, using the same stress scale
but a strain scale of 20 mm = 0.001 mm>mm.
20 mm = 0.05 mm>mm.20 mm = 50 MPa
0
11.1
31.9
37.8
40.9
43.6
53.4
62.3
64.5
62.3
58.8
0
0.0175
0.0600
0.1020
0.1650
0.2490
1.0160
3.0480
6.3500
8.8900
11.9380
Load (kN) Elongation (mm)

Stress and Strain:
0 0
90.45 0.00035
259.9 0.00120
308.0 0.00204
333.3 0.00330
355.3 0.00498
435.1 0.02032
507.7 0.06096
525.6 0.12700
507.7 0.17780
479.1 0.23876
Modulus of Toughness: The modulus of toughness is equal to the
total area under the stress–strain diagram and can be
approximated by counting the number of squares. The total
number of squares is 187.
Ans.(ut)approx = 187(25)A106
B ¢
N
m2 ≤ a0.025
m
m
b = 117 MJ>m3
e =
dL
L
(mm/mm)s =
P
A
(MPa)
3–5. A tension test was performed on a steel specimen
having an original diameter of 12.5 mm and gauge length
of 50 mm. Using the data listed in the table, plot the
stress–strain diagram, and determine approximately the
modulus of toughness. Use a scale of and
20 mm = 0.05 mm>mm.
20 mm = 50 MPa
4
0
11.1
31.9
37.8
40.9
43.6
53.4
62.3
64.5
62.3
58.8
0
0.0175
0.0600
0.1020
0.1650
0.2490
1.0160
3.0480
6.3500
8.8900
11.9380
Load (kN) Elongation (mm)

5
Normal Stress and Strain: Applying and .
Modulus of Elasticity:
Ans.E =
¢s
¢e
=
9.167 - 2.546
0.000750
= 8.83A103
B ksi
¢e =
0.009
12
= 0.000750 in.>in.
s2 =
1.80
p
4 (0.52
)
= 9.167 ksi
s1 =
0.500
p
4 (0.52
)
= 2.546 ksi
e =
dL
L
s =
P
A
3–6. A specimen is originally 1 ft long, has a diameter of
0.5 in., and is subjected to a force of 500 lb. When the force
is increased from 500 lb to 1800 lb, the specimen elongates
0.009 in. Determine the modulus of elasticity for the
material if it remains linear elastic.
Allowable Normal Stress:
Ans.
Stress–Strain Relationship: Applying Hooke’s law with
Normal Force: Applying equation .
Ans.P = sA = 7.778 (0.2087) = 1.62 kip
s =
P
A
s = Ee = 14 A103
B (0.000555) = 7.778 ksi
e =
d
L
=
0.02
3 (12)
= 0.000555 in.>in.
A = 0.2087 in2
= 0.209 in2
19.17 =
4
A
sallow =
P
A
sallow = 19.17 ksi
3 =
57.5
sallow
F.S. =
sy
sallow
3–7. A structural member in a nuclear reactor is made of a
zirconium alloy. If an axial load of 4 kip is to be supported
by the member, determine its required cross-sectional area.
Use a factor of safety of 3 relative to yielding. What is the
load on the member if it is 3 ft long and its elongation is
0.02 in.? ksi, ksi. The material has
elastic behavior.
sY = 57.5Ezr = 14(103
)

6
Here, we are only interested in determining the force in wire AB.
a
The normal stress the wire is
Since , Hooke’s Law can be applied to determine the strain
in wire.
The unstretched length of the wire is . Thus, the wire
stretches
Ans.= 0.0821 in.
dAB = PAB LAB = 0.6586(10-3
)(124.71)
LAB =
9(12)
sin 60°
= 124.71 in
PAB = 0.6586(10-3
) in>in
sAB = EPAB; 19.10 = 29.0(103
)PAB
sAB 6 sy = 36 ksi
sAB =
FAB
AAB
=
600
p
4 (0.22
)
= 19.10(103
) psi = 19.10 ksi
+©MC = 0; FAB cos60°(9) -
1
2
(200)(9)(3) = 0 FAB = 600 lb
*3–8. The strut is supported by a pin at C and an A-36
steel guy wire AB. If the wire has a diameter of 0.2 in.,
determine how much it stretches when the distributed load
acts on the strut.
9 ft
200 lb/ft
C
A
B
60Њ

7
From the graph
Ans.d = eL = 0.035(6.5) = 0.228 in.
e = 0.035 in.>in.
s =
P
A
=
343.75
0.229
= 1.50 ksi
•3–9. The diagram for a collagen fiber bundle from
which a human tendon is composed is shown. If a segment
of the Achilles tendon at A has a length of 6.5 in. and an
approximate cross-sectional area of determine its
elongation if the foot supports a load of 125 lb, which causes
a tension in the tendon of 343.75 lb.
0.229 in2
,
s–P
125 lb
s (ksi)
P (in./in.)
0.05 0.10
4.50
3.75
3.00
2.25
1.50
0.75
A
From the stress–strain diagram, Fig. a,
Ans.
Thus,
Ans.
Ans.Pu>t = su>t A = 100Cp
4 (0.52
)D = 19.63 kip = 19.6 kip
PY = sYA = 60Cp
4 (0.52
)D = 11.78 kip = 11.8 kip
sy = 60 ksi su>t = 100 ksi
E
1
=
60 ksi - 0
0.002 - 0
; E = 30.0(103
) ksi
3–10. The stress–strain diagram for a metal alloy having an
original diameter of 0.5 in. and a gauge length of 2 in. is given
in the figure. Determine approximately the modulus of
elasticity for the material,the load on the specimen that causes
yielding, and the ultimate load the specimen will support.
0
105
90
75
60
45
30
15
00
0 0.350.05 0.10 0.15 0.20 0.25 0.30
0.0070.001 0.002 0.003 0.004 0.005 0.006
P (in./in.)
s (ksi)

From the stress–strain diagram Fig. a, the modulus of elasticity for the steel alloy is
when the specimen is unloaded, its normal strain recovered along line AB, Fig. a,
which has a gradient of E.Thus
Ans.
Thus, the permanent set is
Then, the increase in gauge length is
Ans.¢L = PPL = 0.047(2) = 0.094 in
PP = 0.05 - 0.003 = 0.047 in>in
Elastic Recovery =
90
E
=
90 ksi
30.0(103
) ksi
= 0.003 in>in
E
1
=
60 ksi - 0
0.002 - 0
; E = 30.0(103
) ksi
3–11. The stress–strain diagram for a steel alloy having an
original diameter of 0.5 in. and a gauge length of 2 in. is
given in the figure. If the specimen is loaded until it is
stressed to 90 ksi, determine the approximate amount of
elastic recovery and the increase in the gauge length after it
is unloaded.
8
0
105
90
75
60
45
30
15
00
0 0.350.05 0.10 0.15 0.20 0.25 0.30
0.0070.001 0.002 0.003 0.004 0.005 0.006
P (in./in.)
s (ksi)

9
The Modulus of resilience is equal to the area under the stress–strain diagram up to
the proportional limit.
Thus,
Ans.
The modulus of toughness is equal to the area under the entire stress–strain
diagram. This area can be approximated by counting the number of squares. The
total number is 38.Thus,
Ans.C(ui)tDapprox = 38 c15(103
)
lb
in2
d a0.05
in
in
b = 28.5(103
)
in # lb
in3
(ui)r =
1
2
sPLPPL =
1
2
C60(103
)D(0.002) = 60.0
in # lb
in3
sPL = 60 ksi PPL = 0.002 in>in.
*3–12. The stress–strain diagram for a steel alloy having an
original diameter of 0.5 in. and a gauge length of 2 in.
is given in the figure. Determine approximately the modulus
of resilience and the modulus of toughness for the material.
0
105
90
75
60
45
30
15
00
0 0.350.05 0.10 0.15 0.20 0.25 0.30
0.0070.001 0.002 0.003 0.004 0.005 0.006
P (in./in.)
s (ksi)

Normal Stress and Strain:
Modulus of Elasticity:
Ans.E =
s
e
=
11.43
0.000400
= 28.6(103
) ksi
e =
dL
L
=
0.002
5
= 0.000400 in.>in.
s =
P
A
=
8.00
0.7
= 11.43 ksi
•3–13. A bar having a length of 5 in. and cross-sectional
area of 0.7 is subjected to an axial force of 8000 lb. If the
bar stretches 0.002 in., determine the modulus of elasticity
of the material.The material has linear-elastic behavior.
in2
10
8000 lb8000 lb
5 in.
Here, we are only interested in determining the force in wire BD. Referring
to the FBD in Fig. a
a
The normal stress developed in the wire is
Since , Hooke’s Law can be applied to determine the strain in
the wire.
The unstretched length of the wire is . Thus, the
wire stretches
Ans.= 0.0632 in
dBD = PBD LBD = 1.054(10-3
)(60)
LBD = 232
+ 42
= 5ft = 60 in
PBD = 1.054(10-3
) in.>in.
sBD = EPBD; 30.56 = 29.0(103
)PBD
sBD 6 sy = 36 ksi
sBD =
FBD
ABD
=
1500
p
4 (0.252
)
= 30.56(103
) psi = 30.56 ksi
+©MA = 0; FBDA4
5 B(3) - 600(6) = 0 FBD = 1500 lb
3–14. The rigid pipe is supported by a pin at A and an
A-36 steel guy wire BD. If the wire has a diameter of
0.25 in., determine how much it stretches when a load of
acts on the pipe.P = 600 lb
3 ft 3 ft
C
DA
B
P4 ft

11
Here, we are only interested in determining the force in wire BD. Referring to the
FBD in Fig. a
a
The unstretched length for wire BD is . From the
geometry shown in Fig. b, the stretched length of wire BD is
Thus, the normal strain is
Then, the normal stress can be obtain by applying Hooke’s Law.
Since , the result is valid.
Ans.P = 569.57 lb = 570 lb
sBD =
FBD
ABD
; 29.01(103
) =
2.50 P
p
4 (0.252
)
sBD 6 sy = 36 ksi
sBD = EPBD = 29(103
)C1.0003(10-3
)D = 29.01 ksi
PBD =
LBD¿ - LBD
LBD
=
60.060017 - 60
60
= 1.0003(10-3
) in.>in.
LBD¿ = 2602
+ 0.0752
- 2(60)(0.075) cos143.13° = 60.060017
LBD = 232
+ 42
= 5 ft = 60 in
+©MA = 0; FBDA4
5 B(3) - P(6) = 0 FBD = 2.50 P
3–15. The rigid pipe is supported by a pin at A and an
A-36 guy wire BD. If the wire has a diameter of 0.25 in.,
determine the load P if the end C is displaced 0.075 in.
downward.
3 ft 3 ft
C
DA
B
P4 ft

12
Normal Stress and Strain: The cross-sectional area of the hollow bar is
.When ,
From the stress–strain diagram shown in Fig. a, the slope of the straight line OA
which represents the modulus of elasticity of the metal alloy is
Since , Hooke’s Law can be applied.Thus
Thus, the elongation of the bar is
Ans.
When ,
From the geometry of the stress–strain diagram, Fig. a,
When is removed, the strain recovers linearly along line BC, Fig. a,
parallel to OA.Thus, the elastic recovery of strain is given by
The permanent set is
Thus, the permanent elongation of the bar is
Ans.dP = ePL = 0.0285(600) = 17.1 mm
eP = e2 - er = 0.0305 - 0.002 = 0.0285 mm>mm
er = 0.002 mm>mm
s2 = Eer; 400(106
) = 200(109
)er
P = 360 kN
e2 - 0.00125
400 - 250
=
0.05 - 0.00125
500 - 250
e2 = 0.0305 mm>mm
s2 =
P
A
=
360(103
)
0.9(10-3
)
= 400 MPa
P = 360 kN
d1 = e1L = 0.5556(10-3
)(600) = 0.333 mm
e1 = 0.5556(10-3
) mm>mm
s1 = Ee1; 111.11(106
) = 200(109
)e1
s1 6 250 MPa
E =
250(106
) - 0
0.00125 - 0
= 200 GPa
s1 =
P
A
=
100(103
)
0.9(10-3
)
= 111.11 MPa
P = 100kNA = 0.052
- 0.042
= 0.9(10-3
)m2
*3–16. Determine the elongation of the square hollow bar
when it is subjected to the axial force If this
axial force is increased to and released, find
the permanent elongation of the bar. The bar is made of a
metal alloy having a stress–strain diagram which can be
approximated as shown.
P = 360 kN
P = 100 kN.
P
P
600 mm
50 mm250
0.00125 0.05
P (mm/mm)
500
50 mm 5 mm
5 mm
s (MPa)

13
3–16. Continued

14
Proportional Limit and Yield Strength: From the stress–strain diagram, Fig. a,
Ans.
Ans.
Modulus of Elasticity: From the stress–strain diagram, the corresponding strain for
is Thus,
Ans.
Modulus of Resilience: The modulus of resilience is equal to the area under the
E =
44 - 0
0.004 - 0
= 11.0(103
) ksi
epl = 0.004 in.>in.sPL = 44 ksi
sY = 60 ksi
spl = 44 ksi
3–17. A tension test was performed on an aluminum
2014-T6 alloy specimen.The resulting stress–strain diagram
is shown in the figure. Estimate (a) the proportional limit,
(b) the modulus of elasticity, and (c) the yield strength
based on a 0.2% strain offset method.
P (in./in.)
0.02 0.04 0.06 0.08 0.10
0.002 0.004 0.006 0.008 0.010
10
20
30
40
50
60
70
0
s (ksi)

15
stress–strain diagram up to the proportional limit. From the stress–strain diagram,
Thus,
Ans.
Modulus of Toughness: The modulus of toughness is equal to the area under the
entire stress–strain diagram.This area can be approximated by counting the number
of squares.The total number of squares is 65.Thus,
Ans.
The stress–strain diagram for a bone is shown, and can be described by the equation
C AUiBtDapprox = 65B10(103
)
lb
in2 R c0.01
in.
in.
d = 6.50(103
)
in # lb
in3
AUiBr =
1
2
splepl =
1
2
(44)(103
)(0.004) = 88
in # lb
in3
spl = 44 ksi epl = 0.004 in.>in.
3–18. A tension test was performed on an aluminum
2014-T6 alloy specimen. The resulting stress–strain
diagram is shown in the figure. Estimate (a) the modulus of
resilience; and (b) modulus of toughness.
P (in./in.)
0.02 0.04 0.06 0.08 0.10
0.002 0.004 0.006 0.008 0.010
10
20
30
40
50
60
70
0
s (ksi)
,
Ans.E =
ds
dP
2
s=0
=
1
0.45(10-6
)
= 2.22 MPa
dP = A0.45(10-6
) + 1.08(10-12
) s2
Bds
e = 0.45(10-6
)s + 0.36(10-12
)s3
3–19. The stress–strain diagram for a bone is shown, and
can be described by the equation ϩ
where is in kPa. Determine the yield
strength assuming a 0.3% offset.
s0.36110-12
2 s3
,
P = 0.45110-6
2 s
P
P
P ϭ 0.45(10Ϫ6
)s + 0.36(10Ϫ12
)s3
P
s

16
When
Solving for the real root:
Ans.
Ans.d = eL = 0.12(200) = 24 mm
= 613 kJ>m3
= 0.12 s - 0.225(10-6
)s2
- 0.09(10-12
)s4
|
6873.52
0
ut =
L
6873.52
0
(0.12 - 0.45(10-6
)s - 0.36(10-12
)s3
)ds
ut =
LA
dA =
L
6873.52
0
(0.12 - e)ds
s = 6873.52 kPa
120(103
) = 0.45 s + 0.36(10-6
)s3
e = 0.12
*3–20. The stress–strain diagram for a bone is shown and
can be described by the equation ϩ
where is in kPa. Determine the modulus
of toughness and the amount of elongation of a 200-mm-
long region just before it fractures if failure occurs at
P = 0.12 mm>mm.
ss3
,0.36110-12
2
0.45110-6
2 sP =
P
P
P ϭ 0.45(10Ϫ6
)s + 0.36(10Ϫ12
)s3
P
s

17
From the stress–strain diagram,
Thus,
Angle of tilt :
Ans.tan a =
18.535
1500
; a = 0.708°
a
dCD = eCDLCD = 0.002471(500) = 1.236 mm
dAB = eABLAB = 0.009885(2000) = 19.771 mm
eCD =
sCD
E
=
7.958(106
)
3.22(109
)
= 0.002471 mm>mm
sCD =
FCD
ACD
=
40(103
)
p
4(0.08)2
= 7.958 MPa
eAB =
sAB
E
=
31.83(106
)
3.22(109
)
= 0.009885 mm>mm
sAB =
FAB
AAB
=
40(103
)
p
4(0.04)2
= 31.83 MPa
E =
32.2(10)6
0.01
= 3.22(109
) Pa
•3–21. The stress–strain diagram for a polyester resin
is given in the figure. If the rigid beam is supported by a
strut AB and post CD, both made from this material, and
subjected to a load of determine the angle
of tilt of the beam when the load is applied.The diameter of
the strut is 40 mm and the diameter of the post is 80 mm.
P = 80 kN,
0
tension
compression
0.01 0.02 0.03 0.04
95
80
100
70
60
50
40
32.2
20
0
0.75 m
B
C
D
A
P
0.75 m 0.5 m
2 m
P (mm/mm)
s (MPa)

Normal Stress:
Normal Strain:
From the stress–strain diagram, the copolymer will satisfy both stress and strain
requirements. Ans.
e =
0.25
5
= 0.0500 in.>in.
s =
P
A
=
20
p
4(22
)
= 6.366 ksi
3–23. By adding plasticizers to polyvinyl chloride, it is
possible to reduce its stiffness. The stress–strain diagrams
for three types of this material showing this effect are given
below. Specify the type that should be used in the
manufacture of a rod having a length of 5 in. and a diameter
of 2 in., that is required to support at least an axial load of
20 kip and also be able to stretch at most 1
4 in.
18
Rupture of strut AB:
Ans.
Rupture of post CD:
P = 239 kN
sR =
FCD
ACD
; 95(106
) =
P>2
p
4(0.04)2
P = 11.3 kN (controls)
sR =
FAB
AAB
; 50(106
) =
P>2
p
4(0.012)2
;
3–22. The stress–strain diagram for a polyester resin is
given in the figure. If the rigid beam is supported by a strut
AB and post CD made from this material, determine the
largest load P that can be applied to the beam before it
ruptures. The diameter of the strut is 12 mm and the
diameter of the post is 40 mm.
0
tension
compression
0.01 0.02 0.03 0.04
95
80
100
70
60
50
40
32.2
20
0
0.75 m
B
C
D
A
P
0.75 m 0.5 m
2 m
P (mm/mm)
s (MPa)
s (ksi)
0
15
(in./in.)
0.10 0.20 0.30
P
P
flexible
(plasticized)
unplasticized
copolymer
P
10
5
0

19
Choose,
Ans.
Ans.k = 4.23(10-6
)
n = 2.73
ln (0.3310962) = n ln (0.6667)
0.3310962 = (0.6667)n
0.29800 = k(60)n
0.098667 = k(40)n
0.3 =
60
30(103
)
+ k(60)n
0.1 =
40
30(103
)
+ k(40)n
s = 60 ksi, e = 0.3
s = 40 ksi, e = 0.1
*3–24. The stress–strain diagram for many metal alloys
can be described analytically using the Ramberg-Osgood
three parameter equation where E, k, and
n are determined from measurements taken from the
diagram. Using the stress–strain diagram shown in the
figure, take and determine the other two
parameters k and n and thereby obtain an analytical
expression for the curve.
E = 301103
2 ksi
P = s>E + ksn
,
s (ksi)
P (10–6
)
0.1 0.2 0.3 0.4 0.5
80
60
40
20
Ans.
Ans.¢d = elatd = -0.0002515 (15) = -0.00377 mm
elat = -Velong = -0.4(0.0006288) = -0.0002515
d = elong L = 0.0006288 (200) = 0.126 mm
elong =
s
E
=
1.697(106
)
2.70(109
)
= 0.0006288
s =
P
A
=
300
p
4(0.015)2
= 1.697 MPa
•3–25. The acrylic plastic rod is 200 mm long and 15 mm in
diameter. If an axial load of 300 N is applied to it, determine
the change in its length and the change in its diameter.
np = 0.4.Ep = 2.70 GPa,
300 N
200 mm
300 N

Normal Stress:
Normal Strain: From the stress–strain diagram, the modulus of elasticity
.Applying Hooke’s law
Poisson’s Ratio: The lateral and longitudinal strain can be related using Poisson’s
ratio.
Ans.V = -
elat
elong
= -
-0.56538(10-3
)
1.8835(10-3
)
= 0.300
elat =
d - d0
d0
=
12.99265 - 13
13
= -0.56538A10-3
B mm>mm
elong =
s
E
=
376.70(106
)
200(104
)
= 1.8835A10-3
B mm>mm
E =
400(106
)
0.002
= 200 GPa
s =
P
A
=
50(103
)
p
4 (0.0132
)
= 376.70 Mpa
3–27. The elastic portion of the stress–strain diagram for a
steel alloy is shown in the figure. The specimen from which
it was obtained had an original diameter of 13 mm and a
gauge length of 50 mm. When the applied load on the
specimen is 50 kN, the diameter is 12.99265 mm. Determine
Poisson’s ratio for the material.
20
a)
Ans.
b)
Ans.d¿ = d + ¢d = 0.5000673 in.
¢d = elat d = 0.00013453 (0.5) = 0.00006727
elat = -0.35 (-0.0003844) = 0.00013453
V =
-elat
elong
= 0.35
d = elong L = -0.0003844 (1.5) = -0.577 (10-3
) in.
elong =
s
E
=
-4074.37
10.6(106
)
= -0.0003844
s =
P
A
=
800
p
4 (0.5)2
= 4074.37 psi
3–26. The short cylindrical block of 2014-T6 aluminum,
having an original diameter of 0.5 in. and a length of 1.5 in.,
is placed in the smooth jaws of a vise and squeezed until the
axial load applied is 800 lb. Determine (a) the decrease in its
length and (b) its new diameter.
800 lb 800 lb
400
P(mm/mm)
0.002
s(MPa)

21
Normal Stress:
Normal Strain: From the Stress–Strain diagram, the modulus of elasticity
.Applying Hooke’s Law
Thus,
Ans.
Poisson’s Ratio: The lateral and longitudinal can be related using poisson’s ratio.
Ans.d = d0 + dd = 13 + (-0.003918) = 12.99608 mm
dd = elat d = -0.3014A10-3
B(13) = -0.003918 mm
= -0.3014A10-3
B mm>mm
elat = -velong = -0.4(0.7534)A10-3
B
L = L0 + dL = 50 + 0.03767 = 50.0377 mm
dL = elong L0 = 0.7534A10-3
B(50) = 0.03767 mm
elong =
s
E
=
150.68(106
)
200(109
)
= 0.7534A10-3
B mm>mm
= 200 GPaE =
400(106
)
0.002
s =
P
A
=
20(103
)
p
4 (0.0132
)
= 150.68Mpa
*3–28. The elastic portion of the stress–strain diagram for
a steel alloy is shown in the figure. The specimen from
which it was obtained had an original diameter of 13 mm
and a gauge length of 50 mm. If a load of kN is
applied to the specimen, determine its diameter and gauge
length.Take n = 0.4.
P = 20
400
P(mm/mm)
0.002
s(MPa)
Ans.
Ans.h¿ = 2 + 0.0000880(2) = 2.000176 in.
v =
-0.0000880
-0.0002667
= 0.330
elat =
1.500132 - 1.5
1.5
= 0.0000880
elong =
s
E
=
-2.667
10(103
)
= -0.0002667
s =
P
A
=
8
(2)(1.5)
= 2.667 ksi
•3–29. The aluminum block has a rectangular cross
section and is subjected to an axial compressive force of
8 kip. If the 1.5-in. side changed its length to 1.500132 in.,
determine Poisson’s ratio and the new length of the 2-in.
side. Eal ϭ 10(103) ksi.
3 in.
1.5 in.
8 kip
8 kip 2 in.

The shear force developed on the shear planes of the bolt can be determined by
considering the equilibrium of the FBD shown in Fig. a
From the shear stress–strain diagram, the yield stress is .Thus,
Ans.
From the shear stress–strain diagram, the shear modulus is
Thus, the modulus of elasticity is
Ans.E = 28.6(103
) ksi
G =
E
2(1 + y)
; 11.01(103
) =
E
2(1 + 0.3)
G =
60 ksi
0.00545
= 11.01(103
) ksi
P = 53.01 kip = 53.0 kip
ty =
Vy
A
; 60 =
P>2
p
4 A0.752
B
ty = 60 ksi
:+ ©Fx = 0; V + V - P = 0 V = =
P
2
22
Normal Strain:
Ans.
Poisson’s Ratio:The lateral and longitudinal strain can be related using Poisson’s ratio.
Ans.
Shear Strain:
Ans.gxy =
p
2
- b =
p
2
- 1.576032 = -0.00524 rad
b = 180° - 89.7° = 90.3° = 1.576032 rad
= 0.00540 in. >in.
ex = -vey = -0.36(-0.0150)
ey =
dLy
Ly
=
-0.06
4
= -0.0150 in.>in.
3–30. The block is made of titanium Ti-6A1-4V and is
subjected to a compression of 0.06 in. along the y axis, and its
shape is given a tilt of Determine and gxy.Py,Px,u = 89.7°.
4 in. u
y
x
5 in.
P
0.00545
60
g(rad)
t(ksi)
P/2
P/2
3–31. The shear stress–strain diagram for a steel alloy is
shown in the figure. If a bolt having a diameter of 0.75 in.
is made of this material and used in the double lap joint,
determine the modulus of elasticity E and the force P
required to cause the material to yield.Take n = 0.3.

23
Shear Stress–Strain Relationship: Applying Hooke’s law with .
(Q.E.D)
If is small, then tan .Therefore,
At
Then,
At
Ans.d =
P
2p h G
ln
ro
ri
r = ri, y = d
y =
P
2p h G
ln
ro
r
C =
P
2p h G
ln ro
0 = -
P
2p h G
ln ro + C
r = ro, y = 0
y = -
P
2p h G
ln r + C
y = -
P
2p h G L
dr
r
dy
dr
= -
P
2p h G r
g = gg
dy
dr
= -tan g = -tan a
P
2p h G r
b
g =
tA
G
=
P
2p h G r
tA =
P
2p r h
*3–32. A shear spring is made by bonding the rubber
annulus to a rigid fixed ring and a plug. When an axial load
P is placed on the plug, show that the slope at point y in
the rubber is For small
angles we can write Integrate this
expression and evaluate the constant of integration using
the condition that at From the result compute
the deflection of the plug.y = d
r = ro.y = 0
dy>dr = -P>12phGr2.
-tan1P>12phGr22.dy>dr = -tan g =
P
y
ro
ri
y
r
h
d

Ans.d = 40(0.02083) = 0.833 mm
g =
t
G
=
4166.7
0.2(106
)
= 0.02083 rad
tavg =
V
A
=
2.5
(0.03)(0.02)
= 4166.7 Pa
•3–33. The support consists of three rigid plates, which
are connected together using two symmetrically placed
rubber pads. If a vertical force of 5 N is applied to plate
A, determine the approximate vertical displacement of
this plate due to shear strains in the rubber. Each pad
has cross-sectional dimensions of 30 mm and 20 mm.
Gr = 0.20 MPa.
24
C B
40 mm40 mm
A
5 N
Average Shear Stress: The rubber block is subjected to a shear force of .
Shear Strain: Applying Hooke’s law for shear
Thus,
Ans.d = a g = =
P a
2 b h G
g =
t
G
=
P
2 b h
G
=
P
2 b h G
t =
V
A
=
P
2
b h
=
P
2 b h
V =
P
2
3–34. A shear spring is made from two blocks of rubber,
each having a height h, width b, and thickness a. The
blocks are bonded to three plates as shown. If the plates
are rigid and the shear modulus of the rubber is G,
determine the displacement of plate A if a vertical load P is
applied to this plate. Assume that the displacement is small
so that d = a tan g L ag.
P
h
aa
A
d

25
From the stress–strain diagram,
When specimen is loaded with a 9 - kip load,
Ans.Gal =
Eat
2(1 + v)
=
11.4(103
)
2(1 + 0.32332)
= 4.31(103
) ksi
V = -
elat
elong
= -
-0.0013
0.0040208
= 0.32332
elat =
d¿ - d
d
=
0.49935 - 0.5
0.5
= - 0.0013 in.>in.
elong =
s
E
=
45.84
11400.65
= 0.0040208 in.>in.
s =
P
A
=
9
p
4 (0.5)2
= 45.84 ksi
Eal =
s
e
=
70
0.00614
= 11400.65 ksi
3–35. The elastic portion of the tension stress–strain
diagram for an aluminum alloy is shown in the figure. The
specimen used for the test has a gauge length of 2 in. and a
diameter of 0.5 in. When the applied load is 9 kip, the new
diameter of the specimen is 0.49935 in. Compute the shear
modulus for the aluminum.Gal
0.00614
70
s(ksi)
P (in./in.)
From the stress–strain diagram
Ans.d¿ = d + ¢d = 0.5 - 0.001117 = 0.4989 in.
¢d = elat d = - 0.002234(0.5) = - 0.001117 in.
elat = - velong = - 0.500(0.0044673) = - 0.002234 in.>in.
G =
E
2(1 + v)
; 3.8(103
) =
11400.65
2(1 + v)
; v = 0.500
elong =
s
E
=
50.9296
11400.65
= 0.0044673 in.>in.
E =
70
0.00614
= 11400.65 ksi
s =
P
A
=
10
p
4 (0.5)2
= 50.9296 ksi
*3–36. The elastic portion of the tension stress–strain
diagram for an aluminum alloy is shown in the figure. The
specimen used for the test has a gauge length of 2 in. and a
diameter of 0.5 in. If the applied load is 10 kip, determine
the new diameter of the specimen. The shear modulus is
Gal = 3.81103
2 ksi.
0.00614
70
s(ksi)
P (in./in.)

Ans.
Ans.
Ans.ut =
1
2
(2)(11) = 11 psi
ut =
1
2
(2)(11) +
1
2
(55 + 11)(2.25 - 2) = 19.25 psi
E =
11
2
= 5.5 psi
3–37. The diagram for elastic fibers that make up
human skin and muscle is shown. Determine the modulus
of elasticity of the fibers and estimate their modulus of
toughness and modulus of resilience.
s–P
26
21 2.25
11
55
P(in./in.)
s(psi)
a)
Ans.
b)
Ans.d¿ = d + ¢d = 20 + 0.0016 = 20.0016 mm
¢d = elat d = 0.00008085(20) = 0.0016 mm
elat = 0.00008085 mm>mm
v = -
elat
elong
; 0.35 = -
elat
-0.0002310
d = elong L = - 0.0002310(75) = - 0.0173 mm
elong = - 0.0002310 mm>mm
s = E elong ; - 15.915(106
) = 68.9(109
) elong
s =
P
A
=
-5(103
)
p
4 (0.02)2
= - 15.915 MPa
3–38. A short cylindrical block of 6061-T6 aluminum,
having an original diameter of 20 mm and a length of
75 mm, is placed in a compression machine and squeezed
until the axial load applied is 5 kN. Determine (a) the
decrease in its length and (b) its new diameter.

27
a (1)
a (2)
Since the beam is held horizontally,
Ans.
From Eq. (2),
Ans.dA
œ
= dA + d elat = 30 + 30(0.0002646) = 30.008 mm
elat = -velong = -0.35(-0.000756) = 0.0002646
elong =
sA
E
= -
55.27(106
)
73.1(109
)
= -0.000756
sA =
FA
A
=
39.07(103
)
p
4(0.032
)
= 55.27 MPa
FA = 39.07 kN
x = 1.53 m
80(3 - x)(220) = 80x(210)
dA = dB ;
80(3 - x)
3 (220)
AE
=
80x
3 (210)
AE
d = eL = a
P
A
E
b L =
PL
AE
s =
P
A
; e =
s
E
=
P
A
E
dA = dB
+ ©MB = 0; -FA(3) + 80(3 - x) = 0; FA =
80(3 - x)
3
+ ©MA = 0; FB(3) - 80(x) = 0; FB =
80x
3
3–39. The rigid beam rests in the horizontal position on
two 2014-T6 aluminum cylinders having the unloaded lengths
shown. If each cylinder has a diameter of 30 mm, determine
the placement x of the applied 80-kN load so that the beam
remains horizontal. What is the new diameter of cylinder A
after the load is applied? nal = 0.35.
3 m
210 mm220 mm
x
A B
80 kN
Normal Stress:
Normal Strain: Since , Hooke’s law is still valid.
Ans.
If the nut is unscrewed, the load is zero.Therefore, the strain Ans.e = 0
e =
s
E
=
28.97
29(103
)
= 0.000999 in.>in.
s 6 sg
s =
P
A
=
800
p
4 A 3
16 B2
= 28.97 ksi 6 sg = 40 ksi
*3–40. The head H is connected to the cylinder of a
compressor using six steel bolts. If the clamping force in
each bolt is 800 lb, determine the normal strain in the
bolts. Each bolt has a diameter of If and
what is the strain in each bolt when the
nut is unscrewed so that the clamping force is released?
Est = 291103
2 ksi,
sY = 40 ksi3
16 in. H
LC

Equations of Equilibrium:
a [1]
[2]
Note:The normal force at A does not act exactly at A. It has to shift due to friction.
Friction Equation:
[3]
Solving Eqs. [1], [2] and [3] yields:
Average Shear Stress: The pad is subjected to a shear force of .
Modulus of Rigidity:
Shear Strain: Applying Hooke’s law for shear
Thus,
Ans.dh = hg = 30(0.1005) = 3.02 mm
g =
t
G
=
148.89(103
)
1.481(106
)
= 0.1005 rad
G =
E
2(1 + v)
=
4
2(1 + 0.35)
= 1.481 MPa
t =
V
A
=
3126.69
(0.14)(0.15)
= 148.89 kPa
V = F = 3126.69 N
FA = 3908.37 N F = P = 3126.69 N
F = ms FA = 0.8 FA
:+ ©Fx = 0; P - F = 0
+©MB = 0; FA(2.75) - 7848(1.25) - P(0.3) = 0
•3–41. The stone has a mass of 800 kg and center of gravity
at G. It rests on a pad at A and a roller at B.The pad is fixed
to the ground and has a compressed height of 30 mm, a
width of 140 mm, and a length of 150 mm. If the coefficient
of static friction between the pad and the stone is
determine the approximate horizontal displacement of the
stone, caused by the shear strains in the pad, before the
stone begins to slip. Assume the normal force at A acts
1.5 m from G as shown. The pad is made from a material
having MPa and n = 0.35.E = 4
ms = 0.8,
28
0.4 m
1.25 m 1.5 m
0.3 m
P
B A
G

29
Normal Stress:
Normal Strain: Applying Hooke’s Law
Ans.
Ans.es =
ss
Emg
=
39.79(106
)
45(109
)
= 0.000884 mm>mm
eb =
sb
Eal
=
159.15(106
)
70(109
)
= 0.00227 mm>mm
ss =
P
As
=
8(103
)
p
4 (0.022
- 0.0122
)
= 39.79 MPa
sb =
P
Ab
=
8(103
)
p
4 (0.0082
)
= 159.15 MPa
3–43. The 8-mm-diameter bolt is made of an aluminum
alloy. It fits through a magnesium sleeve that has an inner
diameter of 12 mm and an outer diameter of 20 mm. If the
original lengths of the bolt and sleeve are 80 mm and
50 mm, respectively, determine the strains in the sleeve and
the bolt if the nut on the bolt is tightened so that the tension
in the bolt is 8 kN. Assume the material at A is rigid.
Emg = 45 GPa.Eal = 70 GPa,
Ans.
a
Ans.
Ans.eBC =
sBC
E
=
55.94
29 (103
)
= 0.00193 in.>in.
sBC =
W
ABC
=
0.112
0.002
= 55.94 ksi
W = 0.112 kip = 112 lb
+ ©MA = 0; -(0.0672) (5) + 3(W) = 0
FDE = sDEADE = 33.56 (0.002) = 0.0672 kip
sDE = EeDE = 29(103
)(0.00116) = 33.56 ksi
eDE =
d
L
=
0.0417
3(12)
= 0.00116 in.>in.
d = 0.0417 in
3
0.025
=
5
d
3–42. The bar DA is rigid and is originally held in the
horizontal position when the weight W is supported from C.
If the weight causes B to be displaced downward 0.025 in.,
determine the strain in wires DE and BC. Also, if the wires
are made of A-36 steel and have a cross-sectional area of
0.002 in2, determine the weight W. 2 ft 3 ft
4 ft
3 ft
D AB
E
C
W
50 mm
30 mm
A

30
a
(1)
However,
From Eq. (1),
Ans.P = 2.46 kN
FAB = sA = 348.76(106
)(10)(10-6
) = 3.488 kN
P(400 cos 0.2°) - FAB sin 44.9° (400) = 0
+©MA = 0
s = Ee = 200(109
) (0.001744) = 348.76 MPa
e =
L¿
AB - LAB
LAB
=
566.67 - 565.69
565.69
= 0.001744
LAB =
400
sin 45°
= 565.69
L¿
AB = 566.67 mm
L¿
AB
sin 90.2°
=
400
sin 44.9°
*3–44. The A-36 steel wire AB has a cross-sectional area
of and is unstretched when Determine
the applied load P needed to cause u = 44.9°.
u = 45.0°.10 mm2
400 mm
A
B
P
400 mm
u

Chapter 03

More Related Content

What's hot (20)

Viewers also liked (14)

Similar to Chapter 03 (20)

Recently uploaded (20)

Chapter 03