Finite Element Analysis of the Composite Patch Repairs of the Plates

Ch. Ramakrishna.et al. Int. Journal of Engineering Research and Application www.ijera.com
ISSN : 2248-9622, Vol. 7, Issue 2, ( Part -2) February 2017, pp.10-18
www.ijera.com DOI: 10.9790/9622- 0702021018 10 | P a g e
Finite Element Analysis of the Composite Patch Repairs of the
Plates
Ch. Ramakrishna*1
, J. Krishna Balu2
, S. Rajashekar3
, N. Sivateja4
1, 2, 4
Assistant Professor, Department of Mechanical Engineering, KL University, Guntur, AP, India-522502.
3
Assistant Professor, Mechanical Department, KITS,Singapur Huzurabad, Karimnagar,TS- 505468
ABSTRACT:
Adhesively-bonded patches are used for repair of different types of damages such as holes, notches, scratches,
cracks etc. occurring in metallic as well as composite structures. The composite patching is the most widely
used method of restoring the load-carrying capacity of the weakened structure. Due to the rapid growth of
aerospace industry, analysis of adhesively-bonded patches to repair cracked structures have been the focus for
many years. Most of these studies investigated repaired structures using linear analysis and demonstrated the
viability of adhesively-bonded patch-repairs as a means to improve the durability and damage tolerance of
cracked metallic structures efficiently and economically.Many researchers performed more intensive research
on the method and presented the advantages of a composite material patch used for the cracked plate repairing.
It was found that the bonded patch method not only reduces the weight but also increases the service life.In this
research work, the analysis of cracked metallic and composite plates which are repaired by bonded-composite
patches is performed using Finite Element Analysis package FRANC2D/L. This package is available with its
corresponding mesh generating program CACSA. They are developed by Cornel Fracture Group, Cornel
University.In this study, various fracture parameters for the structures are found out. It revealed that, the
application of the bonded composite patches effectively reduces the stress intensity factor (SIF) near the crack
tip and hence retards or eliminates the crack propagation. As the chances of fracture are almost reduced, the life
of the structures increases by almost double of the initial. The main advantage of this patch repair technology is
that, it doesn’t increase the weight of the structure too much.
Keywords: Adhesively-bonded patches, Finite Element Analysis (FEA), Crackpropagation, Stress intensity
factor (SIF).
I. INTRODUCTION
The objective of the adhesively bonded
composite repair is to restore the damaged structure
back to its original condition in terms of strength
and stiffness. They restore the static strength and
durability of the structure and decrease the high
stresses caused by local damage in the form of cut
outs, indentations, and cracks.The aim of this work
is to review the capability of finite element models
in estimating the mechanical behaviour of metallic
and composite panels repaired by adhesively
bonded composite patches. The interest in
commercial finite element codes is due to their use
in most of the industrial applications.So, after the
application of bonded patches, we should be able to
retard or eliminate crack growth, in metallic and
composite structures. The aim is to determine the
stress intensity near the crack tip, before and after
the application of composite patch using Finite
Element Package FRANC2D/L. Based on the
results, necessary conclusions regarding bonded
patch repair technology can be made.
II. ANALYTICAL ASPECTS OF
BONDED PATCH REPAIRS
A. The adhesively bonded repairs
The usual objective of a Bonded Repair is
to restore the damaged structure back to its original
condition in terms of strength and stiffness. The
objectives of such repair work are to restore the
static strength and durability of the structure and to
decrease the high stresses caused by local damage
in the form of cut outs, indentations, and cracks.
The aim of this work is to review the capability of
finite element models in estimating the mechanical
behaviour of metallic panels repaired by composite
patches.The interest in commercial finite element
codes is due to their use in most of the industrial
applications.
Figure 1: Typical bonded patch arrangement over
cracked specimen
RESEARCH ARTICLE OPEN ACCESS

B. Stress intensity factor (SIF)
The stress intensity factor, K, is used in
fracture mechanics to predict the stress state
("stress intensity") near the tip of a crack caused by
a remote load or residual stresses. It is a theoretical
construct usually applied to a homogeneous, linear
elastic material and is useful for providing a failure
criterion for brittle materials, and is a critical
technique in the discipline of damage tolerance.
The general equation used for calculation of SIF for
a rectangular plate with crack is,
K = σ (Π*a) ½
* f (a/w)
Where, σ = stress
a = semi-crack length
w = semi-plate width
f (a/ w)is a polynomial which depends on the
number of terms taken in the Taylorsexpansion.
Higher the number of terms more is the accuracy.
The general value of this term varies between 0.90
to 0.99.The SI unit of K is MPa√m.
C. Rose and Baker’s model for finding SIF for a
structure with patch
This is one of the very few analytical methods
available to find SIF for patched configuration.
According to it,Patch repaired SIF, KR is given by,
KR = Y.σ0√K
Where, Y= 1 for centre cracks and
σ0= σ/(1 + S)
s = Spring constant which depends on material
properties of the specimen and the patch.
III. FINITE ELEMENT ANALYSIS OF
COMPOSITE PATCH REPAIRED
CRACKED METALLIC PLATE
In this work, the analytical and numerical
analysis of centre cracked Aluminium plate[4, 10],
under the given loading and boundary conditions
are done. The analysis is carriedout for three
different configurations of the structure.
a) Un-patched or without patch configuration
b) Un-symmetric patch configuration
c) Symmetric patch configuration
The analytical analysis is carried out using
Rose and Baker’s model while the Finite Element
Analysis is done using package FRANC2D/L. The
mesh for this program is generated in CASCA
program. These two programs are available
simultaneously and developed by Cornell Fracture
Group, Cornell University. The FRANC2D/L
program runs on the specially designed algorithm
called Sahara-Fukoda.
A. The geometry of the problem
The following figure shows the geometry of the
problem.
Fig 2. The un-patched and patched configuration of
the Al plate
B. All properties of the plate, patch and adhesive
The dimensions, material properties and boundary
conditions of the Al plate are as given below.
 Dimensions: 10 X 10 X 0.12 inch
 Material Properties:
1. Young’s modulus, E = 70 GPa ,
2. Poisson’s ratio, ν = 0.33.
 Boundary and loading conditions
1. Plate is simply supported at
lower edge.
2. A uniformly distributed load of
200 MPa (tensile) is applied at upper edge.
 Original crack size of the centre crack, 2a
= 1 inch.
The material properties and the dimensions of the
patch are as given below.
 Patch material: Carbon Fiber Reinforce
Plastic (CRPF)
 Dimensions: 10 X 4 X 0.09 inch
 Material properties,
1. Young’s moduli, E 1 = 135 GPa, E2 = E3 = 9
GPa
2. Poisson’s ratios, ν12 = ν13 = 0.3, ν23 = 0.02
3. Shear moduli, G12 = G13 = 5 GPa, G23 = 8 GPa
The properties of the adhesive used for the bond
between the patch and the plate are as given below.
 Adhesive: Epoxy film adhesive, FM-73.
 Young’s modulus: E = 2158 MPa
 Shear modulus: G = 800 MPa
 Poisson’s ration: 0.3
 Thickness of the adhesive film: t = 0.006 inch.

IV. GENERATION OF THE MESH
USING CASCA
Fig. 3: plate and patch mesh
The CASCA program is used for
generating mesh for the plate and the patch
separately. One need to remember that, the
common portion between the plate and patch,
which is going to be bonded, should have the same
structure of mesh. Otherwise, the Castofranc
program will not merge the patch and plate meshes
for the layered analysis. The bi-linear 4 sided
elements are used. The above figures show the
plate and patch meshes respectively.
V. FEA USING FRANC2D/L
A. Analysis of the cracked plate without patch
The cracked plate with given boundary
conditions and loading conditions, is simulated in
FRANC2D/L using its meshed structure. The
analysis is performed and various results such as
deformed shape of the plate, crack tip stresses and
SIF at the crack tip are obtained.The pictorial
results are plotted as below.
a) Deformed shape of the plate
Fig. 4: deformed shape of the plate with enlarged
view near the crack.
b) Crack propagation simulation
Fig. 5 a) simulation of crack propagation, b) SIF
versus crack length
c) Variation of σy for a semi crack size of 0.5
inch
Following figure shows the variation of σy in the
plate structures. The enlarged view of crack tip
stresses is also shown.
Fig. 6: variation ofσyin the plate structure for a =
0.5 inch.(All stresses are in psi)
B. Analysis of the cracked plate with un-
symmetric patch.
A one sided CRPF patch called un-
symmetric patch is applied on the patch over its top
surface. The corresponding meshing of the patch is
done. The meshes of plate and patch are merged
using Castofranc program.Keeping all other
conditions same, the FEA analysis of the plate with
un-symmetric patch is carried out inFRANC2D/L
and all the results are obtained as earlier, which are
plotted below.
 The deformed shape of the plate is same as that
of figure 4, but the deformation now is
retarded by the presence of a patch. Hence the
opening of the crack is reduced. The shape is
not shown here for space constraints.

a) Crack propagation simulation
Fig. 7: Variation of SIF versus crack length for un-
symmetric patch configuration.
b) Variation of σy in the structure using un-
symmetric patch
Fig.8: Variation ofσyin un-symmetric patch
configuration.(All stresses are in psi)
C. Analysis of the cracked plate with symmetric
patch configuration
In this analysis, the patches of same
dimensions are applied on both sides of the plate.
So, the crack is now completely invisible. The
patch that was earlier used on one side, is used on
both sided now. Hence, the same mesh that was
defined earlier is used for both patches along with
plate, hence called as symmetric patch
configuration. The plate mesh and two patch
meshes are merged using Castofranc program. The
common portion between patches and plate has
same mesh structures.This analysis is carried out
again in FRANC2D/L. The various fracture
parameters, and property variations are found out,
which are discussed below.
 The deformed shape of the plate is same as that
of figure 4, but the deformation now is
retarded more and more by the presence of two
patches. Hence the opening of the crack is
further reduced. The shape is not shown here
for space constraints.
a) Crack propagation simulation
Fig. 9: Variation of SIF versus crack length using
symmetric patch configuration.
b) Variation of σy in the structure using
symmetric patch configuration
Fig. 10: variation ofσyand enlarged portion near the
crack tip.(All stresses are in psi)
VI. ANALYTICAL ANALYSIS OF THE
PROBLEM
As discussed earlier, the SIF is given by,
K = σ (Π*a) ½
* f (a/w)
There are different terms of f (a/ w) are available in
the literature as well as SIF handbook. Here we
chosen one of the most correct form of f (a/
w)using that SIF is given by,

K1= σ.√ (∏a).[1.12 - 0.23 (a/2w) + 10.6 (a/2w)2
–
21.7(a/2w) 3
+ 30.4(a/2w)4
]
This equation gives SIF for un-patched
configuration. The results are obtainedand
discussed in Results and discussions topic.
VII. FINITE ELEMENT ANALYSIS
OF A COMPOSITE PATCH
REPAIRED,CRACKED LAMINATE
In this chapter, the numerical analysis of
the centre cracked graphite epoxy (Narmco
ThornelT300/5208) laminate [9] under the given
loading and boundary conditions are done. The
analysisis carried out for only symmetric patch
configuration.The Finite Element Analysis is done
using package FRANC2D/L. The mesh for this
program is generated in CASCA program. These
two programs are available simultaneously and
developed by Cornell Fracture Group, Cornell
University. The FRANC2D/L program runs on the
specially designed algorithm called Sahara-
Fukoda.
A. The geometry of the problem
Fig. 11: Geometry of the problem
B. All properties of the problem
 Material properties of the plate.
The basic ply is made up of a graphite-epoxy
(Narmco Thornel T300/5208), which
havefollowing properties.
Young’s moduli, E 1 = 141 GPa and E1/E2 = 14.96
Shear modulus, G = 5.18 GPa
Poisson’s ratio, ν12 = 0.31
 Dimensions of the laminate and a
crack
The centrally located crack is of length 160 mm in
a graphite epoxy laminate having dimensions of
800 mm X 800 mm x 3 mm.
The moduli of the panel were taken to be as for a
symmetric lay up of (O/90)s.
 Dimensions of the patch
A symmetric patch configuration is assumed for the
panel. The patch dimensions are 320 mm x 320 mm
x 1 mm. The size and shape of the patch are
selected according to the Baker’s
recommendations. He suggests that, the length of
the patch should not be more than twice of the
crack length.
 Adhesive properties
The adhesive material used is Epoxy-film adhesive
FM-73.
Young’s modulus, E = 2158 MPa,
Shear modulus, G = 800 MPa,
Poisson’s ratio, ν = 0.35,
Thickness of the adhesive film, t = 0.2 mm
VIII. GENERATION OF THE MESH
FOR LAMINATE AND THE PATCH
Fig 12:a) laminate mesh and b) patch mesh
The laminate is to be applied with
symmetric patch. Hence, we need to design the
meshes of the two patches exactly the same as that
of the common are covered by laminate and
patches. The meshes are generated in CASCA
program, separately for patch and plate. The bi-
linear 4 sided elements are used for the meshes.
Later they are merged using Castofranc program in
order to use in the FRANC2D/L. Above figure
shows the mesh structures of the laminate and the
patches.
IX. FEA WITHOUT PATCH IN
FRANC2D/L
After generating the mesh in CASCA, the mesh is
transferred to FRANC2D/L for FEA analysis. By
giving all the inputs related to properties and other
conditions, the analysis is run. The results are
obtained in terms of plots and some fracture
parameters are also obtained.
A. Deformed shape of the laminate without
patch, Variation of σy in the laminate and
around the crack tip

Fig 13:a) Deformed shape of the laminate without
patch b) Variation ofσyin the laminate and around
the crack tip
B. Analysis of the problem using symmetric
patch configuration
Fig 13:a) deformed shape with symmetric patches
b) σyvariation in laminate with symmetric patches
X. THE STATEMENT OF THE PATCH
REPAIR PROBLEM FOR AN EDGE
CRACKED LAMINATE
The above problem is analyzed again for an edge
crack, instead of centre crack. All otherproperties
and dimension of the plate, patch and adhesives are
kept unchanged. The initial cracksize is also same
and it is 160 mm.
A. Geometry of the problem
Fig 14: The geometry of the edge crack problem
B. All properties of the problem
The change in the current problem and the problem
in section VII-B is that, the centre crack is replaced
with edge crack. All other parameters are
unchanged.
XI. GENERATION OF THE MESH FOR
THE LAMINATE AND THE PATCH
The same procedure is applied as described in
section VIII and the meshes for the laminate and
the patch are obtained as below.
Figure 15:a) laminate mesh and b) patch mesh
XII. FEA WITHOUT PATCH IN
FRANC2D/L
The same procedure, as explained in section IX is
applied in FRANC2D/L and the results are plotted
as shown in below.
A. Deformed shape of the laminate without
patch and Variation of σy in the laminate and
around the crack tip
Fig 16: a) deformed shape of the laminate without
patch b) Variation of σy in the laminate and around
the crack tip

B. Deformed shape with symmetric patches and
σy variation in laminate with symmetric
patches
Fig 17:a) deformed shape with symmetric patches
b) Variation of σy in the laminate with symmetric
patches
XIII. RESULTS AND DISCUSSION
A. Results for patch repair of the aluminium
(Al) plate from section III:
Various parameters are found out in the analysis
carried out in section III. The results are as
presented below in the tabular format.
Results for SIF found by various methods for an
initial crack size of a = 0.5 inch, all values are in
psi σinch.
Configurat
ion
SIF
(experimen
tal) (psi
σinch)
SIF
(analytic
al)
(psi
σinch)
SIF
(psi
σinch)
Percent
age
error
Without
patch
0.372E5 0.363E5 0.3679
E5
3.6
With un-
symmetric
patch
0.212E5 0.189E5 0.20E5 3.3
With
symmetric
patch
0.148E5 0.135E5 0.14E5 3.7
Table 1: SIF found by various methods for cracked
Al plate.
Crack tip stresses (σy) for all cases
Form the above table it is seen that, the crack tip
stresses reduce with the application of the patches.
Hence, the SIF at the tip reduces and crack growth
can be avoided.
Table 2: Crack tip stresses (σy) for all cases
Configuration
σyat the crack tip using
FEA (psi)
Without patch 1.41E5
With un-symmetric patch 0.782E5
With symmetric patch 0.581E5
Effect of the thickness of the patch on SIF
Thickness of the
patch (inch)
SIF using FEA
(psi σinch)
Percentage
reduction
0.03 0.20E5 -
0.06 0.168E5 15
0.09 0.1484E5 12
Table 3: Effect of the thickness of the patch on SIF
Effect of patch shape on the SIF
Shape of the patch SIF using FEA (psiσinch)
Symmetric, rectangular 0.1484 E5
Symmetric, elliptic 0.213 E5
Symmetric, circular 0.256 E5
Table 4: Effect of the patch shape on the SIF
From the above table, it is seen that, the rectangular
patch gives the least SIF, while circular patchgives
the highest SIF. Hence, rectangular p the
rectangular patch is most advantageous of all
theshapes of patches.
B. Results for the patch repair of the centre
cracked graphite-epoxy laminate from section
VII
The Finite Element Analysis of the cracked
graphite-epoxy laminate is done in FRANC2D/L.
The crack tip stresses are found out along with SIF
for various values of crack sizes. The analysis is
done for two configurations, un-patched and
symmetric patch cases.
Crack tip stresses (σy)
Configuration σyfor 2a =
160 mm
(MPa)
σyfor 2a =
200 mm
(MPa)
σyfor 2a =
240 mm
(MPa)
Without patch 976.8 1120.2 1255.6
With symmetric
patch
326.9 448.5 582.5
Stress intensity factor (SIF)
Configuration SIF for 2a =
160 mm
(MPa√mm)
SIFfor 2a =
200 mm
(MPa√mm)
SIF for 2a =
240 mm
(MPa√mm)
Without patch 618.7 730.5 849.6
With
symmetric
patch
92.8 131.5 186.9
Stress intensity factor ratio (R)
Some of the literatures take into consideration the
ratio of SIF with patched configuration to the SIF
with un-patched configuration. This ratio is called
as stress intensity factor ratio (R). It is a measure of
the efficiency of the patch. The calculated values of
R are shown in the following table. Also, the initial
value of R is compared with the literature value.

Crack size,
2a (mm)
‘R’ from
literature
‘R’ from
FEA
Percentage
error
160 0.140 0.147 5
200 - 0.178 -
240 - 0.212 -
From the above analysis of SIF ratio using FEA, it
is seen that, SIF at the crack tip is reduced by
almost 78-85% of the initial value. It is an
extremely important conclusion and justifies the
use of bonded composite patch repairs.
C. Results for the patch repair of the edge-
cracked graphite-epoxy laminate from section
VII
The Finite Element Analysis of the edge-cracked
graphite-epoxy laminate is done in FRANC2D/L.
The crack tip stresses are found out along with SIF
for various values of crack sizes. The analysis is
done for two configurations, un-patched and
symmetric patch cases.
Crack tip stresses (σy)
Configuration σyfor 2a =
160 mm
(MPa)
σyfor 2a =
200 mm
(MPa)
σyfor 2a =
240 mm
(MPa)
Without patch 1016 1250.6 1405.9
With symmetric
patch
448.2 564.8 695.5
Stress intensity factor (SIF)
Configurati
on
SIF for 2a
= 160 mm
(MPa√m
m)
SIF for 2a
= 200 mm
(MPa√m
m)
SIF for 2a
= 240 mm
(MPa√m
m)
Without
patch 730.6 845.1 960.4
With
symmetric
patch 205.1 278.9 355.3
Stress intensity factor ratio (R)
Crack size, 2a (mm) ‘R’ from FEA
160 0.28
200 0.33
240 0.37
From the above analysis of SIF ratio using FEA, it
is seen that, SIF at the crack tip is reduced by
almost 60-70% of the initial value. It is an
extremely important conclusion and justifies the
use of bonded composite patch repairs.
XIV. CONCLUSION
Following important conclusions are made in this
analytical study of adhesively-bonded composite
patch repairs.
1. The most important conclusion drawn from the
study is that, the use of bonded composite
patches reduces the SIF and crack tip stresses
by very large amount. Therefore, it retards or
eliminates the crack growth which eventually
avoids fracture.The service life of the material
can be increased up to twice of the initial.
2. Among the various shapes of the bonded
patches, the rectangular patches are most
efficient as they reduce the SIF by highest
amount.As the thickness of the patch increases,
the SIF decreases.
3. The symmetric patch configuration is the most
efficient over un-symmetric because, it reduces
the SIF by highest value. The adhesively-
bonded composite repairs are the easiest,
efficient way of repairing damages in
structures.
4. These bonded composite repairs can be
regarded as a versatile cost-effective method of
repairing, strengthening or upgrading
inadequate metallic structures. The
reinforcements or patches are ideally
implemented, avoiding the need for costly
disassembly of built-up structures.
5. CASCA and FRANC2D/L are very easy and
user friendly FEA packages. They have many
advantages such as; the layer-wise analysis of
3-D structure can be done assuming each layer
in plane stress conditions. It simplifies the
analysis, with much greater accuracy.
6. Finite Element Analysis is the easiest way of
finding approximately accurate primary
results. They are advantageous over analytical
and experimental work in this regard. Hence, it
is used vastly in industrial applications.
REFERENCES
[1]. Ong C. L., Shen S.B., “The reinforcing effect of
composite patch repairs on metallicaircraft
structures”, Aero industry development centre,
Taiwan, China, 1991.
[2]. Baker A. A., “Fibber composite repair of cracked
metallic aircraft components – practicaland basic
aspects”, composites, volume 18, No .4, 1987.
[3]. Baker A. A., “Repair of cracked or defective
metallic aircraft components with advancedfibre
composites- an overview of Australian work”,
composite structures 2 (1984) 153-181.
[4]. Mahadesh Kumar A., Hakeem S. A., “Optimum
design of symmetric composite patchrepair to centre
cracked metallic sheet”, Aircraft Research and
Design Centre, HindustanAeronautics Limited,
Design Complex, Bangalore.
[5]. Ramji M., Mohammed K., “Design of optimum
patch shape and size for bonded repairon damaged

carbon fiber reinforced polymer panels”, materials
and design –54(2014)174-153.
[6]. Baker, A.A., Chester, R.J., Davis, M.J.,
“Reinforcement of the F-111 wing pivot fittingwith
a boron/epoxy doubler system - materials
engineering aspects”. Composites, 24, pp.51 1-521,
1993).
[7]. Anderson T. L., “Fracture Mechanics –
Fundamentals and Applications, 3rdEdition”,Taylor
and Francis Group, 2005.
[8]. Bartholomeusz, R.A., Baker, A.A., Chester, R.J.,
“Bonded joints with through thicknessadhesive
stresses - reinforcing the F/A-18 Y470.5 Bulkhead”,
Int. J. of Adhesion and Adhesives, 19,pp. 173-180,
1999.
[9]. Jonnes R., Callinan R., Aggarwal K, “Analysis Of
Bonded repairs to damaged fibercomposite
structures”, Vol. 17, pp-37-46, 1983.
[10].Ricci F., Francesco F., “Bonded Composite Patch
repairs on cracked aluminiumplates: “Theory,
modelling and experiments”, Advances in
composite materials- 2011.
AUTHOR PROFILE
Ch. Ramakrishna pursued his M.Tech from JNT
University, Hyderabad. He has been working
presently as an Assistant Professor, Department of
Mechanical Engineering, KL University, and
Guntur, India-522502.
J. Krishna Balu pursued his M.Tech from IIT
Madras. He has been working presently as an
Assistant Professor, Department of Mechanical
Engineering, KL University, and Guntur, India-
522502.
Eswara Kumar.A pursued his M.Tech from VR
Siddhartha to JNTU Kakinada. He has been
working presently as an Assistant Professor,
Department of Mechanical Engineering, KL
University, and Guntur, India-522502.

Finite Element Analysis of the Composite Patch Repairs of the Plates

More Related Content

What's hot (18)

Viewers also liked (20)

Similar to Finite Element Analysis of the Composite Patch Repairs of the Plates (20)

Recently uploaded (20)

Finite Element Analysis of the Composite Patch Repairs of the Plates