IRJET- Mitigation of Effect of Sulphate in Lime Stabilized Marine Clay

International Research Journal of Engineering and Technology (IRJET) e-ISSN: 2395-0056
Volume: 06 Issue: 05 | May 2019 www.irjet.net p-ISSN: 2395-0072
© 2019, IRJET | Impact Factor value: 7.211 | ISO 9001:2008 Certified Journal | Page 8066
Mitigation of Effect of Sulphate in Lime Stabilized Marine Clay
Anas Ali1, Anjaly Das2, Bismi Aliyar3, Vishnu Haridas4, Jobin Johnson5
1,2,3,4Student, Civil Engineering, Ilahia College of Engineering and Technology, Kerala, India
5Asst. Professor, Civil Engineering, Ilahia College of Engineering and Technology, Kerala, India
---------------------------------------------------------------------***---------------------------------------------------------------------
Abstract - Water plays an important role in the concrete preparation. It plays an important role in workability and strength of
concrete. A new technology known as magnetized water in which when added to concrete improves the workability and
compressive strength of concrete. Also, this magnetically processed water causes a reduction in the cement content required for the
specified compressive strength value. In this project work, we check the effects of magnetic water on properties of concrete such as
workability and strengths of M25 grade concrete. Magnetized water is prepared by passing the normal tap water through a
magnetic field. When water passes through the magnetic field, some of the physical properties of water changes. The water clusters
are broken due to magnetic field and which will increase the water activity. In this study magnetized water is used for mixing of
concrete. When magnetic water was used there was an increase in compressive strength by 50% after 7days of curing and 60%
after 28 days of curing, split tensile strength is increased by 44% after 7 days of curing and 39% after 28 days of curing and flexural
strength is increased by 20% after 7 days of curing and 19% after 28 days of curing.
Key Words: Magnetized water, stabilization, turbid metric method, free swell index, Desiccators
1. INTRODUCTION
Marine clays located in coastal and offshore areas of the world forms one of the important groups of fine grained soils and lots of
civil construction activities take place in such marine clays throughout the world. Since these clays are characterized by low
strength and high compressibility, the design and construction of many coastal and offshore structures in these deposits are
confronted with many geotechnical problems. Such low strength and high compressible soils are generally associated with
increased moisture content and they are weak in strength due to the presence of swelling clay minerals. Lime stabilization is one
of the many processes available and is commonly resorted to improve the geotechnical properties of expansive and soft clays.
1.1 Problem Statement
Greater Cochin area forms part of a coastal belt which was first uplifted and then partially submerged by sea water and is
covered by thick marine clay deposits. Structures resting on these soils are subjected to distresses caused by large scale total
and differential settlements. It has been proved conclusively that the most effective stabilizing agent for marine clays in Cochin
is lime.
1.2 Objectives
The objective of this study is to evaluate the long term influence of natural sulphate present in clays as well the effect of varying
concentrations of sulphate on the physical and engineering properties lime treated Cochin marine clays. This study helps to
understand the effect of barium hydrooxide in mitigating the deleterious long term effect of sulphate on lime treated marine
clays.
2. METHODOLOGY
It explains about the literature review, material collection and tests to be accomplished for getting the final results. It also
describes about preparation of samples with various percentage of materials. Rajasekaran et al [2] discussed about laboratory
investigation was carried out to examine the influence of sodium and calcium sulphates on the behavior of lime column treated
marine clay. The presence of sulphate in lime-treated clays may result in high swelling due to the formation of the expansive
mineral, ettringite.

2.1 Raw Materials
a) Cochin marine clay
The Marine Clay conducted for this project is collected from Petta, located in Cochin. The depth at which marine clay deposits, usually
overlain by loose sandy soils, found in these areas, varies from 2m to 9m. Clay was collected from a depth of 5m to9m by auguring from
piling site.
Fig – 1 : Marine Clay
b) Lime
Specially selected uniform shells were used for the preparation of the stabilizing agent. The shells were burnt to remove CO2
completely when they change to brittle white shells of calcium oxide which were preserved in air tight multilayer polyethylene
bags. Just sufficient water was sprinkled over the lime shells taken from these bags, on each day till all the shells crumble to fine
powder which was then sieved through IS 425 microns sieve. This method of preparation of lime was used because of its
simplicity and ease with which it can be prepared for field application.
Fig – 2 : Lime
C) Other Additives
It includes sodium sulphate [Na2SO4], and barium hydroxide [Ba(OH)2].
2.2 Test for Soil
a) Test For Sulphate Content
1. Take 100 ml of the sample or a suitable portion made up to 100 ml into a 250ml in Erlenmeyer flask.
2. Add 20ml buffer solution and mix in stirring apparatus. While stirring, add a spoon full of barium chloride crystals and
turning immediately. Stir for 60±2 seconds at constant speed.

3. Pour solution into absorption cell of nephelometer and measure turbidity at 5 min and stirring period.
4. Obtained Sulphate concentration in the sample from calibration curve prepared by carrying sulphate standards through the
entire procedure.
Fig – 3 : Clay sample for the determination of sulphate content
b) Unconfined Compression Test (UCC)
1. The remolded soil was placed into a split mould of standard dimensions with a spatula, and care was taken so that no air was
entrapped in the sample during for mingprocess.
2. The specimen was extruded from the sampling tube with the help of the sample extractor.
3. The initial length and diameter of the specimen was measured.
4. The specimen was placed in the compression apparatus, ready for testing.
5. Compression load was applied by giving about half a turn of the handle per second till the sample fails.
6. The readings of the dial gauge and the proving ring reading corresponding to each deformation was recorded.
c) Test For Liquid Limit
1. About 100 gm of air dried soil passing through 4.25µ sieve was taken, and it was mixed thoroughly with distilled water to
form a uniform paste.
2. A portion of the paste was placed in the cup of the liquid limit device, and the surface was smoothened off to a maximum
depth of 1cm.
3. The groove was cut by means of the grooving tool through the sample along the symmetrical axis of the cup.
4. The crank was turned at the rate of about 2 revolutions per second until the groove closed at the bottom to a distance of
12mm.
5. Approximately 10g of soil was taken from near the closed groove for water content determination.
6. The above procedure was repeated by altering the water content of the soil so as to get the number of blows ranging from 10
to 40.
d) Test For Plastic Limit
1. About 30g of air dry soil passing 425μ sieve was taken and it was mixed thoroughly with distilled water until the mass
became plastic enough to be easily rolled into a ball.

2. A portion of the ball was taken and rolled on a glass plate with the hand to form the soil mass into a thread of uniform
diameter of 3mm throughout its length.
3. The soil was now kneaded together and again rolled out in the form of a ball.
4. The step 2 was repeated until a 3mm diameter thread showed signs of crumbling. Some of the crumbled material was taken
for water content determination.
e) Test For Free Swell Index
1. Take 20 grams of sand and pass it through the 4.25 µm sieve.
2. Then, dry it in the oven until it gets dry without any presence of moisture.
3. Take 10 grams of sand in a graduated glass cylinder with distilled water of 100 ml capacity, and another 10 grams of sand in a
graduated glass cylinder with kerosene of 100 ml capacity.
4. Stir and shake both the glass cylinder thoroughly, until all entrapped air and bubbles get eliminated.
5. Allow the entire setup without disturbing for 24 hours, so that it will be in an equilibrium state.
6. After 24 hours period, determine the volume of the sand in distilled water as Vd and determine the volume of the sand in
kerosene as Vk.
f) Test For Specific Gravity
1. Clean and dry the density bottle
wash the bottle with water and allow it to drain.
Wash it with alcohol and drain it to remove water.
Wash it with ether, to remove alcohol and drain ether.
2. Weigh the empty bottle with stopper (W1)
3. Take about 10 to 20 gm of oven soil sample which is cooled in a desiccator. Transfer it to the bottle. Find the weight of the
bottle and soil (W2).
4. Put 10ml of distilled water in the bottle to allow the soil to soak completely. Leave it for about 2 hours.
5. Again fill the bottle completely with distilled water put the stopper and keep the bottle under constant temperature water
baths (Tx0 ).
6. Take the bottle outside and wipe it clean and dry note. Now determine the weight of the bottle and the contents (W3).
7. Now empty the bottle and thoroughly clean it. Fill the bottle with only distilled water and weigh it. Let it be W4 at temperature
(Tx0 C).
8. Repeat the same process for 2 to 3 times, to take the average reading of it.
g) Test For Moisture Content
1. Clean the container with lid and dry the container. After that weigh it and note it as (W1).
2. Take a specimen of the sample in the container and weigh with lid (W2).
3. Keep the container in the oven with lid removed. Dry the specimen to constant weight maintaining the temperature
between 10500C to 11000C for a period varying with the type of soil. Usually 16 to 24 hours are taken for oven drying the
specimen.

4. Record the final constant weight (W3) of the container with dried soil sample. Peat and other organic soils are to be dried at
lower temperature (say 600) possibly for a longer period.
3. RESULTS AND DISSCUSSIONS
The test results of the samples are given below. Table - 1: Physical Properties of Clay
Sl No.
Soil
Clay
Property
1 Specific 2.7
Gravity
2
Natural
92.23
Moisture
Content (%)
3 Liquid Limit 110
(%)
4 Plastic Limit 52.1
(%)
5 Free Swell 4.15
Index (cc/g)
Table – 2 : Physical Properties of Clay treated with 6% Lime and 4% Sulphate
Curing Liquid Plastic Free Unconfine
Sl Period Limit Limit Swell d
No (%) (%) Index Compress
(Cc / G) ion Test
(Kpa)
1 0 day 118 55.7 4.77 7.50
2 7 day 117 61.8 4.72 28.04
3 28 day 114 59.31 4.68 53.88
4 60 day 100 60.29 4.59 49.83
Table – 3 : Physical Properties of Clay treated with 6% Lime , 4% Sulphate and Barium Hydroxide
S SAMPLE CUR LIQ PLAS FRE UNCONF
L DESCRI ING UID TIC E INED
N PTION PERI LIM LIMI SW COMPRE
O. OD IT T ELL SSION
(%) (%) IND TEST
EX (KPa)
(cc
/ g)
1 Clay + 0 4.64 6.15
6% lime day 116 58.2
+ 4% 7 60.15 4.60 26.57
sulphate day 113
+0.5% 28 104 63.91 4.35 45.69
barium day
60 96 64.48 4.27 69.43
day
2 Clay + 0 107 58.37 4.49 7.11

6% lime day
+ 4% 7 100 60.29 4.21 25.80
sulphate day
+1.5% 28 93 59.8 4.19 47.27
barium day
60 89 63.4 4.07 81.99
day
3 Clay + 0 98 58.8 4.18 7.51
6% lime day
+ 4% 7 95 59.74 4.09 27.4
sulphate day
+3.5% 28 94 62.07 3.98 61.35
barium day
60 87 64.6 - 100.9
day
Chart – 1: Variation of Unconfined Compressive Strength with curing period
4. CONCLUSIONS
1. With 6% lime and presence of any quantity of sulphate, liquid limit is found to show a decreasing trend with time.
2. It is necessary to determine the sulphate content prior to stabilization of Cochin marine clays with lime.
3. Addition of barium compound further decreases the liquid limit.
4. Free swell index decreases with curing period for lime treated sulphatic clays.
5. Treatment with barium compounds further decreases free swell index.
6. The clay containing sodium sulphate has increased strength values when barium compound was used with lime as
compared with specimens treated with lime only.
7. Percentage variation of strength by barium compound 0.5 Ba - 39.33% Ba - 64.53% Ba - 102.48%
REFERENCES
[1] Arabani, M. and Veis, M. “Geomechanical properties of limestabilized clayey sands”, The Arabian Journal for Science and
Engineering, 2007 Vol. 32, No. 1B, pp. 11-25.
[2] G Rajasekaran “Sulphate Attack and Ettringite formation in Lime Stabilized Marine Clay”Ocean Engineering, 2005, Vol. 32
(8–9),pp. 1133–1159.
[3] ASTM C 1580 – 09, Standard test method for water – soluble sulfate in soil.

[4] Abraham, B. M. “A study on the strength and compressibility characteristics of Cochin marine clays”, Ph.D Thesis, School of
Engineering, Cochin University of Science & Technology, Kochi, 1993.
[5]. Ferris, G. A., Eades, J. L., Graves, R. E. and McClellan,
G. H.“Improved characteristics in sulphate soils treated with barium compounds before lime stabilization”, Trans. Res. Rec.
1295, Washington, 1991, DC,pp. 45–51.
[6]. Bell, F.G. “Stabilization and treatment of clay soils with lime”,part I - Basic Principles, Ground Engineering, 1988 (a), vol. 21,
No. 1, pp 10-15.
[7]. Bell, F.G.“Stabilization and treatment of clay soils withlime”, part II – Some applications, Ground Engineering, 1988 (b) vol.
21, No. 2,pp 25-29.
[8]. Al-Rawi, N. M.“The effect of curing temperature on lime stabilization”, Proceedings of the 2nd Australian Conference on
Engineering Materials, 1988, Sydney, pp. 611-662

IRJET- Mitigation of Effect of Sulphate in Lime Stabilized Marine Clay

More Related Content

What's hot (20)

Similar to IRJET- Mitigation of Effect of Sulphate in Lime Stabilized Marine Clay (20)

More from IRJET Journal (20)

Recently uploaded (20)

IRJET- Mitigation of Effect of Sulphate in Lime Stabilized Marine Clay