Lec 11 polymer and polymerization part ii

Polymer And Polymerization
Part II
Lec. 11
DR. Heba A. Mohammad
Uruk University

Denture Base Resin Material
• Various materials has been used to construct dentures like cellulose
products, phenol- formaldehyde, vinyl resins and vulcanite, however they
have suffering from a variety of problems.
• Acrylic resin (polymethyl methacrylate) (PMMA) is now the material of
choice to use as denture base material because it is easy to process and
use, cheep and good esthetic. Even so it is not ideal in all respects.
03/02/2016Uruk University Dr. Heba A. Mohammad
2

The ideal requirements of denture base material
1. Natural appearance.
2. High strength, stiffness, hardness and toughness.
3. Dimensionally stability.
4. Tasteless, odorless, non toxic and none irritating the oral tissue.
5. Insoluble in saliva or other fluids taken in to the mouth.
6. Good retention to polymer, porcelain and metals.
7. Easy to fabricate and Easy to repair.
8. Good shelf life.
3

9. Low density.
10.Accurate reproduction of surface details.
11.Resistance to bacterial growth.
12.Good thermal conductivity.
13.Radiopacity
14.Easy to clean
15.Inexpensive to use
16.The softening temperature should be higher than mouth temperature.
4

The types of polymethyl methacrylate resin denture base
1. Heat cure denture base resin, set by heat (water bath and microwave).
2. Cold cure, self cure denture base resin.
3. Light cure denture base resin.
4. Pour and cure resin. Very fluid resin and poured into the model.
5

Heat cure denture base resin
Compositions:
• The heat cure acrylic resin supplied as powder and liquid.
6

Powder:
1. Poly methyl methacrylate beads or granules so they are already
polymerized not monomer. (Main ingredient which will polymerize).
2. Benzoyl peroxide (initiator to produce free radicals).
3. Dibutyl phthalate (Plasticizer to make it softer and added flexibility).
4. Zinc or titanium oxide (opacifier to make it radio-opaque).
5. Pigments.
6. Synthetic fibers (nylon acrylic to look like blood vessels and to give the
gingival tissues natural appearance).
7

Liquid:
1. Methyl methacrylate monomer.
2. Cross linking agent that improves the mechanical properties (add
strength)
3. Hydroquinone Inhibitor prevent setting while storage.
8

Methyl methacrylate monomer
It is a clear transparent liquid (colorless), liquid at room temperature. It
has typical smell of its own (Sweetish Odor).
Can get evaporated (Volatile).
Inflammable.
Should store in dark colored bottle.
It is a known allergen.
Boiling point 100.8 C, Melting point -48C.
Light weight.
Volumetric shrinkage during polymerization of 21%.
Powder/liquid ratio is 3:1 by volume or 2.5:1 by weight.
9

Manipulation of heat cure acrylic resin (polymer-
monomer interaction)
• The liquid is placed in clean and dry mixing jar-then powder is
added slowly and mixed in proper proportion and allow each
powder particles to become wetted by monomer and workable
mass is formed and left until it reaches a consistency suitable
for packing. During this period, a cover should be placed above
the mixing jar to avoid monomer evaporation. The type of the
reaction is addition polymerization reaction (it is extremely
exothermic reaction).
10

• The resultant mixture will pass into 5 stages:
1. Sandy stage: the monomer wets the outside of the
polymers particles.
2. Sticky stage: the monomer attaches the surface of the
polymer beads, some polymer chains are dispersed in
the liquid monomer, the viscosity of the mixture was
increased, this stage is characterized by stickiness when
the materials is touched.
3. Dough like stage: when the monomer diffuses further
into the polymer particles and the mass become
saturated. The mass doe snot adhere to the walls of the
mixing jar, clinically the mass behaves like as pliable
dough.
11

4. Rubber or elastic stage: in this stage monomer is dissipated by
evaporation and by further penetration into the remaining polymer beads.
The mass is no longer plastic, its rubber like.
5. Stiff stage: on standing for period, the mixture becomes stiff. This may
be attributed to the evaporation of free monomer. Clinically the mixture
appears very dry.
12

• Dough forming time: the time from beginning of mixing of polymer with
monomer until reaching the dough like consistency less than 10 min.
• Working time: The time that the mixture remains in dough like stage.
The dough remains moldable for at least 5mins.
• the working time is affected by temperature.
• In warm weather when the working time is insufficient can be extended by
refrigeration (the resin store in refrigerator in airtight container to avoid
moisture contamination).
13

• The complete Polymerization not occurs until the denture flask
is heated to above 70 C. (In heat activated acrylic resin).
• The chemically activated materials start to polymerization soon
after the powder and liquid are mixed and proceed more rapidly
through the various consistency stages than the heat accelerated
types.
14

Technical consideration: Heat activated denture resin are shaped by:
1. Injection molding technique.
2. Compression mold technique
15

Injection Molding Technique
• This technique required a special thermoplastic resin
and special equipment.
• The fluid resin is contained in the injector and is
forced into the mould space as needed.
• It is kept under pressure until it has hardened.
16

17

Compression mold technique
• This is the most commonly used technique in the fabrication of acrylic
resin denture.
• The steps of this technique are:
1. Preparation of the waxed denture pattern.
2. Preparation of the mould. (Flasking, De waxing).
18

19

20
COMPLETED FLASKING
FOR THE MANDIBULAR
COMPLETE DENTURE.
STONE CAP
UPPER
HALF STONE
STONE CAST
LOWER HALF STONE

21
Wax Elimination procedure

22

3. Application of separating medium.
4. Mixing of powder and liquid (Placing acrylic dough in the mould).
5. Packing, closing the flask together and removing the excess.
23

24

25

6. Curing (Heat curing under pressure, the denture flask under pressure is
placed in heated water bath or microwave oven).
7. Cooling, deflasking, finishing and polishing.
26

27

28

Polymerization cycle or curing cycle
• The curing cycle or polymerization cycle is the technical name
for the heating process used to control the initial propagation of
polymerization in the denture mould.
• This process should be well controlled to avoid the effect of
uncontrolled temperature rise such as boiling of monomer and
denture base porosity
29

• Curing may be done either:
1. In water bath to raise the temperature.
2. In microwave oven (where the flask used should be non metallic
type).
• There are two recommended curing cycles:
1. Long curing cycle: Curing in a constant temperature water bath (8hr-
10hr at 74 C). (The satisfactory processing).
2. Short curing cycles: curing for 2hr at 74C then l hour at 100C.
30

Cooling: The flask should be cooled slowly i.e. bench cooled. Fast
cooling can result in warpage of the denture due to different in thermal
contraction of the resin and the gypsum product mould. Cooling over
night is ideal.
Deflasking: The cured acrylic denture is removed from the flask,
deflasking should be done with care to avoid breaking of the acrylic
denture.
31

Properties of heat cured acrylic resin
1. Taste and odor: completely polymerized acrylic resin is tasteless and
odorless.
2. Esthetic: it is clear transparent resin which can be pigmented (colored)
easily to duplicate the oral tissue. It is compatible with dyed synthetic
fillers so esthetic is accepted.
3. Density: the polymer has a density about 1.2 gm/Cm3.
4. Strength: these materials are typically low in strength. Compression
strength=75 Mpa , while the tensile strengths 52 Mpa. The cold cured
resin has lower strength value than the heat cure acrylic.
32

5. Impact strength: it has lower impact strength, the ideal denture resin
should have high impact strength to prevent breakage when it is
accidently dropped, Addition of plasticizers increases the impact
strength. Self cured acrylic has lower impact strength.
6. Hardness: acrylic has lower hardness, can he easily scratches. Self
cured acrylic has lower hardness value than Heat cured acrylic.
Brienell hardness number heat cure acrylic: 22 while for cold cure resin
16-18.
7. Modulous of elasticity: they are sufficient stiff for use in complete and
partial dentures. When compared with metal denture bases it has very
low stiffness (more flexible than metal). The cold cured resin have
slightly low modulous of elasticity than the heat cure acrylic.
33

8. Dimensional stability: well processed acrylic resin denture base has
good dimensional stability. The processing shrinkage is balanced by
expansion due to water sorption.
9. Shrinkage: acrylic resin shrinkage during processing due to:
1. Thermal shrinkage on cooling.
2. Polymerization shrinkage.
• Polymerization shrinkage of heat cure acrylic (volume shrinkage 8%,
linear shrinkage 0.53 %) while the linear shrinkage of cold cure resin
about 0.25%
10.Water sorption: acrylic resins absorb water and expand (0.6mg/cm2).
This partially compensates for its processing shrinkage. This
shrinkage is reversible. Thus on drying they lose water and
shrink.
• However repeated wetting and drying should be avoided as it may cause
warpage of the denture.
34

11.Solubility: acrylic resin is insoluble in water and oral fluids. They are
soluble in Ketons and esters.
12.Thermal conductivity: they are poor conductors of heat. This is
undesirable because the patient wearing acrylic dentures often
complain that they cannot feel the temperature of food or liquids they
ingest.
13.Coefficient of Thermal Expansion: Acrylic has High Coefficient of
Thermal Expansion about 76 *10'6 Cm/Cm.C°. Addition of fillers
reduces the coefficient of expansion.
14.Color stability: Heat cured acrylic have good color stability. Cold
cured is slightly lower (yellows very slightly).
15.Biocompatibility: Completely polymerized acrylics are
biocompatible due to low percentage of residual monomer, so allergic
reactions to acrylic resin may be seen in the oral cavity.
35

16. Adhesion: Adhesion of acrylic to metal and porcelain is poor and
mechanical retention is required. Adhesion to plastic denture teeth is good
(chemical adhesion).
17.Residual monomer: Instances of toxicity or allergic reaction have been
related to excessive residual Monomer that results from improper
processing. The highest Residual monomer level is observed with cold cure
acrylic. During the polymerization process of the hot cured acrylic the
amount of Residual monomer decrease firstly rapidly and then later more
slowly. It should be processed for a long time to reduce the Residual
monomer.
36

Chemical Activated Resin
• Also called auto polymerized or cold cure or self cure polymethyl
methacrylate.
• Composition same as the heat cure version with following differences:
1. The powder contains small particles size beads of polymer of poly
methyl methacrylate that have a lower molecular wt. and contain
benzyl peroxide (initiator).
2. The liquid contains a chemical activator ((l-2%)tertiary aromatic
amine) which activated the benzyl peroxide (initiator) to produce free
radicals so that polymerization is initiated in manner similar to that
describe for heat cure acrylic. (Upon mixing tertiary amine causes
activation of benzyl peroxide). 03/02/2016Uruk University Dr. Heba A. Mohammad
37

Cold cure compared to heat cure acrylic
1. Low molecular weight (degree of polymerization not completed
compared to that achieved using heat activated).
2. Dentures processed have more residual monomer (3-5%). While heat
cured resin is reach up to 1%.
3. Color stability inferior (tertiary aromatic amine susceptible to
oxidation), stabilizing agents should be added.
38

4. Working time is shorter than heat cure acrylic. The chemically
accelerated materials start to polymerize soon after the powder and liquid
are mixed and proceed more rapidly through the various consistency stage
than the heat accelerated type.
5. Less shrinkage than heat cures resin (Lower dimensional change).
6. Decreased transverse strength (residual monomer act as plasticizer).
7. Lower hardness.
39

Light activated denture base resins
This material is a composite having a matrix of urethane
dimethacrylate with an acrylic copolymer, microfine silica fillers,
inhibitors and light initiator for polymerization (comphorquinone
amine).
It is supplied in premixed sheets (Single component) and rope form in
light proof pouches having clay like consistency.
 It is polymerized in a light chamber (curing unit) with visible blue light
(400-500nm) is the activator in curing unit.
40

41

Microwave polymerized polymer
• Resins are the same as used with conventional material or using
specially microwave acrylic resin and are processed in a microwave by
using non metallic flask.
• The properties and the accuracy of these materials have been shown to
be as good as or better than those of the conventional heat cured
material. The advantages of microwave curing are cleaner and faster
than the water bath polymerization. Processing time is much shorter
(4-5 min).
42

43

Thermoplastic polymer (flexible dentures)
• Thermoplastic resins are used for the fabrication of flexible
denture.
• A thermoplastic is a plastic which becomes pliable or
moldable above a specific temperature and returns to a solid
state upon cooling.
• There are different kinds of thermoplastic resin like:
1. Thermoplastic acetal. 3. Thermoplastic polycarbonate.
2. Thermoplastic acrylic. 4. Thermoplastic nylon.
44

• The Thermoplastic nylon is used as a denture base in every case
specially used in partial and complete denture when we have undercut
(because of the flexibility of the material) also used in tilted teeth,
patient allergy to acrylic monomer, (there is no free monomer in this
material), patient allergic to nickel, if there is reduced mouth opening
and when we need high esthetic demand.
45

• Chemically nylons are condensation copolymers formed by
reacting equal parts of diamide and dicarboxylic acid.
• Water result as reaction by product.
• Usually the Thermoplastic nylon is supply as beads and prepared
by injection molding technique (the injection temperature ranges
from 274-293C).
46

Properties of the Thermoplastic nylon
(Flexible dentures)
1. High strength.
2. Excellent flexibility and ductility.
3. It is semi translucent and provides excellent esthetic. No metal clasp
appearance on the tooth surface
4. Bio compatible (frees of monomer and metal which are the principle
cause of allergic reaction).
5. High fracture resistance and impact properties, unbreakable martial
(not fracture even if thrown from height).
47

6. Difficult to adjust, polish and repair.
7. Lower water sorption than PMMA resin.
8. Good resistance to most chemical but they can affect by strong acids and
alcohols.
9. Lightweight.
10.Nylon is aproned to creep.
11.Minimal bonding strength to artificial teeth and to relining material.
12.After short period of time the flexible dentures deteriorate, stain and
develop a rough surface.
48

Processing Errors
1. Porosity.
2. Crazing.
3. Warpage.
49

Porosity
• Presence of voids or bubbles within structure of resin.
• When the porosity present in the surface it:
a. Makes the appearance of the denture base unsightly.
b. Proper cleaning of the denture is not possible, so denture hygiene
and oral hygiene is suffered.
c. It weakens the denture base.
• Porosity can be of two types: internal porosity and external porosity.
50

Internal porosity
It is in form of voids and bubbles within the mass of polymerized acrylic.
Not present on the surface of the denture. It is developed in thick portion of
the denture base.
 Causes:
1. Vaporization of the monomer when the temperature of the resin increases
above the boiling point of the monomer (100.8C).
2. Very low molecular weight polymer exothermic heat of the surface resin
dissipates easily into the investing plaster.
3. The center of the thick portion, the heat cannot be conducted away
therefore the temperature in the thick portion may rise above the boiling
point of monomer causing porosity.
• Minimized by: Denture with excessive thickness should be cured using long
and low temperature curing cycle.
51

External porosity
It can occur due to two reasons
1. Lack of homogeneity: Causes: if the dough is not homogenous at the time of
polymerization the portions containing more monomer will shrink more than
the adjacent area. This localized shrinkage results in voids, the resin appears
white. Minimized by Using proper powder liquid ratio and mix it well. The
mixture is more homogenous in the dough stage (so packing should be done in
dough stage).
2. Lack of adequate pressure: Causes: lack of pressure during polymerization
or inadequate amount of dough in the mould during final closure cause
bubbled which are not spherical and the resin color is lighter. Minimized by
using the required amount of dough in flask and check for excess of flash
during closure (flash indicate there is adequate material).
52

Crazing
Crazing is formation of surface cracks on denture base resin
and has a weakling effect on the resin and reduces the esthetic
qualities.
 The cracks formed can cause fracture.
Causes:
Mechanical stresses (tensile stress).
Attack by solvent (alcohol).
Incorporation of water during processing.
53

Denture warpage
• It is change in shape or deformation of denture which can affect
the fit of the denture.
• Warpage can occur during processing as well as at other times.
54

Causes of Warpage
1. Release of stresses incorporation in denture during
processing. Causes of stress are (curing shrinkage or rapid
cooling or packing of the acrylic in rubber stage or improper
deflasking).
2. Rise in temperature while polishing.
3. Immersion of processed denture in hot water.
4. Re curing of the denture after addition of relining material.
5. Repeated wetting and drying cause warpage of the denture.
55

56

Lec 11 polymer and polymerization part ii

More Related Content

What's hot (20)

Viewers also liked (20)

Similar to Lec 11 polymer and polymerization part ii (20)

More from Ahmed S.Ibrahim (20)

Recently uploaded (20)

Lec 11 polymer and polymerization part ii