Unit 4 ppt mt1

UNIT IV
SHEET METAL PROCESSES
Sheet metal characteristics - Typical shearing operations, bending
and drawing operations – Stretch forming operations ––
Formability of sheet metal – Test methods– Working principle
and application of special forming processes - Hydro forming –
Rubber pad forming – Metal spinning – Introduction to Explosive
forming, Magnetic pulse forming, Peen forming, Super plastic
forming.
1IFETCE/MECH/MERGED/II YR/III SEM/ME2201/MTI/PPT/UNITIV/VER 1.2

• Introduction
• Shearing
• Sheet Metal Characteristics
• Test Methods for Formability
of sheet metals
• Bending sheet and Plate
• Common Bending Operations
• Tube Bending and Forming
• Stretch Forming
• Deep Drawing
• Rubber Forming
• Spinning
• Super Plastic Forming
• Explosive , Magnetic- Pulse, peen,
and Other Forking Processes
• Manufacturing of Honeycomb
Structures
Sheet metal characteristics
2
IFETCE/MECH/MERGED/II YR/III SEM/ME2201/MTI/PPT/UNITIV/VER 1.2

Shearing :
• Sheet metal subjected to shear stress developed between
a punch and a die is called shearing
Schematic illustration of
shearing with a punch and
die, indicating some of the
process variables.
Characteristic features of (b)
a punched hole and (c) the
slug. Note that the scales of
the two figures are different.
3

Shearing
• Shearing usually starts with formation of cracks on
both the top and bottom edges of the work
piece.These cracks meet each other and separation
occurs
Process parameters :
• Shape of the material for the punch and die
• Speed of the punching ,lubrication and clearance

Typical shearing operations
• Several operations based on shearing performed
Punching – sheared slug discarded
Blanking – Slug is the part and the rest is scrap

• Die cutting
• Fine blanking
• Slitting
• Steel rules
• Nibbling
• Scrap in shearing
• Tailor welded blanks
TYPICAL SHEARING
OPERATION

Shearing dies (OPERATIONS):
Clearance : function of type of material,its temper and its
thickness and of the size of the blank and its proximity to
the edges
• Clearance of soft materials are less than harder grades
Punch & die shapes :
• Surfaces of punch and die are flat
• Punch force builds rapidly and entire thickness is
sheared at same time.

Shearing dies
• Fig 16.3 (a) Effect of the clearance,c, between punch
and die in the deformation zone in shearing .As the
clearance increases the material trends to be pulled into
the die rather than be sheared .
8

Compound dies :
• Several operations on the same strip performed in one
stroke at one station with a compound dies
9

Progressive dies :
• Parts produced with multiple operations such as, punching, blanking
and notching are made at high production rates in progressive dies.
16.11 (c) Schematic illustration of making a washer in a progressive die
(d) Forming of the top piece of an aerosol spray can in a progressive die.
Note the part is attached to the strip until the last operation is completed
10

Transfer dies :
• Sheet metal undergoes different operations at different
stations in a straight line or circular path.
11IFETCE/MECH/MERGED/II YR/III SEM/ME2201/MTI/PPT/UNITIV/VER
1.2

Other sheet metal cutting methods
• Band saw
• Flame cutting
• Laser beam cutting
• Friction sawing
• Water-jet cutting

Sheet metal characteristics
TYPICAL RANGE OF AVERAGE NORMAL ANISTROPY(Ravg) FOR
VARIOUS SHEET METALS
Table 16.2
Zinc 0.2
Hot rolled steel 0.8-1.0
Cold rolled rimmed steel 1.0-1.35
Cold rimmed aluminum–killed steel 1.35-1.8
Aluminum 0.6-0.8
Copper and Brass 0.8-1.0
Titanium 4-6

Bending and drawing
operations
• Low carbon steels exhibit this behavior
• This produces lueder’s bands(stretch strain marks)
• These marks can be eliminated by reducing thickness of sheet 0.5 % to 1.5
% by cold rolling process
14

Anisotropy :
• Anisotropy is caused by thermo-mechanical processing
of sheet.
2-types
• Crystallographic anisotropy
• Mechanical fibering
Strains on a tensile-test specimen removed from a piece of sheet metal.These strains
are used in determining the normal and planar anisotropy of sheet metal
15

Grain size :
• Grain size effects mechanical properties & surface appearance
• The coarser the grain the rougher the appearance
Sheet metal formability :
• Sheet metal undergoes two forms of deformation
• Stretching
• Drawing

Cupping test :
• The sheet metal specimen is clamped between two circular
flat dies and a steel or round punch is pushed hydraulically
into the sheet metal until a crack begins to appear on the
stretched specimen
(a) A cupping test (the Erichsen test) to determine the formability of sheet metals. (b) Bulge-
test results on steel sheets of various widths.The specimen farthest left is subjected
to,basically,simple tension.The specimen farthest right is subjected to equal biaxial
stretching
17

BENDING OPERATIONS :
• In bending outer fibers are in tension and inner fibers are in
compression
(a) and (b) The effect of elongated inclusions
(stringers) on cracking,as a function of the
direction of bending with respect to the original
rolling direction of the sheet. (c) Cracks on the
outer surface of an aluminum strip bent to an
angle of 90 degree.Note the narrowing of the
top surface due to the Poisson effect
18

Bend allowance :
• Lb = alf ( R + KT)
Alf – bend angle (radians)
T-sheet thickness
R-bend radius
K-constant
• Bend allowance for ideal case the sheet thickness ;k=0.5
Lb = alf(R+(T/2))
In practice the value of K ranges from 0.33-0.5
• Minimum bend radius
• Engineering strain on a sheet during bending
E = 1 / (2R/T)+1
19IFETCE/MECH/MERGED/II YR/III
SEM/ME2201/MTI/PPT/UNITIV/VER 1.2

Spring back :
• In Bending ,after plastic deformation there is an elastic recovery
this recovery is called spring back.
• Spring back can be calculated approximately in terms if radii Ri
and Rf
• Ri/Rf = 4 ( Ri Y / ET )3
– 3 (Ri Y /ET) + 1
Spring back Increases as (R/T ratio & yield stress of material )
increases as elastic modulus E decreases
Spring back in bending .The part tends to
recover elastically after ending,and its
bend radius becomes larger.Under
certain conditions,it is possible for the
final bend angle to be smaller than the
original angle(negative spring)
20

Cont’d
Compensation for spring back
• Over bending of part
• Bottoming the punch – coin the bend area by
subjecting it to high localized compressive
between the technique tip of the punch and the die
surface.
• Stretch bending – Part is subjected to tension
while being bent.In order to reduce spring back
bending may also be carried to reduce spring back
bending may also be carried out at elevated
temperatures
21IFETCE/MECH/MERGED/II YR/III
SEM/ME2201/MTI/PPT/UNITIV/VER 1.2

Bending force :
Maximum bending force, P = KYLT2
W
K – constant ranges from 0.3(wiping die) – 0.7(u-die)-1.3(V-die)
Y – yield stress
L- length of the bend
T- thickness of sheet
For a V-die
Max bending force, P = (UTS)LT 2
W
1.2

Press brake forming
– Used for sheets 7M(20ft) or longer and other narrow pieces
– Long dies in a mechanical or hydraulic press for small production runs
– Die material range from hardwood to carbides.
1.2

Roll bending :
– Plates are bent using a set if rolls,various curvatures can
be obtained by adjusting the distance between three rolls
Common die-bending operations,
Showing the die-opening
dimensions, W, used in
calculating bending forces
24

Beading :
• The periphery if the sheet metal is bent into the
cavity of a die
Bead forming with a single die (b) Bead forming with two dies,in a press
brake
25

Dimpling :
• First hole is punched and expanded into a flange
• Flanges can be produced by piercing with shaped
punch
• When bend angle < 90 degrees as in fitting conical
ends its called flanging
1.2

Hemming :
• The edge of the sheet is folded over itself
• This increases stiffness of the part
The metal strip is bent in stages by passing it through a
series of rolls
Seaming :
• Joining two edges of sheet metal by hemming specifically
shaped rollers used for watertight and airtight joints
Stretch forming operations

• Roll forming is used for continuous lengths of sheet metal
• Used for large production runs
Fig: Schematic illustration of the
roll-forming process
Roll forming :
28

Tube bending and forming
• Special tooling required to avoid buckling and folding
29

Bulging
• Process involves placing tabular,conical or curvilinear part into a split-
female die and expanding it

Formability of sheet metal
• Individuals are placed inside the parts and mechanically
expanded in radial direction and finally retracted.
Stretch forming
• Sheet metal clamped along its edges and stretched over
a die or form block in required directions.

Stretch forming
Schematic illustration of a stretch forming process. Aluminum
skins for aircraft can be made by this process
32

Test methods
• Punch forces a flat sheet metal into a deep die
cavity
• Round sheet metal block is placed over a
circular die opening and held in a place with
blank holder & punch forces down into the die
cavity
33

Deep drawing process :
• Wrinkling occurs at the edges

Deep drawability :
• Deep drawability is expressed in LDR
• Limiting drawing ratio (LDR)
LDR – Max blank dia/punch dia =Do/Dp
• Drawability of metal is determined by normal anisotropy( R )
or plastic anisotropy.
R = width strain / thickness strain =Ew /Et

Working principle and application of
special forming processes
• Edges of cups may be wavy this
phenomenon is called Earing
• The above condition is called
planar anisotropy
• Del R = R0 – 2 R45 + R 90 / 2
Where Del R = 0 => no ears formed
Height of the ears increases Del R
increases.
Earning in a drawn steel cup, caused
by the planar anisotropy of the
sheet metal
36

Deep drawing Practice :
• Blank holder pressure – 0.7% -1.0 % of Yield strength + UTS
• Clearance usually – 7% -14 % > sheet thickness
• Draw beads are used to control flow of blank into die cavity.
• Ironing is a process in which the thickness of a drawn cup is
made constant by pushing of the cup through ironing rings.
• Redrawing – Containers or shells which are too difficult to
draw in one operation undergo redrawing

• Drawing without blank holder :
Deep drawing without blank holder must be
provided with sheet metal which is sufficiently
thick to prevent wrinkling
Range : Do – Dp < 5T
Hydro forming

• Lowers forces and increases drawability
• commonly used lubricants are mineral oils ,soap
solutions,heavy duty emulsions.
Tooling & equipment for drawing :
• Tool & die materials are tool steels cast irons carbides
• Equipment is hydraulic press or mechanical press
Lubricants

Rubber forming :
• In bending and embossing of sheet metal , the female
die is replaced with rubber pad
Hydro-form (or) fluid forming process :
• The pressure over rubber membrane is controlled
through out the forming cycle ,with max pressure up to
100 Mpi
• As a result the friction at the punch-cup interface
increases ,this increase reduces the longitudinal tensile
stresses in the cup and delays fracture
40

Rubber pad forming
• Shaping thin sheets by pressing them against a form
with a blunt tool to force the material into a desired
form
• Conventional spinning :
A circular blank if flat or performed sheet metal
hold against a mandrel and rotated ,while a rigid
metal is held against a mandrel and rotated ,wile a
rigid tool deforms and shapes the material over the
mandrel.

Schematic illustration of the conventional spinning process (b) Types of parts
conventionally spun.All parts are antisymmetric
Shear Spinning
42

Metal spinning
• Known as power spinning, flow turning, hydro-spinning,
and spin forging
• Produces axisymmetric conical or curvilinear shape
• Single rollers and two rollers can be used
• It has less wastage of material
• Typical products are rocket-
motor casing and missile
nose cones.

Tube spinning :
• Thickness of cylindrical parts are reduced by spinning
them on a cylindrical mandrel rollers
• Parts can be spun in either direction
• Large tensile elongation up to 2000 % are obtained within
certain temperature ranges and at low strain rates.

Super Plastic forming :
Advantages :
• Lower strength is required and less tooling costs
• Complex shapes with close tolerances can be made
• Weight and material savings
• Little or no residual stress occurs in the formed parts
Disadvantages :
• Materials must not be super elastic at service
temperatures
• Longer cycle times

Introduction to Explosive forming
• Explosive energy used s metal forming
• Sheet-metal blank is clamped over a die
• Assembly is immersed in a tank with water
• Rapid conversion of explosive charge into gas generates a shock
wave .the pressure of this wave is sufficient to form sheet metals

Peak pressure (due to explosion):
caused due to explosion , generated in water
P = k( 3sqrt(w) /R)9
P- in psi
K- constant
TNT- trinitrotoluene
W-weight of explosive in pounds
R- the distance of explosive from the work piece

Diffusion Bonding and Superplastic
Forming

Magnetic
pulse forming
• Suranaree University of Technology Jan-Mar 2007
• Stretch formiing
• • Forming by using tensile forces
• to stretch the material over a tool
• or form block.
• • used most extensively in the
• aircraft industry to produce parts
• of large radius of curvature.
• (normally for uniform cross
• section).

Peen forming
• Known as power spinning, flow turning, hydro-spinning,
and spin forging
• Produces axisymmetric conical or curvilinear shape
• Single rollers and two rollers can be used
• It has less wastage of material
• Typical products are rocket-
motor casing and missile
nose cones.

Super plastic forming.
Maximum bending force, P = KYLT2
W
K – constant ranges from 0.3(wiping die) – 0.7(u-die)-1.3(V-die)
Y – yield stress
L- length of the bend
T- thickness of sheet
For a V-die
Max bending force, P = (UTS)LT 2
W

Unit 4 ppt mt1

More Related Content

What's hot (20)

Viewers also liked (20)

Similar to Unit 4 ppt mt1 (20)

Recently uploaded (20)

Unit 4 ppt mt1