EVALUATION OF CURING BEHAVIOR OF TETRA-FUNCTIONAL EPOXY RESIN WITH METHYL NADIC ANHYDRIDE

International Journal of Advanced Research in Engineering and Technology (IJARET), ISSN 0976 –
6480(Print), ISSN 0976 – 6499(Online), Volume 6, Issue 5, May (2015), pp. 16-23 © IAEME
16
EVALUATION OF CURING BEHAVIOR OF TETRA-
FUNCTIONAL EPOXY RESIN WITH METHYL NADIC
ANHYDRIDE
Krishna Pratap Singh1, 2
*, Vineeta Nigam2
, Anuradha Mishra3
Vijay Kumar1
A.K. Saxena2
1
Central Institute of Plastic Engineering & Technology, Lucknow, India
2
DMSRDE, G. T. Road, Kanpur-208013, India
3
Gautam Buddha University, Greater Noida, India
ABSTRACT
Tetra-functional epoxy resin has been synthesized, starting from 4,4’-diaminodiphenylether
and epichlorohydrin. The curing behavior of synthesized epoxy resin has been evaluated using
methyl nadic anhydride (MNA) as a curing material. The obtained resin was characterized by FT-IR
and 1
HNMR spectroscopy. The curing behavior of epoxy resin with MNA has been studied using
FT-IR and Differential scanning calorimetry (DSC) techniques. The thermal behavior of epoxy resin
has been evaluated using Thermo gravimetric Analyzer (TGA) and DSC techniques. The DSC
analysis of uncured resin with MNA showed the maximum rate of curing at 177 0
C. The cured epoxy
resin showed Tg at 197 0
C. The TGA analysis of cured epoxy resin showed two step degradation,
Tonset at 350 0
C with char yield of 22% at 800 0
C.
Key Words: Epichlorohydrin, Methyl Nadic Anhydride, Curing Agents, Thermo Gravimetric
Analyzer.
INTRODUCTION
Epoxy resins constitute a diverse family of polymers which may be formulated into
elastomers, bonding agents, coatings and matrix formers. A precursor containing multiple epoxy
groups is allowed to react with a co-reactant to form an additive crosslinked network. The diverse
properties which may be engineered into epoxy resin systems find their origin in the chemical
composition of the precursors which bear the epoxy groups and their co-reactants [1-4]. Epoxy resins
are most versatile compounds, widely used for surface protective coatings, electric & electronic
INTERNATIONAL JOURNAL OF ADVANCED RESEARCH IN ENGINEERING
AND TECHNOLOGY (IJARET)
ISSN 0976 - 6480 (Print)
ISSN 0976 - 6499 (Online)
Volume 6, Issue 5, May (2015), pp. 16-23
© IAEME: www.iaeme.com/ IJARET.asp
Journal Impact Factor (2015): 8.5041 (Calculated by GISI)
www.jifactor.com
IJARET
© I A E M E

17
insulating materials and composite matrices because the properties of the composites are primarily
determined by the structure of matrix resins [5-6]. The epoxy resins show superior heat resistance,
better adhesive properties and good mechanical properties. Intensive research efforts are currently
going on to develop new epoxy resins with improved thermal and thermo-mechanical properties
along with physical modification of the classical epoxy resins to enhance the desired properties [7-8].
Another approach to improve the properties of epoxy resins without sacrificing their useful
properties, which is very important, is the choice of a suitable hardener [9].
Recently tetra-functional epoxy resins have been used as a matrix resin to developed high
performance composite materials [10-11]. The conventional epoxy resins have failed to satisfy the
desired properties like superior thermo-oxidative stabilities, high thermo-mechanical strength along
with chemical and moisture resistance to be used for advanced composite material applications [12-
13]. Various ways have been applied to enhance the thermal properties of the epoxy resins, either by
the introduction of aromatic rings which can improve the heat resistance of epoxy resins or by
increasing the number of functionalities of the epoxy resins which can enhance the thermal
properties because of high curing density of cured epoxy resins [14]. Recently multifunctional epoxy
resins have attracted extensive interest of researchers and Industrialist because of their use in
Military and civilian sectors due to their highly cross linked structures, good thermal and mechanical
properties [15-17].
The main aim of the present study is to report the curing behavior of a tetra-functional epoxy
resin using methyl nadic anhydride (MNA) as a curing material and its characterization by FT-IR &
DSC. The thermal properties of the cured resin have been evaluated by thermo gravimetric analysis.
EXPERIMENTAL
4, 4’-diaminodiphenylether (DDE) and methyl nadic anhydride (MNA) were obtained from
Aldrich and used as received. Epichlorohydrin, triethyl amine was purchased from across and used
without any further purification.
INSTRUMENTATION
A 1
HNMR spectrum was recorded in CDCl3 on a 400MHz Bruker T spectrometer. FT-IR
spectrum was recorded on a Perkin Elmer spectrophotometer using KBr as a reference material. The
thermo gravimetric analysis was performed under nitrogen atmosphere on a TA instrument. The
DSC graph was recorded on TA instrument.
The synthesis of epoxy resin has been shown in scheme 1.
SYNTHESIS OF TETRA-FUNCTIONAL EPOXY RESIN
To a 500ml three necked flask equipped with a reflux condenser under nitrogen atmosphere
containing epichlorohydrin (100 ml) was added 4,4’-diaminodiphenylether (19.1g) and triethyl
amine (40.4 g) gradually and the mixture was heated at 65 0
C for 6 hrs. The reaction mixture was
cooled and distilled off to remove the excess of epichlorohydrin. The final viscous product was dried
under vacuum oven at 60 0
C for over night.
1
HNMR (Fig.1): 6.6-6.8ppm (two doublets, 8H) 2.5-3.8ppm (multiplet, 20H),
FT-IR (KBr cm-1
) (Fig.1): 2968, 2927, 2873, 1609, 1510, 1460, 1362, 1245, 1033.

18
Fig.1: 1
HNMR spectrum of synthesized epoxy resin
CURING PROCEDURE OF EPOXY RESIN
The synthesized epoxy was cured with methyl nadic anhydride (MNA). The chemical
structures of epoxy and curing agents are showed in scheme- 1. The reactant compositions were
mixed homogeneously in a 1:0.8 molar ratio for epoxy/anhydride system. The curing cycles were
determined by DSC tracing of the respective epoxy/curing agent composition.
O
H2N NH2
O
Cl
Excess
TEA, 60 0C
O
N NO
O
O
O
O
O
O
Crosslinked
Polymer network
Scheme-1: Synthetic route of epoxy resin.
RESULTS AND DISCUSSION
The tetra-functional epoxy resin has been synthesized by using a conventional method [14].
The formation of precursor material and its polymer have been confirmed by its FT-IR, 1
HNMR
spectroscopy, TGA & DSC.
CURING ANALYSIS
The curing analysis of tetra functional epoxy resin is evaluated by heating a mixture of 1:0.8
ratio of synthesized resin/MNA. At 1000
C for 1 hr, 1250
C for 2 hrs , 1500
C for 2 hrs, 1750
C for 2 hrs,
2000
C for 1 hr, 2500
C for 2 hrs , 3000
C for 2 hrs and 3250
C for 1 hr. No external curing accelerator
has been added, as lone pair of N-atom of tetra functional epoxy resin itself acted as an initiator as
shown in scheme 2.

19
FT-IR ANALYSIS
The FT-IR spectrum of uncured epoxy/MNA resin (Fig. 2) showed the characteristic peak at
1779.5 cm-1
corresponding to the stretching vibration of C=O (anhydride) linkage. The peak at 3063-
2873 cm-1
corresponding to =C-H and –C-H stretching vibrations. The peak at 1609 cm-1
attributed
to the aromatic C=C bond while the peak at 1460 cm-1
which correspond to the characteristic peak of
aromatic ring. The –C-O stretching of epoxide ring showed the characteristic peak at 1033 cm-1
. The
FT-IR spectrum of cured epoxy resin (Fig. 3) showed the characteristic broad peak at 3500 cm-1
corresponding to the stretching vibration of the hydroxyl group of the free and hydrogen bonded -O-
H group. The peak at 1680 cm-1
correspond to the –C=O stretching. The peaks at1779.5 cm-1
which
correspond to the stretching vibration of C=O (anhydride) linkage of uncured resin was not seen in
FT-IR spectrum of cured epoxy resin which supported the formation of polymer network.
Fig.2: FT-IR spectrum of uncured epoxy resin.
Fig.3: FT-IR spectrum of cured epoxy resin.
THERMO-GRAVIMETRIC ANALYSIS
The TGA graph (Fig.4) of cured epoxy resin showed thermal stability of the tetra-functional
epoxy resin up to 350 0
C without any weight loss. The cured epoxy resin showed two step
degradation patterns. The weight loss after 350 0
C was probably due to degradation of aliphatic
chains present in epoxy matrix. The maximum rate of decomposition of cured epoxy resin was
observed at 444 0
C. The weight loss at higher temperature of the cured epoxy resin was attributed
500 1000 1500 2000 2500 3000 3500 4000
0
5
10
15
20
25
30
%T
Wavenumber cm
-1

20
due to degradation of epoxy main chain. The endset degradation temperature of first step degradation
was observed at 525 0
C with char yield 22% at 800 0
C.
Fig.4: TGA graph of cured epoxy resin.
DSC ANALYSIS
The curing behavior of the epoxy resin and curing agent composition was studied by DSC
(Fig.5). The reactivity of the epoxy resin can be directly read from the exothermic starting
temperature. The DSC graph of uncured epoxy/MNA for the curing procedure showed two step
curing pattern (Fig.5). The onset of an exothermic peak at 150 0
C depicted initiation of curing while
the maximum rate of curing was observed at 177 0
C. The curing of tetra-functional epoxy resin
subsided at 225 0
C. The first step curing pattern was observed due to opening of epoxy ring and
formation of ester linkage. The second step curing process initiated at 250 0
C with maximum rate of
curing at 325 0
C. The second step of curing was attributed due to cross linking of double bond of
esterified methyl nadic anhydride. The DSC graph of cured tetra-functional epoxy resin showed the
glass transition temperature at 197 0
C (Fig.6).
0 50 100 150 200 250 300 350
-2
-1
0
1
2
3
4
mW
Temperature (
o
C)
Fig.5: DSC graph of uncured epoxy resin.

21
Fig.6: DSC graph of cured epoxy resin.
O
N NO
O
O
O
O
O
O
O
N NO
O
O
O
O
N NO
O
O
O
OO
NH2R2Ar
O
O N
O
Ar
NO
O
O
OO
NH2R2Ar
Ar
O
N
O
Ar
Step growth nu cleoph ilic
addition p olymeriza tio n
O
O
NH2R2Ar
O
O
O
ArR2H2N
O
O
O
O
O
O
O
O
O
Crosslinking
O
O
O
O
O
O
O
O
Scheme-2: Possible mechanism of polymerization.

22
CONCLUSION
The tetra-functional epoxy resin has been synthesized by the reaction between diamino-
diphenyl ether with epichlorohydrin under mild basic condition. The curing properties of synthesized
epoxy resin have been evaluated using methyl nadic anhydride as a curing agent. The resin has been
characterized by FT-IR and 1
HNMR spectroscopy. The curing behavior of synthesized epoxy resin
has been studied using FT-IR and DSC techniques. The FT-IR analysis of uncured resin along with
MNA showed characteristic peak at 1033 cm-1
corresponding to C-O stretching of epoxy ring,
diminished upon curing and a peak at 3500 corresponding to O-H stretching increased due to
formation of free hydroxyl group by the opening of epoxide ring. The DSC analysis of uncured resin
showed maximum rate of curing at 177 0
C while the cured resin showed Tg at 197 0
C. The TGA
analysis showed two step degradation with thermal stability up to 350 0
C.
REFERENCES
1. Tania D., Patrick J. M., Yan C., William T. K. S. Thermal analysis of some aromatic amine
cured model epoxy resin systems-II: Residues of degradation. Polymer Degradation and
Stability. 54, 67-83, (1996).
2. Wang, C.S., Lee, M.C. Synthesis and modification of a naphthalene-containing tri-functional
epoxy resin for electronic applications. J. Appl. Poly. Sci. 70, 1907-1921, (1998).
3. Wang, C.S., Lee, M.C. Synthesis, characterization, and properties of multifunctional
naphthalene-containing epoxy resins cured with cyanate ester. J. App. Poly. Sci. 73, 1611-
1622, (1999).
4. Kaji, M., Endo, T. Synthesis of a novel epoxy resin containing naphthalene moiety and
properties of its cured polymer with phenol novolac. J. Poly. Sci. Part A Poly. Chem. 37, 3063-
3069, (1999).
5. Cheng, J., Li, J., Zhang, J.Y. Curing behavior and thermal properties of trifunctional epoxy
resin cured by 4, 4’-diaminodiphenyl sulphone, eXPRESS poly. Letters. 3, 501-509, (2009).
6. Cai, Z.Q., Sun, J., Zhou, Q., Xu, J. Synthesis and characterization of a novel liquid-crystalline
epoxy resin combining biphenyl and aromatic ester-type mesogenic units. J. Poly. Sci. Part A
Poly. Chem. 45, 727-720, (2007).
7. Han, S., Yoon, H.G., Suh, K.S., Kim, W.G., Moon, T.J. Cure kinetics of biphenyl epoxy-
phenol novolac resin system using triphenylphosphine as catalyst. J. Poly. Sci. Part A Poly.
Chem. 37, 713-720, (1999).
8. Wang, C.S., Lin, C.H. Synthesis and properties of phosphorus containing advanced epoxy
resins. J. Appl. Poly. Sci. 75, 429-436, (2000).
9. Shieh, J.Y., Wang, C.S. Synthesis and properties of novel phosphorus-containing hardener for
epoxy resins. J. Appl. Poly. Sci. 78, 1636-1644, (2000).
10. Maity, T., Samanta, B.C., Dalai, S. Synthesis, characterisation and curing studies of
BCCOMB. Pigm. & Resin Tech. 36, 30-38, (2007).
11. Ni, Y., Zheng, S. Epoxy resin containing polyphenylsilsesquioxane: Preparation, morphology,
and thermo-mechanical properties. J. Poly. Sci. Part A Poly. Chem. 44, 1093-1105, (2006).
12. Ding, J.P., Tao, J.Q., Fan, L., Yang, S.Y. Synthesis and properties of fluorinated biphenyl-type
epoxy resin. J. Appl. Poly. Sci. 113, 1429-1437, (2009).
13. Carrasco, F., Pages, P., Lacorte, T., Briceno, K. Fourier transform IR and differential scanning
calorimetry study of curing of trifunctional amino-epoxy resin. J. Appl. Poly. Sci. 98, 1524-
1535, (2005).
14. Mustata, F., Bicu, I. Multifunctional epoxy resins: Synthesis and characterization. J. Appl.
Poly. Sci. 77, 2430-2436, (2000).

23
15. Wang, C., Lee, M. Synthesis, characterization, and properties of multifunctional naphthalene-
containing epoxy resins cured with cyanate ester. J. Appl. Poly. Sci. 73, 1611-1622, (1999).
16. Liu, P., Zhang, Q., He, L., Xie, Q., Ding, H. Synthesis and properties of poly (urethane-imide)
diacid/epoxy composites cured with an aziridine system. J. Appl. Poly. Sci. 113, 2628-2637,
(2009).
17. Becker, O., Cheng Y.B., Rusell, J.V., Simon, G.P. Layered Silicate Nanocomposites Based on
Various High-Functionality Epoxy Resins: The Influence of Cure Temperature on
Morphology, Mechanical Properties, and Free Volume. Macromolecules. 36, 1616 –1625,
(2003).
18. T. K. Vishnuvardhan, V. R. Kulkarni, C. Basavaraja, S C Raghavendra, M Revanasiddappa,
Ambika Prasad Mvn and Do Sung Hu, “Synthesis Characterization and Study of Dielectric
Properties of Conducting Co-Polymer of Panippy-Y2o3 Nanocomposites” International
Journal of Advanced Research in Engineering & Technology (IJARET), Volume 4, Issue 6,
2013, pp. 278 - 287, ISSN Print: 0976-6480, ISSN Online: 0976-6499.

EVALUATION OF CURING BEHAVIOR OF TETRA-FUNCTIONAL EPOXY RESIN WITH METHYL NADIC ANHYDRIDE

More Related Content

What's hot (15)

Viewers also liked (12)

Similar to EVALUATION OF CURING BEHAVIOR OF TETRA-FUNCTIONAL EPOXY RESIN WITH METHYL NADIC ANHYDRIDE (20)

More from IAEME Publication (20)

Recently uploaded (20)

EVALUATION OF CURING BEHAVIOR OF TETRA-FUNCTIONAL EPOXY RESIN WITH METHYL NADIC ANHYDRIDE