![Mipa P 911 gb 30/0511
page 1 / 2
Product Information
Product description
Operational Sector : Especially easy to sand two-component polyester filling putty. To
be applied in order to equalise or close possible pin holes, small
irregularities, small paint damages or scratches on the body of
cars, vehicles or machines. Recommended also to be used as a
putty and dowel setting material as well as an adhesive for iron,
wood, stone and porcelain.
Features : - adhesive on iron, steel, aluminium, galvanized substrates and
glass fibre reinforced materials
- easy to sand even after 24h drying
- excellent bending strength
- maximum stability on vertical surfaces.
Characteristics : Binder base: unsaturated polyester resins
Solid content: 87 - 89 weight -%
Spec. weight: 1.70 - 1.74 kg/l DIN 51 757
Colour : beige
Storage : At least 12 months, if the original tins are kept closed.
Hazards identification : VbF: Hazardous materials ordinance:
Mipa P 911 n/a inflammable, Xn harmful
Härter P n/a Xi irritant, O oxidizing, contains
benzoyl peroxide
VOC legislation: EU limiting value for the product (cat. B/b): 250 g/l (2007)
This product contains max. 3 g/l VOC [ 0.03 lbs/gal]
Application
Processing conditions : From 10 °C and up to 90% relative air humidity.
The polyester putty will not harden at under + 10 °C.
Substrate treatment : Iron, steel, aluminium, zinc plated sheet, glass fibre
reinforced materials:
Clean, derust and sand the surface, degrease with Mipa
Silikonentferner (Mipa anti-silicone).
Old coatings:
Remove by sanding all traces of old thermoplastic coats (nitro-
cellulose based paint, 1K-acrylic coats) as well as acid reacting
coats (Washprimer) and synthetic paints.
Primary coats to be treated:
Mipa EP-Grundierfiller and Mipa 2K-Acrylgrund after they have
complete cured.
This data sheet is for information purpose only.To our knowledge the data provided complies with the latest standard and is based
on years of experience in the manufacture of our products.However the data is not binding and without warranty.
MIPA AG · D-84051 Essenbach · Tel. 08703/922-0 · Telefax 08703/922-100](https://image.slidesharecdn.com/infop911lang-110811024208-phpapp01/85/Info-p911-lang-1-320.jpg)
Info p911 lang
- 1. Mipa P 911 gb 30/0511 page 1 / 2 Product Information Product description Operational Sector : Especially easy to sand two-component polyester filling putty. To be applied in order to equalise or close possible pin holes, small irregularities, small paint damages or scratches on the body of cars, vehicles or machines. Recommended also to be used as a putty and dowel setting material as well as an adhesive for iron, wood, stone and porcelain. Features : - adhesive on iron, steel, aluminium, galvanized substrates and glass fibre reinforced materials - easy to sand even after 24h drying - excellent bending strength - maximum stability on vertical surfaces. Characteristics : Binder base: unsaturated polyester resins Solid content: 87 - 89 weight -% Spec. weight: 1.70 - 1.74 kg/l DIN 51 757 Colour : beige Storage : At least 12 months, if the original tins are kept closed. Hazards identification : VbF: Hazardous materials ordinance: Mipa P 911 n/a inflammable, Xn harmful Härter P n/a Xi irritant, O oxidizing, contains benzoyl peroxide VOC legislation: EU limiting value for the product (cat. B/b): 250 g/l (2007) This product contains max. 3 g/l VOC [ 0.03 lbs/gal] Application Processing conditions : From 10 °C and up to 90% relative air humidity. The polyester putty will not harden at under + 10 °C. Substrate treatment : Iron, steel, aluminium, zinc plated sheet, glass fibre reinforced materials: Clean, derust and sand the surface, degrease with Mipa Silikonentferner (Mipa anti-silicone). Old coatings: Remove by sanding all traces of old thermoplastic coats (nitro- cellulose based paint, 1K-acrylic coats) as well as acid reacting coats (Washprimer) and synthetic paints. Primary coats to be treated: Mipa EP-Grundierfiller and Mipa 2K-Acrylgrund after they have complete cured. This data sheet is for information purpose only.To our knowledge the data provided complies with the latest standard and is based on years of experience in the manufacture of our products.However the data is not binding and without warranty. MIPA AG · D-84051 Essenbach · Tel. 08703/922-0 · Telefax 08703/922-100
- 2. Mipa P 911 gb 30/0511 page 2 / 2 Product Information Once Mipa P 911 has dried, it can be over- coated using all customary paint systems. For the sealing of the eventual pores, Mipa P 85 or Mipa P 99 is recommended Mask putty stains with Mipa Füller. Mixing ratio : 2 % Härter P (by weight). Pot life : 4 - 5 minutes. Sanding (20 °C) : Sand dry or wet-on-wet after approx. 20 minutes. Special Remarks Insufficient or an excess addition of hardener can result in a stainy overcoat. A sealing of the surface with Mipa Füller is recommended. Safety Remarks Use only in well ventilated rooms. Do not smoke, eat or drink during application. Keep away from children. When the ventilation is not adequate, suitable individual respiratory protection must be worn. Cleaning of tools Tools should be cleaned immediately after use with Mipa Universalverdünnung. When set hard the putty cannot be removed. This data sheet is for information purpose only. To our knowledge the data provided complies with the latest standard and is based on years of experience in the manufacture of our products.However the data is not binding and without warranty. MIPA AG · D-84051 Essenbach · Tel. 08703/922-0 · Telefax 08703/922-100