Laminating

American Journal of Polymer Science 2012, 2(3): 39-49
DOI: 10.5923/j.ajps.20120203.04
A Review on Coating & Lamination in Textiles: Processes
and Applications
Kunal Singha
Department of Textile Technology, Panipat Institute of Engineering & Technology, Harayana, India
Abstract Coating and lamination are two functional processes which are used make a proper finishing to the textile
material. The coating formulation with different textile grade polymer like PVC, PU, acrylic, PTFE are hugely used to make
a textile product with multipurpose way like- waterproof protective clothing, tarpaulin, protective clothing, electrical insu-
lation etc. on the other hand lamination process is used to prepare some important textile products with daily uses in our
practical life like- blackout curtains and blinds, and c. In this current work is related to details of lamination theory, various
processes, formulations, application, recent developments of the coating and lamination in the textile field.
Keywords Coating, Lamination, PVC, PU, Acrylic, Waterproof Protective Clothing, Tarpaulin, Tarpaulin, Lamination
Theory, Processes, Formulations, Application, Recent Developments
1. Introduction
Coating and laminating are increasingly important tech-
niques for adding value to technical textiles. Coating and
lamination enhance and extend the range of functional per-
formance properties of textiles and the use of these tech-
niques is growing rapidly as the applications for technical
textiles become more diverse. Cheaper fabric structures may
be coated or laminated to provide higher added value to
end-users and higher profit margins to manufacturers. The
key to success in textile coating and lamination depends
upon the application of appropriate technology using modern
machinery[1-3]. Machine productivity is important, but
flexibility in terms of production speed and the versatility of
coating/lamination methods are important factors to consider,
as well as a high level of process monitoring, process control
and automation to satisfy demanding technical specifica-
tions.
2. Coating Technology
Coating is a process in which a polymeric layer is applied
directly to one or both surfaces of the fabric. The polymer
coating must adhere to the textile and a blade or similar
aperture controls the thickness of the viscous polymer. The
coated fabric is heated and the polymer is cured (that is,
polymerized). Where a thick coating is required this may be
built up by applying successive coating layers, layer on
* Corresponding author:
kunalsingha28@gmail.com (Kunal Singha)
Published online at http://journal.sapub.org/ajps
Copyright © 2012 Scientific & Academic Publishing. All Rights Reserved
layer,Interlayer adhesion must therefore be high[2]. Finally,
a thin top layer may be applied for aesthetic or technical
enhancement of the coating. Depending upon the end-use
requirements, heavy-duty technical textile coatings may be
applied at high weight, while other end-uses for high- tech-
nology apparel may require coating weights very low. The
chemical formulation of the coating, the coating thickness
and weight, the number of layers, the form of the technical
textile and the nature of any pre-treatment (such as to stabi-
lize the fabric dimensions prior to coating) are of great im-
portance. Traditionally, coating has been applied to woven
technical textiles, but increasingly warp-knitted, raschel[3],
weft-knitted and nonwoven fabrics must be coated on the
same line. The machinery and method of application of the
coating formulation must be versatile, minimize tensions on
the fabric that may lead to distortion or stretch, and eliminate
problems in knitted fabrics such as curling selvedges. Scroll
opening equipment, weft straightening, tension bars and
selvedge uncurlers may thus be fitted[4-6]. The lighter the
weight of the technical textile the more prone will be the base
fabric for coating to weft line distortion and selvedge curling.
2.1. Coating Formulations
The formulation of a coating is complicated, and it can
contain a wide range of chemicals depending upon the nature
of the polymer, the necessary additives for the specific end
use, whether the coating has to be foamed prior to applica-
tion, and the type of coating machinery to be used. Coatings
may be coloured, translucent or opaque, fluorescent, photo-
luminescent or retro-reflective, according to the end user
requirements[7]. Some thermoplastics are used as they allow
the material to be used as they allow the material to be used
as hot melt adhesive and in some cases for welding tech-
niques. They are used as coating polymers.

40 Kunal Singha: A Review on Coating & Lamination in Textiles: Processes and Applications
Table 1. Some of the useful applications of coating[1,7-9]
Polymer Typical Products
Poly Vinyl Chloride (PVC)
Tarpaulins,Coverings,Large tents and architectural uses
Seat upholstery
PVC polyester-tent covers
Leather
Protective clothing ,aprons
Leisure products,banners,burnting
Polyvynilidene Chloride (PVDC) Blends with acrylics to improve FR in coatings
Polyurethane (PU)
Waterproof protective clothing
Waterproof/breathable protective coating
Aircraft life jackets
Adhesives ,filters used as lacquers for PVC tarpaulins and leather
Acrylic
Backcoating for upholstery including autoseats
Binders for nonwovens & glass fibres
Adhesives
Used as lacquers for tarpaulins
Ethylene Vinyl Acetate (EVA)
Backings for carpets & upholstery
Wall coverings, exhibition board backing
Adhesives
Polyolefins,LDPE,HDPE,Polypropylene.
Light weight coverings, tarpaulins (alternative to PVC)
Sacks
Bulk bags
Silicone
Air bags
Food, Medical applications
Gaskets,seals
Parachutes
Woven curtains
Poly Tetra Fluoro Ethylene (PTFE)
Architectural applications (High abrasion resistance)
Calender belts
Food & Medical uses
Gasket, seats
Natural Rubber (NR)
Carpet backing
Tyres
Life rafts
Conveyor belts
Protective clothing
Escape chutes
Styrene Butadiene Rubber (SBR)
Carpet backing
As Natural Rubber
Nitrile Rubber (acrylonitrile/butadiene)NBR
Oil resistant clothing
Oil seals
Belts & items handling oily or gresy products
Neoprene Rubber
Resistance to chemicals ,ozone,hydrocarbon,selected oils,solvent
Neoprene/glass –High temperature application
Neoprene/polyester –Life rafts,shelter
Neoprene/nylon –Industrial covers,bellows
EPDM Rubber Electric insulasion
Butyl Rubber (BR)
Items containing gases , e.g. air cushions ,pneumatic springs,bellows
(Gas barrier)
Protective clothing – especially for chemicals and acids
Light weight life jackets
Life rafts
Protective clothing
Aircraft carpet backing
Aircraft slide/rafts
Life jackets
Polychlororpene rubber. Hovercraft skirts
(e.g. Neoprene – DuPont)CR Flexible gangway bellow (trains)
Airsprings
Random covers
Airbags
V-belts
Chlorosulphonated polyethylene/rubber
(e.g.Hypalon –DuPont) CSM
Similar to Neoprene used where coloration is necessary and higher
temperature resistance is required . Linear and covers for portable waste
reservoir and waste containment ponds.Single ply roofing
Hypalon/glass-thermal insulation
Hypalon/polyester- diapharm
Hypalon/nylon –roofing
Hypalon/Kevlar-FR protective clothing
Hypalon/neoprene/nylon- inflatable boats
Fluoro elastomer (Viton –DuPont)FKM Specialist protective clothing
Color resistant
Low maintenance finish

American Journal of Polymer Science 2012, 2(3): 39-49 41
Exellent abrasion resistance
Seals substrate from moisture resistance
Modified vinyl acetate Tapes
Nitrile Belting ,tapes,gaskets
Styrene/Acrylic Building products
Butadiene Tapes,footwears,gaskets,binder,labels
Vinididiene Electric paper
Table 2. Function of functional properties of different coating composition[8-10]
Functional Properties Coating chemicals
Stain release
Perfluoro chemical, Polyacrylates, Silicone based products & PVC,
Vinylacetate
Soil release
Water repellent
Hot oil repellent/resistance
Waterproof
Deodrant/antibacterial clean room fabric finishes,Chemicals Poly -hexamethylene biguanide hydrochloride-PHMB,Cyclo dextrin
Chemical odour absorbing Activated carbon based coatings.
Chemical protective Based on Aramide,Teflon, PTFE,Carbon, Neoprene Coating
Breathable coating Hydrophilic, polyacrilamide based products,Polyurethanes
Thermal resistance & insulating PVC,Teflon,Carbon coating,Silicon rubber
Heat & corrosive resistant coating Polytetrafluoroethylene,Perfluorooctanoic acid,Teflon
Stiffness/interlining coating LDPE/HDPE/PVC
Solvent resistance,abrasion resistance,ageing resistance,ozone
resistance
Polyurethane coating
Waterproofing, electrical encapsulasion, sealants Butadiene polyurethane resin
It is important to realize that coating formulations consists
of several additives. Amongst these are UV radiation and
heat stabilizers, antioxidants, fillers to improve the me-
chanical properties, fillers for economy, FR chemicals, re-
inforcement fibers (turning the plastic into a ‘Composite’),
pigments and other compounds necessary to confer further
special properties or to assist with processing[9]. It is nec-
essary to make sure that all the ingredients are compatible
with each other.
The formulation of water-proof coating is become very
popular in the recent uses of demand and for example; some
typical formulations of coatings are as follows;
Table: 3 Formulation of water proof coating using Poly-
urethane solvent-based resins[11]
Polyurethane (granular form) - 30%., Polyisocyanate
crosslinking agent or Melamine formaldehyde resin type and
Acid catalyst
Table 3. Typical formulation of PVC based coating is as follows[12-13]
PVC 40%
Filler(CaCO3) 35%
Primary Plasticiser Dioctyl phthalate
Secondary Plasticiser Carboxy Pardtin Wax
Solvent Ketone/DMT
3. Types of Coating Methods
There are several processes for the application of coating
to the textile material depending upon the requirement of end
product. Some of these processes are described below:
3.1. Direct Coating
The simplest coating procedure is the direct method,
sometimes called the ‘floating knife’ or knife over air tech-
nique where the fabric is stretched flat to form an even uni-
form surface and is transported under a stationary doctor
blade[13]. As the fiber moves forward, it is scraped by the
knife and the polymer resin compound is spread evenly over
the surface as per Fig.1 &Fig.2.These show the knife or
blade over roller method of direct coating. The amount of
polymer applied, the ‘add-on’[14] depends on the concen-
tration of dispersion or solution- this is the so-called ‘solids
content’; other parameters also affect resin add-on as will be
seen.
Uses: Generally fairly tightly woven fabrics capable of
being pulled flat and uniform can be coated by the direct
method. Waterproof protective clothing fabric, automotive
car seat fabrics, tarpaulins and light weight material for
inflatable are produced by the direct method.
3.2. Foamed and Crushed Foam Coating
This method can be used to apply polymer to woven fab-
rics and knitted fabrics and also to fabric produced from spun
yarns or fabrics of a general open construction which cannot
generally be direct coated. This is possible because the foam,
which is rather like shaving cream, sits on the top of coating.
Crushed foam coating increases the no. of fabrics which can
be coated ; it also greatly reduces penetration of resin into the
fabric , which allows the production of much softer handles
and better drape than can generally produced by direct
coating[14]. This technique is used for apparel goods, floor
coverings, wall coverings ,black-out curtains and curtain
linings and filter materials.
3.3. Transfer Coating
The principle of transfer coating is first to spread the
polymer on to release paper to form a film and then to
laminate this film to the fabric. The process is divided in few

steps like;
● Coat the resin (which will become the top layer) on to
the transfer paper and evaporate off the solvent.
● Coat on the second layer, which will become the base
layer (and is actually the adhesive which joins the top layer
to the fabric).
● Lay the fabric on top of the coating, nip together,
evaporate the solvent and crosslink the two layers together.
● Peel the coated fabric off the release paper[15-17].
The main uses of this type of coating technique are the
transfer coated polyurethane fabrics is in up-market and the
waterproof protective clothing. Other outlets for transfer
coated polyurethane include upholstery, luggage, footwear,
gloves and waterproof mattress covers. Woven velvet
automotive seat fabric is sometimes processed in this way to
lock in the pile. Carpets and other articles are also processed
using back licking techniques.
3.4. Hot Melt Extrusion Coating
This method is used for thermoplastic polymers such as
polyurethane, polyolefins and PVC, which are applied by
feeding granules of the material into the nip between moving
heated rollers. There are two general designs in use, the
Zimmer machine, which has two melt rollers the Bema
machine, which has three[18-20]. They are smaller version
of calenders but differ in that they need a fabric (or paper or a
film) as a substrate on which to deposit the film as it is
produced. This method can apply resin (in the form of films)
to fabric at a faster rate than that can be achieved by transfer
coating or direct coating. This process is used to produce
light weight coverings or tarpaulins.
3.5. Calender Coating
Calenders are primarily used to produce unsupported films
of PVC and rubbers from compounded polymer ‘dough’ .
This process can also be adapted to apply freshly produced
film to fabric. Calenders consist of a number of massive
rollers, sometimes five or more in various configurations,
which rotate to crush the ‘dough’ and smooth it into films of
uniform thickness. The thickness of the film is determined by
the gap separation of the rollers, but there is usually a limit to
the thinness of films which may be produced by this
method[21]. The more rollers, film produced is more accu-
rate. Some of the rollers also generates heat, and the material
is fabricated into a continuous sheet which can be brought
into contact with the fabric to which it adheres.
3.6. Rotary Screen Coating
The rotary screen technique which applies compound to a
fabric by forcing it through a cylindrical screen, it is used
mainly for textile printing. The technique can also be used
for coating polymer onto fabric with add-ons; it is
claimed .from between 5 and 500 g/m2
. The add-on is con-
trolled by resin viscosity, the mesh of the cylindrical screen;
the speed and the pressure of the squeegee bar inside the
screen .An array of dots are pushed through the perforated
screen by the squeegee bar inside the screen and by cen-
trifugal force onto the fabric. The fabric moves at the same
speed as the rotation of the rotary screen and there is, thus, no
frictional contact between the two[22]. When deposited on to
the fabric, the resin in the dots flows and merges together to
form a continuous coating. The rotary screen method can be
used to apply foamed coatings or for foam processing of
fabric finishes instead of padding.
4. Recent Development
These are all the conventional process of coating applica-
tion and formulation but in today’s era the requirements of
human beings has been totally changed , so research is going
on to achieve human needs . Some of such achievements are
phase change coatings, conductive coating, anti bacterial
coating etc. After all introduction of nanotechnology has
changed the thinking. Some of those are discussed below.
4.1. Phase Change Materials
Phase change materials (PCM) take advantage of latent
heat that can be stored or released from a material over a
narrow temperature range[23]. PCM possesses the ability to
change their state with a certain temperature range. These
materials absorb energy during the heating process as phase
change takes place and release energy to the environment in
the phase change range during a reverse cooling process.
Insulation effect reached by the PCM depends on tempera-
ture and time. Recently, the incorporation of PCM in tex-
tiles by coating or encapsulation to make thermo-regulated
smart textiles is going on.
● Working principle of PCM
Figure 1. Change in phase change material with the change in tempera-
ture[24]
The PCMs change phases within a temperature range just
above and below human skin temperature would be suitable
for application in textiles. This interesting property of
PCMs would be useful for making protective textiles in
all-season. Fiber, fabric and foam with PCMs could store
the heat body creates then release it back to body, as it
needs. Since the process of phase change is dynamic (Fig-
ure 1); therefore the materials are constantly changing from
a state to another depending upon level of physical activity
of the body and outside temperature. The thermo-regulating
characteristic is possible in manmade fiber by adding PCM
microcapsules to a polymer solution prior to fiber extrusion.
In the process[24], PCM microcapsules are integrated inside
the fiber itself. Coating, lamination, finishing, melt spinning,
bi-component synthetic fiber extrusion, molding, foam
techniques are some of the convenient processes for PCMs’
incorporation into the textile matrix.

● Coatings using PCM
A coating composition for textiles includes wetted mi-
crospheres containing a phase change material dispersed
throughout a polymer binder, a surfactant, a dispersant, an
antifoam agent and a thickener. Preferred phase change
materials include paraffinic hydrocarbons. The micro-
spheres may be microencapsulated. To prepare the coating
composition, microspheres containing phase change mate-
rial are wetted and dispersed in a dispersion[25-26] of water
solution containing a surfactant, a dispersant, an antifoam
agent and a polymer mixture. The coating would be then
applied to a textile substrate. In an alternative embodiment,
an extensible fabric would be coated with an extensible
binder containing microencapsulated phase change material
to form an extensible, coated fabric. PCM could be incor-
porated into the textiles by coating using polymer such as
acrylic, polyurethane, etc, and applied to the fabric. There
are various coating processes available such as
knife-over-roll, knife-over-air, pad-dry-cure, gravure, dip
coating, and transfer coating. This technique is used in
space suits, sports-wear, medical applications, shoes and
accessories & in automobile textile such as seat cover.
Automobile interior applications use paraffin due to their
high capacity for heat storage; lack of toxicity, corrosive-
ness, or hygroscopic properties; low cost; and amenability
to mixing to realize the desired temperature range.
4.2. Flame Retardancy
Two types of microcapsules of di-ammonium hydrogen
phosphate (DAHP) with respectively polyether- polyure-
thane shell and polyester-polyurethane shell were evaluated
as intumescent flame retardant (FR) in a commercial poly-
urea coating for textiles. The advantages of this new concept
of encapsulated FR agent are to be compatible with a poly-
meric matrix in order to give a permanent FR effect and to be
itself an efficient FR intumescent formulation for many
materials. The thermal degradation for the two types of
DAHP microcapsules shows characteristics of an intumes-
cent formulation. The reaction to fire of cotton fabrics coated
by FR polyurea loaded with neat or microencapsulated
DAHP was studied with the cone calorimeter as the fire
model. Both types of DAHP microcapsule present in the
polyurea coatings on cotton fabric give an efficient FR effect,
although the char developed with microcapsules is a little
less heat resistant than that developed with the pure
DAHP[27]. Coatings containing microcapsules with poly-
ester-polyurethane shells evolve the smallest quantity of
smoke and CO.
4.3. Antibacterial Coating
A novel antibacterial coating for cotton fabrics has been
developed using core-shell particles that consist of poly
(n-butyl acrylate) (PBA) cores and chitosan shells. The
spherical particles are prepared via a surfactant-free emul-
sion copolymerization of n butyl acrylate in an aqueous
chitosan solution induced by a small amount of t-butyl hy-
droperoxide. The PBA-chitosan core-shell particles have a
narrow particle size distribution with average particle di-
ameter of approximately 300 nm, and display highly positive
surface charges. Transmission electron microscopic (TEM)
images clearly reveal well-defined core-shell morphology of
the particles where PBA cores are coated with chitosan shells.
The particle is composed of both the PBA homopolymer and
the chitosan-g-PBA copolymer[28]. The cotton fabric is
coated with PBA-chitosan particles by using a conventional
pad-dry-cure method. The cotton treated with PBA-chitosan
particles demonstrates an excellent antibacterial activity with
bacterial reductions more than 99%. The presence of apa-
tite-coated TiO2 shows antibacterial activity in the presence
of black light or visible light, suggesting its potential use in
reducing the risk of microorganism transmission for textile
applications.
4.4. Conductive Coating
Polypropylene (PP) and viscose (VS) textiles were modi-
fied by the in situ synthesis of a conducting polypyrrole (PPy)
overlayer. To improve adhesion of the conducting layer to
the textile surface, a pyrrole-functionalized silane (SP) was
synthesized and bonded onto the surface before polypyrrole
formation. Moreover, to introduce hydroxyl groups into the
surface, PP was pretreated by grafting vinyltrimethoxysilane
by means of a radiofrequency plasma discharge. The com-
promise between the influence of SP and penetration phe-
nomenon (best conductivity after washing: wVS–
0.2SP/25Py = 3×10−5 S/square)[29]. In the case of poly-
propylene the effect of pretreatment with SP is much better
than for viscose, and a higher concentration of SP leads to
improved fastness of the conductive layer (wmPP–
0.2SP/25Py = 3×10−5 S/square; wmPP–1SP/25Py = 8×10−5
S/square), which indicates that the coating promoted by
means of SP is more favoured than for viscose.
Figure 2. A broad view of different parts of lamination machine[29]
5. Lamination
A laminated (or combined) fabric consists of two or more
layers, one of which is a textile fabric, bonded closely to-
gether by means of an added adhesive, or by the adhesive
properties of one or more of the component layers. Conven-
tional laminated technical textiles normally consist of one or
more textile substrates that are combined using a pre- pre-

pared polymer film or membrane by using adhesives or by
using heat and pressure (Figure 2). Usually the layer in a
laminated fabric consists of a polymeric substance; however,
in some metalized fabrics the metal is not deposited by
chemical deposition but is laminated using an adhesive or by
use of an electric arc.
Environmental considerations have generated greater in-
terest in hot -melt adhesives, compared with the older sol-
vent-based adhesives, or the flame lamination technique, in
which a flame melts polyurethane foam that, while molten, is
pressed in contact with the textile. Adhesion in lamination
may be over the whole fabric surface or of the discrete
type[1-3]. Here the adhesive is applied as a thermo-fusible
resin in the form of a dot coating that imparts greater flexi-
bility and less stiffness to the laminate, factors important in
subsequent molding applications.
5.1. Lamination Theory in Brief
A new first-order shear deformation theory (FSDT) and
sandwich plates has been developed and verified for lami-
nated plates and sandwich plates. Based on the definition of
Reissener - Mindlin's plate theory, the average transverse
shear strains, which are constant through the thickness, are
improved to varythrough the thickness. It is assumed that the
displacement and in-plane strain fields of FSDT can ap-
proximate, in an average sense, those of three-dimensional
theory. Relationship between FSDT and three-dimensional
theory has been systematically established in the averaged
least-square sense. This relationship provides the closed-
form recovering relations for three-dimensional variables
expressed in terms of FSDT variables as well as the im-
proved transverse shear strains. This makes two main con-
tributions. First an enhanced first-order shear deformation
theory (EFSDT) has been developed using an available
higher-order plate theory. Second, it is shown that the dis-
placement fields of any higher-order plate theories can be
recovered by EFSDT variables. The present approach is
applied to an efficient higher-order plate theory[26-27].
Comparisons of deflection and stresses of the laminated
plates and sandwich plates using present theory are made
with the original FSDT and three-dimensional exact solu-
tions. A refined nonlinear zigzag shear deformation theory
of composite laminated plates is presented using a modified
mixed variational formulation. The theory accounts for con-
tinuous piecewise layer-by-layer linear variation approxi-
mation in the thickness direction for the displacements.
Moreover, it includes piecewise stress distributions satisfy-
ing the continuity conditions at the layer interfaces and the
surface conditions. The advantages of this theory are that it
recovers the interlaminar stresses, and does not need any
shear correction factor used in other first-order theories. To
assess this theory, the bending problems of symmetric and
anti symmetric cross-ply laminated plates are solved. Some
numerical results for the deflection and stresses are com-
pared with their counterparts obtained due to three- dimen-
sional elasticity solution and higher-order laminate theories.
In the classical theory of plates (CPT), it is assumed that
plane sections initially normal to the mid surface before
deformation remain plane and normal to that surface after
deformation. This is the result of neglecting transverse shear
strains. However, non-negligible shear deformations occur
in thick and moderately thick plates and the theory gives
inaccurate results for laminated plates. So, it is obvious that
transverse shear deformations have to be taken into account
in the analysis. First order shear deformation theory (FSDT)
and takes the displacement field as linear variations of mid-
plane displacements. In this theory, the relation between the
resultant shear forces and the shear strains is affected by the
shear correction factors. This method has some advantages
due to its simplicity and low computational cost. Some an-
other plate theories, namely, higher order shear deformation
theories (HSDT),[29] which include the effect of transverse
shear deformations provided a simple higher- order theory
which accounts not only for transverse shear strains but also
for a parabolic variation of the transverse shear strains
through the thickness.
5.2. Flame Lamination
Flame lamination can be used to adhere polyurethane
foam to a textile material. A web of
Figure 3. Process of flame lamination[30]
Polyurethane (P.U.) foam from a supply roller is passed
over a gas flame at around 950⁰C and combined with the
textile material from a second roller in the first nip of a
three-bowl system[30]. The foam-laminated textile material
is then passed through the second nip and wound up on a
third roller (Figure 3). Three-ply laminates are possible by
the addition of a second burner to the machine. The major
disadvantage is the high capital cost of equipment-for in-
stance, carbon filter absorbers are needed to clean up the
gaseous emissions so that they comply with legislative re-
quirements. Flame lamination has been widely used for
automotive fabrics.
5.3. Adhesive Lamination-aqueous Based
Adhesive lamination can be used to laminate two fabrics
by applying an aqueous-based pressure-sensitive adhesive

by knife-over-roller spreading. Alternatively, the pres-
sure-sensitive adhesive can be spread on a release paper and
then transfer coated to the textile material, which can then be
combined with a second fabric by bringing these into contact
under heat and pressure to remove the water[21]. Typical of
the adhesives used are natural and synthetic rubber, sty-
rene-butadiene resins (SBRs), polyvinyl alcohol and acrylic
polymers (Figure 4).
Figure 4. Process of adhesive lamination[21]
Figure 5. Process of adhesive lamination-solvent-based[31]
A second method of applying aqueous-based adhesives
using hot -melt polymers is to use rotary screen-printing. The
water is evaporated using infra-red heating, the polymer is
melted and a second layer of material brought into contact
with it to create bonding. Aqueous-based adhesives such as
ethylene vinyl acetate, polyethylene, polyamide, polyesters
and polyurethane can be used, and the adhesives may be
foamed, applied in a specific pattern, and spread by a second
blade after the print head[24-25]. A softer handle with
greater breathability can be obtained using this technique,
but heat-sensitive textile materials may be difficult to control.
Typical uses of this type of technique products include
blackout curtains and blinds, and disposable hospital ap-
parel.
5.4. Adhesive Lamination-solvent-based
Solvent-based adhesives can be used to laminate mi-
cro-porous membranes to textile fabrics to provide a barrier
against liquids (for use in hospital theatre gowns and to
protect mattresses, for instance)[31]. Solvent-based poly-
urethane that cures in the presence of moisture is sprayed on
the fabric and the membrane is nipped against the adhesive
surface (Figure 5). Then the two are held together while
cross-linking takes place to form the necessary bonding.
Engraved roller or screen-printing techniques may also apply
solvent-based adhesives.
5.5. Heat Lamination
Heat lamination using a coating or hot -melt adhesive
supplied as a solid, or slit film net or web can be carried out
on the surface of a heated central drum (180-250[degrees]C)
where the materials are held together as a two-ply composite
under a tensioned continuous pressure blanket[7]. Flatbed
laminating machines can also be used, but the method is
unsuitable for heat-sensitive fabrics (Figure 6). Heat lami-
nation has been widely used for heat-sensitive fabrics.
Figure 6. Process of heat lamination[5]
5.6. Hot -melt Adhesives
Hot -melt adhesives are thermoplastic and can be melted
or softened by heat. When spread on the fabric in the hot
state, lamination with another fabric can occur on
re-solidification as the coating cools down. A variety of
methods can be used with hot -melt adhesives. Slot die ex-
trusion allows high viscosity hot -melt adhesives to be ex-
truded as a continuous film directly on all types of textiles.
Mixing the ho-melt adhesive with air inside. Alternatively,
roller and calender hot -melt coating and laminating may be
used. Hot -melt adhesive, ground down to 60-200 [mu]m
particle size can be applied from an engraved roller (at 250⁰C
or above) in a predetermined pattern to a heat-stable fabric
(Figure 7). Then a second fabric or film is brought into
contact while the adhesive is still molten[23]. In another
application method, adhesive is applied from a hopper
placed above a card-wire covered roller that holds the pow-
der until this is released by a vibrating wire brush. This
scatter-coating method applies the powder in a discontinuous
random pattern. The scatter-coated fabric may be passed into
a flatbed laminator. This contains two driven belts (top and
bottom) with a heating section, in which the adhesive is
melted, and a cooling section, to solidify the adhesive while

the laminate is still under pressure[25].
Figure 7. Hot melt laminating principle in case of PET yarn[25,27]
5.7. Film Lamination
Laminate film is generally categorized into these five
categories (Figure 8):
● Standard thermal laminating films
● Low-temperature thermal laminating films
● Heat-set (or heat-assisted) laminating films
● Pressure-sensitive films
● Liquid laminates[5]
Figure 8. Working principle of film laminating machine[8]
6. Recent Developments in Lamination
Technique
There are several modern developments is going on
through in the field of coating and lamination technology
with the aim of improvements of this emerging area; for
example a few of them has been discussed in below;
6.1. Manufacture of 3D Structures by Cold Low Pressure
Lamination of Ceramic Green Tapes
3D multilayer devices were generated by Laminated Ob-
ject Manufacturing (LOM), a well-known rapid-prototyping
technology. Divergent from this method, commercial ce-
ramic green tapes were used which were laminated by Cold
Low Pressure Lamination (CLPL). In contrast to
thermo-compression, which works at pressures and elevated
temperatures, CLPL allows to join particularly fine, complex
structures with cavities or undercuts, because no mass flow
occurs. This technique is based on gluing the adjacent tapes
by means of an adhesive film at room temperature under a
low pressure[16]. After binder burnout and sintering the
ceramic laminate has a homogenous and dense microstruc-
ture free of interfaces. This modified LOM technique is
particularly suitable for the production of Micro Electro
Mechanical Systems (MEMS).
6.2. Embedding Capacitors and Resistors into Printed
Circuit Boards Using a Sequential Lamination
Technique
Embedding capacitors and resistors into printed circuit
boards (PCBs) offers many benefits over surface mount
technology (SMT) and through-hole packaging (PTH).
These benefits include improvements in electrical perform-
ance and reliability, and potential cost reduction. Embedded
devices also enable signal integrity at speeds over 1 GHz.
Also, replacement of surface mounted discrete passives with
an embedded passives layer allows for tighter component
spacing, fewer holes and a larger routing area[32]. All these
are essential for board miniaturization. However, the goals of
reliability improvement (Table 4), space conservation, per-
formance enhancement and solder joint reduction by using
embedded passives can only be realized if the PCB fabricator
can produce high quality boards in a practical production
environment in a timely manner.
Table 4. Comparison between the continuous and discontinuous lamination techniques
Continuous Lamination (On- / Offline) [20-24] Discontinuous Lamination (Definite-Length) [21,22]
For rubber and plastic parts For rubber and plastic extrusion
Max. lamination. speed : 15 m/min; (depending on compound) Max. lamination. speed : 30 m/min; (depending on compound)
Lamination of most available tapes: heat-bond / Lamination of most available tapes: heat-bond /
pressure sensitive pressure sensitive
Combination equipment for heat-bond
Combination equipment for heat-bond and
and pressure sensitive tapes
Precise tape position Pressure sensitive tapes
Controlled lamination force Precise tape position
Controlled tape stretch Controlled lamination force
Defined tape tension Controlled tape stretch
Controlled temperatures Defined tape tension
Reliable controlled process Controlled temperatures
Control of the process parameter Reliable controlled process
Manual - semiautomatic - automatic – robot-lamination Interface for external data log

6.3. High-performance Polymer Photovoltaic Devices
with Inverted Structure Prepared by Thermal
Lamination
Use of a lamination process for the introduction of Au
electrode, instead of conventional metal evaporation, im-
proved the power conversion efficiency (PCE) of in-
verted-structure photovoltaic devices from 1.6% to 2.6%
based on a bulk hetero junction of poly(3-hexylthiophene)
(P3HT) and (6,6)-phenyl C61 butyric acid methyl ester
(PCBM). X-ray photoelectron spectroscopy indicated that a
thin layer of P3HT is spontaneously formed at the
air/polymer blend layer interface during the spin-coating
process. It is suggested that the vacuum-evaporated gold
could destroy the surface-segregated thin layer of
P3HT[10,25], while the lamination process preserves the
surface structure working as an electron-blocking layer. The
insertion of a PEDOT:PSS layer, between the metal elec-
trode and polymer layer, in the lamination process further
improved the PCE to 3.3% with a short-circuit current den-
sity of 9.94 mA cm−2
, an open-circuit voltage of 0.60 V, and
a fill factor of 55% under AM1.5 100 mW cm−2
irradiation.
6.4. Processing of an Aqueous Tape Casting of
Mesocarbon Microbeads for High-performance
Carbonaceous Laminations
Tape casting is a traditional method for the manufacture of
ceramic laminations. In this study, aqueous tape casting
was adopted to obtain high-performance carbonaceous
laminations with homogeneous density and high strength.
For the preparation of a stable and homogeneous slurry of
mesocarbon microbeads, the research focuses on the
rheological behavior of slurries consisting of a solvent and
additives such as a binder, plasticizer and dispersant. After
three to five slips of casting tape laminated together under 40
MPa at 85 °C and sinter heated to 1400 °C for 1 h at a given
heating ratio, carbonized laminations are obtained with an
average density of 1.66 g/cm3
, a bending strength of 82.76
MPa and an electrical conductivity of 169.2 S/cm. During
sintering of green laminations, the additives are pyrolyzed
at 500 °C to form amorphous carbon[28], which reduces the
electrical conductivity and the mechanical strength of the
carbonized laminations. However, by controlling the total
additive content of the slurries, the influence of the additives
can be reduced to a minimum.
6.5. Novel Cold Chemical Lamination Bonding Tech-
nique—A simple LTCC Thermistor-based Flow
Sensor
Lamination is a quality determining processing step in
fabrication of LTCC multilayer devices for packaging, flu-
idic microsystems, and sensors. DM765E distilled water
dilution was applied, using a paint brush, on a top surface of
a green ceramic piece. The gluing process was carried out at
low pressure about 15MPa at room temperature, achieving
good bonding quality. The method is dedicated to wa-
ter-based slurries. The common LTCC tape bonding method
is thermo-compression. The tapes are joined at high tem-
perature, up to 80°C, and pressures, up to 30 MPa, for 2–15
min. The temperature softens the tapes, facilitating pressure
bonding. This method has several advantages:
thermo-compression gives good encapsulation of the final
device, strong bonding[25, 26], and allows the resulting
structure to have more than 40 layers. However, there is one
important problem: high pressure and temperature cause
deformation of the manufactured structure. The main ad-
vantage of this technique is that the bond is made at room
temperature and low pressure, about 5 MPa, thereby de-
creasing the deformation of the chambers and channels.
However, it also has disadvantages: the increase of pressure
in the chamber during firing destroys modules with closed
chambers, and the laminated stack may crack during the
firing process. The method is therefore best used for mak-
ing open chambers and channels.
7. Lamination Faults
There some faults can be usually appears in the laminated
products during the process. This faults can be removed or
partially decreased by a proper m/c setting, controlling dif-
ferent parameters like; heating, temperature, degree of ad-
hesion limit etc. Few of the lamination faults which generally
frequently appears in lamination process have been dis-
cussed in below (Table 5);
8. Conclusions
The coating and lamination gives a powerful tool for the
advancement of textile technology. It provides the opportu-
nities to produce the special fabrics like water-proof resistant
tarpaulins, coverings, large tents and architectural uses,
backcoating for upholstery including autoseats, Food,
Medical applications, parachutes, Woven curtains, for heat-
sensitive fabrics, automotive fabrics, disposable hospital
apparel etc. the recent developments also enhanced the
lamination and coating technique into state-of-art process of
the future in textile field.
Table 5. List of some common lamination fault in textile finishing[11,12,18]
Faults name Reasons Remedies
Bubbles Improper roller nip pressure Proper roller surface mapping
Particles Poor mixing of laminating pest Excellent grinding of the materials in the laminating pest
Age cracks In stability of the laminating pest/solution/adhesives Advanced camera technology for highest contrast
Misalignment of edges Luck of proper supervisation to the process Easy integration into production lines
Laminating faults Quick process, less time Networking for further evaluation

REFERENCES
[1] Ian H., 2003, Coating and lamination enhance textile per-
formance., Ed. 3rd
Edition, Technical Textiles International.
[2] Mondal. S., 2008, Phase change materials for smart textiles –
An overview, Applied Thermal Engineering., 28,
1536–1550.
[3] Stephen, G., Serge, B., Meryline, R., Isabelle, V., Lan, T.,
Rene, D., and Frank, P., 2005, Flame retarded polyurea with
microencapsulated ammonium phosphate,, Polymer Degra-
dation & Stability, 88, 106-113.
[4] Weijun, Y.L., Fai, M., John, X., Leung, T., Kam, L.D., and
Pei, L., 2005, Novel Core -shell particles with poly (n-butyl
acrylate) cores & chitosan shells as an antibacterial coating
for textiles, Polymer, 46, 10538-10543.
[5] Kangwansupamonkon ,Vichuta ,Suvimol(2009) Antibacterial
effect of apatite-coated titanium dioxide for textiles applica-
tion,Nanomedicine:Nanotechnology,Biology & Medi-
cine,Vol 5,Pages 240-249.
[6] Matejmicusik, T., Igor, M., Katarina, F., and Mohamed, 2007,
Conductive polymer coated textiles: The role of fabric
treatment by pyrrole-functionalised triethoxySilane., 157,
914-923.
[7] Bidoki, S.M., and Wittlinger, R., 2010, Environmental and
economical acceptance of polyvinyl chloride (PVC) coating
agents., Journal of Cleaner Production, 18(3), 219-225.
[8] Krebs, F.C., 2010, Fabrication and processing of polymer
solar cells: A review of printing and coating techniques.,
Solar Energy Materials and Solar Cells, 93(4), 394-412.
[9] Mondal. S., 2008, Phase change materials for smart textiles-
An overview., Applied Thermal Engineering, 28(11-12),
1536-1550.
[10] Krebs, F.C., 2009, Fabrication and processing of polymer
solar cells: A review of printing and coating techniques.,
Solar Energy Materials and Solar Cells, 93(4), 394-412.
[11] Covarel, G., Bensaid, B., Boddaert, X., Giljean, S., Benaben,
P., and Louis, P., In Press, Corrected Proof, Available online
1 October 2011, Characterization of organic ultra-thin film
adhesion on flexible substrate using scratch test technique.,
Surface and Coating Technology.
[12] Gross, M.E., and Martin, P.M., Chapter 11 - Vacuum Polymer
Deposition, Handbook of Deposition Technologies for Films
and Coatings (Third Edition), 2010, Pages 532-553.
[13] Chang, H.Y., Tzeng, W.J., Lin, C.H., and Cheng, S.Y., 2011,
Ionic compounds lamination reaction and characteristics of
photosensitive copper indium sulfide on titania nanotube ar-
rays., Journal of Alloys and Compounds, 509, 35(1),
8700-8706.
[14] Nakamura, M., Yang, C., Tajima, K., and Hashimoto, K.,
2009, High-performance polymer photovoltaic devices with
inverted structure prepared by thermal lamination., Solar
Energy Materials and Solar Cells, 93(9), 1681-1684.
[15] Park, H., Moon, H., Park, S., Lee, J., Yoon, D., Hyun, S., and
Kim, D., 2010, Performance improvement of
anode-supported electrolytes for planar solid oxide fuel cells
via a tape-casting/lamination/co-firing technique., Journal of
Power Sources, 195, 9(1), 2463-2469.
[16] Fern, N., Alam, P., Touaiti, F., and Toivakka, M., 2012,
Fatigue life predictions of porous composite paper coating.,
International Journal of Fatigue, 38, 181-187.
[17] Saxena, K., Mehta, D. S., Rai, V. K., Srivastava, R., Chauhan,
G., and Kamalasanan, M.N., 2008, Implementation of an-
ti-reflection coating to enhance light out-coupling in organic
light-emitting devices., Journal of Luminescence, 128(3),
525-530.
[18] Natural wood effect with UV curable powder coatings., Focus
on Powder Coatings, Volume 2008, Issue 11, November 2008,
Pages 2-5.
[19] Reid, R.G., and Paskaramoorthy, R., 2011, An extension to
classical lamination theory for use with functionally graded
plates., Composite Structures, 93(2), 639-648.
[20] Chang, Y., Chen, C.Y., Luo, F.T., Chao, Y.C., Meng, H.F.,
Zan, H.W., Lin, H.W., Horng, S.F., Chao, T.C., Yeh, H.C.,
and Tseng, M.R., 2012, Vacuum-free lamination of low work
function cathode for efficient solution-processed organic
light-emitting diodes., Organic Electronics, 13(3), 388-393.
[21] Bailey, B.A., Reese, M.O., Olson, D.C., Shaheen, S.E., and
Kopidakis, N., 2011, Air-processed organic photovoltaic de-
vices fabricated with hot press lamination., Organic Elec-
tronics, 12(1), 108-112.
[22] Buchegger, W., Wagner, C., Svasek, P., Lendl, B., Kraft, M.,
and Vellekoop, M.J., 2011, Fabrication and characterization
of a vertical lamination micromixer for mid-IR spectroscopy.,
Sensors and Actuators B: Chemical, 159(1), 336-341.
[23] Shafique, M.F., Laister, A., Clark, M., Miles, R.E., and Ro-
bertson, I.D., 2011, Fabrication of embedded microfluidic
channels in low temperature co-fired ceramic technology
using laser machining and progressive lamination, Journal of
the European Ceramic Society, 31(13), 2199-2204.
[24] J.R. Wagner Jr., 2010, Chapter 9 - Blown film, cast film and
lamination processes., Multilayer Flexible Packaging, 2010,
107-112.
[25] Bishop, C.A., 2011, Products Using Vacuum Deposited
Coatings, Vacuum Deposition onto Webs, Films and Foils
(Second Edition), 2011, 13-51.
[26] Tsukamoto, H., 2010, Design of functionally graded thermal
barrier coatings based on a nonlinear micromechanical ap-
proach., Computational Materials Science, 50(2), 429-436.
[27] Teisala, H., Tuominen, M., Aromaa, M., Makela, J.M., Ste-
pien, M., Saarinen, J.J., Toivakka, M., and Kuusipalo, J.,
2010, Development of superhydrophobic coating on paper-
board surface using the Liquid Flame Spray., Surface and
Coatings Technology, 205(2), 436-445.
[28] Poultney, D., Snell, D., 2008, Use of the Fourier transform
infrared (FTIR) technique for determination of the composi-
tion of final phosphate coatings on grain-oriented electrical
steel., Journal of Magnetism and Magnetic Materials, 320(20),
e649-e652.
[29] Niu, L., Cheng, Y.F., 2008, Development of innovative
coating technology for pipeline operation crossing the per-

mafrost terrain., Construction and Building Materials, 22(4),
417-422.
[30] Ke, X.B., Zheng, Z.F., Zhu, H.Y., Zhang, L.X., and Gao, X.P.,
2009, Metal oxide nanofibres membranes assembled by
spin-coating method., Desalination, 236(1-3), 1-7.
[31] Bang, G., and Kim, S.W., In Press, Corrected Proof, Availa-
ble online 21 December 2011, Biodegradable poly(lactic ac-
id)-based hybrid coating materials for food packaging films
with gas barrier properties., Journal of Industrial and Engi-
neering Chemistry.
[32] Fang, Y., Eames, P.C., Norton, B., Hyde, T., Huang, Y.,
Hewitt, N., 2008, The thermal performance of an electroch-
romic vacuum glazing with selected low-emittance coatings.,
Thin Solid Films, 516, Issue 6(30), 1074-1081.

Laminating

More Related Content

What's hot (20)

Viewers also liked (18)

Similar to Laminating (20)

More from ABU TALEB TARAQUE (20)

Recently uploaded (20)

Laminating