Partial replacement of coarse aggregates by expanded polystyrene beads in concrete

IJRET: International Journal of Research in Engineering and Technology eISSN: 2319-1163 | pISSN: 2321-7308
_______________________________________________________________________________________
Volume: 03 Issue: 02 | Feb-2014, Available @ http://www.ijret.org 238
PARTIAL REPLACEMENT OF COARSE AGGREGATES BY EXPANDED
POLYSTYRENE BEADS IN CONCRETE
Thomas Tamut1
, Rajendra Prabhu2
, Katta Venkataramana3
, Subhash C Yaragal4
1 PG Student, Dept. of Civil Engineering, National Institute of Technology, Karnataka, India
2 Research Scholar, Dept. of Civil Engineering, National Institute of Technology, Karnataka, India
3&4 Professors, Dept. of Civil Engineering, NITK, India
Abstract
With the increase in demand for construction materials, there is a strong need to utilize alternative materials for sustainable
development. The main objective of this investigation is to study the properties, such as compressive strength and tensile strengths of
lightweight concrete containing Expanded Polystyrene (EPS) beads. Its properties are compared with those of the normal concrete
i.e., without EPS beads. EPS beads are used as partial replacement to coarse aggregates. The results showed that the amount of
polystyrene beads incorporated in concrete influences the properties of hardened concrete. At 28 days, it was found that compressive
strength of 5%, 10%, 15%, 20%, 25% and 30% EPS incorporated concrete strengths were 91%, 77 %, 71%, 63%, 57%, and 45%,
respectively when compared to concrete with no EPS case.
Key Words: Expanded polystyrene beads (EPS); Workability; Compressive strength; Splitting tensile strength;
-----------------------------------------------------------------------***-----------------------------------------------------------------------
1. INTRODUCTION
Increase in the developmental activities world over, the
demand for construction materials is increasing exponentially.
This trend will have certainly greater impact on the economic
system of any country. India also is aiming at a high
developmental rate compared to other nations in Asia. There
is heavy demand for the building materials in the domestic
market, which is becoming scarce day by day. At this point
researchers and engineers who have the foresight to keep the
developmental activities abreast and curtail the cost factor
should look out for other alternative building materials.
In this work, an attempt is made to address the possibility of
utilizing Expanded Polystyrene (EPS), a packing material in
the form of beads in concrete, which otherwise is posing a
threat to waste disposal as well as for waste management.
This material is a cause of concern to environmentalists. In
this study, it is attempted to partially replace coarse aggregates
by means of EPS beads. A general discussion on EPS, its
production and its application along with environmental
concerns are being discussed.
Expanded polystyrene (EPS) is a lightweight cellular plastics
material consisting of fine spherical shaped particles which are
comprised of about 98% air and 2% polystyrene. It has a
closed cell structure and cannot absorb water. It has a good
sound and thermal insulation characteristics as well as impact
resistance. Polystyrene foam is a non-biodegradable material.
It is a waste material from packaging industry. It creates
disposal problem. Utilizing crushed polystyrene granules in
concrete is a valuable waste disposal method.
There are many advantages to be gained from the use of
lightweight concrete. These include lighter loads during
construction, reduced self-weight in structures, and increased
thermal resistance. Lightweight concrete is generally accepted
as concrete having a density of about 1800 kg/m3
or less. The
present investigation was taken up, keeping two targets in
view, disposal of the polystyrene waste from the point of view
of environment and for the replacement of aggregate from the
point of view of construction industry. The present study aims
at utilization and the suitability of polystyrene beads as coarse
aggregate. A comparative study on strength parameters is also
done against conventional concrete to study the behavior of
the polystyrene aggregate. For this 5%, 10%, 15%, 20%, 25%
and 30% replacement of coarse aggregate by expanded
polystyrene beads is attempted in this work.
2.0 MATERIALS AND METHODS
The test procedures for assessing the quality of various
materials that are used for preparation of test concrete are
detailed. The types of tests on fresh and hardened concrete are
also described in detail. Expanded polystyrene (EPS) is a
lightweight cellular plastics material consisting of fine
spherical shaped particles which are comprised of about 98%
air and 2% polystyrene. It has a

_______________________________________________________________________________________
2.1 Materials
The ingredients of concrete were Expanded Polystyrene beads
in the form of spheres, (used for filling bean bags), River sand
as fine aggregate, crushed granite stones as coarse aggregate,
43 grade Ordinary Portland Cement conforming to I.S: 8112
and water. The physical properties EPS beads related to the
work are shown in Table1.
Table 1: Properties of expanded polystyrene beads
Specific Gravity Bulk density Particle size
0.011 6.86 kg/m3 Spherical
(8-9 mm dia)
2.2 Experimental program
The physical properties of individual ingredients were
determined. The mix proportions for M30 conventional
concrete mix was arrived as per IS: 10262-2009.
Adopting w/c = 0.46, the proportion of concrete mix is,
W : C : FA : CA
200 : 434 : 660.67 : 999.5
0.461 : 1.000 : 1.522 : 2.303
This concrete mix proportion is taken as the reference or
control mix in the present study. The mix proportion for EPS
beads based concrete is obtained by partially replacing coarse
aggregate with different dosages of polystyrene beads
volumetrically. The quantities of materials for various mixes
are obtained by partial replacement (by volume) of coarse
aggregates by EPS beads.
Cubes of 150mm size for compressive strength evaluation and
cylinders of 150 mm diameter for split tensile tests were
prepared. The specimens were cured in water for 28 days and
then tested. For every mix, 6 cubes of 150 mm size (for
compression tests: 3 numbers each for 7 days and 28 days),
and 3 cylinders of 150mm diameter and 300mm height for
split tensile test were cast. Six levels of replacement of
aggregate were considered, i.e., 5, 10, 15, 20, 25 and 30%.
2.3 Tests on EPS based concretes
2.3.1 Workability
The slump test is the most well-known and widely used test
method to characterize the workability of fresh concrete.
2.3.2 Compressive Strength
Strength of concrete is the most important, although other
characteristics may also be critical and cannot be neglected.
Strength is an important indicator of quality because strength
is directly related to the structure of hardened cement paste.
Even though strength is not a direct measure of durability or
dimensional stability, it has a strong relationship with the
water to cement ratio of the concrete, which in turn influences
durability, dimensional stability and other properties of
concrete.
2.3.3 Split Tensile Strength
Tensile strength governs the cracking behavior and affects
other properties such as stiffness, damping action, and
durability of concrete. It is also important regarding the
behavior of concrete under shear loads. Tensile strength is
determined by either direct tensile tests or by indirect tensile
tests such as flexural or split cylinder tests in accordance with
national standards.
3.0 RESULTS AND DISCUSSION
3.1. General
In this section, results of the various tests conducted on both
control and Polystyrene concrete mixes, both in their fresh and
in hardened states are discussed. In fresh state, their
workability, and in hardened state, their mechanical properties
(compressive and split tension) at 7-days and 28-days of
curing are discussed and are evaluated.
3.2. Fresh concrete mixes
In general, it was observed that workability of a concrete mix
increased on addition of polystyrene. Workability of the
mixes was observed to increase with increase in percentage
replacement of coarse aggregate with polystyrene (as a partial
replacement of aggregate) i.e., higher the polystyrene
replacement, higher was the workability. Bleeding was
observed with the increase in water/cement ratio. Compactions
of the specimen were done with vibrating machine, high
degree of vibration resulted in segregation of polystyrene
beads from the rest and bleeding occurred. The slump values
obtained are tabulated in Table 2.
Table 2: Variation in slump with EPS (%)
Sl.
No.
EPS
Replacement
(%)
Slump (mm)
1 0 35
2 5 35
3 10 40
4 15 42
5 20 45
6 25 55
7 30 60
3.3. Tests on hardened concrete
3.3.1. Compression Tests
Compression testing of the cube specimens was carried out in
a Universal Testing Machine of capacity 2000 kN, as per IS:
516-1959. The load was applied without shock at a rate of
140 kg/sq.cm/min. A set of three cubes were tested for each
of the mix for their compressive strengths at 7 and 28 days of

_______________________________________________________________________________________
curing. The ultimate load at which specimen failed was noted
down for each specimen. Linear average was calculated over
three specimens, provided the individual variation was not
more than ± 15 percent of the average. Specimens after
testing were visually inspected for the rupture surface and
polystyrene beads distribution. The results of compression
test are shown in Figure 1.
It is seen that the compressive strength of all concrete mixes
increased with the increase of age. It is observed that, the
larger the amount of polystyrene beads in concrete, the lesser
the compressive strength. As expected, the normal weight
concrete has more compressive strength at all ages compared
to lightweight concrete. At 28 days, it was found that
compressive strength of 5%, 10%, 15%, 20%, 25% and 30%
EPS based concretes compared to control concrete were 91%,
77 %, 71%, 63%, 56%, and 45%, respectively.
It can be observed that the compressive strengths of all the
Fig. 1: Compressive strength variation percentage of EPS
variation
EPS based concrete mixes, in general, decrease with an
increase in polystyrene beads content. This can be attributed
to,
a. Increase in polystyrene volume, increases the voids
as compared to the control mix.
b. Smooth surface of the polystyrene; hence the
polystyrene beads tend to bond loosely with the
cement paste. It is seen that the polystyrene particles
could be easily plucked and removed from the
rupture surfaces of the cubes after compression tests.
Due to this poor bond characteristic, failure takes
place through the cement paste- polystyrene
interface at much lower stress levels.
c. Low specific gravity of the polystyrene due to which
there is a reduction in overall density of the concrete.
Density affects the compressive strength i.e., an
increase in the density of the mix will increase its
compression strength.
In 0% EPS (control concrete), at 7 days the compressive
strength was 31.77 MPa, and then at 28 days it increased
considerably to 37.18 MPa. In 5%, 10%, 15%, 20%, 25% and
30% EPS based concretes on the other hand, the compressive
strength increased from 7 days to 28 days, the absolute
difference was about 6 to 9 MPa.
3.3.2 Split Tensile Tests
Split tensile tests were carried out, on standard cylindrical
specimens of all the EPS based concrete mixes, as per IS
5816: 1999. This is an indirect method of applying
tension in the form of splitting. The test was
performed on the cylinders of 150 mm diameter and
300 mm height, as per I.S. specifications. The specimen
is placed with its axis horizontal between the platens of
testing machine. Thin strips of 12 mm wide and 3mm
thick were inserted between the cylinder and the
platens of testing machine. The load increment of 140
kN/minute was applied until the failure by splitting
along the vertical diameter took place. The stone
aggregates and EPS beads were uniformly distributed in
the matrix as shown in the Fig.2.
Fig. 2: Broken surfaces of failed cylinders

_______________________________________________________________________________________
The results of split tensile tests are presented in Fig.3.
It is clear from the bar chart that, the higher the amount of
polystyrene beads in concrete mixture, the lower the tensile
strength. Mix with 15% EPS has a relative strength of 80%
and that with 30% EPS has a relative strength of 70%.
Fig. 3: Split Tensile strength at 28 days
4. CONCLUSIONS
The following conclusions were drawn from the study.
1. Increase in the EPS beads content in concrete
mixes reduces the compressive and tensile
strength of concrete.
2. All the EPS concrete without any special bonding
agent show good workability and could easily be
compacted and finished.
3. Workability increases with increase in EPS beads
content.
4. The replacement by using EPS has shown a
positive application as an alternate material in
building nonstructural members, and it also serves
as a solution for EPS disposal.
5.
Obtained results suggest that expanded polystyrene concrete
has scope for nonstructural applications, like wall panels,
partition walls, etc.
REFERENCES
[1] IS 383:1970 “Specifications for coarse and fine aggregates
from natural sources for concrete”, Bureau of Indian
Standards, New Delhi.
[2] IS 456: 2000 – „Code of practice for plain and reinforced
concrete‟, Bureau of Indian Standards, New Delhi.
[3] IS 516: 1959 (Reaffirmed 1999) “Methods of Test for
Strength of Concrete”, Bureau of Indian Standards, New Delhi
[4] IS 2386:1963 “Methods of tests for aggregates for
concrete”, Bureau of Indian Standards, New Delhi
[5] IS: 8112:1989, “Specification for 43 grade ordinary
Portland cement” Bureau of Indian Standards, New Delhi.
[6] IS: 10262: 1982, “Recommended guidelines for concrete
mix design” Bureau of Indian Standards, New Delhi
BIOGRAPHIES:
Thomas Tamut, P.G Student, graduated
in Civil Engineering from Basaveshwar
Engineering College, Bagalkot,
Karnataka, in the year 2011.
Mr. Rajendra Prabhu obtained his B.E
(Civil) and M. Tech (Structural Engg.)
from MIT, Manipal. He worked in the
areas of consultancy, teaching and ready
mix concrete industry. Currently he is
pursuing his doctoral degree in the area
of concrete technology in NITK,
Surathkal.
Prof. Katta Venkataramana graduated from
NIE Mysore, did his Master‟s degree from
Kagoshima University, Japan. He obtained
his doctoral degree from University of
Kyoto, Japan. He is serving as Professor in
the department of Civil Engineering,
NITK, Surathkal from 2002. Currently he
is also discharging his duties as Head of the Department. His
areas of research interests include Earthquake engineering and
Earthquake resistant design, concrete technology, etc.
Dr. Subhash C Yaragal graduated from
NITK Surathkal and obtained his post
graduation and doctoral degrees from
the Indian Institute of Science,
Bangalore. Currently he is serving as
Professor and Associate Dean
(Academic). His areas of interest
include concrete technology, concrete
performance, pipeline engineering and building aerodynamics
and wind tunnel testing.

Partial replacement of coarse aggregates by expanded polystyrene beads in concrete

More Related Content

What's hot (20)

Viewers also liked (10)

Similar to Partial replacement of coarse aggregates by expanded polystyrene beads in concrete (20)

More from eSAT Journals (20)

Recently uploaded (20)

Partial replacement of coarse aggregates by expanded polystyrene beads in concrete