Preparation of metal matrix composites by stir-casting method

INTERNATIONAL Mechanical Engineering and Technology (IJMET), ISSN 0976 –
International Journal of JOURNAL OF MECHANICAL ENGINEERING
6340(Print), ISSN 0976 – 6359(Online) Volume 3, Issue 3, Sep- Dec (2012) © IAEME
AND TECHNOLOGY (IJMET)

ISSN 0976 – 6340 (Print)
ISSN 0976 – 6359 (Online)
IJMET
Volume 3, Issue 3, September - December (2012), pp. 404-411
© IAEME: www.iaeme.com/ijmet.asp ©IAEME
Journal Impact Factor (2012): 3.8071 (Calculated by GISI)
www.jifactor.com

PREPARATION OF METAL-MATRIX COMPOSITES BY STIR-
CASTING METHOD

Mr. Amol D. Sable1, Dr. S. D. Deshmukh2
1
Student of M.E. (Manufacturing Engg), Jawaharlal Nehru Engineering College (JNEC),
Aurangabad, Dr. Babasaheb Ambedkar Marathwada University, Maharashtra, India, E-mail:
amol672006@gmail.com
2
Principal , Jawaharlal Nehru Engineering College (JNEC), Aurangabad, Dr. Babasaheb
Ambedkar Marathwada University, Aurangabad, Maharashtra, India
E-mail: sdeshmukh47@rediffmail.com

ABSTRACT

Composite materials play a vital role at the present modern industrial sectors. Preparations of
metal-matrix composites are light weighted, high strength, extremely hard materials which
were useful for every industrious area like aerospace, motor vehicle industries, mechanical
tools manufacturing industries due to its advantageous properties like light in weight,
flexibility, hardness, simplicity and easily applicable and so on. At the centre of research and
growth of these sectors this paper emphasize the production of metal-matrix AlSiC
composites using the duplex stir-casting method and prepared total six samples of varying
percentile compositions of SiCp – 5%, 10%, 15%, 20%, 25% and 30% with aluminium.
Presently these samples were tested under the hardness test, impact strength test, design of
experiment and micrograph examinations were conducted.

Keywords: Composite Materials, Metal-Matrix Composite, AlSiC Stir-Casting

I. INTRODUCTION

As we know that the metal-matrix composites having extremely hard, abrasion resistance and
mostly light weighted which are useful for the preparation of the high temperature and speed

404

International Journal of Mechanical Engineering and Technology (IJMET), ISSN 0976 –

parts like pistons, axles, high speed wheels and so on. The main focus of this paper is the
preparation of AlSiC composites using stir-casting method homogeneously. We prepared
metal-matrix of AlSiC composites using Al (98.41% Cp) and SiC (320 grit size) by duplex
stir-casting method with high temperature into the graphite crucible with coal-fired furnace.
The prepared homogeneous molten mixture should be poured into the sand moulds and kept
it for solidification. We were prepared six rounded bars and six square shaped bar samples of
varying the composition. These samples are to be checked further the test of hardness, impact
strength, DOE and micrograph examination which will discussed in the next paper.

II. THE MAIN OBJECTIVES OF THE PAPER
2.1 Objectives
The main purpose this paper is to develop the strong light weighted metal-matrix AlSiC
composite material which is useful in the industrial sectors as well as advanced machineries.
The most important part of this paper is to fabricate AlSiC metal-matrix of by homogeneous
stir-casting to produce High Strength Low Cost Material (HSLCM). We adopt the stir-casting
method with high temperature in this project. This types of metal-matrix composite have very
high specific strength, temperature resistance, fatigue resistance, abrasion resistance,
corrosion resistance and stiffness properties that they are used in automotive and heavy goods
vehicle, Braking systems, piston rods, frames, piston pins, valve spring cap, brake discs, axle
tubes, reinforcement blade, gear box casing, turbine blades, racing car wheels and so on.

2.2 Composite Materials

Composites are considered to be mixture of materials different composition. The materials
retain their identities in the composite; that is, they do not dissolve or unite completely into
each other even though they perform. Normally, these materials can be physically identified
and reveal an interface between one another. There were various types of composite
materials; on the basis of matrix constituents these are Metal Matrix Composites (MMCs)
Polymer Matrix Composites (PMCs) and Ceramic Matrix Composites (CMCs) and the other
on the basis of fiber reinforced composites like particulate composites are by dispersing the
particles of different shapes and sizes, layered composites prepared by parallel layers with
two alternate different phases and fiber-reinforced plastics prepared by reinforcing plastic
matrix with high strength fiber materials and infiltration composites. But nowadays the use of
metal-matrix, ceramic-matrix and honey-comb structure plays a significant job which is
useful for the new development. Nowadays fabrication of Silicon-Carbide (SiC) improves the

405


life of modern tools. Silicon carbide or carborundum used as an excellent materials which is
made by 60% sand and 40% coke with addition of saw dust in an electric furnace at very high
temperature about 1500°C with traces amount of salts. The SiC particles are mixed with a
temporary binding agent like glue resins and then compressed and dried at the temperature
2000°C that gives homogeneous interlocked SiC crystals. Duplex-composite materials like
Silicon carbide particles reinforced with aluminium (AlSiC) gives the great strength and also
significantly prevent the severe wear-tear and high stress working.

2.3 Metals-Matrix Composites

Metal-matrix composite structure is generally designated purely by the term metal alloy of
the matrix and the material in the form of the strengthening. The matrix is permeating soft
part generally having excellent tensile strength, hardness, ductility and thermal conductivity
which are set in the hard reinforcements having high toughness and low thermal expansion.
For the development of metal-matrix, light metal composite materials mixed with light metal
alloys are applied as matrix materials. During the metal-matrix production, the main
contribution of special alloys is used in powder metallurgy which is used for the
solidification.
2.4 Stir Casting

The term stir-casting is the process of stirring molten metal’s are used for continuous stirring
particles into metal alloy to melt and immediately pour into the sand mould then cooled and
allow to solidify. In stir-casting, the particles are often tends to form agglomerates, which can
be only dissolved by vigorous stirring with high temperature.

III. METHOD OF PREPARATION OF AlSiC METAL-MATRIX COMPOSITE

There are various types of metal-matrix composite materials fabrication techniques in
engineering field like, Metallurgical melting method, Gas or Pressure infiltration method,
Finishing by machining method, Pressing and sintering method, Forging and extrusion
method, Squeeze or pressure casting method, Compo-casting method, vortex and Stir-casting
method.

406


3.1 Stir-Casting Fabrication

Here we have been adopting the stir-casting method for the preparation of metal-matrix
AlSiC composites. This whirlpool technique provides the high strength homogeneous set of
aluminium composite materials. The necessary apparatus are required to fabricate the
material with stepwise procedure are discussed below;

3.1.1 Frame of stirring system: Frame of the stir-casting system is prepared by 1" x 1"
MS square iron pipes. The height of the frame is 70 cm from the ground and its length
and width is 70 cm each side. The two square pipes are joined in the middle side at a
distance 27cm from both sides which is used for the fitting of motor cum stirrer.
3.1.2 Stirrer Fabrication: Stirrer is made up of mild carbon steel. The length of stirrer is
95 cm and exactly plus sign blade having zigzag angle 90° of each side. The length of
every side of stirrer blade is 9 cm each.
3.1.3 Graphite Crucible: Graphite crucible is used for heating the matrix material. The
height of the crucible is 12 inch and upper side diameter is 8 inch and the bottom side
diameter of the crucible is 6 inch.

407


3.1.4 Motor-Dimmer: The motor is fitted on the centre of the frame having 220 to 1400
rpm for stirring process and the rate of speed is adjusted by dimmer (0 to 260 volts).
3.1.5 Furnace Specification: Underground coal-fired furnace is used for the preparation of
the homogenous metal matrix. The furnace opening dimensions 15" x 15" and the depth
is 30”. Coal is used as fuel in for the preparation.
3.1.6 Raw Material Selection: For the preparation of metal-matrix composite silicon
carbide and aluminium scraps are used as a raw material. Silicon carbide 320 grit size
and 98.41% aluminium scraps required for the preparation.

3.2 Methodology

In the preparation process of this method, stirring has been carried out in graphite crucible in
coal-fired furnace with continuous stirring of the molten metal-matrix gives homogeneous
mixture of composites and instantaneously poured in to the sand mould to get solidify. Coal
is used as a fuel for preparation. The working diagram of the coal-fired furnace is given in the
experimental figure 2;

Experimentation

The experimental arrangement has been assembled by the coupling gear-box motor and mild
steel four blade stirrer used. The melting of the aluminium (98.41%) scraps and silicon
carbide powder (SiCp – 320 grit size) is carried out in the graphite crucible into the coal-fired
furnace. First the scraps of aluminium were preheated for 3 to 4 hours at 450°C and SiC
powder also heated with 900°C and both the preheated mixtures is then mechanically mixed
with each other below their melting points. This metal-matrix AlSiC is then poured into the
graphite crucible and put in to the coal-fired furnace at 760°C temperature.

408


The furnace temperature was first increases above the composites completely melt the scraps
of aluminium and then cooled down just below the components temperature and keep it in a
semi-solid state. At this stage the preheated SiCp were added with manually mixed with each
other. It is very difficult to mix by machine or stirrer when metal-matrix composites are in
semi molten state with manual mixing taking place. When the manual mixing is complete
then automatic stirring will carried out for ten minutes with normal 400 rpm of stirring rate
The temperature rate of the coal-fired furnace should be controlled at 760 ± 10°C in final
mixing process. After complete the process the slurry has been taken into the sand mould
within thirty seconds allow it to solidify. Tests should be taken of solidified samples like
hardness and impact tests. This experiment should repeatedly conducted by varying the
compositions of the composite powder of SiC (5%, 10%, 15%, 20%, 25% and 30%), weight
of aluminium scraps in grams plus weight in grams of SiC powder as shown in the following
chart 1. For each composition variation a total 2 kg (2000 gms) material mix is used for
casting the test samples.

409


Finally we prepared the six types varying samples including rounded bars and square bars as
shown in the given fig. 3.

These final samples are now ready for further testing processes of hardness test, impact
strength test and microstructure examination.

IV. RESULT AND DISCUSSION

The major aim and objectives of this paper is to prepare aluminum based silicon carbide
particulate MMCs with an objective to develop a conventional low cost method of producing
MMCs and to obtain homogenous dispersion of ceramic material. To achieve these objectives
stir casting technique has been adopted. Pure Aluminum and SiC has been chosen as matrix
and reinforcement material respectively. These metal-matrixes are very popular, cheap and
beneficial for the modern engineering fields. After getting the varying the composition AlSiC
(5%, 10%, 15%, 20%, 25% and 30%) samples are ready for the testing. Further we will check
the hardness test, impact strength test and uniform distribution study of reinforcement in
metal-matrix with micro-spectrograph analysis. And also DOE (design of experiment) is
employed to evaluate the parameters for optimization. A full factorial design for several
readings for a given matrix of data would be treated using ANOVA (Analysis of Variance)
based on the percentage of SiC around the prospective sample Our main target is to prepare a
very hard metal-matrix sample which becomes very popular, cheap and beneficial for the
modern engineering era.

V. REFERENCES
[1] Muhammad Hayat Jokhio, Muhammad Ibrahim Panhwar, Mukhtiar Ali Unar,
“Manufacturing of Aluminum Composite Material Using Stir Casting Process”, Mehran
University Research Journal of Engineering & Technology, Volume 30, No. 1, January,
2011, ISSN 0254-7821
[2] Neelima Devi. C, Mahesh.V, Selvaraj. N, “Mechanical characterization of Aluminium

410


silicon carbide composite”, International journal of applied engineering research,
dindigul, Volume 1, No 4, 2011, ISSN 09764259
[3] J.U. Ejiofor, R.G. Reddy, “Developments in the Processing and Properties of
Particulate Al-Si Composites”, JOM publication, of The Minerals, Metals & Materials
Society (1997)
[4] Karl Ulrich Kainer, “BASICS OF METAL MATRIX COMPOSITES”, WILEY-VCH
Verlag GmbH & Co. KGaA, Weinheim, (2006).
[5] Jain & Jain, “ENGINEERING CHEMISTRY”, 15th Edition, Dhanpat Rai Publishing
Company, New Delhi (2006).
[6] R.K. Jain, “PRODUCTION TECHNOLOGY”, 16th Edition, Khanna Publishers, New
Delhi (2006).
[7] “Development of Aluminium Based Silicon Carbide Particulate Metal Matrix
Composite”, Journal of Minerals & Materials Characterization & Engineering, Vol. 8,
No.6, Printed in the USA, (2009) , pp 455-467.
[8] “Development of Particulate Reinforced Aluminium Metal Matrix Composite”, 2nd
International Conference on Engineering Research & Development: Innovations, Benin
City, Nigeria, (2008).
[9] “Metal matrix composites: production by the stir casting method”, Journal of
Materials Processing Technology
[10] http://www.substech.com
[11] http://www.ipublishing.co.in
[12] http://www.ethesis.nitrkl.ac.in/1845/1/nigam%26dilip.pdf

411

Preparation of metal matrix composites by stir-casting method

More Related Content

What's hot (20)

Viewers also liked (20)

Similar to Preparation of metal matrix composites by stir-casting method (20)

More from IAEME Publication (20)

Preparation of metal matrix composites by stir-casting method