Sheeet metal

©2007 John Wiley & Sons, Inc. M P Groover, Fundamentals of
Modern Manufacturing 3/e
SHEET METALWORKING
1. Cutting Operations
2. Bending Operations
3. Drawing
4. Other Sheet Metal Forming Operations
5. Dies and Presses for Sheet Metal Processes
6. Sheet Metal Operations Not Performed on
Presses
7. Bending of Tube Stock

Sheet Metalworking Defined
Cutting and forming operations performed on
relatively thin sheets of metal
 Thickness of sheet metal = 0.4 mm (1/64 in) to
6 mm (1/4 in)
 Thickness of plate stock > 6 mm
 Operations usually performed as cold working

Sheet and Plate Metal Products
 Sheet and plate metal parts for consumer and
industrial products such as
 Automobiles and trucks
 Airplanes
 Railway cars and locomotives
 Farm and construction equipment
 Small and large appliances
 Office furniture
 Computers and office equipment

Advantages of Sheet Metal Parts
 High strength
 Good dimensional accuracy
 Good surface finish
 Relatively low cost
 Economical mass production for large
quantities

Sheet Metalworking Terminology
 Punch and die -‑ ‑ tooling to perform
cutting, bending, and drawing
 Stamping press - machine tool that
performs most sheet metal operations
 Stampings - sheet metal products

Basic Types of Sheet Metal Processes
1. Cutting
 Shearing to separate large sheets
 Blanking to cut part perimeters out of
sheet metal
 Punching to make holes in sheet metal
2. Bending
 Straining sheet around a straight axis
3. Drawing
 Forming of sheet into convex or concave
shapes

Figure 20.1 Shearing of sheet metal between two cutting edges:
(1) just before the punch contacts work; (2) punch begins to
push into work, causing plastic deformation;
Sheet Metal Cutting

Figure 20.1 Shearing of sheet metal between two cutting edges:
(3) punch compresses and penetrates into work causing a
smooth cut surface; (4) fracture is initiated at the opposing
cutting edges which separates the sheet.
Sheet Metal Cutting

Shearing, Blanking, and Punching
Three principal operations in pressworking that
cut sheet metal:
 Shearing
 Blanking
 Punching

Shearing
Sheet metal cutting operation along a straight line
between two cutting edges
 Typically used to cut large sheets
Figure 20.3 Shearing operation: (a) side view of the
shearing operation; (b) front view of power shears
equipped with inclined upper cutting blade.

Blanking and Punching
Blanking - sheet metal cutting to separate piece
(called a blank) from surrounding stock
Punching - similar to blanking except cut piece is
scrap, called a slug
Figure 20.4 (a) Blanking and (b) punching.

Clearance in Sheet Metal Cutting
Distance between punch cutting edge and die
cutting edge
 Typical values range between 4% and 8% of
stock thickness
 If too small, fracture lines pass each other,
causing double burnishing and larger force
 If too large, metal is pinched between
cutting edges and excessive burr results

Clearance in Sheet Metal Cutting
 Recommended clearance is calculated by:
c = at
where c = clearance; a = allowance; and t =
stock thickness
 Allowance a is determined according to type of
metal

Sheet Metal Groups Allowances
Metal group a
1100S and 5052S aluminum alloys, all
tempers
0.045
2024ST and 6061ST aluminum alloys;
brass, soft cold rolled steel, soft
stainless steel
0.060
Cold rolled steel, half hard; stainless
steel, half hard and full hard
0.075

Punch and Die Sizes
 For a round blank of diameter Db:
 Blanking punch diameter = Db 2‑ c
 Blanking die diameter = Db
where c = clearance
 For a round hole of diameter Dh:
 Hole punch diameter = Dh
 Hole die diameter = Dh + 2c
where c = clearance

Figure 20.6 Die size
determines blank
size Db; punch size
determines hole
size Dh.; c =
clearance
Punch and Die Sizes

Purpose: allows slug or blank to drop through die
 Typical values: 0.25° to 1.5° on each side
Figure 20.7
Angular
clearance.
Angular Clearance

Cutting Forces
Important for determining press size (tonnage)
F = S t L
where S = shear strength of metal; t = stock
thickness, and L = length of cut edge

Straining sheetmetal around a straight axis to
take a permanent bend
Figure 20.11 (a) Bending of sheet metal
Sheet Metal Bending

Metal on inside of neutral plane is compressed,
while metal on outside of neutral plane is
stretched
Figure 20.11 (b) both
compression and
tensile elongation of the
metal occur in bending.
Sheet Metal Bending

Types of Sheet Metal Bending
 V bending - performed with a V shaped die‑ ‑
 Edge bending - performed with a wiping die

 For low production
 Performed on a press brake
 V-dies are simple and inexpensive
Figure 20.12
(a) V bending;‑
V-Bending

 For high production
 Pressure pad required
 Dies are more complicated and costly
Edge Bending
Figure 20.12
(b) edge
bending.

Stretching during Bending
 If bend radius is small relative to stock
thickness, metal tends to stretch during
bending
 Important to estimate amount of stretching, so
final part length = specified dimension
 Problem: to determine the length of neutral axis
of the part before bending

Bend Allowance Formula
where Ab = bend allowance; α = bend angle; R=
bend radius; t = stock thickness; and Kba is
factor to estimate stretching
 If R < 2t, Kba = 0.33
 If R ≥ 2t, Kba = 0.50
)tKR(A bab +
360
2=
α
π

Springback
Increase in included angle of bent part relative to
included angle of forming tool after tool is
removed
 Reason for springback:
 When bending pressure is removed, elastic
energy remains in bent part, causing it to
recover partially toward its original shape

Figure 20.13 Springback in bending is seen as a decrease in bend angle
and an increase in bend radius: (1) during bending, the work is forced
to take radius Rb and included angle αb' of the bending tool, (2) after
punch is removed, the work springs back to radius R and angle α‘.
Springback
α α

Bending Force
Maximum bending force estimated as follows:
where F = bending force; TS = tensile
strength of sheet metal; w = part width in
direction of bend axis; and t = stock
thickness. For V- bending, Kbf = 1.33; for
edge bending, Kbf = 0.33
D
TSwtK
F bf
2
=

Figure 20.14 Die opening dimension D: (a) V die, (b) wiping die.‑
Die Opening Dimension

Drawing
Sheet metal forming to make cup shaped,‑
box shaped, or other complex curved,‑ ‑
hollow shaped parts‑
 Sheet metal blank is positioned over die cavity
and then punch pushes metal into opening
 Products: beverage cans, ammunition shells,
automobile body panels
 Also known as deep drawing (to distinguish it
from wire and bar drawing)

Figure 20.19 (a) Drawing
of cup shaped part:‑
(1) before punch
contacts work, (2)
near end of stroke;
(b) workpart: (1)
starting blank, (2)
drawn part.
Drawing

Clearance in Drawing
 Sides of punch and die separated by a
clearance c given by:
c = 1.1 t
where t = stock thickness
 In other words, clearance is about 10% greater
than stock thickness

Tests of Drawing Feasibility
 Drawing ratio
 Reduction
 Thickness-to-diameter ratio

Drawing Ratio DR
where Db = blank diameter; and Dp = punch
diameter
 Indicates severity of a given drawing operation
 Upper limit: DR ≤ 2.0
Most easily defined for cylindrical shape:
p
b
D
D
DR =

Reduction r
 Defined for cylindrical shape:
b
pb
D
DD
r
−
=
 Value of r should be less than 0.50

Thickness to Diameter Ratio‑ ‑ t/Db
Thickness of starting blank divided by blank
diameter
 Desirable for t/Db ratio to be greater than 1%
 As t/Db decreases, tendency for wrinkling
increases

Blank Size Determination
 For final dimensions of drawn shape to be
correct, starting blank diameter Db must be right
 Solve for Db by setting starting sheet metal
blank volume = final product volume
 To facilitate calculation, assume negligible
thinning of part wall

Shapes other than Cylindrical Cups
 Square or rectangular boxes (as in sinks),
 Stepped cups
 Cones
 Cups with spherical rather than flat bases
 Irregular curved forms (as in automobile body
panels)
 Each of these shapes presents its own unique
technical problems in drawing

Other Sheet Metal Forming on Presses
Other sheet metal forming operations performed
on conventional presses
 Operations performed with metal tooling
 Operations performed with flexible rubber
tooling

 Makes wall thickness of cylindrical cup more
uniform
Figure 20.25 Ironing to achieve more uniform wall thickness in a
drawn cup: (1) start of process; (2) during process. Note thinning
and elongation of walls.
Ironing

Creates indentations in sheet, such as raised
(or indented) lettering or strengthening ribs
Figure 20.26 Embossing: (a) cross section of punch and die‑
configuration during pressing; (b) finished part with embossed ribs.
Embossing

Figure 20.28 Guerin process: (1) before and (2) after. Symbols v
and F indicate motion and applied force respectively.
Guerin Process

Advantages of Guerin Process
 Low tooling cost
 Form block can be made of wood, plastic, or
other materials that are easy to shape
 Rubber pad can be used with different form
blocks
 Process attractive in small quantity production

Dies for Sheet Metal Processes
Most pressworking operations performed with
conventional punch and die tooling‑ ‑
 Custom designed for particular part‑
 The term stamping die sometimes used for
high production dies

Figure 20.30 Components of a punch and die for a blanking
operation.
Punch and Die Components

Figure 20.31 (a)
Progressive die;
(b) associated
strip development
Progressive Die

Figure 20.32 Components of a typical mechanical drive stamping press
Stamping Press

Types of Stamping Press Frame
 Gap frame
 Configuration of the letter C and often
referred to as a C frame‑
 Straight sided frame‑
 Box-like construction for higher tonnage

Figure 20.33 Gap frame
press for sheet
metalworking (ohoto
courtesy of E. W. Bliss
Co.); capacity = 1350 kN
(150 tons)

Figure 20.34 Press
brake (photo courtesy
of Niagara Machine &
Tool Works); bed
width = 9.15 m (30 ft)
and capacity = 11,200
kN (1250 tons).

Figure 20.35 Sheet metal parts produced on a turret press, showing
variety of hole shapes possible (photo courtesy of Strippet Inc.).

Figure 20.36 Computer numerical control turret press (photo
courtesy of Strippet, Inc.).

Figure 20.37
Straight sided frame‑
press (photo courtesy of
Greenerd Press &
Machine Company,
Inc.).

Power and Drive Systems
 Hydraulic presses - use a large piston and
cylinder to drive the ram
 Longer ram stroke than mechanical types
 Suited to deep drawing
 Slower than mechanical drives
 Mechanical presses – convert rotation of motor
to linear motion of ram
 High forces at bottom of stroke
 Suited to blanking and punching

Operations Not Performed on Presses
 Stretch forming
 Roll bending and forming
 Spinning
 High energy rate forming processes.‑ ‑

Sheet metal is stretched and simultaneously
bent to achieve shape change
Figure 20.39 Stretch forming: (1) start of process; (2) form die is
pressed into the work with force Fdie, causing it to be stretched and
bent over the form. F = stretching force.
Stretch Forming

Force Required in Stretch Forming
where F = stretching force; L = length of sheet in
direction perpendicular to stretching; t =
instantaneous stock thickness; and Yf = flow
stress of work metal
 Die force Fdie can be determined by balancing
vertical force components
fLtYF =

Large metal sheets and plates are formed into
curved sections using rolls
Figure 20.40 Roll bending.
Roll Bending

Continuous bending process in which opposing
rolls produce long sections of formed shapes
from coil or strip stock
Figure 20.41 Roll
forming of a
continuous
channel section:
(1) straight rolls,
(2) partial form,
(3) final form.
Roll Forming

Spinning
Metal forming process in which an axially
symmetric part is gradually shaped over a
rotating mandrel using a rounded tool or roller
 Three types:
1. Conventional spinning
2. Shear spinning
3. Tube spinning

Figure 20.42 Conventional spinning: (1) setup at start of process;
(2) during spinning; and (3) completion of process.
Conventional Spinning

High Energy Rate Forming (HERF)‑ ‑
Processes to form metals using large amounts of
energy over a very short time
 HERF processes include:
 Explosive forming
 Electrohydraulic forming
 Electromagnetic forming

Explosive Forming
Use of explosive charge to form sheet (or plate)
metal into a die cavity
 Explosive charge causes a shock wave whose
energy is transmitted to force part into cavity
 Applications: large parts, typical of aerospace
industry

Figure 20.45 Explosive forming: (1) setup, (2) explosive is
detonated, and (3) shock wave forms part and plume
escapes water surface.
Explosive Forming

Electromagnetic Forming
Sheet metal is deformed by mechanical force of
an electromagnetic field induced in the
workpart by an energized coil
 Presently the most widely used HERF process
 Applications: tubular parts

Figure 20.47 Electromagnetic forming: (1) setup in which coil is
inserted into tubular workpart surrounded by die; (2) formed part.
Electromagnetic Forming

Sheeet metal

More Related Content

What's hot (19)

Similar to Sheeet metal (20)

More from Eajaz Khan (6)

Recently uploaded (20)

Sheeet metal