SSPC-2: Surface Prep Guide through webinar.pdf

SSPC-PA 2
Procedure for Determining
Conformance to Dry Coating
Thickness Requirements
William D. Corbett, KTA-Tator, Inc.
Chair – SSPC Committee C.3.2 on
Dry Film Thickness Measurement

SSPC-PA 2
Procedure for Determining Conformance to
Dry Coating Thickness Requirements
• Webinar Content
 Background of SSPC PA 2
 Overview and Purpose of SSPC-PA 2 (2012)
 Purpose of ASTM D 7091-12
 Definitions
 Gage Descriptions
 Calibration, Verification of Accuracy & Adjustment
 Measurement Procedures
 Frequency and Number of Measurements
 Conformance to Specified Thickness
 Content of Eight Appendices

Learning Objectives/Outcomes
• Completion of this webinar will enable the participant to:
 Describe the purpose and content of SSPC-PA 2
 Describe the differences between Type 1 and Type 2 gages
 Describe the processes associated with calibration, verification of
accuracy and adjustment
 Explain Base Metal Reading acquisition
 Describe the frequency and tolerance of measurements
 Describe the procedure for determining the magnitude of a non-
conforming area
 Describe the basic content of eight appendices to the standard

Background of SSPC-PA 2
• Originally published in
SSPC Volume 2 in 1973(T)
• Most recent update was 2004
• Editorial revision to an
Appendix in 2009
• SSPC committee work on
revisions initiated in 2007
• Current version dated May 1,
2012
• Standard re-balloted in
August/September 2013

Background of SSPC-PA 2
• Update to ASTM D 7091-05
concurrent with revisions to
SSPC-PA 2
• ASTM D7091-12 focuses on
gage use
• SSPC-PA 2 (2012) focuses
on acceptability of acquired
measurements
• Both address ferrous and
non-ferrous metal surfaces

Scope of SSPC-PA 2
• Describes a procedure for determining shop/field
conformance to a specified DFT range on ferrous and
non-ferrous metals
• Measurements are acquired using commercially
available gages (two “types”)
• Procedures for gage calibration, verification of
accuracy and adjustment are described
• Procedure for determining conformance to specified
thickness range over extended areas is described

Scope of SSPC-PA 2
• Standard contains 8 non-mandatory appendices
(described later)
• 9th appendix was recently balloted (precautions
regarding the use of the standard for coating failure
investigations)
• Standard is not intended to be used for measurement
of thermal spray coatings (procedure described in
SSPC-CS 23.00)

Definitions in SSPC-PA 2
• Gage Reading: A single instrument reading
• Spot Measurement: The average of three or at
least three gage readings made within a
1 ½” (4 cm) diameter circle
• Area Measurement: The average of five spot
measurements over each 100 square feet of
coated surface

Gage Descriptions
• Gage type is determined by magnetic properties
employed to measure thickness (not the read-out
mode)
Type 1 – Magnetic Pull-off Gages
Type 2 – Electronic Gages

Gage Types
Type 1 – Magnetic Pull-off
Gages
Type 2 – Electronic Gages

Gage Types, continued
• Type 1 – Magnetic Pull-
off Gages
Permanent magnet
contacts coated surface
Force required to
detach magnet is
measured
Force interpreted as the
coating thickness on
scale or display
Scale is nonlinear

Gage Types, continued
• Type 2 – Electronic
Gages
Electronic circuitry
converts reference signal
to coating thickness

Calibration & Verification of
Accuracy
• ASTM D7091 describes 3 operational steps to
ensure accurate measurement:
Calibration
Verification of Accuracy
Adjustment
• Steps are required to be completed before
coating thickness data acquisition to determine
conformance to a specification

Gage Calibration
• Performed by the gage manufacturer or an
accredited calibration laboratory
• Test certificate traceable to a National
Metrology institution required
• No standard calibration interval (established
based on experience & work environment)
• One year interval is common

Verification of Type 1 Gage Accuracy
 Performed as described in
ASTM D7091
 Beginning and end of each work shift
(minimum)
 During (e.g., hourly), if:
 Obtaining a large no. of readings
 Gage is dropped or readings are
suspect
 Record:
 Serial no. of gage & standard
 Stated & measured thickness
 Method used to verify accuracy

• Type 1 gages should not be “adjusted”
• Adjustments to the helical spring may void the
gage warranty
• Combined tolerance of gage and coated
standard determines gage accuracy
E.g., if gage accuracy is 5% and reference standard
accuracy is 3%, combined tolerance is ~ 6%,
calculated as: √ 52 + 32
On a 10 mil reference standard, the gage reading
can range from 9.4-10.6 mils

Correction for Surface Roughness
• Base Metal Reading (BMR)
• Effect of surface roughness
on coating thickness gage
• NOT surface profile
• Measure the prepared,
uncoated substrate; calculate
average BMR
• Deduct BMR from
measured coating thickness BMR

Correction for Surface
Roughness
Area BMR
1 30 µm (1.2 mils)
2 25 µm (1.0 mils)
3 18 µm (0.7 mil)
4 13 µm (0.5 mil)
5 20 µm (0.8 mil)
6 8 µm (0.3 mil)
7 25 µm (1.0 mil)
8 28 µm (1.1 mils)
9 23 µm (0.9 mil)
10 13 µm (0.5 mil)
Measuring Base Metal Effect with Type 1
DFT Gage
Average BMR: 21 µm (0.8 mil)

BMR Correction for Multiple Coat
Systems
Measured Primer Thickness: 102 µm (4.0 mils)
BMR: 13 µm (0.5 mils)
Actual Primer Thickness: 89 µm (3.5 mils)
Measured Primer + Finish Thickness: 178 µm (7.0 mils)
BMR: 13 µm (0.5 mils)
Actual Total System Thickness: 165 µm (6.5 mils)

 What if access to blast cleaned steel is not
available (already coated)?
 Appendix A8.3 addresses smooth surface
adjustment
 Verify gage accuracy on a smooth surface (per
gage manufacturer instructions)
 Deduct “assumed” approximate correction value
from each gage reading

Table A8
Typical Gage Correction Values Using
ISO 8503 Profile Grades
ISO 8503 Profile
Grade
Correction Value
(µm)
Correction value
(mils)
Fine 10 0.4
Medium 25 1.0
Coarse 40 1.6

 Verify accuracy per
manufacturer instructions
(use coated standards)
 Performed as described in
ASTM D7091
 Beginning and end of each work
shift (minimum)
 During (e.g., hourly), if:
 Obtaining a large no. of readings
 Gage is dropped or readings are
suspect
 Record:
 Serial no. of gage & standard
 Stated & measured thickness

• Single Point Verification
Select one reference coated standard representing the
mid-range of the anticipated coating thickness
E.g., 4-6 mils (100-150 µm), select 5 mil (125 µm)
reference standard
• Tw0 Point Verification
Select reference coated standards below and above the
median anticipated coating thickness
E.g., 5 mils (125 µm), select 3 mil (75 µm) and 7 mil
(175 µm) coated standards

Adjustment of Type 2 Gages
• Aligning a gage’s thickness
readings to those of a known
thickness value to improve gage
accuracy on a specific surface or
within a measuring range
• Corrects for:
 Surface Roughness
 Substrate Properties (metallurgy)
 Curvature
 Etc.
• Use Certified or Measured shims

Adjustment of Type 2 Gages
• Addressed in Appendix 8
• Follow the gage
manufacturers step-by-step
procedures for gage
adjustment
• Instructions vary by gage
manufacturer
• Adjustment is performed
using certified or measured
plastic shims (foils)

Measurement Frequency
 For areas of coating not exceeding 300 square feet,
(~30 square meters) each 100 square feet (~10 square
meters) is measured
 For areas of coating exceeding 300 square feet and
not exceeding 1000 square feet, arbitrarily select 3
random 100 square foot (~10 square meter) areas and
measure

Measurement Frequency
 For areas of coating exceeding 1000 square feet
(~100 square meters), arbitrarily select 3 - 100 square
feet (~10 square meter) areas for the first 1000 square
feet (~100 square meters), and 1 additional 100
square foot(~10 square meter) area for each
additional 1000 square feet (100 square meters), or
portion thereof

Size of Coated Area: 900 square feet
No. of Areas: 3 areas
No. of Spots: 3 Areas x 5 Spots/Area = 15
Spots
Minimum No. of Gage
Readings: 15 Spots x 3 Readings/Spot =
45 Gage Readings
Measurement Frequency Example 1
(US Standard)

Size of Coated Area : 12,500 square feet
No. of Areas: 3 + 12 = 15 areas
No. of Spots: 15 Areas x 5 Spots/Area = 75
Spots
Minimum No. of Gage
Readings: 75 Spots x 3 Readings/Spot =
225 Gage Readings
Measurement Frequency Example 2
(US Standard)

Conformance to Specified
Coating Thickness
 Specifications normally indicate the
range of coating thickness (e.g., 5-7
mils), not as a single value (e.g., 5
mils)
 When a single thickness value is
specified and no range is indicated
by manufacturer:
 Range established at +/-20% of stated
thickness value
 E.g., 7 mils is 5.6-8.4 mils

Table 1
Coating Thickness Restriction Levels
Thickness Gage Reading
Spot
Reading
Area Measurement
Level 1
Minimum Unrestricted As specified As specified
Maximum Unrestricted As specified As specified
Level 2
Minimum Unrestricted As specified As specified
Maximum Unrestricted 120% of maximum As specified
Level 3
Minimum Unrestricted 80% of minimum As specified
Level 4
Level 5
Maximum Unrestricted Unrestricted Unrestricted
Note: If unspecified, Level 3 is the default

Measurement Tolerance
EXAMPLE 1:
 Target DFT: 4-6 mils
 Coating Thickness Restriction Level 3 (default)
 Individual gage readings unrestricted
 Spot measurements must be between 3.2 mils and 7.2 mils
 Area measurement must be between 4 and 6 mils
 If spot or area measurements are out of tolerance, the
magnitude of the nonconforming thickness must be determined
and demarcated.

Measurement Tolerance
EXAMPLE 2:
 Target DFT: 4-6 mils
 Coating Thickness Restriction Level 2
 Individual gage readings unrestricted
 Spot measurements must be between 4 mils and 7.2 mils
 Area measurement must be between 4 and 6 mils
 If spot or area measurements are out of tolerance, the
magnitude of the nonconforming thickness must be determined
and demarcated.

Audible and/or visual
indicators if spot readings are
out of tolerance
SSPC-PA 2 Measurement Specifications
Built Into Type 2 Gages

Determining the Magnitude of a
Nonconforming Area
• Obtain spot measurements at 5 foot intervals in 8 equally
spaced directions radiating out from the nonconforming area
up to the limit of area coated during the work shift
Each spot must conform to requirements
When 2 consecutive spots conform to requirements,
measuring can stop
• Area within 5 feet of any nonconforming measurement is
suspect and must be re-inspected after correction
• Repeating structural units or parts – 1 spot measurement on
each unit
Repeat until spot readings on 2 consecutive units conform

5 ft
NO
OK
OK
STOP
OK
OK
STOP
OK
STOP OK
STOP
OK
OK
Dashed line indicates boundary of area painted during work shift
Suspect area
preceding a
nonconforming
spot must be re-
measured after
corrections are
made
OK
NO
STOP
OK
OK
(Limit of
area
coated
during
work shift)
5
ft
5
ft
STOP
OK
5
ft
Dashed line indicates boundary of area painted during work shift
Dashed
line
indicates
boundary
of
area
painted
during
work
shift
Dashed
line
indicates
boundary
of
area
painted
during
work
shift
(Limit of
area
coated
during
work shift)
STOP
(Limit of
area
coated
during
work shift)

SSPC-PA 2 Appendices
1. Numerical Example of Average Thickness
Measurement
2. Methods for Measuring DFT on Steel Beams
(Girders)
3. Methods for Measuring DFT for a Laydown
of Beams, Structural Steel & Misc. Parts after
Shop Cleaning
4. Method for Measuring DFT on Coated Steel
Test Panels

SSPC-PA 2 Appendices, cont.
5. Method for Measuring the DFT of Thin
Coatings on Coated Steel Test Panels that
Have Been Abrasive Blast Cleaned
6. Method for Measuring the DFT of Coatings
on Edges
7. Method for Measuring the DFT of Coated
Steel Pipe Exterior
8. Examples of the Adjustment of Type 2 Gages
Using Shims

Appendix 2: Measuring Coating
Thickness on Steel Beams (Girders)
 Full Determination
 Sample Determination
 Beams < 20 ft (<6 m)
 Beams 20 ft - 60 ft (6 m-18 m)
 Beams > 60 ft (> 18 m)
 Coating Thickness Restriction
Level 3 (default)
 The average of all spot
measurements (per area) must
conform to specified range
 Measurement locations on
stiffeners arbitrarily selected
Stiffener

 Full Determination
 Divide beam into 5 equal
sections along the length
 Web > 36”: Obtain one spot
measurement in 14 areas, per
section (total of 70 spot
measurements)
 Web < 36”: Obtain one spot
measurement in 12 areas, per
section (total of 60 spot
measurements)

Full Determination
Note: Areas 2, 6, 8 and 12 (Toe) may not be measured.
The top of the top flange may not be accessible

 Sample Determination
 Beam length < 20 ft: Obtain 2
spot measurements randomly
distributed in all 12 areas (total
of 24 spot measurements)
 Beam length 20-60 ft: Obtain 3
spot measurements randomly
distributed in all 12 areas (total
of 36 spot measurements)
Note: If toe areas are not
included, measure in 8 areas
(16 or 24 spot measurements)

Thickness on Laydown of Beams
 Laydown: Group of steel
members laid down to be
painted in one shift by one
applicator
 Full DFT Determination
 Beams (girders)
 Miscellaneous parts
 Sample DFT Determination
 Beams < 20 ft (6 m)
 Beams 20 ft - 60 ft (6 m-18 m)

Thickness on Test Panels
 Minimum panel size:
3” x 6” (7.5 x 15 cm)
 Maximum panel size:
12” x 12” (30 x 30 cm)
 Use Type 2 gage
 Two gage readings from top,
middle and bottom third
 At least 0.5” from edge and
1” from other readings
 80% min. & 120% max.
applies to gage readings
1 2
3 4
5 6

Appendix 5: Measuring Thickness of Thin
Coatings on Abrasive Blast Cleaned Test
Panels
• “Thin” is considered 1 mil
(25.4 µm) or less
• Obtain 10 gage readings
from each of three “zones”
• Calculate the mean and
standard deviation in each
zone
• The mean of all three
zones is the coating
thickness
10 gage readings
10 gage readings
10 gage readings

Appendix 6: Measuring Thickness on Edges
(Type 2 Gages Only)
• Gage probe configurations
less affected by edge
proximity
• Consult gage manufacturer
• SSPC Guide 11 (discusses
edge retentive coatings)
• Verify probe will measure
using shim placed on edge
• Minimum 3 readings within
1.5 linear inches along edge
(“spot”)
• Number of “spots” will vary

Appendix 7: Measuring Thickness on Coated
Steel Pipe Exterior
• Pipe sections on cart or rack
considered a complete unit
• Area = (length of each pipe x
circumference) x no. of pipe
sections on cart
• Alternative: Pipe DFT Frequency
Factors (FF) 1 through 5
• EXAMPLE:
– Total coated area exceeds 100 sq. ft.
– FF 2 invoked
– 175 sq. feet of coated pipe
– 10 spot measurements
– FF 2 results in 20 spot measurements

Appendix 7: Measuring Thickness on Coated
Steel Pipe Exterior
• Pipe spools measured
individually
• Table A7 describes frequency
• Pipe spools < 10 ft: 3 sets of
circumferential spot
measurements
Pipe Diameter Circumferential Spot
Measurements
Interval Spacing
Up to 12 inch (30 cm) 4 evenly spaced 10 ft (3 m) apart
14-24 inches (36-60 cm) 6 evenly spaced 10 ft (3 m) apart
> 24 inches (60 cm) 8 evenly spaced 10 ft (3 m) apart
Table A7

Summary
 Background of SSPC-PA 2
 Overview and Purpose of SSPC-PA 2 (2012)
 Purpose of ASTM D 7091-12
 Definitions
 Gage Descriptions
 Calibration, Verification of Accuracy & Adjustment
 Measurement Procedures
 Frequency and Number of Measurements
 Conformance to Specified Thickness
 Content of Eight Appendices

SSPC-PA 2, Procedure for
Determining Conformance to Dry
Coating Thickness Requirements

SSPC-2: Surface Prep Guide through webinar.pdf

More Related Content

Similar to SSPC-2: Surface Prep Guide through webinar.pdf (20)

Recently uploaded (20)

SSPC-2: Surface Prep Guide through webinar.pdf