Study on Ni 0.5-X Znx Cu0.5 Fe2 O4 Sintered Ferrite System Using Xrd & High Field Techniques

ISSN 2350-1030
International Journal of Recent Research in Physics and Chemical Sciences (IJRRPCS)
Vol. 2, Issue 1, pp: (18-25), Month: April 2015 – September 2015, Available at: www.paperpublications.org
Page | 18
Paper Publications
Study on Ni 0.5-X Znx Cu0.5 Fe2 O4 Sintered
Ferrite System Using Xrd & High Field
Techniques
1
Dhanalakshmi.A, 2
Dr. S.Aravazhi
1
Department of Physis, IFET Engineering college, Villupuram
2
Department of Physics, Arignar Anna Govt.Arts College,Villupuram.
Abstract: Nickel ,Zinc, copper Mixed spinel ferrite compound was synthesized by using High field technique
method and the well ground powder is fired at 9000
C for 20 hours and furnace cooled approximately at the rate of
1000
C per hour. The resulting powders were characterized by X- ray diffraction (XRD). The magnetic properties
of the compound analyzed by hysteresis loop measured using high field measurements.
Keywords: Ferrites, High field measurements, Hysteresis loop X - ray diffraction.
1. INTRODUCTION
Ferrites are candidate substances which find wide applications in microwave devices, computer memories and magnetic
recording. They offer low eddy currents and dielectric looses for the propagation of electromagnetic waves within the
range of frequencies up to few GHz. In view of their importance several researchers have studied the electric and
magnetic properties of ferrite materials in the past few years.
Smit and Wijn [1] have systematically and elaborately studied the electric and magnetic properties of the ferrites NiFe2O4
and CuFe2O4. They have reported that the saturation magnetization value of NiFe2O4 is 300 Gauss at 00
K and its curie
temperature is 585O
C. For the ferrite CuFe2O4 the values are 160 Gauss and 455O
C respectively. Similarly Arrot and
Goldman [2] and Hartmann-Boutron and Imbert [3] have studied ZnFe2O4 magnetically and have found out ZnFe2O4 is
antiferromagnetic below 10O
K. Many attempts have been made to lower the curie temperature of NiFe2O4 and CuFe2O4
and for increasing the transition point of ZnFe2O4 thereby suitably tailoring the saturation magnetization, resitivity,
chemical stability and mechanical hardness. Such attempts have been made possible by mixing the end member ferrites
namely NiFe2O4 and CuFe2O4[4], NiFe2O4 and ZnFe2O4 [5-21]and ZnFe2O4 and CuFe2O4[22-28].
Continuing on the same lines, several reports of earlier researchers [29-31] on mixed ferrites of Ni-Zn-Cu have motivated
to prepare ferrites of ternary mixtures to provide additional electric and magnetic data. It is of interest to dope Zn2+
ions in
some of the sites of Ni2+
ions in Ni-Cu mixed ferrite system. It is known that the magnetic behavior of Ni-Cu ferrite is
largely governed by Fe-O-Fe interaction and Ni-O-Fe interaction (the coupling of spins of the 3d electrons). Introducing
Zn2+
ions in the spinel lattice is expected to bring in a substantial change in magnetization.
2. EXPERIEMENTAL METHOD
To suit to the needs of technology different types of ferrites are prepared by varying the composition. A system of ferrites
namely Ni0.5-xZnxCu0.5Fe2O4 is prepared and studied. The values of x are 0.0, 0.1, 0.2, 0.3, 0.4 and 0.5. The systematic
procedure of preparation falls into four categories. They are Powder preparation, Compact formation, Heat treatment
processes and Machining to final shape.The composite oxides of Ni0.5-xZnxCu0.5Fe2O4 system are A.R grade NiO, ZnO,
CuO and Fe2O3. The powders of reactants are mixed and ground well using an agate mortar. The acetone is only used for

ISSN 2350-1030
Page | 19
Paper Publications
cleaning the mortar after each concentration is ground. Well ground powder is fired at 900 o
C for 20 hours and furnace
cooled approximately at the rate of 100 o
C per hour. This process is termed as pre-sintering. The pre-sintered powders are
again ground well and are pelletized using hydraulic press at a constant pressure of 70 Kg/cm2
.This powder pressing is an
important and commonly used ceramic forming technique that warrants a brief treatment. In essence, the process is the
compaction of a powdered mass into a desired shape. The degree of compaction is maximized and fraction of void space
is minimized by using coarse and fine particle mixed in appropriate proportion.
3. CHARACTERIZATION OF THE SINTERED Ni0.5-xZnxCu0.5Fe2O4 SYSTEM
PROPOSAL FOR THE SITES OF CATIONS:
A prior knowledge of the site preference of the constituent ions of a ferrite is an important requirement for working out
the spinel structure. Secondly a accurate data of ionic size of the constituent ions is advantageous. In the present system of
ferrite Cu2+
,Ni2+
,Zn2+
and Fe2+
are the constituent cations. Using knowledge of site preference of the ions and the ionic
size data of the respective ions viz Table- I and substituting the ions in A and B sites of spinel structure. A systematic
calculation of radii of individual sites ra and rb is proceeded. Theoretical values of lattice constants are estimated
permuting the ra and rb values in the modified formula for lattice constant calculation of Bhongale et.al.[32]
a  {(ra /3 +2.0951ro) + [(ra /3 +2.0951ro)2
–1.866 (1.333ra
2
+ 0.0675ro
2
-0.6rarb )]1/2
} / 0.933 An appropriate set of
values of lattice constants is estimated according to the criteria of Vegard’s law[33] Change of lattice constant with
concentration and A close agreement of lattice constant for each concentration with its experimental value. This procedure
helps to propose a good fit set of cations and their respective sites of spinel structure.
The theoretical and experimental lattice constants are tabulated in TABLE-II The porosity, particle size, molecular density
and u- parameter are also listed in the same table. In order to appreciate the variation of lattice constant with concentration
a graph is drawn between them, which is given in Figure-3.The proposed cation distribution is given in TABLE-III
TAB LE – I Ionic radii and magnetic moments of the cations used in the present study
Cations Ionic radius
(A0
)
Magnetic
moment ( µB )
Fe3+
0.64 5.92
Fe2+
0.74 4.90
Ni2+
0.69 2.84
Zn2+
0.74 0.0
Cu2+
0.72 1.73
TABLE – II Experimental and theoretical lattice constants, particle size, porosity, molecular and macroscopic densities and U –
parameter of sintered Ni 0.5-x Zn x Cu 0.5 Fe2O4 ferrite system.
Cncentratio
n
X
Lattice constant A0
Particl
e size
A0
Molecular
density
ρ m Kg/m3
Macrosco -pic
density ρ A Kg/m3
Porosi
ty P%
‘U’
parameter
Experim-
ental
Theor-
etical
0.0 8.547 8.5222 310 5037 4165 17.31 0.398
0.1 8.544 8.5246 286 5057 4126 18.41 0.398
0.2 8.535 8.5266 343 5087 4002 21.32 0.399
0.3 8.550 8.5287 371 5073 4090 19.37 0.399
0.4 8.553 8.5307 343 5084 4235 18.66 0.400
0.5 8.548 8.5326 431 5167 4178 19.14 0.400
TABLE –III Proposed Cations distribution for the Sintered Ni0.5-xZnxCu0.5Fe2O4 System
Concentrationx Tetrahedral site (A) Octahedral site [B]
0.0 Fe1.0 Zn0.0 Cu0.5 Ni0.5Zn0.0 Fe1.0
0.1 Fe0.925 Zn0.075 Cu0.5 Ni0.4 Zn0.025 Fe1.075
0.2 Fe0.85 Zn0.15 Cu0.5 Ni0.3 Zn0.05 Fe1.15
0.3 Fe0.775 Zn0.225 Cu0.5 Ni0.2 Zn0.075 Fe1.225

ISSN 2350-1030
Page | 20
Paper Publications
0.4 Fe0.7 Zn0.3 Cu0.5 Ni0.1 Zn0.1Fe1.3
0.5 Fe0.625 Zn0.375 Cu0.5Ni0.0Zn0.125Fe1.375
HIGH FIELD MEASUREMENTS:
Hysteresis loops are traced using the A.C High Field Hysteresis Loop Tracer in the field ranging up to 3600 Oe. A sample
of approximately 3 mm thickness and 15 mm diameter is placed in the upper part of the pick-up coil and pushed back into
the pole gap. When the current is increased, the hysteresis loop of the sample will be seen on the oscilloscope screen.
Vertical and horizontal sensitivities of the scope could be adjusted to get a suitable size of the hysteresis loop. The
representative loops for the present study is given in Figure-2. The parameters calculated from the hysteresis loop are
given in TABLES-IV and V
TABLE - IV Saturation induction, remanance induction, BrBs ratio and coercive field of sintered Ni 0.5-x ZnX Cu 0.5Fe2O4
system
Concentration Saturation induction Remanance Br/Bs Ratio Coercive field Hc Oe
0.0 4581 2094 0.457 24.67
0.1 4283 1638 0.382 25.01
0.2 4346 1534 0.352 22.94
0.3 4841 1767 0.364 21.25
0.4 4784 1794 0.375 22.16
0.5 5320 1915 0.359 23.02
TABLE – V Saturation magnetization, magnetic moment, Y – K angle, exchange energy, molecular field coefficient and
exchange field of sintered Ni 0.5-x Zn x Cu 0.5 Fe2O4 system.
4. RESULTS AND DISCUSSION
The observed XRD patterns of the samples of the present study are shown in the Figure-1 It is seen from Figure-1 that
there are separated and distinguished peaks with varying intensities. This observation easily ensures that the samples
prepared are in single phase and polycrystalline nature. The measured values of diffraction angles vary between 34O
and
35O
for the characteristic peak of 311 plane. The presence of 311 reflection plane for these ferrites provides the first
evidence of the phase centered cubic structure (FCC). The values of experimental lattice constants given in TABLE-II are
found to range between 8.535A0
to 8.553A0
for the spinel ferrites. The variation of experimental lattice constants is well
depicted from Figure-3.It shows clearly indicates that there is an increase of lattice constants with increase of
concentration (x). According to the plan of preparation of the spinel ferrite system Ni2+
ions are replaced by a
Concen
tration
X
Sat.mag
-netization
Ms
Gauss
σemugm Magnetic moment
ηB
µB
Y-K
Angle
Degree
s
Exchang
e energy
JX 10-16
ergs
Mol.
Field
Coeff.
λW
Exchange
field
Be
x103
Gauss
Experi
-ental
Theori
-tical
0.0 365 88 3.71 2.285 - 38.648 447.64 163.16
0.1 341 83 3.507 2.889 - 40.604 470.28 160.3
0.2 346 87 3.688 3.493 - 33.732 390.68 135.17
0.3 385 94 4.019 4.095 7o
1’ 27.38 317.12 122.09
0.4 381 92 3.944 4.701 23o
3’ 23.812 275.80 104.94
0.5 424 102 4.364 5.305 26o
26’ 16.772 194.26 82.26

ISSN 2350-1030
Page | 21
Paper Publications
proportionate substitution of Zn2+
ions when concentration x is increased. It is wise to relate the increase of Zn2+
ions at
the expense of Ni2+
ions with the increase of lattice constant as concentration increases. Actually the size of Zn2+
ions
(0.74AO
) is larger than that of the Ni2+
ions (0.69AO
) which legitimately conforms to the increase of lattice constant as
Zn2+
ions increase.
Fig 1 XRD Spectra of the sintered Ni 0.5-x Zn x Cu 0.5 Fe2O4 System
The measured values of particle size of the spinel ferrite lie in-between 286A0
and 431A0
. They are in good agreement
with the values reported earlier for similar ferrites prepared by double sintering methods [7]. The values of % of porosity
vary from 17.31 to 21.32. The range of values of % of porosity of the present samples reflects a good schedule of heat
treatment of ceramics. Further the values of porosity are found to be well with in the range of values reported by the
earlier workers [6,10].
The values of molecular density determined using experimental lattice constant data are also given in the TABLE II.
Molecular density of the spinel ferrites is found to vary between 5037 Kg/m3
and 5167Kg/m3
which show good agreement
with the molecular density of similar ferrites. It may be concluded that the polycrystalline ferrite of the present study has a
better compaction. The values of Oxygen parameter change from 0.398 to 0.400 which is clearly found to be close to the
ideal value of Oxygen parameter 0.375. It means that the spinel ferrites of the present study have a better compaction with
a small amount of loose packing. This explanation is in agreement with the ones suggested by porosity, molecular density
and particle size measurements.
Fig2. Hysteresis loops of the sintered Ni0.5-xZnxCu0.5Fe2O4

ISSN 2350-1030
Page | 22
Paper Publications
TABLE-III provides a picture of distribution of cations in the A and B sites. It is noticed form the TABLE-III that Zn2+
ions show more preference for A sites though they are supposed to occupy the B site where Ni2+
ions might have created
vacancy positions. In order to explain the site preference of transition metal ions two theories have been proposed which
differ in the concept of chemical bondings in oxides. Dunitz and Orgel [34] have used crystal field theory, which is based
on purely ionic type of bonding, where as Blasse[35] has used a simplified molecular orbital approach, taking into
account, the covalent bonding between oxygen and transition metal atoms. Normally large divalent ions like Zn2+
tend to
occupy the tetrahedral sites as this is favored by polarization effects. Daniels [36] and Matsui et.al.[37] have explained
that Ni2+
and Cu2+
ions have a tendency to occupy octahedral sites. The proposed cations distribution of spinel ferrites of
the present study is in vogue with the criteria reported earlier. However a small % of Zn2+
ions is found to occur in the
octahedral sites for compensating the condition of covalancy. Theoretical value of lattice constant is also plotted with
respect to concentration and shown in the same Figure-3 for comparison. Both the curves of theoretical and experimental
lattice constants show a straight line behavior and an increasing trend with concentration. Such an observation on
theoretical and experimental lattice constants certifies that the proposed cation distribution is an equivalent of actual
distribution of the ions in this spinel ferrites system. It is also noticed in Figure-3 that there is an appreciable gap between
the two straight line curves of theoretical and experimental lattice constants. A judicious incorporation of the rules of
packing of ions reveals that the loose packing of the ions is surely a contributor of lattice constant expansion. The
presence of crystal field distortions is unavoidable, as there are Cu2+
ions in B site.
Therefore the occurrence of loose packing and crystal field distortions is estimated as the cause mechanism of the gap
between the theoretical and experimental lattice constants. It is also understood that the increasing trend of lattice
constants with concentration is solely attributed to that part of Zn2+
ions replacing Ni2+
ions in the B site. Replacement of
Fe2+
ions by the doped Zn2+
ions in the A sites contributes insignificantly for the expansion of the lattice
In the present study the parameters of primary importance are saturation magnetization, coercive field, remanance
magnetization and magnetic moment. The shape of magnetic hysteresis loop renders explanation for the nature of a
magnetic domain and type of the magnetic materials. Bean[38] it has shown from theoretical considerations that the
hysteresis loops of dilute magnetic materials of various size of particles would be different. It has been worked out that
the shapes of the loops will be divided into four categories. Each kind of loop is found to be indicative of one type domain
or mixed types of domains. The type of the domains so categorized is single-domain (SD), multidomain (MD), super

ISSN 2350-1030
Page | 23
Paper Publications
paramagnetic domain (SP) and cation deficient states (CD). The reason for the occurrence of different domain states is
well established in the literature[39].
According to the fairly well established criteria for domains, the loops obtained for the Ni0.5-xZnxCu0.5Fe2O4 system
(Figure-2) of the present study are indicative of multidomains. The value of coercive field varies between 21.25 Oe and
25.01Oe. It is seen from the TABLE-IV that the coercive field is found to be fairly low and there is no much change with
respect to concentration. Low value of coercive field is effected due to soft nature of the ferrite. It is found to be
insensitive to concentration variation. The values of remanance ratio range from 0.352 to 0.457. Therefore it is understood
that the ferrites prepared in the present study are multidomain cases. The values of saturation magnetization (Ms) values
vary from 341 Gauss to 424 Gauss and the specific magnetization () values are form 83 to 102 emu / g. These values are
in good agreement with the values reported by Smit and Wijn [1], Wisvanathan and V.R.K. Murthy [90 ] and Derek
Craik et.al [40] for the similar types of ferrites.According to Neel’s two sublattice molel [41] of ferrimagnetism,
theoretical magnetic moments can be calculated by the relation
n B (Neel) = MB - MA
MB and MA are the B and A sublattice magnetic moments respectively. In the present studies nB values are calculated
using ionic magnetic moments of Fe3+
,Ni2+
,Zn2+
,and Cu2+
. The observed magnetic moments are compared with the
theoretical (Neel’s model) magnetic moment and are summarized in TABLE-V. In the earlier studies [42], agreement
between the observed and theoretical magnetic moment values have been found confirming the collinear spin ordering
and disagreement also found indicating the non-collinear order. The present discrepancy between observed and theoretical
nB values can be understood in terms of significant non-collinear behavior.
For x>0.3 the discrepancy between observed and theoretical nB values are increased with the dopant concentration (x).
With the increase of x , the increased discrepancy of nB values suggests the dominant role of canted spin (non-collinear)
on B sites existing and Yafet-Kittel angles having strong influence on the MS variation with x. The values of canting angle
(YK) have been obtained from the observed nB variation with x by the relation [43]
nB(x)(obs) = MB(x)CosYK - MA(x)
These values are also given in TABLE-V. Thus the observed MS variation has been explained on the basis of Yafet-Kittel
angles existing on the B site spin besides two sub lattice models. Zn2+
ions going into B sites decrease the magnetic
moment of the B sub lattice and also modify the exchange interactions of A and B sites. Hence, the net magnetization, MS
decreases.
Surprisingly for x<0.3 the theoretical nB values are smaller than their experimental values. Thus these studies indicate the
modification of A-B and B-B exchange interactions. However, studies using Mossbauer spectrometer would give clear
information about the magnetic structure of the ferrites to understand in terms of Neel’s two sub lattice model and canting
spin on B sites. Magnetic moment contribution and magnetic energy bear direct relation to nB and curie temperature. From
Figures-4 it is confirmed that Tc and magnetic moment decrease with concentration.
In order to check the validity of molecular field theory for the present system of ferrites, the values of exchange energy,
molecular field coefficient and exchange field are obtained and reported in TABLE-V. Variation of particle size with
concentration is as shown in figure 5 which shows an increasing trend due to the replacement of smaller Ni2+ ion by
bigger Zn2+ ions. The variation of exchange field with concentration is as shown in the figure 6 which has a decreasing
trend. The value of exchange energy lies between 16.77210-16
and 40.604 10-16
ergs. The molecular field coefficient
ranges between 194.26 and 470.28, and the exchange field varies from 82.26103
to 163.16103
Gauss. The order of
values of these parameters shows that the spinel ferrite prepared is ferromagnetic in nature.
5. CONCLUSION
Ni 0.5-x Znx Fe2O4 Sintered ferrite system is well prepared under ideal condition. The magnetic properties (magnetic
moment, exchange field etc.,) of this ferrites system are very sensitive with concentration as shown by the hysteresis
loops.

ISSN 2350-1030
Page | 24
Paper Publications
ACKNOWLEDGEMENT
The authors would like to thank Dr. ARAVAZHI Professor in Physics (Thiruvalluvar University) for her great assistance
in the Ferrites synthesis. This work was supported by Rev. Fr. P. PAUL RAJKUMAR, Secretary of St. Jospeh college of
Arts & Science Cuddalore, to carry out this work in a successful manner.
REFERENCES
[1] J. Smit and H.P.J. Wijn, “Ferrites” Philips Techinical Library (1959).
[2] Arrot and J.E. Goldman, Phy. Rev. 98, 1201 (1995).
[3] F. Hartmann-Boutron and P. Imbert, J. Appl. Phys. 39, 775 (1968).
[4] Ashok M Sankpal, S.R. Sawant and A.S. Vaingankar, Ind. J. Pure and Appl. Phys. Vol. 26, 459 (1988).
[5] C.M. Srivastava, S.N. Shringi, M.S. Patni and S.M. Joglekar, Bull. Mater.Sci, Vol. 6, 7 (1984).
[6] A.B. Naik and J.I. Powar. Ind. J. Pure and appl. Pjhys, Vol. 23, 436 (1985).
[7] T.T. Srinivasan, P. Ravindranathan, L.E. Cross, R. Roy and R.E. Newnham, J. Appl. Phys. 63, 8 (1988).
[8] M.L. Crauss, E. Rezlescu and N. Rezlescu. Phys. Stat. Solidi (a), 133, 439 (1992).
[9] N. Rezlescu and E. Rezlescu, Solid State Commun, Vol. 88, 139 (1993).
[10] N. Rezlescu, E. Rezlescu, C. Pasnicu and M.L. Craus, J. Phys. Cond. Matter 6, 5707 (1994).
[11] B.V. Bhise, V.L. Mahajan, M.G. Patil, S.D. Lotke and S.A. Patil, Indian. J. Pure and Appl. Phys, Vol.33, 459
(1995).
[12] A.K. Ghatage, S.A. Patil and S.K. Paranjpe, Indian. J. Phys. 73 A(3), 329 (1999).
[13] A. Verma, T.C. Goel,R.G. Mendiratta and M.I. Alam, Mater.Sci and Engi. B 60 156 (1999).
[14] .A. Dias, R.L. Moreira, Materials Letters, 39, 69 (1999).
[15] G. Ranga Mohan, D. Ravinder, A.V. Ramana reddy and B.S. Boyanov, Materials Letters .40, 39 (1999).
[16] D. Ravinder, G. RangaMohan, Materials Letters, 44, 139 (2000).
[17] Yong Choi, H.S. Shim, J.S. Lee, J. of. Alloys and Compounds, 326, 56 (2001).
[18] D. Ravinder, K. Vijaya kumar, P. Balaya, Materials Letters, 48, 210 (2001).
[19] Elsa E. Sileo, Ramiro Rotelo, Silvia E. Jacobo, Physica B, 320, 257 (2002).
[20] K. Vijaya kumar, D. Ravinder, Materials Letters, 52, 166 (2002).
[21] S.E. Jacob, W.G. Fano, A.C. Razzitte, Physica B 320, 261 (2002).
[22] S.R. Sarvant, D.S. Birajdar, S.S. Suryavanshi, A.M. Sankpal, B.L. Patil, S.A. Patil and R.N. Patil, Indian. J of Pure
and Appl. Phys, Vol. 28, 424 (1990).
[23] V.M. Nanoti, C.S. Prakash, D.K. Kulkarni, Materials Letters 24, 167 (1995).
[24] Kunal B Modi, V.T. Thamki and H.H. Joshi, Indian J. Phys. 70A, 497 (1996).
[25] V.G. Parmar, Kumal B Modi and H.H. Joshi, Ind. J. of Pure and Appl. Phys. Vol. 37, 207 (1999).
[26] D. Ravinder, K. Vijaya kumar and B.S. Boyanov, Materials Letters 38, 22 (1999).
[27] K.B. Modi, P.V. Tanna, S.S. Laghate and H.H. Joshi, J. Mat. Sci. Letters 19, 1111 (2000).
[28] R.A. Borzi, S.J. Stewart, G. Punte, R.C. Mercader, R.D. Zysler and M. Tovar, Solid State Commun. 117, 311
(2001).

ISSN 2350-1030
Page | 25
Paper Publications
[29] Zhenxing Yue, Longtuli, Ji Zhou, Hong guo, Zhang and Zhilum Gui, Materials Sci. and Eng. B 64, 68 (1999).
[30] S.F. Wang, Y.R. Wang, Thomas C.K. Yang, C.F. Chen and C.A. Lu, Scripta Mater, 43, 269 (2000).
[31] Zhenxing Yue, Longtu Li, Ji Zhou, Hongguo Zhang, Zhenwei Ma, and Zhilum Givi, Materials Letters, 44, 279
(2000).
[32] G.M. Bhongale, D.K. Kulkarni and V.B.S. Sappne, Bull, Mat. Sci, 15,121 (1992).
[33] C.G. Whifrey, D.W. Eckort and A. Tauber, J. Am. Chem.. Soc, 82, 2695 (1960).
[34] J.D. Dunitz and L.E. Orgel, J. Phys. Chem. Solids, 3, 318 (1957).
[35] G. Blasse, Philips Research Report Supplement, 3, 13 (1964).
[36] J.M. Daniels and A. Rosenberg, Can. J. Phys, 48, 381 (1970).
[37] T. Matsui and J.B. Wagner Jr., J. Elec. Chem. Soc., 124, 1141 (1977).
[38] C.P. Bean, J. Appl. Phys., 26, 1381 (1955).
[39] C. Radhakrishnamurthy and N.G. Nanadikar, Pramana, 13, 413 (1979).
[40] B. Viswanathan and V.R.K. Murthy, “ Ferrite Materials”, Springer Verlag, (1990).
[41] Derek Craik. “Magnetism”, Wiley (1995).
[42] L. Neel, L R Acad. Sci., 230, 375 (1950).
[43] S.S. Shinde, K.M. Jadhar, G.K. Bischite, et.al., Bull. Mat. Sci., 21, 409 (1998).
[44] B. Ramesh, A.D.P. Rao, P.R.M. Rao and S.B. Raju, Ind. J. Pure and Appl. Physics, 38, 550 (2000).

Study on Ni 0.5-X Znx Cu0.5 Fe2 O4 Sintered Ferrite System Using Xrd & High Field Techniques

More Related Content

What's hot (14)

Similar to Study on Ni 0.5-X Znx Cu0.5 Fe2 O4 Sintered Ferrite System Using Xrd & High Field Techniques (20)

Recently uploaded (20)

Study on Ni 0.5-X Znx Cu0.5 Fe2 O4 Sintered Ferrite System Using Xrd & High Field Techniques