Studying the Structure and the Optical Properties of Pd Nanoparticles Affected by Precursor Concentration

Munaf. S. Majeed et al. Int. Journal of Engineering Research and Applications www.ijera.com
ISSN: 2248-9622, Vol. 6, Issue 1, (Part - 1) December 2015, pp.12-17
www.ijera.com 12|P a g e
Studying the Structure and the Optical Properties of Pd
Nanoparticles Affected by Precursor Concentration
Munaf. S. Majeed*, Mohamed K. Dhahir*, Zainab. F. Mahdy*
*(Institute of laser for postgraduate study, Baghdad University, Baghdad, Iraq
ABSTRACT
In this paper, Palladium (Pd) nanoparticales (NPs) at different concentrations (150 and 500) capped with poly
(vinylpyrrolidone) (PVP) were Synthesized by a polyol reduction method in an ethylene glycol solution at
temperature of 45C˚. The structural and optical properties of Pd NPs has been investigated, all thin films were
tested using X-ray diffraction (XRD), all XRD peaks can be indexed as face centered cubic (FCC)
Structure, with strong crystalline orientation at (111) plane. The morphology properties of the prepared films
were study by Atomic Force Microscopy (AFM) the results indicated that all films have nanoscale grain size
around 80 nm and Scan Electron Microscopy (SEM) images show spherical nanoscale particles with clusters
shape. The size of the particles decreased with increasing of concentrations
Keywords - Metallic cations, Polyol Reduction, Pd Nanoparticles, Poly (vinylpyrrolidone), Precursor
concentration.
I. INTRODUCTION
Photonics researches require materials with large
nonlinear susceptibilities and fast response time.
These two important properties are available in noble
metal nanoparticles like gold, silver, and palladium.
Such materials have close-lying bands and their
conduction bands lye near Fermi level. The electrons
in conduction band move nearly free with oscillation
motion leads to rise resonance of the surface
plasmon[1].
Among many noble metal nanoparticles,
palladium occupies a large importance in hydrogen
storage, sensing, and other applications which require
catalytic materials [2].In addition to catalysis and
sensing, metal nanoparticles are used in optics,
electronics, biomedicine cancer therapy and fuel cells
that work at low temperature [3]. Noble metal
nanoparticles (NPs) work as homogeneous and
heterogeneous catalyst in chemical process industry,
therefore; they are considered as an enhancement
factor in these processes. Such properties have been
of interest for centuries.
Over the last few years, efforts have been
focused on manufacturing noble metal NPs with
controlled size, shape, and size distribution of the
nanoparticles [4]. Accordingly different methods
have been employing for this purpose. One of the
preferred methods over the mentioned period is
polyol’s synthesis. It is suitable for synthesizing
noble metal nanocrystals with well-defined shapes
due to the ability of polyols such as ethylene glycol
(EG) to dissolve many metal salts, in addition to the
dependence of the reducing power of the reaction on
the temperature [5]. In this process, the EG works as
reducing agent to reduce a metallic cations to
metallic collids [6]. The reduction reaction occurs at
high temperature with the assistance of polymeric
stabilizer usually polyvinylpyrroidone (PVP).
K.Patel et. al. [7] synthesized Pt, Pd, Pt – Ag,
and Pd – Ag nanoparticles using microwave – polyol
method. In their work thy studied the effect of PVP
on complexing and stabilizing nanoparticles. T.Nishi
et. al. [8] prepared Pd nanoparticles using laser
ablation in heavy and light water and tested the
magnetic properties of the product.
In this paper, we report our results on preparation
well shaped Pd nanoparticles using polyol system.
The effect of variation of precursor concentration on
the particle size is shown. Also the experimental
conditions were fixed.
II. EXPERIMENTAL STEPS
Palladium nanoparticles (Pd NPs), prepared
using Palladium nitrate dehydrate Pd(NO3 )2 .2H2O
and Polyvinylpyroiodine (PVP) as a stabilizer agent.
They were dissolved by ethylene glycol (C2H6O2).
The samples were prepared at temperature (45
o
C) ± 2 o
C for reaction time (60) min. Palladium
nanoparticles (Pd NPs) were prepared by adding
(500, 150) mg Pd(NO3) 2 .2H2O in 5 ml of ethylene
glycol. Also 100 mg PVP as a stabilizing agent was
dissolved in 25 ml of ethylene glycol. On the other
hand 45 ml of ethylene glycol was heated by
magnetic stirrer at (45o
C) ± 2o
C for reaction time (60)
minute, the temperature was monitored using a
thermometer. The inject of the two solutions in the
heated ethylene glycol with a burette and a syringe
pump and fed to reaction mixture for 15 minute after
RESEARCH ARTICLE OPEN ACCESS

dosing the precursor/stabilizing agent solution. A
light brown coloration was observed indicating the
formation of Pd nanoparticles. After the dosing was
completed, the resulting mixture was heated in the
same temperature of the E.G for the same reaction
time. Finally the solution was cooled to room
temperature.
An optical interferometer method was used to
determine the films thickness. In this method, the
samples were exposed to He:Ne laser beam. An
interference pattern formed due to the interference
between the light beam reflected from the film
surface with that reflected from the substrate. Then
the sample thickness was found using the following
equation [9].
2
x
t
x
 
 (1)
where λ is the wavelength of the laser, x is the width
of the bright fringes, and x is of the dark fringes
III. RESULTS AND DISCUSSION.
3.1 Structure measurement using
3.1.1 X-ray diffraction (XRD) analysis
X-ray diffraction has been employed for
identification and understanding the crystalline
growth nature. Diffraction patterns of the palladium
nanoparticles are shown in Figs. (1) and (2) at
different concentrations (150) and (500) respectively.
Fig.(1): The XRD pattern of Pd NPs at
concentration (150).
Fig.(2): The XRD pattern of Pd NPs at concentration
(500).
These nanoparticles which prepared at 45Co
show two different located peaks (111) and (200) for
Pd (150) and three peaks from (111), (200), and (220)
plans for Pd at (500) respectively. From the figures,
all XRD peaks can be indexed as faced centered
cubic (FCC) with strong peak at (111) direction for
both concentrations. The absence of peaks of any
other plans gives an indication that the product is at
high purity. Further from the figure, it can be seen
that the peaks’ intensities increased with increased
concentrations.
The grain size of the produced Pd nanoparticles
can be calculated from the peak broadening using
Scherer equation [10,11].
0.4
cosFWHM d
D

 
 (2)
where D: the mean diameter of the Pd nanoparticles,
 is the wave length of the X-ray source
diffracotmeter, and  is the full-width-half-maximum
(FWHM) of the XRD peak corresponding to the
Bragg angle 2 d . Also the diffraction patterns have
been used to calculate the lattice constant and the
results with the grain size are listed in Tables 1 and 2
for experimental and standard values. These results
show a good agreement with literature [12,13].
Table (1):- experimental and standard dhkl values for Pd NPs at concentration (150)
2θ (Deg.) FWHM (Deg.) dhkl Exp.(Å) G.S (nm) hkl dhkl Std.(Å) Card No.
39.938 1.329 2.2556 6.4 (111) 2.2395 96-101-1106
45.714 0.954 1.9831 9.0 (200) 1.9395 96-101-1106

Table (2):- experimental and standard dhkl values for Pd NPs at concentration (500).
3.1.2 AFM analysis.
The surface morphology of the Pd NPs was
investigated using (AFM) analysis. The value of
roughness and average grain size were calculated
from the height values in AFM image using the
commercial software. Fig. 3(A and B) and4 (A and
B) shows two and three-dimensional of (AFM)
images of Pd NPs deposited at various construction
(150, 500) respectively.
Fig. (3): Two -dimensional AFM images of Pd NPs
(A 150 )and (B 500) deposited on galas plate
Fig. (4): Three -dimensional AFM images of Pd NPs
(A 150) and (B 500) deposited on galas plate.
The average grain size of the particles is in
nanoscale and the values of average grain size and
surface roughness were listed in Table (3).
Table (3): Average Grain size and surface roughness
of Pd NPs.
Pd at different
construction
Average
grain size
(nm)
Roughness
(nm)
150 75 6.69
500 80 3.52
A grain is a single crystalline or polycrystalline.
It refers to agglomerate in bulk or thin film. The grain
size is estimated by XRD pattern or Scherer equation
2θ (Deg.)
FWHM
(Deg.)
dhkl Exp.(Å) G.S (nm) hkl dhkl Std.(Å) Card No.
40.1188 1.4303 2.2458 5.9 (111) 2.2395 96-101-1106
46.8048 1.3437 1.9394 6.4 (200) 1.9395 96-101-1106
68.6006 1.0836 1.3669 8.9 (220) 1.3714 96-101-1106
A
B
A
B

but the latter is only an approximation. One particle
consists of several grains and its size is larger. The
particle size can be measured either by AFM, SEM,
or TEM. This explanation justifies why there is a
different between nanosizes measured by AFM and
that of XRD pattern. The large values given in table 3
comperes to that in tables 1 and 2 indicate that our
product is in polycrystalline form.
3.1.3 SEM Analysis.
SEM technique provides detail topography and
structural information at suitable magnifications. By
scanning with an electron beam, an image that is a
good representation of the three dimensional sample
is formed. Thus morphology studies of Pd
nanoparticles were carried out with SEM and the
results are displayed in Fig.(5). As seen,
nanoparticles have been grown as individual clusters
with a few agglomerates over the surface.
Figure 5: SEM images of Pd NPs clusters.
3.2 Optical measurement.
3.2.1 Absorbance spectrum.
UV – VIS spectrophotometer was used to record
the optical absorption spectra of the Pd nanoparticles
thin films. The absorption spectra for the different
precursor concentration and within the wavelength
range of (200 – 1100 nm) are shown in fig. 6 (A and
B).
Fig.6A: Absorption spectrum of Pd NPs at
construction 150.
Fig.6B: Absorption spectrum of Pd NPs at
construction 500.
It can be observed that when the concentration
increases; the absorption value is also increases. This
occurs due to the participation of more atoms in the
absorption process. At visible light region, the strong
photo-absorption is presented in the wavelength 330
nm at each pulse. The spectra in figure 6 (A and B)
agree with references [7,14].
3.2.2 Absorption Coefficient and Optical Band Gap.
Materials are characterized and classified
according to their optical parameters such as
absorption coefficient, refractive index, and optical
energy gap. These parameters can be evaluated from
transmittance as well as absorbance. The absorption
coefficient is obtained from the relation [15].
2.303( )
A
t
  (3)
where A is the absorbance, t = 138nm for Pd 150 and
92 nm for Pd500; is the thickness of the thin films
which were obtained from Eq. (1). Both films
showed decreasing in absorption coefficient with

increasing wavelength. Therefore, the samples
transparency increased in the Vis – IR region.
According to this result, the product can be used in
solar cells.
The dependence of the optical band gab (Eg) on
the absorption coefficient and the incident photon
energy (hν) is given by [16].
1
2
( h ) k(h )gE    (4)
where k is a constant, ν is the frequency of the
incident photon. The value of Eg is obtaind by
plotting
2
( h )  versus h then extrapolating the
linear region on the energy axis as in Fig.( 7) A and
B.
Fig. 7A: Energy gab of Pd 150.
Figure 7B: Energy gab of Pd 500.
The value of Eg is 3.7 eV for 138nm film
thickness and 4 eV for 92nm. The decreasing of Eg
with increasing film thickness may be due to
possibility of structural defects which in their rule
lead to the formation of donor levels within the
energy gap. These results are identical to those in
reference [17].
IV. CONCLUSIONS
Pd nanoparticles with uniform shape were
prepared by polyol method at 45˚C. The current
results show that polyol method is an easy and
efficient method for synthesizing nanoparticles and
modifying the kinetics of atoms to assembly, growth,
and generate particle shapes. The size of the Pd
nanoparticles could be manipulated by varying the
metal precursor concentration. Further, using
ethylene glycol as reducing agent leads to formation
of chemical residues that can be easily removed from
the reaction mixture.
V. Acknowledgements
This work was supported by ILPS( Institute of
Laser for Post Graduate Study/ Baghdad University).
We thank Dr. Abdu Alkareem, School of Since/
department of Chemistry, who conducted the AFM
characterization of the samples.
REFERENCES
[1] U. Gurudas, E. Brooks, D. Bubb, and et. al.,
Saturable and reverse saturable absorption in
silver nanodots at 532 nm using
picosecond laser pulses, J. Appl. Phys.
Vol. 104, PP. 073-107, 2008.
[2] J. Cookson, The preparation of palladium
nanoparticles, platinum metals Rev, Vol. 56,
No. (2), PP.83-98, 2012.
[3] H. Hei, H. He, R. Wang, and et. al.,
Controlled synthesis characterization of
noble metal nanoparticles, soft science
letters, Vol.2, PP.34-40, (2012).
[4] C. Shen, C. Hui, T. Yang, and et. al.
Monodisperse Noble-Metal Nanoparticles
and Their Surface Enhanced Raman
Scattering Properties ,Chem. Mater. 20,
6939–6944, 2008.
[5] B. Lim, M. Jiang, J. Tao, and et. al. , Shape-
Controlled Synthesis of Pd Nanocrystals in
Aqueous Solutions, Adv. Funct. Mater. 19,
189–200, 2009.
[6] D. Berger, G. Traistaru, B.Vasileand et. al.,
Palladium Nanoparticl Synthesis with
Controlled Morphology Obtaind by Polyol
Method, U.P.B. Sci. Bull., Series B, Vol. 72,
Iss. 1, 2010.
[7] K. Patel, S. Kapoor, D. Purshot, and et. al. ,
Synthesis of Pt, Pd, Pt/Ag and Pd/Ag
nanoparticles by microwave-polyol method,
J. Chem. Sci., Vol. 117, No. 4, pp. 311–316.
2005.
[8] T. Nishi, A. Takeichi, H. Azuma,
Fabrication of Palladium Nanoparticles by
Laser Ablation in Liquid, JLMN-Journal of
Laser Micro/Nanoengineering Vol. 5, No. 3,
2010.

[9] M. Hernández, A. Juárez,* R. Hernández,
Interferometric thickness determination of
thin metallic films, Superficies y Vacío 9,
283-285, 1999.
[10] R. Devi, P. Purka, P. Kalita, and et. al.,
Synthesis of nanocrystalline CdS thin films
in PVA matrix, Bull. Mater. Sci., Vol. 30,
No. 2, pp. 123–128, 2007.
[11] I.Rathinamala, J.Pandiarajan, N.
Jeyakumaran, and et. al., Synthesis and
Physical Properties of nanocrystalline CdS
Thin Films – Influence of sol Aging Time
& Annealing Temperature, Int. J. Thin
Film Sci. Tec. 3, No. 3, 113-120 ,2014.
[12] V. Nguyen, D. Nguyen, H. Hirata, and et.
al., Chemical synthesis and characterization
of palladium nanoparticles, Adv. Nat. Sci.:
Nanosci. Nanotechnol. 1 035012 (5pp),
2010.
[13] S. Navaladian , B. Viswanathan ,T. K.
Varadarajan,and et. al., A Rapid Synthesis
of Oriented Palladium Nanoparticles by UV
Irradiation, Nanoscale Res Lett 4:181–186,
2009.
[14] H. Hei, H. He, R. Wang, and et. al.,
Controlled Synthesis and Characterization of
Noble Metal Nanoparticles, Soft
Nanoscience Letters, 2, 34-40, 2012.
[15] J. Mohammad, and H.Al-jumaili, Structural
and optical properties of Nanocrystalline
ZnxCd1-xS thin films deposited by chemical
bath technique , IJAIEM, Volume 3, Issue 5,
2014.
[16] M. Baykula , A. Balcioglub, AFM and SEM
studies of CdS thin films produced by an
ultrasonic spray pyrolysis method,
Microelectronic Engineering 51–52 ,703–
713, 2000.
[17] F. Samavat, F. Mahmoodi, P. Ahmad, Effect
of Annealing Temperature on the Optical
Properties of Palladium Thin Film, Open
Journal of Physical Chemistry, 2, 103-106,
2012.

Studying the Structure and the Optical Properties of Pd Nanoparticles Affected by Precursor Concentration

More Related Content

What's hot (20)

Similar to Studying the Structure and the Optical Properties of Pd Nanoparticles Affected by Precursor Concentration (20)

Recently uploaded (20)