Failure analysis & test procedure #1 rev
Download as PPTX, PDF2 likes1,224 views
This document provides information on failure analysis procedures for polymer materials. It discusses visual examination, identification analysis through techniques like FTIR and DSC, and microstructural analysis. Specifically, it describes different failure modes like excessive deformation, ductile failure, and brittle failure. It also outlines how FTIR can be used to analyze multilayer films and provides examples of glass transition temperatures and decomposition temperatures for various polymers.
Failure analysis & test procedure #1 rev
- 1. FAILURE ANALYSIS & TEST PROCEDURE #1
- 2. TOPIC • Visual examination • Identification analysis • Microstructural analysis
- 3. VISUAL EXAMINATION • Sample visualization is the important first step in the characterization of almost any sample. • Visualization of the sample can provide important physical information about the sample.
- 5. • Mechanical failure in polymer materials caused by : • Excessive deformation • Ductile failure • Brittle failure • Crazing
- 6. • Excessive deformation • Very large deformations are possible in low-modulus polymers are able to accommodate large strains before failure. • Such deformations could occur without fracture design features and other considerations might only tolerate deformations to a prescribed ceiling value. • The case in rubbery thermoplastics, such as flexible PVC or EVA, for pressurized tubing.
- 7. • Ductile failure • Encountered in materials that are able to undergo large-scale irreversible plastic deformation under loading, known as yielding, before fracturing. • Yielding marks the onset of failure setting the upper limit to stress in service to be below the yield point is common practice. • Estimate loading conditions likely to cause yielding (yield criteria), in order to design components with a view to avoid it in service.
- 8. • Brittle failure • This is a type of failure involves low strains accompanied by negligible permanent deformation and is frequently characterized by "clean" fracture surfaces. • It occurs in components that contain geometrical discontinuities that act as stress concentrations. Contrary to ductile failures plastic deformation provides a warning signal for the ultimate fracture, • Brittle failures can occur without prior warning, except for the formation of crazes, as in glassy thermoplastics. • Because of this design specifications based on fracture strength data tend to be conservative (e.g., will incorporate very large safety margins) with respect to the maximum stress levels allowed relative to the strength.
- 9. • Crazing • Crazing is a phenomenon that often occurs in glassy polymers before yielding, i.e. for deformation at temperatures below the glass transition. • It occurs at a strain level which is below the level required for brittle fracture and although undesirable, this type of "failure" is not catastrophic. • Crazing is often observed in highly strained regions during bending. • Crazes are made up of microcavities whose surfaces are joined by highly oriented, or fibrillar, material. • They are initiated near structural discontinuities, such as impurities, and are collectively visible at the strained surface because they become large enough to reflect light. • Crazes are not cracks and can continue to sustain loads after they are formed. • However, they can transform into cracks via the breakage of the fibrils.
- 10. IDENTIFICATION ANALYSIS FOURIER TRANSFORM INFRARED (FTIR) DIFFERENTIAL SCANNING CALORIMETER (DSC) THERMOGRAVIMETRY ANALYZER (TGA) MOLECULAR WEIGHT
- 11. FTIR • The most important techniques used to identify polymeric materials. • It is based on the interaction between matter and electromagmetic radiation of wavelengths in the infrared region (13300 – 20 cm-1).
- 12. FTIR TECHNIQUES • Transmission • Very simple FTIR technique. • For solid and liquid samples. • Attenuated Total Reflectance (ATR) • The IR radiation is reflected in a high refractive index crystal. • The ATR technique is very useful for the analysis of liquids, coextruded films, laminations, coatings, diagnose of blooming problems, metallic depositions, and surface chemical analysis.
- 13. FTIR TECHNIQUES • Photoacoustic Spectroscopy (PAS) • The PAS technique is an advantageous technique because it is not necessary to prepare the sample. • It is non-destructive. • Diffused Reflectance Infrared Fourier Transform Spectroscopy (DRIFTS) • Very useful technique for powders because preparation is not required. • It is appropriate for matte or rough surface.
- 14. FTIR TECHNIQUES – TRANSMISSION SOLID SAMPLES • IR transparent powder • Mull • Cast film • Pressed film • Free-standing film LIQUID SAMPLES • IR transparent powder
- 15. IR TRANSPARENT POWDER Material IR spectral range (cm-1) Reflactive index (at 2000 cm-1) KBr 40000 to 400 1.52 KCl 40000 to 500 1.46 CsI 40000 to 200 1.74 KRS-5 20000 to 250 2.45 Polyethylene 625 to 33 -
- 16. COMMERCIALLY AVAILABLE ATR CRYSTAL ATR crystal IR spectral range (cm-1) Reflactive index (at 2000 cm-1) Comments ZnSe IRTRAN 4® Orange color 20000 to 454 2.43 Ideal for aqueous solutions. Scratches easily. Brittle. Sensitive to acids and strong alkalis. Germanium mirror-like 5500 to 600 4.01 Due to the high refractive index is useful for low penetration analysis. High chemical resistance only attacked by hot sulfuric acid and aqua regia. KRS-5® Red color 20000 to 250 2.38 Mixed crystal (thallium bromide and iodide). Highly toxic. Ideal for wide spectral range studies. ZnS CLEARTAN® and IRTRAN 2® 17000 to 838 2.25 Ideal for aqueous solutions. High mechanical and thermal strength. Sensitive to strong oxidizing agents.
- 17. FTIR ANALYSIS OF MULTILAYER FILM
- 19. DSC • DSC is a thermal technique that measures the enthalpy changes, coupled with diverse physical and chemical events. • DSC can measure glass transition temperature, melting point, crystallization, crosslinking, chemical decomposition.
- 20. • Glass transition temperature (Tg) : temperature at which the relaxation mechanism of the macromolecules stops when the polymer is cooled. • Melting temperature (Tm) : temperature at which the crystalline domains are desegregated and a viscoelastic fluid is obtained. • Crystallization temperature (Tc) is always between Tm and Tg.
- 21. VARIOUS TRANSITIONS ASSOCIATED WITH POLYMERIC MATERIALS
- 22. GLASS TRANSITION TEMPERATURE OF SOME POLYMERS
- 23. MELTING POINT OF SOME POLYMERS
- 24. DSC ANALYSIS OF MULTILAYER FILM Melting peak 1 : 112.12°C (LDPE) Melting peak 2 : 123.83°C (LLDPE) Melting peak 3 : 175.66°C (EVOH) Melting peak 4 : 253.25°C (PET)
- 25. TGA • TGA is a thermal analysis technique that measures the weight changes of a sample under a certain temperature-time program working on the principle of a beam balance. • It is possible to evaluate : • Volatilization of moisture and additives • Decomposition of polymers and additives • Decomposition of organic pigments • Decomposition of some mineral fillers (calcium carbonate) • Thermogravimetric analysis is a key analytical technique used in the assessment of the composition of polymeric-based materials.
- 26. TEMPERATURE DECOMPOSITION OF SOME POLYMERS Polymer Temp decomposition at 20°C/min Temp decomposition at 50°C/min PVC 333 466 LDPE - 487 PS - 443 PA66 - 430 to 473 POM 315 370
- 28. MOLECULAR WEIGHT • Molecular weight and molecular weight distribution are probably the most important properties for characterizing plastics. • These parameters have a significant impact on the entirety of characteristics of a plastic resin, including mechanical, physical, and chemical resistance properties. • Changes can result in molecular weight decreases through such mechanisms as chain scission, oxidation, and hydrolysis, or as increases through destructive cross linking. • Changes in molecular weight can occur throughout the material life cycle and can significantly impact the performance of the molded part.
- 29. GPC for molecular weight analysis
- 30. MICROSTRUCTURAL ANALYSIS Fatigue striations in ABS vacuum cleaner part
- 31. MICROSTRUCTURAL ANALYSIS Characteristic brittle fracture features on the housing crack surface.