Material selection BSI.pdf

raising standards worldwide™
NO COPYING WITHOUT BSI PERMISSION EXCEPT AS PERMITTED BY COPYRIGHT LAW
BSI Standards Publication
BS EN ISO 21457:2010
Petroleum, petrochemical
and natural gas industries
— Materials selection and
corrosion control for oil and
gas production systems (ISO
21457:2010)
Copyright British Standards Institution
Provided by IHS Markit under license with BSI - Uncontrolled Copy
Licensee=ADNOC 9999103
Not for Resale, 2019/2/6 03:24:44
No reproduction or networking permitted without license from IHS
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010 BRITISH STANDARD
National foreword
This British Standard is the UK implementation of EN ISO
21457:2010.
The UK participation in its preparation was entrusted to Technical
Committee PSE/17/-/7, UK experts in ISO TC 67 Working Groups.
A list of organizations represented on this committee can be
obtained on request to its secretary.
This publication does not purport to include all the necessary
provisions of a contract. Users are responsible for its correct
application.
© BSI 2010
ISBN 978 0 580 59223 2
ICS 75.180.01
Compliance with a British Standard cannot confer immunity from
legal obligations.
This British Standard was published under the authority of the
Standards Policy and Strategy Committee on 30 September 2010.
Amendments issued since publication
Date Text affected
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

EUROPEANSTANDARD
NORMEEUROPÉENNE
EUROPÄISCHENORM
EN ISO 21457
September 2010
ICS 75.180.01
English Version
Petroleum, petrochemical and natural gas industries - Materials
selection and corrosion control for oil and gas production
systems (ISO 21457:2010)
Industries du pétrole, de la pétrochimie et du gaz naturel -
Choix des matériaux et contrôle de la corrosion pour les
systèmes de production de pétrole et de gaz (ISO
21457:2010)
Erdöl-, petrochemische und Erdgasindustrie -
Werkstoffauswahl und Korrosionsprüfung für Öl- und
Gasproduktionssysteme (ISO 21457:2010)
This European Standard was approved by CEN on 11 September 2010.
CEN members are bound to comply with the CEN/CENELEC Internal Regulations which stipulate the conditions for giving this European
Standard the status of a national standard without any alteration. Up-to-date lists and bibliographical references concerning such national
standards may be obtained on application to the CEN Management Centre or to any CEN member.
This European Standard exists in three official versions (English, French, German). A version in any other language made by translation
under the responsibility of a CEN member into its own language and notified to the CEN Management Centre has the same status as the
official versions.
CEN members are the national standards bodies of Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech Republic, Denmark, Estonia,
Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia, Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland,
Portugal, Romania, Slovakia, Slovenia, Spain, Sweden, Switzerland and United Kingdom.
EUROPEAN COMMITTEE FOR STANDARDIZATION
COMITÉ EUROPÉEN DE NORMALISATION
EUROPÄISCHES KOMITEE FÜR NORMUNG
Management Centre: Avenue Marnix 17, B-1000 Brussels
© 2010 CEN All rights of exploitation in any form and by any means reserved
worldwide for CEN national Members.
Ref. No. EN ISO 21457:2010: E
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
EN ISO 21457:2010 (E)
3
Foreword
This document (EN ISO 21457:2010) has been prepared by Technical Committee ISO/TC 67 “Materials,
equipment and offshore structures for petroleum, petrochemical and natural gas industries” in collaboration
with Technical Committee CEN/TC 12 “Materials, equipment and offshore structures for petroleum,
petrochemical and natural gas industries” the secretariat of which is held by AFNOR.
This European Standard shall be given the status of a national standard, either by publication of an identical
text or by endorsement, at the latest by March 2011, and conflicting national standards shall be withdrawn at
the latest by March 2011.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. CEN [and/or CENELEC] shall not be held responsible for identifying any or all such patent rights.
According to the CEN/CENELEC Internal Regulations, the national standards organizations of the following
countries are bound to implement this European Standard: Austria, Belgium, Bulgaria, Croatia, Cyprus, Czech
Republic, Denmark, Estonia, Finland, France, Germany, Greece, Hungary, Iceland, Ireland, Italy, Latvia,
Lithuania, Luxembourg, Malta, Netherlands, Norway, Poland, Portugal, Romania, Slovakia, Slovenia, Spain,
Sweden, Switzerland and the United Kingdom.
Endorsement notice
The text of ISO 21457:2010 has been approved by CEN as a EN ISO 21457:2010 without any modification.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
© ISO 2010 – All rights reserved iii
Contents Page
Foreword ............................................................................................................................................................iv
Introduction.........................................................................................................................................................v
1 Scope......................................................................................................................................................1
2 Normative references............................................................................................................................1
3 Terms, definitions and abbreviated terms..........................................................................................2
3.1 Terms and definitions ...........................................................................................................................2
3.2 Abbreviated terms.................................................................................................................................5
4 Design information for materials selection ........................................................................................6
5 Materials selection report.....................................................................................................................7
6 General guidelines for corrosion evaluations and materials selection...........................................7
6.1 General ...................................................................................................................................................7
6.2 Internal corrosion in oil and gas production and processing ..........................................................8
6.3 Internal corrosion in injection systems ............................................................................................12
6.4 Internal corrosion in utility systems..................................................................................................12
6.5 Sand erosion........................................................................................................................................13
6.6 External corrosion...............................................................................................................................13
6.7 Polymeric materials.............................................................................................................................15
6.8 Glass-fibre-reinforced plastic ............................................................................................................15
6.9 Mechanical properties and material usage limitations....................................................................15
7 Materials selection for specific applications and systems.............................................................16
7.1 General .................................................................................................................................................16
7.2 Oil and gas production and processing systems ............................................................................17
7.3 Injection systems ................................................................................................................................19
7.4 Utility systems .....................................................................................................................................20
7.5 Pipelines and flowlines.......................................................................................................................24
8 Corrosion control ................................................................................................................................25
8.1 Chemical treatment .............................................................................................................................25
8.2 Internal corrosion allowance..............................................................................................................26
8.3 Selection of internal and external coatings......................................................................................27
8.4 External splash zone protection ........................................................................................................27
8.5 Cathodic protection.............................................................................................................................27
8.6 Corrosion protection of closed compartments................................................................................28
8.7 Connection of dissimilar materials....................................................................................................28
8.8 Sealing materials.................................................................................................................................29
8.9 Fasteners..............................................................................................................................................29
8.10 Weld overlay ........................................................................................................................................30
8.11 Preferential weld corrosion ................................................................................................................30
8.12 Corrosion management ......................................................................................................................30
Annex A (informative) Design basis for hydrocarbon systems ...................................................................31
Annex B (informative) Corrosion monitoring.................................................................................................33
Annex C (informative) Chemical composition of some typical oilfield alloys............................................34
Bibliography......................................................................................................................................................38
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
iv © ISO 2010 – All rights reserved
Foreword
ISO (the International Organization for Standardization) is a worldwide federation of national standards bodies
(ISO member bodies). The work of preparing International Standards is normally carried out through ISO
technical committees. Each member body interested in a subject for which a technical committee has been
established has the right to be represented on that committee. International organizations, governmental and
non-governmental, in liaison with ISO, also take part in the work. ISO collaborates closely with the
International Electrotechnical Commission (IEC) on all matters of electrotechnical standardization.
International Standards are drafted in accordance with the rules given in the ISO/IEC Directives, Part 2.
The main task of technical committees is to prepare International Standards. Draft International Standards
adopted by the technical committees are circulated to the member bodies for voting. Publication as an
International Standard requires approval by at least 75 % of the member bodies casting a vote.
Attention is drawn to the possibility that some of the elements of this document may be the subject of patent
rights. ISO shall not be held responsible for identifying any or all such patent rights.
ISO 21457 was prepared by Technical Committee ISO/TC 67, Materials, equipment and offshore structures
for petroleum, petrochemical and natural gas industries.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
© ISO 2010 – All rights reserved v
Introduction
The provision of well-established and robust material selection guidelines offers a means of satisfying
long-term materials performance that meet the minimum requirements for a broad range of end users in the
petroleum, petrochemical and natural gas industries. An additional benefit can be to enable product suppliers
to develop, manufacture and provide off-the-shelf equipment that meets these requirements.
Oil and gas production projects benefit from a structured evaluation of materials used for the different fluids
being handled. Therefore, the main objective of this International Standard is to provide general requirements
with guidelines for the selection of materials for systems and components, with due consideration to the
transported fluids and the external environment.
It is the end user's responsibility to provide a project document with respect to implementation of the
requirements and guidelines of this International Standard, and to specify the design conditions for material
selection. In addition to the end user, the organization responsible for the facility or for the equipment design,
or for both, is regarded as responsible for materials selection.
This International Standard is developed to provide responsible parties with a structured process to carry out
materials selection in a consistent manner as a part of the engineering work, based upon a design basis for a
particular installation. This International Standard is intended for use by oil companies and engineering
contractors.
Users of this International Standard are advised that further or differing requirements might be needed for
individual applications. This International Standard is not intended to inhibit a vendor from offering, or the
purchaser from accepting, alternative equipment or engineering solutions for the individual application. This
can be particularly applicable where there is innovative or developing technology. Where an alternative is
offered, it is advisable that the vendor identify any variations from this International Standard and provide
details.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
INTERNATIONAL STANDARD ISO 21457:2010(E)
© ISO 2010 – All rights reserved 1
Petroleum, petrochemical and natural gas industries —
Materials selection and corrosion control for oil and gas
production systems
1 Scope
This International Standard identifies the corrosion mechanisms and parameters for evaluation when
performing selection of materials for pipelines, piping and equipment related to transport and processing of
hydrocarbon production, including utility and injection systems. This includes all equipment from and including
the well head, to and including pipelines for stabilized products. This International Standard is not applicable
to downhole components.
Guidance is given for the following:
⎯ corrosion evaluations;
⎯ materials selection for specific applications, or systems, or both;
⎯ performance limitations for specific materials;
⎯ corrosion control.
This International Standard refers to materials that are generally available, with properties that are known and
documented. It also allows other materials to be evaluated and qualified for use.
This International Standard does not provide detailed material requirements or guidelines for manufacturing
and testing of equipment. Such information can be found in particular product and manufacturing standards.
2 Normative references
The following referenced documents are indispensable for the application of this document. For dated
references, only the edition cited applies. For undated references, the latest edition of the referenced
document (including any amendments) applies.
ISO 15156-11), Petroleum and natural gas industries — Materials for use in H2S-containing environments in
oil and gas production — Part 1: General principles for selection of cracking-resistant materials
oil and gas production — Part 2: Cracking-resistant carbon and low-alloy steels, and the use of cast irons
oil and gas production — Part 3: Cracking-resistant CRAs (corrosion-resistant alloys) and other alloys
1) ISO 15156 (all parts) has been adopted by NACE as NACE MR0175/ISO 15156.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
2 © ISO 2010 – All rights reserved
3 Terms, definitions and abbreviated terms
3.1 Terms and definitions
For the purposes of this document, the following terms and definitions apply.
3.1.1
aquifer water
water from an underground layer of water-bearing permeable rock or unconsolidated materials
3.1.2
carbon steel
alloy of carbon and iron containing up to 2 % mass fraction carbon and up to 1,65 % mass fraction
manganese and residual quantities of other elements, except those intentionally added in specific quantities
for deoxidation (usually silicon and/or aluminium)
NOTE Carbon steels used in the petroleum industry usually contain less than 0,8 % mass fraction carbon.
[ISO 15156-1:2009, definition 3.3]
3.1.3
corrosion-resistant alloy
alloy intended to be resistant to general and localized corrosion by oilfield environments that are corrosive to
carbon steels
NOTE This definition is in accordance with ISO 15156-1 and is intended to include materials such as stainless steel
with minimum 11,5 % (mass fraction) Cr, and nickel, cobalt and titanium base alloys. Other ISO standards can have other
definitions.
3.1.4
end user
owner or organization that is responsible for operation of an installation/facility
3.1.5
free-machining steel
steel composition to which elements such as sulfur, selenium or lead have been intentionally added to
improve machinability
3.1.6
fugacity
non-ideal partial pressure that a component in a mixture exerts in the vapour phase when in equilibrium with
the liquid mixture
NOTE The fugacity factor depends on the temperature and the total pressure.
3.1.7
glass-fibre-reinforced plastic
composite material made of thermosetting resin and reinforced with glass fibres
3.1.8
hydrogen-induced cracking
HIC
planar cracking that occurs in carbon and low alloy steels when atomic hydrogen diffuses into the steel and
then combines to form molecular hydrogen at trap sites
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
NOTE Cracking results from the pressurization of trap sites by hydrogen. No externally applied stress is needed for
the formation of hydrogen-induced cracks. Trap sites capable of causing HIC are commonly found in steels with high
impurity levels that have a high density of planar inclusions and/or regions of anomalous microstructure (e.g. banding)
produced by segregation of impurity and alloying elements in the steel. This form of hydrogen-induced cracking is not
related to welding.
[ISO 15156-1:2009, definition 3.12]
3.1.9
hydrogen stress cracking
HSC
cracking that results from the presence of hydrogen in a metal and tensile stress (residual and/or applied)
NOTE HSC describes cracking in metals that are not sensitive to SSC but which can be embrittled by hydrogen when
galvanically coupled, as the cathode, to another metal that is corroding actively as an anode. The term “galvanically
induced HSC” has been used for this mechanism of cracking.
[ISO 15156-1:2009, definition 3.13]
3.1.10
liquid metal embrittlement
form of cracking caused by certain liquid metals coming into contact with specific alloys
3.1.11
low alloy steel
steels containing a total alloying element content of less than 5 % mass fraction, but more than that specified
for carbon steel
EXAMPLE AISI 4130; AISI 8630; ASTM A182 Grade F22[20].
3.1.12
manufacturer
firm, company or corporation responsible for making a product in accordance with the requirements of the
order, or with the properties specified in the referenced product specification, or both
3.1.13
marine atmosphere
atmosphere over and near the sea
NOTE A marine atmosphere will extend a certain distance inland, depending on topography and prevailing wind
direction. It is heavily polluted with sea-salt aerosols (mainly chlorides).
[ISO 12944-2:1998, definition 3.7.4]
3.1.14
maximum operating temperature
maximum temperature to which a component is subjected, including during deviations from normal operations,
such as start-up/shutdown
3.1.15
onshore
inland area with a non-chloride-containing atmosphere
3.1.16
operating temperature
temperature to which a component is subjected during normal operation
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
3.1.17
pH stabilization
increasing the bulk pH by addition of a suitable chemical to reduce CO2 corrosion in hydrocarbon systems
with condensing water
3.1.18
pitting resistance equivalent number
PREN
FPREN
number, developed to reflect and predict the pitting resistance of a stainless steel, based upon the proportions
of Cr, Mo, W and N in the chemical composition of the alloy
NOTE 1 For the purposes of this International Standard, FPREN is calculated from Equation (1):
FPREN = wCr + 3,3(wMo + 0,5wW) + 16wN (1)
where
wCr is the percent (mass fraction) of chromium in the alloy;
wMo is the percent (mass fraction) of molybdenum in the alloy;
wW is the percent (mass fraction) of tungsten in the alloy;
wN is the percent (mass fraction) of nitrogen in the alloy.
NOTE 2 Adapted from ISO 15156-3:2009, definition 3.10, and ISO 15156-3:2009, 6.3.
3.1.19
type 13Cr
martensitic stainless steel alloys with nominal 13 % Cr mass fraction alloying
EXAMPLE UNS S41000; UNS S41500.
3.1.20
type 316
austenitic stainless steel alloys of type UNS S31600/S31603
3.1.21
type 6Mo
austenitic stainless steel alloys with PREN W 40 and a nominal Mo alloying content of 6 % mass fraction, and
nickel alloys with Mo content in the range 6 % to 8 % mass fraction
EXAMPLE UNS S31254; UNS N08367; UNS N08926.
3.1.22
type 22Cr duplex
ferritic/austenitic stainless steel alloys with 30 u PREN u 40 and Mo u 2,0 % mass fraction
3.1.23
type 25Cr duplex
ferritic/austenitic stainless steel alloys with 40 u PREN u 45
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
3.1.24
stress corrosion cracking
SCC
cracking of metal involving anodic processes of localized corrosion and tensile stress (residual and/or applied)
NOTE 1 Parameters that influence the susceptibility to SCC are temperature, pH, chlorides, dissolved oxygen, H2S
and CO2.
NOTE 2 The above definition differs from that of the same term given in ISO 15156-1:2009, definition 3.21, since it
includes external environments.
3.1.25
sulfide stress cracking
SSC
cracking of metal involving corrosion and tensile stress (residual and/or applied) in the presence of water and
H2S
NOTE SSC is a form of hydrogen stress cracking (HSC) and involves embrittlement of the metal by atomic hydrogen
that is produced by acid corrosion on the metal surface. Hydrogen uptake is promoted in the presence of sulfides. The
atomic hydrogen can diffuse into the metal, reduce ductility and increase susceptibility to cracking. High strength metallic
materials and hard weld zones are prone to SSC.
[ISO 15156-1:2009, definition 3.23]
3.2 Abbreviated terms
AFFF aqueous film-forming foams
API American Petroleum Institute
ASCC alkaline stress corrosion cracking
ASME American Society of Mechanical Engineers
CP cathodic protection
CRA corrosion-resistant alloy
CUI corrosion under insulation
GRP glass-fibre-reinforced plastic
HAZ heat-affected zone
HB Brinell hardness
HDG hot-dip galvanized
HIC hydrogen-induced cracking
HRC Rockwell hardness C scale
HSC hydrogen stress cracking
HVAC heating-ventilation-air conditioning
MEG monoethylene glycol
MIC microbiologically induced corrosion
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
PE polyethylene
PP polypropylene
PREN pitting resistance equivalent number
PTFE polytetrafluoroethylene
PVC polyvinyl chloride
SCC stress corrosion cracking
SMYS specified minimum yield strength
SS stainless steel
SSC sulfide stress cracking
SWC step-wise cracking
TEG triethylene glycol
UNS unified numbering system (for alloys)
4 Design information for materials selection
This International Standard provides guidelines for material selection for oil and gas production facilities. To
enable the contractor to perform the material selections for the facility, the end user should as a minimum
provide the information specified in Table 1 at the time of enquiry and contract.
Table 1 — Design information for materials selection
Information to be provided Subclause
Project design basis, ref. Annex A 6.1
Corrosion-prediction model 6.2.1 and 6.2.2.2
Future changes in reservoir H2S- content 6.2.2.4
Methodology or model for pH calculation of produced water 6.2.3.2
Formation water analysis 6.2.3.2
Content of mercury in production fluids or gas 6.2.3.8
The oxygen content in de-aerated seawater for injection 6.3
Erosion-prediction model 6.5
Temperature limitations for use of stainless steels in marine atmosphere 6.6.2, Table 3
Compliance with DNV-RP-F112[21] for duplex stainless steel exposed to cathodic protection 6.6.4
Limitations in mechanical properties and use of materials 6.9
Temperature limitations for non-metallic materials 7.4.2, Table 9
Environmental requirements regarding use of corrosion inhibitors 8.1
Model for inhibitor evacuation, corrosion inhibition test methods and acceptance criteria 8.1
Use of external coatings to increase maximum temperature for stainless steel (SS) 8.3
Applicable standard for cathodic protection (CP) design to be defined 8.5.1
Strength and hardness limitation of fasteners in marine atmosphere 8.9
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
5 Materials selection report
Corrosion evaluations and materials selection should be documented in a report for further use by the project
and operations.
The following elements should be included:
⎯ short description of the project and expected facilities, e.g. field layout, remoteness of location, manned
versus unmanned facilities, etc.;
⎯ materials-related design input data for the operating conditions during the design life of the facility, e.g.
temperatures, pressures, fluid composition, sand production, etc. (see Annex A);
⎯ corrosion evaluations and materials selection;
⎯ requirements for corrosion inhibitor efficiency and availability;
⎯ requirements for corrosion control, e.g. CP and coatings;
⎯ requirements for corrosion monitoring;
⎯ identification of uncertainties from a materials perspective, new application for materials, use of new
grades;
⎯ need for material qualification testing.
6 General guidelines for corrosion evaluations and materials selection
6.1 General
The materials selection process shall take into account all statutory and regulatory requirements. The project
design criteria, such as design lifetime, inspection and maintenance philosophy, safety and environmental
profiles, operational reliability and specific project requirements, should be considered.
In general, robust materials selection should be made to ensure operational reliability throughout the design
life. For offshore installations and particularly subsea, access for the purposes of maintenance and repair can
be limited and costly, and should be carefully considered in the design.
Materials selection should normally be based on an evaluation of corrosion and erosion as described in the
following subclauses. All internal and external media should be considered for the entire design life. This
should also include the stages of transportation, storage, installation, testing and preservation. Degradation
mechanisms not specifically covered in this International Standard, such as fatigue, corrosion-fatigue, wear
and galling, should be considered for relevant components and design conditions.
Mechanical properties and usage limitations for different material grades should comply with applicable design
code requirements and guidelines given in 6.9. The material weldability should also be considered to ensure
an effective fabrication.
Cost and material availability have a significant influence on materials selection, and evaluations should be
made to support the final selection.
NOTE If life-cycle cost evaluations are considered appropriate, then ISO 15663-2 describes one methodology.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
6.2 Internal corrosion in oil and gas production and processing
6.2.1 Corrosion evaluation
A corrosion evaluation should be carried out to determine the general corrosivity of the internal fluids for the
materials under consideration. The corrosion mechanisms and the specified process design parameters
included in 6.2.2 and 6.2.3 should be considered.
The corrosion evaluation should be based on a corrosion prediction model, or on relevant test or field
corrosion data agreed with the end user. General and localized corrosion of carbon steel takes place over
time, and the anticipated corrosion rate should be calculated for the operating conditions.
6.2.2 Corrosion mechanisms
6.2.2.1 General
For wet hydrocarbon systems made of carbon steel or corrosion-resistant alloy (CRA) the corrosion
mechanisms indicated in Table 2 should be evaluated.
Table 2 — Materials prone to internal corrosion mechanisms in hydrocarbon systems
Corrosion mechanism Carbon and low alloy steel CRA
CO2 and H2S corrosion Yes Yesa
MIC Yes Yes
SSC/SCC caused by H2S Yes Yes
HIC/SWC Yes No
ASCC Yes No
SCC without H2S No Yes
a The presence of H2
S in combination with CO2
can also lead to localized attacks of CRAs. The critical parameters are temperature,
chloride content, pH and partial pressure of H2
S. There are no generally accepted limits and the limits vary with type of CRA.
6.2.2.2 CO2 and H2S corrosion
CO2 corrosion is one of the most common corrosion mechanisms that occur on carbon steels in oil and gas
production and processing systems. The most important parameters for CO2 corrosion are temperature,
partial pressure of CO2, pH, content of organic acids and flow conditions. Several models for the prediction of
CO2 corrosion on carbon steel are available, and the model used should be agreed with the end user.
The presence of H2S in combination with CO2 influences the corrosion of carbon steel. The type of corrosion
is dependent on the proportions of these constituents in the production fluids. For carbon steel, general
mass-loss corrosion caused by H2S-dominated corrosion conditions is rarely a problem, since the iron sulfide
scale is generally protective. However, if the scale is damaged, then localized pitting corrosion can occur.
Deposition of elemental sulfur or solids due to stagnant flow conditions may promote such localized corrosion.
No generally accepted corrosion models exist to predict this form of localized attack, and the evaluation
should therefore be based on operational experience.
Top-of-line corrosion can take place due to condensation of water in the top of the pipe in a stratified flow
regime. Important parameters for such top-of-line corrosion are flow regime, operating temperature,
condensation rate, CO2 fugacity and content of organic acids. Top-of-line corrosion should be evaluated using
models specifically made for this or using test data gathered under similar operating conditions. Top-of-line
corrosion can also be influenced by the presence of H2S.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
Under flowing conditions flow-enhanced corrosion or erosion-corrosion can occur. Flow-enhanced corrosion
will occur under high flow rates, as a result of accelerated mass transport of the reactants and reaction
products. Many corrosion models consider the influence of flow-enhanced corrosion and such models should
be used for prediction of corrosion rate under flowing conditions. At very high fluid velocities, even in the
absence of solids, the liquid phase can be so energetic as to mechanically erode any protective scales or
remove the protective inhibitor film in inhibited lines and cause erosion-corrosion. In the presence of solids,
such mechanical erosion of the protective layers/films can occur at lower fluid velocities. In both cases, the
consequences are more rapid material wastage rates than would be expected if simply summing predicted
erosion and corrosion rates. This erosion-corrosion can occur even at low predicted sand erosion rates in
fluids that are corrosive to the material under consideration. More information on sand erosion is provided
in 6.5.
6.2.2.3 Microbiologically induced corrosion
Microbiologically induced corrosion (MIC) from sulfate-reducing bacteria, or other bacteria such as
acid-producing bacteria and nitrate-reducing bacteria, can lead to high local corrosion rates. Low flow
velocities in pipelines increase the likelihood of MIC.
MIC is likely to occur in dead legs and other settling locations. Cleaning and chemical treatment can be used
to prevent MIC. The need for sampling points and biocide injection facilities should be considered in design.
NOTE MIC is normally caused by sessile bacteria in contact with carbon steel rather than planktonic bacteria.
6.2.2.4 Sulfide stress cracking (SSC)/stress corrosion cracking (SCC) caused by H2S
The evaluation and use of materials in conditions containing H2S, where cracking including hydrogen-induced
cracking (HIC) is possible, shall follow the requirements given in ISO 15156 (all parts). This evaluation should
include the potential for future changes in reservoir H2S content, especially if water injection is planned.
Dehydration of gas or use of corrosion inhibitors should not relax the requirement to use H2S-resistant
materials if the conditions are otherwise categorized as sour in accordance with ISO 15156 (all parts).
6.2.2.5 Alkaline stress corrosion cracking
Alkaline environments containing compounds such as amines, caustic or carbonates can cause alkaline
stress corrosion cracking (ASCC) of carbon steels, especially where there is the potential to concentrate these
compounds, e.g. in the presence of crevices or evaporation.
Typical mitigation measures may include heat treatment after welding or forming, use of protective coatings,
CRA or non-metallic materials.
NOTE Reference can be made to NACE RP0403[26] for guidance on caustic cracking or to API RP 945[18] for
guidance on amine cracking.
6.2.2.6 Stress corrosion cracking without H2S
Occasionally, internal SCC can occur in SS in the absence of H2S and dissolved oxygen in oil and gas
production systems. This is due to local process conditions causing water evaporation and
deposition/concentration of chlorides in high salinity waters and at high temperatures. Systems where this can
occur should be designed with fresh wash water injection facilities to prevent concentration of chlorides or
resistant materials should be used.
6.2.3 Corrosion parameters
6.2.3.1 General
Parameters considered in a corrosion evaluation should include the following, as appropriate:
a) CO2;
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
b) H2S;
c) temperature;
d) organic acids;
e) oil/gas properties and water content;
f) oxygen;
g) elemental sulfur;
h) mercury (Hg);
i) production chemicals.
Annex A gives an example of the contents of the design basis for materials evaluation in hydrocarbon systems.
It should be noted that the design basis should consider the possibility of changing operational conditions over
a facility's design life, such as increasing water cut and reservoir souring over the design life of the facilities.
6.2.3.2 CO2 and H2S contents
Most CO2 corrosion prediction models for carbon steel require input in terms of CO2 fugacity. The CO2 partial
pressure in the gas phase should be used, which can be derived from flash calculations for the actual
conditions. For piping/pipelines transporting wet hydrocarbon liquids (oil and condensate), the CO2 content
and the total pressure for the last separation stage should be used to estimate the corrosion rate. For lines
carrying wet gas, the CO2 fugacity is a function of the lines operational pressure and temperature.
To compensate for non-equilibrium conditions downstream of a pressure reduction, the corrosion rate found
for the conditions upstream of a pressure reduction may be assumed.
For evaluation of cracking including HIC in H2S-containing service, the partial pressure is normally used. The
H2S content in the gas phase should be used, which should be derived from flash calculations for the actual
conditions.
Corrosion and H2S cracking resistance vary with pH which is difficult to measure accurately since it has to be
done under actual pressure and temperature. Therefore, pH should be calculated by a suitable model or by
using ISO 15156. The calculation should be based on CO2 and H2S fugacities at the actual pressure,
temperature and composition of the produced water. The methodology used should be agreed with the end
user.
If a full water analysis is not available, the values used for corrosion and cracking evaluations should be
agreed with the end user. The following values may be used for an initial evaluation:
⎯ for solutions representing condensed water, as in gas-producing wells, the pH should be calculated
based on the actual temperature and CO2/H2S fugacity for pure water; with no data available, a pH of 3,5
and a chloride content of 600 mg/l may be used (1 000 mg/l of NaCl) (this corresponds to a CO2 fugacity
of 1,0 MPa);
⎯ for solutions representing formation water, as in oil-producing wells, a pH of 4,5 and a chloride content of
100 000 mg/l may be used (165 000 mg/l of NaCl).
When calculating the pH used in CO2 corrosion predictions in gas production environments with condensing
water, it should be evaluated if the water contains sufficient corrosion products, as they act to increase pH and
reduce corrosivity. Downstream of CRA piping or equipment, such as gas coolers, it should be assumed that
the water is free from corrosion products and potentially corrosive to carbon steel.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
6.2.3.3 Temperature
Resistance to corrosion and SCC vary with temperature for carbon steels and CRAs. Sensitivity calculations
or evaluations can be necessary to determine the most critical temperature range.
The possibility of periods involving higher temperatures, such as heat tracing, steam-out or solar radiation,
should be considered in the corrosion evaluation.
Temperatures during construction, transportation, storage and installation should also be considered.
6.2.3.4 Organic acids
Organic acids increase the corrosivity of the produced fluids and their presence should be included in the
corrosion evaluation for carbon steel.
NOTE The corrosivity due to organic acids is determined by the presence of undissociated organic acid, as opposed
to organic acid salts. Hence, it is essential to consider the complete water chemical analysis.
6.2.3.5 Oil/gas properties and water content
Flow effects and liquid properties can keep the water entrained in the oil phase. This may prevent contact
between the separated water and the steel surface. However, the potential inhibition effect of the oil phase
should be used with caution. Laboratory testing can be utilized to determine if oil can have inhibiting properties.
A gas is considered dry when the water dew point at the operational pressure is at least 10 °C lower than the
minimum operating temperature for the system. Such systems are not subject to electrochemical corrosion
and no corrosion prediction is required.
NOTE Gas dehydration in glycol contactors leads to condensation of a glycol/water mixture in dry gas pipelines
[typically less than 10 % (mass fraction) water]. Even though this does not represent any corrosion threat for the pipeline,
large quantities of corrosion products can accumulate in the pipeline. These products can cause problems, since the
corrosion products can arrive at the receiving facility as “black dust” during pigging operations.
If the export gas specification is less than this dew point limit or there is a possibility of transient periods of
operation with insufficient or no dehydration, this should be considered in the corrosion evaluation.
6.2.3.6 Oxygen
Oxygen is not normally present in production streams. Chemicals for injection may contain oxygen and the
need for controlling the oxygen content should be evaluated.
The risk of oxygen ingress is likely in systems operating under vacuum and when an inert gas is used as
blanket gas. The purity of the inert gas is a parameter that should be included in the corrosion evaluation.
Oxygen ingress due to imperfect seals in pumps and compressors should be considered.
NOTE The fact that the internal system pressure exceeds the external pressure does not alleviate this risk, because
the partial pressure of oxygen in the atmosphere will most likely exceed the internal partial pressure of oxygen. Hence, a
driving force for oxygen ingress exists in spite of the negative absolute pressure difference.
6.2.3.7 Elemental sulfur
Elemental sulfur can be present in natural gas, and it can precipitate when the pressure or the temperature is
reduced. Elemental sulfur also forms if H2S comes into contact with oxygen, e.g. as a result of oxygen ingress
into the process systems.
Elemental sulfur is extremely corrosive to carbon steel as well as to some CRA materials. If elemental sulfur is
present, tolerant materials or chemical treatment should be used. ISO 15156-3 gives guidance on
sulfur-resistant materials.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
6.2.3.8 Mercury
Effects of the presence of mercury in produced fluids or gas should be considered in selection of materials.
Limits are not well established and therefore mercury-bearing streams should not use copper-, titanium- or
aluminium-based alloys for any components.
NOTE Mercury and associated mercury compounds can be detrimental to certain materials. Mercury can occur
naturally as a contaminant in well-production fluids or gas. It is necessary to recognize the possible presence of mercury
at the earliest possible stage of design, in order to avoid specification of potentially susceptible materials. It is generally
accepted that damage can occur only when mercury is present as liquid. Attack can be by amalgam formation or by liquid
metal embrittlement.
6.2.3.9 Production chemicals
Chemicals injected into the process stream or downhole can be potentially corrosive, and this should be
considered in the corrosion evaluation. The selection of the actual chemicals is normally performed after all
materials are selected and installed. Testing should be required to qualify the chemicals with respect to
compatibility with all materials, including organic materials in seals, pipes, coatings and liners.
6.3 Internal corrosion in injection systems
The most relevant corrosion mechanisms for injection of gas, produced water and aquifer water are the same
as for hydrocarbon carrying systems covered in 6.2 and the corrosion evaluation should be made accordingly.
For de-aerated seawater, there are two possible corrosion mechanisms, oxygen corrosion and bacterial
corrosion. A typical residual oxygen concentration for unchlorinated de-aerated seawater under normal
operation is 20 mg/m3 to 50 mg/m3, but can be significantly higher during upset conditions and during
chemical treatments. The actual concentration of oxygen varies with type of de-aeration system. To select
materials effectively, the assumed oxygen content in the seawater should be agreed with the end user.
6.4 Internal corrosion in utility systems
A corrosion evaluation should be carried out to determine the general corrosivity of the internal fluids under
the applicable design conditions and for the materials under consideration.
Evaluation of corrosivity in water-carrying systems should include parameters such as:
⎯ maximum design/operating temperature;
⎯ flow rate (stagnant, intermittent or continuously flowing).
In addition, chloride concentration (salinity), water chemistry and pH should be considered for fresh-water
systems, and residual chlorine and operating mode (dry or wet when not in use) should be considered for
seawater systems.
Residual chlorine level and temperature are the two most important parameters that affect the corrosion
performance of passive materials. Seawater systems are often continuously chlorinated to prevent bio-fouling;
a typical residual chlorine level for continuous use is 0,3 mg/l to 0,7 mg/l. Initial start-up without chlorination for
a period of two weeks can be used to promote build-up of the passive layer.
NOTE Biofouling treatment packages containing copper additives and much lower residual chlorine levels can be
specified as an alternative. This can reduce the corrosion threat.
Materials such as CuNi 90/10 and NiAl bronze are sensitive to the flow rate; see EEMUA 194[24].
Corrosion evaluations of utility systems not particularly addressed below should be made to the extent
deemed relevant for each project.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
6.5 Sand erosion
In cases where the potential exists for significant sand production, a sand erosion evaluation should be carried
out. The evaluation should include sand prediction studies in the reservoir to provide information regarding
reservoir sanding potential, as well as an evaluation of possible erosion damage. Erosion-prediction models
can be used to evaluate the likelihood of erosion damage. The model used should be specified by or agreed
with the end user. Even where the predicted erosion rate is low, the potential for synergistic erosion-corrosion
should be considered as discussed in 6.2.2.2.
Evaluation of sand-removal equipment, evaluation of safe operating conditions, monitoring of sand production,
setting of operational alarms and confirmation of the integrity of the production systems are also important
issues for consideration as part of the overall sand management strategy for each facility.
6.6 External corrosion
6.6.1 General
General and localized external corrosion including SCC and hydrogen stress cracking (HSC) should be
considered.
The external environment affects the selection of materials and the method(s) chosen to provide protection
from external corrosion. Typical environments to be considered in the evaluation of external corrosion are
classified in ISO 12944-2.
In addition to guidelines and criteria for steel structures design given in ISO 12944-3, the following items
should be considered in order to avoid premature corrosion and degradation of coating, or structures, or both:
⎯ normal atmospheric conditions (marine or non-marine);
⎯ contact with soil, or pipe supports, or both;
⎯ ambient temperature and maximum operating temperature;
⎯ presence of external insulation, with or without heat tracing;
⎯ solar heating;
⎯ presence of water, such as flooding by deluge systems.
Guidelines for suitable coating systems as a function of design life and corrosivity category are considered in
ISO 12944-5.
6.6.2 External marine atmospheric environments
The external marine atmospheric environment contains water and chloride salts. Carbon steels will corrode
under such conditions. CRAs can suffer from corrosion, including SCC. Welds are particularly vulnerable to
SCC due to residual stresses and geometric stress concentrations.
Table 3 presents typical maximum operating temperature limits that have been applied to avoid
chloride-induced SCC for some uncoated SS. The lower temperature limit represents cracking in the “worst
case situation” at high tensile stresses and at concentrated chloride salt levels experienced when salt
containing water is continuously evaporated. The lower temperature limits are based mostly on laboratory
experiments. Many end users have used the higher temperature limits indicated in Table 3. Extensive field
experience over many years shows that very few SCC failures have occurred on uncoated and uninsulated
pipes when these higher temperature limits were used.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
Table 3 — Typical temperature limits for uncoated SS in marine atmospheric environments
Material type Grade
Maximum operating temperature limitsab
°C
Type 316 50 to 60
Austenitic SS
Type 6Mo 100 to 120
Type 22Cr 80 to 100
Duplex SS
Type 25Cr 90 to 110
a The materials may be used at higher maximum operating temperatures at marine installations within areas with full
heating-ventilation-air conditioning (HVAC) control.
b Nickel-based and titanium alloys do not have established temperature limits in marine environments, but are recognized to be more
resistant than stainless steels.
Pitting and crevice corrosion can occur on CRAs at temperatures lower than those given in Table 3. A coating
may be applied to prevent such corrosion. This is particularly the case under insulation and under pipe
supports and clamps. Coating to prevent SCC should be used with caution (see 8.3).
Nickel-, titanium- and copper-based alloys are in general considered to be immune to SCC in marine
environments.
6.6.3 External non-marine atmospheric environments
External non-marine atmospheric environments can contain water, but normally very low chloride content.
NOTE Non-marine environments can be corrosive depending on the local atmospheric conditions.
The potential for external corrosion in non-marine, arctic and desert environments varies depending on
geographic location and industrial pollution. Consequently, it is necessary to evaluate the requirements for
painting on a case-by-case basis. Guidelines for defining environments in terms of external corrosivity are
considered in ISO 12944-2.
6.6.4 Buried and submerged installations
The external protection of buried or submerged structures is usually achieved by a combination of external
coatings and cathodic protection. The evaluation for corrosivity categories may be difficult to define, but some
guidelines are given in ISO 12944-2. For external corrosion mechanisms and protection of buried pipelines,
see ISO 13623.
It has been shown that some materials are susceptible to HSC if they are subjected simultaneously to
stresses and cathodic protection resulting in potential hydrogen charging of the cathodic component.
Depending on metallurgical condition, some CRAs, such as UNS S17400, UNS N05500 and duplex stainless
steel, can be susceptible to HSC while cathodically protected. To minimize such risk in these alloys, they
should be used in a heat treatment condition compliant with ISO 15156/NACE MR0175. DNV-RP-F112[21] is a
guideline for avoiding HSC in duplex stainless steel.
6.6.5 Corrosion under insulation
Corrosion under insulation (CUI) and fireproofing is a major integrity threat, particularly to installations located
offshore and at coastal locations. The problem is generally associated with carbon and low alloy steels, but
austenitic stainless steels and duplex stainless steels should also be considered. The CUI integrity threat is
influenced strongly by the external material surface temperature, presence of chlorides, and local
condensation conditions on the metal surface.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
Specification of marine service external coating systems is essential in mitigation of CUI when such a threat is
identified. Additionally, careful selection of external insulation systems and sealing systems to minimize water
entry needs to be considered in the design of the insulation system. Guidelines for selection of external
coatings and insulation systems for austenitic stainless steel and carbon steel are given in NACE RP0198[25].
Other guidelines are given in EFC Document No. 55[23].
The design should also consider the insulation integrity inspection requirements in service.
6.7 Polymeric materials
The selection of polymeric materials, including elastomeric materials, should be based on an evaluation of the
functional requirements for the specific application. The materials should be qualified according to procedures
described in applicable material/design codes.
Dependent upon application, the following properties should be included in the evaluation and documented:
⎯ thermal stability and ageing resistance at specified service temperature and environment;
⎯ physical and mechanical properties;
⎯ thermal expansion;
⎯ swelling and shrinking by gas and by liquid absorption;
⎯ gas and liquid permeation;
⎯ decompression and creep resistance at high temperature and pressure;
⎯ resistance to thermal cycling and dynamic movement;
⎯ low-temperature flexibility;
⎯ chemical resistance;
⎯ fire resistance.
NOTE ISO 23936-1 gives guidelines for selection and qualification of thermoplastic polymers in contact with media
related to oil and gas production, and also provides guidance on maximum and minimum allowable temperatures.
6.8 Glass-fibre-reinforced plastic
For systems where glass-fibre-reinforced plastic (GRP) may be applied, epoxy and vinyl ester resins should
be evaluated as alternatives for vessels and tanks; see also ISO 14692 (all parts). Polyester resin may be
used in tanks for seawater and open-drain services. For other than seawater and fresh-water services, the
fluid compatibility should be evaluated and documented in accordance with 6.7.
The temperature and aggressiveness of the medium can require that the GRP be lined with a thermoplastic
barrier/liner, e.g. tanks for hypochlorite systems.
6.9 Mechanical properties and material usage limitations
6.9.1 General
Mechanical properties such as yield strength, tensile strength, hardness and impact toughness should be
considered in the selection of materials. In addition, for parts of the production system that can operate at low
temperatures or experience low temperatures during blow-down conditions, the equipment can still be cold
when it is repressurized or constrained, causing thermal cooling stresses and thus requiring material
toughness to be sufficient to prevent brittle fracture under these transient conditions. Material properties based
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
upon the minimum and maximum design metal temperatures and wall thicknesses shall be in compliance with
specified design codes.
Exposure temperatures during intermediate stages, such as manufacturing, storage, testing, commissioning,
transport and installation, should be considered when specifying the minimum design temperature.
The following guidelines for design and limitations in mechanical properties should apply for materials
selection:
⎯ the specified minimum yield strength (SMYS) of carbon and low alloy steels intended for welding should
not exceed 560 MPa. A higher SMYS may be specified, provided that documentation showing acceptable
properties with respect to weldability and the properties of the base material, heat-affected zone and weld
metal is presented;
⎯ usage limitations for materials in H2S-containing environments shall be in accordance with ISO 15156-2
and ISO 15156-3;
⎯ free-machining steel grades should not be used;
⎯ austenitic SS castings with PREN W 40 should not be used for butt weld components due to risk of micro
cracking in the heat-affected zone (HAZ) in weldments;
⎯ the hardness of weld and HAZ of any steel grade should not exceed 350 HV10 for non-H2S-containing
service;
⎯ titanium should not be used for hydrofluoric acid or anhydrous methanol with water content less than 5 %.
6.9.2 Submerged installations
For submerged components that can be exposed to cathodic protection including fasteners, the following
guidelines are given:
⎯ the actual yield strength of any steel grade should not exceed 950 MPa;
⎯ the hardness of any components in any steel grade should not exceed 35 HRC or 328 HB;
NOTE 1 For conversion of hardness numbers, ISO 18265 is used.
⎯ for components made with duplex stainless steel, compliance with DNV-RP-F112[21] should be specified
(see 6.6.4);
⎯ the hardness of components in nickel-based alloys should not exceed hardness values stated in
ISO 15156-3;
⎯ titanium-based alloys should not be used for applications involving exposure to cathodic protection.
NOTE 2 Practical design solutions, including application of a suitable electrical isolation of the integrated titanium
component, can be agreed with the end user.
7 Materials selection for specific applications and systems
7.1 General
Typical materials selection for specific systems and areas are given in Tables 4 to 12. However, this does not
exclude the use of other materials.
The chemical compositions of typical alloys used for oilfield developments are listed in Table C.1.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
7.2 Oil and gas production and processing systems
7.2.1 General
For wet hydrocarbon processing involving flowlines and pipelines, carbon steel should be evaluated for
corrosion performance as the base-case materials selection option. This evaluation may include successful
operating experience, or may be based on the fact that the calculated annual corrosion rate, taking into
account protective measures, is less than the corrosion allowance divided by the specified design life.
CRA should be evaluated against carbon steel when this is considered appropriate in the materials selection
process.
For wet gas/condensate processing, the corrosivity of the wet gas to carbon steel can be very high due to the
low pH of the condensed-water phase. Additionally, corrosion inhibition might not be practical in these
systems, and the appropriate material choice is either carbon steel with a corrosion allowance or a CRA.
For dry gas/oil/condensate systems, carbon steel can be selected with no requirements for internal corrosion
control. However, a corrosion allowance may be required if periods of wetness are envisaged during the
construction/commissioning phases or during the operational phase.
7.2.2 Heat exchangers
Materials selection for heat exchangers requires the following special considerations:
⎯ corrosion allowances are not generally available for carbon steel tubes (shell-and-tube type)/plates (plate
type), and thus it is necessary to consider CRA for many applications in which carbon steel is chosen as
a piping material;
⎯ the design of the heat exchanger, e.g. shell-and-tube, air coolers, plate coolers, strongly influences the
materials selection;
⎯ the materials selection considerations should be very specific, e.g. severe crevicing conditions in hot
seawater;
⎯ ingress of water from deluge systems between plates in bolted plate heat exchangers should be
considered;
⎯ high surface temperature creates a risk of SCC or crevice corrosion of the plate or tube material on both
the crude and hot water sides of crude oil heaters or gas coolers.
7.2.3 Wellhead, production and process systems
Typical materials selection for production and process system are given in Table 4. Closed drain and fuel-gas
systems are listed under utility systems in this International Standard.
Pressure vessel materials for oil/gas/water separation and gas-treating systems should be selected based on
the same corrosivity criteria as for hydrocarbon piping systems. Pressure vessels manufactured in solid CRAs,
internally CRA clad or weld overlaid, do not need additional internal corrosion protection systems. To eliminate
the risk of external SCC of a pressure vessel in solid stainless steel, it is advantageous in some cases to use
internally CRA clad carbon steel pressure vessels.
Materials for valve internals should have wear resistance, or abrasion resistance, or wear and abrasion
resistance, for use in fluid services that contain suspended solids. The internals should have the same or
better corrosion resistance than the body, and should be corrosion resistant to the internal service conditions.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
Table 4 — Typical materials for hydrocarbon production and process systems
Equipment Materials
Wellhead equipment/Xmas trees
⎯ Carbon steel or low alloy steel with or without alloy 625 weld overlay
covering seal areas and other fluid-wetted areas
⎯ Type 13Cr steel with/without alloy 625 overlay at sealing surfaces
Piping
⎯ Carbon steel or low alloy steel with or without CRA clad
⎯ Type 316; type 22Cr duplex; type 25Cr duplex; type 6Mo
Valve body/bonnets
⎯ Carbon steel or low alloy steel with or without alloy 625 weld overlay
⎯ Type 13Cr; type 316; type 22Cr duplex; type 25Cr duplex; type 6Mo
Surface installations and
subsea retrievable
Type 13Cr steel or alloys with better corrosion resistance than the body
Valve internals
Subsea installations
non-retrievable
Alloy 718 or alloys with equivalent or better corrosion resistance than the
body
Vessels
⎯ Carbon steel with and without internal organic coating or lininga
⎯ Carbon steel with CRA clad or weld overlay such as type 316,
alloy 904, alloy 825 or alloy 625
⎯ Type 316, type 22Cr duplex, type 25Cr duplex
a Sacrificial anodes may be required for pressure vessels made of carbon steel with internal coating or lining. The requirement for
regular inspection and coating repairs should be accounted for in materials selection.
7.2.4 Flare systems
The typical materials selection for flare systems is given in Table 5.
Table 5 — Typical materials for flare systems
Equipment Materials
Relief system, piping and vessels Carbon steel, type 316; type 6Mo; alloy 904
Flare-tip assembly UNS S31000; UNS S30815; alloy 800H; alloy 625
7.2.5 Produced water
There are several corrosion mechanisms that can occur in produced water systems. The materials selection is
influenced strongly by operating experience.
Produced water systems can be complex, and oxygen contamination can occur, as described in 6.2.3.6.
Seawater ingress from drain systems has also been reported. Some produced water systems can support
bacterial activity, especially if the sulfate concentration is high, due to breakthrough of seawater from previous
seawater injection. In such circumstances, microbiological corrosion is the main integrity threat for carbon
steel. Oxygen ingress and MIC strongly influence the selection of corrosion control chemicals.
The typical materials for produced water systems are given in Table 6.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
Table 6 — Typical materials for produced water systems
Equipment Materials
(for re-injection systems)
Carbon or low alloy steel internally clad with alloy 625 on all sealing surfaces or on all
wetted surfaces
Piping Carbon steel; type 316; type 22Cr duplex; type 6Mo; GRP
Vessels and equipment Carbon steel with and without internal organic coatinga; type 316; type 22Cr duplex
Pumpsb Type 316; type 22Cr duplex; type 25Cr duplex
Valve body/bonnets Carbon steel; type 316; type 22Cr duplex; carbon steel internally clad with alloy 625
Valve internalsc Type 316; type 22Cr duplex, or alloys with equivalent or better corrosion resistance
a Sacrificial anodes should be required for pressure vessels made of carbon steel with internal coating or lining. Regular inspection
and coating repairs should be specified.
b For details on pump materials, see ISO 13709.
c Type 13Cr should not be used in produced water service.
7.3 Injection systems
7.3.1 General
Injection systems involve injection of water or gas into the sub-surface for disposal or stimulation purposes.
Water injection systems include injection of de-aerated seawater, untreated seawater, chlorinated seawater,
produced water, aquifer water, and combinations and mixing of different waters.
Brackish water should be considered as seawater.
NOTE Aquifer water comes from an underground layer of water-bearing, permeable rock from which ground water
can be extracted. This water can be used for injection into oil-bearing reservoirs.
7.3.2 De-aerated seawater
Typical materials for systems carrying de-aerated seawater are listed in Table 7.
7.3.3 Aerated seawater
Typical materials for use in untreated and chlorinated seawater injection systems are listed in Table 8. In
Table 10 typical maximum operating temperature limitations in chlorinated seawater with crevices for specific
material grades are specified.
7.3.4 Produced water and aquifer water
The requirements for produced and aquifer water injection systems are the same as for produced water
systems; see 7.2.5.
Nitrate injection should not be used for restraining sulfate-reducing bacteria activity in carbon steel produced
water systems.
Aquifer water may be used as injection water. It can contain a high concentration of dissolved CO2 which
should be taken into account when evaluating corrosivity.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
The effects of combined seawater and produced water injection should be considered with respect to
corrosion and scaling effects. The corrosion rates can be higher than expected from simple CO2 and O2
corrosion models. The risk of MIC can be substantial and should be considered in the design.
7.3.5 Gas injection systems
The typical materials selection for dry gas injection systems is carbon steel. If the gas is not dehydrated, the
system can be treated as a production system (wet gas).
Table 7 — Typical materials for de-aerated seawater systems
Equipment Materials
Carbon or low alloy steel internally clad with alloy 625 on all sealing surfaces
or on all wetted surfaces
Piping Carbon steel; GRP; type 316; type 22Cr duplex
De-aeration tower
Carbon steel with internal organic coating plus cathodic protection in the
bottom section
Pumpsa Type 316; type 22 Cr duplex; type 25Cr duplex
Valve body/bonnets Type 316; type 22Cr duplex
Valve internalsb Type 316; type 22Cr duplex, or alloys with equivalent or better corrosion
resistance
a For details on pump materials, see ISO 13709.
b Type 13Cr should not be used in produced water service.
Table 8 — Typical materials for untreated seawater systems
Equipment Materials
Wellhead equipment/Xmas trees Carbon or low alloy steel internally clad with alloy 625 on all wetted surfaces
Piping GRP; type 25Cr duplex; type 6Mo; CuNi 90/10a; titanium grade 2
Vessels
Carbon or low alloy steelb with internal organic coating or lining in combination
with cathodic protection; GRP; type 6Mo; type 25Cr duplex
Pumps Type 25Cr duplex
Valve body/bonnet Carbon or low alloy steel clad with alloy 625; type 25Cr duplex
Valve internals Type 25Cr duplex or alloys with equivalent or better corrosion resistance
a CuNi 90/10 is not compatible with CRAs or more noble materials with respect to galvanic corrosion.
b Carbon steel clad with CRA may be used as alternative to solid CRA.
7.4 Utility systems
7.4.1 General
The materials selection guideline for utility systems includes fuel gas, open drains, closed drains, water
services, chemicals, air and nitrogen systems.
Many utility systems contain fluids that are not or only mildly corrosive. Therefore, the integrity of the systems
is generally not at risk, but it should be considered that even small amounts of corrosion products may result
in unacceptable contamination.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
7.4.2 Fresh-water systems
Potable water, demineralized water, de-ionized water and desalinated water are considered as fresh water.
The chloride concentration is normally less than 100 mg/l.
Typical materials for handling fresh water are listed in Table 9.
Table 9 — Typical materials for handling fresh water
Equipment Material
Typically applied maximum
internal temperature
°C
Piping, valves, vessels, heat exchangers and tanks Type 316 60a to120
Piping, vessels, heat exchangers and tanks CuNi 90/10 120b
Valves Al-bronze 120b
Piping Copper 120b
Piping, vessels and tanks GRP (epoxy resin) 95
Piping, vessels and tanks GRP (polyester resin) 40
Piping, vessels and tanks GRP (vinyl ester resin) 80c
Piping, vessels and tanks Epoxy-coated carbon steel 95c
Piping Carbon steel HDG 50
Piping and tanks PVC 70c
Piping and tanks PE 60c
Piping and tanks PP 90c
a
The chloride concentration should be kept below 200 mg/l up to 60 °C. For higher temperatures, the chloride should be limited to
lower concentrations to prevent internal pitting corrosion that can occur on type 316. A commonly used maximum operating temperature
for uncoated type 316 is 50-60 °C in marine atmospheric environment, due to risk of external SCC (see 6.6.2 and 8.3).
b
Copper and copper nickel alloys should be used only with potable water in the pH range of 6 to 9. For temperatures higher than
60 °C, the ratio of HCO3/SO4
2−
should be greater than 1 to avoid pitting.
c
The actual maximum operating temperature for any specific non-metallic material should be determined by the end user with input
from the material manufacturer.
7.4.3 Seawater carrying systems
In Table 10, typical materials for seawater-carrying systems are listed, with typically used maximum operating
temperature for piping systems with crevices.
NOTE 1 Systems that are heat-traced or exposed to solar heating can be exposed to temperatures higher than those
expected from process calculations.
NOTE 2 Untreated seawater is normally regarded as less corrosive than chlorinated seawater, but very few application
limits have been established.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
Table 10 — Typical materials for chlorinated seawater-carrying systems with crevices
Equipment Material
Maximum operating
temperature
°C
Other limitations
PEa 60
Piping
Elastomer pipea 70
Piping, vessels GRP (epoxy resin)a 95 Maximum velocity: 5 m/s
Piping, vessels, valves Carbon steel with an internal
non-metallic coating or lining
with or without CP
Temperature is limited by the
selected type of coating or
lining
Piping, vessels Type 6Mo 20
Piping, equipment, valves Alloy 625 30
Piping, equipment, vessels,
valves, pumps
Type 25Cr duplex 20
Alloy C276/C22 50
Alloy 686/59/C2000 60
Maximum residual chlorine
concentration: 0,7 mg/l
Piping, equipment, valves,
heat exchangersb
Titanium grades 1 and 2 85
Pipingc, heat exchangersb CuNi 90/10 100 Maximum velocity:
2,5 m/s-3,5 m/s dependent
on pipe diameter
NiAl bronze 75 Maximum velocity: 15 m/s
Pumps and valves
Type 25Cr duplex 20
a The actual maximum operating temperature and fire resistance properties for any specific non-metallic material should be
determined by the end user with input from the material manufacturer.
b The final choice of heat exchanger material will be influenced by the cooling/heating medium and heat exchanger design.
c Stagnant conditions and coupling to SS, titanium and nickel alloys should be avoided.
Resistors or diodes to control the potential and currents in internal cathodic protection systems have been
applied to increase the temperature limits for alloy 625, type 6Mo and type 25Cr duplex in components of
chlorinated systems. Care should be taken to operate these systems correctly.
Threaded connections are regarded as very sensitive to crevice corrosion and should be avoided in CRA
materials. Surface preparation (pickling and passivation) and start-up procedures can affect the risk of crevice
corrosion if materials are applied in borderline conditions.
For plate and shell/tube heat exchanger applications with seawater on the shell side, severe crevice
conditions exist and SS is generally not used. Titanium alloys are generally used for this service, while the use
of copper or nickel-based alloys should be evaluated on a case-by-case basis.
HDG carbon steel is not commonly used for seawater systems, except for short design life (5 years to
10 years). If galvanized piping is specified for use in normally stagnant systems, e.g. fire-water systems,
suitable measures, such as frequent fresh water flushing of the system, should be implemented to avoid
plugging of sprinkler/deluge nozzles. Galvanizing should be performed on completed welded spools to ensure
that the entire internal surface including the welds is coated.
Graphite containing gaskets should not be used in metallic seawater piping systems.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
7.4.4 Other utility systems
Materials selection for these systems is given in Table 11, with amendments as given below. This listing does
not exclude other materials to be used, but lists the most typically used materials.
For closed-loop heating and cooling systems, fresh water or fresh water with 30 % (mass fraction) triethylene
glycol (TEG) is used as cooling/heating medium. Proprietary hot-oil fluids are also often used as heating
medium and are considered non-corrosive to carbon steel.
Carbon steel has been used with success in TEG systems, but for heat exchangers and other critical
components in these systems, type 316 can be a good alternative to carbon steel. Galvanic corrosion
between carbon steel and type 316 is not expected. For carbon steel, it is essential to specify a suitable
chemical treatment, such as corrosion inhibition, or pH control, or both, to ensure that the system is protected.
Table 11 — Typical materials for utility use
Service Equipment Materials Notes
Open drain Piping Non-marine: carbon steel HDG; PE; GRP
Marine: GRP; carbon steel; type 25Cr duplex
—
Closed drain Piping Carbon steel; type 316; type 22Cr duplex; type 25Cr
duplex; GRP
—
Sewage Piping Type 316; GRP; polyethylene —
Jet fuel Piping Type 316 —
Piping Carbon steel; type 316 or other SS (where cleanliness
is required)
—
Dry fuel gas and diesel
Tanks Carbon steel; GRP a
Tubing Non-marine: type 316
Marine: type 316; UNS S31700; alloy 904; alloy 825;
alloy C276; type 6Mo; type 22/25Cr duplex; titanium
and Cu alloys
bc
Junction boxes/cabinets Non-marine: carbon steel painted or HDG with or
without paint
Marine: GRP; type 316
—
Instrumentation
Cable trays Non-marine: carbon steel HDG; type 316
Marine: type 316; carbon steel HDG in fully HVAC
controlled areas
—
Ventilation/air intake ducts Non-marine: carbon steel HDG; type 316
Marine: type 316; carbon steel HDG may be used in
living quarters and domestic areas
c
Air-handling units Non-marine: carbon steel HDG; type 316
Marine: type 316
—
HVAC ducts and units
Cooling coils Air and fresh water: type 316; copper-based alloys
Seawater: titanium grade 2
b
Dry CO2 systems Carbon steel —
Deluge system Carbon steel HDG; type 25Cr; type 6Mo; CuNi 90-10;
titanium grade 2
bg
AFFF piping Type 316; GRP
c
Fire-fighting systems
Fresh water/plant
air/nitrogen
Non-marine: Carbon steel; type 316
Marine: Type 316
c
Lubrication and seal oil Piping and vessels Type 316; type 22Cr duplex; type 6Mo
c
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
Table 11 (continued)
Service Equipment Materials Notes
Hydraulic oil/fluid Piping and vessels Carbon steel upstream filters; type 316
c
Piping Carbon steel; carbon steel HDG; type 316
c
Instrument air
Air receivers Carbon steel; internally coated carbon steel; type 316 —
Inert gas/plant air piping Piping and vessels Carbon steel; type 316
c
Glycol Piping and vessels Carbon steel; type 316 —
Methanol Piping and vessels Carbon steel; type 316 —
Heating/cooling media Piping and vessels Carbon steel; CRA in heat exchangers d
Miscellaneous chemical
injection systems
Piping and vessels GRP; type 316; type 6Mo; titanium grade 2 ef
a Diesel tanks in carbon steel should have a 3 mm corrosion allowance in the bottom section. In addition, the bottom and roof should
be coated. Cathodic protection should be used only if corrosion products from the sacrificial anodes do not cause damage to the
downstream equipment. No corrosion allowance is required for cathodically protected surfaces. Consider coating the entire diesel tank if
corrosion products can be detrimental when stored product is utilized.
b Copper alloys should not be used in combination with stainless steel or nickel alloy in seawater systems.
c In a marine atmosphere, there may be a high risk for localized corrosion of type 316, in particular crevice corrosion under clamps.
The use of alternative tubing material should be evaluated.
d Fresh-water heating and cooling media are normally treated with a corrosion inhibitor and an oxygen scavenger. In a freezing
environment, it is normally mixed with TEG.
e The combination of chemical and material should be considered in each case. Titanium grade 2, GRP or chlorinated polyvinyl
chloride should be used for hypochlorite systems.
f Typical chemicals include corrosion inhibitor, scale inhibitor, anti-foam, de-emulsifier wax, biocide and oxygen scavenger.
g
Systems made in carbon steel HDG may suffer from nozzle blocking.
7.5 Pipelines and flowlines
In principle, there are no differences between pipelines/flowlines and other systems with respect to corrosion
evaluation and materials selection. However, since the material costs for these items can represent a
significant part of the total investment for a project, they should be evaluated separately. The material selected
for a pipeline/flowline can also influence the installation method, or vice versa.
Typical materials for pipelines/flowlines in different service conditions are listed in Table 12.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
Table 12 — Typical materials for pipelines/flowlines dependent on type of service
Type of service Materials
Carbon steel with or without chemical treatment
Flexible pipe with carcass in type 316 or duplex stainless steel
Carbon steel, internally clad/lined with type 316, alloy 825 or alloy 625
Type 22Cr
Hydrocarbon production
Type 13Cr with low carbon content
Wet hydrocarbon gas (not
dehydrated)
Same materials as for unprocessed hydrocarbon production
Dry gas (dehydrated) Carbon steel
Stabilized or partly stabilized oil or
condensate
Carbon steel with or without corrosion inhibitor
Carbon steel with chemical treatment
Carbon steel with organic coating or lining
De-aerated seawatera and
produced water for injection
Flexible pipes with carcass in type 316 or duplex stainless steel
a Several failures due to bacterial corrosion have been reported in carbon steel subsea injection flowlines transporting de-aerated
seawater. The corrosion that occurs in the 6 o'clock position in the pipe is caused by sulfate-reducing bacteria. The attack is very difficult
to control and even with cleaning pigs and bacterial treatment, corrosion rates in the order of 1 mm/year have been experienced.
Carbon steel with an internal organic coating/lining has been used with success and can be considered for water-injection pipelines.
Alternatively, controlling injected de-aerated seawater chemistry to specified low oxygen levels and including a biocide or nitrate
treatment can permit the use of unlined carbon steel. Nitrate improves the corrosion control and, in addition, reduces the reservoir
souring and, hence, the H2
S production.
8 Corrosion control
8.1 Chemical treatment
Carbon steel, with one or several corrosion control measures as described in this clause, is the material most
commonly used in production and processing facilities. Common methods of chemical treatment are the use
of film-forming inhibitors, oxygen scavengers, biocides, anodic inhibitors and pH stabilizers.
If the imposition of environmental requirements by national regulators or by the end user is likely, then the
types of corrosion inhibitors suitable for use can be limited. Environmental requirements for the use of
corrosion inhibitors should be agreed with the end user.
Application and monitoring of chemical treatment is mainly an issue related to operation of the facility, but
some issues should be addressed during materials selection. The remainder of this clause addresses
chemical treatment only for corrosion control in production and processing systems.
Parameters that can strongly influence the feasibility of chemical inhibition are temperature, flow conditions,
H2S content and compatibility with other chemicals. For produced water systems, contaminants such as
oxygen and MIC should also be considered. These parameters should be defined in the design basis.
There is limited experience relating to the effects of erosion in solids-containing systems where the system is
corrosive and protection to carbon steel is provided by a corrosion inhibitor. The performance of the corrosion
inhibitor can be affected by solids, both by physical removal of the corrosion inhibitor layer and by absorption
of the inhibitor onto the solids, thus reducing the amount of inhibitor available to contact the metal surfaces.
The performance of inhibitors should be confirmed via laboratory testing. Actual field trials should be
performed to test and optimize the dosing.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
In deciding whether carbon steel combined with corrosion inhibitors can be applied for the actual system, the
above parameters should be addressed and operating measures should be defined as a part of the materials
selection process. It should be proven that a corrosion inhibitor can give satisfactory protection for the actual
service conditions, either by relevant field experience or by laboratory testing. The models, data, test methods
and acceptance criteria for application in this process should be agreed with the end user.
Corrosion inhibition to prevent CO2/H2S corrosion is not effective in mitigating top-of-line corrosion.
Alternatively, periodic treatments such as spray pigging or batch treatment of concentrated corrosion inhibitor
between two pigs should be evaluated.
NOTE 1 A common methodology is the use of the “inhibitor availability”. The inhibitor might not be available during start
of the system or due to failures in the injection system. The inhibited corrosion rate is typically 0,1 mm/year (to be agreed
with the end user).
In pipeline systems with only condensed water as the water phase and monoethylene glycol (MEG) as
hydrate inhibitor, the corrosion can be controlled by pH stabilization in non-sour systems.
NOTE 2 pH stabilization means that an alkaline chemical is added to the MEG/water phase in order to increase the pH,
reduce the solubility of iron ions and form protective surface films that reduce the corrosion to an acceptable rate.
Examples of suitable chemicals are NaOH and amines. The MEG concentration is typically above 50 % (mass fraction).
Due to the risk of scaling, the use of this treatment requires confirmation from the end user that no formation water will be
produced.
NOTE 3 A pH-stabilizing chemical can also be used in combination with a film-forming inhibitor. The advantage of this
method is that the pH of the water phase is stabilized to a level where scaling does not take place if formation water starts
to be produced.
Issues such as inhibitor selection, compatibility with other chemicals, required concentrations and compatibility
with non-metallic materials in the system should be addressed in due time to be ready before start of
operation.
8.2 Internal corrosion allowance
An internal corrosion allowance is commonly used for carbon steel piping. The corrosion allowance should be
added in response to expected internal corrosion. Each system should be evaluated and the selected
corrosion allowance supported by corrosion evaluations. Possible corrosion during the construction,
installation, preservation, start-up period and production upsets should be included, in addition to the expected
corrosion during normal operation.
Commonly used corrosion allowances in piping systems are listed below:
a) 1,0 mm to 1,5 mm for non-corrosive service;
b) 3,0 mm for mildly corrosive service;
c) 6,0 mm for severely corrosive service.
For pipeline systems, a maximum internal corrosion allowance of 8 mm to 10 mm should be used as a general
upper limit for use with carbon steel.
For pipelines with dry gas or non-corrosive fluids, corrosion during installation and testing prior to start-up
should be considered.
Corrosion allowance for pipelines can have a great effect on installation cost, or pipeline operational life, or
both, and detailed corrosion evaluations should support the selected allowances.
For corrosion allowances at galvanic connections, see 8.7.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
8.3 Selection of internal and external coatings
External coating system selection for carbon steel should consider the design life, operating conditions and
conditions during construction, transport, storage, commissioning and installation of the facilities.
Guidance on selection of coating system selection for different environments is given in ISO 12944-5 and
surface preparation grades are defined in ISO 12944-4. Performance of the external coating system for
carbon steel for offshore atmospheric and immersed conditions should generally conform to the requirements
of ISO 20340.
For equipment specified in SS for use in marine atmosphere, an agreement with the end user should be
reached when using external coatings to mitigate the external SCC and pitting corrosion. For these materials,
special consideration should be given to coating selection, surface preparation and quality control during
application of the selected coating system. It should be recognized that external coatings can have service
lives that are shorter than the anticipated operational life cycle, and can require maintenance in order to
minimize the threat of SCC of SS equipment or external corrosion of carbon steel.
Selection of internal coating for equipment should be performed on an individual basis due to the very wide
range of possible service conditions. Additionally, some internal coating systems are specified in conjunction
with cathodic protection, and for these systems it is necessary to evaluate the coating selection separately.
Galvanic corrosion between CRA equipment and the vessel wall in coated or lined carbon steel vessels
should be addressed in case of coating damage. As a minimum, internal CRA support brackets should be
painted. Other protection methods, such as cathodic protection, may be considered.
8.4 External splash zone protection
For structures and risers in splash zones, the selected coating should be designed to perform for the entire
design life. Damage to the coating system should be expected. The corrosion allowance for risers should take
into account exposure of bare steel to the environment for a realistic period for repair of coating damage. The
corrosion allowance for carbon steel should be based on the predicted corrosion rate and design life, but
should be a minimum of 6 mm unless otherwise specified.
Riser splash zone protection depends on the design and maintenance philosophy and on operating conditions.
Suitable protection is dependent on the operating temperature. Thermal sprayed aluminium, polypropylene
(PP), GRP and polychloroprene coatings are typical, but consideration should be given to the operating
temperature. Polychloroprene with embedded granules/cuttings of CuNi alloy may be used as an antifouling
layer over polychloroprene.
Splash zone protection for structures is typically provided by organic coatings or thermal sprayed aluminium.
8.5 Cathodic protection
8.5.1 Offshore
Structures and all retrievable components should have self-supporting CP systems designed for the specified
design life. The cathodic protection design should be based on NACE SP0176[27] or DNV-RP-B401[22] for
subsea structures and components, and ISO 15589-2 for offshore pipelines. Subsea installations should be
protected against corrosion using paint or other coating systems combined with cathodic protection, unless
otherwise agreed. Cathodic protection systems, or coating systems, or both, should be used for all metallic
materials that are susceptible to seawater corrosion. An exception is made for components where it is
impractical to obtain a reliable electrical contact with the anode system. Such components shall be made
either of seawater-resistant materials or of carbon steel with a sufficient corrosion allowance for the required
lifetime. Coating of components and structures limits the number of anodes required.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
8.5.2 Onshore
The cathodic protection design for onshore buried pipelines should be as described in ISO 15589-1.
Cathodic protection should be considered for all other underground steel equipment, e.g. buried fire-water ring
mains, but this should depend on the external corrosivity evaluation.
8.6 Corrosion protection of closed compartments
Internal corrosion protection is not necessary for completely closed and sealed dry atmospheric compartments
in carbon steel structures. Dehumidification equipment can be applied in a closed or semi-closed atmospheric
compartment to prevent humidity and corrosion.
For seawater-filled compartments which are completely sealed or have restricted seawater exchange, the
need for CP or chemical treatment should be evaluated on a case-by-case basis. Parameters to be
considered are structural loading, degree of exchange of seawater and ratio between volume and uncoated
area.
Subsea structures and covers are often made of hollow components that will be filled with seawater, but the
in-service utilization is normally low in terms of stress and fatigue. For such components having volume to
uncoated area ratios less than 1 m3/m2, internal corrosion protection or corrosion allowance may not be
necessary.
8.7 Connection of dissimilar materials
8.7.1 Piping systems
Galvanic corrosion can occur when dissimilar metallic materials are connected together in a conductive
corrosive fluid. The potential difference between the two metals can cause a significant increase in corrosion
rate of the less noble material. However, the extent of the galvanic corrosion risk is influenced strongly by
such factors as the area ratio of the two metals, the cathode efficiency of the more noble metal, the
conductivity of the electrolyte, oxygen content and temperature. It is necessary to evaluate all these
parameters in the design of the facilities.
For hydrocarbon production and processing systems, galvanic corrosion is usually a consideration only
between carbon steel and CRA. For those systems that involve anaerobic corrosive fluids in which the
cathodic process is not driven by dissolved oxygen, there is a significant amount of operating experience
worldwide to indicate that galvanic corrosion is generally not a concern, since very few cases have been
reported. This is especially true for systems in which the internal corrosion of carbon steel is mitigated by
corrosion inhibition. Consequently, for hydrocarbon production and processing systems, it is necessary to
evaluate the requirements for designing for galvanic corrosion on a case-by-case basis.
In seawater systems, the galvanic couples that give rise to galvanic corrosion risk are well documented, and it
is necessary to design the facilities to prevent galvanic corrosion. Flange connection is the preferred method
of connecting dissimilar materials when there is a significant risk for internal galvanic corrosion.
Examples of techniques that can be used to mitigate the galvanic corrosion threat to dissimilar metal flanged
interfaces in corrosive service are as described below.
⎯ Install a flanged distance spool between the dissimilar metals, the length of which depends on the
resistance path and pipe diameter. The distance spool material may be either a solid electrically non-
conducting material (e.g. GRP) or a metal that is coated internally with an electrically non-conducting
material, e.g. vulcanized rubber or polymeric coating. The metal of the distance spool piece can be
specified as carbon steel if vulcanized rubber is used.
⎯ Apply a corrosion allowance on the less noble metal or a sacrificial thick-walled carbon steel spool, which
is designed for replacement at scheduled intervals.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
⎯ Install internal sacrificial anodes through access fittings near the interface, e.g. resistor-controlled
cathodic protection for seawater systems.
⎯ Apply electrical isolation of dissimilar metals; however, the risk of electrical continuity via pipe supports,
decks and earthing cables should be evaluated.
⎯ Reduce the cathode area by internally coating the more noble material in the couple.
⎯ At critical interfaces between dissimilar metals in hydrocarbon production and processing systems, weld
overlay of the flange face of the less noble material with a corrosion-resistant material may be considered.
8.7.2 Submerged installations
For submerged installations, the cathodic protection system prevents galvanic corrosion externally when the
different materials are in electrical contact with each other and no special precautions are necessary.
8.7.3 Structural installations
The design requirements should be evaluated on a case-by-case basis for dissimilar metal combinations for
structural applications, e.g. aluminium alloys to steel in marine atmospheric environments. It is also necessary
to evaluate the practicality of any possible mitigation measures to avoid galvanic corrosion for each of these
applications. For fasteners, it is important to ensure that they are the cathode in the dissimilar metal
combination for such applications.
Similarly, if the environment is considered dry and non-corrosive or intermittently wetted, special precautions
may be required and thus the materials selection requirements should be evaluated separately.
8.8 Sealing materials
All possible environmental conditions (including commissioning) should be considered when deciding on the
optimum choice for ring gaskets. The seal ring shall as a minimum be resistant to the actual process
environment.
For non-metallic seals, the possibility of crevice corrosion at the metal to non-metallic seal interface should be
considered.
For raw seawater service, careful consideration should be given to ensure adequate crevice and galvanic
corrosion resistance of materials at the expected operating conditions.
Material for sealing ring in ASME ring-type joints are normally selected to be of lower hardness than the flange
material to assist seating and prevent permanent damage to the flange ring groove.
Sealing rings designed to operate within the elastic area, such as rings for hub connectors and compact
flanges, should be made from a material with appropriate strength, ductility and toughness properties.
Selection of the sealing ring material should also address any environmental limits imposed by other
standards such as ISO 15156, if applicable.
8.9 Fasteners
Material for fasteners should be selected in accordance with the requirements of the applicable design code
for the connection.
The possibility of galvanic corrosion and the consequences of different thermal coefficients, if relevant, should
be considered when dissimilar metals are used in fasteners and materials being connected.
Fasteners screwed into component bodies should be of material that is compatible with the body with respect
to galling and corrosion properties.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
In non-marine atmospheres, fasteners should be of a low alloy steel material coated with electrolytic applied
zinc, HDG or polytetrafluoroethylene (PTFE) with anticorrosion pre-treatment.
In marine atmosphere, fasteners in low alloy steel should be HDG in accordance with ISO 10684 or
ASTM A153[19], or coated with PTFE with anticorrosion pre-treatment such as cermet. Other pre-treatment
coatings should be selected with caution with respect to corrosion. CRA fasteners should be chosen for
connections in CRA materials in frequently wet environments such as extensive condensation or salt spray.
Fasteners in low alloyed steel and SS may suffer from SCC and limitations to strength and hardness
properties should be established and agreed with the end user.
Fasteners should be avoided in splash zone applications. However, when this is unavoidable, fasteners shall
be made of seawater resistant material, e.g. alloy 625/725 or similar.
Fasteners in carbon steel or low alloy steel used with equipment installed subsea may be used in the black
(uncoated) condition or coated for intermediate protection with electrolytic zinc, chemically converted coatings
such as phosphates or PTFE (provided electrical continuity is verified). If cathodic protection cannot be
ensured, fasteners shall be made of seawater-resistant material.
All plating materials shall be selected with due regard to national health, safety and environmental issues
concerning manufacture and use.
Hydrogen embrittlement may occur on fasteners caused by hydrogen introduced from chemical cleaning
related to coating operations, e.g. electrolytic plating and HDG. Baking in accordance with ISO 9588 should
be performed for chemical cleaned fasteners with an actual tensile strength greater than 1 000 MPa or
hardness greater than 31 HRC.
Fasteners submerged in seawater shall be resistant to hydrogen embrittlement. The material strength of
carbon, low alloy and SS should therefore not exceed a SMYS of 725 MPa. Limitations for maximum
hardness and actual yield strength are given in 6.9.2.
8.10 Weld overlay
In corrosive hydrocarbon systems, a CRA weld overlay with a minimum as-finished thickness of 3,0 mm may
replace homogeneous CRA. Weld-overlay materials on carbon steel should be alloy 625 at sealing surfaces.
When alloy 625 and other nickel-based alloys are used as overlay metal, the maximum iron content at the
finished surface should be 10 % (mass fraction).
8.11 Preferential weld corrosion
Care should be taken when choosing welding consumables to make sure that the corrosion resistance of the
entire weld metal, HAZ and base metal are compatible with the environment. In addition, corrosion testing
may be necessary to demonstrate adequate corrosion resistance.
8.12 Corrosion management
Carbon steel in combination with suitable measures to control corrosion is the base case material selection for
most production facilities. Requirements for corrosion monitoring including locations for monitoring devices
and sample points should be included as a part of detailed engineering. If subsea corrosion monitoring is
required to ensure effective inhibitor performance, this should be included as a part of the selection of
materials.
Detailed guidance on corrosion monitoring is given in Annex B.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
Annex A
(informative)
Design basis for hydrocarbon systems
DATA FORM FOR DESIGN BASIS INFORMATION FOR HYDROCARBON PROCESSING FACILITIES
Field name
Contract name
Contract No.
Design life
RESERVOIR DATA
Reservoir pressure Type of fluid
Reservoir temperature Completion fluid
composition
Bubble point pressure Design value for CO2
content (mole fraction, %)
Reservoir fluid density Design value for H2S
content (mole fraction, %)
Sand and silt
production
Mercury
Wax Elemental sulfur
Presence of free water
FORMATION WATER CHEMISTRY
Bicarbonate, HCO3
− or total alkalinity
Total amount of chlorides Organic acids
Na+ K+ Mg2+ Ca2+ Sr2+ Ba2+ Fe2+/3+ Cl− SO4
2−
PRODUCTION WELLHEAD DESIGN CONDITIONS
Shut-in pressure Operation pressure
Min. temperature Operation temperature
Max. temperature
INJECTION WELLHEAD DESIGN CONDITIONS
Type of injection fluid
Max. O2 content Max. design pressure
CO2 content Normal injection pressure
H2S content Min. temperature
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
DATA FORM FOR DESIGN BASIS INFORMATION FOR HYDROCARBON PROCESSING FACILITIES
FLOWLINE DESIGN CONDITIONS
Design temperature H2S content
Inlet temperature Condensed or formation
water
Outlet temperature Flowline inner diameter
Design pressure Flow regime
Inlet pressure Oil production rate
Outlet pressure Gas production rate
CO2 content in gas
phase
Water production rate
General design basis for corrosion evaluations and materials selection
Corrosion-prediction
model (6.2.1)
Methodology or model for
pH calculations (6.2.3.2)
Type 316
Type 22Cr
Type 25Cr
Erosion-prediction
model (6.5)
Maximum operation
temperature for use of
uncoated SS in marine
environments (6.6.2)
Type 6Mo
Mandatory
Recommended
limitations in
mechanical properties
(6.9)
Informative
Temperature limits for
non-metallic materials
(7.4.2)
Environmental
requirements for use
of corrosion inhibitors
(8.1)
Corrosion inhibition test
model and acceptance
criteria (8.1)
Design standard for
CP (8.5.1)
NOTE Users of this International Standard are permitted to copy this form.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
Annex B
(informative)
Corrosion monitoring
B.1 General
Corrosion monitoring is part of a corrosion management system. Details on planning, identification of locations,
data acquisition and reporting should, therefore, be included in the corrosion management system.
In general, the condition in systems needs to be monitored to provide a check on the effectiveness of
corrosion-control methods adopted, and to provide the basis for remedial measures in the event of
deficiencies being identified in these methods.
Monitoring can also give advance warning of potential problems in the event of operational upsets or changes
in the corrosivity of the product fluids.
For hydrocarbon production systems, electrical-resistance probes and corrosion coupons are widely used to
measure the corrosivity of the product, but might not necessarily reflect the actual corrosion rate for the
associated pipe. Therefore, the interpretation of data collected from the probes and coupons should be
performed by personnel experienced with corrosion monitoring. For some systems, monitoring of the actual
pipe-wall thickness is an option. Other methods, such as linear polarization resistance (LPR) probes, galvanic
probes, field signature monitoring (FSM) and acoustic methods, can also be used depending on the
application.
Unless otherwise agreed, both a corrosion probe and a mass-loss coupon should be used for monitoring
corrosion for pipelines and pipework in carbon steel to provide complementary data and an improved level of
confidence. In addition, the monitoring data should be supplemented by operational data, i.e. analyses of
production water and other fluids, to measure corrosion-inhibitor residuals, bacterial activity or to identify
possible changes in the process that can influence the corrosivity of the product.
NOTE Sand-monitoring probes are intended to detect sand in the fluids and are not suitable replacements for
corrosion-monitoring equipment.
Permanently installed monitoring systems for cathodically protected components should be considered when
the components are not accessible for potential measurements. Monitoring may include both reference
electrode(s) for potential measurement and monitored anodes for current determination.
For subsea flowlines and trunklines in carbon steel, where the local corrosivity cannot be evaluated by
monitoring at the inlet or outlet of the flowline, permanent subsea monitoring equipment should be fully
evaluated. Such an evaluation should also consider the possibility and frequency of inspection pigging and the
criticality of the flowline.
B.2 Location of probes
Evaluation of the location and type of corrosion-monitoring equipment should be performed based on the
probability of failure in combination with criticality of the system. Unless otherwise specified, location of the
probes should be at the 6 o'clock position where water is likely to accumulate.
The monitoring probes/coupons should be installed at preselected locations in each pipe to be monitored,
within a reciprocal distance of at least 0,5 m (two fittings). A retriever tool is required to install/retrieve the
probes/coupons from equipment under production. Sufficient clearance for the tool shall be allowed for in the
piping layout and when selecting the sensor location.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
Annex C
(informative)
Chemical composition of some typical oilfield alloys
Table C.1 gives the chemical composition of some typical oilfield alloys.
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
Table
C.1
—
Chemical
composition
of
some
typical
oilfield
alloys
Fe
C
Cr
Ni
Mo
N
W
Nb
Cu
Mn
Other
elements
min.
max.
max.
min.
max.
min.
max.
min.
max.
min.
max.
min.
max.
min.
max.
min.
max.
min.
max.
Group
Common
name
UNS
w
Fe
%
w
Fe
%
w
C
%
w
Cr
%
w
Cr
%
w
Ni
%
w
Ni
%
w
Mo
%
w
Mo
%
w
N
%
w
N
%
w
W
%
w
W
%
w
Nb
%
w
Nb
%
w
Cu
%
w
Cu
%
w
Mo
%
w
Mo
%
w
%
13Cr
S41000
balance
0,150
11,5
13,5
1,00
S41425
balance
0,050
12,0
15,0
4,00
7,00
1,50
2,00
0,06
0,12
0,50
1,00
Si
0,05
max.
F6NM
S41500
balance
0,050
11,5
14,0
3,50
5,50
0,50
1,00
0,50
1,00
Si
0,06
max.
CA6NM
J91540
balance
0,060
11,5
14,0
3,50
4,50
0,40
1,00
1,00
S30815
balance
0,100
20,0
22,0
10,00
12,00
0,14
0,20
0,80
Si
1,40
to
2,00
Ce
0,03
to
0,08
S31000
balance
0,250
24,0
26,0
19,00
22,00
Si
1,50
max.
AISI
316L
S31603
balance
0,030
16,0
18,0
10,00
14,00
2,00
3,00
2,00
Type
6Mo
S31254
balance
0,020
19,0
20,0
17,00
18,00
6,00
6,50
0,18
0,22
0,50
1,00
1,00
Alloy
286
S66286
balance
0,080
13,0
16,0
24,00
27,00
1,00
1,50
2,00
Ti
1,9
to
2,35
V
0,10
to
0,50
Si
1,0
max.
22Cr
duplex
S31803
a
balance
0,030
21,0
23,0
4,00
6,50
2,00
3,00
0,08
0,20
2,00
22Cr
duplex
S32205
balance
0,030
22,0
23,0
4,00
6,50
3,00
3,00
0,14
0,20
2,00
25Cr
duplex
b
S32550
balance
0,040
24,0
27,0
4,00
6,50
2,90
3,90
0,10
0,25
1,50
2,50
1,50
25Cr
duplex
b
S31260
balance
0,030
24,0
26,0
5,00
7,50
2,00
3,00
0,10
0,30
0,10
0,50
0,20
0,80
1,00
25Cr
duplex
b
S32520
balance
0,030
24,0
26,0
5,00
8,00
3,00
5,00
0,20
0,35
0,50
3,00
1,50
25Cr
duplex
b
S32750
balance
0,030
24,0
26,0
6,00
8,00
3,00
5,00
0,24
0,32
1,20
25Cr
duplex
b
S32760
balance
0,030
24,0
26,0
6,00
8,00
3,00
4,00
0,20
0,30
0,50
1,00
0,50
1,00
1,00
Stainless
steel
25Cr
duplex
b
S39274
balance
0,030
24,0
26,0
6,00
8,00
2,00
3,00
0,24
0,32
1,50
2,50
0,20
0,80
1,00
ISO 21457:2010(E)
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
Table
C.1
(continued)
Fe
C
Cr
Ni
Mo
N
W
Nb
Cu
Mn
Other
elements
min.
max.
max.
min.
max.
min.
max.
min.
max.
min.
max.
min.
max.
min.
max.
min.
max.
min.
max.
Group
Common
name
UNS
w
Fe
%
w
Fe
%
w
C
%
w
Cr
%
w
Cr
%
w
Ni
%
w
Ni
%
w
Mo
%
w
Mo
%
w
N
%
w
N
%
w
W
%
w
W
%
w
Nb
%
w
Nb
%
w
Cu
%
w
Cu
%
w
Mo
%
w
Mo
%
w
%
N04400
2,5
0,300
63,00
70,00
28,00
34,00
2,00
Ti
1,0
max.
Alloy
K500
N05500
2,0
0,250
63,00
70,00
balance
1,50
Al
2,30
to
3,15
Ti
0,35
to
0,85
Alloy
20
N08020
balance
0,070
19,0
21,0
32,00
38,00
2,00
3,00
3,00
4,00
2,00
Si
1,00
max.,
Nb+Ta=
8C-1,00
Alloy
800H
N08810
balance
0,100
19,0
23,0
30,00
35,00
0,75
1,50
Al
0,15
to
0,60
Ti
0,15
to
0,60
Alloy
825
N08825
balance
0,050
19,5
23,5
38,00
46,00
2,50
3,50
1,00
Ti
0,6
to
1,2
Alloy
904
N08904
balance
0,020
19,0
23,0
23,00
28,00
4,00
5,00
2,00
Type
6Mo
N08367
balance
0,030
20,0
22,0
23,50
25,50
6,00
7,00
0,18
0,25
Si
0,50
max.
Type
6Mo
N08926
balance
0,020
19,0
21,0
24,00
26,00
6,00
7,00
0,15
0,25
0,50
1,50
2,00
Alloy
925
N09925
22,0
0,030
19,5
23,5
38,00
46,00
2,50
3,50
1,00
Ti
1,90
to
2,40
Si
0,50
max.
Alloy
625
N06625
5,0
0,100
20,0
23,0
balance
8,00
10,00
3,15
4,15
0,50
Ti
0,40
max.
Alloy
625+
N07716
balance
0,030
19,0
22,0
57,00
63,00
7,00
9,50
2,75
4,00
0,20
Ti
1,00
to
1,60
Alloy
718
N07718
balance
0,080
17,0
21,0
50,00
55,00
2,80
3,30
4,75
5,50
0,35
Al
0,2
to
0,80,
Cu
0,30
max.
Ti
0,65
to
1,15
Alloy
725
N07725
0,030
19,0
22,5
55,00
59,00
7,00
9,50
2,75
4,00
0,35
Ti
1,0
to
1,7
Si
0,20
max.
X-750
N07750
5,0
9,0
0,080
14,0
17,0
70,00
0,70
1,20
1,00
Ti
2,25
to
2,75
Si
0,50
max.
Alloy
28
N08028
balance
0,030
26,0
28,0
30,00
34,00
3,00
4,00
0,60
Alloy
2050
N06250
0,020
20,0
23,0
50,00
52,00
10,10
12,00
0,25
1,25
0,25
1,25
1,00
Stainless
steel
Alloy
2550
N06255
0,030
23,0
26,0
47,00
52,00
6,00
9,00
1,00
Cu
1,2
max.
ISO 21457:2010(E)
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
Table
C.1
(continued)
Fe
C
Cr
Ni
Mo
N
W
Nb
Cu
Mn
Other
elements
min.
max.
max.
min.
max.
min.
max.
min.
max.
min.
max.
min.
max.
min.
max.
min.
max.
min.
max.
Group
Common
name
UNS
w
Fe
%
w
Fe
%
w
C
%
w
Cr
%
w
Cr
%
w
Ni
%
w
Ni
%
w
Mo
%
w
Mo
%
w
N
%
w
N
%
w
W
%
w
W
%
w
Nb
%
w
Nb
%
w
Cu
%
w
Cu
%
w
Mo
%
w
Mo
%
w
%
Alloy
276
N10276
4,0
7,0
0,020
14,5
16,5
balance
15,00
17,00
3,00
4,50
1,00
Co
2,5
max.
Alloy
22
N06022
2,0
6,0
0,015
20,0
22,5
balance
12,50
14,50
2,50
3,50
Co
2,5
max.
Alloy
2000
N60200
3,0
0,010
22,0
24,0
balance
15,00
17,00
1,30
1,90
Co
2,0
max.
Mn
0,50
max.
Stainless
steel
Alloy
59
N06059
1,5
0,010
22,0
24,0
balance
15,00
16,50
Si
0,10
max.
Al
0,1
to
0,4
CuNi
70/30
C71500
0,4
1,0
0,050
29,00
33,00
balance
Mn
1,0
max.
Pb
0,02
max.
Zn
0,5
max.
Copper-based
alloys
CuNi
90/10
C70600
1,0
1,8
0,050
9,00
11,00
balance
Mn
1,0
max.
Pb
0,02
max.
Zn
0,5
max.
NOTE
1
This
table
is
intended
for
reference
purposes
and
represents
a
non-inclusive
list;
other
materials
can
be
used.
Trade
names
are
included
for
information
only.
NOTE
2
The
chemical
composition
of
UNS
numbers
is
given.
Phosphorus
and
sulfur
are
impurity
elements
and
are
not
included.
a
UNS
S31803
should
be
used
in
order
to
have
a
minimum
nitrogen
content
of
0,14
%
(mass
fraction).
b
Type
25Cr
duplex
should
be
specified
to
have
a
PREN
W
40.
ISO 21457:2010(E)
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
Bibliography
[1] ISO 898-1, Mechanical properties of fasteners made of carbon steel and alloy steel — Part 1: Bolts,
screws and studs with specified property classes — Coarse thread and fine pitch thread
[2] ISO 9588, Metallic and other inorganic coatings — Post-coating treatments of iron or steel to reduce
the risk of hydrogen embrittlement
[3] ISO 10684, Fasteners — Hot dip galvanized coatings
[4] ISO 12944-2:1998, Paints and varnishes — Corrosion protection of steel structures by protective paint
systems — Part 2: Classification of environments
[5] ISO 12944-3, Paints and varnishes — Corrosion protection of steel structures by protective paint
systems — Part 3: Design considerations
systems — Part 4: Types of surface and surface preparation
systems — Part 5: Protective paint systems
[8] ISO 13623, Petroleum and natural gas industries — Pipeline transportation systems
[9] ISO 13709, Centrifugal pumps for petroleum, petrochemical and natural gas industries
[10] ISO 14692 (all parts), Petroleum and natural gas industries — Glass-reinforced plastics (GRP) piping
[11] ISO 15156-1:2009, Petroleum and natural gas industries — Materials for use in H2S-containing
environments in oil and gas production — Part 1: General principles for selection of cracking-resistant
materials
[12] ISO 15156-3:2009, Petroleum and natural gas industries — Materials for use in H2S-containing
environments in oil and gas production — Part 3: Cracking-resistant CRAs (corrosion-resistant alloys)
and other alloys
[13] ISO 15589 (all parts), Petroleum and natural gas industries — Cathodic protection of pipeline
transportation systems
[14] ISO 15663-2, Petroleum and natural gas industries — Life-cycle costing — Part 2: Guidance on
application of methodology and calculation methods
[15] ISO 18265, Metallic materials — Conversion of hardness values
[16] ISO 20340, Paints and varnishes — Performance requirements for protective paint systems for
offshore and related structures
[17] ISO 23936-1, Petroleum, petrochemical and natural gas industries — Non-metallic materials in contact
with media related to oil and gas production — Part 1: Thermoplastics
[18] API RP 945, Avoiding Environmental Cracking in Amine Units
[19] ASTM A153, Standard Specification for Zinc Coating (Hot-Dip) on Iron and Steel Hardware
[20] ASTM A182, Standard Specification for Forged or Rolled Alloy and Stainless Steel Pipe Flanges,
Forged Fittings, and Valves and Parts for High-Temperature Service
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BS EN ISO 21457:2010
ISO 21457:2010(E)
[21] DNV-RP-F112, Design of duplex stainless steel for subsea equipment exposed to cathodic protection
[22] DNV-RP-B401, Cathodic protection design
[23] EFC Document No. 55, Corrosion in Refinery Industry: Corrosion under Insulation (CUI) Guideline
[24] EEMUA 194, Guidelines for Materials Selection and Corrosion Control for Subsea Oil and Gas
Production Equipment
[25] NACE RP0198, The Control of Corrosion under Thermal Insulation and Fireproofing materials —
A systems approach
[26] NACE RP0403, Avoiding Caustic Stress Corrosion Cracking of Carbon Steel Refinery Equipment and
Piping
[27] NACE SP0176, Corrosion Control of Steel Fixed Offshore Platforms Associated with Petroleum
Production
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

This page deliberately left blank
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

BSI is the independent national body responsible for preparing British Standards
and other standards-related publications, information and services.
It presents the UK view on standards in Europe and at the international level.
It is incorporated by Royal Charter.
British Standards Institution (BSI)
raising standards worldwide™
BSI Group Headquarters
389 Chiswick High Road London W4 4AL UK
Tel +44 (0)20 8996 9001
Fax +44 (0)20 8996 7001
www.bsigroup.com/standards
Revisions
British Standards are updated by amendment or revision. Users of British Stan-
dards should make sure that they possess the latest amendments or editions.
It is the constant aim of BSI to improve the quality of our products and serv-
ices. We would be grateful if anyone finding an inaccuracy or ambiguity while
using this British Standard would inform the Secretary of the technical com-
mittee responsible, the identity of which can be found on the inside front
cover.
Tel: +44 (0)20 8996 9001 Fax: +44 (0)20 8996 7001
BSI offers Members an individual updating service called PLUS which ensures
that subscribers automatically receive the latest editions of standards.
Tel: +44 (0)20 8996 7669 Fax: +44 (0)20 8996 7001
Email: plus@bsigroup.com
Buying standards
You may buy PDF and hard copy versions of standards directly using a
credit card from the BSI Shop on the website www.bsigroup.com/shop.
In addition all orders for BSI, international and foreign standards publications
can be addressed to BSI Customer Services.
Tel: +44 (0)20 8996 9001 Fax: +44 (0)20 8996 7001
Email: orders@bsigroup.com
In response to orders for international standards, it is BSI policy to
supply the BSI implementation of those that have been published
as British Standards, unless otherwise requested.
Information on standards
BSI provides a wide range of information on national, European
and international standards through its Knowledge Centre.
Tel: +44 (0)20 8996 7004 Fax: +44 (0)20 8996 7005
Email: knowledgecentre@bsigroup.com
Various BSI electronic information services are also available which
give details on all its products and services.
Tel: +44 (0)20 8996 7111 Fax: +44 (0)20 8996 7048
Email: info@bsigroup.com
BSI Subscribing Members are kept up to date with standards
developments and receive substantial discounts on the purchase price
of standards. For details of these and other benefits contact Membership Ad-
ministration.
Tel: +44 (0)20 8996 7002 Fax: +44 (0)20 8996 7001
Email: membership@bsigroup.com
Information regarding online access to British Standards via British
Standards Online can be found at www.bsigroup.com/BSOL
Further information about BSI is available on the BSI website at www.bsi-
group.com/standards
Copyright
Copyright subsists in all BSI publications. BSI also holds the copyright,
in the UK, of the publications of the international standardization bodies. Ex-
cept as permitted under the Copyright, Designs and Patents Act 1988 no ex-
tract may be reproduced, stored in a retrieval system or transmitted in any
form or by any means – electronic, photocopying, recording or otherwise –
without prior written permission from BSI. This does not preclude the free
use, in the course of implementing the standard of necessary details such as
symbols, and size, type or grade designations. If these details are to be used
for any other purpose than implementation then the prior written permission
of BSI must be obtained. Details and advice can be obtained from the Copy-
right & Licensing Manager.
Tel: +44 (0)20 8996 7070
Email: copyright@bsigroup.com
Not for Resale, 2019/2/6 03:24:44
--`,,``,,,`,,`,,`,````````-`-``,```,,,`---

Material selection BSI.pdf

More Related Content

What's hot (20)

Similar to Material selection BSI.pdf (20)

Recently uploaded (20)

Material selection BSI.pdf