TALAT Lecture 3100: Machining of Products

TALAT Lecture 3100

Machining of Products

38 pages and 31 figures

Basic Level

prepared by P. Johne, Aluminium-Zentrale e.V., Düsseldorf

Objectives:
− In general, aluminium alloys have excellent machining properties compared
with other common engineering metals. It is the objective of these lectures to
describe the machinability of aluminium alloys, the necessary tools and
equipments in order to obtain optimum results.

Prerequisites:
− General background in production engineering, machine tools

Date of Issue: 1994
 EAA – European Aluminium Association

3100 Machining of Products

Table of Contents

3100 Machining of Products................................................................................2

3101 Machinability of Aluminium Alloys........................................................... 3
3101.01 Definition of Machinability .....................................................................3
3101.02 Forms of Aluminium Chips .....................................................................5
3101.03 Surface of Machined Aluminium Alloys .................................................6
3101.04 Tool Wear while Machining Aluminium.................................................8
3101.05 Cutting Force for Machining Aluminium ..............................................11
3101.06 Classification of Aluminium Alloys in Groups with Similar Machinability
...............................................................................................................................12

3102 Tools for Machining Aluminium ............................................................... 14
3102.01 Survey of Appropriate Cutting Materials...............................................14
3102.02 Machining Aluminium with High-Speed Steel......................................15
3102.03 Machining Aluminium Using Carbide-Tipped Tools............................17
3102.04 Machining Aluminium with Diamond...................................................17
3102.05 General Remarks Regarding Tool Design .............................................19
3102.06 Milling Tools .........................................................................................20
3102.07 Drills ......................................................................................................21
3102.08 Saws .......................................................................................................23
Guide Values for Milling Wrought Aluminium Alloys...................................... 25
Guide Values for Milling Aluminium Casting Alloys ....................................... 26
Guide Values for Sawing Aluminium with Circular Saws................................ 27

3103 Machines for Machining Aluminium....................................................... 28
3103.01 Specifications.........................................................................................28
3103.02 Drives and Rigidity ................................................................................29
3103.03 Spindle Construction..............................................................................30
3103.04 Control and Regulation ..........................................................................31
3103.05 Clamping and Gripping Tools ...............................................................32
3103.06 Equipment for Cooling Lubricants and Cutting Fluids..........................34
3103.07 Chip Removal Equipment......................................................................35
3103.08 Aluminium Specific Machines ..............................................................36

3104 List of Figures................................................................................................. 38

TALAT 3100 2

3101 Machinability of Aluminium Alloys

3101.01 Definition of machinability
3101.02 Forms of aluminium chips
3101.03 Surface of machined aluminium alloys
3101.04 Tool wear while machining aluminium
3101.05 Cutting force for machining aluminium
3101.06 Classification of aluminium alloys in groups with similar
machinability
Compared to other construction materials, aluminium is easy to machine. However,
considering the wide range of alloys available, it is necessary to go into details regarding
the machining characteristics of aluminium alloys. In this chapter such machinability
characteristics will be defined.

3101.01 Definition of Machinability

The term machinability includes all those properties which are relevant for the
machining and cutting process:
• the wear of tools
• the necessary cutting force
• the resulting form of the chips
• the quality of the surface produced (Figure 3101.01.01).

Definition of Machinability
Cutting Process

Machinability

Operational Cutting Surface Chip Form
Life Force
T F FS
s Rt
FV
FR

V t
Source: Fritsch

alu
Definition of Machinability 3101.01.01
Training in Aluminium Application Technologies

Machinability is not a material property which can be defined using a single
characteristic parameter. It is, in fact, a complex technological term. The machinability

TALAT 3100 3

depends both on the physical and chemical properties of the aluminium as well on the
fabrication process used to produce it.

The Machining Process
The kinematical arrangement of tool and workpiece is by far the most decisive criterion
for the machining process. Strictly speaking, the term machinability should be defined
separately for each individual machining process (turning, drilling etc.). Because of the
clearly defined arrangements of tools and workpiece, the term machinability applies
generally to the turning process.
The technology used for the machining process itself depends on a number of
independent parameters (see also Figure 3101.01.02):
Cutting parameters and tool geometry: Even these parameters exert
considerable influence. Currently guidelines exist giving the most efficient
settings of these values for aluminium.
The machines used: This governing parameter has a special importance as far as
aluminium is concerned; both the condition of the machine as well as its design
must fulfil the special conditions required for cutting aluminium.
Material of the cutting tool: This criterion is very important, especially when
machining aluminium.

Process Parameters and Machinability
Cutting Parameters

Governing Parameter Chip Surface Wear Cutting
Form Force
Process

Aluminium Material

Cutting Conditions
and Tool Geometry

Machine

Tool Material

Hardly any or no Influences
Moderate Influence
Large Influence

alu

Process Parameters and Machinability 3101.01.02

TALAT 3100 4

3101.02 Forms of Aluminium Chips

The form of the aluminium chips is an important criterion, especially when one bears in
mind the very large volume of chips created while machining aluminium. The general
aim is to obtain short cylindrically wound chips, spirally wound chips and spiral chips.
A large variety of aluminium chip forms exist so that, depending on the aluminium
alloy, almost all known forms of chips can be produced. Generally the basic guideline
is: the harder and stronger the aluminium alloy, the shorter the chips. This leads to the
following general rules:
• Pure aluminium and soft wrought alloys produce extremely long chips,
making it essential to introduce special corrective measures (chip breakers
on the tools).
• High-strength wrought alloys (e.g. AlMg5, AlMgSi1,0) present no problems
as far as chip form is concerned.
• Hypoeutectic casting alloys (G-AlSi8Cu3, G-AlSi10Mg etc.) lead to the
formation of short coiled and spiral chips which can be removed easily.
• Eutectic casting alloys (G-AlSi12) tend to produce longer chips.
• Hypereutectic casting alloys (piston alloys) inevitably lead to the formation
of short fragmented chips which can in some cases be difficult to remove.
Machining alloys are a special group of alloys containing low-melting soft metals which
help in forming the preferred short chips. Machining alloys, especially the leaded variety
AlCuBiPb, are widely used.
One of the technological parameters affecting the form of chips is the tool geometry.
Thus, a reduced rake angle tends to form shorter chips in alloys which would otherwise
deliver long chips (Figure 3101.02.01).

Chip Compression for Large and Small Rake Angles

γ = 30 °

alu
Chip Compression for Large and Small Rake Angles 3101.02.01

TALAT 3100 5

Chip form diagrams can be compiled, thereby making it possible to consider the
machining criterion „form of chips“ in setting up the cutting routine. These diagrams
show the regions for best chip forms as a function of the variables cutting speed, feed
and depth (Figure 3101.02.02).

Chip Form Diagrams for AlMgSi1
0.8 0.8

s in mm / rpm
0.6 0.6

0.4 0.4

0.2 0.2
v = 900 m / min
s in mm / rpm

v = 300 m / min
0 0
1 2 3 4 5 6 7
0.8 a in mm

0.6

0.4
Criterion Chip Breaking
0.2
v = 600 m / min Criterion Surface
0
1 2 3 4 5 6 7
a in mm

alu
Chip Form Diagrams for AlMgSi1 3101.02.02

3101.03 Surface of Machined Aluminium Alloys

In general, the quality of the surface produced by machining depends on three
independent parameters:

• The kinematical roughness: This is the theoretical depth of roughness
(peak-to-valley height), calculated on the basis of the relative movement of
tool and workpiece.
• The machined surface roughness: This reflects the separating behaviour of
the material, i.e. the typical characteristics of aluminium alloys in regard to
surface quality.
• External influences: Such influencing parameters (stability of system,
condition of cutting edges etc.) become extremely important especially when
machining aluminium at very high speeds.

In general, the machined surface roughness, i.e. the influence of material on the quality
of the cut surface, adheres to the same rules that apply to the form of chips. The
following rule applies for wrought alloys at least: the higher the strength and hardness of
the wrought alloy to be machined, the smoother is the surface produced.

TALAT 3100 6

As far as casting alloys are concerned, the micro-structure exerts a certain influence, i.e
hard particles embedded in a soft matrix can be gouged out, resulting in rougher
machined surfaces. On the whole, the quality of the surface produced by machining
casting alloys can also be classified as being good to very good.

The purity of the material used is of paramount importance for special-purpose
aluminium alloys (e.g. hard disks for storage and drums for copying machines) which
have to be machined to deliver extremely smooth surfaces (Rt< 0.1 µm). To fulfil these
conditions, the wrought aluminium materials used must have an extremely uniform
micro-structure, free from inhomogenities and impurities.

The cutting speed is an important machining parameter which influences the surface
quality. In general, the roughness is inversely proportional to the cutting speed. At low
cutting speeds the roughness of the surface produced increases dramatically, due to the
increased edge build-up. The region of low cutting speeds must, as a rule, be avoided
when aluminium is to be machined. Edge build-up is a phenomenon which is typical for
aluminium and is caused by the periodical sticking and removal of aluminium particles
deposited on the cutting tool (Figure 3101.03.01).

Edge Build-Up at Low Cutting Speed
24

20

16
Rt in µm

12

8

4
0 100 200 300 400 500
v in m/ min

alu
Edge Build-Up at Low Cutting Speed 3101.03.01

The influence of the tool construction on the quality of the surface produced can be
ascertained from the previously mentioned process: It is important that the chips can
glide smoothly over the cutting tool surface. This means that a sufficiently large rake
angle, good lubrication and a smooth cutting tool surface are essential. A clean smooth
surface cannot be obtained using worn cutting tools.
Based on the factors which affect the surface quality, the machining operation can be
divided into four separate regions:

TALAT 3100 7

Region I: Due to edge build-up, the surface quality is unsatisfactory, the
cutting action being replaced by tearing. This region must be avoided.
Region II: Decreasing surface roughness with increasing cutting speed.
Region III: Increasing influence of interferences, e.g. tool chatter and machine
vibrations in a region which is otherwise suitable for machining aluminium.
Thus, to obtain the best results the machines used have to be specially
designed for aluminium.
Region IV: Poor surface quality caused by virtual chips. These virtual chips are
an accumulation of the material being worked and which stick (weld) to the
surface of the tool, thereby scratching the freshly cut surface. Such build-ups
are produced during the machining of casting alloys using worn tools and
high cutting speeds (Figure 3101.03.02).

Surface Quality and Cutting Speed
During Machining of Aluminium

I II III IV
Rt

V

alu Surface Quality and Cutting Speed
Training in Aluminium Application Technologies During Machining of Aluminium 3101.03.02

3101.04 Tool Wear while Machining Aluminium

Scouring (as is typical for steel) is practically not observed while machining aluminium.
The tool wear while machining aluminium occurs due to abrasion of the free surface.
Consequently, the deciding criterion for measuring tool life objectively is the wear
width VB. The wear of the free surface depends on the temperature and is caused mainly
by abrasion. While using carbide-tipped tools one normally assumes an allowable
maximum value of 0.3 to 0.5 mm for VB (Figure 3101.04.01).

TALAT 3100 8

Cutting Edge Displacement and Wear Width

γ
γ
VB
VB

β β

alu
Cutting Edge Displacement and Wear Width 3101.04.01

As far as wear is concerned, the material of the workpiece and the cutting parameters are
equally important.

The material of the workpiece has a very important influence. The following model can
help us understand the basic underlying principles: The process of cutting can be
considered to be a grinding process in which a grinding disk (= the aluminium material
to be cut) causes wear of the workpiece (= tool). In fact the aluminium piece to be
machined consists of an aluminium matrix in which hard particles are embedded. The
desired abrasion of material during grinding is identical to the undesired free surface
attrition (wear) of the tool. Based on this model, the most important correlations of the
wear process can be derived:
• Wear increases with the number of large hard particles which are embedded in
the aluminium workpiece. Such particles could be primary precipitations of
silicon particles in a hypereutectic alloy. This is the reason that aluminium
castings cause high wear of tools. The wear is extremely high in the case of cast
hypereutectic piston alloys. On the other hand, wrought alloys with low silicon
contents cause a minimum of tool wear (Figure 3101.04.02).
• Wear increases with the strength of the material. Hard particles embedded in a
soft matrix can be gouged out easily. However, if the matrix material is harder,
inclusions cannot be removed easily, thus increasing tool wear.
• Finally, wear depends on the wear resistance of the free surface of the tool.

TALAT 3100 9

100 µm 100 µm 100 µm

alu Hypereutectic AlSi Alloys (treated differently)
Training in Aluminium Application Technologies with coarse Si Inclusions 3101.04.02

As far as cutting conditions are concerned, cutting speed has the greatest influence on
tool life. The correlation between cutting speed, v, and tool life, T, is given by Taylor’s
equation: v c = C ⋅ T 1/ k . This equation, which can be depicted as a straight line in a
double logarithmic scale T-v, correlates very well with experimental values. Such
straight life-lines can be derived to show the varying tool wear for different aluminium
alloys.

200 GK - Al Si 8 Cu 3

100
80
60 GK - Al Si 12
40
T (VB = 0.3 mm) in min

20
GK - Al Si 10 Mg wa
10
8
6

4
GK - Al Si 17 Cu 4 Fe Mg
2

200 400 600 800 1000 2000
v in m/min

alu Operational Life for the Machining of
3101.04.03
Training in Aluminium Application Technologies Gravity Die Castings

TALAT 3100 10

The diagram shown in Figure 3101.04.03 is an example for gravity die casting alloys. It
is not possible to plot wrought alloys in this diagram. In the case of wrought alloys, the
tool life is measured in number of shifts or days rather than in minutes. Because of the
much greater experimental effort required, T-v curves have not been constructed for
wrought alloys.
Since tool wear also depends on other cutting conditions, the life-lines are valid only for
a definite set of cutting conditions. Further factors which influence tool wear are:

• Cooling lubricants. Efficient cooling can reduce tool wear.
• Cutting interruptions. These increases tool wear. Pores in the material act as
interruptions during cutting.
• Feed and cutting depth. Tool wear tends to increase with increasing chip
cross-section.

3101.05 Cutting Force for Machining Aluminium

The influence of material is reflected in the so-called specific cutting force ks1.1
introduced in 1957 by O. Kienzle, who used an empirical equation for its calculation.
Because of its ease of use, this equation has come to be widely accepted. The specific
cutting force gives the correlation between cutting force, material and chip dimensions.
The specific cutting forces for the different aluminium alloys can be obtained from
tables. In general, the following rules apply:
• Different alloys have varying specific cutting forces, the variations being,
however, relatively small.
• In general one can assume that the specific cutting force for aluminium is
about 30 % that of steel.
• The specific cutting force can not be derived from either the chemical
composition or the physical properties.
• The specific cutting force has to be determined experimentally for each
individual case.

The cutting force required depends not only on the dimensions of the chips but also on
the cooling lubricants used and the tool construction:
• A cooling lubricant has opposing influences: The cooling action reduces the
temperature at the shear zone thus tending to increase the cutting force
required. At the same time, the lubricating action eases chip motion, thereby
reducing the cutting force required.
• As far as the tool geometry is concerned, the cutting force can be influenced
by the rake angle, γ. A larger rake causes less chip compression resulting in
a lower cutting force (Figure 3101.05.01).
• The wear condition of the cutting edge has a relatively large influence. As a
consequence, the cutting force increases with machining time.

TALAT 3100 11

Cutting Forces for Machining Aluminium

x x x x
x x x x
x x

γ=0° γ = 10 ° γ = 20 °
60 100 140 180 220 60 100 140 180 220 60 100 140 180 220

v in m/min

alu
Cutting Forces for Machining Aluminium 3101.05.01

3101.06 Classification of Aluminium Alloys in Groups with Similar Machinability

From the influence of the different parameters as mentioned above, it is clear that the
correlations are much too complex to be of help in planning the machining operation.
This is especially true for those cases in which the optimum cutting conditions have to
be chosen from data bases for operating fully automatic cutting machines.
In order to make it possible to handle the very large palette of available aluminium
alloys, it is recommended to classify these in groups having similar machining
characteristics. The following classification is adopted:

Group 1: Wrought aluminium alloys of low strength
Group 2.1: Wrought aluminium alloys of high strength
Group 2.2: Free-machining alloys
Group 3.1: AlSi casting alloys with up to 10 % Si
Group 3.2: Eutectic AlSi casting alloys
Group 3.3: Hypereutectic AlSi casting alloys

These alloy groups are described in the following table.

TALAT 3100 12

Classification of Aluminium Alloys Based on Machining Characteristics

Group Alloy type Alloy example Characteristic machining
properties
Group 1: • Non-heat-treatable Pure aluminium, Soft, ductile, homogeneous, low
Wrought low alloys in soft or AlMn, AlMg1, strength, no hard components. Sticking
strength partially hardened AlMgMn during machining
Al alloys state
• Heat-treatable alloys AlMgSi0,5, Tendency for edge build-up, no virtual
in unaged condition AlMgSi1 chips
Group 2.1: • Non-heat-treatable AlMn, AlMg1 to Strength between 300 and 600 N/mm²
Wrought Al alloys in strained AlMg5, AlMgMn, with good elongation values, no hard
alloys of condition AlMg4,5Mn components (low tool wear),
higher • Heat-treatable alloys AlCuMg1, decreasing tendency for edge build-up
strength in aged and/or strain- AlZnMg1, with increasing strength, no virtual
hardened state AlZnMgCu0,5 chips
AlZnMgCu1,5
Group 2.2: • Heat-treatable AlMgSiPb Short chips due to presence of chip
Free- wrought alloys with AlCuBiPb, breakers, strength 280 to 380 N/mm²,
machining chip - breaking AlCuMgPb low tendency for edge build-up, no
alloys components virtual chips
Group 3.1: • AlSiCu alloys AlSi5Cu1, Strength up to 250 N/mm²
AlSi casting AlSi6Cu4,
alloys with AlSi8Cu3,
up to 10 % Si • AlSiMg alloys AlSiCu3AlSi5, Strength up to 360 N/mm², increased
AlSi7Mg, tool wear due to hard alloy
AlSi9Mg, components and inclusions, good chip
AlSi10Mg breaking properties and smooth
surfaces, tendency for edge build-up
for more than than approximately 5 %
silicon. Increasing virtual chips
Group 3.2: • AlSi alloys with about AlSi12 Low hardness of matrix material. Hard
AlSi casting 12 % silicon metallic alloying components and
alloys of eventually inclusions, high tendency
low for edge build-up and for virtual chips
hardness
Group 3.3: • AlSi alloys with over AlSi18CuMgNi, Medium strength, high hardness, very
AlSi-casting 12 % silicon AlSi21CuNiMg, low ductility. High wear caused by
alloys of AlSi25CuMgNi, very hard intermetallic constituents
high AlSi17Cu4FeMg and primary silicon; high tendency for
hardness edge build-up and for virtual chips

TALAT 3100 13

3102 Tools for Machining Aluminium

3102.01 Survey of appropriate cutting materials
3102.02 Machining aluminium with high-speed steel
3102.03 Machining aluminium using carbide-tipped tools
3102.04 Machining aluminium with diamond
3102.05 General remarks regarding tool design
3102.06 Milling tools
3102.07 Drills
3102.08 Saws

Tools suitable for machining aluminium differ from those required for machining steel
in as far as both the geometry and the cutting tool material are concerned. Aluminium
cannot be worked with tools which are used for steel. This chapter will specify the
cutting materials and tool forms most suitable for machining aluminium.

3102.01 Survey of Appropriate Cutting Materials

Aluminium is machined using tools made of tool steel, high-speed steel, cemented
carbides and diamond (Figure 3102.01.01).

Hardness and Toughness of
Cutting Tool Materials
Tool Steel
High-Speed Steel
Carbide Inserts
4000
Bending Fracture Strength in N/mm2

Ceramic Inserts
Diamond
3000

2000

1000

0
5 6 8 103 2 3 5 . 103
Hardness HV

alu
Hardness and Toughness of Cutting Tool Materials 3102.01.01

Ceramic cutting materials are not recommended for machining aluminium since the
matrix of this material has a chemical affinity for the aluminium thus making it difficult
to achieve a satisfactory operating life.
Synthetic cutting materials which can be successfully used for machining steel, are not
suitable for aluminium. Thus, tools made of cubic crystalline boron nitride (CBN) are

TALAT 3100 14

very susceptible to free surface wear and scouring. Such tools fail within a short period
even at medium cutting speeds of lower than 1000 m/min.
Even tools with coated cutting edges have proved unsatisfactory. Such tools consist of a
relatively tough substrate coated with a thin film of hard material, thus combining good
wear properties together with a high toughness. However, since titanium compounds are
mostly used as coating material, the same phenomenon occurs as in the case of ceramic
cutting tools; titanium diffuses out of the hard coating so that this soon loses its
effectiveness.

3102.02 Machining Aluminium with High-Speed Steel

High-speed steels offer the following advantages: high toughness, high bending
strength, ease of working, low price. Toughness is important, especially since the slim
form of the cutting tool typically used for cutting aluminium has a higher tendency to
break than tools with a negative geometry (as are typical for cutting steel). The property
of high-speed steel which makes it comparatively easy to form (compared to other tool
materials) is especially helpful in designing complicated tool forms (twist drills, form
and profile cutters).
For machining aluminium, the following main types of tools are used:

• twist drills S 12-1-1
• taps S 9-1-2
• milling cutters S 12-1-2
• form turning tools S 12-1-4
• profiling tools S 12-1-2

These are mostly made of steel with 12 % tungsten having a relatively high hardness,
low bending strength and good temperature stability.

HSS steels have a lower resistance to free surface abrasion (the characteristic wear
criterion for aluminium) than carbide-tipped or diamond tools. HSS tools are used
almost only for wrought aluminium alloys since it is only here that an acceptable tool
operating life can be attained. Wrought alloys contain only few hard inclusions and thus
cause little tool wear.

As an added precaution, the cutting parameters chosen should be such that the
temperature does not rise too high. This can be achieved mainly by choosing limited
cutting speeds - mainly below 500 m/min (Figure 3102.02.01).

High-speed steel tools can also be used to drill abrasive castings in cases where the
cutting speed is limited due to process technology reasons Figure 3102.02.02).

TALAT 3100 15

Machining Aluminium with High-Speed Steel
1.25
v = 1800 m/min
1.00

2400
0.75
VB in mm

1200 900
0.50
600
VB=0.3 mm
0.25

0 5 10 15 20 25 30 35
T in min

alu

Training in Aluminium Ap plication Technolog ies
Machining Aluminium with High-Speed Steel 3102.02.01

115
Machining 100
VB=0.5 mm

Aluminium Castings 80

with 60
Porenarm
High-Speed Steel 40 Porenreich
(Drilling) 2 GD - Al Si 12
20
T in min

10
8
1 GD - Al Si 8 Cu 3
6
4

3 GD - Al Si 17 Cu 4 Fe Mg
2

γ α σ δ β f
1
7° 8° 120° 35° 75° 0.8 mm
10 20 40 60 80 100 200
v in m/min
alu
Machining Aluminium Castings with
Training in Aluminium Application Technologies High-Speed Steel (Drilling) 3102.02.02

TALAT 3100 16

3102.03 Machining Aluminium Using Carbide-Tipped Tools

The use of carbide tipped tools is gaining in popularity. Casting alloys which have a
relatively high abrasive action are mostly machined using carbide-tipped tools. High
cutting speeds which are characteristic for machining aluminium, cannot be used with
HSS tools.
For economic reasons, carbide-tipped tools are being increasingly used for machining
the less abrasive wrought alloys also. The extremely long tool operating life - of one
week or more - and the high cutting speeds attainable, more than compensate for the
higher price of carbide-tipped tools.
The K01 and K10 type of tools with high WC contents have proven to be very
successful for machining aluminium. The titanium carbide (TiC) types of tools are not
suitable for machining aluminium since the high affinity of TiC for aluminium causes
an intolerable diffusion out of the hard surface. The K type tools have a very fine-
grained structure so that it is possible to obtain smooth cut surfaces and edges with low
roughness. This is indeed one of the top priorities while machining aluminium.
Because of the above mentioned reasons, coated hard metals are not suitable for
machining aluminium.

3102.04 Machining Aluminium with Diamond

The extremely high hardness of diamond makes it a very suitable material for cutting
tools. Such tools are used especially for machining hypereutectic AlSi alloys (piston
alloys) which, due to the coarse silicon inclusions present, are extremely abrasive and
thus very difficult to machine. Compared to carbide-tipped tools, diamond tools have
longer operating lives (Figure 3102.04.01), higher precision and better operating
stability. It is essentially this last property which makes them ideal for use in automatic
machines which are typical for the automotive industry.

Currently polycrystalline diamond (PCD) tools are widely used since these possess
much better isotropic mechanical properties than monocrystalline (natural) diamonds.
PCD tools are less sensitive to impact loading and can be used where interrupted cutting
actions occur (Figure 3102.04.02).

PCD tools have cutting properties which are much superior to those of carbide-tipped
tools. Depending on the cutting conditions, PCD tools are about 40 to 100 times more
efficient than carbide tools. This means that in individual cases the operating life of
PCD tools can be up to 100 times longer than that of carbide tools thus more than
compensating for their higher price.

The wear characteristics indicate that Taylor’s rules are valid for diamond tools also.
Free surface wear without scouring is observed on diamond tools. Close to the end of
the operating life, a rounding of the otherwise sharp tool cutting edge is observed.
Intensive cooling of the cutting edge is an effective method of increasing operating life.

TALAT 3100 17

Machining Al-Castings with Carbide-Tipped
and Diamond Tools
103

0 .2
7
Number of machined motor blocks

Diamond
102

101 0 .3
5

Carbide insert

100
102 103 104
V in m/min
alu Machining Al-Castings with
Carbide-Tipped and Diamond Tools 3102.04.01

Source: De Beers

alu
Cutting Inserts Made of Polycrystalline Diamond 3102.04.02

TALAT 3100 18

3102.05 General Remarks Regarding Tool Design

Tools have to be designed keeping the processes which occur at the cutting edge in
mind. These processes depend on the material, i.e. ductility, plasticity and other material
properties of the aluminium workpiece influence the chip type produced and
consequently the tool design.
• A positive cutting angle should be used for tools for machining aluminium. The
exact values to be used are determined by the tool-workpiece-material
combination.
• The cutting edge should be smooth. Tools with polished cutting and free
surfaces deliver very good results.
• The tool construction should be such as to allow sufficient stability even at the
extremely high speeds used nowadays for machining aluminium. This is
especially important for moving tools.
These general comments pertain only to the turning process which is characterised by a
clearly defined arrangement of tool and workpiece. For the other cutting processes, a
number of other process parameters, which influence the tool design and construction,
have to be considered. A description of a few such processes follows.
For turning operations universally adaptable mountings and holders have been
developed which allow rapid changes. With the help of these it is possible to position
the tool exactly (precision) and to keep the idle time down to a minimum (economy)
(Figure 3102.05.01).

Source: Plansee Tizit

alu
Mounting Systems for Carbide -Tipped Tools 3102.05.01

TALAT 3100 19

3102.06 Milling Tools

Characteristic for milling tools is the fact that the chips produced are not removed but
are instead diverted to closed chip chambers in the tool and are thus transported forcibly
together with the tool itself. Consequently, this fact has to be considered while designing
the tool (see Figure 3102.06.01). Since the chip cross section is relatively large, the
number of cutter inserts used is less than that used for machining steel so that a
sufficiently large chip room is accounted for. Because of the high cutting speeds used,
the cutter inserts experience large centrifugal forces and have consequently to be firmly secured.
Milling tools, at least those having diameters of 100 mm and more, should be statically
and dynamically balanced.


alu
Interchangeable Tools for Milling Aluminium 3102.06.01

Since the surface quality could be affected by the very high revolving speeds used, the
milling tools (Figure 3102.06.02) should have a rigid construction and be distributed
nonuniformly. Due to the nonuniform distribution, the cutters are loaded unevenly, since
at constant feed rates, the cutting depth changes proportionally to the cutter distance. It
is important that those cutter inserts which are set to give the precision cut also come
into action.

TALAT 3100 20


alu
Tool Systems for High Speed Cutting 3102.06.02

In some cases, the milling tools are fitted with arrangements for fine adjustments so that
the individual cutter inserts can be adjusted both radially and axially. Using special
adjustment equipment, it is possible to adjust the cutters with a precision of up to a few
µm. For milling machines fitted with PCD tools, this adjustment of the individual
cutting plates is essential.
Interchangeable tool holders for aluminium (see schematic diagram Figure 3102.06.03)
must have the appropriate geometry for aluminium with large rake angle (here 20°) and
a relatively slim cutting form.

alu Geometry of an Interchangeable Tool Holder
3102.06.03
Training in Aluminium Application Technologies for Aluminium

3102.07 Drills

During drilling, the chips cannot be transported freely but are instead forced out through
the relatively narrow flute by frictional forces causing the chips to glide along the inside

TALAT 3100 21

surface of the hole. When drilling aluminium, the drill used must take the deviation of
diameter caused by the expansion of the material on one hand, and the differing amounts
of expansion of tool and workpiece on the other into consideration.
Twist drills are classified into three groups: N, H and W types (Figure 3102.07.01).
Each drill type has a different set of point and helix angles. The type W with a point
angle of 140° and a helix angle between 30° and 40°is suitable for aluminium.
Standardised drills for aluminium differ from those for steel, the larger helix angle used
(45°, compared to 25° for steel) being one of the major differences.
It is generally recommended to use drills having keen cutting edges and polished
surfaces for aluminium. A high polish in the flutes minimises friction and thus reduces
material buildup. Since the cutting speeds (ca. 100 m/min) used while drilling are small
compared to other operations, the danger of material buildup is especially large.
Aluminium can be drilled using larger feeds than for drilling steel. Consequently, a
much larger amount of chips has to be transported within the same period of time
through the flutes.
High-Speed Drill Forms (Aluminium Type W)

γx

σ Type N

γx
Type H
σ

γx

Type W
σ

alu

High-Speed Drill Forms (Aluminium Type W) 3102.07.01

When drilling soft, tough alloys, long coiled chips which can clog the flutes are created.
Thus it is very important to support the chip transport and removal. This is best achieved
using drills with as large flute areas as possible and having highly polished flute
surfaces. Cooling lubricants for the cutting edges also facilitate chip transport.
In order to improve the efficiency of drilling, numerous types of special drills have been
developed for different applications. The main types of developments are as follows:
• HSS drills with special geometric designs. Here special forms of drills have
been designed to do the individual jobs most efficiently.
• Hard metal carbide tools are most suitable for drilling aluminium alloys
having very abrasive properties. The drilling tools are made either
completely of hard metal or carbide tipped tools are used (Figure
3102.07.02).
• Tools tipped with PCD are used for machining piston alloys.

TALAT 3100 22


alu

Carbide - Tipped Drills for Aluminium Castings 3102.07.02

3102.08 Saws

Either circular or bandsaws are widely used for cutting aluminium although the latter are
obviously winning in popularity, especially for sawing compact cross-sections.
Nowadays, the circular saws used are mostly carbide-tipped (Figure 3102.08.01). Such
saw blades are made of steel and have individually brazed carbide-tipped teeth of type
K10. Chip-breaker and finishing teeth are arranged alternatingly on the circumference.
The chip-breaker teeth are chamfered on both sides. The finishing teeth cut out the
edges and a certain height difference.

S
β β
β β

h
γ
45°

α

χ χ
χ χ

Source: Gustav Wagner

alu Carbide Tipped Saws and Tooth
Geometry for Cutting Aluminium 3102.08.01

TALAT 3100 23

The DIN standards 1837 and 1838 classify three types of bandsaws, N, H and W types.
Type N is preferably used for aluminium. The H type is suitable for sawing very hard
alloys and the type W for very soft ones. According to DIN 1840, saws with type C teeth
(bowed teeth with chip-breaking and finishing teeth) and those with type B teeth (bowed
teeth) are suitable for aluminium.
Bimetallic bandsaws are used to cut aluminium. The cutting geometry is mostly problem
oriented, especially since this technology is still in the experimental stages. It is now
possible to have an acceptable operating life even at very high sawing speeds of up to
2000 m/min. Bandsaws have economical advantages, since the material cut out with a
bandsaw is only 10 % as much as that for circular saws. Consequently, valuable metal
can be saved while cutting compact cross-sections.

TALAT 3100 24

Guide Values for Milling Wrought Aluminium Alloys

Cutting parameter Tool material**) Low strength wrought High strength
alloys wrought alloys
(e.g. non-heat-treatable in (heat-treated,
unstrained condition or highly strained)
heat-treatable in soft
condition)

Rake angle τ in ° HSS 15 to 30 15 to 30
HM 10 to 20 (25) 10 to 20
Diamond 2 2

Clearance angle α HSS 9 to 20 9 to 20
in ° HM 9 to 20 9 to 20
Diamond 6 6

Cutting speed HSS up to 1200 up to 800
v in m/min HM up to 2500 up to 2500
Diamond up to 2500 up to 2500
)
Feed sz* in HSS approx. 0.3 approx. 0.3
mm/tooth max. HM approx. 0.3 approx. 0.3
Diamond approx. 0.3 approx. 0.2

Cutting depth
)
HSS up to 6 (∇) up to 6 (∇)
a* in mm up to 0.5 (∇∇) up to 0.5 (∇∇)
HM up to 8 (∇) up to 8 (∇)
up to 0.5 (∇∇) up to 0.5 (∇∇)
Diamond up to 2.5 (∇) up to 2.5 (∇)
up 0.5 (∇∇) up to 0.5 (∇∇)

cooling HSS (emulsion) emulsion
lubricant HM - (emulsion)
Diamond - (emulsion)

*) For shank-type milling cutters, the feed is also a function of the milling cutter diameter:
up to 6 mm milling cutter diameter: 0.1 mm/t (∇) or 0.08 mm/t (∇∇)
∇ ∇
∇ ∇
∇ ∇

**) HM = carbide-tipped tools
HSS = high-speed tools

TALAT 3100 25

Guide Values for Milling Aluminium Casting Alloys
(for silicon-free casting alloys, the corresponding values for wrought alloys are
approximately valid)

Cutting parameter Tool material**) Casting alloy Casting alloy with
with ≤ 12% Si > 12% Si

Rake angle τ in ° HSS 12 to 20 -
HM 8 to 20 8 to 20
Diamond 2 2

Clearance angle HSS 10 to 20 -
α in ° HM 10 to 20 10 to 20
Diamond 6 6

Cutting speed HSS up to 600 -
v in m/min HM up to 1500 up to 300
Diamond up to 2500 up to 1000
)
Feed sz* in HSS approx. 0.2
mm/tooth max. HM approx. 0.2 approx. 0.2
Diamond approx. 0.2 approx. 0.15

Cutting depth HSS up to 6 (∇) -
a*) in mm up to 0.8 (∇∇) -
HM up to 8 (∇) up to 8 (∇)
up to 0.8 (∇∇) up to 0.8 (∇∇)
Diamond up to 2.5 (∇) up to 2.5 (∇)
up 0.5 (∇∇) up to 0.5 (∇∇)

cooling HSS (emulsion)
lubricant HM (emulsion) emulsion
Diamond (emulsion) emulsion
∇ ∇
∇ ∇
∇ ∇


TALAT 3100 26

Guide Values for Sawing Aluminium with Circular Saws

)
Cutting Tool )
Workpiece material group1 Remarks
parameter material** I II III

Clearance HSS 8 8 8
angle α in ° HM 9-7 9-7 9-7

Rake HSS ) 25 25 15
angle τ in ° HM2 10 8 6

Cutting HSS 800 - 2000 500 - 1000 120 - 200 medium tooth pitch
speed 400 - 600 200 - 300 80 - 150 rough tooth pitch
v in m/min
HM up to 3500 up to 2000

Feed per ) HSS up to 0.04 up to 0.04 up to 0.04 medium tooth pitch
tooth sz* up to 0.06 up to 0.06 up to 0.06 rough tooth pitch
in mm HM up to 0.06 up to 0.06

cooling For lower cut lengths and lower cutting speeds: dry
lubricant For longer cut lengths and higher cutting speeds: emulsion, cutting oil or
synthetic lubricants dissolved in water (spray or mist lubrication)

1) Group I : non-heat-treatable wrought alloys, heat-treatable wrought alloys soft state
Group II : aged wrought alloys, casting alloys with low silicon content
Group III : casting alloys with more than 12 % silicon
2) Circular saws for anodised sections often have smaller rake angles

∇ ∇
∇ ∇
∇ ∇


TALAT 3100 27

3103 Machines for Machining Aluminium

3103.01 Specifications
3103.02 Drives and rigidity
3103.03 Spindle construction
3103.04 Control and regulation
3103.05 Clamping and gripping tools
3103.06 Equipment for cooling lubricants and cutting fluids
3103.07 Chip removal equipment
3103.08 Aluminium specific machines

The very good machinability of aluminium and the very effective cutting materials
available can be used to their full advantage only if machines ideally suited for this
purpose are available. Conventional equipment is unsuitable, especially since machines
which are suitable for working aluminium are fundamentally different from those
necessary for machining steel. This chapter will give a survey of these differences and
explain the design and construction parameters for machines especially suited for
aluminium.

3103.01 Specifications

General requirements for tool machines giving optimum performance for machining of
aluminium and its alloys are described as follows:
• High cutting speeds.
Nowadays, castings can be machined at speeds exceeding 2000 m/min.
Wrought alloys can be machined at much higher cutting speeds (up to 4000
m/min). Carbide-tipped tools have acceptable operating lives even at these
extremely high cutting speeds.
• High power requirements.
The fact that the cutting force required for aluminium is only a third of that
required for steel, does not in any case mean that the power of a machine
designed for machining steel is sufficient for machining aluminium also. On
the contrary, much more power is required to be able to operate the
machines at the much higher cutting speeds.
• High dynamic rigidity.
The effect of centrifugal and unbalanced forces at high rotational speeds
makes it necessary to increase the dynamic rigidity.

TALAT 3100 28

• Fixtures and clamps.
The low modulus of elasticity of aluminium has to be taken into account
while clamping the workpiece. Deformations due to the reaction of
clamping and cutting forces should be avoided. Magnetic fixtures are not to
be used with aluminium. The surface of aluminium parts is relatively
sensitive to scratches caused by clamping fixtures.
• Sufficient chip removal.
Due to the high cutting speeds, the volume of chips produced is much higher
than for steel. The type of chips produced ranges from fragmented to long
and straight. While removing the chips, care must be taken to see that the
chips do not come in contact with the freshly machined surface.
• High feed rates with efficient control.
High feed rates are necessary for the high cutting speeds used. This in turn
means that a precise control is required, for example when radii are being
turned.
• Equipment for cooling lubricants.
Although it is possible, in some cases, to machine aluminium without
cooling lubricants, the machines used should be equipped with the necessary
arrangements.

3103.02 Drives and Rigidity

The machines used must have as high a dynamical rigidity as possible to accommodate
the high rotational speeds and the high acceleration and deceleration of the spindle
drive. This is achieved by the following measures:

• Careful design and construction using appropriate methods (for example,
finite element calculation) and computers.
• Highly ribbed construction and heavy construction of the machine
components.
• Using reinforced concrete with good damping properties for supports and
stands.
• Light construction for moving parts.
• Broad guiding tracks having a high wear resistance and long life expectancy.

The drive is designed taking the cutting speed and machining rate into consideration
(Figure 3103.02.01). With increasing speeds, an ever increasing part of the installed
power is converted into heat which must then be removed using cooling systems. The
reason is that friction in the precision ball bearings and sleeve bearings increases with
increasing rotational speeds. The power required increases over-proportionally.

TALAT 3100 29

Criteria for Designing Drives
Main cutting force: Fs = a • s • ks
Torque: Msp = a • s • ks • d
Cutting power: Psp = a • s • ks • v
Drive power: PM = a • s • ks • v/η

a Cutting depth
d Turn diameter
ks Specific cutting force
s Feed
v Cutting speed
η Efficiency

alu

Criteria for Designing Drives 3103.02.01

3103.03 Spindle Construction

Most of the parts to be machined have diameters of less than 100 mm. Fast rotating
spindles are required to be able to machine these parts at cutting speeds up to 2000
m/min. The same holds true for milling. In order to attain these high cutting speeds, the
spindles must rotate at speeds of around 20,000 rpm and reach peak speeds of 40,000
rpm. Besides being able to turn at high speeds, the spindles must be able to transmit this
power to the workpiece and, as in the case of drilling and thread cutting, be able to
accommodate large axial forces.

Conventionally constructed spindles cannot fulfil these requirements. For this reason, in
the last few years, different new types of spindle systems which fulfil the above
requirements, have been constructed:

• Special spindle types with ball bearings. Speeds of up to 20,000 rpm can be
reached.
• Spindle types in sleeve bearings (for example, ceramic bearings, pressure
reduction through trapped air etc.) up to 40,000 rpm.
• Spindles with active magnetic bearings for speeds up to 50,000 rpm. In this
system, a cylindrical rotor floats in an electromagnetic field created by
electromagnets arranged in symmetrical pairs in a stator
(Figure 3103.03.01).

TALAT 3100 30

Schematic Construction of an Active Magnetic Bearing for a Spindle

1

3 2

4

alu Schematic Construction of an Active Magnetic
Training in Aluminium Application Technologies Bearing for a Spindle 3103.03.01

3103.04 Control and Regulation

The control of the shaft drive at high cutting speeds and feed rates is problematic. The
unavoidable switching time-lag causes a difference between planned and actual
positions, called the lag error. This error results in an inadmissible rounding-off of the
edges which is proportional to the feed rate (Figure 3103.04.01). A similar error occurs
during milling operations. Due to the lag error, the programmed radius cannot be
obtained. The amount by which the radius is shortened depends on the feed rate.

Edge Rounding During High-Speed Cutting

B A

2

1

1 Programmed Tool Path

C 2 Actual Tool Path

alu
Edge Rounding During High-Speed Cutting 3103.04.01

TALAT 3100 31

A further problem which occurs especially at high feed rates is the processing time of
the control system. In the free programmed paths, the feed rate depends on the block
processing time of the control and on the distance of the programmed coordinates. For
the normal block processing times of 10 ms and programmed distances of 0.5 mm, a
maximum feed rate of 3,000 mm/min should not be exceeded so that the control system
can keep in step with the data processing. This would otherwise lead to interruptions in
the feed, which would make themselves felt during machining as vibrations.
The problems described above show that standard control systems can have only a
limited use for controlling machining operations for aluminium efficiently. This has led
to the development of special control concepts for high speed machines for aluminium.
Such controls have passed the testing phase and are now available.

3103.05 Clamping and Gripping Tools

Torque is transmitted by chucks through friction at the grips. The torque changes
proportionally to the main cutting force; for aluminium workpieces, it is about 2/3 less
than that for steel. The frictional force is larger in the case of aluminium than with steel.
As far as the statics are concerned, it should, therefore, be possible to hold aluminium
with much lower clamping forces, thereby reducing the possibility of marring the
sensitive aluminium surface with grip markings.
When machining aluminium workpieces, which rotate at high speeds, the centrifugal
force acts against the gripping force and causes it to be reduced (Figure 3103.05.01).

Reduction of Clamping Force Due to Centrifugal
Forces Acting on Chucks
6000

5000
n in min-1

4000

3000

2000

1000

0 20 40 60 80 100 120 140 160
PSp in kN

alu Reduction of Clamping Force Due to Centrifugal
Training in Aluminium Application Technologies Forces Acting on Chucks 3103.05.01

TALAT 3100 32

This effect has to be taken into account during clamping and can be counteracted by
using a number of different measures:
• Chucks with counterbalances.
• Controlling the gripping force by regulating the pressure in the operating
cylinder.
• Distributing the clamping force over a large number of gripping locations.

Aluminium is nonmagnetic. When it is to be machined on palettes, it is best to be fixed
using vacuum activated grips. As soon as the palette is introduced into the machine, the
vacuum is activated, thereby holding the workpiece flat in place.

Special gripping equipment is required for machining large series of parts on automatic
machines. Such equipment consists basically of gripping equipment which is adapted
for the specific needs of the work material and allows the shortest time for tool changes.
Such fixtures are relatively complicated, especially since problematic boundary
parameters have to be taken into account. Figure 3103.05.02 shows an example of a
clamping fixture for a petrol pump housing.

150 kp 450 kp

64 kp

alu
Clamping Fixtures for Petrol Pump Housing 3103.05.02

A major problem that occurs during the cutting operation is the tendency of the material
to deform elastically under the action of the residual stresses. In the case of aluminium
with its relatively low modulus of elasticity, such deformations are rather large. Thus,
during sawing operations for example, the equilibrium of the residual stresses is
disturbed and the resulting forces set free can cause the saw to jam. To prevent this
happening, the clamping fixture shown in Figure 3103.05.03 causes the cut gap to
widen out.

TALAT 3100 33


alu Elastic Widening of Cutting Gap During Sawing
3103.05.03
Training in Aluminium Application Technologies of Aluminium Ingots

3103.06 Equipment for Cooling Lubricants and Cutting Fluids

Cooling lubricants (cutting fluids) play a double role: The lubricating action reduces
transport friction of the chips and prevents heat generation and wear, whereas the
cooling action helps to transport the generated heat. The composition and viscosity used
depends on the cutting conditions. In general one can say that the lubricating action
should be greater for workpieces which are harder to machine. Aluminium can be
classified here as being easy to machine so that the emulsions used should have a high
cooling action.

The supply system used should be able to deliver the fluid effectively up to the cutter.
Due to the high cutting speeds, special measures are necessary for this purpose.
Delivering the fluid under high pressure gives good results especially since the fluid jet
can destroy the vapour film which tends to prevent heat exchange. Mist or spray
lubrication using exceedingly fine droplets have proven to be very effective. Such spray
equipment works economically and has a good cooling action due to the relatively large
contact area (Figure 3103.06.01).

TALAT 3100 34

Operational life

Cutting oil Emulsion

Cutting speed

alu Influence of Water-Insoluble and Water-Soluble
Training in Aluminium Application Technologies Cooling Lubricants on Operational Life 3103.06.01

3103.07 Chip Removal Equipment

An automatic removal system is indispensable because of the large volume of chips
created. An efficient chip removal system must be considered in the design and
construction of the frame. It is important that the chips are broken and fragmented. An
aggregate consisting of continuous chips cannot be removed easily.

The actual tasks required can vary depending on the chip types and the local conditions.
A number of transport and removal systems are available:
• Slat band chain conveyors are the most widely used types since they have clear
advantages: They can be used effectively for all types of chips. They do not
occupy much space and can be adapted flexibly in the machines. The cutting
fluid sticking on the chips can drop down through the conveyor. The volume of
chips to be transported can be easily controlled by regulating the conveyor
speed.
• Scraper flight conveyors are particularly useful for transporting short chips not
longer than 5 cm. A big disadvantage is the high wear. On the other hand,
scraper flight conveyors are cheap and almost as flexible in use as link band
conveyors.
• Screw (worm) conveyors are used to transport short and medium length chips
over short distances. The energy required for transporting is relatively high.
• Pneumatic transport systems are particularly useful for transporting the very
light aluminium chips over long distances. Thrust rod conveyors arranged as
floor-mounted collective conveyors are used for distances of up to 200 m.

TALAT 3100 35

3103.08 Aluminium Specific Machines

The characteristics described above show that machines which can machine aluminium
efficiently must meet the very high specific standards required. Such machines are,
however, only available as special purpose constructions, since the demand for these is
relatively low. In actual practice one may find machines designed specially for
machining aluminium mostly there where a sufficiently large machining potential exists:
wheel fabrication, milling machines for the aerospace industry, ingot milling machines,
machining castings for the automotive industry.

Special purpose machines designed for aluminium are most consequently used for the
recently developed high speed machining. High speed milling machines which fulfil all
the requirements for machining aluminium are available nowadays. Till now, such
machines are used mainly in the aerospace industry for milling integrated components
made of high-strength wrought alloys. In such components, about 90 % of the material
has to be milled to produce a thin-walled stable component.

With these machines it was possible to reduce the machining time by 50 % or more.
Besides the economical advantages, it was possible to improve the quality of the
components produced, since both temperature of the components as well as its surface
roughness at these extremely high cutting speeds could be drastically reduced
(Figure 3103.08.01).

alu
Machines for the High-Speed Machining of Aluminium 3103.08.01

TALAT 3100 36

Another successful application is the use of circular saws in the fabrication of
aluminium semifabricates. Efficient sawing equipment is used for cutting rolling and
extrusion billets. With the large tool diameters, it is possible to attain high cutting
speeds without any additional measures regarding spindles and controls. Extrusion billet
saws require a power of about 100 kW, rolling billets about 200 kW.

Sawing equipment used in plants for semifabricates, clearly illustrate the necessity of
having efficient peripheral equipment to cope with efficiently designed machines for
machining aluminium. The machines can be used to their full capacity only if a very
quick transport of the blanks and workpieces is guaranteed. For moving heavy parts (e.g.
extrusion billets) to and from the machines a much greater effort is required than for the
sawing itself. The sawing of even large billets having diameters of about 200 mm
requires only a few seconds. All other handling operations on the workpieces should be
ideally completed within this time (Figure 3103.08.02).


alu Integrated Billet Sawing Equipment
Training in Aluminium Application Technologies in an Aluminium Smelter 3103.08.02

TALAT 3100 37

3104 List of Figures

Figure No. Figure Title (Overhead)
3101.01.01 Definition of Machinability
3101.01.02 Process Parameters and Machinability
3101.02.01 Chip Compression for Large and Small Rake Angles
3101.02.02 Chip Form Diagrams for AlMgSi1
3101.03.01 Edge Build-Up at Low Cutting Speed
3101.03.02 Surface Quality and Cutting Speed during Machining of Aluminium
3101.04.01 Cutting Edge Displacement and Wear Width
3101.04.02 Hypereutectic AlSi Alloys (Treated Differently) with Coarse Si Inclusions
3101.04.03 Operational Life for the Machining of Gravity Die Castings
3101.05.01 Cutting Forces for Machining Aluminium

3102.01.01 Hardness and Toughness of Cutting Tool Materials
3102.02.01 Machining Aluminium with High-Speed Steel
3102.02.02 Machining Aluminium Castings with High-Speed Steel (Drilling)
3102.04.01 Machining Aluminium Castings with Carbide-Tipped and Diamond Tools
3102.04.02 Cutting Inserts Made of Polycrystalline Diamond
3102.05.01 Mounting Systems for Carbide-Tipped Tools
3102.06.01 Interchangeable Tools for Milling Aluminium
3102.06.02 Tool Systems for High Speed Cutting
3102.06.03 Geometry of an Interchangeable Tool Holder for Aluminium
3102.07.01 High-Speed Drill Forms. (Aluminium Type W)
3102.07.02 Carbide-Tipped Drills for Aluminium Castings
3102.08.01 Carbide-Tipped Saws and Tooth Geometry for Cutting Aluminium

3103.02.01 Criteria for Designing Drives
3103.03.01 Schematic Construction of an Active Magnetic Bearing for a Spindle
3103.04.01 Edge Rounding during High-Speed Cutting
3103.05.01 Reduction of Clamping Force due to Centrifugal Forces Acting on Chucks
3103.05.02 Clamping Fixtures for Petrol Pump Housing
3103.05.03 Elastic Widening of Cutting Gap during Sawing of Aluminium Ingots
3103.06.01 Influence of Water-Insoluble and Water-Soluble Cooling Lubricants on
Operational Life
3103.08.01 Machines for the High-Speed Machining of Aluminium
3103.08.02 Integrated Billet Sawing Equipment in an Aluminium Smelter

TALAT 3100 38

TALAT Lecture 3100: Machining of Products

More Related Content

What's hot (16)

Viewers also liked (20)

Similar to TALAT Lecture 3100: Machining of Products (20)

More from CORE-Materials (20)

Recently uploaded (20)

TALAT Lecture 3100: Machining of Products