Parametric Optimization on MIG Welded EN8 Material Joints by using Taguchi Method
2 likes689 views
The document discusses the optimization of MIG welding parameters for EN-8 material using the Taguchi method to enhance tensile strength and hardness. It outlines various studies related to gas metal arc welding (GMAW), experimental designs, and the significant role of welding current on the quality of welded joints. Results indicate optimal parameters for achieving the best tensile strength and hardness based on the analysis of variance (ANOVA) and signal-to-noise (S/N) ratio methodologies.
![IJSRD - International Journal for Scientific Research & Development| Vol. 1, Issue 9, 2013 | ISSN (online): 2321-0613
All rights reserved by www.ijsrd.com 1847
Abstract—Welding is a manufacturing process, which is
carried out for joining of metals. By MIG Welding it is
possible to weld in all positions. Optimization of the
parameter will be carried out by Taguchi method. We will
use EN-8 material which is more use in Automobile parts.
EN8 plate with dimensions 250mm x 125mm x 6mm with
V- Groove 650.Where the input parameters are welding
current, Wire feed and gas flow rate and output parameters
are tensile strength and Hardness.
Key words: MIG Welding, Orthogonal array Method,
ANOVA, S/N Ration.
I. INTRODUCTION
Welding is recognized all over the world today, as a
remarkably versatile means of metal fabrication. Welding is
the process of metallurgical joining of metals by the
application of heat or pressure or both. Welding, in
combination with allied processes like thermal cutting,
brazing and metal spraying has provided ample freedom to
the modern designer to develop metallic products in which
optimum mechanical properties, lightness and aesthetics are
harmoniously blended. A large number of welding and
allied processes have come into industrial use in last 30
years. Variations and extensions of these processes are being
developed and put to practical use from time to time. Thus
the metal joining technology is in a constant state of flux.
The unbalance radial electromagnetic force was firstly
obtained by measuring the real time input electrical
impedance of GMAW. This force serves as an attaching
force because it pushes the droplet aside of the welding wire
and sticks on the tip of welding wire as a result of surface
tension force. In spray transfer mode, lower unbalance radial
electromagnetic force was observed when argon shielding
gas was used [1]. The wide range and variety of these
processes enables to the modern engineer to join almost all
commercial metals and alloys in many different shapes and
sizes and in thicknesses ranging from a fraction of
millimetre to over 500 mm.
II. LITERATURE REVIEW
A. The effect of Gas Metal Arc Welding (GMAW) processes
on different welding parameters [2]
Izzatul Aini Ibrahim et al (2012): Gas Metal Arc Welding
(GMAW) process is leading in the development in arc
welding process which is higher productivity and good in
quality. In this study, the effects of different parameters on
welding penetration, microstructural and hardness
measurement in mild steel that having the 6mm thickness of
the base metal by using the robotic gas metal arc welding
are investigated. The variables that choose in this study are
arc voltage, welding current and welding speed. The arc
voltage and welding current were chosen as 22, 26 and 30 V
and 90, 150 and 210 A respectively. The welding speed was
chosen as 20, 40 and 60 cm/min. The penetration,
microstructure and hardness were measured for each
specimen after the welding process and the effect it was
studied.
As a result, it obvious that increasing the parameter value of
welding current increased the value of depth of penetration.
Other than that, arc voltage and welding speed is another
factor that influenced the value of depth of penetration. The
microstructure had shown the different grain boundaries of
each parameter that affected of the welding parameters. The
grain boundaries of microstructure changes from bigger size
to smallest size when the variable welding parameters
changed.
B. A study on V-groove GMAW for various welding
positions [3].
D.W. Cho et al (2012-13): This study performed three-
dimensional transient numerical simulations using the
volume of fluid method in a gas metal arc V-groove welding
process with and without root gap for flat, overhead, and
vertical welding positions. The elliptically symmetric arc
models for arc heat flux, electromagnetic force and arc
pressure were used to describe the more accurate molten
pool behaviours. The numerical models not only formed a
stable weld bead but also simulated the dynamic molten
pool behaviours such as overflow which was not described
before. This study analysed these molten pool flow patterns
for various welding positions and validated the numerical
models used by comparing the simulation results with
experimental ones.
1) Without the root gap, it is difficult to form a fully
penetrated weld bead in the flat and overhead positions,
while humping and melt-through beads are formed in
the vertical-upward position under the same welding
condition.
2) With a 1-mm root gap, the molten pool overflow
patterns can be described for various welding positions
under the given welding conditions. The overflow
patterns in some welding positions do not induce the
weld defects, while a weld bead with incomplete
penetration can be formed in the vertical downward
position. Thus, it is necessary to avoid the overflow
patterns in such a case by increasing the welding speed.
C. Parametric optimization of weld strength of Metal Inert
Gas Welding [4]
Chandresh N. Patel et al (2013): He has studied Design of
Experiment method (Full factorial method) for this work
and by the use of the experimental data has optimized by
Parametric Optimization on MIG Welded EN8 Material Joints by using
Taguchi Method
Meet Shah1
Div Ray 2
Jigar Thakkar3
Dhaval Patel4
R. B. Prajapati5
1, 2, 3, 4
U.G. Student 5
Asst. Professor
1, 2, 3, 4, 5
Department of Mechanical Engineering
1, 2, 3, 4, 5
SSESGI, Rajpur](https://image.slidesharecdn.com/ijsrdv1i9040-140812032035-phpapp02/85/Parametric-Optimization-on-MIG-Welded-EN8-Material-Joints-by-using-Taguchi-Method-1-320.jpg)
![Parametric Optimization on MIG Welded EN8 Material Joints by using Taguchi Method
(IJSRD/Vol. 1/Issue 9/2013/0040)
All rights reserved by www.ijsrd.com 1848
gray relational analysis (GRA) optimization technique. In
which input parameters for MIG welding are welding
current, wire diameter and wire feed rate and the output
parameter is hardness.
We were used AISI 1020 or C20 material for
welding. It is a plain carbon steel and also known as “soft”
or mild steel. Small scale trial welding experiments, in the
light of field joint of the plate have been planned to perform
on 5 mm plate thicknesses of low alloy steel AISI 1020 or
C20 and double V-groove joint is used. For Experimental
design we were used full factorial method (L=mⁿ) to find
out number of readings. To find out the percentage
contribution of each input parameter for obtaining optimal
conditions, we were used analysis of variance (ANOVA)
method. We take a gray relational analysis (GRA)
optimization technique for optimization of different values.
A gray relational grade obtained from the gray relational
analysis is used to optimize the process parameters. By
analysing the gray relational grade we find the optimum
parameters.
Based on the result obtained, it can be concluded as
follows:
By use of ANOVA analysis the percentage contribution
of MIG welding for welding current is 94.01 %, wire
diameter of 0.402 % and wire feed rate of 0.016 % and
the error is about 5.56 %. This error is due to human
ineffectiveness and machine vibration. From the
ANOVA it is concluded that the welding current is the
most significant parameter for MIG welding. Increase
in welding current, the value of hardness is increased in
MIG welding.
By use of the GRA optimization technique the optimal
parameter combination is meeting at its parameter value
100 Amp welding current, 1.2 mm wire diameter and 3
m/min wire feed rate for MIG welding.
III. DESIGN OF EXPERIMENT (DOE)
Taguchi Method is used to arrange the experiments. The
Taguchi technique has become a powerful tool for
improving productivity during research and development
work, so that higher quality products can be produced
rapidly and at minimum cost. Dr. Taguchi of Nippon
Telephones and Telegraph Company, Japan has introduced a
method based on "ORTHOGONAL ARRAY" methods
which give much reduced "variance" for the experiment
with "optimum settings" of control parameters. So the
marriage of Design of Experiments with optimization of
control parameters to get best results is achieved in the
Taguchi Method “Orthogonal Arrays" provide group of well
balanced (least) experiments and Dr. Taguchi's Signal-to-
Noise ratios (S/N), they are log functions of desired output,
serve as objective functions for optimization, help in data
analysis and prediction of optimum results [5].
1) Signal-to-noise ratio
1) Larger the better:
(
∑
)
2) Smaller the better:
(
∑
)
3) Nominal the better:
( )
Where, ƞ - Signal to Noise(S/N) Ratio,
Yi - it’s observed value of the response,
n - no. of observations in a trial,
y - Average of observed values (responses) [7].
Work Material: The work material used in the present work
is En - 8, the dimensions of the work piece length 250mm,
width 125mm, thickness is 6mm. Shielding Gas: 20 %CO2,
80 % Argon.
Chemical Composition Of EN-8 Material
Carbon 0.36-0.44 %
Silicon 0.10-0.40%
Manganese 0.60-1.00%
Sulphur 0.050 max.
Phosphorus 0.050 max.
Table. 1: EN8 Material Composition
080M40 (EN-8) – mechanical properties
Yield Stress 465 N/mm2
0.2% Proof Stress 450 N/mm2
Elongation 16% Min
Hardness 201-255 Brinell
Table. 2: Properties of Material
Chemical composition of wire electrode
Carbon 0.06-0.15%
Silicon 0.80-1.15%
Manganese 0.08-0.15%
Phosphorus ≤ 0.025%
Silicon ≤ 0.035%
Copper ≤ 0.50%
Table. 3: Chemical Composition of wire electrode ER70S-6
B. ANALYSIS OF S/N RATIO
In the Taguchi Method the term ‘signal’ represents the
desirable value (mean) for the output characteristic and the
term ‘noise’ represents the undesirable value (standard
Deviation) for the output properties. Therefore, the S/N ratio
to the desirable value of the S. D. S/N ratio used to calculate
the quality characteristic variable from the desired value.
The S/N ratio S is defined as
S = - 10 log (Mean of sum square of reciprocal of measured
Data)
To get the optimal welding performance, higher the better
quality characteristic for penetration must be taken.
Regardless of the category of the quality, a greater S/N ratio
corresponds to better quality characteristics. Therefore, the
optimal level of the process parameters is the level with the
greatest S/N ratio.
C. ANALYSIS OF VARIANCE
The purpose of the analysis of variance (ANOVA) is to
investigate which design parameters significantly affect the
quality characteristic. This is to be accomplished by](https://image.slidesharecdn.com/ijsrdv1i9040-140812032035-phpapp02/85/Parametric-Optimization-on-MIG-Welded-EN8-Material-Joints-by-using-Taguchi-Method-2-320.jpg)
![Parametric Optimization on MIG Welded EN8 Material Joints by using Taguchi Method
(IJSRD/Vol. 1/Issue 9/2013/0040)
All rights reserved by www.ijsrd.com 1850
Fig. 3: Main effect plot for Mean of Hardness
Fig. 4: Main effect plot for S/N Ration of Hradness
V. CONCLUSION
1) By use of ANOVA it can conclude that Current is the
most significant parameter.
2) The gas flow rate is found to have an effect on hardness.
Increase in welding current as increase the hardness.
3) In this experiment the value of the S/N ratio of tensile
strength 55.87 which indicate optimal input parameter
current 125 A, wire feed 2.5 m/min and gas flow rate is
16 l/min.
4) In this experiment the value of the S/N ratio of tensile
strength 38.33 which indicate optimal input parameter
current 125 A, wire feed 2.5 m/min and gas flow rate is
16 l/min.
REFERENCES
[1] Wong, Y.-R., Ling, S.-F., An investigation of
dynamical metal transfer in GMAW - effects of argon
shielding gas, Journal of Materials Processing
Technology (2013), 2013.08.003
[2] Izzatul Aini Ibrahim, The Effect of Gas Metal Arc
Welding (GMAW) processes on different welding
parameters, International Symposium on Robotics
and Intelligent Sensors 2012 (IRIS 2012),
2012.07.342
[3] D.W. Cho, A study on V-groove GMAW for various
welding positions, Journal of Materials Processing
Technology 213 (2013)
[4] Chandresh N. Patel, Parametric Optimization of Weld
Strength of Metal Inert Gas Welding and Tungsten
Inert Gas Welding By Using Analysis of Variance
and Grey Relational Analysis, Modern Engineering
and Emerging Technology, Vol. 1, Issue: 3, April-
2013.
[5] Upinder kumar, Optimization of Cutting Parameters
in High Speed Turning by Grey Relational Analysis,
International Journal of Engineering Research and
Applications (IJERA) ISSN: 2248-9622, Vol. 3, Issue
1, January -February 2013, pp.832-839
[6] P. T. Houldcroft, Reference Book - Arc Welding &
Welding Process Technology.
[7] S. V. Sapakal, Parametric Optimization of MIG
Welding Using Taguchi Design Method, International
Journal of Advanced Engineering Research and
Studies, Vol. 1, July-Sept.2012.](https://image.slidesharecdn.com/ijsrdv1i9040-140812032035-phpapp02/85/Parametric-Optimization-on-MIG-Welded-EN8-Material-Joints-by-using-Taguchi-Method-4-320.jpg)
Parametric Optimization on MIG Welded EN8 Material Joints by using Taguchi Method
- 1. IJSRD - International Journal for Scientific Research & Development| Vol. 1, Issue 9, 2013 | ISSN (online): 2321-0613 All rights reserved by www.ijsrd.com 1847 Abstract—Welding is a manufacturing process, which is carried out for joining of metals. By MIG Welding it is possible to weld in all positions. Optimization of the parameter will be carried out by Taguchi method. We will use EN-8 material which is more use in Automobile parts. EN8 plate with dimensions 250mm x 125mm x 6mm with V- Groove 650.Where the input parameters are welding current, Wire feed and gas flow rate and output parameters are tensile strength and Hardness. Key words: MIG Welding, Orthogonal array Method, ANOVA, S/N Ration. I. INTRODUCTION Welding is recognized all over the world today, as a remarkably versatile means of metal fabrication. Welding is the process of metallurgical joining of metals by the application of heat or pressure or both. Welding, in combination with allied processes like thermal cutting, brazing and metal spraying has provided ample freedom to the modern designer to develop metallic products in which optimum mechanical properties, lightness and aesthetics are harmoniously blended. A large number of welding and allied processes have come into industrial use in last 30 years. Variations and extensions of these processes are being developed and put to practical use from time to time. Thus the metal joining technology is in a constant state of flux. The unbalance radial electromagnetic force was firstly obtained by measuring the real time input electrical impedance of GMAW. This force serves as an attaching force because it pushes the droplet aside of the welding wire and sticks on the tip of welding wire as a result of surface tension force. In spray transfer mode, lower unbalance radial electromagnetic force was observed when argon shielding gas was used [1]. The wide range and variety of these processes enables to the modern engineer to join almost all commercial metals and alloys in many different shapes and sizes and in thicknesses ranging from a fraction of millimetre to over 500 mm. II. LITERATURE REVIEW A. The effect of Gas Metal Arc Welding (GMAW) processes on different welding parameters [2] Izzatul Aini Ibrahim et al (2012): Gas Metal Arc Welding (GMAW) process is leading in the development in arc welding process which is higher productivity and good in quality. In this study, the effects of different parameters on welding penetration, microstructural and hardness measurement in mild steel that having the 6mm thickness of the base metal by using the robotic gas metal arc welding are investigated. The variables that choose in this study are arc voltage, welding current and welding speed. The arc voltage and welding current were chosen as 22, 26 and 30 V and 90, 150 and 210 A respectively. The welding speed was chosen as 20, 40 and 60 cm/min. The penetration, microstructure and hardness were measured for each specimen after the welding process and the effect it was studied. As a result, it obvious that increasing the parameter value of welding current increased the value of depth of penetration. Other than that, arc voltage and welding speed is another factor that influenced the value of depth of penetration. The microstructure had shown the different grain boundaries of each parameter that affected of the welding parameters. The grain boundaries of microstructure changes from bigger size to smallest size when the variable welding parameters changed. B. A study on V-groove GMAW for various welding positions [3]. D.W. Cho et al (2012-13): This study performed three- dimensional transient numerical simulations using the volume of fluid method in a gas metal arc V-groove welding process with and without root gap for flat, overhead, and vertical welding positions. The elliptically symmetric arc models for arc heat flux, electromagnetic force and arc pressure were used to describe the more accurate molten pool behaviours. The numerical models not only formed a stable weld bead but also simulated the dynamic molten pool behaviours such as overflow which was not described before. This study analysed these molten pool flow patterns for various welding positions and validated the numerical models used by comparing the simulation results with experimental ones. 1) Without the root gap, it is difficult to form a fully penetrated weld bead in the flat and overhead positions, while humping and melt-through beads are formed in the vertical-upward position under the same welding condition. 2) With a 1-mm root gap, the molten pool overflow patterns can be described for various welding positions under the given welding conditions. The overflow patterns in some welding positions do not induce the weld defects, while a weld bead with incomplete penetration can be formed in the vertical downward position. Thus, it is necessary to avoid the overflow patterns in such a case by increasing the welding speed. C. Parametric optimization of weld strength of Metal Inert Gas Welding [4] Chandresh N. Patel et al (2013): He has studied Design of Experiment method (Full factorial method) for this work and by the use of the experimental data has optimized by Parametric Optimization on MIG Welded EN8 Material Joints by using Taguchi Method Meet Shah1 Div Ray 2 Jigar Thakkar3 Dhaval Patel4 R. B. Prajapati5 1, 2, 3, 4 U.G. Student 5 Asst. Professor 1, 2, 3, 4, 5 Department of Mechanical Engineering 1, 2, 3, 4, 5 SSESGI, Rajpur
- 2. Parametric Optimization on MIG Welded EN8 Material Joints by using Taguchi Method (IJSRD/Vol. 1/Issue 9/2013/0040) All rights reserved by www.ijsrd.com 1848 gray relational analysis (GRA) optimization technique. In which input parameters for MIG welding are welding current, wire diameter and wire feed rate and the output parameter is hardness. We were used AISI 1020 or C20 material for welding. It is a plain carbon steel and also known as “soft” or mild steel. Small scale trial welding experiments, in the light of field joint of the plate have been planned to perform on 5 mm plate thicknesses of low alloy steel AISI 1020 or C20 and double V-groove joint is used. For Experimental design we were used full factorial method (L=mⁿ) to find out number of readings. To find out the percentage contribution of each input parameter for obtaining optimal conditions, we were used analysis of variance (ANOVA) method. We take a gray relational analysis (GRA) optimization technique for optimization of different values. A gray relational grade obtained from the gray relational analysis is used to optimize the process parameters. By analysing the gray relational grade we find the optimum parameters. Based on the result obtained, it can be concluded as follows: By use of ANOVA analysis the percentage contribution of MIG welding for welding current is 94.01 %, wire diameter of 0.402 % and wire feed rate of 0.016 % and the error is about 5.56 %. This error is due to human ineffectiveness and machine vibration. From the ANOVA it is concluded that the welding current is the most significant parameter for MIG welding. Increase in welding current, the value of hardness is increased in MIG welding. By use of the GRA optimization technique the optimal parameter combination is meeting at its parameter value 100 Amp welding current, 1.2 mm wire diameter and 3 m/min wire feed rate for MIG welding. III. DESIGN OF EXPERIMENT (DOE) Taguchi Method is used to arrange the experiments. The Taguchi technique has become a powerful tool for improving productivity during research and development work, so that higher quality products can be produced rapidly and at minimum cost. Dr. Taguchi of Nippon Telephones and Telegraph Company, Japan has introduced a method based on "ORTHOGONAL ARRAY" methods which give much reduced "variance" for the experiment with "optimum settings" of control parameters. So the marriage of Design of Experiments with optimization of control parameters to get best results is achieved in the Taguchi Method “Orthogonal Arrays" provide group of well balanced (least) experiments and Dr. Taguchi's Signal-to- Noise ratios (S/N), they are log functions of desired output, serve as objective functions for optimization, help in data analysis and prediction of optimum results [5]. 1) Signal-to-noise ratio 1) Larger the better: ( ∑ ) 2) Smaller the better: ( ∑ ) 3) Nominal the better: ( ) Where, ƞ - Signal to Noise(S/N) Ratio, Yi - it’s observed value of the response, n - no. of observations in a trial, y - Average of observed values (responses) [7]. Work Material: The work material used in the present work is En - 8, the dimensions of the work piece length 250mm, width 125mm, thickness is 6mm. Shielding Gas: 20 %CO2, 80 % Argon. Chemical Composition Of EN-8 Material Carbon 0.36-0.44 % Silicon 0.10-0.40% Manganese 0.60-1.00% Sulphur 0.050 max. Phosphorus 0.050 max. Table. 1: EN8 Material Composition 080M40 (EN-8) – mechanical properties Yield Stress 465 N/mm2 0.2% Proof Stress 450 N/mm2 Elongation 16% Min Hardness 201-255 Brinell Table. 2: Properties of Material Chemical composition of wire electrode Carbon 0.06-0.15% Silicon 0.80-1.15% Manganese 0.08-0.15% Phosphorus ≤ 0.025% Silicon ≤ 0.035% Copper ≤ 0.50% Table. 3: Chemical Composition of wire electrode ER70S-6 B. ANALYSIS OF S/N RATIO In the Taguchi Method the term ‘signal’ represents the desirable value (mean) for the output characteristic and the term ‘noise’ represents the undesirable value (standard Deviation) for the output properties. Therefore, the S/N ratio to the desirable value of the S. D. S/N ratio used to calculate the quality characteristic variable from the desired value. The S/N ratio S is defined as S = - 10 log (Mean of sum square of reciprocal of measured Data) To get the optimal welding performance, higher the better quality characteristic for penetration must be taken. Regardless of the category of the quality, a greater S/N ratio corresponds to better quality characteristics. Therefore, the optimal level of the process parameters is the level with the greatest S/N ratio. C. ANALYSIS OF VARIANCE The purpose of the analysis of variance (ANOVA) is to investigate which design parameters significantly affect the quality characteristic. This is to be accomplished by
- 3. Parametric Optimization on MIG Welded EN8 Material Joints by using Taguchi Method (IJSRD/Vol. 1/Issue 9/2013/0040) All rights reserved by www.ijsrd.com 1849 separating the total variability of the S/N ratios, which is measured by the sum of the squared deviations from the total mean S/N ratio, in contributions by each of the design parameters and the error. First, the total sum of squared deviations SST from the total mean S/N ratio can be calculated. IV. EXPERIMENTAL PLAN AND DETAILS The experimental design was according to an L’9 array based on Taguchi method, while using the Taguchi orthogonal array would markedly reduce the number of experiments. A set of experiments designed using the Taguchi method was conducted to investigate the relation between the process parameters and response factor. Minitab 16 software is used for optimization and graphical analysis for obtaining data. Parameters Level 1 Level 2 Level 3 Welding Current(Amp) 120 125 130 Wire feed (m/min) 2.4 2.8 3.2 Gas flow rate (l/min) 12 14 16 Table. 4: Mig welding parameters and their levels Ru n Weldi ng curren t Amp Wire feed m/min Gas flow rate l/min Tensile strength Ha rd ne ss 1 120 2.4 12 590 70 2 120 2.8 14 603 88 3 120 3.2 16 594 74 4 125 2.4 14 592 84 5 125 2.8 16 622 88 6 125 3.2 12 522 80 7 130 2.4 16 440 84 8 130 2.8 12 511 74 9 130 3.2 14 540 78 Table. 5: Design of Experiments Exp. Tensile strength Hardness Run S/N MEAN S/N MEAN 1 55.41704 590 36.90196 70 2 55.60635 603 38.84965 88 3 55.47573 594 37.38463 74 4 55.44643 592 38.48559 84 5 55.87581 622 38.88965 88 6 54.35341 522 38.0618 80 7 52.86905 440 38.48559 84 8 54.16842 511 37.38463 74 9 54.64788 540 37.84189 78 Table. 6: Mean and S/N ratio for Tensile strength and hardness Level Welding Current Wire Feed Gas Flow Rate 1 595.7 540.7 541.0 2 578.7 578.7 578.3 3 497.0 552.0 552.0 Delta 98.7 38.0 37.3 Rank 1 2 3 Table. 7: Response table for Mean of Tensile strength Fig. 1: Main effect plot for a mean of tensile strength Level Welding Current Wire Feed Gas Flow Rate 1 37.73 37.96 37.45 2 38.48 38.39 38.41 3 37.9 37076 38.25 Delta 0.75 0.63 0.96 Rank 2 3 1 Table. 8: Response table of S/N Ratio for Tensile strength Level Welding current Wire feed Gas flow rate 1 77.33 79.33 74.67 2 84.00 83.33 83.33 3 78.67 77.33 82.00 Delta 6.67 6.00 8.67 Rank 2 3 1 Table. 9: Response table of mean for Hardness Fig. 2: Main effect plot for S/N Ration of tensile Strength Level Welding current Wire Feed Gas Flow Rate 1 37.73 37.96 37.45 2 38.48 38.39 38.41 3 37.90 37.76 38.25 Delta 0.75 0.63 0.96 Rank 2 3 1 Table. 10: Response table of S/N Ratio for Hardness
- 4. Parametric Optimization on MIG Welded EN8 Material Joints by using Taguchi Method (IJSRD/Vol. 1/Issue 9/2013/0040) All rights reserved by www.ijsrd.com 1850 Fig. 3: Main effect plot for Mean of Hardness Fig. 4: Main effect plot for S/N Ration of Hradness V. CONCLUSION 1) By use of ANOVA it can conclude that Current is the most significant parameter. 2) The gas flow rate is found to have an effect on hardness. Increase in welding current as increase the hardness. 3) In this experiment the value of the S/N ratio of tensile strength 55.87 which indicate optimal input parameter current 125 A, wire feed 2.5 m/min and gas flow rate is 16 l/min. 4) In this experiment the value of the S/N ratio of tensile strength 38.33 which indicate optimal input parameter current 125 A, wire feed 2.5 m/min and gas flow rate is 16 l/min. REFERENCES [1] Wong, Y.-R., Ling, S.-F., An investigation of dynamical metal transfer in GMAW - effects of argon shielding gas, Journal of Materials Processing Technology (2013), 2013.08.003 [2] Izzatul Aini Ibrahim, The Effect of Gas Metal Arc Welding (GMAW) processes on different welding parameters, International Symposium on Robotics and Intelligent Sensors 2012 (IRIS 2012), 2012.07.342 [3] D.W. Cho, A study on V-groove GMAW for various welding positions, Journal of Materials Processing Technology 213 (2013) [4] Chandresh N. Patel, Parametric Optimization of Weld Strength of Metal Inert Gas Welding and Tungsten Inert Gas Welding By Using Analysis of Variance and Grey Relational Analysis, Modern Engineering and Emerging Technology, Vol. 1, Issue: 3, April- 2013. [5] Upinder kumar, Optimization of Cutting Parameters in High Speed Turning by Grey Relational Analysis, International Journal of Engineering Research and Applications (IJERA) ISSN: 2248-9622, Vol. 3, Issue 1, January -February 2013, pp.832-839 [6] P. T. Houldcroft, Reference Book - Arc Welding & Welding Process Technology. [7] S. V. Sapakal, Parametric Optimization of MIG Welding Using Taguchi Design Method, International Journal of Advanced Engineering Research and Studies, Vol. 1, July-Sept.2012.